JPS6320100A - Excreta treating agent for pet - Google Patents

Abstract

PURPOSE:To dehydrate or deodorize excreta or urine and to permit easy removing and clearing thereof by spraying and applying a material formed by grinding and drying an ore material such as zeolite to the excreta or urine from above when a pet produces the excreta or urine. CONSTITUTION:At least one kind of the ore material selected from the group consisting of the zeolite, crystobalite and bentonite is ground to 10 mesh pass particle size and is dried to <=5wt% moisture to prepare the dung treating agent for pets. More specifically, the above-mentioned dung treating agent is sprayed and applied to the excreta or urine from above or side way when a small animal such as dog or cat produces the excreta or urine indoors or out. The excreta or urine is thereby dehydrated and deodorized so that the excreta or urine can be easily removed and cleared.

Description

Detailed Description of the Invention (Industrial Applicability) The present invention is applied by spraying from the top or side of small animals (pets) such as dogs and cats when they defecate or urine indoors or outdoors. The present invention relates to a granular treatment agent for dehydrating and removing feces or urine to facilitate their removal and cleaning.

(Prior art) In order to dispose of pet excrement, inorganic substances such as sand and zeolite, granulated materials such as pulp and peanut shells are placed in a bed container, and the pet excrement is replaced with the excrement as necessary. has been known for a long time.

However, if your pet defecates or urinates indoors in a place other than this container, this container will not be useful, and you will have to spend a lot of time and effort to remove the feces and urine and clean it.

Also, if you take your pet outside for a walk and it feces or urinates, it may be difficult to remove it depending on the condition of the feces and other factors.However, if you leave it as it is, it may cause a bad odor or a buildup of flies, etc. It causes a great nuisance to people and passersby. In addition, when a pet such as a dog or cat feces or urinates outdoors, if there are plants nearby, this can cause a phenomenon called fertilization, so it is desirable to dispose of it immediately.

Devices designed to immediately remove feces for pet walking are also available on the market, but they are cumbersome to carry when walking a dog, and are often unusable depending on the condition of the feces. Furthermore, since it is a mechanical device, it cannot provide a deodorizing effect.

(Problem to be solved by the invention) By making it easier to dehydrate, deodorize, remove and clean,
The purpose of the present invention is to provide a granular treatment agent that eliminates fly buildup and prevents fertilization of plants when they are nearby.

(Means for Solving the Problems) The present invention provides at least one mineral material selected from the group consisting of zeolite, cristobalite, and bentonite in the form of powder and granules of 10 mesh baths, and with a water content of 5% by weight.
To provide a pet excrement treatment agent containing the following dry matter as an active ingredient.

Furthermore, there is provided a pet excrement treatment agent comprising a mixture of 100 parts by weight of the mineral material and 15 parts by weight or less of a deodorizing agent in the form of powder or granules of 10 mesh baths.

As a deodorizer, ferrous sulfate or Zero Shoe (trade name, Biochemical Research Disruption) may be used.

Furthermore, 20 parts by weight or less of sodium polyacrylate (super absorbent polymer) may be added to the mixture as an absorbent.

The reason why the water content of the mineral material is set to be 5% by weight or less is that if it is more than 5% by weight, the purpose of absorbing water from excrement cannot be sufficiently achieved.

Also, the reason why the size of the powder and granular material is set to 10 mesh passes is that in order to cover the surface of the excrement, it is necessary to increase the surface area by reducing the size of the treatment agent to the extent that it becomes heather, and if the size is larger than 10 mesh, the covering effect will be reduced. as well as insufficient contact between them. In addition, the amount of deodorizing agent used is 15 parts by weight or less per 100 parts by weight of the mineral material, thereby achieving a nearly perfect deodorizing effect, but even if more than 15% by weight is used, the deodorizing effect does not change. It's for a reason.

Since zeolite, cristobalite or bentonite used according to the present invention is a mineral material, it not only captures ammonia that causes bad odors, but also has a dehydrating effect, and has the effect of adsorbing and consolidating manure, thereby improving manure. to prevent

The powdered treatment agent of the present invention is placed in a simple container such as a squirt can, carried when walking the dog, and sprayed on the dog's excrement and urine to deodorize it. will be further explained.

Example 1 The olide crushed pieces were crushed using a fine pulverizer r manufactured by Fuji Baudal Co., Ltd.
Finely pulverized using ASK-nJ (trade name), with an average particle size of 1
0 micron, and then dried at 120° C. for 6 hours to form a fine powder with a moisture content of 0.1%, which was used as a pet excrement treatment agent.

Example 2 For 100 parts by weight of the zeolite fine powder of Example 1, 1
10 parts by weight of ferrous sulfate in the form of powder with 0 mesh pass was mixed to prepare a pet excrement coating treatment agent consisting of a mixture.

Example 3 For 100 parts by weight of the zeolite fine powder of Example 1, 1
1.0 parts by weight of the deodorizer Zero Shoe (trade name) pulverized to a particle size of 0 mesh pass was uniformly mixed.

A pet excrement coating treatment agent consisting of a mixture was prepared.

Example 4 After drying bentonite raw ore at 120°C for 3 hours to reduce the free moisture to 1 t or less,
-4" (trade name) to give a powder of 10 mesh size. This dried bentonite powder 1
00 parts by weight was mixed with 10 parts by weight of ferrous sulfate having a particle size of 10 mesh baths to prepare a pet excrement treatment agent consisting of a mixture.

Example 5 100 parts by weight of the dried bentonite powder obtained according to Example 4 was uniformly mixed with 1.0 parts of a deodorizer (Zero Shoe) crushed to a particle size of 10 mesh passes, and the mixture was extracted. It was made into a pet waste treatment agent.

Example 6 To 100 parts by weight of the dry zeolite powder obtained according to Example 2, 20 parts by weight of sodium polyacrylate with a particle size of 10 mesh baths and Example surface treatment effect (caking property) +++ +++ +++++++
+' +++ (deodorizing) ++ ++-1-
The tests for each item of ++++++ ++ ++++++ were conducted as follows.

1) Ammonia removal rate: 10.0y of sample powder in a 300ml Erlenmeyer flask
Measure out the felt and impregnate it with 0.5 g of 0.3% ammonia water (2CTLX 2crrLX 2ho)
After charging the flask, the mouth of the flask was immediately closed with a polyethylene film, and the flask was left at a temperature of 30°C to 35°C for 60 minutes, and the ammonia gas concentration inside the flask was measured using a Kitayo type gas detector. . Based on the results of the blank test obtained before charging the sample, the ammonia removal rate was calculated using the following formula.

×100 11) Water absorption rate Seal the bottom of a glass tube with a diameter of 4 CTL and a length of 5 cr IL with r paper, measure 20 g of the sample into it, and
The bottom of the boat was brought into contact with the water surface, and the water absorption amount (increase in g) of the sample in the glass tube was measured after 1 minute, and the water absorption rate was calculated using the following formula.

111) Treatment effect The caking ability and deodorizing ability of the treatment agent against excrement and urine were checked by a sensory test, and evaluated within this range, with +++ being the most effective and O being the least effective.

(Effects of the Invention) As explained above, according to the present invention, the present invention provides a manure treatment agent prepared by pulverizing a mineral material to a powder particle size of 10 mesh baths and drying it to a moisture content of 5% by weight or less, or a powder of 10 mesh baths containing this mineral material. A deodorizer ground to particle size was mixed. In addition, we have developed a water purifier made of a mixture of these mixtures and sodium polyacrylate, which is deodorized and easy to remove and clean, so that it can be used to remove excrement and urine from pets indoors and outdoors outside of designated areas. Treatment becomes extremely easy and is beneficial for public health. In particular, by treating manure near outdoor plants in this way, effects such as preventing fertilization of plants can be obtained.

Claims (1)

[Claims] 1. At least one mineral material selected from the group consisting of zeolite, cristobalite, and bentonite.
A pet excrement treatment agent that is in the form of 0 mesh pass powder and contains dry matter with a water content of 5% by weight or less as an active ingredient. 2. The pet excrement treatment agent according to claim 1, which comprises a mixture of 100 parts by weight of a mineral material and 15 parts by weight or less of a 10 mesh pass deodorizing agent. 3. Claim 2 consisting of a mixture of 100 parts by weight of the mineral material and 20 parts by weight or less of the water absorbing agent.
Pet excrement treatment agent as described in section.