KR20020023980A - Method of making paraffin wax of waterproof and mortar - Google Patents

Abstract

The present invention relates to a paraffin wax of mortar, and to a cracking crack of a building, a surface waterproofing, and an easy manufacturing method for attaching urgent construction and marble.

(A) To do this, mix polystyrene polynormal, paraffin wax, microwax and rosin (AT) with sand selected by drying at a melting point temperature of 150-220 degrees Celsius in a tank container that can dissolve paraffin wax. Manufacturing method of paraffin wax of mortar to make it into small size so that consumers can easily dissolve it in iron containers or bowls

(B) To do this, mix polystyrene polynormals, paraffin wax, microwax, and rosin at a melting point temperature of 150-220 degrees Celsius in a tank container that can dissolve paraffin wax at The manufacturing method in which the paraffin wax (2) for waterproofing is formed by pouring it into the mold case mold (1) and cooling it.

(C) Cement plastering work by penetrating (12) waterproof paraffin wax on the surface (11) of the building, and forming a thin waterproof layer (13) on the surface, and then applying a (pytal) asphalt (14) to the surface of the thin waterproof layer again. Waterproof construction method made easy to adhere to

Description

Waterproofing and Mortar Process for Making Paraffin Wax {omitted}

The present invention relates to a cracking part of a building as a paraffin wax of mortar and a manufacturing method which is easy to use, such as surface waterproofing and urgent construction tairu and marble attachment.

Conventionally, the concrete construction structure is a waterproof construction method due to leakage such as cracks (floor) in the floor and walls, such as the method of directly injecting the waterproofing liquid to the cracks (cracking) and the surface portion, and spraying by spraying the waterproofing liquid itself, etc. Various methods such as construction method by mixing liquid and concrete (cement) have survived, but high repair cost and simple construction method are inexpensive repair cost, but the crack (crack) part of the concrete structure During this period, the accumulated dust and impurities such as concrete fragments are accumulated, so even if it is repaired by spraying the waterproofing liquid, the waterproofing liquid has a low penetration and is applied lightly only on the outer surface, resulting in a short lifespan and high waterproofing effect. In rainy season or when heavy rain falls, or when there is rain on the surface of the concrete floor. Was likely to be re-induced by rainwater easily re-invading the cracked concrete structure, and when re-repaired later, it was necessary to separate and rework the material that was previously repaired. There were a lot of inconveniences due to insecure waterproof construction methods.

In the present invention can be used for waterproof work and emergency repair work in concrete buildings and other buildings, work by maintaining the safety and spraying machine device by filling and bonding the crack (crack) cracks on the inner surface of the cracked site The present invention relates to a method of manufacturing waterproofing and mortar that can help simplify and increase work efficiency.

1 is an illustration of a mold case frame

Figure 2 is an illustration of a general waterproof paraffin wax

3 is a cut-off view of the penetration of waterproofing and thin waterproofing layer and asphalt on the building (example)

(Explanation of symbols for the main parts of the drawing)

1: Mold case frame 2: Water-resistant paraffin wax

11: Building surface 12: Penetration 13: Light waterproofing layer 14: Asphalt (pyramid)

The present invention is produced by dividing the paraffin wax of mortar and paraffin wax for general waterproofing to solve the above problems.

Let's introduce how to use it first.

Paraffin wax is a material having high waterproofing effect. It uses heat of fire such as a firepower tool to directly heat the heat of the building, and at the same time, paraffin wax is applied to the surface of the building 11 as patent application number 10-2000-0080981. When the paraffin wax is melted and applied at the same time while heating, the paraffin wax dissolved in a liquid state becomes a fast, strong and adhesive material having high penetration (12).

The method of using paraffin wax of mortar is to dissolve it in iron container or bowl by applying heat, and to dissolve it in spraying machine device and to use it simply by using a rope. It shows strength similar to that of concrete.

It is used for emergency construction of the surface of buildings, floors and waterproofing, attaching to the roofing and marble, cracking (cracking), and heating the heat tools such as thermal tools directly to the cracked areas to maintain safety in the construction site and waterproof. Can be increased.

Paraffin wax for general waterproofing is used by using the heat of thermal power tools such as inverted lamps, and sprayed in liquid state by spraying it in the spraying machine device. It can be applied by first penetrating 12 into the thin film and again forming a thin waterproof layer 13 on the upper surface of the secondary surface.

Even the deepest cracks of cracks can be filled to provide a good waterproof effect and easy installation.

1) The method of manufacturing mortar and paraffin wax described above is as follows.

Prepared by dry sorting of ordinary sand and preparing solid material in weight% ratio in tank tank which can dissolve paraffin wax. Polystyrene polynormal 10-50% paraffin wax 50-90% microwax 5-30% rosin Put 5-30% (KT5-30) at the weight ratio into the tank and mix the mixture at the melting point temperature of 150-220 degrees Celsius, and then put the dried and sorted sand in the tank at the weight ratio of 70-85%. As a result, paraffin wax of mortar is produced, and the color of the powder may be selected by adding the color of stone powder, soil, and other color pigments as necessary. The paraffin wax of mortar mixed and mixed in this way is mortar paraffin wax that is solidified and formed into a small size that is easily melted and used by a consumer.

2) The manufacturing method of the general waterproof paraffin wax described above is as follows.

Waterproofing paraffin wax refers to a manufacturing method in the state of excluding the selected sand.

Prepare the solid raw material in the weight ratio% in the above tank tank, and put it in the tank barrel according to the weight ratio of polystyrene polynormal 5-40% paraffin wax 50-90% microwax 5-35 rosin 5-30%. When mixing mixer at 150-220 degrees Celsius, general waterproof paraffin wax is manufactured.The color of this is selected as above, add pigments, etc., and add liquid paraffin wax to the tank case (1). After moving and cooling and separating each, a general waterproof paraffin wax (2) is formed.

Paraffin wax prepared as described above is easy to construct and easy to handle and store.

The mortar and general waterproofing paraffin wax of the present invention has a fast penetration force and strong adhesion to the friction surface in the state dissolved in the liquid during construction.

Morphal paraffin wax has a short solid time (positive) and has a strength close to concrete in the 100% solid state.

Crack (Crack) The gold is melted and penetrated into the liver area, and the adhesion is high as it is filled, so it can protect the construction site and increase the waterproof effect.

It can also be used for surface flooring, emergency construction, and for attachment of tieru or marble

Paraffin wax for general waterproofing penetrates even the deepest and deepest part of cracks and is formed as a thin waterproof layer on the surface.

Claims (5)

A tank barrel that can prepare dry-selected sand and melt paraffin wax in the method of manufacturing paraffin wax of mortar, which is easy to use for cracking (cracking) and surface floor of concrete and other buildings, and for urgent construction, and attaching to tairu and marble. Prepared by weight percentage of solid raw material in polyvinyl polyphenol 5-40% paraffin wax 50-80% microwax 5-30% rosin 5-30% (AT5-30%) in the tank After mixing the mixed mixer in the liquid state of melting temperature 150-220 degrees Celsius, and mixing the dried screened sand with the weight g ratio 70-90 of the tank barrel, the color of the powder of stone and soil and other colors Method for manufacturing paraffin wax of mortar, which selectively adds pigments, etc. and mixes and mixes mortar paraffin wax in a small size so that it can be easily melted and used by consumers. A tank barrel that can prepare dry-selected sand and melt paraffin wax in the method of manufacturing paraffin wax of mortar, which is easy to use for cracking (cracking) and surface floor of concrete and other buildings, and for urgent construction, and attaching to tairu and marble. Prepared by weight percentage of solid raw material in polyvinyl polyphenol 5-40% paraffin wax 50-80% microwax 5-30% rosin 5-30% (AT5-30%) in the tank After mixing the mixed mixer in the liquid state of melting point temperature 150-220 degrees Celsius and mixing the dried screened sand with the weight g ratio 70-90 in the tank barrel, the color of the color of the powder of stone and soil and the pigment of other colors The paraffin wax of mortar mixed and mixed as necessary and mixed and mixed as necessary, and the paraffin wax of mortar which solidifies and forms into a small size so that it can be melted and used easily by a consumer. Cracks and surfaces in concrete and other structures. In the method of manufacturing paraffin wax for general waterproofing, which is easy for waterproofing the floor, a solid raw material is prepared in a weight ratio% in a tank container capable of dissolving paraffin wax, and polystyrene polynormal 5-40% paraffin wax 50-85% micro Wax 5-30% Rosin 5-30% in a tank by weight ratio and mix in a liquid state with a melting point temperature of 150-220 degrees Celsius. According to the present invention, a liquid paraffin wax (2) is added to the mold case and poured into the mold case mold (1), cooled, and then separated to form paraffin wax (2). Cracks and surfaces in concrete and other structures. In the manufacturing method of paraffin wax for general waterproofing, which is easy for waterproofing the floor, a solid raw material is prepared in a weight ratio% in a tank container capable of dissolving paraffin wax, and polystyrene polynormal 5-40% paraffin wax 50-85% micro Wax 5-30% Rosin 5-30% in a tank by weight ratio and mix in a liquid state with a melting point temperature of 150-220 degrees Celsius. Paraffin wax (2), which is formed by selectively adding according to the present invention and transferring the liquid paraffin wax into the mold case mold (1), cooling it, and then separating it. It is easy to bond with cement and plaster because it is applied by spraying the (octale) asphalt (14) on the surface of the thin waterproof layer (13) of water-resistant paraffin wax such as cracks and cracks of concrete and other buildings (11). In the construction method, heat the surface of the building using the heat of the inverted lamp, thermal tools, etc., at the same time, dissolve paraffin wax into liquid using the spraying machine, etc., and then spray it through the nozzle of the motor pump and the sprayer. Penetrate (12) with a waterproofing liquid while heating the heat of a fire tool, etc. (more than 80 degrees Celsius) on the surface of the building, and apply it to the surface with a thin waterproof layer (13) again, and then again (solid) asphalt (14) in a solid state. Waterproof construction method that is easy to work with cement plastering because it is applied by using a nozzle or pulley brush of motor pump or sprayer