JP3014685B1 - Multi-layer wrapping paper - Google Patents
Multi-layer wrapping paperInfo
- Publication number
- JP3014685B1 JP3014685B1 JP10363333A JP36333398A JP3014685B1 JP 3014685 B1 JP3014685 B1 JP 3014685B1 JP 10363333 A JP10363333 A JP 10363333A JP 36333398 A JP36333398 A JP 36333398A JP 3014685 B1 JP3014685 B1 JP 3014685B1
- Authority
- JP
- Japan
- Prior art keywords
- film
- layer
- wrapping paper
- laminate layer
- sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
【要約】
【課題】 一度のラミネート加工で製造が可能であり、
巻き取りや包装が容易な多層構造包装紙の提供を目的と
する。
【解決手段】 基材シート２と、基材シート２に積層さ
れた合成樹脂製のラミネート層３と、フィルム４とを有
し、ラミネート層３とフィルム４とが部分接着状態で密
に積層されている多層構造包装紙１である。上記部分接
着状態を獲得する手段として、ラミネート層３及びフィ
ルム４間に目抜け部分６を有する目抜けシート５を挿入
する方法、フィルムの積層面に接着抑止剤又は接着促進
剤を部分的にコーティングする方法、隙間を開けて平行
に配設した複数の帯状シートをラミネート層３及びフィ
ルム４間に挿入する方法がある。Abstract: [Problem] It is possible to manufacture by one lamination process,
An object of the present invention is to provide a multi-layer wrapping paper that can be easily wound and wrapped. SOLUTION: It has a base sheet 2, a synthetic resin laminate layer 3 laminated on the base sheet 2, and a film 4, and the laminate layer 3 and the film 4 are densely laminated in a partially bonded state. This is a multi-layered wrapping paper 1. As a means for obtaining the above partially adhered state, a method of inserting a blank sheet 5 having a blank portion 6 between the laminate layer 3 and the film 4, and partially coating a laminated surface of the film with an adhesion inhibitor or an adhesion promoter. And a method of inserting a plurality of strip-shaped sheets arranged in parallel with a gap between the laminate layer 3 and the film 4.
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、例えば鉄鋼コイル
の包装に好適な多層構造包装紙に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a multi-layer wrapping paper suitable for, for example, wrapping steel coils.
【０００２】[0002]
【従来の技術】上記鉄鋼コイルなどの包装紙としては、
従来、図４（ａ）および（ｂ）に示すような多層構造包
装紙３１、４１が使用されている。図４（ａ）の多層構
造包装紙３１は、基材シート３２、ラミネート層３３お
よびフィルム３４からなり、基材シート３２およびラミ
ネート層３３が積層されたＡ層とフィルム３４のＢ層と
が線状の接着剤層３５により部分的に接着されている。
また図４（ｂ）の多層構造包装紙４１は、上記（ａ）の
多層構造包装紙３１のＡ層に補強材４６を加え、この補
強材４６とフィルム４４が線状の接着剤層４５により部
分的に接着されている。2. Description of the Related Art As wrapping paper for the above-mentioned steel coils and the like,
Conventionally, multi-layer wrapping papers 31 and 41 as shown in FIGS. 4A and 4B are used. 4A includes a base sheet 32, a laminate layer 33, and a film 34. The A layer on which the base sheet 32 and the laminate layer 33 are laminated and the B layer of the film 34 are linear. It is partially adhered by an adhesive layer 35 in a shape.
Further, in the multilayer wrapping paper 41 of FIG. 4B, a reinforcing material 46 is added to the layer A of the multilayer wrapping paper 31 of FIG. 4A, and the reinforcing material 46 and the film 44 are formed by a linear adhesive layer 45. Partially glued.
【０００３】上記Ａ層とＢ層の部分接着方法としては、
ホットメルト接着剤を両層間に線状に配設、塗布する方
法や、両層間に合成樹脂を線状に押出ラミネート加工す
る方法がある。[0003] As a method of partially bonding the A layer and the B layer,
There is a method in which a hot melt adhesive is linearly arranged and applied between both layers, and a method in which a synthetic resin is linearly extruded and laminated between both layers.
【０００４】上述の多層構造包装紙は、上記Ａ層とＢ層
とを合わせた強度と防湿性を有し、鉄鋼コイルなどの包
装として必要な機能を確保することで、Ａ層のみからな
る包装紙とＢ層のみからなる包装紙とによる別々の包装
作業を当該多層構造包装紙による一度の包装作業で済ま
せることを目的とする。また上記多層構造包装紙は、Ａ
層とＢ層とを全面的に接着せず、部分的に接着すること
で、両層が同時に破れてしまうことや、コシが強くなり
すぎて包装作業が困難になることなどを防止している。[0004] The above-mentioned multilayer wrapping paper has the strength and moisture-proofness of the combined A layer and B layer, and secures the functions required for the wrapping of a steel coil or the like. It is an object of the present invention to perform separate wrapping work using paper and wrapping paper consisting of only the B layer by a single wrapping work using the multilayer wrapping paper. In addition, the above-mentioned multilayer wrapping paper has A
The layer and the B layer are not completely adhered but are partially adhered, thereby preventing both layers from being torn at the same time, and preventing the packaging work from becoming too strong to make the packaging work difficult. .
【０００５】[0005]
【発明が解決しようとする課題】上記従来の多層構造包
装紙３１、４１を製造するには、Ａ層を構成する基材シ
ート３２およびラミネート層３３（図４（ａ））又は基
材シート４２、ラミネート層４３および補強材４６（図
４（ｂ））を積層する工程と、Ａ層とＢ層とを部分的に
接着する工程との２工程が必要であり、手間がかかって
いた。In order to manufacture the above-mentioned conventional multi-layer wrapping papers 31 and 41, the base sheet 32 and the laminate layer 33 (FIG. 4A) constituting the A layer or the base sheet 42 are formed. And a step of laminating the laminate layer 43 and the reinforcing material 46 (FIG. 4B) and a step of partially bonding the A layer and the B layer, which are troublesome.
【０００６】また上記従来の多層構造包装紙３１、４１
は、Ａ層とＢ層とが接着剤層３５、４５を介し、微妙に
離隔して積層されていることから、両層間には空間３
７、４７が形成され易い。そのため、当該多層構造包装
紙３１、４１をコンパクトに巻き取ることが困難であ
り、ぴったり包装することが難しい。Further, the above-mentioned conventional multi-layer wrapping paper 31, 41
Is that the layer A and the layer B are delicately laminated with the adhesive layers 35 and 45 interposed therebetween, so that a space 3 is provided between the two layers.
7, 47 are easily formed. Therefore, it is difficult to wind up the multilayer wrapping paper 31 and 41 compactly, and it is difficult to wrap the wrapping paper 31 and 41 tightly.
【０００７】本発明はこれらの不都合に鑑みてなされた
ものであり、一度のラミネート加工で製造が可能であ
り、巻き取りや包装が容易な多層構造包装紙の提供を目
的とするものである。The present invention has been made in view of these disadvantages, and an object of the present invention is to provide a multi-layer wrapping paper which can be manufactured by a single lamination process and which can be easily wound and wrapped.
【０００８】[0008]
【課題を解決するための手段】上記課題を解決するため
になされた発明は、基材シートと、この基材シートに積
層された合成樹脂製のラミネート層と、フィルムとを有
し、前記ラミネート層とフィルムとが部分接着状態で密
に積層されており、上記部分接着状態を獲得する手段と
して、上記ラミネート層とフィルムとの間に目抜け素材
のシートが挿入されている多層構造包装紙である。本明
細書中に記載した「密に積層」とは、当該多層構造包装
紙に外部から何も負荷が作用しない状態において、ラミ
ネート層とフィルムとの隙間が少なく積層されている趣
旨であり、常に両層間に空間が形成されないように積層
されている趣旨ではない。従って、当該多層構造包装紙
に折り曲げや湾曲によって外力が作用した場合、ラミネ
ート層とフィルムとの間、特に非接着部分に隙間が形成
される場合がある。また「目抜け素材のシート」とは、
シート面に目抜け部分（開口）を有するシートを意味す
る。Means for Solving the Problems The invention made to solve the above-mentioned problems has a base sheet, a synthetic resin laminate layer laminated on the base sheet, and a film. The layer and the film are densely laminated in a partially bonded state, and as a means for obtaining the partially bonded state, a multilayer structure wrapping paper in which a sheet of a blank material is inserted between the laminate layer and the film. is there. The term `` densely laminated '' described in the present specification means that in a state where no load is applied to the multilayer wrapping paper from the outside, the gap between the laminate layer and the film is laminated with a small amount, and is always It does not mean that the layers are stacked so that no space is formed between both layers. Therefore, when an external force acts on the multilayer wrapping paper by bending or bending, a gap may be formed between the laminate layer and the film, particularly at a non-adhered portion. Also, "sheets of blank material"
It means a sheet having a blank portion (opening) on the sheet surface.
【０００９】この手段によれば、ラミネート層とフィル
ムが部分接着状態であることから、上記従来の多層構造
包装紙のように基材シート及びラミネート層からなる層
とフィルムとが同時に破れることや、コシが強くなりす
ぎて包装作業が困難になること等の不都合の発生を防止
できる。さらに、本発明の多層構造包装紙は、ラミネー
ト層とフィルムとの隙間が少なく密に積層されているこ
とから、だぶついてしまうことがなく、当該多層構造包
装紙の巻き取りや、当該包装紙を用いた包装作業が容易
になる。According to this means, since the laminate layer and the film are in a partially adhered state, the layer consisting of the base sheet and the laminate layer and the film are torn at the same time as in the above-mentioned conventional multilayer wrapping paper. It is possible to prevent the occurrence of inconveniences such as stiffness becoming too strong to make the packaging operation difficult. Furthermore, since the multilayer wrapping paper of the present invention has a small gap between the laminate layer and the film and is densely laminated, the multilayer wrapping paper is not wound up, and the multilayer wrapping paper can be wound up or the wrapping paper can be removed. The packaging work used becomes easier.
【００１０】上記部分接着状態を獲得する手段として、
上記ラミネート層とフィルムとの間に目抜け素材のシー
トを挿入することから、目抜け素材のシートが介在する
部分ではラミネート層とフィルムとが接着せず、目抜け
部分ではラミネート層とフィルムとが接着し、これによ
り部分接着状態が形成できる。なお、かかる目抜け部分
の大きさを調整することで、接着部分の面積比率、つま
り接着強度を制御することができる。[0010] As means for obtaining the above partially adhered state,
Since the sheet of the blank material is inserted between the laminate layer and the film, the laminate layer and the film do not adhere to each other at the portion where the sheet of the blank material is interposed, and the laminate layer and the film are not bonded at the blank portion. Bonding, thereby forming a partially bonded state. By adjusting the size of the missing portion, the area ratio of the bonding portion, that is, the bonding strength can be controlled.
【００１１】上記目抜け素材のシートを、フラットヤー
ンを織成したもの、割布、不織布又は組布にするとよ
い。ここで、「割布」とは、スプリットファイバーで作
った布をいい、多くの目抜け部分を有する。また「組
布」とは、糸や高密度ポリエチレン、ポリプロピレン等
が延伸されたテープヤーンを縦横に連続的に直交積層し
て格子状にしたものをホットメルト接着剤等で接着固定
させた経緯直交不織布をいう。この手段によれば、目抜
け素材のシートの厚みを薄くしつつ、容易に目抜け部分
を形成することができる。このように目抜け素材のシー
トを薄くすると、目抜け部分を通してラミネート層を構
成する合成樹脂がフィルムに接触しやすい構造になる。The sheet of the blank material may be a flat yarn woven, split cloth, non-woven cloth or braided cloth. Here, the “split cloth” refers to a cloth made of split fibers, and has many missing portions. The term "braided cloth" refers to a continuous crosswise vertical and horizontal lamination of tape, yarn, or high-density polyethylene, polypropylene, or other stretched tape yarn, which is then glued and fixed with a hot melt adhesive or the like. Refers to nonwoven fabric. According to this means, it is possible to easily form the missing portion while reducing the thickness of the sheet of the missing material. When the sheet of the blank material is made thin in this manner, the synthetic resin constituting the laminate layer easily comes into contact with the film through the blank portion.
【００１２】また、上記部分接着状態を獲得する手段と
して、隙間を開けて平行に配設した複数の帯状シートを
上記ラミネート層とフィルムとの間に挿入することも可
能である。この手段によれば、ラミネート層とフィルム
間において、帯状シートが挿入されている部分は接着せ
ず、かつ、隣り合う帯状シート間の隙間の部分は接着
し、その結果、ラミネート層とフィルムとを部分接着状
態に積層させることができる。Further, as a means for obtaining the partial adhesion state, it is possible to insert a plurality of strip-shaped sheets arranged in parallel with a gap between the laminate layer and the film. According to this means, between the laminate layer and the film, the portion where the band-shaped sheet is inserted does not adhere, and the gap portion between the adjacent band-like sheets adheres, and as a result, the laminate layer and the film are separated. They can be laminated in a partially bonded state.
【００１３】[0013]
【発明の実施の形態】以下、適宜図面を参照しつつ本発
明の実施の形態を詳説する。図１は本発明の第１の実施
形態に係る多層構造包装紙を示す模式的断面図で、図３
は第２の実施形態に係る多層構造包装紙を示す模式的断
面図である。なお、図２は本発明の参考形態に係る多層
構造包装紙を示す模式的断面図である。Embodiments of the present invention will be described below in detail with reference to the drawings as appropriate. FIG. 1 is a schematic cross-sectional view showing a multilayer wrapping paper according to a first embodiment of the present invention.
FIG. 4 is a schematic cross-sectional view showing a multilayer wrapping paper according to a second embodiment. FIG. 2 is a schematic cross-sectional view showing a multi-layer wrapping paper according to a reference embodiment of the present invention.
【００１４】図１の多層構造包装紙１は、基材シート
２、ラミネート層３およびフィルム４がこの順に積層さ
れ、さらにこのラミネート層３とフィルム４との間に目
抜け部分６を有する目抜けシート５（上述の目抜け素材
のシートに相当する）が挿入された構造である。そのた
め、ラミネート層３とフィルム４との間は、目抜けシー
ト５における目抜け部分６の部分でのみ当接し、接着し
ている。一方、ラミネート層３とフィルム４との間のう
ち目抜けシート５が存在する部分では、この目抜けシー
ト５によって両層が接着していない。したがって、ラミ
ネート層３とフィルム４とは、部分接着状態にある。The multilayer wrapping paper 1 shown in FIG. 1 has a base sheet 2, a laminate layer 3, and a film 4 laminated in this order, and further has a through hole 6 between the laminate layer 3 and the film 4. This is a structure in which a sheet 5 (corresponding to the above-described blank material sheet) is inserted. Therefore, the lamination layer 3 and the film 4 are in contact with and bonded only at the portion of the blanking portion 6 of the blanking sheet 5. On the other hand, in the portion between the laminate layer 3 and the film 4 where the blank sheet 5 exists, the two layers are not bonded by the blank sheet 5. Therefore, the laminate layer 3 and the film 4 are in a partially bonded state.
【００１５】上述のように当該多層構造包装紙１は、基
材シート２及びラミネート層３からなるＡ層と、フィル
ム４からなるＢ層とが部分接着状態にあるため、包装
時、Ａ層とＢ層間に剥離する方向にせん断力が働いて
も、両層が完全に接着されている包装紙と比較して、両
層が同時に破れてしまうことを防止できる。また、上記
両層が部分接着状態であり、接着していない部分を有す
るため、包装紙自体のコシが硬くならず、包装作業や包
装紙の巻き取り作業が容易になる。さらに、Ａ層とＢ層
との間に空間が形成され難く、だぶつかないため、コン
パクトかつ容易に巻き取ることができ、包装作業も容易
になる。かかる作用を考慮すると、ラミネート層３とフ
ィルム４との接着面積比は、１％以上３０％以下にする
とよい。As described above, the multi-layered wrapping paper 1 has a partially bonded state of the layer A composed of the base sheet 2 and the laminate layer 3 and the layer B composed of the film 4, so that the layer A is Even if a shearing force acts in the direction of peeling between the B layers, both layers can be prevented from being simultaneously torn as compared with a wrapping paper in which both layers are completely adhered. In addition, since the two layers are partially adhered and have a non-adhered portion, the stiffness of the wrapping paper itself is not hardened, and the wrapping work and the wrapping paper winding operation are facilitated. Furthermore, since a space is not easily formed between the layer A and the layer B and does not cling, it can be wound up compactly and easily, and the packaging operation becomes easy. In consideration of such an effect, the bonding area ratio between the laminate layer 3 and the film 4 is preferably set to 1% or more and 30% or less.
【００１６】上記目抜け部分６を有する目抜けシート５
としては、ａ）ポリエチレン製やポリプロピレン製など
のフラットヤーンを目抜け部分６が形成されるよう平織
りしたもの、ｂ）前記フラットヤーンを平織りしたもの
から縦糸用ヤーン又は横糸用ヤーンを抜き、スリット状
の目抜け部分６を形成したもの、ｃ）割布、ｄ）組布、
ｅ）不織布などが挙げられる。これらの目抜けシート５
の厚さは、３μｍ以上１００μｍ以下と薄くし、目抜け
部分６を通したラミネート層３とフィルム４との当接及
び接着の弊害にならないようにする。The blank sheet 5 having the blank portion 6
A) a flat yarn made of polyethylene or polypropylene, which is plain-woven so as to form the perforated portion 6, b) a warp yarn or a weft yarn is removed from the flat yarn obtained by plain weaving, and a slit is formed. C) split cloth, d) braided cloth,
e) Nonwoven fabric and the like. These missing sheets 5
Is made as thin as not less than 3 μm and not more than 100 μm so as not to adversely affect the contact and adhesion between the laminate layer 3 and the film 4 through the through-holes 6.
【００１７】上記基材シート２には、紙素材、合成樹脂
フィルム等を用いることができる。基材シート２に使用
可能な紙素材としては、例えば未晒クラフト紙、晒クラ
フト紙、上質紙、中質紙、片艶未晒クラフト紙、純白ロ
ール、グラシン紙、感熱紙、感圧紙、合成紙、和紙、ト
レーシングペーパー、各種コート紙、板紙、ライナー
紙、クレープ加工紙等が挙げられ、これらに防錆処理が
施されたものも可能である。また、基材シート２に使用
可能な合成樹脂としては、例えばポリエチレン、ポリプ
ロピレン、ポリメチルペンテン、エチレン酢酸ビニル樹
脂、ポリアミド樹脂、エチレンエチルアクリレート樹
脂、エチレンアクリル酸樹脂、エチレンメタクリル酸樹
脂、エチレンアクリル酸メチル樹脂、アイオノマー樹
脂、ポリビニルアルコール、ポリエステル等が挙げられ
る。またいわゆるメタロセン触媒を用いて重合されたポ
リエチレン、ポリプロピレン等も、好適に用いることが
できる。かかる基材シート２に紙素材を用いる場合、こ
の紙素材の秤量は、特には限定されないが、一般的には
３０ｇ／ｍ2以上４５０ｇ／ｍ2以下程度とされる。ま
た、基材シート２に合成樹脂フィルムを用いる場合、こ
の合成樹脂フィルムの厚みは特には限定されないが、一
般的には８μｍ以上２００μｍ以下程度とされる。As the base sheet 2, a paper material, a synthetic resin film, or the like can be used. Examples of paper materials that can be used for the base sheet 2 include unbleached kraft paper, bleached kraft paper, high quality paper, medium quality paper, single gloss unbleached kraft paper, pure white roll, glassine paper, heat-sensitive paper, pressure-sensitive paper, and synthetic paper. Examples include paper, Japanese paper, tracing paper, various coated papers, paperboard, liner paper, creped paper, and the like, and those subjected to rustproofing treatment are also possible. Examples of the synthetic resin usable for the base sheet 2 include polyethylene, polypropylene, polymethylpentene, ethylene vinyl acetate resin, polyamide resin, ethylene ethyl acrylate resin, ethylene acrylate resin, ethylene methacrylate resin, and ethylene acrylate. Examples include a methyl resin, an ionomer resin, polyvinyl alcohol, and polyester. Further, polyethylene, polypropylene and the like polymerized using a so-called metallocene catalyst can also be suitably used. When a paper material is used for the base sheet 2, the weighing of the paper material is not particularly limited, but is generally about 30 g / m 2 to 450 g / m 2 . When a synthetic resin film is used for the base sheet 2, the thickness of the synthetic resin film is not particularly limited, but is generally about 8 μm or more and 200 μm or less.
【００１８】ラミネート層３に使用可能な熱可塑性樹脂
としては、例えばポリエチレン、ポリプロピレン、ポリ
メチルペンテン、エチレン酢酸ビニル樹脂、エチレンエ
チルアクリレート樹脂、エチレンアクリル酸樹脂、エチ
レンメタクリル酸樹脂、エチレンアクリル酸メチル樹
脂、アイオノマー樹脂、ポリアミド樹脂、ポリビニルア
ルコール、ポリエステル等が挙げられる。また、いわゆ
るメタロセン触媒を用いて重合されたポリエチレン、ポ
リプロピレン等も、好適に用いることができる。ラミネ
ート層３の厚みは特には限定されないが、一般的には８
μｍ以上１００μｍ以下程度とされる。Examples of the thermoplastic resin usable for the laminate layer 3 include polyethylene, polypropylene, polymethylpentene, ethylene vinyl acetate resin, ethylene ethyl acrylate resin, ethylene acrylate resin, ethylene methacrylate resin, and ethylene methyl acrylate resin. , Ionomer resin, polyamide resin, polyvinyl alcohol, polyester and the like. In addition, polyethylene, polypropylene, and the like polymerized using a so-called metallocene catalyst can also be suitably used. Although the thickness of the laminate layer 3 is not particularly limited, it is generally 8
It is set to about μm or more and 100 μm or less.
【００１９】フィルム４には合成樹脂を用いることがで
き、使用可能な合成樹脂としては、例えばポリエチレ
ン、ポリプロピレン、ポリメチルペンテン、エチレン酢
酸ビニル樹脂、エチレンエチルアクリレート樹脂、エチ
レンアクリル酸樹脂、エチレンメタクリル酸樹脂、エチ
レンアクリル酸メチル樹脂、アイオノマー樹脂、ポリア
ミド樹脂、ポリビニルアルコール、ポリエステル等が挙
げられる。また、いわゆるメタロセン触媒を用いて重合
されたポリエチレン、ポリプロピレン等も、好適に用い
ることができる。A synthetic resin can be used for the film 4, and usable synthetic resins include, for example, polyethylene, polypropylene, polymethylpentene, ethylene vinyl acetate resin, ethylene ethyl acrylate resin, ethylene acrylic acid resin, ethylene methacrylic acid. Resin, ethylene methyl acrylate resin, ionomer resin, polyamide resin, polyvinyl alcohol, polyester and the like. In addition, polyethylene, polypropylene, and the like polymerized using a so-called metallocene catalyst can also be suitably used.
【００２０】ここで、当該多層構造包装紙１の製造方法
について説明する。まず、基材シート２、目抜けシート
５およびフィルム４をこの順に積層するよう繰出ロール
から繰り出して順次圧着ロールに送りつつ、ラミネート
層３を構成する溶融合成樹脂組成物を基材シート２およ
び目抜けシート５間にＴダイからフィルム状に押し出
し、積層して加圧することによる。上記製造方法によれ
ば、基材シート２とフィルム４間にラミネート層３が形
成でき、かつ、目抜けシート５の目抜け部分６を通して
のみラミネート層３とフィルム４とを接着させることが
できる。Here, a method of manufacturing the multilayer wrapping paper 1 will be described. First, the melted synthetic resin composition constituting the laminate layer 3 is fed out of the feed roll so as to laminate the base sheet 2, the blank sheet 5 and the film 4 in this order, and is sequentially fed to the pressure roll. By extruding a film from a T-die between the escaped sheets 5, laminating and pressing. According to the above-described manufacturing method, the laminate layer 3 can be formed between the base sheet 2 and the film 4, and the laminate layer 3 and the film 4 can be bonded only through the perforated portion 6 of the perforated sheet 5.
【００２１】図２の多層構造包装紙１１は、基材シート
１２、ラミネート層１３およびフィルム１４がこの順に
積層された構造であり、フィルム１４裏面に部分的にコ
ーティングを施すことによって、基材シート１２および
ラミネート層１３からなるＡ層とフィルム１４からなる
Ｂ層とが部分接着状態にされている。なお、当該多層構
造包装紙１１を構成する基材シート１２、ラミネート層
１３およびフィルム１４は、図１の多層構造包装紙１の
基材シート２、ラミネート層３およびフィルム４と同様
である。The multi-layer wrapping paper 11 shown in FIG. 2 has a structure in which a base sheet 12, a laminate layer 13 and a film 14 are laminated in this order. Layer A composed of film 12 and laminate layer 13 and layer B composed of film 14 are partially adhered. The base sheet 12, the laminate layer 13 and the film 14 constituting the multi-layer wrapping paper 11 are the same as the base sheet 2, the laminate layer 3 and the film 4 of the multi-layer wrapping paper 1 of FIG.
【００２２】上記フィルム１４裏面のコーティングはラ
ミネート加工前に施される。このコーティングで用いる
塗工物としては、ラミネート層１３とフィルム１４とに
使用される合成樹脂が接着性の悪い組み合わせの場合
（例えば、ポリエステルフィルムとＰＥラミネートとの
場合）、フィルム１４の裏面に接着性を促進する接着促
進剤（例えば、ウレタン系又はポリエステル系アンカー
コート剤等）をコーティングする。反対に、ラミネート
層１３とフィルム１４とに使用される合成樹脂が接着性
のよい組み合わせの場合（例えば、ポリエチレンフィル
ムとポリエチレンラミネートとの場合）、フィルム１４
の裏面に接着性を抑制する接着抑制剤（例えば、シリコ
ーン、フッ素系コート剤等）をコーティングする。The coating on the back surface of the film 14 is performed before laminating. When the synthetic resin used for the laminate layer 13 and the film 14 is a combination having poor adhesion (for example, in the case of a polyester film and a PE laminate), the coating material used in this coating is bonded to the back surface of the film 14. Coating with an adhesion promoter (for example, a urethane-based or polyester-based anchor coat agent) that promotes the property. Conversely, when the synthetic resin used for the laminate layer 13 and the film 14 is a combination having good adhesiveness (for example, in the case of a polyethylene film and a polyethylene laminate), the film 14
Is coated with an adhesion inhibitor (for example, silicone, a fluorine-based coating agent, etc.) for suppressing the adhesiveness.
【００２３】上述の構成を有する図２の多層構造包装紙
１１の製造方法は、上記図１の多層構造包装紙１の製造
方法と略同様であり、基材シート１２とフィルム１４と
を圧着ロールに順次繰り出しつつ、両層間にラミネート
層１３を構成する溶融合成樹脂組成物をＴダイからフィ
ルム状に押し出し、加圧することによる。当該多層構造
包装紙１１も、上述のように、基材シート１２及びラミ
ネート層１３からなるＡ層と、フィルム１４からなるＢ
層とが部分接着状態にあるため、上述のような同時破れ
の防止、包装紙自体の硬化防止およびだぶつきの防止を
図ることができる。The method of manufacturing the multilayer wrapping paper 11 of FIG. 2 having the above-described configuration is substantially the same as the method of manufacturing the multilayer wrapping paper 1 of FIG. The molten synthetic resin composition constituting the laminate layer 13 between the two layers is extruded from a T-die into a film while being sequentially fed out, and is pressed. As described above, the multi-layer wrapping paper 11 also has an A layer including the base sheet 12 and the laminate layer 13 and a B layer including the film 14.
Since the layer and the layer are in a partially bonded state, it is possible to prevent simultaneous tearing, hardening of the wrapping paper itself, and prevention of looseness as described above.
【００２４】図３の多層構造包装紙２１は、基材シート
２２、ラミネート層２３およびフィルム２４がこの順に
積層され、さらにこのラミネート層２３とフィルム２４
との間に複数の帯状シート２５が並列に、かつ、隙間２
６を開けて挿入された構造である。つまり、当該多層構
造包装紙２１は、目抜けシート５に代えて帯状シート２
５が挿入されている点を除いて、上記図１の多層構造包
装紙１と同様である。当該多層構造包装紙２１も、基材
シート２２及びラミネート層２３からなるＡ層とフィル
ム２４からなるＢ層とが部分接着状態であり、上記図１
の多層構造包装紙１及び図２の多層構造包装紙１１と同
様の作用が発揮できる。なお、帯状シート２５に用いら
れる材料としては、上記基材シート１と同様で、紙素
材、合成樹脂フィルム等を用いることができる。The multilayer wrapping paper 21 shown in FIG. 3 has a base sheet 22, a laminate layer 23, and a film 24 laminated in this order.
And a plurality of strip-shaped sheets 25 are arranged in parallel between
6 is a structure inserted and opened. That is, the multi-layered wrapping paper 21 is replaced with the band-like sheet 2 instead of the blank sheet 5.
5 is the same as the multi-layer wrapping paper 1 of FIG. The multi-layer wrapping paper 21 also has a partially adhered state of the A layer composed of the base material sheet 22 and the laminate layer 23 and the B layer composed of the film 24, as shown in FIG.
2 and the multilayer structure wrapping paper 11 of FIG. In addition, as a material used for the belt-shaped sheet 25, a paper material, a synthetic resin film, or the like can be used in the same manner as the base sheet 1.
【００２５】[0025]
【発明の効果】以上説明したように、本発明の多層構造
包装紙によれば、一度のラミネート加工で製造が可能で
あり、製造コストの低減化を図ることができる。また、
上下両層が部分接着状態にあるため、包装時、両層が同
時に破れてしまうことを防止できる。さらに、上記両層
が部分接着状態であり、接着していない部分を有するた
め、包装紙自体のコシが硬くならず、包装作業や包装紙
の巻き取り作業が容易になる。さらに、上層と下層とが
密に積層され、だぶつきが少ないため、コンパクトかつ
容易に巻き取ることができ、包装作業も容易になる。As described above, according to the multi-layer wrapping paper of the present invention, it is possible to manufacture by one lamination process, and it is possible to reduce the manufacturing cost. Also,
Since both the upper and lower layers are partially adhered, it is possible to prevent both layers from being simultaneously torn during packaging. Further, since the two layers are partially adhered and have a non-adhered portion, the stiffness of the wrapping paper itself does not become hard, and the wrapping work and the wrapping paper winding operation become easy. Furthermore, since the upper layer and the lower layer are densely laminated and have little looseness, they can be wound up compactly and easily, and the packaging operation becomes easy.
【図１】本発明の第１の実施形態に係る多層構造包装紙
を示す模式的断面図である。FIG. 1 is a schematic sectional view showing a multilayer wrapping paper according to a first embodiment of the present invention.
【図２】本発明の参考形態に係る多層構造包装紙を示す
模式的断面図である。FIG. 2 is a schematic sectional view showing a multilayer wrapping paper according to a reference embodiment of the present invention.
【図３】本発明の第２の実施形態に係る多層構造包装紙
を示す模式的断面図である。FIG. 3 is a schematic cross-sectional view showing a multilayer wrapping paper according to a second embodiment of the present invention.
【図４】（ａ）および（ｂ）はそれぞれ従来の一般的な
多層構造包装紙を示す模式的断面図である。FIGS. 4A and 4B are schematic cross-sectional views showing conventional general multi-layer wrapping paper.
１ 多層構造包装紙 ２ 基材シート ３ ラミネート層 ４ フィルム ５ 目抜けシート ６ 目抜け部分 １１ 多層構造包装紙 １２ 基材シート １３ ラミネート層 １４ フィルム ２１ 多層構造包装紙 ２２ 基材シート ２３ ラミネート層 ２４ フィルム ２５ 帯状シート ２６ 隙間 DESCRIPTION OF SYMBOLS 1 Multilayer wrapping paper 2 Base sheet 3 Laminating layer 4 Film 5 Sight sheet 6 Sight part 11 Multilayer wrapping paper 12 Base sheet 13 Laminating layer 14 Film 21 Multilayer wrapping paper 22 Base sheet 23 Laminating layer 24 Film 25 belt-like sheet 26 gap
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平３−166943（ＪＰ，Ａ) 特開 平９−48082（ＪＰ，Ａ) 特開 平７−246674（ＪＰ，Ａ) 特開 平５−123631（ＪＰ，Ａ) 特開 昭54−80377（ＪＰ，Ａ) 実開 平２−97027（ＪＰ，Ｕ) (58)調査した分野(Int.Cl.7，ＤＢ名) B32B 1/00 - 35/00 ──────────────────────────────────────────────────続 き Continuation of the front page (56) References JP-A-3-166943 (JP, A) JP-A-9-48082 (JP, A) JP-A-7-246674 (JP, A) JP-A-5- 123631 (JP, A) JP-A-54-80377 (JP, A) JP-A-2-97027 (JP, U) (58) Fields investigated (Int. Cl. 7 , DB name) B32B 1/00-35 / 00
Claims (3)
れた合成樹脂製のラミネート層と、フィルムとを有し、
前記ラミネート層とフィルムとが部分接着状態で密に積
層されており、 上記部分接着状態を獲得する手段として、上記ラミネー
ト層とフィルムとの間に目抜け素材のシートが挿入され
ている多層構造包装紙。 1. A base sheet, a synthetic resin laminate layer laminated on the base sheet, and a film,
The laminate layer and the film are densely laminated in a partially adhered state, and as a means for obtaining the partially adhered state, a multilayer structure packaging in which a sheet of a blank material is inserted between the laminate layer and the film. paper.
ーンを織成したもの、割布、不織布又は組布である請求
項１に記載の多層構造包装紙。 Wherein said second loss material sheet, those woven flat yarn, wherein a split cloth, nonwoven or set cloth
Item 4. The multilayer wrapping paper according to Item 1 .
れた合成樹脂製のラミネート層と、フィルムとを有し、
前記ラミネート層とフィルムとが部分接着状態で密に積
層されており、 上記部分接着状態を獲得する手段として、隙間を開けて
平行に配設した複数の帯状シートが上記ラミネート層と
フィルムとの間に挿入されている多層構造包装紙。 3. It has a base sheet, a synthetic resin laminate layer laminated on the base sheet, and a film,
The laminate layer and the film are densely laminated in a partially adhered state. As a means for obtaining the partially adhered state, a plurality of strip-shaped sheets arranged in parallel with a gap between the laminate layer and the film are provided. Multi-layer wrapping paper inserted in the.