JPH05256037A - Repairing work for plate-bottomed pool - Google Patents
Repairing work for plate-bottomed poolInfo
- Publication number
- JPH05256037A JPH05256037A JP5265792A JP5265792A JPH05256037A JP H05256037 A JPH05256037 A JP H05256037A JP 5265792 A JP5265792 A JP 5265792A JP 5265792 A JP5265792 A JP 5265792A JP H05256037 A JPH05256037 A JP H05256037A
- Authority
- JP
- Japan
- Prior art keywords
- plate
- synthetic resin
- pool
- layer
- resin layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、アルミニュウム板、ス
テンレス鋼板、鉄板、ＦＲＰ複合板などの板材よりなる
プール本体を砂ベース上に設置した板底プールの補修方
法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for repairing a plate bottom pool in which a pool body made of a plate material such as an aluminum plate, a stainless steel plate, an iron plate, and an FRP composite plate is installed on a sand base.
【０００２】[0002]
【従来の技術】最近のプールはアルミニュウム板、ステ
ンレス鋼板、鉄板、ＦＲＰ複合板などの板材よりなるプ
ール本体を砂ベース上に設置した板底プールが主流をな
しているが、この種板底プールの欠点は、底部が肉薄で
あるため使用中に底部に波打ち状の凹凸が生じ、砂ベー
スとの間に空間ができて永年使用していると使用感が損
なわれることである。2. Description of the Related Art A recent pool is mainly a plate bottom pool in which a pool body made of plate material such as aluminum plate, stainless steel plate, iron plate and FRP composite plate is installed on a sand base. The disadvantage of (1) is that since the bottom portion is thin, wavy unevenness is generated on the bottom during use, a space is created between the bottom portion and the sand base, and the usability is impaired when used for many years.
【０００３】このように板底プールの底部に凹凸が生じ
た場合には、現在では補修することが困難とされている
ためプール本体を外して新規なものと交換する外なく、
交換には１ケ月近く使用を止めなければならないうえ
に、その経費はプールを新築する場合と変わらない程度
の莫大なものとなり極めて不経済である。[0003] When the bottom of the plate bottom pool thus has irregularities, it is difficult to repair it at present, so it is necessary to remove the pool body and replace it with a new one.
To replace it, you have to stop using it for about a month, and the cost is as huge as building a new pool, which is extremely uneconomical.
【０００４】[0004]
【発明が解決しようとする課題】本発明は上記のような
従来の問題点を解決して、板底プールの底部に凹凸変形
が生じた場合、これを極めて短期間で安価に補修できる
板底プールの補修方法を提供することを目的として完成
されたものである。DISCLOSURE OF THE INVENTION The present invention solves the above-mentioned conventional problems, and when uneven deformation occurs at the bottom of the plate bottom pool, the plate bottom can be repaired at extremely low cost in a very short period of time. It was completed for the purpose of providing a method for repairing the pool.
【０００５】[0005]
【課題を解決するための手段】上記の課題を解決するた
めになされた本発明に係る板底プールの補修方法は、板
材よりなるプール本体を砂ベース上に設置した板底プー
ルの凹凸変形した底板部表面を粗面化したうえ該プール
本体の素材と接着合成樹脂層の両者に対する接着性に優
れた合成樹脂プライマー層を介して接着合成樹脂層を層
着し、該接着合成樹脂層はその表面をこれに散着された
無数の硬質細粒よりなる凹凸粗面としてその上面に耐水
処理を施した肉厚のコンクリート表層を層着形成するこ
とを特徴とするものである。A method for repairing a plate bottom pool according to the present invention, which was made to solve the above-mentioned problems, is an uneven deformation of a plate bottom pool in which a pool body made of plate material is installed on a sand base. The surface of the bottom plate is roughened, and the adhesive synthetic resin layer is layered through the synthetic resin primer layer having excellent adhesiveness to both the material of the pool body and the adhesive synthetic resin layer. It is characterized in that the surface is formed as an uneven rough surface composed of innumerable hard fine particles scattered on the surface, and a thick concrete surface layer subjected to a water resistance treatment is layered on the upper surface.
【０００６】本発明において、先ず、板材よりなるプー
ル本体を砂ベース上に設置した板底プールの凹凸変形し
た底板部表面を粗面化するのであるが、これは永年使用
して不純物が付着している板底プールの底板部表面は単
に酸洗いなどの洗浄を行っても底板部表面に対する合成
樹脂プライマーの接着が不充分で剥離するおそれがあ
り、合成樹脂プライマー層との接着性を高めるためには
両者の接着面積を高めるとともに底板部表面に付着して
いる不純物を除去しておく必要があるからであって、そ
のためには底板部表面を粗面状に加工しておくことが最
も効率的であるからであって、この工程は一般的にはサ
ンダー掛けしたりボリッシャ掛けしたり、板材の素材に
適したショット材によるショットブラスト加工などで行
うものとする。In the present invention, first, the surface of the bottom plate portion of the plate bottom pool, in which the pool body made of the plate material is installed on the sand base, is roughened, but this is used for many years and impurities adhere to it. The surface of the bottom plate part of the plate bottom pool is insufficiently adhered to the surface of the bottom plate part even if the surface of the bottom plate part is simply washed with acid, which may cause peeling. This is because it is necessary to increase the bonding area between the two and to remove impurities adhering to the bottom plate surface.For that purpose, it is most efficient to process the bottom plate surface into a rough surface. This process is generally performed by sanding, bolishing, or shot blasting with a shot material suitable for the plate material.
【０００７】次に、この表面が粗面とされたプール本体
の底板部表面に合成樹脂プライマー層を層着するのであ
るが、この合成樹脂プライマー層はポリエステル樹脂や
エポキシ樹脂などの強靱な接着合成樹脂層をプール本体
の底板部に直接層着しても充分な接着強度が得られない
ことが多いから両者の一体化を強力なものとするためで
あって、このためプール本体および補強合成樹脂層の両
者に対する接着性に優れた合成樹脂プライマー層をプー
ル本体と接着合成樹脂層間に介在させておくのである。
なお、この合成樹脂プライマー層としてはポリウレタン
系樹脂が一般に使用され、その使用量は接着合成樹脂層
に比べて遙かに薄くてよく、１m2当り０、１kg前後を使
用すれば充分である。Next, a synthetic resin primer layer is layered on the surface of the bottom plate portion of the pool main body whose surface is roughened. The synthetic resin primer layer is a tough adhesive composition of polyester resin or epoxy resin. This is because even if the resin layer is directly layered on the bottom plate of the pool body, sufficient adhesion strength is often not obtained, so that the integration of the two is made strong. A synthetic resin primer layer having excellent adhesion to both layers is interposed between the pool body and the adhesive synthetic resin layer.
A polyurethane resin is generally used as the synthetic resin primer layer, and the amount thereof may be much thinner than that of the adhesive synthetic resin layer, and it is sufficient to use about 0,1 kg per 1 m 2 .
【０００８】次に、この合成樹脂プライマー層の上面
に、強靱な接着合成樹脂層をその表面が該接着合成樹脂
層に基部が強固に接着された硬質細粒により凹凸粗面と
なるように層着するのであるが、このようにして得られ
た表面は接着合成樹脂層の層着後硬化前に接着合成樹脂
層の表面に硬質細粒を散着して基部を埋め込み硬化させ
ることにより硬質細粒による凹凸粗面となっているの
で、後記する肉厚のコンクリート表層との一体化が極め
て良好なものとなる。なお、合成樹脂プライマー層の上
面に層着される接着合成樹脂層としては耐水性およびコ
ンクリート表層への接着性に優れたポリエステル樹脂や
エポキシ樹脂が使用され、その使用量は１m2当り０、３
kg前後とする。Next, a tough adhesive synthetic resin layer is formed on the upper surface of the synthetic resin primer layer so that the surface of the synthetic resin primer layer becomes an uneven rough surface by hard fine particles whose base is firmly adhered to the adhesive synthetic resin layer. The surface thus obtained is hard by applying hard fine particles to the surface of the adhesive synthetic resin layer after the adhesion of the adhesive synthetic resin layer and before curing to embed and harden the base portion. Since the surface is uneven due to the grains, the integration with the thick concrete surface layer, which will be described later, becomes extremely good. Incidentally, the synthesis as the adhesive synthetic resin layer is particle course on the upper surface of the resin primer layer polyester resin or epoxy resin with excellent adhesion to water resistance and concrete surface is used, the amount used 1 m 2 per 0,3
It should be around kg.
【０００９】また、接着合成樹脂層の表面を凹凸粗面と
するための硬質細粒としては、それ自身表面に露呈され
るものではないので珪砂などの安価なものでよい。この
ようにして表面が凹凸粗面とする接着合成樹脂層が底板
部の表面に合成樹脂プライマー層を介して強固に一体化
されたならば、次に、耐水処理を施した肉厚のコンクリ
ート表層を層着形成して完成させる。なお、このコンク
リート表層には必要に応じて仕上加工を施すこととなる
が、この仕上加工としては耐水性のオーバーコーテョン
グ樹脂層などを層着したり青色顔料が添加された耐水塗
料による表面塗装をするなどの表面仕上げでもよいが、
特に、現場においてＦＲＰよりなる内張りを施せば波打
ち現象はコンクリート表層により完全に解消されている
ので仕上がりがよく、極めて体裁がよいうえに強度的に
も優れたものとなる。Further, the hard fine particles for making the surface of the adhesive synthetic resin layer rough and rough are not exposed to the surface themselves, and therefore inexpensive ones such as silica sand may be used. In this way, if the adhesive synthetic resin layer having a rough surface is firmly integrated with the surface of the bottom plate through the synthetic resin primer layer, then a water-resistant thick concrete surface layer is applied. Is layered and completed. The concrete surface layer will be subjected to a finishing process as required.For this finishing process, a water-resistant overcoating resin layer or the like is layered or a surface made of a water-resistant paint to which a blue pigment is added. Surface finish such as painting may be used,
In particular, if a lining made of FRP is applied on site, the corrugation phenomenon is completely eliminated by the concrete surface layer, so that the finish is good, the appearance is very good, and the strength is excellent.
【００１０】[0010]
【実施例】床上に砂ベース１を形成したうえアルミニウ
ム板よりなるプール本体２を設置してその周囲をコンク
リートで覆ったプールにおいて、永年使用により波打ち
状に凹凸変形したプール本体２の底板部３の表面を先ず
高圧水により洗浄したうえ、ディスクサンダーにより底
板部３の表面を微細な粗面４に形成した。なお、波打ち
状の凹凸変形があまりにひどいものにあっては底板部３
に形成された凹凸変形のうち目立った凸部にカッターに
よる切込みを入れておく。次に、この粗面４にポリウレ
タン系樹脂プライマーを１m2当り０、１kgローラコーテ
ィング法により層着し、次に、プール本体２の底板部３
および後記する接着合成樹脂層６の両者に対する接着性
に優れた合成樹脂プライマー層５を肉薄に層着形成した
うえ、この合成樹脂プライマー層５の上面に耐摩耗性に
優れたポリエステル樹脂を１m2当り０、３kgローラコー
ティング法により層着してその表面に珪砂を吹き付け散
布し、基部がポリエステル樹脂の層に埋め込まれた状態
として硬化させて合成樹脂プライマー層５の上面に表面
が硬質細粒７としての珪砂により凹凸粗面を呈した強靱
な接着合成樹脂層６を層着形成した。そして、その上に
土間用メッシュを鉄筋代わりとして耐水剤と豆砂利を混
入した肉厚３０mmの無収縮のコンクリート層８を流し込
んだうえ上方によりコテ仕上げして層着し、乾燥硬化し
たのち最後に仕上げ加工を施した。仕上加工としてはコ
ンクリート層８の表面に青色顔料を添加したオーバーコ
ーティング樹脂層を層着形成して仕上げするか、ＦＲＰ
よりなる内張りを施してコンクリート層８の表面に保護
層９を形成した。[Example] In a pool in which a sand base 1 is formed on a floor, a pool body 2 made of an aluminum plate is installed, and the periphery thereof is covered with concrete, a bottom plate portion 3 of the pool body 2 which has been unevenly deformed into a wavy shape due to long-term use The surface of No. 1 was first washed with high pressure water, and then the surface of the bottom plate 3 was formed into a fine rough surface 4 by a disc sander. If the corrugated deformation is too severe, the bottom plate 3
A notch with a cutter is made on a conspicuous convex portion among the concavo-convex deformation formed on the. Next, a polyurethane resin primer is layered on the rough surface 4 by a roller coating method of 0 and 1 kg per 1 m 2 , and then the bottom plate portion 3 of the pool body 2 is laminated.
In addition, a synthetic resin primer layer 5 having excellent adhesiveness to both of the adhesive synthetic resin layer 6 described later is thinly layered, and 1 m 2 of a polyester resin having excellent abrasion resistance is formed on the upper surface of the synthetic resin primer layer 5. 0-3 kg per layer is applied by roller coating method, and silica sand is sprayed and sprinkled on the surface, and the base is embedded in a layer of polyester resin and cured to harden the synthetic resin primer layer 5 on the upper surface. A tough adhesive synthetic resin layer 6 having a roughened and roughened surface was layered by silica sand as a layer. Then, a 30 mm thick non-shrinkable concrete layer 8 containing a waterproofing agent and gravel mixed with a mesh for dirt as a reinforcing bar is poured on top of it, and a trowel finish is applied to the upper part for layering, followed by drying and hardening, and finally. Finished. As a finishing process, an overcoating resin layer containing a blue pigment is layered on the surface of the concrete layer 8 to finish, or FRP is used.
Then, a protective layer 9 was formed on the surface of the concrete layer 8 by applying the lining.
【００１１】このようにして得られたプール本体２の底
部は、底板部３の表面が肉厚のコンクリート層８で覆わ
れているので肉厚のコンクリート層８の重量でプール本
体２の底板部３は砂ベース１に密接し、底板部３の波打
ち状の凹凸変形が完全に解消され極めて体裁のよい仕上
がりが得られ、また、表面のコンクリート層８は直接プ
ール本体２の底板部３に接着したのではなく、底板部３
の表面を粗面４に加工したうえ合成樹脂プライマー層５
を介して表面が硬質細粒７による凹凸粗面とした接着合
成樹脂層６を形成し、この硬質細粒７による凹凸粗面と
した接着合成樹脂層６に対してコンクリート層８を層着
してあるので接着強度が大で剥離や亀裂が起こることが
なく長期耐用でき、さらに、補修日数も１０日程度でよ
いうえに極めて安価で補修が可能なため経済的なものと
なる。The bottom of the pool body 2 thus obtained is covered with the thick concrete layer 8 on the surface of the bottom plate 3, so that the weight of the thick concrete layer 8 contributes to the bottom plate of the pool body 2. 3 is closely attached to the sand base 1 and the wavy uneven deformation of the bottom plate 3 is completely eliminated to give a very nice finish, and the concrete layer 8 on the surface is directly adhered to the bottom plate 3 of the pool body 2. Not the bottom plate 3
The surface of resin is processed into rough surface 4 and synthetic resin primer layer 5
To form an adhesive synthetic resin layer 6 having a rough surface made of hard fine particles 7, and a concrete layer 8 is layered on the adhesive synthetic resin layer 6 having a rough surface made of hard fine particles 7. Since it has a high adhesive strength, it does not cause peeling or cracks and can be used for a long period of time. Furthermore, the number of repair days is about 10 days and it is economical because it can be repaired at an extremely low cost.
【００１２】[0012]
【発明の効果】本発明は以上の説明からも明らかなよう
に、板底プールの底板部が永年使用により凹凸変形した
場合に、短期間のうちに簡単に補修できるうえに極めて
体裁のよい仕上がりが得られる利点がある。従って、本
発明は永年使用により底板部が凹凸変形する板底プール
の問題点を解決できる板底プールの補修工法として業界
の発展に寄与するところ極めて大きいものがある。As is apparent from the above description, the present invention can be easily repaired within a short period of time when the bottom plate portion of the plate bottom pool is unevenly deformed due to long-term use, and has an extremely well-formed finish. There is an advantage that can be obtained. Therefore, the present invention contributes greatly to the development of the industry as a repairing method for a plate bottom pool that can solve the problem of a plate bottom pool in which the bottom plate portion is unevenly deformed after many years of use.
【図１】本発明により補修された底板プールの底部の断
面図である。FIG. 1 is a cross-sectional view of the bottom of a bottom plate pool repaired according to the present invention.
１ 砂ベース ２ プール本体 ３ 底板部 ４ 粗面 ５ 合成樹脂プライマー層 ６ 接着合成樹脂層 ７ 硬質細粒 ８ コンクリート層 1 Sand Base 2 Pool Main Body 3 Bottom Plate 4 Rough Surface 5 Synthetic Resin Primer Layer 6 Adhesive Synthetic Resin Layer 7 Hard Fine Grain 8 Concrete Layer
Claims (2)
設置した板底プールの凹凸変形した底板部表面を粗面化
したうえ該プール本体の素材と接着合成樹脂層の両者に
対する接着性に優れた合成樹脂プライマー層を介して接
着合成樹脂層を層着し、該接着合成樹脂層はその表面を
これに散着された無数の硬質細粒よりなる凹凸粗面とし
てその上面に耐水処理を施した肉厚のコンクリート表層
を層着形成することを特徴とする板底プールの補修工
法。1. The surface of the bottom plate portion of the plate bottom pool, in which the pool body made of plate material is installed on a sand base, is roughened, and the pool body material and the adhesive synthetic resin layer both have excellent adhesiveness. An adhesive synthetic resin layer is layered through a synthetic resin primer layer, and the surface of the adhesive synthetic resin layer is treated as a rough surface made up of innumerable hard fine particles and water-resistant on its upper surface. A method for repairing a plate bottom pool, which is characterized by forming a layered concrete surface layer with a certain thickness.
内張りするようにした請求項１に記載の板底プールの補
修工法。2. The method for repairing a plate bottom pool according to claim 1, wherein the concrete surface layer is further lined with FRP.