JP3068174B2 - 生分解性プラスチック - Google Patents
生分解性プラスチックInfo
- Publication number
- JP3068174B2 JP3068174B2 JP2295122A JP29512290A JP3068174B2 JP 3068174 B2 JP3068174 B2 JP 3068174B2 JP 2295122 A JP2295122 A JP 2295122A JP 29512290 A JP29512290 A JP 29512290A JP 3068174 B2 JP3068174 B2 JP 3068174B2
- Authority
- JP
- Japan
- Prior art keywords
- biodegradable plastic
- lactic acid
- molecular weight
- plastic
- biodegradable
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 ［産業上の利用分野］ 本発明は生分解性プラスチックに関する。特に、ゴミ
焼却用の袋、食器、ポリ容器など大衆消費材として用い
られる生分解性プラスチックに関する。
焼却用の袋、食器、ポリ容器など大衆消費材として用い
られる生分解性プラスチックに関する。
［従来技術およびその課題］ 近年、環境保全に対する必要性と意識の高まりから生
分解性プラスチックが脚光をあびている。生分解性プラ
スチックは使用済みのプラスチックが土中や水中の微生
物の作用で二酸化炭素と水に分解され自然環境に戻るも
のと一般に定義されている。このような生分解性プラス
チックは世界的に注目されているものの、まだ開発が始
まったばかりであり、現在、様々な材料素材の開発が行
われている。
分解性プラスチックが脚光をあびている。生分解性プラ
スチックは使用済みのプラスチックが土中や水中の微生
物の作用で二酸化炭素と水に分解され自然環境に戻るも
のと一般に定義されている。このような生分解性プラス
チックは世界的に注目されているものの、まだ開発が始
まったばかりであり、現在、様々な材料素材の開発が行
われている。
生分解性プラスチックに求められる性質は、加水分解
性を有し、しかも材料強度が高いことである。しかしな
がら、加水分解性は分子量の増加に伴って低下し、一方
材料強度は分子量の増加に伴って大きくなるため、これ
らは一般に相反する性質である。特にエステル基により
結合したポリエステル樹脂においてはこの傾向が強い。
性を有し、しかも材料強度が高いことである。しかしな
がら、加水分解性は分子量の増加に伴って低下し、一方
材料強度は分子量の増加に伴って大きくなるため、これ
らは一般に相反する性質である。特にエステル基により
結合したポリエステル樹脂においてはこの傾向が強い。
このような問題を解決するため、従来、延伸など材料
の加工法により伸び、引張り強度を向上させることも行
われているが、コストの増加が避けられない。また、紫
外線照射などの外部エネルギーによりポリマーを分解し
て処理する方法も提案されているが、かかる処理方法を
一般家庭で実施することは困難である。
の加工法により伸び、引張り強度を向上させることも行
われているが、コストの増加が避けられない。また、紫
外線照射などの外部エネルギーによりポリマーを分解し
て処理する方法も提案されているが、かかる処理方法を
一般家庭で実施することは困難である。
本発明の目的は通常の使用時には高い強度を有し、一
方、不要となって廃棄されたときには速やかに分解され
地球環境を破壊するおそれのない生分解性プラスチック
を提供することにある。
方、不要となって廃棄されたときには速やかに分解され
地球環境を破壊するおそれのない生分解性プラスチック
を提供することにある。
［課題を解決するための手段］ 本発明は、ベースポリマーとしてポリ乳酸を用い、酵
母エキスを必須の微生物培地成分として配合した生分解
性プラスチックを提供するものである。
母エキスを必須の微生物培地成分として配合した生分解
性プラスチックを提供するものである。
前記ベースポリマーに配合される培地成分としては、
酵母エキスが挙げられ、ペプトン、デンプン、グルコー
スなどの他の微生物の培地成分を併用してもよい。培地
成分の配合量は多いと早く分解し、少量であると分解が
遅くなり、用途、目的に応じて調整し分解時間を制御す
る。通常、プラスチック100部に対して10〜0.01部であ
る。培地成分の配合量がこれより少ないと、充分な生分
解性が得られず、一方この範囲より多くても効果は向上
しない。具体的にはポリマー分子量が数十万以下である
と水中で約１ケ月以内に分解が可能となる。
酵母エキスが挙げられ、ペプトン、デンプン、グルコー
スなどの他の微生物の培地成分を併用してもよい。培地
成分の配合量は多いと早く分解し、少量であると分解が
遅くなり、用途、目的に応じて調整し分解時間を制御す
る。通常、プラスチック100部に対して10〜0.01部であ
る。培地成分の配合量がこれより少ないと、充分な生分
解性が得られず、一方この範囲より多くても効果は向上
しない。具体的にはポリマー分子量が数十万以下である
と水中で約１ケ月以内に分解が可能となる。
また、本発明で用いられるベースポリマーは加水分解
性ポリマーである乳酸の重合体であり、特にポリＬ−乳
酸が好ましい。ポリ乳酸の分子量は１×104〜300×104
が好ましい。ポリＬ−乳酸は加水分解してＬ−乳酸とな
るための生体安全性が高く、近年医用材料としても研究
が活発であり一部実用化されている。また、モノマーで
あるＬ−乳酸は一般に発酵法により乳酸菌から産生され
るが、医薬品、食品にも使用され、かつ生体内での代謝
系路も明らかである。このため、ポリ乳酸は分解後の生
体安全性も極めて高い。ポリＬ−乳酸は分子量1000の場
合、生理食塩水中で約２週間以内に分解し材料強度は低
く実用的でない。これに対し、分子量が10万以上になる
と分解しにくく、100万以上では約１年以上変化なく存
在し、材料強度も高くポリスチレンと同等以上になる。
性ポリマーである乳酸の重合体であり、特にポリＬ−乳
酸が好ましい。ポリ乳酸の分子量は１×104〜300×104
が好ましい。ポリＬ−乳酸は加水分解してＬ−乳酸とな
るための生体安全性が高く、近年医用材料としても研究
が活発であり一部実用化されている。また、モノマーで
あるＬ−乳酸は一般に発酵法により乳酸菌から産生され
るが、医薬品、食品にも使用され、かつ生体内での代謝
系路も明らかである。このため、ポリ乳酸は分解後の生
体安全性も極めて高い。ポリＬ−乳酸は分子量1000の場
合、生理食塩水中で約２週間以内に分解し材料強度は低
く実用的でない。これに対し、分子量が10万以上になる
と分解しにくく、100万以上では約１年以上変化なく存
在し、材料強度も高くポリスチレンと同等以上になる。
前記の成分より生分解性プラスチックを調整するに
は、高分子量のポリＬ−乳酸などの加水分解性樹脂をク
ロロホルム、THFなど適宜の溶媒に溶解し、この溶液に
培地成分を添加し、板状にキャスティング後溶媒を蒸発
させて製膜する。
は、高分子量のポリＬ−乳酸などの加水分解性樹脂をク
ロロホルム、THFなど適宜の溶媒に溶解し、この溶液に
培地成分を添加し、板状にキャスティング後溶媒を蒸発
させて製膜する。
また、別法としては加水分解性樹脂と培地成分とを粉
末状態で混合して圧縮成形して均質な成形体を得てもよ
い。
末状態で混合して圧縮成形して均質な成形体を得てもよ
い。
なお、本発明の生分解性プラスチックには乳酸エステ
ル、オクチル酸などの可塑剤、添加剤が配合されてよ
い。
ル、オクチル酸などの可塑剤、添加剤が配合されてよ
い。
［作用］ 本発明のプラスチックは、通常の使用状態では高い強
度を有するが、使用後、地中や川などの微生物の作用を
受ける環境に廃棄されると、プラスチック中に配合され
た微生物培地成分が環境微生物によるプラスチックの分
解作用を積極的に促進し、分解物の資化が行われて短時
間に分解が進行する。
度を有するが、使用後、地中や川などの微生物の作用を
受ける環境に廃棄されると、プラスチック中に配合され
た微生物培地成分が環境微生物によるプラスチックの分
解作用を積極的に促進し、分解物の資化が行われて短時
間に分解が進行する。
［実施例］ つぎに本発明を実施例によりさらに具体的に説明す
る。
る。
ポリ乳酸（分子量約10万）10gをクロロホルム400gに
溶解し、これにぺプトン、酵母エキス、デンプンを各1g
添加してガラス板状にキャスティングした。溶媒蒸発後
の膜を庭の土中に埋めるといずれも約３ケ月で膜が破壊
されていた。
溶解し、これにぺプトン、酵母エキス、デンプンを各1g
添加してガラス板状にキャスティングした。溶媒蒸発後
の膜を庭の土中に埋めるといずれも約３ケ月で膜が破壊
されていた。
［発明の効果］ 本発明の生分解性プラスチックは、通常の使用時には
高い強度を有し、廃棄後、速やかに環境微生物により分
解される。
高い強度を有し、廃棄後、速やかに環境微生物により分
解される。
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 平２−222421（ＪＰ，Ａ) 特開 平４−58962（ＪＰ，Ａ) 特開 平１−156912（ＪＰ，Ａ) 特開 平４−124127（ＪＰ，Ａ) 化学大辞典編集委員会編，「化学大辞 典（第３巻）」，初版縮刷版第２刷, 1966年４月20日，ｐ．603「酵母エキス」 の項 (58)調査した分野(Int.Cl.7，ＤＢ名) C08L 67/04 C08K 5/00 C08L 3/02 C08L 89/00
Claims (1)
- 【請求項１】ベースポリマーとしてポリ乳酸を用い、酵
母エキスを必須の微生物培地成分として配合した生分解
性プラスチック。