JPH082615B2 - Decorative sheet attached to an alkaline substrate - Google Patents
Decorative sheet attached to an alkaline substrateInfo
- Publication number
- JPH082615B2 JPH082615B2 JP61313741A JP31374186A JPH082615B2 JP H082615 B2 JPH082615 B2 JP H082615B2 JP 61313741 A JP61313741 A JP 61313741A JP 31374186 A JP31374186 A JP 31374186A JP H082615 B2 JPH082615 B2 JP H082615B2
- Authority
- JP
- Japan
- Prior art keywords
- decorative
- sheet
- paper
- adhesive layer
- decorative sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 （産業上の利用分野） 本発明は、コンクリート面、モルタル面等のアルカリ
性下地に貼着される化粧シートに関する。TECHNICAL FIELD The present invention relates to a decorative sheet attached to an alkaline underlayer such as a concrete surface or a mortar surface.
（従来の技術） 従来、壁紙の下地を施工する方法としては、コンクリ
ート、モルタル等の湿式工法と、石膏ボード等の乾式工
法とがある。また、石膏ボードの施工方法としては、GL
ボンドと呼ばれる石膏系の接着剤により直接コンクリー
ト面に張り付けるGL工法がある。この方法は、工期を短
縮できる、コストを低減できる等の点で優れているた
め、近年広く普及してきている。(Prior Art) Conventionally, as a method of constructing a base of a wallpaper, there are a wet construction method such as concrete and mortar, and a dry construction method such as gypsum board. Also, as a construction method of gypsum board, GL
There is a GL method in which a gypsum-based adhesive called a bond is applied directly to the concrete surface. This method has been widely used in recent years because it is excellent in that the construction period can be shortened and the cost can be reduced.
（発明が解決しようとする問題点） しかしながら、上記の湿式工法による下地に壁紙を貼
る場合、下地が充分乾燥されていないと、使用するうち
に壁紙にカビやシミ等が発生し、トラブルを招くことが
多い。特に、マンション等、壁面がコンクリート部材よ
りなる建造物の場合は貼り付け後暫く経てから該部材中
に含まれる水分が滲出してくるため、上記のようなトラ
ブルが生じやすい。また、近年増加しているGL工法の場
合には、GLボンドが完全に乾燥した状態で施工しない
と、ボンドから出る湿気が石膏ボードにより閉じ込めら
れ、その後これが壁紙にまで滲出し、カビが発生すると
いう問題が生じる。このため、従来より、施工用の接着
剤に防カビ剤をいれてカビの発生を防止する試みも実際
行なわれているが、充分な効果は得られていないのが現
状である。(Problems to be solved by the invention) However, when the wallpaper is applied to the base by the above-mentioned wet method, if the base is not dried sufficiently, mold or stains may occur on the wallpaper during use, causing troubles. Often. In particular, in the case of a building such as a condominium whose wall surface is made of a concrete member, the above-mentioned troubles are likely to occur because the moisture contained in the member leaks out a short time after the attachment. In addition, in the case of the GL method, which has been increasing in recent years, unless the GL bond is installed in a completely dry state, the moisture from the bond will be trapped by the gypsum board, and then this will exude to the wallpaper, causing mold. The problem arises. For this reason, conventionally, attempts have been made to prevent the generation of mold by adding a mildew proofing agent to the adhesive for construction, but the present situation is that sufficient effects have not been obtained.
また、シミは特に下地からのアルカリ性水分により生
じやすく、下地がモルタルなどのアルカリ性材料からな
る場合はこの影響が著しい。また、下地の釘に錆が発生
し、錆が化粧表面まで出て来て汚染してしまうこともあ
る。さらに、壁紙の貼り替えの際、下地表面に残った古
い壁紙の模様をなす着色剤等が長い間に接着剤に溶かし
出されて新しい壁紙の表面に滲み出てくる等の問題を生
じる。従って、本発明の目的は、コンクリート表面、モ
ルタル表面等、アルカリ性下地の面に直接貼着したと
き、湿気、アルカリ水分等の下地からの影響を受けにく
くかつ柔軟なシートであって下地表面の凹凸を抑えうる
ところの化粧シートを提供することにある。In addition, stains are likely to occur particularly due to alkaline water from the base, and this effect is remarkable when the base is made of an alkaline material such as mortar. In addition, rust may be generated on the base nail, and the rust may come out to the makeup surface and contaminate it. Furthermore, when the wallpaper is replaced, the coloring agent or the like that forms the pattern of the old wallpaper remaining on the base surface is dissolved into the adhesive for a long time and oozes onto the surface of the new wallpaper. Therefore, an object of the present invention is a flexible sheet that is not easily affected by the base such as moisture and alkaline moisture when directly attached to the surface of an alkaline base such as a concrete surface or a mortar surface, and has a rough surface of the base. It is to provide a decorative sheet that can suppress the above.
（問題点を解決するための手段） 本発明に従う化粧シートは、上記の目的を達成するべ
く改良された、アルカリ性下地に直接貼着される化粧シ
ートであって、その裏面側より、和紙、クラフト紙、薄
葉紙もしくは不織布よりなる繊維質シート；カルボキシ
ルポリエチレン系接着剤層；アルミニウム、鉄等の金属
箔；カルボキシルポリエチレン系接着剤層；和紙、クラ
フト紙、薄葉紙もしくは不織布よりなる繊維質シート；
接着剤層；プラスチックシート、紙、布等の化粧層が順
に積層されそして圧着されてなることを特徴とするもの
である。(Means for Solving Problems) A decorative sheet according to the present invention is a modified decorative sheet which is directly adhered to an alkaline substrate, and is used to achieve the above object. Fiber sheet made of paper, thin paper or non-woven fabric; carboxyl polyethylene adhesive layer; metal foil such as aluminum and iron; carboxyl polyethylene adhesive layer; Japanese paper, kraft paper, fibrous sheet made of thin paper or non-woven fabric;
An adhesive layer; a decorative layer such as a plastic sheet, paper, cloth, etc., which is laminated in order and pressure-bonded.
本発明において、繊維質シートは、和紙、クラフト
紙、薄葉紙もしくは不織布であり、金属箔の輝きがカル
ボキシルポリエチレン系接着剤層を通して紙または布の
化粧層に出ないように隠蔽するとともに、下地の凹凸を
緩衝して化粧シートが浮き上がったりするのを防ぐため
に積層される。繊維質シートの秤量は10〜150g/m2、好
ましくは20〜80g/m2である。In the present invention, the fibrous sheet is Japanese paper, kraft paper, thin paper or non-woven fabric, and hides the glitter of the metal foil so as not to appear in the decorative layer of paper or cloth through the carboxyl polyethylene-based adhesive layer, and the unevenness of the base. Are laminated to prevent the decorative sheet from being lifted up by cushioning the sheet. The basis weight of the fibrous sheet is 10 to 150 g / m 2 , preferably 20 to 80 g / m 2 .
アルミニウム、鉄等の金属箔は、下地からの湿気を防
ぐとともに、化粧シートに良好な寸法安定性を与えるた
めに用いられる。従って、かかる金属箔を積層すること
により化粧層を下地からの湿気から保護することがで
き、また、昼夜、真冬の寒暖の差によって生じる当該シ
ートの膨張、収縮の程度を小さくすることができる。金
属箔の厚さは７〜100μｍ、好ましくは10〜30μｍであ
る。A metal foil made of aluminum, iron or the like is used to prevent moisture from the base and to give the decorative sheet good dimensional stability. Therefore, by laminating such a metal foil, the decorative layer can be protected from moisture from the base, and the degree of expansion and contraction of the sheet caused by the difference in temperature between day and night and midwinter can be reduced. The thickness of the metal foil is 7 to 100 μm, preferably 10 to 30 μm.
カルボキシルポリエチレン系接着剤層は、繊維質シー
トと金属箔とを接着するために積層されるものである。
カルボキシルポリエチレン系接着剤層を設けることによ
り化粧シートに適度な柔軟性を持たせることができ、且
つアルカリ分、水分等が下地から化粧層へ浸透すること
を防止することができる。これは、例えば化粧シートを
貼着する壁剤がモルタルなどのアルカリ性材料からなる
場合には、特に有効である。ポリエチレンまたはポリプ
ロピレンの厚さはそれぞれ７〜100μｍ、好ましくは10
〜50μｍである。The carboxyl polyethylene-based adhesive layer is laminated to bond the fibrous sheet and the metal foil together.
By providing the carboxyl polyethylene-based adhesive layer, the decorative sheet can be made to have appropriate flexibility, and it is possible to prevent alkali content, moisture, etc. from penetrating into the decorative layer from the base. This is particularly effective, for example, when the wall material for attaching the decorative sheet is made of an alkaline material such as mortar. The thickness of polyethylene or polypropylene is 7 to 100 μm, preferably 10
~ 50 μm.
化粧層を繊維質シートと接着するための接着剤は熱可
塑性接着剤や水性エマルジョン系または溶剤系粘着剤が
望ましい。例えば、酢酸ビニル樹脂系やエチレン酢酸ビ
ニル樹脂（EVA）系接着剤またはアクリル系粘着剤など
を挙げることができる。化粧層として紙や布のように通
気性のある材料を用いた場合は、積層体に塗布した接着
剤が半乾燥の状態で該化粧層を圧着するが、プラスチッ
クフイルムのように通気性のない材料を用いた場合は、
圧着前に溶媒が完全に揮散している必要があるため、溶
媒が揮散しても比較的粘着性のある接着剤、例えばEVA
系接着剤、感圧型接着剤を使用する。The adhesive for adhering the decorative layer to the fibrous sheet is preferably a thermoplastic adhesive, an aqueous emulsion-based adhesive or a solvent-based adhesive. For example, a vinyl acetate resin-based or ethylene vinyl acetate resin (EVA) -based adhesive or an acrylic pressure-sensitive adhesive can be used. When a breathable material such as paper or cloth is used as the decorative layer, the adhesive applied to the laminate is pressure-bonded to the decorative layer in a semi-dried state, but it is not breathable like a plastic film. If materials are used,
Since the solvent must be completely evaporated before pressure bonding, an adhesive that is relatively sticky even if the solvent evaporates, such as EVA.
A system adhesive or a pressure sensitive adhesive is used.
本発明の化粧シートは、化粧層としての紙、布または
塩化ビニル樹脂フイルムの裏面に接着剤により繊維質シ
ートを接着したものの裏面に、カルボキシルポリエチレ
ン系接着剤層、金属箔、カルボキシルポリエチレン系接
着剤層、繊維質シートを順に重ね合わせて圧締するか、
または繊維質シート、カルボキシルポリエチレン系接着
剤層、金属箔、カルボキシルポリエチレン系接着剤層、
繊維質シートからなる積層体を溶融押出ラミネートし、
次いでこの溶融押出ラミネートした積層体の上に、化粧
層としての紙、布または塩化ビニル樹脂フィルムを接着
剤を介して重ね合わせて圧締することにより行なうこと
ができる。The decorative sheet of the present invention comprises a paper, cloth or vinyl chloride resin film as a decorative layer on the back side of which a fibrous sheet is adhered by an adhesive, on the back side thereof, a carboxyl polyethylene adhesive layer, a metal foil, a carboxyl polyethylene adhesive. Layers and fibrous sheets are stacked in order and compressed,
Or fibrous sheet, carboxyl polyethylene adhesive layer, metal foil, carboxyl polyethylene adhesive layer,
Melt extrusion laminate a laminate consisting of fibrous sheets,
Then, a paper, cloth or vinyl chloride resin film as a decorative layer is superposed on the laminate extruded by melt extrusion and laminated with an adhesive, and the laminate can be pressed.
（作用） 本発明の化粧シートは、繊維質シート、カルボキシル
ポリエチレン系接着剤層、金属箔、カルボキシルポリエ
チレン系接着剤層、繊維質シートからなる積層体の表面
に壁紙用化粧表面材料の印刷紙、布または塩化ビニル樹
脂フイルム等が圧着された構成を為している。このよう
な構成において、各層はそれぞれ次のような作用を示
す。金属箔は、化粧シートの寸法を安定に保つ。即ち、
昼夜、夏冬の寒暖の差や湿度変化による化粧シートの膨
張及び収縮を防ぎ、これに基づく壁紙の亀裂または剥離
を防止する。また、カルボキシエチレン層は、繊維質シ
ートと金属箔を接着するとともに、下値の湿気、特に下
地のアルカリ分が壁紙面へ透過するのを防止する。さら
に、本発明の化粧シートは適度の厚みを有するようにす
ると、化粧シートの化粧層表面には貼着表面の多少の凹
凸が影響せず、シート表面の平滑性が保たれる。(Function) The decorative sheet of the present invention is a printed sheet of a decorative surface material for wallpaper on the surface of a laminate comprising a fibrous sheet, a carboxyl polyethylene-based adhesive layer, a metal foil, a carboxyl polyethylene-based adhesive layer, and a fibrous sheet, It has a structure in which a cloth or a vinyl chloride resin film is pressure-bonded. In such a structure, each layer exhibits the following actions. The metal foil keeps the dimension of the decorative sheet stable. That is,
Prevents expansion and contraction of the decorative sheet due to differences in temperature and humidity in day and night, summer and winter, and prevents cracking or peeling of wallpaper based on this. In addition, the carboxyethylene layer adheres the fibrous sheet and the metal foil, and also prevents lower moisture, particularly alkali content of the base, from permeating to the wallpaper surface. Furthermore, when the decorative sheet of the present invention is made to have an appropriate thickness, the surface of the decorative layer of the decorative sheet is not affected by some unevenness of the sticking surface, and the smoothness of the sheet surface is maintained.
（実施例） 以下、本発明を実施例に基づいて説明するが、本発明
はこれに限定されるものではない。(Example) Hereinafter, the present invention will be described based on examples, but the present invention is not limited thereto.
実施例1: 第１図は、本発明の一実施例による化粧シート１を示
す図である。化粧シート１は、化粧層2;接着剤層3;繊維
質シート4;カルボキシルポリエチレン系接着剤層5;金属
箔6;カルボキシルポリエチレン系接着剤層7;繊維質シー
ト８が順に積層され圧着された構成を為す。Example 1: FIG. 1 is a diagram showing a decorative sheet 1 according to an example of the present invention. The decorative sheet 1 includes a decorative layer 2, an adhesive layer 3, a fibrous sheet 4, a carboxyl polyethylene-based adhesive layer 5, a metal foil 6, a carboxyl polyethylene-based adhesive layer 7, and a fibrous sheet 8 which are sequentially laminated and pressure-bonded. Make up the composition.
材料としてそれぞれ下記のものを用いた。 The following materials were used as materials.
化粧層2:表面に模様のプリントされた紙 接着剤3:酢酸ビニル系接着剤 繊維質シート4:薄葉紙（秤量:30g/m2） カルボキシルポリエチレン系接着剤層5:厚さ40μｍのカ
ルボキシルポリエチレン系接着剤 金属箔6:厚さ15μｍのアルミニウム箔 カルボキシルポリエチレン系接着剤層7:厚さ40μｍのカ
ルボキシルポリエチレン系接着剤 繊維質シート8:薄葉紙（秤量:30g/m2） 化粧シートの製造例を下記に示す。まず、繊維質シー
ト4/カルボキシルポリエチレン系接着剤層5/金属箔6/カ
ルボキシルポリエチレン系接着剤層7/繊維質シート８の
積層体を溶融押出ラミネートにより作る。次いで、この
積層体の上に接着剤３グラビアロールコーターで塗布
し、乾燥炉（60℃×１分）を通過させて半乾燥の状態に
し、化粧層２と80℃熱ロールで３本で圧着させ、化粧シ
ート１を製造した。Decorative layer 2: Paper with a pattern printed on the surface Adhesive 3: Vinyl acetate adhesive Fibrous sheet 4: Thin paper (weighing 30 g / m 2 ) Carboxylic polyethylene adhesive layer 5: Carboxylic polyethylene 40 μm thick Adhesive Metal foil 6: Aluminum foil with a thickness of 15 μm Carboxylic polyethylene adhesive layer 7: Carboxylic polyethylene adhesive with a thickness of 40 μm Fibrous sheet 8: Thin paper (weighing 30 g / m 2 ) Examples of manufacturing decorative sheets are as follows Shown in. First, a laminate of fibrous sheet 4 / carboxyl polyethylene-based adhesive layer 5 / metal foil 6 / carboxyl polyethylene-based adhesive layer 7 / fibrous sheet 8 is prepared by melt extrusion lamination. Then, apply 3 adhesive gravure roll coater on this laminate, pass through a drying oven (60 ° C x 1 min) to make it semi-dry, and press-bond it with the decorative layer 2 and 80 ° C hot roll with 3 rolls. Then, the decorative sheet 1 was manufactured.
実施例2: 化粧層２としてプラスチックフイルムを使用し、化粧
層２とラミネートを接着するための接着剤３としてEVA
系接着剤を使用し、その他は実施例１と同様の材料を用
いて、化粧シートを製造した。製造は、実施例１の方法
により製造された溶融押出ラミネートに接着剤３（EVA
系接着剤）をグラビアロールコーターで塗布し、乾燥炉
を通して完全に溶媒を飛ばし、その後、化粧層２（プラ
スチックフィルム）を圧着させることにより行われる。Example 2: A plastic film is used as the decorative layer 2, and EVA is used as the adhesive 3 for bonding the decorative layer 2 and the laminate.
A decorative sheet was manufactured using a system adhesive and using the same materials as in Example 1 except for the above. Manufacturing was carried out by using the adhesive 3 (EVA) on the melt extrusion laminate manufactured by the method of Example 1.
System adhesive) is applied by a gravure roll coater, the solvent is completely blown through a drying oven, and then the decorative layer 2 (plastic film) is pressure-bonded.
応用例： 第２図は、応用例の化粧板11を示す断面図である。該
化粧板11は、上記実施例１で得られた化粧シート１に、
接着剤９を介して合板10を重ね、110℃×7kg/cm2×120
秒の熱圧締条件で接着することにより製造される。同様
の方法により実施例２の化粧シートから化粧板を製造す
る。Application Example: FIG. 2 is a sectional view showing a decorative plate 11 of an application example. The decorative board 11 is the same as the decorative sheet 1 obtained in Example 1 above.
Plywood 10 is overlaid with adhesive 9 and 110 ℃ × 7kg / cm 2 × 120
It is manufactured by adhering under the condition of heat pressing for seconds. A decorative board is manufactured from the decorative sheet of Example 2 by the same method.
試験例： 実施例１および２で得られた化粧シートをそれぞれ水
分を過剰に含ませたコンクリート壁に接着し、一定期間
放置した後の化粧シートの湿り具合を調べた。本実施例
により得られた化粧シートの化粧層は、殆ど湿気を含ん
でいなかった。なお、従来方法により、上記とほぼ同量
の水分を含有するコンクリートに壁紙及び壁紙用クロス
を直に接着した場合、壁紙及び壁紙用クロスは多量の湿
気を含み、湿気により膨潤して凹凸を形成するまでにな
った。Test Example: Each of the decorative sheets obtained in Examples 1 and 2 was adhered to a concrete wall containing an excessive amount of water, and the wetness of the decorative sheet after standing for a certain period was examined. The decorative layer of the decorative sheet obtained in this example contained almost no moisture. By the conventional method, when wallpaper and wallpaper cloth are directly adhered to concrete containing almost the same amount of water as above, the wallpaper and wallpaper cloth contain a large amount of moisture and swell due to humidity to form irregularities. I'm done.
（発明の効果） 以上説明したように、本発明に従い提供される化粧シ
ートは、表面側より、化粧層（プラスチックシート、
紙、布等）；接着剤層；繊維質シート（和紙、クラフト
紙、薄葉紙もしくは不織布）；カルボキシルポリエチレ
ン系接着剤層；金属箔（アルミニウム、鉄）；カルボキ
シルポリエチレン系接着剤層；上記の繊維質シートとい
う積層構造を有するので、湿気、アルカリ水分等の下地
からの影響を受けにくく、コンクリート表面、モルタル
表面等、アルカリ性下地の表面に直接貼り付けた場合
も、カビ、シミ等を生じることがなく、下地の釘の錆等
が壁紙上に映ることもない。また、従来方法においてカ
ビ、シミ等を防ぐために必要とされていた乾燥、防カビ
剤塗布等の工程を省略することができるため、コスト、
労力、さらに施工時間を節減できる。(Effects of the Invention) As described above, the decorative sheet provided according to the present invention has a decorative layer (plastic sheet, plastic sheet,
Paper, cloth, etc.); adhesive layer; fibrous sheet (Japanese paper, kraft paper, thin paper or non-woven fabric); carboxyl polyethylene adhesive layer; metal foil (aluminum, iron); carboxyl polyethylene adhesive layer; Since it has a laminated structure called a sheet, it is not easily affected by moisture, alkali moisture, etc. from the base, and even when directly attached to the surface of an alkaline base such as concrete surface, mortar surface, etc., it does not cause mold or stains. , The rust of the nail of the base is not reflected on the wallpaper. Further, in the conventional method, it is possible to omit the steps of drying, coating of an antifungal agent, etc., which were required to prevent mold, stains, etc.
You can save labor and construction time.
要するに、本発明の化粧シートは、コンクリート表
面、モルタル表面等、アルカリ性下地用の化粧シートと
して大変適するものである。In short, the decorative sheet of the present invention is very suitable as a decorative sheet for an alkaline base such as a concrete surface or a mortar surface.
第１図は本発明の一実施例の化粧シートを示す断面図、
第２図は応用例の化粧板を示す断面図である。 １……化粧シート、２……化粧層 3,9……接着剤層、4,8……繊維質シート ６……金属箔 5,7……カルボキシルポリエチレン系接着剤層 10……合板、11……化粧板FIG. 1 is a sectional view showing a decorative sheet according to an embodiment of the present invention,
FIG. 2 is a sectional view showing a decorative board of an application example. 1 ... Decorative sheet, 2 ... Decorative layer 3,9 ... Adhesive layer, 4,8 ... Fibrous sheet 6 ... Metal foil 5,7 ... Carboxylic polyethylene adhesive layer 10 ... Plywood, 11 …… Veneer
Claims (1)
トであって、その裏面側より、和紙、クラフト紙、薄葉
紙もしくは不織布よりなる繊維質シート；カルボキシル
ポリエチレン系接着剤層；アルミニウム、鉄等の金属
箔；カルボキシルポリエチレン系接着剤層；和紙、クラ
フト紙、薄葉紙もしくは不織布よりなる繊維質シート；
接着剤層；プラスチックシート、紙、布等の化粧層が順
に積層されそして圧着されてなる化粧シート。1. A decorative sheet which is directly adhered to an alkaline substrate, and from the back side thereof, a fibrous sheet made of Japanese paper, kraft paper, thin paper or non-woven fabric; a carboxylpolyethylene adhesive layer; aluminum, iron, etc. Metal foil; Carboxyl polyethylene adhesive layer; Fibrous sheet made of Japanese paper, kraft paper, thin paper or non-woven fabric;
Adhesive layer: A decorative sheet in which decorative layers such as a plastic sheet, paper and cloth are sequentially laminated and pressed.