JPH1170965A - Cap liner material composition and cap molded article - Google Patents
Cap liner material composition and cap molded articleInfo
- Publication number
- JPH1170965A JPH1170965A JP9231575A JP23157597A JPH1170965A JP H1170965 A JPH1170965 A JP H1170965A JP 9231575 A JP9231575 A JP 9231575A JP 23157597 A JP23157597 A JP 23157597A JP H1170965 A JPH1170965 A JP H1170965A
- Authority
- JP
- Japan
- Prior art keywords
- cap
- liner
- composition
- synthetic resin
- liner material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、キャップライナー
材用組成物およびそれを用いたキャップ成形品に関し、
更に詳細には本発明は、臭気成分の発散を防止して内容
物の香味劣化を防止することを企図したキャップライナ
ー材用組成物およびそれを用いたキャップ成形品に関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a composition for a cap liner material and a molded article of a cap using the same.
More specifically, the present invention relates to a composition for a cap liner material intended to prevent the emission of odor components and prevent the flavor of the contents from deteriorating, and a cap molded product using the same.
【０００２】[0002]
【従来の技術】従来、清涼飲料水やジュースなどの液体
を、合成樹脂製容器或いはガラス容器に充填し、その容
器の口部を密封するためのキャップとしては、アルミ合
金などの金属製のキャップシェルを備えた金属キャッ
プ、或いはポリプロピレンなどの合成樹脂製のキャップ
シェルを備えた合成樹脂キャップが使用されている。金
属キャップは、金属薄板からなる円形の天板部とその周
縁から垂下した筒部とからなるキャップシェルと、該天
板部内面側に固着された軟質の合成樹脂からなる薄肉状
のライナーとを備えている。この金属キャップは、容器
の口部に被せ、容器の口部外周に形成された雄螺子に合
わせて筒部を塑性加工することによって口部に装着する
ようになっている。合成樹脂製キャップは、円形の天板
部とその周縁から垂下した筒部とからなり、筒部内壁面
に容器の雄螺子と螺合する螺子部が設けられたキャップ
シェルと、該天板部の内面側に固着された軟質の合成樹
脂からなる薄肉状のライナーとを備えている。この合成
樹脂製のキャップは、容器の口部に被せ、キャップを閉
方向に回転させて容器口部に螺着するようになってい
る。そして従来、これらのキャップのライナー材として
は、下地の天板部内面に強固に接着する、低密度ポリエ
チレン、ポリプロピレン、エチレンビニルアルコール
（ＥＶＡ）などの１種、または２種以上を混合してなる
ベースポリマーに、エチレン-プロピレンゴムなどのゴ
ム成分、顔料、滑剤、酸化防止剤などの添加剤を必要に
応じて添加、混合した樹脂組成物が用いられている。2. Description of the Related Art Conventionally, a liquid such as soft drink or juice is filled in a synthetic resin container or a glass container, and a metal cap such as an aluminum alloy is used as a cap for sealing the mouth of the container. A metal cap with a shell or a synthetic resin cap with a cap shell made of synthetic resin such as polypropylene is used. The metal cap includes a cap shell composed of a circular top plate portion made of a thin metal plate and a cylindrical portion hanging down from the periphery thereof, and a thin liner made of a soft synthetic resin fixed to the inner surface side of the top plate portion. Have. The metal cap is placed over the mouth of the container by plastically processing the cylindrical portion in accordance with a male screw formed on the outer periphery of the mouth of the container. The cap made of a synthetic resin is composed of a circular top plate portion and a cylindrical portion hanging down from the periphery thereof, and a cap shell provided with a screw portion to be screwed with a male screw of the container on the inner wall surface of the cylindrical portion, and a cap shell of the top plate portion. A thin liner made of a soft synthetic resin fixed to the inner surface side. The cap made of synthetic resin is placed over the mouth of the container, and the cap is rotated in the closing direction and screwed onto the mouth of the container. Conventionally, as a liner material for these caps, one or a mixture of two or more of low-density polyethylene, polypropylene, ethylene vinyl alcohol (EVA), etc., which are firmly adhered to the inner surface of the top plate portion of the base material. A resin composition is used in which a rubber component such as ethylene-propylene rubber, an additive such as a pigment, a lubricant, and an antioxidant are added to and mixed with a base polymer as needed.
【０００３】[0003]
【発明が解決しようとする課題】しかしながら、従来の
キャップに用いていたライナー用組成物は、ベースポリ
マーに配合する、ある種の添加成分が、臭気を呈する場
合があり、それを配合した組成物を用いたライナーを形
成し、そのキャップを容器口部に装着すると、ライナー
から臭気成分が容器内の液体に移り、飲用する際にその
臭気によって風味を損ねる場合があった。この臭気の移
行を防ぐため、臭気のある添加成分を省こうとしても、
所望のライナー特性を得るためには、その成分がどうし
ても必要であったり、代替材料が無いなどの理由によっ
て、その成分を省くことができず、仮にその成分を省く
とライナーの性能が低下してしまい、成形性、開栓性や
密封性が悪化する恐れがある。However, in the liner composition used in the conventional cap, a certain additive component added to the base polymer sometimes exhibits an odor. When a cap made of a liner is formed on the mouth of a container, an odor component is transferred from the liner to the liquid in the container, and the flavor may be impaired by the odor when drinking. In order to prevent the transfer of this odor, even if we try to eliminate odorous additives,
In order to obtain the desired liner properties, the component is absolutely necessary, or the component cannot be omitted because there is no alternative material, and if the component is omitted, the performance of the liner is reduced. As a result, the moldability, the opening property and the sealing property may be deteriorated.
【０００４】本発明は前記事情に鑑みてなされたもの
で、臭気成分の発散を生じないキャップライナー材用組
成物およびそれを用いたキャップ成形品の提供を目的と
している。The present invention has been made in view of the above-mentioned circumstances, and an object of the present invention is to provide a composition for a cap liner material that does not emit odorous components and a molded article of a cap using the same.
【０００５】[0005]
【課題を解決するための手段】本発明の請求項１に係る
発明は、合成樹脂主材１００重量部に対し、モレキュラ
ーシーブ吸着剤を０．０５〜２．０重量部混合してなる
キャップライナー材用組成物である。請求項２に係る発
明は、前記合成樹脂主材が、低密度ポリエチレンを、キ
ャップライナー材用組成物に対し１０〜９５重量部含有
した、金属キャップに用いられる請求項１記載のキャッ
プライナー材用組成物である。請求項３に係る発明は、
前記合成樹脂主材が、ポリプロピレンを、キャップライ
ナー材用組成物に対し５〜２０重量部含有した、合成樹
脂キャップに用いられる請求項１記載のキャップライナ
ー材用組成物である。請求項４に係る発明は、キャップ
と、請求項１記載のキャップライナー材用組成物からな
るライナーを備えたことを特徴とするキャップ成形品で
ある。請求項５に係る発明は、金属キャップと、請求項
２記載のキャップライナー材用組成物からなるライナー
とからなるキャップ成形品である。請求項６に係る発明
は、合成樹脂キャップと、請求項３記載のキャップライ
ナー材用組成物からなるライナーとからなるキャップ成
形品である。According to a first aspect of the present invention, there is provided a cap liner obtained by mixing 0.05 to 2.0 parts by weight of a molecular sieve adsorbent with 100 parts by weight of a synthetic resin base material. It is a material composition. The invention according to claim 2 is for a cap liner material according to claim 1, wherein the synthetic resin main material is used for a metal cap containing 10 to 95 parts by weight of low-density polyethylene based on the composition for the cap liner material. A composition. The invention according to claim 3 is
The composition for a cap liner material according to claim 1, wherein the synthetic resin main material contains 5 to 20 parts by weight of polypropylene with respect to the composition for a cap liner material and is used for a synthetic resin cap. According to a fourth aspect of the present invention, there is provided a molded cap product comprising a cap and a liner comprising the composition for a cap liner material according to the first aspect. The invention according to claim 5 is a cap molded product comprising a metal cap and a liner comprising the composition for a cap liner material according to claim 2. The invention according to claim 6 is a cap molded product comprising a synthetic resin cap and a liner comprising the composition for a cap liner material according to claim 3.
【０００６】[0006]
【発明の実施の形態】本発明によるキャップライナー材
用組成物は、合成樹脂主材１００重量部に対し、モレキ
ュラーシーブ吸着剤を０．０５〜２．０重量部混合して
なるものである。モレキュラーシーブ吸着剤とは、合成
ゼオライトのことをさし、代表的には、ユニオンカーバ
イド社よって工業化され、吸収特性の異なる各種のグレ
ードがある。一般にモレキュラーシーブ吸着剤は、アル
ミノ・シリケート組成を有している。その結晶構造は蜂
の巣状で、細孔を通して三次元的に連結している内部空
洞を有している。モレキュラーシーブ吸着剤は、きわめ
て大きな内部表面積を有している。一般にモレキュラー
シーブ吸着剤の内部空洞は全て均一であり、分子径サイ
ズの細孔を通して連結されていて、結晶内の全ての表面
積が吸着に有効に作用する。その結果、モレキュラーシ
ーブ吸着剤は、優れたガス吸着特性を有している。本発
明において使用されるモレキュラーシーブ吸着剤は、ラ
イナー材用組成物の他の添加成分の持つ臭気を吸着でき
るものであれば良い。好ましくは、高湿度下または水の
存在下においても、臭気除去能力を保持するものが用い
られる。そのような吸着剤として、市販品を例示すれ
ば、UNION SHOWA K.K.製の商品名アブセンツ（登録商
標）が挙げられる。BEST MODE FOR CARRYING OUT THE INVENTION The composition for a cap liner material according to the present invention is obtained by mixing 0.05 to 2.0 parts by weight of a molecular sieve adsorbent with 100 parts by weight of a synthetic resin main material. The molecular sieve adsorbent refers to a synthetic zeolite, and is typically industrialized by Union Carbide and has various grades having different absorption characteristics. Generally, the molecular sieve adsorbent has an alumino-silicate composition. Its crystal structure is honeycomb, with internal cavities connected three-dimensionally through pores. Molecular sieve adsorbents have a very large internal surface area. Generally, the internal cavities of the molecular sieve adsorbent are all uniform and connected through pores of molecular size, so that all surface area within the crystal effectively affects adsorption. As a result, the molecular sieve adsorbent has excellent gas adsorption characteristics. The molecular sieve adsorbent used in the present invention may be any as long as it can adsorb the odor of other components added to the liner composition. Preferably, one that retains the odor removing ability even under high humidity or in the presence of water is used. As an example of such an adsorbent, commercially available products include Absents (registered trademark) manufactured by UNION SHOWA KK.
【０００７】モレキュラーシーブ吸着剤の、キャップラ
イナー材用組成物に対する添加量は、０．０５〜０．２
重量部とする。このモレキュラーシーブ吸着剤の添加量
が０．０５重量部よりも少ないと、モレキュラーシーブ
吸着剤による配合成分の臭気除去効果が十分に得られな
くなる。モレキュラーシーブ吸着剤の添加量が０．２重
量部よりも多いと、そのライナー材用組成物の成形特性
が悪くなり、ライナー形状に加工するのが困難となる。
又、あまりモレキュラーシーブ吸着剤の添加量を増やし
ても、コストが上昇すると共に、余分な吸着作用によっ
て液体の香気成分をも吸着してしまい、製品の風味を低
下させる原因にもなる。The addition amount of the molecular sieve adsorbent to the composition for the cap liner material is 0.05 to 0.2.
Parts by weight. If the amount of the molecular sieve adsorbent is less than 0.05 parts by weight, the effect of the molecular sieve adsorbent to remove the odor of the compounded components cannot be sufficiently obtained. If the amount of the molecular sieve adsorbent is more than 0.2 parts by weight, the molding characteristics of the composition for a liner material will deteriorate, and it will be difficult to process the composition into a liner shape.
Further, even if the amount of the molecular sieve adsorbent is excessively increased, the cost is increased, and the extra odor component is also adsorbed due to the extra adsorption action, which causes a reduction in the flavor of the product.
【０００８】本発明によるキャップライナー材用組成物
の合成樹脂主材（ベースポリマー）は、適用するべきキ
ャップの材質に合わせて、各種の合成樹脂の中から、１
種又は２種以上を混合して用いて良い。キャップがアル
ミ合金などの金属からなる金属キャップである場合、好
適な合成樹脂主材は、低密度ポリエチレンを、キャップ
ライナー材用組成物に対し（１０〜９５重量部含有した
ものである。低密度ポリエチレン量が１０重量部よりも
少ないとライナー材の金属表面への接着が悪くなり、９
５重量部より多いと成型性が困難となり、ライナー材の
弾性に欠け、開栓トルクや密封性が悪くなる。キャップ
がポリプロピレンなどの合成樹脂からなる合成樹脂キャ
ップである場合、好適な合成樹脂主材は、ポリプロピレ
ンを、キャップライナー材用組成物に対し５〜２０重量
部含有したものである。ポリプロピレン量が５重量部よ
り少ないとポリプロピレンからなるキャップ表面への接
着が悪くなり、２０重量部より多いと成型性が困難とな
り、ライナー材の弾性に欠け、開栓トルクや密封性が悪
くなる。これら金属キャップ用、合成樹脂キャップ用の
合成樹脂主材とも、その他の成分として、エチレンビニ
ルアルコール、エラストマー成分としてエチレンプロピ
レンゴム、流動パラフィンなどの配合成分を加えて良
い。The synthetic resin main material (base polymer) of the composition for a cap liner material according to the present invention is selected from various synthetic resins in accordance with the material of the cap to be applied.
Species or a mixture of two or more species may be used. When the cap is a metal cap made of a metal such as an aluminum alloy, a suitable synthetic resin main material contains low-density polyethylene (10 to 95 parts by weight based on the composition for the cap liner material. If the amount of polyethylene is less than 10 parts by weight, the adhesion of the liner material to the metal surface becomes poor,
If the amount is more than 5 parts by weight, the moldability becomes difficult, the elasticity of the liner material is lacking, and the opening torque and the sealing property deteriorate. When the cap is a synthetic resin cap made of a synthetic resin such as polypropylene, a suitable synthetic resin main material contains 5 to 20 parts by weight of polypropylene based on the composition for the cap liner material. If the amount of polypropylene is less than 5 parts by weight, adhesion to the surface of the cap made of polypropylene will be poor, and if it is more than 20 parts by weight, moldability will be difficult, the elasticity of the liner material will be lacking, and the opening torque and sealing property will be poor. In addition to these synthetic resin main materials for the metal cap and the synthetic resin cap, blending components such as ethylene vinyl alcohol as an additional component, ethylene propylene rubber as an elastomer component, and liquid paraffin may be added.
【０００９】この合成樹脂主材には、モレキュラーシー
ブ吸着剤以外に、 酸化チタン、フタロシアニンブルー、フタロシアニン
グリーンなどの顔料、 ポリグリセリン脂肪酸エステル、オレイン酸アミド、
エチレンビスオレイン酸アミド、エルカ酸アミドなどの
滑剤（スリップ材）、 シリカなどのアンチブロッキング剤、 酸化防止剤などの添加成分を必要に応じて添加して良
い。[0009] In addition to the molecular sieve adsorbent, pigments such as titanium oxide, phthalocyanine blue, phthalocyanine green, polyglycerin fatty acid ester, oleic amide,
Additives such as a lubricant (slip material) such as ethylenebisoleic amide and erucamide, an antiblocking agent such as silica, and an antioxidant may be added as necessary.
【００１０】本発明のキャップライナー材組成物を得る
には、合成樹脂主材とモレキュラーシーブ吸着剤との必
須成分、或いは必須成分と上記〜も添加成分を必要
に応じて添加し、公知な種々の方法、例えば、ヘンシェ
ルミキサー、Ｖ−ブレンダー、リボンブレンダー、タン
ブラーブレンダー等で混合後、一軸押出機、二軸押出
機、ニーダー、バンバリーミキサー等で溶融混練し、造
粒あるいは粉砕する方法か、もしくは事前に溶融混練せ
ずにドライブレンド品、オートフィーダーによる方法を
用いることができる。In order to obtain the cap liner composition of the present invention, the essential components of the synthetic resin main material and the molecular sieve adsorbent, or the essential components and the above-mentioned additives are added as necessary, and various known components are added. For example, after mixing with a Henschel mixer, a V-blender, a ribbon blender, a tumbler blender, etc., melt-kneading with a single screw extruder, a twin screw extruder, a kneader, a Banbury mixer, or the like, or a method of granulating or pulverizing, or A dry blended product or a method using an auto feeder can be used without prior melt-kneading.
【００１１】次に、本発明のキャップライナー材用組成
物を用いたキャップ成形品について説明する。図１は本
発明によるキャップ成形品の一例を示すものであり、こ
のキャップ成形品１は、金属製のキャップ２と、このキ
ャップ２の内部に設けられたライナー３とからなってい
る。キャップ２は、アルミ合金よりなり、円板状の天面
部４と、その周縁から垂下した筒部５とからなってい
る。筒部５の下部には複数の細いブリッジ６を残して周
方向に筒部を切断する水平スリット７が設けられてい
る。Next, a cap molded product using the composition for a cap liner material of the present invention will be described. FIG. 1 shows an example of a cap molded product according to the present invention. The cap molded product 1 includes a metal cap 2 and a liner 3 provided inside the cap 2. The cap 2 is made of an aluminum alloy, and includes a disk-shaped top surface portion 4 and a cylindrical portion 5 hanging down from a peripheral edge thereof. A horizontal slit 7 is provided at a lower portion of the tubular portion 5 to cut the tubular portion in a circumferential direction while leaving a plurality of narrow bridges 6.
【００１２】キャップ２内に設けられたライナー３は、
天面部４の内面を覆う薄肉状に形成され、天面部４の内
面に密着して設けられている。このライナー３は、上述
した合成樹脂主材１００重量部に対し、モレキュラーシ
ーブ吸着剤を０．０５〜２．０重量部混合してなる本発
明のキャップライナー材用組成物によって形成されてい
る。このキャップライナー材用組成物中の合成樹脂主材
は、低密度ポリエチレンを、キャップライナー材用組成
物に対し１０〜９５重量部含有してなり、金属キャップ
２の天板部４内面に、強固に密着するものである。この
キャップ２の内部に上記キャップライナー材用組成物か
らなるライナー３を密着形成するためのライナー形成法
としては、例えば樹脂組成物を０．５〜１ｍｍ程度の厚
みのシート状に成形後、キャップの形状に合った直径に
打ち抜き、これをキャップ内に挿入、接着する方法、あ
るいは、この組成物を加熱溶融した溶融樹脂を、キャッ
プ２内に一定量落し入れ、キャップ２内に押し型を挿入
して薄肉状のライナー３を成形する、インシェルモール
ド法が好適に用いられる。The liner 3 provided in the cap 2 is
It is formed in a thin shape to cover the inner surface of the top surface portion 4 and is provided in close contact with the inner surface of the top surface portion 4. The liner 3 is formed of the composition for a cap liner material of the present invention, which is obtained by mixing 0.05 to 2.0 parts by weight of a molecular sieve adsorbent with 100 parts by weight of the above-mentioned synthetic resin main material. The synthetic resin main material in the composition for a cap liner material contains 10 to 95 parts by weight of a low-density polyethylene with respect to the composition for a cap liner material. It adheres to. As a liner forming method for tightly forming the liner 3 made of the composition for a cap liner material inside the cap 2, for example, a resin composition is formed into a sheet having a thickness of about 0.5 to 1 mm, and then the cap is formed. A method of punching out to a diameter suitable for the shape of the above, inserting this into a cap and bonding it, or dropping a certain amount of molten resin obtained by heating and melting this composition into the cap 2 and inserting a die into the cap 2 The in-shell molding method of forming the thin liner 3 by using the in-shell molding method is preferably used.
【００１３】このキャップ成形品１は、口部の上端部外
周に雄ネジ８が形成され、この雄ネジ８の直下に膨出段
部９が設けられた容器１０に被せられ、雄ネジ８の溝に
沿うように成形ローラで筒部５を押圧し、かつ筒部５の
下端部を径方向内方に押し曲げて膨出段部９の下端に当
接させるように巻き締めて装着される。容器１０の口部
上端は、キャップ成形品１のライナー３に密接し、それ
によって容器１０の密封性が保たれる。The cap molded product 1 is covered with a container 10 having a male screw 8 formed on the outer periphery of the upper end of the mouth and a bulging step 9 provided immediately below the male screw 8. The cylindrical portion 5 is pressed by the forming roller along the groove, and the lower end portion of the cylindrical portion 5 is pressed inward in the radial direction and bent so as to abut on the lower end of the bulging step portion 9. . The upper end of the mouth of the container 10 is in close contact with the liner 3 of the cap molded product 1, thereby keeping the container 10 hermetically sealed.
【００１４】このキャップ成形品１は、ライナー３の材
料に、合成樹脂主材１００重量部に対し、モレキュラー
シーブ吸着剤を０．０５〜２．０重量部混合してなるキ
ャップライナー材用組成物を用いたことによって、ベー
スポリマーに配合するある種の添加成分が臭気を呈する
場合でも、その臭気をモレキュラーシーブ吸着剤が完全
に吸収し、その臭気が容器内の液体に移って風味を損ね
る不都合を防止することができる。また、材料組成物に
臭気を有する成分が含まれていても、その臭気をモレキ
ュラーシーブ吸着剤が完全に吸収し、その臭気が容器内
の液体に移って風味を損ねる不都合を防止できるので、
少量であれば、臭気のある添加成分をキャップライナー
材用組成物に添加することができるようになる。This cap molded product 1 is a composition for a cap liner material obtained by mixing the material of the liner 3 with 0.05 to 2.0 parts by weight of a molecular sieve adsorbent based on 100 parts by weight of a synthetic resin main material. By using, even if a certain additive component blended in the base polymer has an odor, the molecular sieve adsorbent completely absorbs the odor, and the odor is transferred to the liquid in the container, and the flavor is impaired. Can be prevented. Also, even if the material composition contains a component having an odor, the molecular sieve adsorbent completely absorbs the odor, so that the odor can be prevented from being transferred to the liquid in the container and the inconvenience of impairing the flavor can be prevented.
If the amount is small, an odorous additive component can be added to the composition for a cap liner material.
【００１５】図２は、本発明のキャップ成形品の別な例
を示すものである。このキャップ成形品１１は、合成樹
脂キャップ１２と、この合成樹脂キャップ１２の内部に
設けられたライナー１３とからなっている。合成樹脂キ
ャップ１２は、ポリプロピレンなどの合成樹脂よりな
り、円板状の天面部１４と、その周縁から垂下した筒部
１５とからなっている。筒部１５の下部には複数の細い
ブリッジ１６を残して周方向に筒部を切断する水平スコ
ア１７が設けられている。筒部１５は、この水平スコア
１７によって上部の主部１８とその下方のタンパーエビ
デンスリング部１８とに区画されている。この主部１８
の内面には、容器１０の螺子８に螺合する螺子部２０が
設けられ、タンパーエビデンスリング部１８内面には、
複数の板状のタブ２１が突出形成されている。FIG. 2 shows another example of a cap molded product of the present invention. The cap molded product 11 includes a synthetic resin cap 12 and a liner 13 provided inside the synthetic resin cap 12. The synthetic resin cap 12 is made of a synthetic resin such as polypropylene, and includes a disk-shaped top surface portion 14 and a cylindrical portion 15 hanging down from the periphery. A horizontal score 17 is provided below the tubular portion 15 to cut the tubular portion in the circumferential direction while leaving a plurality of narrow bridges 16. The cylindrical portion 15 is partitioned by the horizontal score 17 into an upper main portion 18 and a tamper evidence ring portion 18 below the main portion 18. This main part 18
A screw portion 20 that is screwed to the screw 8 of the container 10 is provided on an inner surface of the container 10, and a tamper evidence ring portion 18 has an inner surface
A plurality of tabs 21 are formed to project.
【００１６】キャップ１２内に設けられたライナー１３
は、天面部１４の内面を覆う薄肉状に形成され、天面部
１４の内面に密着して設けられている。このライナー１
３は、合成樹脂主材１００重量部に対し、モレキュラー
シーブ吸着剤を０．０５〜２．０重量部混合してなる本
発明のキャップライナー材用組成物によって形成されて
いる。このキャップライナー材用組成物中の合成樹脂主
材は、ポリプロピレンを、キャップライナー材用組成物
に対し５〜２０重量部含有してなり、合成樹脂キャップ
１２の天板部１４内面に強固に密着するものである。こ
の合成樹脂キャップ１２の内部に上記キャップライナー
材用組成物からなるライナー１３を密着形成するための
ライナー形成法としては、例えば樹脂組成物を０．５〜
１ｍｍ程度の厚みのシート状に成形後、キャップの形状
に合った直径に打ち抜き、これをキャップ内に挿入、接
着する方法、あるいは、この組成物を加熱溶融した溶融
樹脂を、合成樹脂キャップ１２内に一定量落し入れ、合
成樹脂キャップ１２内に押し型を挿入して薄肉状のライ
ナー１３を成形する、インシェルモールド法が好適に用
いられる。Liner 13 provided in cap 12
Is formed in a thin shape covering the inner surface of the top surface portion 14, and is provided in close contact with the inner surface of the top surface portion 14. This liner 1
No. 3 is formed of the composition for a cap liner material of the present invention obtained by mixing 0.05 to 2.0 parts by weight of a molecular sieve adsorbent with 100 parts by weight of a synthetic resin main material. The synthetic resin main material in this composition for cap liner material contains 5 to 20 parts by weight of polypropylene based on the composition for cap liner material, and firmly adheres to the inner surface of the top plate portion 14 of the synthetic resin cap 12. Is what you do. As a liner forming method for tightly forming the liner 13 made of the composition for a cap liner material inside the synthetic resin cap 12, for example, a resin composition of 0.5 to
After forming into a sheet having a thickness of about 1 mm, the sheet is punched into a diameter suitable for the shape of the cap, and is inserted into the cap and bonded. Alternatively, a molten resin obtained by heating and melting this composition is placed in the synthetic resin cap 12. , And a thin mold liner 13 is formed by inserting a pressing mold into the synthetic resin cap 12 to preferably use an in-shell molding method.
【００１７】このキャップ成形品１１は、容器１０の口
部に被せ、閉方向に回転させることで、容器１０の口部
に螺着嵌合させる。容器１０に装着された状態では、タ
ンパーエビデンスリング部１９のそれぞれのタブ２１
は、容器１０の螺子８の直下に設けられた膨出段部９の
下面に係合する。容器１０の口部上端は、ライナー１３
に押圧された状態になり、容器１０内が密閉される。容
器１０の口部に装着されたこのキャップ成形品１１を、
開栓方向に回すと、タンパーエビデンスリング部１９の
内面に設けられた多数のタブ２１が、容器１０の膨出段
部９の下端に係止し、タンパーエビデンスリング部１９
の上方への移動を阻止する。これによって、筒部１５の
主部１８とタンパーエビデンスリング部１９の間をつな
ぐ多数の細いブリッジ１６に引張り力が作用し、それら
が切断され、タンパーエビデンスリング部１９が切り離
されることによって開栓が表示される。The molded cap 11 is placed over the mouth of the container 10 and rotated in the closing direction to be screwed and fitted to the mouth of the container 10. When mounted on the container 10, each tab 21 of the tamper evidence ring 19 is
Engages with the lower surface of the bulging step 9 provided immediately below the screw 8 of the container 10. The top end of the mouth of the container 10 is liner 13
, And the inside of the container 10 is sealed. This cap molded product 11 attached to the mouth of the container 10 is
When turned in the opening direction, a large number of tabs 21 provided on the inner surface of the tamper evidence ring portion 19 are engaged with the lower end of the bulging step 9 of the container 10, and the tamper evidence ring portion 19 is locked.
Prevents upward movement of As a result, a tensile force acts on a large number of narrow bridges 16 connecting between the main portion 18 of the cylindrical portion 15 and the tamper evidence ring portion 19, and they are cut, and the tamper evidence ring portion 19 is cut off to open the plug. Is displayed.
【００１８】このキャップ成形品１１は、ライナー１３
の材料に、合成樹脂主材１００重量部に対し、モレキュ
ラーシーブ吸着剤を０．０５〜２．０重量部混合してな
るキャップライナー材用組成物を用いたことによって、
ベースポリマーに配合するある種の添加成分が臭気を呈
する場合でも、その臭気をモレキュラーシーブ吸着剤が
完全に吸収し、その臭気が容器内の液体に移って風味を
損ねる不都合を防止することができる。また、材料組成
物に臭気を有する成分が含まれていても、その臭気をモ
レキュラーシーブ吸着剤が完全に吸収し、その臭気が容
器内の液体に移って風味を損ねる不都合を防止できるの
で、少量であれば、臭気のある添加成分をキャップライ
ナー材用組成物に添加することができるようになる。This cap molded product 11 has a liner 13
By using a composition for a cap liner material obtained by mixing 0.05 to 2.0 parts by weight of a molecular sieve adsorbent with respect to 100 parts by weight of a synthetic resin main material,
Even when a certain additive component added to the base polymer has an odor, the molecular sieve adsorbent completely absorbs the odor, and the odor can be prevented from being transferred to the liquid in the container, thereby preventing the disadvantage of impairing the flavor. . In addition, even if the material composition contains an odorous component, the molecular sieving adsorbent completely absorbs the odor, and the odor can be prevented from being transferred to the liquid in the container to prevent inconvenience of deteriorating the flavor. If so, an odorous additive component can be added to the composition for a cap liner material.
【００１９】[0019]
実施例１：金属キャップ用ライナーの作製 低密度ポリエチレンを主体とするベースレジンと、ポリ
グリセリン脂肪酸エステルを主成分とするスリップ剤及
びモレキュラーシーブ（UNION SHOWA K.K.製の商品名ア
ブセンツ（登録商標））を、表１に示す組成で配合した
樹脂組成物を、０．８ｍｍ厚のシート状に成形後、公称
２８ｍｍ径のアルミキャップに合った直径に打ち抜き、
キャップ内に挿入、接着し、サンプルキャップを作製し
た。次に精製水を８５℃にて、５００ｍｌのＰＥＴボト
ルに充填し、サンプルキャップを巻き締めて装着した。
このキャップ装着後のボトルを４０℃の恒温槽に１週間
保管し、次いで５℃の冷蔵庫に２４時間保管した後、内
容物を試飲し、スリップ剤のオイル臭やパラフィン臭が
するか否かで香味適性を確認した。オイル臭やパラフィ
ン臭のするものを×、オイル臭やパラフィン臭のしない
ものを○として判定した。その結果を表１に示す。Example 1 Production of Liner for Metal Cap A base resin mainly composed of low-density polyethylene, a slip agent mainly composed of polyglycerin fatty acid ester and molecular sieve (Absentz (registered trademark) manufactured by UNION SHOWA KK) were used. After molding the resin composition blended with the composition shown in Table 1 into a 0.8 mm thick sheet, it was punched out to a diameter matching a nominal 28 mm diameter aluminum cap,
The sample cap was inserted into and adhered to the cap to prepare a sample cap. Next, purified water was filled into a 500 ml PET bottle at 85 ° C., and the sample cap was fastened and mounted.
The bottle with the cap attached was stored in a constant temperature bath at 40 ° C. for one week, and then stored in a refrigerator at 5 ° C. for 24 hours. After tasting the contents, it was determined whether or not there was an oily smell or a paraffin smell of the slip agent. Flavor suitability was confirmed. Those having an oily odor or paraffin odor were evaluated as x, and those having no oily odor or paraffin odor were evaluated as ○. Table 1 shows the results.
【表１】 [Table 1]
【００２０】表１に示した通り、ライナー組成物にモレ
キュラーシーブを０．０５重量部加えることで、オイル
臭やパラフィン臭の発生を防止することができた。また
モレキュラーシーブの量を０．２５重量部とした場合、
ライナー材用組成物の成形特性が悪くなり、しかもコス
ト高となった。As shown in Table 1, by adding 0.05 parts by weight of molecular sieve to the liner composition, generation of oily odor and paraffinic odor could be prevented. When the amount of the molecular sieve is 0.25 parts by weight,
The molding properties of the composition for liner materials deteriorated, and the cost increased.
【００２１】実施例２：合成樹脂キャップ用ライナーの
作製 ポリプロピレンを含むオレフィン系樹脂とエラストマー
及び流動パラフィンを配合したベースレジンと、スリッ
プ剤（エルカ酸アミド）及びモレキュラーシーブ（UNIO
N SHOWA K.K.製の商品名アブセンツ（登録商標））を、
表２に示す組成で配合した樹脂組成物を加熱溶融し、溶
融した樹脂をポリプロピレン製の樹脂キャップ内に一定
量落し入れ、押し型にて、ライナー形状として、樹脂用
サンプルキャップを作製した。次に精製水を８５℃に
て、５００ｍｌのＰＥＴボトルに充填し、サンプルキャ
ップを巻き締めて装着した。このキャップ装着後のボト
ルを４０℃の恒温槽に１週間保管し、次いで５℃の冷蔵
庫に２４時間保管した後、内容物を試飲し、スリップ剤
のオイル臭やパラフィン臭がするか否かで香味適性を確
認した。オイル臭やパラフィン臭のするものを×、オイ
ル臭やパラフィン臭のしないものを○として判定した。
その結果を表２に示す。Example 2: Preparation of a liner for a synthetic resin cap A base resin containing an olefin resin containing polypropylene, an elastomer and liquid paraffin, a slip agent (erucamide) and a molecular sieve (UNIO)
N SHOWA KK brand name Absents (registered trademark))
A resin composition blended with the composition shown in Table 2 was heated and melted, a fixed amount of the melted resin was dropped into a resin cap made of polypropylene, and a liner shape was formed with a pressing die to prepare a sample cap for resin. Next, purified water was filled into a 500 ml PET bottle at 85 ° C., and the sample cap was fastened and mounted. The bottle with the cap attached was stored in a constant temperature bath at 40 ° C. for one week, and then stored in a refrigerator at 5 ° C. for 24 hours. After tasting the contents, it was determined whether or not there was an oily smell or a paraffin smell of the slip agent. Flavor suitability was confirmed. Those having an oily odor or paraffin odor were evaluated as x, and those having no oily odor or paraffin odor were evaluated as ○.
Table 2 shows the results.
【表２】 [Table 2]
【００２２】表２に示した通り、ライナー組成物にモレ
キュラーシーブを０．０５重量部加えることで、オイル
臭やパラフィン臭の発生を防止することができた。また
モレキュラーシーブの量を０．２５重量部とした場合、
ライナー材用組成物の成形特性が悪くなり、しかもコス
ト高となった。As shown in Table 2, by adding 0.05 parts by weight of molecular sieve to the liner composition, generation of oily odor and paraffinic odor could be prevented. When the amount of the molecular sieve is 0.25 parts by weight,
The molding properties of the composition for liner materials deteriorated, and the cost increased.
【００２３】[0023]
【発明の効果】以上説明した通り、本発明によれば、次
のような優れた効果を奏する。請求項１に係るキャップ
ライナー材用組成物は、合成樹脂主材１００重量部に対
し、モレキュラーシーブ吸着剤を０．０５〜２．０重量
部混合してなるものなので、ベースポリマーに配合する
ある種の添加成分が臭気を呈する場合でも、その臭気を
モレキュラーシーブ吸着剤が完全に吸収し、その臭気が
容器内の液体に移って風味を損ねる不都合を防止するこ
とができる。また、材料組成物に臭気を有する成分が含
まれていても、その臭気をモレキュラーシーブ吸着剤が
完全に吸収し、その臭気が容器内の液体に移って風味を
損ねる不都合を防止できるので、少量であれば、臭気の
ある添加成分をキャップライナー材用組成物に添加する
ことができるようになる。請求項２に係るキャップライ
ナー材用組成物は、前記合成樹脂主材が、低密度ポリエ
チレンを、キャップライナー材用組成物に対し１０〜９
５重量部含有したものなので、このキャップライナー材
用組成物を金属キャップに用いれば、金属キャップとの
密着性に優れ、かつ含有成分の臭気を外に漏らさない、
優れた金属キャップライナー材用組成物となる。請求項
３に係るキャップライナー材用組成物は、前記合成樹脂
主材が、ポリプロピレンを、キャップライナー材用組成
物に対し５〜２０重量部含有したものなので、このキャ
ップライナー材用組成物を合成樹脂キャップに用いれ
ば、合成樹脂キャップとの密着性に優れ、かつ含有成分
の臭気を外に漏らさない、優れた合成樹脂キャップライ
ナー材用組成物となる。請求項４に係る発明は、請求項
１記載のキャップライナー材用組成物からなるライナー
を備えたキャップ成形品であり、これは、ライナーに臭
気を有する成分が入っていても、その臭気がモレキュラ
ーシーブ吸着剤に吸収され、外に漏れ出す恐れがない。
従って、このキャップ成形品は、容器内の液体に移って
風味を損ねる不都合を防止することができる。請求項５
に係るキャップ成形品は、金属キャップと、請求項２記
載のキャップライナー材用組成物からなるライナーとか
らなるものであり、キャップとライナーとの密着性が良
好でかつ臭気漏れ出し防止効果を有する優れたものとな
る。請求項６に係るキャップ成形品は、合成樹脂キャッ
プと、請求項３記載のキャップライナー材用組成物から
なるライナーとからなるものであり、キャップとライナ
ーとの密着性が良好で、かつ臭気漏れ出し防止効果を有
する優れたものとなる。As described above, according to the present invention, the following excellent effects can be obtained. The composition for a cap liner material according to claim 1 is obtained by mixing 0.05 to 2.0 parts by weight of a molecular sieve adsorbent with respect to 100 parts by weight of a synthetic resin main material. Even when the kind of added component has an odor, the molecular sieving adsorbent can completely absorb the odor and prevent the disadvantage that the odor is transferred to the liquid in the container and impairs the flavor. In addition, even if the material composition contains an odorous component, the molecular sieving adsorbent completely absorbs the odor, and the odor can be prevented from being transferred to the liquid in the container to prevent inconvenience of deteriorating the flavor. If so, an odorous additive component can be added to the composition for a cap liner material. The composition for a cap liner material according to claim 2, wherein the synthetic resin main material is a low-density polyethylene, and the composition for a cap liner material is 10 to 9%.
Since the composition for a cap liner material is used in a metal cap, the composition has excellent adhesion to the metal cap and does not leak out the odor of the contained components.
An excellent composition for a metal cap liner material. In the composition for a cap liner material according to claim 3, since the synthetic resin main material contains 5 to 20 parts by weight of polypropylene based on the composition for a cap liner material, the composition for a cap liner material is synthesized. When used for a resin cap, an excellent composition for a synthetic resin cap liner material having excellent adhesion to the synthetic resin cap and not leaking the odor of the contained components to the outside is obtained. According to a fourth aspect of the present invention, there is provided a cap molded article provided with a liner comprising the composition for a cap liner material according to the first aspect, wherein even if a component having an odor is contained in the liner, the odor is molecular. It is absorbed by the sieve adsorbent and does not leak out.
Therefore, the molded cap product can prevent the inconvenience of transferring to the liquid in the container and impairing the flavor. Claim 5
The cap molded product according to the above is composed of a metal cap and a liner made of the composition for a cap liner material according to claim 2, has good adhesion between the cap and the liner, and has an effect of preventing odor leakage. It will be excellent. According to a sixth aspect of the present invention, there is provided a cap molded product comprising a synthetic resin cap and a liner comprising the composition for a cap liner material according to the third aspect, having good adhesion between the cap and the liner and odor leakage. It becomes an excellent thing which has an outflow prevention effect.
【図１】 本発明のキャップ成形品の一例を示す一部断
面視した正面図。FIG. 1 is a partially sectional front view showing an example of a cap molded product of the present invention.
【図２】 本発明のキャップ成形品の別な例を示す一部
断面視した正面図。FIG. 2 is a partially sectional front view showing another example of the cap molded product of the present invention.
１，１１……キャップ成形品、２……金属キャップ、
３，１３……ライナー、１２……合成樹脂キャップ。1, 11: Cap molded product, 2: Metal cap,
3, 13 ... liner, 12 ... synthetic resin cap.
Claims (6)
キュラーシーブ吸着剤を０．０５〜２．０重量部混合し
てなるキャップライナー材用組成物。1. A composition for a cap liner material obtained by mixing 0.05 to 2.0 parts by weight of a molecular sieve adsorbent with 100 parts by weight of a synthetic resin main material.
ンを、キャップライナー材用組成物に対し１０〜９５重
量部含有した、金属キャップに用いられるものであるこ
とを特徴とする請求項１記載のキャップライナー材用組
成物。2. The metal cap according to claim 1, wherein the main component of the synthetic resin contains low-density polyethylene in an amount of 10 to 95 parts by weight based on the composition for the cap liner material. A composition for a cap liner material.
を、キャップライナー材用組成物に対し５〜２０重量部
含有した、合成樹脂キャップに用いられるものであるこ
とを特徴とする請求項１記載のキャップライナー材用組
成物。3. The synthetic resin cap according to claim 1, wherein the synthetic resin main material contains polypropylene in an amount of 5 to 20 parts by weight based on the composition for the cap liner material. A composition for a cap liner material.
イナー材用組成物からなるライナーを備えたことを特徴
とするキャップ成形品。4. A molded cap product comprising a cap and a liner comprising the composition for a cap liner material according to claim 1.
プライナー材用組成物からなるライナーとからなるキャ
ップ成形品。5. A molded cap comprising a metal cap and a liner comprising the composition for a cap liner material according to claim 2.
ャップライナー材用組成物からなるライナーとからなる
キャップ成形品。6. A molded cap product comprising a synthetic resin cap and a liner comprising the composition for a cap liner material according to claim 3.