JP4491261B2 - Electrophotographic photosensitive member, image forming method using the same, image forming apparatus, and process cartridge for image forming apparatus - Google Patents

Description

  The present invention provides an electronic device having high durability and high image quality over a long period of time by using a photosensitive layer having high wear resistance, smooth surface properties, and good electrical characteristics. The present invention relates to a photographic photoreceptor. The present invention also relates to an image forming method, an image forming apparatus, and a process cartridge for the image forming apparatus using the long-life, high-performance photoconductor.

In recent years, organic photoreceptors (OPC) have been widely used in copying machines, facsimile machines, laser printers, and composite machines in place of inorganic photoreceptors because of their good performance and various advantages. This is because, for example, (1) optical characteristics such as the light absorption wavelength range and the amount of absorption, (2) electrical characteristics such as high sensitivity and stable charging characteristics, and (3) material selection range (4) Ease of manufacturing, (5) Low cost, (6) Non-toxicity, and the like.
On the other hand, the diameter of the photoconductor has recently been reduced due to the downsizing of the image forming apparatus, and the high speed of the machine and the maintenance-free movement have been added to increase the durability of the photoconductor. From this point of view, organophotoreceptors are generally soft because the surface layer is mainly composed of a low molecular charge transport material and an inert polymer, and when used repeatedly in an electrophotographic process, the organic photoreceptor is a machine using a development system or a cleaning system. There is a drawback that wear is likely to occur due to a typical load. In addition, due to the demand for higher image quality, the cleaning blade has to be increased in rubber hardness and contact pressure for the purpose of improving the cleaning properties as the toner particle size is reduced. This also promotes the wear of the photoreceptor. It is a factor. Such wear of the photoreceptor deteriorates electrical characteristics such as sensitivity deterioration and chargeability, and causes abnormal images such as image density reduction and background stains. Further, scratches where wear is locally generated cause streak-like stain images due to poor cleaning. Under the present circumstances, the wear and scratches are rate-determined and the life of the photoreceptor has been replaced.

Therefore, it is indispensable to reduce the above-mentioned wear amount in order to increase the durability of the organic photoreceptor, and this is the most pressing issue in this field.
Techniques for improving the abrasion resistance of the photosensitive layer include (1) using a curable binder for the surface layer (see, for example, Patent Document 1), and (2) using a polymeric charge transport material ( For example, refer patent document 2), (3) what dispersed the inorganic filler in the surface layer (for example, refer patent document 3), etc. are mentioned. Among these techniques, those using the curable binder (1) have poor compatibility with the charge transport material, and the residual potential increases due to impurities such as polymerization initiators and unreacted residues, resulting in a decrease in image density. Tends to occur. In addition, although the polymer charge transport material (2) can improve the abrasion resistance to some extent, the durability required for the organic photoreceptor is not fully satisfied. Not reached. In addition, polymer charge transport materials are difficult to polymerize and purify, and it is difficult to obtain a high-purity material. Therefore, it is difficult to stabilize electrical characteristics between materials. Furthermore, production problems such as high viscosity of the coating liquid may occur. The dispersion of the inorganic filler (3) exhibits higher abrasion resistance than a photoreceptor in which a normal low molecular charge transport material is dispersed in an inert polymer, but traps present on the surface of the inorganic filler. As a result, the residual potential increases, and the image density tends to decrease. In addition, when the unevenness of the inorganic filler and the binder resin on the surface of the photoconductor is large, defective cleaning may occur, which may cause toner filming and image flow. With these technologies (1), (2), and (3), the overall durability including the electrical durability and mechanical durability required for the organic photoreceptor is sufficiently satisfied. Has not reached.
Furthermore, a photoreceptor containing a polyfunctional acrylate monomer cured product in order to improve the abrasion resistance and scratch resistance of (1) is also known (see Patent Document 4). However, in this photoreceptor, although there is a description that the polyfunctional acrylate monomer cured product is contained in the protective layer provided on the photosensitive layer, the protective layer may contain a charge transport material. However, when the surface layer contains a low-molecular charge transport material, there is a problem of compatibility with the cured product. In some cases, the molecular charge transport material is precipitated and the cloudiness phenomenon occurs, and the mechanical strength is also lowered.
Furthermore, since this photoconductor specifically reacts with a monomer in a state containing a polymer binder, curing does not proceed sufficiently, and there is a problem of compatibility between the cured product and the binder resin. There was a tendency for surface irregularities due to phase separation to cause poor cleaning.

  As a wear resistance technology for a photosensitive layer that replaces these, a charge transport layer formed by using a coating liquid comprising a monomer having a carbon-carbon double bond, a charge transport material having a carbon-carbon double bond, and a binder resin. The binder resin has a carbon-carbon double bond and is reactive with the charge transfer agent, and the double resin is known to be provided. Those having no bond and no reactivity are included. This photoconductor is remarkably compatible with wear resistance and good electrical properties, but when a non-reactive binder resin is used, the binder resin, the monomer and the charge transport agent are used. The compatibility with the cured product produced by this reaction was poor, and surface irregularities were generated during the crosslinking from phase separation, and a tendency to cause poor cleaning was observed. In addition, as described above, in this case, the binder resin prevents the curing of the monomer, and what is specifically described as the monomer used in the photoreceptor is a bifunctional one. A monomer has a small number of functional groups and a sufficient crosslinking density cannot be obtained. From these points, it has not yet been satisfactory in terms of wear resistance. In addition, even when a reactive binder is used, it is difficult to achieve both the binding amount and the crosslinking density of the charge transport material due to the low number of functional groups contained in the monomer and the binder resin, and the electrical characteristics. In addition, the wear resistance was not sufficient.

A photosensitive layer containing a compound obtained by curing a hole transporting compound having two or more chain polymerizable functional groups in the same molecule is also known (for example, see Patent Document 6).
However, in this photosensitive layer, the bulky hole-transporting compound has two or more chain-polymerizable functional groups, so that the cured product is distorted and the internal stress is increased, resulting in surface layer roughness and cracks over time. It may be easy to do.
Even in the conventional photoconductors having a cross-linked photosensitive layer in which a charge transporting structure is chemically bonded, it cannot be said that the present invention has sufficient comprehensive characteristics.

JP 56-48637 A JP-A 64-1728 JP-A-4-281461 Japanese Patent No. 3262488 Japanese Patent No. 3194392 JP 2000-66425 A

  The subject of the present invention is high abrasion resistance and good electrical characteristics, and particularly by forming a photosensitive layer excellent in surface smoothness, the cleaning characteristics are good, and the durability is high. In addition, the present invention is to provide an electrophotographic photosensitive member that realizes high image quality over a long period of time, and also provides an image forming method, an image forming apparatus, and a process cartridge for the image forming apparatus using the long-life, high-performance photosensitive member. Is to provide.

  As a result of intensive studies, the inventors of the present invention cured at least a trifunctional or higher functional radical polymerizable monomer having no charge transport structure and a radical polymerizable compound having a monofunctional charge transport structure on the surface layer of the photosensitive layer. The present invention has been made upon the discovery that the object can be achieved by making the crosslinked surface layer have a surface roughness Rz of 1.3 μm or less.

That is, the above-described problem is (1) “an electrophotographic photosensitive member having at least a photosensitive layer on a conductive support, wherein the crosslinked surface layer of the photosensitive member does not have a charge transporting structure. A coating film containing a functional polymerizable or higher radical polymerizable monomer, a radical polymerizable compound having a monofunctional charge transporting structure, and a polymerization initiator and not containing a filler is crosslinked and cured by light irradiation or heat. The formed electrophotographic photosensitive member, wherein the surface roughness Rz is 1.3 μm or less, and the coating film contains a solvent that dissolves the lower layer of the crosslinked surface layer ”, (2)“ The surface roughness Rz of the crosslinked surface layer is 1.0 μm or less, wherein the electrophotographic photosensitive member according to the item (1), (3) “charge transporting structure used for the surface layer” A tri- or more functional radical polymerizable compound that does not contain The electrophotographic photosensitive member according to (1) or (2) above, wherein the functional group of the nomer is an acryloyloxy group and / or a methacryloyloxy group ”, (4)“ the surface layer ” The ratio of the molecular weight to the number of functional groups (molecular weight / number of functional groups) in the trifunctional or higher functional radical polymerizable monomer having no charge transporting structure used in the above (1) to (1) The electrophotographic photoreceptor according to any one of (3) and (5), wherein the functional group of the radical polymerizable compound having a monofunctional charge transporting structure used in the surface layer is an acryloyloxy group or methacryloyloxy The electrophotographic photosensitive member according to any one of (1) to (4) above, (6) “a monofunctional charge transporting structure used for the outermost surface layer” The electrophotographic photosensitive member according to any one of (1) to (5) above, wherein the charge transport structure of the radical polymerizable compound having a triarylamine structure ”, (7) “The radical polymerizable compound having a monofunctional charge transporting structure used for the surface layer is one or more of the following general formulas (1) or (2): The electrophotographic photosensitive member according to any one of (6);

（式中、Ｒ_１は水素原子、ハロゲン原子、置換基を有してもよいアルキル基、置換基を有してもよいアラルキル基、置換基を有してもよいアリール基、シアノ基、ニトロ基、アルコキシ基、−ＣＯＯＲ_７（Ｒ_７は水素原子、置換基を有してもよいアルキル基、置換基を有してもよいアラルキル基又は置換基を有してもよいアリール基）、ハロゲン化カルボニル基若しくはＣＯＮＲ_８Ｒ_９（Ｒ_８及びＲ_９は水素原子、ハロゲン原子、置換基を有してもよいアルキル基、置換基を有してもよいアラルキル基又は置換基を有してもよいアリール基を示し、互いに同一であっても異なっていてもよい）を表わし、Ａｒ_１、Ａｒ_２は置換もしくは未置換のアリーレン基を表わし、同一であっても異なってもよい。Ａｒ_３、Ａｒ_４は置換もしくは未置換のアリール基を表わし、同一であっても異なってもよい。Ｘは単結合、置換もしくは無置換のアルキレン基、置換もしくは無置換のシクロアルキレン基、置換もしくは無置換のアルキレンエーテル基、酸素原子、硫黄原子、ビニレン基を表わす。Ｚは置換もしくは無置換のアルキレン基、置換もしくは無置換のアルキレンエーテル２価基、アルキレンオキシカルボニル２価基を表わす。ｍ、ｎは０〜３の整数を表わす。）」、（８）「前記表面層に用いられる１官能の電荷輸送性構造を有するラジカル重合性化合物が、下記一般式（３）の一種以上であることを特徴とする前記第（１）項乃至第（７）項のいずれかに記載の電子写真感光体；

(In the formula, R ₁ represents a hydrogen atom, a halogen atom, an alkyl group which may have a substituent, an aralkyl group which may have a substituent, an aryl group which may have a substituent, a cyano group, a nitro group, Group, alkoxy group, —COOR ₇ (R ₇ is a hydrogen atom, an alkyl group which may have a substituent, an aralkyl group which may have a substituent or an aryl group which may have a substituent), halogen Carbonyl group or CONR ₈ R ₉ (R ₈ and R ₉ may have a hydrogen atom, a halogen atom, an alkyl group which may have a substituent, an aralkyl group which may have a substituent, or a substituent. Ar ₁ and Ar ₂ each represent a substituted or unsubstituted arylene group, and may be the same or different.Ar ₃ , which may be the same or different from each other. Ar ₄ may be substituted Represents an unsubstituted aryl group, which may be the same or different, X represents a single bond, a substituted or unsubstituted alkylene group, a substituted or unsubstituted cycloalkylene group, a substituted or unsubstituted alkylene ether group, O represents an oxygen atom, a sulfur atom, or a vinylene group, Z represents a substituted or unsubstituted alkylene group, a substituted or unsubstituted alkylene ether divalent group, or an alkyleneoxycarbonyl divalent group, and m and n are integers of 0 to 3. ) ”, (8)“ The radical polymerizable compound having a monofunctional charge transporting structure used in the surface layer is one or more of the following general formula (3): The electrophotographic photosensitive member according to any one of items 1) to (7);

（式中、ｏ、ｐ、ｑはそれぞれ０又は１の整数、Ｒａは水素原子、メチル基を表わし、Ｒｂ、Ｒｃは水素原子以外の置換基で炭素数１〜６のアルキル基を表わし、複数の場合は異なっても良い。ｓ、ｔは０〜３の整数を表わす。Ｚａは単結合、メチレン基、エチレン基；

(Wherein, o, p and q are each an integer of 0 or 1, Ra represents a hydrogen atom or a methyl group, Rb and Rc represent a substituent other than a hydrogen atom and an alkyl group having 1 to 6 carbon atoms, And s and t each represents an integer of 0 to 3. Za is a single bond, a methylene group or an ethylene group;

を表わす。）」、（９）「前記表面層に用いられる電荷輸送性構造を有しない３官能以上のラジカル重合性モノマーの成分割合が、架橋表面層全量に対し３０〜７０重量％であることを特徴とする前記第（１）項乃至第（８）項のいずれかに記載の電子写真感光体」、（１０）「前記表面層に用いられる１官能の電荷輸送性構造を有するラジカル重合性化合物の成分割合が、架橋表面層全量に対し３０〜７０重量％であることを特徴とする前記第（１）項乃至第（９）項のいずれかに記載の電子写真感光体」、（１１）「前記感光層が支持体側から電荷発生層、電荷輸送層、架橋表面層の積層構成であることを特徴とする前記第（１）項乃至第（１０）項のいずれかに記載の電子写真感光体」、（１２）「前記感光層の電荷輸送層が高分子電荷輸送物質を含有することを特徴とする前記第（１１）項に記載の電子写真感光体」、（１３）「前記高分子電荷輸送物質がトリアリールアミン構造を主鎖又は側鎖に有するポリカーボネートであることを特徴とする前記第（１２）項に記載の電子写真感光体」により解決される。

Represents. ) ", (9)" The proportion of the trifunctional or higher functional radical-polymerizable monomer having no charge transport structure used in the surface layer is 30 to 70% by weight based on the total amount of the crosslinked surface layer. The electrophotographic photosensitive member according to any one of (1) to (8) above, (10) “component of radically polymerizable compound having a monofunctional charge transporting structure used for the surface layer” The electrophotographic photosensitive member according to any one of (1) to (9) above, wherein the ratio is 30 to 70% by weight based on the total amount of the crosslinked surface layer. The electrophotographic photosensitive member according to any one of items (1) to (10), wherein the photosensitive layer has a laminated structure of a charge generation layer, a charge transport layer, and a crosslinked surface layer from the support side. (12) "The charge transport layer of the photosensitive layer is a polymer charge transport material The electrophotographic photosensitive member according to item (11), wherein the polymer charge transporting substance is a polycarbonate having a triarylamine structure in the main chain or side chain. It is more resolved the electrophotographic photosensitive member "described in the second (12) section, characterized.

In addition, the above-described problem is that at least charging, image exposure, development, and transfer are repeated using the electrophotographic photosensitive member according to any one of ( 14 ) and (1) to ( 13 ) of the present invention. The image forming method is characterized in that it is solved.

In addition, the above-described problems are solved by ( 15 ) “an image forming apparatus comprising the electrophotographic photosensitive member according to any one of (1) to ( 13 )” of the present invention. .

In addition, the above-described problems are solved by the electrophotographic photosensitive member according to any one of ( 16 ) and (1) to ( 13 ), a charging unit, a developing unit, a transfer unit, a cleaning unit, and a static eliminating unit. An image forming apparatus process cartridge having at least one means selected from the group consisting of means and detachable from the main body of the image forming apparatus is solved.

  According to the present invention, a radical polymerizable monomer having a trifunctional or higher functionality having no charge transporting structure and a radical polymerizable compound having a monofunctional charge transporting structure are cured, and the surface roughness Rz is 1. The photosensitive layer having a smooth cross-linked surface layer of 3 μm or less has high wear resistance, is unlikely to deteriorate in a high-humidity environment, and has good electrical characteristics and cleaning characteristics. A photoreceptor is obtained. Therefore, it is possible to provide a high-performance and highly reliable image forming process, an image forming apparatus, and a process cartridge for an image forming apparatus that can provide a good image over a long period of time by using this photoconductor.

Hereinafter, the present invention will be described in detail.
The present invention comprises a surface layer of a photosensitive layer comprising at least a trifunctional or higher-functional radical polymerizable monomer having no charge transport structure and a crosslinked layer obtained by curing a radical polymerizable compound having a monofunctional charge transport structure. By setting the surface roughness Rz of the surface layer to 1.3 μm or less, an electrophotographic photoreceptor having high durability and realizing high image quality over a long period of time is achieved.
The reasons for this are as follows.
In the formation of the outermost surface layer of the photoreceptor of the present invention, a radically polymerizable monomer having three or more functional groups is used, whereby a three-dimensional network structure is developed and a high hardness surface layer having a very high degree of crosslinking is obtained. And high wear resistance is achieved. On the other hand, when only monofunctional and bifunctional radically polymerizable monomers are used, the cross-linking bond in the cross-linked surface layer becomes dilute, and a dramatic improvement in wear resistance cannot be achieved. When a polymer material is contained in the cross-linked surface layer, the development of the three-dimensional network structure is inhibited and the degree of cross-linking is lowered, so that sufficient wear resistance cannot be obtained as compared with the present invention. Furthermore, the compatibility between the polymer material and the cured product resulting from the reaction of the radical polymerizable composition (radical polymerizable monomer or radical polymerizable compound having a charge transporting structure) is poor, resulting in localized from phase separation. Wears and appears as a scratch on the surface. In addition, in the formation of the outermost surface phase of the present invention, in addition to the above trifunctional radical polymerizable monomer, a radical polymerizable compound having a monofunctional charge transporting structure is contained, which is a trifunctional or higher functional group. Incorporated into the cross-linking during curing of the radical polymerizable monomer. On the other hand, when a low molecular charge transport material having no functional group is contained in the cross-linked surface layer, precipitation of the low molecular charge transport material and white turbidity occur due to its low compatibility, and the cross-linked surface layer The mechanical strength also decreases. On the other hand, when a bifunctional or higher functional charge transporting compound is used as the main component, it is fixed in the cross-linked structure with a plurality of bonds. The internal stress of the surface layer increases, and cracks and scratches frequently occur due to carrier adhesion and the like.

  Furthermore, the photoreceptor of the present invention has good electrical characteristics, and thus high image quality can be realized over a long period of time. This is because a radically polymerizable compound having a monofunctional charge transporting structure is used and is immobilized in a pendant shape between crosslinks. As described above, the charge transport material having no functional group causes precipitation and clouding phenomenon, and deterioration due to repeated use such as reduction in sensitivity and increase in residual potential is remarkable. When a bifunctional or higher-functional charge transporting compound is used as the main component, it is fixed in the crosslinked structure with a plurality of bonds, so the intermediate structure (cation radical) during charge transport cannot be kept stable, Sensitivity decreases due to trapping and residual potential increases. Such deterioration of the electrical characteristics appears as an image such as a decrease in image density and thinning of characters.

  Furthermore, according to the photoconductor-forming material of the present invention, it is possible to obtain a photoconductor with high surface smoothness. In particular, when the surface roughness Rz of the crosslinked surface layer is 1.3 μm or less, the photoconductor forming material is shown above. The effect is fully demonstrated. When the surface roughness Rz exceeds 1.3 μm, minute toner slips out easily in the cleaning blade, causing background stains and streaky images. In addition, since the film strength is high, there is little wear, and the paper dust adhering to the recesses, the oxidizing gas generated from the charger and the deteriorated surface of the photoreceptor cannot be sufficiently removed. For this reason, image flow and character fattening easily occur in a high humidity environment.

（ただし、式中、Ｘ_１は、置換基を有していてもよいフェニレン基、ナフチレン基等のアリーレン基、置換基を有していてもよいアルケニレン基、−ＣＯ−基、−ＣＯＯ−基、−ＣＯＮ（Ｒ_１０）−基（Ｒ_１０は、水素、メチル基、エチル基等のアルキル基、ベンジル基、ナフチルメチル基、フェネチル基等のアラルキル基、フェニル基、ナフチル基等のアリール基を表す。）、または−Ｓ−基を表わす。）
これらの置換基を具体的に例示すると、ビニル基、スチリル基、２−メチル−１，３−ブタジエニル基、ビニルカルボニル基、アクリロイルオキシ基、アクリロイルアミノ基、ビニルチオエーテル基等が挙げられる。
（２）１，１−置換エチレン官能基としては、例えば以下の式で表わされる官能基が挙げられる。

（ただし、式中、Ｙは、置換基を有していてもよいアルキル基、置換基を有していてもよいアラルキル基、置換基を有していてもよいフェニル基、ナフチル基等のアリール基、ハロゲン原子、シアノ基、ニトロ基、メトキシ基あるいはエトキシ基等のアルコキシ基、−ＣＯＯＲ_１１基（Ｒ_１１は、水素原子、置換基を有していてもよいメチル基、エチル基等のアルキル基、置換基を有していてもよいベンジル、フェネチル基等のアラルキル基、置換基を有していてもよいフェニル基、ナフチル基等のアリール基、または−ＣＯＮＲ_１２Ｒ_１３（Ｒ_１２およびＲ_１３は、水素原子、置換基を有していてもよいメチル基、エチル基等のアルキル基、置換基を有していてもよいベンジル基、ナフチルメチル基、あるいはフェネチル基等のアラルキル基、または置換基を有していてもよいフェニル基、ナフチル基等のアリール基を表わし、互いに同一または異なっていてもよい。）、また、Ｘ_２は上記式１０のＸ_１と同一の置換基及び単結合、アルキレン基を表わす。ただし、Ｙ，Ｘ_２の少なくとも何れか一方がオキシカルボニル基、シアノ基、アルケニレン基、及び芳香族環である。）
これらの置換基を具体的に例示すると、α−塩化アクリロイルオキシ基、メタクリロイルオキシ基、α−シアノエチレン基、α−シアノアクリロイルオキシ基、α−シアノフェニレン基、メタクリロイルアミノ基等が挙げられる。
なお、これらＸ_１，Ｘ_２、Ｙについての置換基にさらに置換される置換基としては、例えばハロゲン原子、ニトロ基、シアノ基、メチル基、エチル基等のアルキル基、メトキシ基、エトキシ基等のアルコキシ基、フェノキシ基等のアリールオキシ基、フェニル基、ナフチル基等のアリール基、ベンジル基、フェネチル基等のアラルキル基等が挙げられる。
これらのラジカル重合性官能基の中では、特にアクリロイルオキシ基、メタクリロイルオキシ基が有用であり、３個以上のアクリロイルオキシ基を有する化合物は、例えば水酸基がその分子中に３個以上ある化合物とアクリル酸（塩）、アクリル酸ハライド、アクリル酸エステルを用い、エステル反応あるいはエステル交換反応させることにより得ることができる。また、３個以上のメタクリロイルオキシ基を有する化合物も同様にして得ることができる。また、ラジカル重合性官能基を３個以上有する単量体中のラジカル重合性官能基は、同一でも異なっても良い。 Next, the constituent material of the outermost surface layer coating solution of the present invention will be described.
The trifunctional or higher functional radical polymerizable monomer having no charge transporting property used in the present invention is a hole transporting structure such as triarylamine, hydrazone, pyrazoline, carbazole, such as condensed polycyclic quinone, diphenoquinone, cyano group. And a monomer having no electron transport structure such as an electron-withdrawing aromatic ring having a nitro group and having three or more radical polymerizable functional groups. The radical polymerizable functional group may be any group as long as it has a carbon-carbon double bond and can be radically polymerized.
Examples of these radical polymerizable functional groups include 1-substituted ethylene functional groups and 1,1-substituted ethylene functional groups shown below.
(1) Examples of the 1-substituted ethylene functional group include functional groups represented by the following formulas.

(In the formula, X ₁ is an arylene group such as a phenylene group or a naphthylene group which may have a substituent, an alkenylene group which may have a substituent, a —CO— group, a —COO— group. , —CON (R ₁₀ ) — group (R ₁₀ represents an alkyl group such as hydrogen, methyl group or ethyl group, an aralkyl group such as benzyl group, naphthylmethyl group or phenethyl group, or an aryl group such as phenyl group or naphthyl group. Or -S- group.)
Specific examples of these substituents include vinyl group, styryl group, 2-methyl-1,3-butadienyl group, vinylcarbonyl group, acryloyloxy group, acryloylamino group, vinylthioether group and the like.
(2) Examples of the 1,1-substituted ethylene functional group include functional groups represented by the following formulas.

(In the formula, Y is an aryl group such as an alkyl group which may have a substituent, an aralkyl group which may have a substituent, a phenyl group which may have a substituent, or a naphthyl group. Group, halogen atom, cyano group, nitro group, alkoxy group such as methoxy group or ethoxy group, -COOR ₁₁ group (R ₁₁ is a hydrogen atom, an alkyl such as an optionally substituted methyl group or ethyl group) Group, an aralkyl group such as benzyl which may have a substituent, a phenethyl group or the like, an aryl group such as a phenyl group or a naphthyl group which may have a substituent, or -CONR ₁₂ R ₁₃ (R ₁₂ and R ₁₃ is a hydrogen atom, which may have a substituent an alkyl group such as methyl group and ethyl group, which may have a substituent group benzyl group, naphthylmethyl group, or Ara such phenethyl group, Kill group or substituent a phenyl group which may have a, an aryl group such as a naphthyl group, which may be the same or different from each other.) Further, X ₂ is the same as X ₁ in the formula 10 A substituent, a single bond, or an alkylene group, provided that at least one of Y and X ₂ is an oxycarbonyl group, a cyano group, an alkenylene group, and an aromatic ring.
Specific examples of these substituents include an α-acryloyloxy chloride group, a methacryloyloxy group, an α-cyanoethylene group, an α-cyanoacryloyloxy group, an α-cyanophenylene group, and a methacryloylamino group.
In addition, examples of the substituent further substituted with the substituent for X ₁ , X ₂ , and Y include, for example, a halogen atom, a nitro group, a cyano group, a methyl group, an alkyl group such as an ethyl group, a methoxy group, an ethoxy group, and the like And an aryloxy group such as a phenoxy group, an aryl group such as a phenyl group and a naphthyl group, and an aralkyl group such as a benzyl group and a phenethyl group.
Among these radical polymerizable functional groups, acryloyloxy group and methacryloyloxy group are particularly useful, and a compound having three or more acryloyloxy groups is, for example, a compound having three or more hydroxyl groups in the molecule and an acrylic group. It can be obtained by using an acid (salt), an acrylic acid halide, or an acrylic ester to cause an ester reaction or a transesterification reaction. A compound having three or more methacryloyloxy groups can be obtained in the same manner. Further, the radical polymerizable functional groups in the monomer having three or more radical polymerizable functional groups may be the same or different.

Specific examples of the trifunctional or higher functional radical polymerizable monomer having no charge transporting structure include the following, but are not limited to these compounds.
That is, examples of the radical polymerizable monomer used in the present invention include trimethylolpropane triacrylate (TMPTA), trimethylolpropane trimethacrylate, trimethylolpropane alkylene-modified triacrylate, trimethylolpropane ethyleneoxy-modified (hereinafter referred to as EO modification). ) Triacrylate, trimethylolpropane propyleneoxy modified (hereinafter PO modified) triacrylate, trimethylolpropane caprolactone modified triacrylate, trimethylolpropane alkylene modified trimethacrylate, pentaerythritol triacrylate, pentaerythritol tetraacrylate (PETTA), glycerol triacrylate Glycerol epichlorohydrin modified (hereinafter ECH modified) Acrylate, glycerol EO modified triacrylate, glycerol PO modified triacrylate, tris (acryloxyethyl) isocyanurate, dipentaerythritol hexaacrylate (DPHA), dipentaerythritol caprolactone modified hexaacrylate, dipentaerythritol hydroxypentaacrylate, alkylated di Pentaerythritol pentaacrylate, alkylated dipentaerythritol tetraacrylate, alkylated dipentaerythritol triacrylate, dimethylolpropane tetraacrylate (DTMPTA), pentaerythritol ethoxytetraacrylate, phosphoric acid EO-modified triacrylate, 2, 2, 5, 5 , -Tetrahydroxymethylcyclopentanone tetraacrylate And the like, which can be used in combination either alone or in combination.

  The trifunctional or higher functional radical polymerizable monomer having no charge transport structure used in the present invention is a ratio of molecular weight to the number of functional groups in the monomer in order to form a dense crosslink in the cross-linked surface layer. (Molecular weight / functional group number) is preferably 250 or less. When this ratio is larger than 250, the crosslinked surface layer is soft and wear resistance is somewhat lowered. Therefore, among the monomers exemplified above, monomers having a modifying group such as EO, PO, and capracton are extremely long. It is not preferable to use one having a modifying group alone. In addition, the proportion of the trifunctional or higher functional radical polymerizable monomer having no charge transport structure used for the surface layer is 20 to 80% by weight, preferably 30 to 70% by weight, based on the total amount of the crosslinked surface layer. Specifically, it depends on the ratio of the tri- or higher functional radical polymerizable monomer in the solid content of the coating liquid. When the monomer component is less than 20% by weight, the three-dimensional cross-linking density of the cross-linked surface layer is small, and a drastic improvement in wear resistance is not achieved as compared with the case of using a conventional thermoplastic binder resin. On the other hand, if it exceeds 80% by weight, the content of the charge transporting compound is lowered, and the electrical characteristics are deteriorated. Since the required wear resistance and electrical characteristics differ depending on the process used, it cannot be said unconditionally, but considering the balance of both characteristics, the range of 30 to 70% by weight is most preferable.

  The radically polymerizable compound having a monofunctional charge transporting structure used in the present invention is a hole transporting structure such as triarylamine, hydrazone, pyrazoline, carbazole, such as condensed polycyclic quinone, diphenoquinone, cyano group, and the like. A compound having an electron transport structure such as an electron-withdrawing aromatic ring having a nitro group and having one radical polymerizable functional group. Examples of the radical polymerizable functional group include functional groups represented by the above formula 10 or formula 11. More specifically, those shown in the above radical polymerizable monomer can be mentioned, and acryloyloxy group and methacryloyloxy group are particularly useful. In addition, a triarylamine structure is highly effective as a charge transporting structure, and in particular, when a compound represented by the structure of the following general formula (1) or (2) is used, electrical characteristics such as sensitivity and residual potential are good. To last.

（式中、Ｒ_１は水素原子、ハロゲン原子、置換基を有してもよいアルキル基、置換基を有してもよいアラルキル基、置換基を有してもよいアリール基、シアノ基、ニトロ基、アルコキシ基、−ＣＯＯＲ_７（Ｒ_７は水素原子、置換基を有してもよいアルキル基、置換基を有してもよいアラルキル基又は置換基を有してもよいアリール基）、ハロゲン化カルボニル基若しくはＣＯＮＲ_８Ｒ_９（Ｒ_８及びＲ_９は水素原子、ハロゲン原子、置換基を有してもよいアルキル基、置換基を有してもよいアラルキル基又は置換基を有してもよいアリール基を示し、互いに同一であっても異なっていてもよい）を表わし、Ａｒ_１、Ａｒ_２は置換もしくは未置換のアリーレン基を表わし、同一であっても異なってもよい。Ａｒ_３、Ａｒ_４は置換もしくは未置換のアリール基を表わし、同一であっても異なってもよい。Ｘは単結合、置換もしくは無置換のアルキレン基、置換もしくは無置換のシクロアルキレン基、置換もしくは無置換のアルキレンエーテル基、酸素原子、硫黄原子、ビニレン基を表わす。Ｚは置換もしくは無置換のアルキレン基、置換もしくは無置換のアルキレンエーテル２価基、アルキレンオキシカルボニル２価基を表わす。ｍ、ｎは０〜３の整数を表わす。）

(In the formula, R ₁ represents a hydrogen atom, a halogen atom, an alkyl group which may have a substituent, an aralkyl group which may have a substituent, an aryl group which may have a substituent, a cyano group, a nitro group, Group, alkoxy group, —COOR ₇ (R ₇ is a hydrogen atom, an alkyl group which may have a substituent, an aralkyl group which may have a substituent or an aryl group which may have a substituent), halogen Carbonyl group or CONR ₈ R ₉ (R ₈ and R ₉ may have a hydrogen atom, a halogen atom, an alkyl group which may have a substituent, an aralkyl group which may have a substituent, or a substituent. Ar ₁ and Ar ₂ each represent a substituted or unsubstituted arylene group, and may be the same or different.Ar ₃ , which may be the same or different from each other. Ar ₄ may be substituted Represents an unsubstituted aryl group, which may be the same or different, X represents a single bond, a substituted or unsubstituted alkylene group, a substituted or unsubstituted cycloalkylene group, a substituted or unsubstituted alkylene ether group, O represents an oxygen atom, a sulfur atom, or a vinylene group, Z represents a substituted or unsubstituted alkylene group, a substituted or unsubstituted alkylene ether divalent group, or an alkyleneoxycarbonyl divalent group, and m and n are integers of 0 to 3. Represents.)

Specific examples of general formulas (1) and (2) are shown below.
In the general formulas (1) and (2), in the substituent of R ₁ , examples of the alkyl group include a methyl group, an ethyl group, a propyl group, and a butyl group, and examples of the aryl group include a phenyl group and a naphthyl group. The aralkyl group includes a benzyl group, a phenethyl group, and a naphthylmethyl group, and the alkoxy group includes a methoxy group, an ethoxy group, a propoxy group, and the like. These include a halogen atom, a nitro group, a cyano group, and a methyl group. Substituted with an alkyl group such as an ethyl group, an alkoxy group such as a methoxy group or an ethoxy group, an aryloxy group such as a phenoxy group, an aryl group such as a phenyl group or a naphthyl group, an aralkyl group such as a benzyl group or a phenethyl group, etc. May be.
Of the substituents for R ₁ , particularly preferred are a hydrogen atom and a methyl group.
Substituted or unsubstituted Ar ₃ and Ar ₄ are aryl groups, and examples of the aryl group include condensed polycyclic hydrocarbon groups, non-fused cyclic hydrocarbon groups, and heterocyclic groups.
The condensed polycyclic hydrocarbon group preferably has 18 or less carbon atoms forming a ring, for example, a pentanyl group, an indenyl group, a naphthyl group, an azulenyl group, a heptaenyl group, a biphenylenyl group, an as-indacenyl group. , S-indacenyl group, fluorenyl group, acenaphthylenyl group, preadenyl group, acenaphthenyl group, phenalenyl group, phenanthryl group, anthryl group, fluoranthenyl group, acephenanthrenyl group, aceanthrylenyl group, triphenylyl group, pyrenyl group , A chrycenyl group, a naphthacenyl group, and the like.

  Examples of the non-fused cyclic hydrocarbon group include monovalent groups of monocyclic hydrocarbon compounds such as benzene, diphenyl ether, polyethylene diphenyl ether, diphenyl thioether and diphenyl sulfone, or biphenyl, polyphenyl, diphenylalkane, diphenylalkene, diphenylalkyne, Monovalent groups of non-condensed polycyclic hydrocarbon compounds such as triphenylmethane, distyrylbenzene, 1,1-diphenylcycloalkane, polyphenylalkane, and polyphenylalkene, or ring assemblies such as 9,9-diphenylfluorene And monovalent groups of hydrocarbon compounds.

Examples of the heterocyclic group include monovalent groups such as carbazole, dibenzofuran, dibenzothiophene, oxadiazole, and thiadiazole.
The aryl group represented by Ar ₃ or Ar ₄ may have a substituent as shown below, for example.
(1) Halogen atom, cyano group, nitro group and the like.
(2) Alkyl groups, preferably C ₁ -C _12, especially C ₁ -C ₈ , more preferably C ₁ -C ₄ linear or branched alkyl groups, further including fluorine atoms , a hydroxyl group, a cyano _group, an alkoxy group of C 1 -C _4, a phenyl group or a halogen _atom, which may have a phenyl group substituted by an alkoxy group C 1 -C ₄ alkyl or _C 1 -C ₄ Good. Specifically, methyl group, ethyl group, n-butyl group, i-propyl group, t-butyl group, s-butyl group, n-propyl group, trifluoromethyl group, 2-hydroxyethyl group, 2-ethoxyethyl Group, 2-cyanoethyl group, 2-methoxyethyl group, benzyl group, 4-chlorobenzyl group, 4-methylbenzyl group, 4-phenylbenzyl group and the like.
(3) An alkoxy group (—OR ₂ ), and R ₂ represents the alkyl group defined in (2). Specifically, methoxy group, ethoxy group, n-propoxy group, i-propoxy group, t-butoxy group, n-butoxy group, s-butoxy group, i-butoxy group, 2-hydroxyethoxy group, benzyloxy group And a trifluoromethoxy group.
(4) An aryloxy group, and examples of the aryl group include a phenyl group and a naphthyl group. It _may contain an alkoxy group having C 1 -C _4, alkyl group, or a halogen atom C 1 -C ₄ as a substituent. Specific examples include a phenoxy group, a 1-naphthyloxy group, a 2-naphthyloxy group, a 4-methoxyphenoxy group, and a 4-methylphenoxy group.
(5) Alkyl mercapto group or aryl mercapto group, and specific examples include methylthio group, ethylthio group, phenylthio group, p-methylphenylthio group and the like.
(6)

（式中、Ｒ_３及びＲ_４は各々独立に水素原子、前記（２）で定義したアルキル基、またはアリール基を表わす。アリール基としては、例えばフェニル基、ビフェニル基又はナフチル基が挙げられ、これらはＣ_１〜Ｃ_４のアルコキシ基、Ｃ_１〜Ｃ_４のアルキル基またはハロゲン原子を置換基として含有してもよい。Ｒ_３及びＲ_４は共同で環を形成してもよい）
具体的には、アミノ基、ジエチルアミノ基、Ｎ−メチル−Ｎ−フェニルアミノ基、Ｎ，Ｎ−ジフェニルアミノ基、Ｎ，Ｎ−ジ（トリール）アミノ基、ジベンジルアミノ基、ピペリジノ基、モルホリノ基、ピロリジノ基等が挙げられる。
（７）メチレンジオキシ基、又はメチレンジチオ基等のアルキレンジオキシ基又はアルキレンジチオ基等が挙げられる。
（８）置換又は無置換のスチリル基、置換又は無置換のβ−フェニルスチリル基、ジフェニルアミノフェニル基、ジトリルアミノフェニル基等。

(In the formula, R ₃ and R ₄ each independently represent a hydrogen atom, an alkyl group defined in (2) above, or an aryl group. Examples of the aryl group include a phenyl group, a biphenyl group, and a naphthyl group. these may form a ring _C 1 -C ₄ alkoxy _groups, C 1 -C a alkyl group or a halogen atom ₄ which may contain as substituents .R ₃ and _{R 4} jointly)
Specifically, amino group, diethylamino group, N-methyl-N-phenylamino group, N, N-diphenylamino group, N, N-di (tolyl) amino group, dibenzylamino group, piperidino group, morpholino group And pyrrolidino group.
(7) An alkylenedioxy group or an alkylenedithio group such as a methylenedioxy group or a methylenedithio group.
(8) A substituted or unsubstituted styryl group, a substituted or unsubstituted β-phenylstyryl group, a diphenylaminophenyl group, a ditolylaminophenyl group, and the like.

The arylene group represented by Ar ₁ and Ar ₂ is a divalent group derived from the aryl group represented by Ar ₃ and Ar ₄ .

X represents a single bond, a substituted or unsubstituted alkylene group, a substituted or unsubstituted cycloalkylene group, a substituted or unsubstituted alkylene ether group, an oxygen atom, a sulfur atom, or a vinylene group. However, when m is 0, X is preferably not a single bond.
The substituted or unsubstituted alkylene group is a C ₁ -C ₁₂ , preferably C ₁ -C ₈ , more preferably C ₁ -C ₄ linear or branched alkylene group, and these alkylene groups include a fluorine atom, a hydroxyl group, a cyano _group, an alkoxy group of C 1 -C _4, a phenyl group or a halogen _atom, a phenyl group substituted with an alkyl group or a _C 1 -C ₄ alkoxy group C 1 -C ₄ It may be. Specifically, methylene group, ethylene group, n-butylene group, i-propylene group, t-butylene group, s-butylene group, n-propylene group, trifluoromethylene group, 2-hydroxyethylene group, 2-ethoxyethylene Group, 2-cyanoethylene group, 2-methoxyethylene group, benzylidene group, phenylethylene group, 4-chlorophenylethylene group, 4-methylphenylethylene group, 4-biphenylethylene group and the like.
The substituted or unsubstituted cycloalkylene _group, a cyclic alkylene group of C 5 -C _7, these are the cyclic alkylene group fluorine atom, a hydroxyl _group, an alkyl group of C 1 -C _4, a C 1 -C ₄ It may have an alkoxy group. Specific examples include a cyclohexylidene group, a cyclohexylene group, and a 3,3-dimethylcyclohexylidene group.
The substituted or unsubstituted alkylene ether group represents ethyleneoxy, propyleneoxy, ethylene glycol, propylene glycol, diethylene glycol, tetraethylene glycol, tripropylene glycol, alkylene ether group alkylene group is hydroxyl group, methyl group, ethyl group, etc. You may have the substituent of.
The vinylene group is

で表わされ、
Ｒ_５は水素、アルキル基（前記（２）で定義されるアルキル基と同じ）、アリール基（前記Ａｒ_３、Ａｒ_４で表わされるアリール基と同じ）、ａは１または２、ｂは１〜３を表わす。

Represented by
R ₅ is hydrogen, an alkyl group (same as the alkyl group defined in (2) above), an aryl group (same as the aryl group represented by Ar ₃ or Ar ₄ above), a is 1 or 2, and b is 1 to 2 3 is represented.

Z represents a substituted or unsubstituted alkylene group, a substituted or unsubstituted alkylene ether divalent group, or an alkyleneoxycarbonyl divalent group.
Examples of the substituted or unsubstituted alkylene group include the same alkylene groups as those described above for X.
Examples of the substituted or unsubstituted alkylene ether divalent group include the divalent group of the alkylene ether group of X.
Examples of the alkyleneoxycarbonyl divalent group include a caprolactone-modified divalent group.

  Further, the radical polymerizable compound having a monofunctional charge transport structure of the present invention is more preferably a compound having a structure of the following general formula (3).

（式中、ｏ、ｐ、ｑはそれぞれ０又は１の整数、Ｒａは水素原子、メチル基を表わし、Ｒｂ、Ｒｃは水素原子以外の置換基で炭素数１〜６のアルキル基を表わし、複数の場合は異なっても良い。ｓ、ｔは０〜３の整数を表わす。Ｚａは単結合、メチレン基、エチレン基、

(Wherein, o, p and q are each an integer of 0 or 1, Ra represents a hydrogen atom or a methyl group, Rb and Rc represent a substituent other than a hydrogen atom and an alkyl group having 1 to 6 carbon atoms, And s and t each represents an integer of 0 to 3. Za is a single bond, a methylene group, an ethylene group,

を表わす。）
上記一般式で表わされる化合物としては、Ｒｂ、Ｒｃの置換基として、特にメチル基、エチル基である化合物が好ましい。
本発明で用いる上記一般式（１）及び（２）特に（３）の１官能性の電荷輸送構造を有するラジカル重合性化合物は、炭素−炭素間の二重結合が両側に開放されて重合するため、末端構造とはならず、連鎖重合体中に組み込まれ、３官能以上のラジカル重合性モノマーとの重合で架橋形成された重合体中では、高分子の主鎖中に存在し、かつ主鎖−主鎖間の架橋鎖中に存在（この架橋鎖には１つの高分子と他の高分子間の分子間架橋鎖と、１つの高分子内で折り畳まれた状態の主鎖のある部位と主鎖中でこれから離れた位置に重合したモノマー由来の他の部位とが架橋される分子内架橋鎖とがある）するが、主鎖中に存在する場合であってもまた架橋鎖中に存在する場合であっても、鎖部分から懸下するトリアリールアミン構造は、窒素原子から放射状方向に配置する少なくとも３つのアリール基を有し、バルキーであるが、鎖部分に直接結合しておらず鎖部分からカルボニル基等を介して懸下しているため立体的位置取りに融通性ある状態で固定されているので、これらトリアリールアミン構造は重合体中で相互に程よく隣接する空間配置が可能であるため、分子内の構造的歪みが少なく、また、電子写真感光体の表面層とされた場合に、電荷輸送経路の断絶を比較的免れた分子内構造を採りうるものと推測される。
本発明の１官能の電荷輸送性構造を有するラジカル重合性化合物の具体例を以下に示すが、これらの構造の化合物に限定されるものではない。

Represents. )
As the compound represented by the above general formula, a compound having a methyl group or an ethyl group as a substituent for Rb and Rc is particularly preferable.
The radically polymerizable compound having a monofunctional charge transport structure represented by the above general formulas (1) and (2), particularly (3) used in the present invention is polymerized by opening a carbon-carbon double bond on both sides. Therefore, in a polymer that does not become a terminal structure, is incorporated in a chain polymer, and is crosslinked by polymerization with a radically polymerizable monomer having three or more functions, it exists in the main chain of the polymer and Present in the cross-linked chain between the chain and the main chain (this cross-linked chain has an intermolecular cross-linked chain between one polymer and another polymer, and a site where the main chain is folded in one polymer. And other intramolecular cross-linked chains that are cross-linked with other sites derived from the polymerized monomer at positions away from this in the main chain), but even if they are present in the main chain, Even if present, the triarylamine structure suspended from the chain moiety is a nitrogen atom. It has at least three aryl groups arranged in the radial direction and is bulky, but is not directly bonded to the chain part, but is suspended from the chain part via a carbonyl group, etc. Since these triarylamine structures can be arranged adjacent to each other in the polymer, there is little structural distortion in the molecule, and the surface of the electrophotographic photosensitive member is also fixed. In the case of a layer, it is presumed that an intramolecular structure that is relatively free from interruption of the charge transport pathway can be adopted.
Specific examples of the radically polymerizable compound having a monofunctional charge transporting structure of the present invention are shown below, but are not limited to the compounds having these structures.

  Further, the radical polymerizable compound having a monofunctional charge transporting structure used in the present invention is important for imparting the charge transporting performance of the crosslinked surface layer, and this component is 20 to 80% by weight based on the total amount of the crosslinked surface layer. %, Preferably 30 to 70% by weight. When this component is less than 20% by weight, the charge transport performance of the crosslinked surface layer cannot be maintained sufficiently, and deterioration of electrical characteristics such as a decrease in sensitivity and an increase in residual potential appears with repeated use. On the other hand, if it exceeds 80% by weight, the content of the trifunctional monomer having no charge transport structure is lowered, and the crosslink density is lowered, so that high wear resistance is not exhibited. The required electrical characteristics and wear resistance differ depending on the process to be used, so it cannot be said unconditionally, but considering the balance of both characteristics, the range of 30 to 70% by weight is most preferable.

The surface layer of the present invention is obtained by curing at least a trifunctional or higher-functional radical polymerizable monomer having no charge transport structure and a radical polymerizable compound having a monofunctional charge transport structure. Monofunctional and bifunctional radically polymerizable monomers and radically polymerizable oligomers can be used in combination for the purpose of imparting functions such as viscosity adjustment at the time, stress relaxation of the cross-linked surface layer, low surface energy and friction coefficient reduction. Known radical polymerizable monomers and oligomers can be used.
Examples of the monofunctional radical monomer include 2-ethylhexyl acrylate, 2-hydroxyethyl acrylate, 2-hydroxypropyl acrylate, tetrahydrofurfuryl acrylate, 2-ethylhexyl carbitol acrylate, 3-methoxybutyl acrylate, benzyl acrylate, and cyclohexyl acrylate. , Isoamyl acrylate, isobutyl acrylate, methoxytriethylene glycol acrylate, phenoxytetraethylene glycol acrylate, cetyl acrylate, isostearyl acrylate, stearyl acrylate, styrene monomer, and the like.
Examples of the bifunctional radical polymerizable monomer include 1,3-butanediol diacrylate, 1,4-butanediol diacrylate, 1,4-butanediol dimethacrylate, 1,6-hexanediol diacrylate, 1, Examples include 6-hexanediol dimethacrylate, diethylene glycol diacrylate, neopentyl glycol diacrylate, bisphenol A-EO modified diacrylate, bisphenol F-EO modified diacrylate, and neopentyl glycol diacrylate.
Examples of the functional monomer include those substituted with a fluorine atom such as octafluoropentyl acrylate, 2-perfluorooctylethyl acrylate, 2-perfluorooctylethyl methacrylate, 2-perfluoroisononylethyl acrylate, No. 60503, JP-B-6-45770, siloxane repeating units: 20-70 acryloyl polydimethylsiloxane ethyl, methacryloyl polydimethylsiloxane ethyl, acryloyl polydimethylsiloxane propyl, acryloyl polydimethylsiloxane butyl, diacryloyl polydimethylsiloxane Examples include vinyl monomers having a polysiloxane group such as diethyl, acrylates and methacrylates.
Examples of the radical polymerizable oligomer include epoxy acrylate, urethane acrylate, and polyester acrylate oligomers. However, when a large amount of monofunctional and bifunctional radically polymerizable monomers and radically polymerizable oligomers are contained, the three-dimensional cross-linking density of the cross-linked surface layer is substantially reduced, resulting in a decrease in wear resistance. For this reason, the content of these monomers and oligomers is limited to 50 parts by weight or less, preferably 30 parts by weight or less, with respect to 100 parts by weight of the tri- or higher functional radical polymerizable monomer.
The surface layer of the present invention is obtained by curing at least a trifunctional or higher-functional radical polymerizable monomer having no charge transport structure and a radical polymerizable compound having a monofunctional charge transport structure. In order to advance this crosslinking reaction efficiently, a polymerization initiator may be used.

  Examples of the thermal polymerization initiator include 2,5-dimethylhexane-2,5-dihydroperoxide, dicumyl peroxide, benzoyl peroxide, t-butylcumyl peroxide, 2,5-dimethyl-2,5-di ( Peroxybenzoyl) hexyne-3, di-t-butyl peroxide, t-butyl hydroperoxide, cumene hydroperoxide, peroxide initiators such as lauroyl peroxide, azobisisobutylnitrile, azobiscyclohexanecarbonitrile Azo initiators such as methyl azobisisobutyrate, azobisisobutylamidine hydrochloride, 4,4′-azobis-4-cyanovaleric acid.

Examples of the photopolymerization initiator include diethoxyacetophenone, 2,2-dimethoxy-1,2-diphenylethane-1-one, 1-hydroxy-cyclohexyl-phenyl-ketone, 4- (2-hydroxyethoxy) phenyl- (2 -Hydroxy-2-propyl) ketone, 2-benzyl-2-dimethylamino-1- (4-morpholinophenyl) butanone-1, 2-hydroxy-2-methyl-1-phenylpropan-1-one, 2- Acetophenone-based or ketal-based photopolymerization initiators such as methyl-2-morpholino (4-methylthiophenyl) propan-1-one, 1-phenyl-1,2-propanedione-2- (o-ethoxycarbonyl) oxime, Benzoin, benzoin methyl ether, benzoin ethyl ether, benzoin isobutyl ether Benzoin ether photopolymerization initiators such as benzoin isopropyl ether, benzophenone, 4-hydroxybenzophenone, methyl o-benzoylbenzoate, 2-benzoylnaphthalene, 4-benzoylbiphenyl, 4-benzoylphenyl ether, acrylated benzophenone, Benzophenone photopolymerization initiators such as 1,4-benzoylbenzene, thioxanthones such as 2-isopropylthioxanthone, 2-chlorothioxanthone, 2,4-dimethylthioxanthone, 2,4-diethylthioxanthone, 2,4-dichlorothioxanthone Examples of photopolymerization initiators and other photopolymerization initiators include ethyl anthraquinone, 2,4,6-trimethylbenzoyldiphenylphosphine oxide, 2,4,6-trimethylbenzoic acid. Phenylethoxyphosphine oxide, bis (2,4,6-trimethylbenzoyl) phenylphosphine oxide, bis (2,4-dimethoxybenzoyl) -2,4,4-trimethylpentylphosphine oxide, methylphenylglyoxyester, 9,10 -Phenanthrene, an acridine type compound, a triazine type compound, an imidazole type compound is mentioned. Moreover, what has a photopolymerization promotion effect can also be used individually or in combination with the said photoinitiator. Examples include triethanolamine, methyldiethanolamine, ethyl 4-dimethylaminobenzoate, isoamyl 4-dimethylaminobenzoate, (2-dimethylamino) ethyl benzoate, 4,4′-dimethylaminobenzophenone, and the like.
These polymerization initiators may be used alone or in combination of two or more. The content of the polymerization initiator is 0.5 to 40 parts by weight, preferably 1 to 20 parts by weight with respect to 100 parts by weight of the total content having radical polymerizability.

  Furthermore, the coating liquid of the present invention can contain additives such as various plasticizers (for the purpose of stress relaxation and adhesion improvement), leveling agents, and low molecular charge transport materials having no radical reactivity as required. As these additives, known additives can be used, and as plasticizers, those used in general resins such as dibutyl phthalate and dioctyl phthalate can be used, and the amount used is the total solid content of the coating liquid. To 20% by weight or less, preferably 10% or less. Moreover, as leveling agents, silicone oils such as dimethyl silicone oil and methylphenyl silicone oil, polymers or oligomers having a perfluoroalkyl group in the side chain can be used, and the amount used is based on the total solid content of the coating liquid. 3% by weight or less is appropriate.

  The crosslinked surface layer of the present invention is formed by applying and curing a coating liquid containing at least a trifunctional or higher functional radical polymerizable monomer having no charge transport structure and a radical polymerizable compound having a monofunctional charge transport structure. It is formed. When the radically polymerizable monomer is a liquid, such a coating liquid can be applied by dissolving other components in the liquid, but if necessary, it is diluted with a solvent and applied. Solvents used at this time include alcohols such as methanol, ethanol, propanol and butanol, ketones such as acetone, methyl ethyl ketone, methyl isobutyl ketone and cyclohexanone, esters such as ethyl acetate and butyl acetate, tetrahydrofuran, dioxane and propyl ether. And ethers such as dichloromethane, dichloroethane, trichloroethane and chlorobenzene, aromatics such as benzene, toluene and xylene, cellosolves such as methyl cellosolve, ethyl cellosolve and cellosolve acetate. These solvents may be used alone or in combination of two or more. The dilution ratio with the solvent varies depending on the solubility of the composition, the coating method, and the target film thickness, and is arbitrary. The coating can be performed using a dip coating method, spray coating, bead coating, ring coating method or the like.

In the present invention, after applying such a coating solution, energy is applied from the outside to be cured to form a crosslinked surface layer. The external energy used at this time includes heat, light, and radiation. The heat energy is applied by heating from the coating surface side or the support side using a gas such as air or nitrogen, steam, various heat media, infrared rays, or electromagnetic waves. The heating temperature is preferably 100 ° C. or higher and 170 ° C. or lower. If the heating temperature is lower than 100 ° C., the reaction rate is slow and the reaction is not completely completed. At a temperature higher than 170 ° C., the reaction proceeds non-uniformly and a large strain is generated in the crosslinked surface layer. In order to advance the curing reaction uniformly, it is also effective to complete the reaction by heating at a relatively low temperature of less than 100 ° C. and then heating to 100 ° C. or more. As the energy of light, UV irradiation light sources such as high-pressure mercury lamps and metal halide lamps, which mainly have an emission wavelength in ultraviolet light, can be used, but a visible light source can also be selected according to the absorption wavelength of radically polymerizable substances and photopolymerization initiators. Is possible. Irradiation light amount is 50 mW / cm ² or more, preferably 1000 mW / cm ² or less, it takes time for the curing reaction is less than 50 mW / cm ^2. When it is higher than 1000 mW / cm ^2, the progress of the reaction becomes non-uniform and the cross-linked surface layer becomes very rough. Examples of radiation energy include those using electron beams. Among these energies, those using heat and light energy are useful because of the ease of reaction rate control and the simplicity of the apparatus.

Since the film thickness of the crosslinked surface layer of the present invention varies depending on the layer structure of the photoreceptor in which the crosslinked surface layer is used, it will be described later together with the layer structure.
The present invention is further characterized in that the surface roughness Rz of the crosslinked surface layer is 1.3 μm or less, preferably 1.0 μm or less.
The surface roughness Rz of the crosslinked surface layer of the present invention is a ten-point average roughness measured according to JIS B0601-1994 standard. In the present invention, the surface roughness Rz is measured using Surfcom 1400D (manufactured by Tokyo Seimitsu). It may be a value measured by any device having a performance equivalent to this.
As described above, when the surface roughness Rz of the cross-linked surface layer exceeds 1.3 μm, it is found that background stains due to poor cleaning, streak-like images and image flow and character thickening tend to occur in a high humidity environment. It was. Since the surface roughness in the crosslinked surface layer of the present invention is related to various conditions, the directivity for making the surface roughness Rz 1.3 μm or less is not uniform. Compositions contained in the surface layer coating liquid, their content, (2) dilution solvent of coating liquid, solid content concentration, (3) coating method, (4) curing means, conditions, (5) The following tendencies are seen due to the solubility of the lower layer.

  In the composition contained in the surface layer coating solution, it is also possible to contain a radical polymerizable compound having a bifunctional or higher functional charge transporting structure or a binder resin, so that the smoothness, electrical characteristics, or durability of the surface of the photoreceptor can be obtained. It is possible as long as the range is not impaired. However, when a radically polymerizable compound having a bifunctional or higher functional charge transporting structure is contained, internal stress is generated during the curing reaction due to the bulk of the charge transporting structure, and irregularities are likely to occur on the surface. In addition, when a polymer material such as a binder resin is included in the coating liquid, a polymer formed by a curing reaction of a radical polymerizable composition (radical polymerizable monomer and radical polymerizable compound having a charge transporting structure) is formed. Due to the poor compatibility, phase separation occurs and the surface of the crosslinked layer becomes uneven. Therefore, it is preferable not to use a radical polymerizable compound having a bifunctional or higher functional charge transporting structure or a binder resin.

  As for the dilution solvent of the coating solution, if a large amount of a solvent that dissolves the lower layer is used in a large amount, a composition such as a resin binder or a low molecular charge transport material in the lower layer is mixed into the outermost surface layer, which hinders the curing reaction Instead, it becomes the same state as when a large amount of the non-curing material is previously contained in the coating solution, which causes disorder of the crosslinked surface. On the other hand, when a solvent that does not dissolve the lower layer is used, the adhesion between the crosslinked surface layer and the lower layer is lowered, and crater-like repellency appears on the crosslinked surface layer due to volume shrinkage during the curing reaction, resulting in a severe surface roughness. These measures include using a mixed solvent to control the solubility of the lower layer, reducing the amount of solvent contained in the outermost coating layer by the liquid composition and coating method, and using a polymer charge transport material, etc., in the lower layer. For example, an intermediate layer having low solubility or an intermediate layer having good adhesion may be provided between the lower layer and the cross-linked surface layer.

  In the cross-linked surface layer of the present invention, it is necessary to contain a bulky charge transporting structure in order to maintain electrical characteristics and to increase the cross-linking density in order to increase the strength. In curing after such surface layer coating, if very high energy is applied from the outside and the reaction proceeds rapidly, the curing proceeds unevenly and the unevenness of the cross-linked film surface becomes severe. For this reason, the thing using the heat | fever which can control reaction rate according to heating conditions, light irradiation intensity | strength, and the amount of polymerization initiators, or the external energy of light is preferable.

In the case of using the crosslinked surface layer forming material of the present invention, for example, a method for making the surface roughness Rz 1.3 μm or less, for example, as an application liquid, an acrylate monomer having three acryloyloxy groups, When a triarylamine compound having one acryloyloxy group is used, the use ratio thereof is 7: 3 to 3: 7, and a polymerization initiator is added in an amount of 3 to 20% by weight based on the total amount of these acrylate compounds. Further, a solvent is added to prepare a coating solution. For example, in the charge transport layer that is the lower layer of the crosslinked surface layer, when the surface layer is formed by spray coating using a triarylamine donor as the charge transport material and polycarbonate as the binder resin, As the solvent, tetrahydrofuran, 2-butanone, ethyl acetate and the like are preferable, and the use ratio thereof is 3 to 10 times the total amount of the acrylate compound.
Next, for example, the prepared coating solution is applied by spraying or the like on a photoreceptor in which an undercoat layer, a charge generation layer, and the charge transport layer are sequentially laminated on a support such as an aluminum cylinder. Thereafter, it is dried at a relatively low temperature for a short time (25 to 80 ° C., 1 to 10 minutes) and cured by UV irradiation or heating.
For UV irradiation, uses a metal halide lamp, illuminance 50 mW / cm ² or more, preferably 1000 mW / cm ² or less, for example, the case of irradiation with UV light of 500 mW / cm ^2, for example upon curing, by rotating the drum All the surfaces may be uniformly irradiated for about 20 seconds. At this time, the drum temperature is controlled so as not to exceed 50 ° C.
In the case of thermosetting, the heating temperature is preferably 100 to 170 ° C. For example, when a blowing oven is used as a heating means and the heating temperature is set to 150 ° C, the heating time is 20 minutes to 3 hours.
After completion of curing, the photosensitive member of the present invention is obtained by heating at 100 to 150 ° C. for 10 to 30 minutes to reduce the residual solvent.

Hereinafter, the present invention will be described according to the layer structure.
<About the layer structure of the electrophotographic photoreceptor>
The electrophotographic photosensitive member used in the present invention will be described with reference to the drawings.
FIG. 1 is a cross-sectional view showing an electrophotographic photosensitive member of the present invention, in which a single layer structure in which a photosensitive layer (33) having a charge generating function and a charge transporting function is provided on a conductive support (31). This is a photoreceptor. FIG. 1A shows the case where the cross-linked surface layer is the entire photosensitive layer, and FIG. 1-B shows the case where the cross-linked surface layer is the surface portion of the photosensitive layer.
FIG. 2 shows a photoreceptor having a laminated structure in which a charge generation layer (35) having a charge generation function and a charge transport layer (37) having a charge transport material function are laminated on a conductive support (31). is there. FIG. 2-A shows the case where the cross-linked surface layer is the entire charge transport layer, and FIG. 2-B shows the case where the cross-linked surface layer is the surface portion of the charge transport layer.

<About conductive support>
As the conductive support (31), a material having a volume resistance of 10 ¹⁰ Ω · cm or less, for example, a metal such as aluminum, nickel, chromium, nichrome, copper, gold, silver, platinum, tin oxide, oxidation Metal oxide such as indium by vapor deposition or sputtering, film or cylindrical plastic, paper coated, or aluminum, aluminum alloy, nickel, stainless steel, etc. After conversion, a tube subjected to surface treatment such as cutting, superfinishing or polishing can be used. Further, an endless nickel belt and an endless stainless steel belt disclosed in Japanese Patent Application Laid-Open No. 52-36016 can be used as the conductive support (31).
In addition, a material obtained by dispersing conductive powder in an appropriate binder resin and coating it on the support can also be used as the conductive support (31) of the present invention.

  Examples of the conductive powder include carbon black, acetylene black, metal powder such as aluminum, nickel, iron, nichrome, copper, zinc and silver, or metal oxide powder such as conductive tin oxide and ITO. Can be mentioned. The binder resin used at the same time is polystyrene, styrene-acrylonitrile copolymer, styrene-butadiene copolymer, styrene-maleic anhydride copolymer, polyester, polyvinyl chloride, vinyl chloride-vinyl acetate copolymer. , Polyvinyl acetate, polyvinylidene chloride, polyarylate resin, phenoxy resin, polycarbonate, cellulose acetate resin, ethyl cellulose resin, polyvinyl butyral, polyvinyl formal, polyvinyl toluene, poly-N-vinyl carbazole, acrylic resin, silicone resin, epoxy resin, Examples thereof include thermoplastic, thermosetting resins, and photocurable resins such as melamine resin, urethane resin, phenol resin, and alkyd resin. Such a conductive layer can be provided by dispersing and coating these conductive powder and binder resin in a suitable solvent such as tetrahydrofuran, dichloromethane, methyl ethyl ketone, and toluene.

  Further, a heat shrinkable tube in which the conductive powder is contained in a material such as polyvinyl chloride, polypropylene, polyester, polystyrene, polyvinylidene chloride, polyethylene, chlorinated rubber, polytetrafluoroethylene-based fluororesin on a suitable cylindrical substrate. Those provided with a conductive layer can be used favorably as the conductive support (31) of the present invention.

<About photosensitive layer>
Next, the photosensitive layer will be described. The photosensitive layer may have a laminated structure or a single layer structure.
In the case of a laminated structure, the photosensitive layer is composed of a charge generation layer having a charge generation function and a charge transport layer having a charge transport function. In the case of a single layer structure, the photosensitive layer is a layer having a charge generation function and a charge transport function at the same time.
Hereinafter, each of the photosensitive layer having a laminated structure and the photosensitive layer having a single layer structure will be described.

<Photosensitive layer comprising a charge generation layer and a charge transport layer>
(Charge generation layer)
The charge generation layer (35) is a layer mainly composed of a charge generation material having a charge generation function, and a binder resin can be used in combination as necessary. As the charge generation material, inorganic materials and organic materials can be used.
Inorganic materials include crystalline selenium, amorphous selenium, selenium-tellurium, selenium-tellurium-halogen, selenium-arsenic compounds, and amorphous silicon. In amorphous silicon, dangling bonds that are terminated with hydrogen atoms or halogen atoms, or those that are doped with boron atoms, phosphorus atoms, or the like are preferably used.
On the other hand, a known material can be used as the organic material. For example, phthalocyanine pigments such as metal phthalocyanine and metal-free phthalocyanine, azulenium salt pigments, squaric acid methine pigments, azo pigments having a carbazole skeleton, azo pigments having a triphenylamine skeleton, azo pigments having a diphenylamine skeleton, dibenzothiophene skeleton Azo pigments having fluorenone skeleton, azo pigments having oxadiazole skeleton, azo pigments having bis-stilbene skeleton, azo pigments having distyryl oxadiazole skeleton, azo pigments having distyrylcarbazole skeleton, perylene Pigments, anthraquinone or polycyclic quinone pigments, quinoneimine pigments, diphenylmethane and triphenylmethane pigments, benzoquinone and naphthoquinone pigments, cyanine and azomethine pigments, Goido based pigments, and bisbenzimidazole pigments. These charge generation materials can be used alone or as a mixture of two or more.

  The binder resin used as necessary for the charge generation layer (35) includes polyamide, polyurethane, epoxy resin, polyketone, polycarbonate, silicone resin, acrylic resin, polyvinyl butyral, polyvinyl formal, polyvinyl ketone, polystyrene, poly-N-. Examples thereof include vinyl carbazole and polyacrylamide. These binder resins can be used alone or as a mixture of two or more. In addition to the binder resin described above as a binder resin for the charge generation layer, a polymer charge transport material having a charge transport function, such as an arylamine skeleton, benzidine skeleton, hydrazone skeleton, carbazole skeleton, stilbene skeleton, pyrazoline skeleton, etc. Polymer materials such as polycarbonate, polyester, polyurethane, polyether, polysiloxane, and acrylic resin, polymer materials having a polysilane skeleton, and the like can be used.

Specific examples of the former include JP-A-01-001728, JP-A-01-009964, JP-A-01-013061, JP-A-01-019049, JP-A-01-241559, Japanese Unexamined Patent Publication Nos. 04-011627, 04-175337, 04-183719, 04-2225014, 04-230767, 04-320420, 05 -232727, JP-A 05-310904, JP-A 06-234836, JP-A 06-234837, JP-A 06-234838, JP-A 06-234839, JP-A 06-234840. No. 1, JP-A 06-234841, JP-A 06-239049, Japanese Unexamined Patent Publication Nos. 06-236050, 06-236051, 06-295077, 07-0756374, 08-176293, 08-208820, 08 No. -21640, JP 08-253568, JP 08-269183, JP 09-062019, JP 09-043883, JP 09-71642, JP 09-87376. No. 1, JP-A 09-104746, JP 09-110974, JP 09-110976, JP 09-157378, JP 09-221544, JP 09-227669. JP 09-235367 A, JP 09-241369 A Charge transporting polymer materials described in JP 09-268226 A, JP 09-272735 A, JP 09-302084 A, JP 09-302085 A, JP 09-328539 A, etc. Can be mentioned.
Specific examples of the latter include polysilylene polymers described in, for example, JP-A No. 63-285552, JP-A No. 05-19497, JP-A No. 05-70595, JP-A No. 10-73944, and the like. Illustrated.

The charge generation layer (35) may contain a low molecular charge transport material.
Low molecular charge transport materials that can be used in combination with the charge generation layer (35) include hole transport materials and electron transport materials.
Examples of the electron transporting material include chloroanil, bromanyl, tetracyanoethylene, tetracyanoquinodimethane, 2,4,7-trinitro-9-fluorenone, 2,4,5,7-tetranitro-9-fluorenone, 2,4 , 5,7-tetranitroxanthone, 2,4,8-trinitrothioxanthone, 2,6,8-trinitro-4H-indeno [1,2-b] thiophen-4-one, 1,3,7-tri Examples thereof include electron-accepting substances such as nitrodibenzothiophene-5,5-dioxide and diphenoquinone derivatives. These electron transport materials can be used alone or as a mixture of two or more.

  Examples of the hole transporting material include the electron donating materials shown below and are used favorably. As hole transport materials, oxazole derivatives, oxadiazole derivatives, imidazole derivatives, monoarylamine derivatives, diarylamine derivatives, triarylamine derivatives, stilbene derivatives, α-phenylstilbene derivatives, benzidine derivatives, diarylmethane derivatives, triaryls Other known materials such as methane derivatives, 9-styrylanthracene derivatives, pyrazoline derivatives, divinylbenzene derivatives, hydrazone derivatives, indene derivatives, butadiene derivatives, pyrene derivatives, bisstilbene derivatives, enamine derivatives, and the like can be given. These hole transport materials can be used alone or as a mixture of two or more.

Methods for forming the charge generation layer (35) include a vacuum thin film preparation method and a casting method from a solution dispersion system.
As the former method, a vacuum deposition method, a glow discharge decomposition method, an ion plating method, a sputtering method, a reactive sputtering method, a CVD method, or the like is used, and the above-described inorganic materials and organic materials can be satisfactorily formed.
In addition, in order to provide a charge generation layer by the casting method described later, if necessary, the inorganic or organic charge generation material together with a binder resin, tetrahydrofuran, dioxane, dioxolane, toluene, dichloromethane, monochlorobenzene, dichloroethane, cyclohexanone, cyclohexane. Can be formed by dispersing with a ball mill, attritor, sand mill, bead mill, etc. using a solvent such as pentanone, anisole, xylene, methyl ethyl ketone, acetone, ethyl acetate, butyl acetate, etc. . Moreover, leveling agents, such as a dimethyl silicone oil and a methylphenyl silicone oil, can be added as needed. The coating can be performed using a dip coating method, spray coating, bead coating, ring coating method or the like.
The thickness of the charge generation layer provided as described above is suitably about 0.01 to 5 μm, preferably 0.05 to 2 μm.

(About charge transport layer)
The charge transport layer (37) is a layer having a charge transport function, and the crosslinked surface layer having the charge transport structure of the present invention is useful as a charge transport layer. When the cross-linked surface layer is the entire charge transport layer (37), the radical polymerizable composition (charge transport structure of the present invention is formed on the charge generation layer (35) as described in the above cross-linked surface layer preparation method. A coating solution containing a radically polymerizable monomer that does not have and a radically polymerizable compound having a monofunctional charge transporting structure; the same applies below) is applied, and if necessary, after drying, a curing reaction is initiated by external energy to cause crosslinking. A surface layer is formed. At this time, the film thickness of the crosslinked surface layer is 10 to 30 μm, preferably 10 to 25 μm. If it is thinner than 10 μm, a sufficient charging potential cannot be maintained, and if it is thicker than 30 μm, peeling from the lower layer tends to occur due to volume shrinkage during curing.
When the cross-linked surface layer is formed on the surface portion of the charge transport layer (37) and the charge transport layer (37) has a laminated structure, the lower layer portion of the charge transport layer has a charge transport material having a charge transport function and a binder. A resin is dissolved or dispersed in an appropriate solvent, and this is formed on the charge generation layer (35) by coating and drying, and a coating solution containing the radical polymerizable composition of the present invention is coated thereon. Then, it is crosslinked and cured by external energy.
As the charge transport material, the electron transport material, hole transport material and polymer charge transport material described in the charge generation layer (35) can be used. As described above, the use of the polymer charge transport material can reduce the solubility of the lower layer at the time of coating the surface layer, and is particularly useful.

Examples of the binder resin include polystyrene, styrene-acrylonitrile copolymer, styrene-butadiene copolymer, styrene-maleic anhydride copolymer, polyester, polyvinyl chloride, vinyl chloride-vinyl acetate copolymer, polyvinyl acetate, Polyvinylidene chloride, polyarylate resin, phenoxy resin, polycarbonate, cellulose acetate resin, ethyl cellulose resin, polyvinyl butyral, polyvinyl formal, polyvinyl toluene, poly-N-vinyl carbazole, acrylic resin, silicone resin, epoxy resin, melamine resin, urethane resin And thermoplastic or thermosetting resins such as phenol resins and alkyd resins.
The amount of the charge transport material is appropriately 20 to 300 parts by weight, preferably 40 to 150 parts by weight, based on 100 parts by weight of the binder resin. However, when a polymer charge transport material is used, it can be used alone or in combination with a binder resin.
As the solvent used for coating the lower layer portion of the charge transport layer, the same solvent as that for the charge generation layer can be used, but a solvent that dissolves the charge transport material and the binder resin well is suitable. These solvents may be used alone or in combination of two or more. The lower layer portion of the charge transport layer can be formed by a coating method similar to that for the charge generation layer (35).

If necessary, a plasticizer and a leveling agent can be added.
As a plasticizer that can be used in combination with the lower layer portion of the charge transport layer, those used as plasticizers for general resins such as dibutyl phthalate and dioctyl phthalate can be used as they are, and the amount used is 100 parts by weight of the binder resin. On the other hand, about 0 to 30 parts by weight is appropriate.
As a leveling agent that can be used in combination with the lower layer portion of the charge transport layer, silicone oils such as dimethyl silicone oil and methylphenyl silicone oil, and polymers or oligomers having a perfluoroalkyl group in the side chain are used. About 0 to 1 part by weight is appropriate for 100 parts by weight of the binder resin.
The thickness of the lower layer portion of the charge transport layer is appropriately about 5 to 40 μm, preferably about 10 to 30 μm.

  When the cross-linked surface layer is the surface portion of the charge transport layer (37), the radical polymerizable composition of the present invention is contained on the lower layer portion of the charge transport layer as described in the method for preparing a cross-linked surface layer. After the coating liquid is applied and dried as necessary, a curing reaction is initiated by external energy such as heat or light to form a crosslinked surface layer. At this time, the film thickness of the crosslinked surface layer is 1 to 20 μm, preferably 2 to 10 μm. When the thickness is less than 1 μm, the durability varies due to uneven film thickness, and when the thickness is more than 20 μm, the entire thickness of the charge transport layer is increased and the reproducibility of the image is deteriorated due to the diffusion of charges.

<Single photosensitive layer>
The photosensitive layer having a single layer structure is a layer having a charge generation function and a charge transport function at the same time, and the cross-linked surface layer having the charge transport structure of the present invention has a single layer structure by containing a charge generation material having a charge generation function. It is useful as a photosensitive layer. As described in the method for forming a charge generation layer, the charge generation material is dispersed together with a coating solution containing a radical polymerizable composition, applied onto the charge generation layer (35), and dried if necessary. The curing reaction is initiated by external energy, and a crosslinked surface layer is formed. In addition, you may add the liquid in which the charge generation material was previously disperse | distributed with the solvent to this coating material for bridge | crosslinking surface layers. At this time, the film thickness of the crosslinked surface layer is 10 to 30 μm, preferably 10 to 25 μm. If the thickness is less than 10 μm, a sufficient charging potential cannot be maintained. If the thickness is more than 30 μm, peeling from the conductive substrate or the undercoat layer tends to occur due to volume shrinkage during curing.

  Further, when the crosslinked surface layer is a surface portion of a photosensitive layer having a single layer structure, the lower layer portion of the photosensitive layer is composed of a charge generating material having a charge generating function, a charge transporting material having a charge transport function, and a binder resin in an appropriate solvent. It can be formed by dissolving or dispersing in, coating and drying. Moreover, a plasticizer, a leveling agent, etc. can also be added as needed. As the charge generation material dispersion method, the charge generation material, the charge transport material, the plasticizer, and the leveling agent may be the same as those already described in the charge generation layer (35) and the charge transport layer (37). As the binder resin, in addition to the binder resin previously mentioned in the section of the charge transport layer (37), the binder resin mentioned in the charge generation layer (35) may be mixed and used. In addition, the polymer charge transport materials listed above can also be used, which is useful in that contamination of the lower layer photosensitive layer composition into the crosslinked surface layer can be reduced. The thickness of the lower layer portion of the photosensitive layer is suitably about 5 to 30 μm, preferably about 10 to 25 μm.

  When the cross-linked surface layer is the surface portion of the photosensitive layer having a single layer structure, the coating solution containing the radical polymerizable composition of the present invention and the charge generating material is applied onto the lower layer portion of the photosensitive layer as described above. If necessary, after drying, it is cured by external energy such as heat or light to form a crosslinked surface layer. At this time, the film thickness of the crosslinked surface layer is 1 to 20 μm, preferably 2 to 10 μm. When the thickness is less than 1 μm, the durability varies due to the film thickness unevenness.

  The charge generation material contained in the photosensitive layer having a single layer structure is preferably 1 to 30% by weight based on the total amount of the photosensitive layer, and the binder resin contained in the lower layer portion of the photosensitive layer is 20 to 80% by weight of the total amount. The transport material is preferably used in an amount of 10 to 70 parts by weight.

<About the intermediate layer>
In the photoreceptor of the present invention, when the crosslinked surface layer becomes the surface portion of the photosensitive layer, it is possible to provide an intermediate layer for the purpose of suppressing mixing of lower layer components into the crosslinked surface layer or improving adhesion with the lower layer. is there. This intermediate layer prevents inhibition of the curing reaction and unevenness of the crosslinked surface layer caused by mixing of the lower photosensitive layer composition in the outermost surface layer containing the radical polymerizable composition. It is also possible to improve the adhesion between the lower photosensitive layer and the surface cross-linked layer.
In the intermediate layer, a binder resin is generally used as a main component. Examples of these resins include polyamide, alcohol-soluble nylon, water-soluble polyvinyl butyral, polyvinyl butyral, and polyvinyl alcohol. As a method for forming the intermediate layer, a generally used coating method is employed as described above. In addition, about 0.05-2 micrometers is suitable for the thickness of an intermediate | middle layer.

<About the undercoat layer>
In the photoreceptor of the present invention, an undercoat layer can be provided between the conductive support (31) and the photosensitive layer. In general, the undercoat layer is mainly composed of a resin. However, considering that the photosensitive layer is coated with a solvent on these resins, the resin may be a resin having high solvent resistance with respect to a general organic solvent. desirable. Examples of such resins include water-soluble resins such as polyvinyl alcohol, casein, and sodium polyacrylate, alcohol-soluble resins such as copolymer nylon and methoxymethylated nylon, polyurethane, melamine resin, phenol resin, alkyd-melamine resin, and epoxy. Examples thereof include a curable resin that forms a three-dimensional network structure such as a resin. Further, a metal oxide fine powder pigment exemplified by titanium oxide, silica, alumina, zirconium oxide, tin oxide, indium oxide and the like may be added to the undercoat layer in order to prevent moire and reduce residual potential.
These undercoat layers can be formed using an appropriate solvent and a coating method like the above-mentioned photosensitive layer. Furthermore, a silane coupling agent, a titanium coupling agent, a chromium coupling agent, or the like can be used as the undercoat layer of the present invention. In addition, in the undercoat layer of the present invention, Al ₂ O ₃ is provided by anodization, organic substances such as polyparaxylylene (parylene), SiO ₂ , SnO ₂ , TiO ₂ , ITO, CeO ₂ A material provided with an inorganic material such as a vacuum thin film can also be used favorably. In addition, known ones can be used. The thickness of the undercoat layer is suitably from 0 to 5 μm.

<Addition of antioxidant to each layer>
In the present invention, in order to improve environmental resistance, for the purpose of preventing a decrease in sensitivity and an increase in residual potential, a surface cross-linked layer, a photosensitive layer, a charge generation layer, a charge transport layer, an undercoat layer, an intermediate layer An antioxidant can be added to each layer such as a layer.

The following are mentioned as antioxidant which can be used for this invention.
(Phenolic compounds)
2,6-di-t-butyl-p-cresol, butylated hydroxyanisole, 2,6-di-t-butyl-4-ethylphenol, stearyl-β- (3,5-di-t-butyl-4 -Hydroxyphenyl) propionate, 2,2'-methylene-bis- (4-methyl-6-tert-butylphenol), 2,2'-methylene-bis- (4-ethyl-6-tert-butylphenol), 4, 4'-thiobis- (3-methyl-6-tert-butylphenol), 4,4'-butylidenebis- (3-methyl-6-tert-butylphenol), 1,1,3-tris- (2-methyl-4 -Hydroxy-5-t-butylphenyl) butane, 1,3,5-trimethyl-2,4,6-tris (3,5-di-t-butyl-4-hydroxybenzyl) benzene, tetrakis- [methylene- -(3 ', 5'-di-t-butyl-4'-hydroxyphenyl) propionate] methane, bis [3,3'-bis (4'-hydroxy-3'-t-butylphenyl) butyric acid ] Cryol ester, tocopherols and the like.

(Paraphenylenediamines)
N-phenyl-N'-isopropyl-p-phenylenediamine, N, N'-di-sec-butyl-p-phenylenediamine, N-phenyl-N-sec-butyl-p-phenylenediamine, N, N'- Di-isopropyl-p-phenylenediamine, N, N′-dimethyl-N, N′-di-t-butyl-p-phenylenediamine and the like.

(Hydroquinones)
2,5-di-t-octylhydroquinone, 2,6-didodecylhydroquinone, 2-dodecylhydroquinone, 2-dodecyl-5-chlorohydroquinone, 2-t-octyl-5-methylhydroquinone, 2- (2-octadecenyl) ) -5-methylhydroquinone and the like.

(Organic sulfur compounds)
Dilauryl-3,3′-thiodipropionate, distearyl-3,3′-thiodipropionate, ditetradecyl-3,3′-thiodipropionate, and the like.

(Organic phosphorus compounds)
Triphenylphosphine, tri (nonylphenyl) phosphine, tri (dinonylphenyl) phosphine, tricresylphosphine, tri (2,4-dibutylphenoxy) phosphine, and the like.
These compounds are known as antioxidants such as rubbers, plastics and fats and oils, and commercially available products can be easily obtained.
The addition amount of the antioxidant in the present invention is 0.01 to 10% by weight based on the total weight of the layer to be added.

<Image Forming Method and Apparatus>
Next, the image forming method and the image forming apparatus of the present invention will be described in detail with reference to the drawings.
The image forming method and the image forming apparatus of the present invention use a photoconductor having a smooth charge transporting surface cross-linked layer. An image forming method and an image forming apparatus including a process of transferring a toner image onto a body (transfer paper), fixing, and cleaning of the surface of a photoreceptor.
In some cases, an image forming method or the like in which an electrostatic latent image is directly transferred to a transfer member and developed does not necessarily have the above-described process arranged on a photosensitive member.

FIG. 3 is a schematic diagram illustrating an example of an image forming apparatus. A charging charger (3) is used as a means for charging the photoconductor on average. As the charging means, a corotron device, a scorotron device, a solid discharge element, a needle electrode device, a roller charging device, a conductive brush device, or the like is used, and a known system can be used.
In particular, the configuration of the present invention is effective when a charging unit such as a contact charging method or a non-contact proximity charging method is used that decomposes the photoreceptor composition by proximity discharge from the charging unit. The contact charging method referred to here is a charging method in which a charging roller, a charging brush, a charging blade, or the like is in direct contact with the photosensitive member. On the other hand, the proximity charging method is, for example, a type in which the charging roller is arranged in a non-contact state so as to have a gap of 200 μm or less between the surface of the photoreceptor and the charging means. If this gap is too large, the charging tends to become unstable, and if it is too small, the surface of the charging member may be contaminated when toner remaining on the photoreceptor exists. is there. Accordingly, the gap is suitably 10 to 200 μm, preferably 10 to 100 μm.
Next, the image exposure unit (5) is used to form an electrostatic latent image on the uniformly charged photoreceptor (1). As the light source, all luminescent materials such as a fluorescent lamp, a tungsten lamp, a halogen lamp, a mercury lamp, a sodium lamp, a light emitting diode (LED), a semiconductor laser (LD), and an electroluminescence (EL) can be used. Various types of filters such as a sharp cut filter, a band pass filter, a near infrared cut filter, a dichroic filter, an interference filter, and a color temperature conversion filter can be used to irradiate only light in a desired wavelength range.
Next, the developing unit (6) is used to visualize the electrostatic latent image formed on the photoreceptor (1). Development methods include a one-component development method using a dry toner, a two-component development method, and a wet development method using a wet toner. When the photosensitive member is positively (negatively) charged and image exposure is performed, a positive (negative) electrostatic latent image is formed on the surface of the photosensitive member. If this is developed with toner of negative (positive) polarity (detection fine particles), a positive image can be obtained, and if developed with toner of positive (negative) polarity, a negative image can be obtained.
Next, the transfer charger (10) is used to transfer the toner image visualized on the photosensitive member onto the transfer member (9). In addition, a pre-transfer charger (7) may be used for better transfer. As these transfer means, a transfer charger, an electrostatic transfer method using a bias roller, a mechanical transfer method such as an adhesive transfer method and a pressure transfer method, and a magnetic transfer method can be used. As the electrostatic transfer method, the charging means can be used.
Next, a separation charger (11) and a separation claw (12) are used as means for separating the transfer body (9) from the photoreceptor (1). As other separation means, electrostatic adsorption induction separation, side end belt separation, tip grip conveyance, curvature separation, and the like are used. As the separation charger (11), the charging means can be used.
Next, a fur brush (14) and a cleaning blade (15) are used to clean the toner remaining on the photoreceptor after transfer. Further, a pre-cleaning charger (13) may be used in order to perform cleaning more efficiently. Other cleaning means include a web method, a magnet brush method, and the like, but each may be used alone or in combination.
Next, a neutralizing unit is used for the purpose of removing the latent image on the photoreceptor as required. As the charge removal means, a charge removal lamp (2) and a charge removal charger are used, and the exposure light source and the charging means can be used respectively.
In addition, known processes can be used for reading, feeding, fixing, paper discharge and the like that are not close to the photoconductor.

The present invention is an image forming method and an image forming apparatus using the electrophotographic photoreceptor according to the present invention for such image forming means.
The image forming means may be fixedly incorporated in a copying apparatus, facsimile, or printer, but may be incorporated in these apparatuses in the form of a process cartridge and detachable. An example of the process cartridge is shown in FIG.
The process cartridge for the image forming apparatus includes a photoreceptor (101), and in addition, a charging unit (102), a developing unit (104), a transfer unit (106), a cleaning unit (107), and a discharging unit (not shown). ), And an apparatus (part) that can be attached to and detached from the image forming apparatus main body.
Referring to the image forming process by the apparatus illustrated in FIG. 4, the surface of the photoconductor (101) is exposed by charging by the charging means (102) and exposure by the exposure means (103) while rotating in the direction of the arrow. An electrostatic latent image corresponding to the image is formed, and the electrostatic latent image is developed with toner by the developing means (104). The toner development is transferred to the transfer body (105) by the transfer means (106), and printed. Out. Next, the surface of the photoconductor after the image transfer is cleaned by a cleaning unit (107), and further neutralized by a neutralizing unit (not shown), and the above operation is repeated again.
The present invention provides a process cartridge for an image forming apparatus in which a photoreceptor having a smooth charge transporting surface cross-linked layer and at least one of charging, developing, transferring, cleaning, and neutralizing means are integrated.
As is apparent from the above description, the electrophotographic photosensitive member of the present invention is not only used in electrophotographic copying machines, but also in electrophotographic application fields such as laser beam printers, CRT printers, LED printers, liquid crystal printers, and laser plate making. Can also be used widely.

<Synthesis example of compound having monofunctional charge transport structure>
The compound having a monofunctional charge transport structure in the present invention is synthesized, for example, by the method described in Japanese Patent No. 3164426. An example of this is shown below.
(1) Synthesis of hydroxy group-substituted triarylamine compound (the following structural formula B) 113.85 g (0.3 mol) of a methoxy group-substituted triarylamine compound (the following structural formula A) and 138 g (0.92 mol) of sodium iodide To this, 240 ml of sulfolane was added and heated to 60 ° C. in a nitrogen stream. In this solution, 99 g (0.91 mol) of trimethylchlorosilane was added dropwise over 1 hour and stirred at a temperature of about 60 ° C. for 4 and a half hours to complete the reaction. About 1.5 L of toluene was added to the reaction solution, cooled to room temperature, and washed repeatedly with water and an aqueous sodium carbonate solution. Thereafter, the solvent was removed from the toluene solution, and purification was performed by column chromatography (adsorption medium: silica gel, developing solvent: toluene: ethyl acetate = 20: 1). Cyclohexane was added to the obtained pale yellow oil to precipitate crystals. In this way, 88.1 g (yield = 80.4%) of white crystals of the following structural formula B was obtained.
Melting point: 64.0-66.0 ° C

(2) Triarylamino group-substituted acrylate compound (Exemplary Compound No. 54 in Table 1)
82.9 g (0.227 mol) of the hydroxy group-substituted triarylamine compound (Structural Formula B) obtained in (1) above was dissolved in 400 ml of tetrahydrofuran, and an aqueous sodium hydroxide solution (NaOH: 12.4 g, Water: 100 ml) was added dropwise. The solution was cooled to 5 ° C., and 25.2 g (0.272 mol) of acrylic acid chloride was added dropwise over 40 minutes. Then, it stirred at 5 degreeC for 3 hours, and reaction was complete | finished. The reaction solution was poured into water and extracted with toluene. This extract was repeatedly washed with an aqueous sodium bicarbonate solution and water. Thereafter, the solvent was removed from the toluene solution and purified by column chromatography (adsorption medium: silica gel, developing solvent: toluene). N-Hexane was added to the obtained colorless oil to precipitate crystals. In this way, Exemplified Compound No. As a result, 80.73 g (yield = 84.8%) of 54 white crystals were obtained.
Melting point: 117.5-119.0 ° C

EXAMPLES Next, although an Example demonstrates this invention further in detail, this invention is not limited to a following example. Note that “parts” used in the examples all represent parts by weight.
<Example 1>
By coating and drying an undercoat layer coating solution, a charge generation layer coating solution, and a charge transport layer coating solution in the following order on a φ30 mm aluminum cylinder in sequence, an undercoat layer of 3.5 μm A 0.2 μm charge generation layer and an 18 μm charge transport layer were formed. On this charge transport layer, a coating solution for a crosslinked surface layer having the following composition is spray-coated, under conditions of metal halide lamp: 160 W / cm, irradiation distance: 120 mm, irradiation intensity: 500 mW / cm ² , irradiation time: 30 seconds. This was irradiated with light, and further dried at 130 ° C. for 20 minutes to provide a 4 μm surface cross-linked layer to obtain the electrophotographic photoreceptor of the present invention.
[Coating liquid for undercoat layer]
Alkyd resin 6 parts (Beckosol 1307-60-EL, manufactured by Dainippon Ink & Chemicals, Inc.)
Melamine resin 4 parts (Super Becamine G-821-60, manufactured by Dainippon Ink & Chemicals, Inc.)
Titanium oxide 40 parts Methyl ethyl ketone 50 parts [Coating liquid for charge generation layer]
Bisazo pigment pigment of the following structural formula (I) 2.5 parts Polyvinyl butyral (XYHL, manufactured by UCC) 0.5 part Cyclohexanone 200 parts Methyl ethyl ketone 80 parts

〔電荷輸送層用塗工液〕
ビスフェノールＺポリカーボネート １０部
（パンライトＴＳ−２０５０、帝人化成製）
下記構造式（II）の低分子電荷輸送物質（Ｄ−１） ７部
テトラヒドロフラン １００部
１％シリコーンオイルのテトラヒドロフラン溶液 ０．２部
（ＫＦ５０−１００ＣＳ、信越化学工業製）

[Coating liquid for charge transport layer]
Bisphenol Z polycarbonate 10 parts (Panlite TS-2050, manufactured by Teijin Chemicals)
Low molecular charge transport material (D-1) having the following structural formula (II) 7 parts Tetrahydrofuran 100 parts 1% silicone oil tetrahydrofuran solution 0.2 part (KF50-100CS, manufactured by Shin-Etsu Chemical Co., Ltd.)

〔架橋表面層用塗工液〕
電荷輸送性構造を有さない３官能以上のラジカル重合性モノマー １０部
トリメチロールプロパントリアクリレート
（ＫＡＹＡＲＡＤ ＴＭＰＴＡ、日本化薬製）
分子量：２９６、官能基数：３官能、分子量／官能基数＝９９
１官能の電荷輸送性構造を有するラジカル重合性化合物 １０部
（例示化合物Ｎｏ．５４）
光重合開始剤 ２部
１−ヒドロキシ−シクロヘキシル−フェニル−ケトン
（イルガキュア１８４、チバ・スペシャルティ・ケミカルズ製）
テトラヒドロフラン １００部

[Coating liquid for cross-linked surface layer]
Trifunctional or higher-functional radical polymerizable monomer having no charge transporting structure 10 parts Trimethylolpropane triacrylate (KAYARAD TMPTA, Nippon Kayaku)
Molecular weight: 296, number of functional groups: trifunctional, molecular weight / number of functional groups = 99
10 parts of a radically polymerizable compound having a monofunctional charge transporting structure (Exemplary Compound No. 54)
Photoinitiator 2 parts 1-hydroxy-cyclohexyl-phenyl-ketone (Irgacure 184, manufactured by Ciba Specialty Chemicals)
Tetrahydrofuran 100 parts

<Example 2>
An electrophotographic photoreceptor in the same manner as in Example 1 except that the trifunctional or higher functional radical-polymerizable monomer having no charge transporting structure contained in the crosslinked surface layer coating solution of Example 1 is replaced with the following monomer. Was made.
Trifunctional or higher radical polymerizable monomer having no charge transporting structure 10 parts Ditrimethylolpropane tetraacrylate (SR-355, manufactured by Kayaku Sartomer)
Molecular weight: 466, number of functional groups: 4 functions, molecular weight / number of functional groups = 117

<Example 3>
Except that the tri- or higher functional radical polymerizable monomer having no charge transporting structure contained in the coating solution for the crosslinked surface layer of Example 1 was replaced with the following monomer and the photopolymerization initiator was replaced with the following compound. An electrophotographic photosensitive member was produced in the same manner as in Example 1.
Trifunctional or higher functional radical polymerizable monomer having no charge transport structure 10 parts Pentaerythritol tetraacrylate (SR-295, manufactured by Kayaku Sartomer)
Molecular weight: 352, number of functional groups: 4 functions, molecular weight / number of functional groups = 88
Photoinitiator 2 parts 2,2-dimethoxy-1,2-diphenylethane-1-one (Irgacure 651, manufactured by Ciba Specialty Chemicals)

<Example 4>
Electrons in the same manner as in Example 1 except that the tri- or higher functional radical polymerizable monomer having no charge transporting structure contained in the crosslinked surface layer coating liquid of Example 1 was replaced with the following two mixed monomers. A photoconductor was prepared.
Trifunctional or higher radical polymerizable monomer having no charge transport structure 5 parts Dipentaerythritol hexaacrylate (KAYARAD DPHA, Nippon Kayaku)
Molecular weight: 536, number of functional groups: 5.5 functional, molecular weight / number of functional groups = 97
Trifunctional or higher functional radical polymerizable monomer having no charge transport structure 5 parts Dipentaerythritol caprolactone-modified hexaacrylate (KAYARAD DPCA-60, manufactured by Nippon Kayaku Co., Ltd.)
Molecular weight: 1263, number of functional groups: 6 functions, molecular weight / number of functional groups = 211

<Example 5>
An electrophotographic photoreceptor in the same manner as in Example 1 except that the trifunctional or higher functional radical-polymerizable monomer having no charge transporting structure contained in the crosslinked surface layer coating solution of Example 1 is replaced with the following monomer. Was made.
Trifunctional or higher functional radical polymerizable monomer having no charge transporting structure 10 parts Dipentaerythritol caprolactone-modified hexaacrylate (KAYARAD DPCA-60, Nippon Kayaku)
Molecular weight: 1263, number of functional groups: 6 functions, molecular weight / number of functional groups = 211

<Example 6>
An electrophotographic photoreceptor in the same manner as in Example 1 except that the trifunctional or higher functional radical-polymerizable monomer having no charge transporting structure contained in the crosslinked surface layer coating solution of Example 1 is replaced with the following monomer. Was made.
Trifunctional or higher functional radical polymerizable monomer having no charge transporting structure 10 parts Dipentaerythritol caprolactone-modified hexaacrylate (KAYARAD DPCA-120, manufactured by Nippon Kayaku Co., Ltd.)
Molecular weight: 1947, number of functional groups: 6 functions, molecular weight / number of functional groups = 325

<Example 7>
Electrons in the same manner as in Example 1 except that the tri- or higher functional radical polymerizable monomer having no charge transporting structure contained in the crosslinked surface layer coating liquid of Example 1 was replaced with the following two mixed monomers. A photoconductor was prepared.
Trifunctional or higher radical polymerizable monomer having no charge transport structure 5 parts Dipentaerythritol hexaacrylate (KAYARAD DPHA, Nippon Kayaku)
Average molecular weight: 536, number of functional groups: 5.5 functional, molecular weight / number of functional groups = 97
Trifunctional or higher functional radical polymerizable monomer having no charge transport structure 5 parts Glycerol PO-modified triacrylate (KAYARAD FM-280, manufactured by Nippon Kayaku)
Molecular weight: 463, number of functional groups: trifunctional, molecular weight / number of functional groups = 154

<Example 8>
The radical polymerizable compound having a monofunctional charge transporting structure contained in the crosslinked surface layer coating solution of Example 1 is exemplified as Compound No. 1. An electrophotographic photosensitive member was produced in the same manner as in Example 1 except that 127 parts and 10 parts were used.

<Example 9>
The radical polymerizable monomer having a monofunctional charge transporting structure is replaced with the following monomer instead of the trifunctional radical polymerizable monomer having no charge transporting structure contained in the coating solution for the crosslinked surface layer of Example 1. The compounds were designated as Exemplified Compound Nos. An electrophotographic photosensitive member was produced in the same manner as in Example 1 except that 138 and 10 parts were used.
Trifunctional or higher radical polymerizable monomer having no charge transport structure 10 parts Dipentaerythritol hexaacrylate (KAYARAD DPHA, Nippon Kayaku)
Average molecular weight: 536, number of functional groups: 5.5 functional, molecular weight / number of functional groups = 97

<Example 10>
The radical polymerizable compound having a monofunctional charge transporting structure contained in the crosslinked surface layer coating solution of Example 1 is exemplified as Compound No. 1. 94 and 10 parts, the photopolymerization initiator was changed to the following thermal polymerization initiator, coated on the charge transport layer in the same manner, heated at 70 ° C. for 30 minutes using a blow-type oven, and further heated at 150 ° C. for 1 hour. A 4 μm cross-linked surface layer was provided to obtain a photoreceptor of the present invention.
Thermal polymerization initiator 1 part 2,2-bis (4,4-di-t-butylperoxycyclohexyl) propane (Perkadox 12-EB20, manufactured by Kayaku Akzo)

<Example 11>
The radical polymerizable compound having a monofunctional charge transporting structure contained in the crosslinked surface layer coating liquid of Example 10 was exemplified as Compound No. 1. An electrophotographic photosensitive member was produced in the same manner as in Example 10 except that 138 and 10 parts were used.

<Example 12>
6 parts of the amount of a tri- or more functional radical polymerizable monomer having no charge transporting structure contained in the coating solution for a crosslinked surface layer of Example 1 and the amount of the radical polymerizable compound having a monofunctional charge transporting structure An electrophotographic photosensitive member was produced in the same manner as in Example 1 except that was changed to 14 parts.

<Example 13>
14 parts of the amount of a tri- or more functional radical polymerizable monomer having no charge transporting structure contained in the outermost surface layer coating liquid of Example 1 and the amount of the radical polymerizable compound having a monofunctional charge transporting structure An electrophotographic photosensitive member was produced in the same manner as in Example 1 except that was changed to 6 parts.

<Example 14>
A liquid containing a polymer charge transport material (PD-1) having the following composition was used as the charge transport layer coating liquid of Example 1 and applied to a similar charge generation layer and dried to form an 18 μm charge transport layer. Formed. A surface cross-linked layer was provided on the charge transport layer in the same manner as in Example 1 to produce an electrophotographic photoreceptor.
[Coating liquid for charge transport layer]
Polymer charge transport material (PD-1) having the following structural formula: 15 parts

テトラヒドロフラン １００部
１％シリコーンオイルのテトラヒドロフラン溶液 ０．３部
（ＫＦ５０−１００ＣＳ、信越化学工業製）

Tetrahydrofuran 100 parts 1% silicone oil tetrahydrofuran solution 0.3 parts (KF50-100CS, manufactured by Shin-Etsu Chemical Co., Ltd.)

<Example 15>
On the charge generation layer of Example 1, a 22 μm cross-linked surface layer was provided in the same manner as in Example 1 except that the coating liquid for the cross-linked surface layer having the following composition was spray-coated and the light irradiation time was 40 seconds. A photoreceptor of the present invention was produced.
[Coating liquid for cross-linked surface layer]
Trifunctional or higher functional radical polymerizable monomer having no charge transporting structure 10 parts Dipentaerythritol caprolactone-modified hexaacrylate (KAYARAD DPCA-60, Nippon Kayaku)
Molecular weight: 1263, number of functional groups: 6 functions, molecular weight / number of functional groups = 211
10 parts of a radically polymerizable compound having a monofunctional charge transporting structure (Exemplary Compound No. 54)
Photoinitiator 2 parts 1-hydroxy-cyclohexyl-phenyl-ketone (Irgacure 184, manufactured by Ciba Specialty Chemicals)
Tetrahydrofuran 60 parts Cyclohexanone 20 parts 1% silicone oil in tetrahydrofuran 0.2 parts (KF50-100CS, manufactured by Shin-Etsu Chemical Co., Ltd.)

<Comparative Example 1>
An electrophotographic photosensitive member was produced in the same manner as in Example 1 except that the coating solution for the crosslinked surface layer of Example 1 was changed to the following composition.
[Coating liquid for cross-linked surface layer]
Trifunctional or higher-functional radical polymerizable monomer having no charge transporting structure 8 parts Trimethylolpropane triacrylate (KAYARAD TMPTA, manufactured by Nippon Kayaku Co., Ltd.)
Molecular weight: 296, number of functional groups: trifunctional, molecular weight / number of functional groups = 99
Polymer part 2 parts Bisphenol A polycarbonate (Panlite C1400, manufactured by Teijin Chemicals)
10 parts of a radically polymerizable compound having a monofunctional charge transporting structure (Exemplary Compound No. 54)
Photoinitiator 2 parts 1-hydroxy-cyclohexyl-phenyl-ketone (Irgacure 184, manufactured by Ciba Specialty Chemicals)
Tetrahydrofuran 100 parts

<Comparative example 2>
The radical polymerizable compound having a monofunctional charge transporting structure contained in the crosslinked surface layer coating liquid of Example 1 is replaced with 10 parts of the radical polymerizable compound having a bifunctional charge transporting structure of the following structural formula. An electrophotographic photosensitive member was produced in the same manner as in Example 1 except that.
10 parts of a radically polymerizable compound having a bifunctional charge transporting structure

<Comparative Example 3>
The trifunctional or higher functional radical polymerizable monomer having no charge transporting structure contained in the coating solution for the crosslinked surface layer of Example 1 is a bifunctional radical polymerizable having no charge transporting structure of the following structural formula. An electrophotographic photosensitive member was produced in the same manner as in Example 1 except that 10 parts of the monomer was used.
Bifunctional radically polymerizable monomer having no charge transporting structure 10 parts 1,6-hexanediol diacrylate (manufactured by Wako Pure Chemical Industries, Ltd.)
Molecular weight: 226, number of functional groups: bifunctional, molecular weight / number of functional groups = 113

<Comparative example 4>
A radical polymerizable compound having a monofunctional charge transport structure without containing a trifunctional or higher functional radical polymerizable monomer having no charge transport structure, which is a composition of the coating liquid for a crosslinked surface layer of Example 1. An electrophotographic photosensitive member was produced in the same manner as in Example 1 except that the amount was changed to 20 parts.

<Comparative Example 5>
A trifunctional or higher functional radical polymerizable monomer having no charge transporting structure and not containing a monofunctional charge transporting structure, which is the composition of the coating liquid for the crosslinked surface layer of Example 1. An electrophotographic photosensitive member was produced in the same manner as in Example 1 except that the amount was changed to 20 parts.

<Comparative Example 6>
The structure used in the coating solution for the charge transport layer instead of the radically polymerizable compound having a monofunctional charge transporting structure which is the composition of the coating solution for the crosslinked surface layer of Example 1 An electrophotographic photosensitive member was produced in the same manner as in Example 1 except that 10 parts of the low molecular charge transport material (D-1) of the formula (II) was contained.

<Comparative Example 7>
An electrophotographic photoreceptor was prepared in the same manner as in Example 1 except that the solvent tetrahydrofuran contained in the crosslinked surface layer coating solution of Example 8 was changed to 80 parts of butanol.

<Comparative Example 8>
4 μm cross-linked surface in the same manner as in Example 1 except that the curing conditions in the surface layer of Example 1 were changed using the same light source as in Example 1 and irradiation intensity of 1500 mW / cm ² and irradiation time: 5 seconds. An electrophotographic photosensitive member was prepared by providing a layer.

<Comparative Example 9>
An electrophotographic photosensitive member was prepared by providing a 4 μm crosslinked surface layer in the same manner as in Example 8 except that the curing condition of the surface layer of Example 10 was heated at 180 ° C. for 1 hour.

<Comparative Example 10>
An electrophotographic photosensitive member was produced in the same manner as in Example 1 except that the cross-linked surface layer of Example 1 was not provided and the thickness of the charge transport layer was 22 μm.

About the electrophotographic photoreceptors of Examples 1 to 15 and Comparative Examples 1 to 10 manufactured as described above, Surfcom 1400D (manufactured by Tokyo Seimitsu) was used, and surface roughness Rz (ten-point average roughness, JIS B0601-1994 standard). ) Was measured for an evaluation length of 2.5 mm and a reference length of 0.5 mm. The measurement points were 50 mm from both ends of the drum in the axial direction, three points in the center of the drum, and four ways of 90 degrees in the circumferential direction. A total of 12 points were measured, and the average value was defined as the surface roughness Rz of the drum. The results are shown in Table 4.
Moreover, about the electrophotographic photoconductor of Examples 1-15 and Comparative Examples 1-10 produced similarly, the paper passing test of 30,000 sheets of A4 size was implemented. First, the photosensitive member was mounted on a process cartridge for an electrophotographic apparatus, and the initial dark portion potential was set to −700 V with a Ricoh imago Neo Neo 270 remodeling machine using a 655 nm semiconductor laser as an image exposure light source. Thereafter, a paper passing test was started, and image evaluation for each initial and every 5,000 sheets was performed, and darkness and exposed area potentials after the initial and 30,000 copies were measured, and the film thickness reduction after 30,000 copies were measured. The results are shown in Table 4. Note that the paper passing test was stopped for the photoconductor having a remarkable image defect from the beginning.

比較例１、６は測定位置による膜厚減少量の差が非常に大きい。比較例４は表面層が硬化していない。
表４の通紙試験結果より、実施例１〜１５で示される本発明の架橋表面層を有する感光体は耐摩耗性が高く、且つ良好な電気的特性を有し、経時において良好な画像が得られる。一方、比較例１、７〜９の架橋表面層成分組成や硬化条件により架橋表面層の表面粗さＲｚが１．３μｍ以上の感光体は、初期または経時で画像不良を発生する。また、比較例２〜６のラジカル重合性組成物が本発明と異なる感光体は、表面の均一性、耐摩耗性または電気的特性が劣り、いずれも耐久性が低い。比較例１０の電荷輸送層に従来の熱可塑性バインダー樹脂を用いた感光体は、本発明の感光体に比べ耐摩耗性が低く、耐久性が劣る。

In Comparative Examples 1 and 6, the difference in film thickness reduction amount depending on the measurement position is very large. In Comparative Example 4, the surface layer is not cured.
From the results of the paper passing test shown in Table 4, the photoreceptors having the crosslinked surface layers of the present invention shown in Examples 1 to 15 have high wear resistance and good electrical characteristics, and a good image with time. can get. On the other hand, a photoreceptor having a surface roughness Rz of 1.3 μm or more of the crosslinked surface layer due to the composition and curing conditions of the crosslinked surface layer components of Comparative Examples 1 and 7 to 9 causes image defects at the initial stage or over time. Further, the photoconductors having different radical polymerizable compositions of Comparative Examples 2 to 6 from the present invention are inferior in surface uniformity, wear resistance or electrical characteristics, and all have low durability. A photoreceptor using a conventional thermoplastic binder resin for the charge transport layer of Comparative Example 10 has lower wear resistance and inferior durability than the photoreceptor of the present invention.

<Example 16>
A photoreceptor manufactured in the same manner as in Example 1 was manufactured using a remodeled imgio MF200 machine (written LD wavelength: 655 nm, AC superimposed charging: amplitude 2 KV, frequency 1 KHz, DC voltage −750 V), temperature 22 ° C., humidity 55% environment. Then, 2000 continuous A4 horizontal charts with an image area of 1% were copied. Thereafter, the photoreceptor and the copying machine were moved to an environment of a temperature of 30 ° C. and a relative humidity of 90%, and an image was output and compared with an initial image. As a result, it was possible to obtain a good image with no resolution reduction and character thickening equivalent to the initial image.

<Comparative Example 11>
A photoconductor produced in the same manner as in Comparative Example 1 was tested in the same manner as in Example 16, and an image at a temperature of 30 ° C. and a humidity of 90% was compared with an initial image. As a result, as compared with the initial image, an extremely low resolution and a halftone image of the image having a temperature of 30 ° C. and a humidity of 90% were recognized.

  The photoconductor having the cross-linked surface layer of Example 16 of the present invention has a cross-linked surface that removes the oxidizing gas generated from the charger and the deteriorated surface of the photoconductor surface as compared with the photoconductor having the uneven surface of the cross-linked surface of Comparative Example 11. Can be maintained at a high resistance, and a good image can be stably obtained even in a high humidity environment.

  Therefore, the outermost surface layer of the photosensitive layer of the present invention is coated with a coating solution containing a tri- or higher functional radical polymerizable monomer having no charge transport structure and a radical polymerizable compound having a monofunctional charge transport structure. A long-life and high-performance photoreceptor capable of maintaining a good image for a long period of time without being subjected to environmental fluctuations by comprising a cured crosslinked layer and having a surface roughness Rz of 1.3 μm or less of the crosslinked surface layer. It turns out that it can provide. In addition, it has been found that the image forming process, the image forming apparatus, and the process cartridge for the image forming apparatus using the photoconductor of the present invention have high performance and high reliability.

1 is an example of a cross-sectional view of an electrophotographic photosensitive member of the present invention. It is another example of sectional drawing of the electrophotographic photosensitive member of this invention. 1 is a schematic diagram illustrating an example of an image forming apparatus of the present invention. FIG. 2 is a schematic diagram illustrating an example of a process cartridge for an image forming apparatus according to the present invention.

Explanation of symbols

DESCRIPTION OF SYMBOLS 1 Photoconductor 2 Static elimination lamp 3 Charger 4 Eraser 5 Image exposure part 6 Development unit 7 Pre-transfer charger 8 Registration roller 9 Transfer paper 10 Transfer charger 11 Separation charger 12 Separation claw 13 Pre-cleaning charger 14 Fur brush 15 Cleaning blade 31 Conductivity Support 33 Photosensitive layer 35 Charge generation layer 37 Charge transport layer 101 Photosensitive drum 102 Charging device 103 Exposure device 104 Development device 105 Transfer body 106 Transfer device 107 Cleaning blade

Claims (16)

An electrophotographic photoreceptor having at least a photosensitive layer on a conductive support, wherein the crosslinked surface layer of the photoreceptor has a trifunctional or higher-functional radical polymerizable monomer having no charge transporting structure and a monofunctional charge. A surface roughness Rz of 1.3 μm or less formed by crosslinking and curing a coating film containing a radically polymerizable compound having a transporting structure and a polymerization initiator and not containing a filler by light irradiation or heat. The electrophotographic photosensitive member is characterized in that the coating film contains a solvent that dissolves the lower layer of the crosslinked surface layer . The electrophotographic photosensitive member according to claim 1, wherein the cross-linked surface layer has a surface roughness Rz of 1.0 μm or less. The functional group of a tri- or more functional radical polymerizable monomer having no charge transporting structure used for the surface layer is an acryloyloxy group and / or a methacryloyloxy group. Electrophotographic photoreceptor. The ratio of the molecular weight to the number of functional groups (molecular weight / number of functional groups) in a trifunctional or higher functional radical polymerizable monomer having no charge transporting structure used for the surface layer is 250 or less. The electrophotographic photosensitive member according to any one of the above. 5. The electron according to claim 1, wherein the functional group of the radical polymerizable compound having a monofunctional charge transporting structure used for the surface layer is an acryloyloxy group or a methacryloyloxy group. Photoconductor. 6. The electrophotography according to claim 1, wherein the charge transport structure of the radical polymerizable compound having a monofunctional charge transport structure used for the outermost surface layer is a triarylamine structure. Photoconductor. The radical polymerizable compound having a monofunctional charge transporting structure used for the surface layer is one or more of the following general formula (1) or (2): The electrophotographic photosensitive member described.

(In the formula, R ₁ represents a hydrogen atom, a halogen atom, an alkyl group which may have a substituent, an aralkyl group which may have a substituent, an aryl group which may have a substituent, a cyano group, a nitro group, Group, alkoxy group, —COOR ₇ (R ₇ is a hydrogen atom, an alkyl group which may have a substituent, an aralkyl group which may have a substituent or an aryl group which may have a substituent), halogen Carbonyl group or CONR ₈ R ₉ (R ₈ and R ₉ may have a hydrogen atom, a halogen atom, an alkyl group which may have a substituent, an aralkyl group which may have a substituent, or a substituent. Ar ₁ and Ar ₂ each represent a substituted or unsubstituted arylene group, and may be the same or different.Ar ₃ , which may be the same or different from each other. Ar ₄ may be substituted Represents an unsubstituted aryl group, which may be the same or different, X represents a single bond, a substituted or unsubstituted alkylene group, a substituted or unsubstituted cycloalkylene group, a substituted or unsubstituted alkylene ether group, O represents an oxygen atom, a sulfur atom, or a vinylene group, Z represents a substituted or unsubstituted alkylene group, a substituted or unsubstituted alkylene ether divalent group, or an alkyleneoxycarbonyl divalent group, and m and n are integers of 0 to 3. Represents.) The electrophotographic image according to any one of claims 1 to 7, wherein the radical polymerizable compound having a monofunctional charge transporting structure used in the surface layer is one or more of the following general formula (3). Photoconductor.

(Wherein, o, p and q are each an integer of 0 or 1, Ra represents a hydrogen atom or a methyl group, Rb and Rc represent a substituent other than a hydrogen atom and an alkyl group having 1 to 6 carbon atoms, And s and t each represents an integer of 0 to 3. Za is a single bond, a methylene group, an ethylene group,

Represents. ) 9. The component ratio of a tri- or higher functional radical polymerizable monomer having no charge transport structure used for the surface layer is 30 to 70% by weight based on the total amount of the crosslinked surface layer. The electrophotographic photosensitive member according to any one of the above. The component ratio of the radically polymerizable compound having a monofunctional charge transporting structure used for the surface layer is 30 to 70% by weight based on the total amount of the crosslinked surface layer. The electrophotographic photoreceptor described in 1. 11. The electrophotographic photosensitive member according to claim 1, wherein the photosensitive layer has a laminated structure of a charge generation layer, a charge transport layer, and a crosslinked surface layer from the support side. 12. The electrophotographic photoreceptor according to claim 11, wherein the charge transport layer of the photosensitive layer contains a polymer charge transport material. 13. The electrophotographic photoreceptor according to claim 12, wherein the polymer charge transport material is a polycarbonate having a triarylamine structure in the main chain or side chain. Using an electrophotographic photosensitive member according to any one of claims 1 to 13, at least charging, image exposure, development, image forming method characterized by repeating the transfer. An image forming apparatus, comprising an electrophotographic photosensitive member according to any one of claims 1 to 13. An electrophotographic photosensitive member according to any one of claims 1 to 13 , and at least one means selected from the group consisting of a charging means, a developing means, a transfer means, a cleaning means, and a charge eliminating means, A process cartridge for an image forming apparatus, wherein the process cartridge is removable from a main body of the forming apparatus.