JPH0765011B2 - Organic precious metal ink - Google Patents
Organic precious metal inkInfo
- Publication number
- JPH0765011B2 JPH0765011B2 JP62154767A JP15476787A JPH0765011B2 JP H0765011 B2 JPH0765011 B2 JP H0765011B2 JP 62154767 A JP62154767 A JP 62154767A JP 15476787 A JP15476787 A JP 15476787A JP H0765011 B2 JPH0765011 B2 JP H0765011B2
- Authority
- JP
- Japan
- Prior art keywords
- terpene
- organic
- noble metal
- ink
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
【発明の詳細な説明】 （産業上の利用分野） 本発明は、セラミック製品やガラスの表面に装飾用、電
子工業用等に使用される有機貴金属インク、特に有機金
インクに関する。TECHNICAL FIELD The present invention relates to an organic noble metal ink, particularly an organic gold ink, which is used on a surface of a ceramic product or glass for decoration, electronic industry and the like.
（従来技術とその問題点） 陶器等のセラミック製品やガラス製品の表面にインクを
使用して文字や図形を描いてその装飾効果を倍増させる
ことが従来から広く行われている。該文字や図形を描く
際には単なるインクではなく、金や銀等の貴金属光沢を
有する有機貴金属インクを使用して所謂金文字等を形成
し、より高級な雰囲気を醸し出すことも行われている。(Prior art and its problems) It has been widely practiced in the past to double the decorative effect by drawing letters and figures using ink on the surface of ceramic products such as pottery and glass products. At the time of drawing the characters or figures, not only ink but also organic sonoble metal ink having noble metal luster such as gold or silver is used to form so-called gold characters and the like to create a higher-class atmosphere. .
これらの有機貴金属インクは、例えば樹脂酸の貴金属
塩、そのフラックス及びバインダとしてのエポキシ樹脂
等から成っている（米国特許第2,842,457号）。一般に
これらの有機貴金属インクのバインダとしては、低粘度
インク用としては、天然ロジン、アスファルト、ニトロ
セルロース、エポキシ樹脂等が、又高粘度インク用とし
ては、エチルセルロース、ポリスチレン、アクリル樹脂
等を使用されている。These organic noble metal inks are composed of, for example, a noble metal salt of resin acid, its flux, and an epoxy resin as a binder (US Pat. No. 2,842,457). Generally, as binders for these organic precious metal inks, natural rosin, asphalt, nitrocellulose, epoxy resin, etc. are used for low viscosity inks, and ethyl cellulose, polystyrene, acrylic resins, etc. are used for high viscosity inks. There is.
これらのバインダのうち低粘度用インクに使用される天
然ロジン、アスファルト、ニトロセルロース、エポキシ
樹脂及び高粘度用インクに使用されるポリスチレン等は
インクとして適当な粘度を与えるために大量に使用され
る（例えば約10〜20重量％）ので、ガス抜けに起因する
ピンホールが発生し易く、製品の表面状態が悪くなる。
又高粘度インク用として使用されるエチルセルロース、
アクリル樹脂等はインク中で分離し均一に分散しないた
め、滑らかな表面状態を得ることができない。Among these binders, natural rosin, asphalt, nitrocellulose, epoxy resin used for low-viscosity inks, polystyrene used for high-viscosity inks, and the like are used in large amounts to give appropriate viscosity as ink ( For example, about 10 to 20% by weight), pinholes due to outgassing are likely to occur and the surface condition of the product deteriorates.
In addition, ethyl cellulose used for high viscosity ink,
Since the acrylic resin and the like are separated in the ink and are not uniformly dispersed, a smooth surface state cannot be obtained.
（発明の目的） 本発明は、有機貴金属インクのバインダとして従来使用
されていたエポキシ樹脂等に換えて、より少量でバイン
ダとして機能することができるテルペン系樹脂を使用す
ることにより、バインダの使用量を減少させて陶器等の
表面に塗布等されたときに、ピンホールを生じさせるこ
となく良好な表面状態を与えることを可能とする有機貴
金属インクを提供することを目的とする。(Object of the Invention) The present invention uses a terpene-based resin that can function as a binder in a smaller amount, instead of an epoxy resin or the like that has been conventionally used as a binder for an organic noble metal ink. It is an object of the present invention to provide an organic noble metal ink capable of giving a good surface condition without causing pinholes when it is applied to the surface of a pottery or the like by reducing the amount.
（問題点を解決するための手段） 本発明は、少なくとも１種類の樹脂酸の貴金属塩とバイ
ンダとしてのテルペン系樹脂及び溶剤を含有することを
特徴とする有機貴金属インクである。(Means for Solving Problems) The present invention is an organic noble metal ink containing at least one noble metal salt of a resin acid, a terpene resin as a binder, and a solvent.
以下本発明をより詳細に説明する。The present invention will be described in more detail below.
樹脂酸の貴金属塩は従来から汎用されている、金、白
金、銀、パラジウム、ロジウム、イリジウム、ルテニウ
ム及びそれらの合金等を含み、これらの樹脂酸の貴金属
塩の１又は２種以上を使用する。The noble metal salt of resin acid includes gold, platinum, silver, palladium, rhodium, iridium, ruthenium and alloys thereof, which have been widely used, and one or more of these noble metal salts of resin acid are used. .
本発明のテルペン系樹脂とは、（C10H16）ｎの一般式で
表される炭化水素であるテルペンから誘導、特に重合に
より誘導される比較的高分子量の物質の総称である。該
テルペン系樹脂には、テルペン重合体、α−ピネン重合
体、β−ピネン重合体、ｄ−リモネン重合体、ジテルペ
ン樹脂、芳香族変性テルペン重合体、変性テルペン重合
体及びテルペンフェノール共重合体が含まれる。The terpene-based resin of the present invention is a general term for relatively high molecular weight substances derived from terpenes, which are hydrocarbons represented by the general formula of (C 10 H 16 ) n , and particularly derived by polymerization. The terpene-based resin includes a terpene polymer, an α-pinene polymer, a β-pinene polymer, a d-limonene polymer, a diterpene resin, an aromatic modified terpene polymer, a modified terpene polymer and a terpene phenol copolymer. included.
又本発明においては、上記樹脂酸の貴金属塩及び前記テ
ルペン系樹脂の他に必須成分として、これら成分の溶
剤、つまりこれらの成分を溶解又は懸濁させる溶媒、例
えばテルペンアルコールを含む。該溶剤は上記物質を溶
解又は懸濁しかつ該物質を含むインクが陶器等に塗布等
された場合に比較的短時間で乾くような揮発性物質であ
ることが好ましい。Further, in the present invention, in addition to the noble metal salt of the resin acid and the terpene-based resin, a solvent for these components, that is, a solvent for dissolving or suspending these components, for example, a terpene alcohol is included as an essential component. The solvent is preferably a volatile substance which dissolves or suspends the substance and dries in a relatively short time when the ink containing the substance is applied to a pottery or the like.
本発明における有機貴金属インクは、前記樹脂酸の貴金
属塩の少なくとも１種と前記テルペン系樹脂の必死成分
の他に、樹脂酸の卑金属塩やアルキド樹脂等を含むこと
ができる。The organic noble metal ink according to the present invention may contain, in addition to at least one kind of the noble metal salt of the resin acid and the desperate component of the terpene-based resin, a base metal salt of the resin acid or an alkyd resin.
本発明の有機貴金属インクでは、従来の粘度の低い天然
ロジン等の換わりに、少量で同程度のバインダとしての
機能を果たすことのできるテルペン系樹脂をバインダと
して使用しているため、バインダ使用量が従来の10〜20
重量％から１〜５重量％まで減少させることができ、同
程度の粘度を有する有機貴金属インクをより少量のバイ
ンダで調製することができる。In the organic noble metal ink of the present invention, in place of the conventional low-viscosity natural rosin, etc., a terpene-based resin that can perform the same function as a binder in a small amount is used as the binder, so the amount of binder used is Conventional 10 ~ 20
It can be reduced from 1% to 5% by weight, and an organic noble metal ink having a similar viscosity can be prepared with a smaller amount of binder.
従って本発明に係わる有機貴金属インクが塗布等された
製品の表面にバインダに起因するピンホールやバインダ
の不均一な分散に基金する凹凸が生じたりすることがな
く装飾用、電子工業用としての有機貴金属インクの性能
が向上する。Therefore, the surface of the product coated with the organic noble metal ink according to the present invention does not cause pinholes due to the binder or unevenness that contributes to the uneven distribution of the binder, and does not form an organic material for decoration or electronic industry. The performance of the precious metal ink is improved.
以下本発明に係わる有機貴金属インクの実施例を記載す
るが、該実施例は本発明を限定するものではない。Hereinafter, examples of the organic noble metal ink according to the present invention will be described, but the examples do not limit the present invention.
（実施例１） 下記の成分を混合して有機金インクとした。(Example 1) The following components were mixed to prepare an organic gold ink.
樹脂酸金 ……20 重量％ 樹脂酸ロジウム …… 0.05重量％ 樹脂酸ビスマス …… 0.3 重量％ 樹脂酸クロム …… 0.04重量％ 樹脂酸アンチモン …… 0.02重量％ 樹脂酸バナジウム …… 0.03重量％ アルキド樹脂 …… 6.0 重量％ 尿素メラミン樹脂 …… 3.0 重量％ α−ピネン重合体 …… 8.0 重量％ テルペンアルコール ……残部。Resin acid gold: 20% by weight Rhodium resinate: 0.05% by weight Bismuth resinate: 0.3% by weight Chromium resinate: 0.04% by weight Antimony resinate: 0.02% by weight Vanadium resinate: 0.03% by weight Alkyd resin …… 6.0 wt% urea melamine resin …… 3.0 wt% α-pinene polymer …… 8.0 wt% terpene alcohol …… balance.
適度な粘性を有する該インクを陶器やガラス表面へ刷
毛、スクリーン印刷を用いて塗布し、500〜900℃で10分
〜30分加熱して焼成させた。The ink having an appropriate viscosity was applied to the surface of a ceramic or glass by using a brush or screen printing, and heated at 500 to 900 ° C. for 10 to 30 minutes to be baked.
一方α−ピネン重合体8.0重量％を天然ロジン20重量％
で置換した以外は上記した組成と同一組成を有する有機
金インクを同様の条件で陶器上に塗布し焼成させた。Meanwhile, 8.0% by weight of α-pinene polymer is added to 20% by weight of natural rosin.
The organic gold ink having the same composition as described above except that it was replaced with was applied onto a pottery under the same conditions and baked.
α−ピネン重合体を含む本実施例インクは、陶器、ガラ
ス表面のうち塗布された部分全体に均一に付着し滑らか
な表面を形成したが、天然ロジンを使用したインクでは
塗布前にはインクとして適度の粘性を有するが、塗布し
硬化した後は塗布面に天然ロジンに起因すると思われる
微細な孔が生じ表面が損なわれていた。The ink of this example containing the α-pinene polymer formed a smooth surface by uniformly adhering to the entire surface of the pottery and the coated portion of the glass surface. Although it has an appropriate viscosity, after the coating and curing, fine pores, which are considered to be caused by natural rosin, appeared on the coated surface and the surface was damaged.
（実施例２） 下記の成分を混合して有機白金インクとした。(Example 2) The following components were mixed to prepare an organic platinum ink.
樹脂酸白金 ……15 重量％ 樹脂酸ロジウム …… 0.05重量％ 樹脂酸ビスマス …… 0.5 重量％ 樹脂酸クロム …… 0.06重量％ 樹脂酸アンチモン …… 0.03重量％ 樹脂酸バナジウム …… 0.05重量％ アルキド樹脂 …… 6.5 重量％ 尿素メラミン樹脂 …… 3.0 重量％ テルペンフェノール共重合体 …… 5.0 重量％ テルペンアルコール ……残部。Platinum resinate: 15% by weight Rhodium resinate: 0.05% by weight Bismuth resinate: 0.5% by weight Chromium resinate: 0.06% by weight Antimony resinate: 0.03% by weight Vanadium resinate: 0.05% by weight Alkyd resin …… 6.5 wt% urea melamine resin …… 3.0 wt% terpene phenol copolymer …… 5.0 wt% terpene alcohol …… balance.
適度な粘性を有する該インクを陶器、ガラス表面へ刷
毛、スクリーン印刷を用いて塗布し、500〜900℃で10分
〜30分加熱して焼成させた。The ink having an appropriate viscosity was applied to a surface of a ceramic or glass by using a brush or screen printing, and heated at 500 to 900 ° C. for 10 to 30 minutes to be baked.
一方テルペンフェノール共重合体5.0重量％をエチルセ
ルロース10重量％で置換した以外は上記した組成と同一
組成を有する有機白金インクを同様の条件で陶器、ガラ
ス上に塗布し焼成させた。On the other hand, an organoplatinum ink having the same composition as described above except that 5.0% by weight of the terpene-phenol copolymer was replaced with 10% by weight of ethyl cellulose was coated and fired on pottery and glass under the same conditions.
テルペンフェノール共重合体を含む本実施例インクは、
陶器、ガラス表面のうち塗布された部分全体に均一に付
着し滑らかな表面を形成した。The ink of this example containing a terpene phenol copolymer was
A smooth surface was formed by uniformly adhering to the entire applied portion of the surface of the pottery and glass.
（発明の効果） 本発明は、有機貴金属インクのバインダとして従来のバ
インダより少量で同等のバインダとしての機能を果たす
テルペン系樹脂を使用しているため、有機貴金属インク
へ混合するバインダの量を大きく減少させることが可能
になる。従って該バインダを大量に使用するとインク焼
成後にインク塗布面に生じ易いバインダに起因する凝集
物あるいはガス抜けによるピンホール等の発生を防止す
ることができ、凹凸のない滑らかな塗布面を与えること
ができるため、本発明に係わる有機貴金属インクの装飾
用、電子工業用としての価値は非常に大きいものがあ
る。(Effect of the invention) Since the present invention uses a terpene-based resin that functions as a binder equivalent to a conventional binder in a small amount as a binder of an organic precious metal ink, the amount of the binder to be mixed with the organic precious metal ink is increased. It becomes possible to decrease. Therefore, when a large amount of the binder is used, it is possible to prevent the generation of agglomerates or pinholes due to gas escape due to the binder, which easily occurs on the ink application surface after the ink is baked, and to provide a smooth application surface without unevenness. Therefore, the value of the organic precious metal ink according to the present invention for decoration and electronic industry is very large.
Claims (3)
インダとしてのテルペン系樹脂及び溶剤を含有すること
を特徴とする有機貴金属インク。1. An organic noble metal ink containing at least one noble metal salt of a resin acid, a terpene resin as a binder, and a solvent.
ジウム、ロジウム、イリジウム、ルテニウム及びそれら
の合金から成る群から選択される１又は２以上の貴金属
である特許請求の範囲第１項に記載の有機貴金属イン
ク。2. The noble metal of the noble metal salt is one or more noble metals selected from the group consisting of gold, platinum, silver, palladium, rhodium, iridium, ruthenium and alloys thereof. The organic precious metal ink described in.
ピネン重合体、β−ピネン重合体、ｄ−リモネン重合
体、ジテルペン樹脂、芳香族変性テルペン重合体、変性
テルペン重合体及びテルペンフェノール共重合体成る群
から選択される特許請求の範囲第１項又は第２項に記載
の有機貴金属インク。3. A terpene-based resin is a terpene polymer, α-
Claim 1 selected from the group consisting of a pinene polymer, a β-pinene polymer, a d-limonene polymer, a diterpene resin, an aromatic modified terpene polymer, a modified terpene polymer and a terpene phenol copolymer. The organic precious metal ink according to item 2.