JP2705751B2 - Manufacturing method of foamed resin products with labels - Google Patents

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing labeled foamed resin products used for instant noodle cup containers, beverage cups such as juice and hot coffee, and other packaging containers. The present invention relates to a method for producing a foamed resin product with a label having a label on which a display of a pattern, a design, or the like is printed in advance.

[0002]

2. Description of the Related Art Foamed bead cups are widely used as containers for instant noodles and cups for drinks such as juice.

[0003] The foamed bead cup is generally made by pre-foaming foamable resin particles (beads) in which a volatile foaming agent such as butane or pentane is added to polystyrene resin particles to obtain pre-foamed particles. Is filled in a cavity of a molding die, and is heated and foamed by a heating medium such as steam or the like.

Some of such foamed bead cups display characters such as a brand name and a manufacturer, or other surface designs such as pictures and patterns.

[0005] As a method of providing the display on the surface of the foamed bead cup, a method of directly printing the displayed content on the surface of the foamed bead cup by a printing machine, a method of bonding a label on which the displayed content is pre-printed to the foamed bead cup, There is known a so-called shrink label method in which a heat-shrinkable film on which display contents are printed in advance is wound around a foamed bead cup and then heated and shrunk to be attached.

[0006]

However, the above conventional structure has the following problems.

That is, in the method of printing directly on the surface of the foamed bead cup, it is difficult to perform clear printing such as gravure printing or multicolor overlapping printing. Therefore, there is a problem in that it is almost impossible to display very fine characters and to display the transition of gradation change smoothly.

[0008] In the method of bonding a label on which the display contents are printed in advance to the foamed bead cup, the label portion protrudes from the foamed bead cup by the thickness thereof, which is unsightly. Further, if the adhesion between the foamed bead cup and the label is insufficient, the label may be peeled off at the stage of distribution or use, causing a problem that the commercial value is reduced.

In the shrink label method using a heat-shrinkable film, the heat-shrinkable film is merely attached to the cup due to heat shrinkage. Therefore, when the outer peripheral surface of the cup is inclined, the film is removed from the cup. Easy to detach. Further, when the shrinkage of the heat-shrinkable film is not uniform, since the film is deformed, it is difficult to read the display contents pre-printed, and it is almost impossible to read fine characters. doing.

Therefore, in order to solve these problems,
In the method for painting a foam-formed container disclosed in Japanese Patent Application Laid-Open No. 4-331132, a paper print sheet having a printing layer and a heat-sealing layer is fitted into the outer periphery of a tubular foam-formed container and set in a mold. By heating, the heat seal layer of the paper print sheet and the tubular foam molded container are fused. As a result, it is possible to paint clear printing without distortion on the cylindrical foam molded container.

However, according to this method, when a label is applied to the entire side surface of a container having a step called a lip on the side near the opening, such as a container of instant noodles, the paper print sheet is put on the step. It is difficult to set. Therefore, there is a problem that a label cannot be efficiently attached to the step portion.

The present invention solves such a conventional problem, and has a label on the entire side in which a fine character display and a clear design display in which gradation changes are smoothly expressed are printed in advance. An object of the present invention is to provide a method for producing a labeled foamed resin product which does not protrude from the surface of the foamed resin product, is beautiful, is hardly peeled off, and is capable of attaching a label to a step portion.

[0013]

SUMMARY OF THE INVENTION In order to solve the above-mentioned problems, a method for producing a foamed resin product with a label according to the present invention has a thickness larger than that of a foamed resin product with a label and has no step on the side surface. After the next molded product is manufactured by the in-mold bead foam molding method, a label with a preprinted label is temporarily fixed so as to cover the entire side surface of the primary molded product, and then the same shape as the labeled foamed resin product is formed. The method is characterized in that after the above-mentioned primary molded product to which the label is temporarily fixed is set in the cavity of the press mold having the cavity, the foamed resin product with the label is obtained by heating under pressure.

[0014]

According to the above construction, there is no step on the side surface of the primary molded product manufactured by the in-mold bead foam molding method.
It is easy to temporarily fix the label on which the display is printed in advance so as to cover the entire side surface of the primary molded product. In addition, by heating the primary molded product with the label temporarily fixed,
Since the labeled foamed resin product as the final product is manufactured, a foamed resin product with a label having a step on the side surface and a label attached to the entire side surface including the step portion can be easily manufactured. Furthermore, the attached label does not protrude from the surface of the foamed resin product, is beautiful, and does not easily peel off.

[0015]

EXAMPLES Hereinafter, the method for producing the labeled foamed resin product of the present invention will be described in more detail with reference to Examples, but the present invention is not limited thereto.

The method for producing a cup-shaped foamed resin product with a display (hereinafter referred to as a foamed bead cup) according to the present embodiment is as follows.
Pre-expanded particles obtained by pre-expanding expandable thermoplastic resin particles containing a foaming agent are filled in the mold cavity of the mold,
A step of manufacturing a primary molded article by heating and foaming with a heating medium such as steam, and temporarily fixing a label on which predetermined contents such as letters, patterns, and designs are separately printed in advance to the primary molded article, From the step of manufacturing a labeled foamed resin product as a secondary molded product, which is the final foamed resin product, by setting it in the cavity of a press mold having a cavity with the same shape as the foamed resin product, and applying pressure and heat It is configured.

First, in the step of manufacturing a cup-shaped primary molded product, as shown in FIG.
And a press device for bead foam molding to which is attached. This press device comprises an upper fixed platen 4 and a lower moving platen 5 which moves up and down by a ram 6. The cavity mold 1 is fixed to the fixed platen 4, and the core mold 2 is a movable platen 5. It is fixed to. Cavity mold 1
When the mold and the core mold 2 are clamped, a cup-shaped cavity 3 is formed therebetween.

The cavity mold 1 has a steam chamber 1a inside, a filling device (not shown) for filling the raw material into the cavity 3, a supply port 1b for steam and cooling water, and a drain. Discharge port 1c, primary molded product is core mold 2
Air supply port (not shown) to transfer to
Is provided. The core mold 2 has a steam chamber 2a inside.
And a supply port 2b for steam and cooling water, a drain discharge port 2c, and a discharge air port (not shown). Furthermore, although not shown, various pressure reducing valves (regulators) such as a filling air valve, a steam valve, a direct heating valve, a drain valve, a cooling water valve, a discharge air valve, and a solenoid valve of the cavity portion 3, and a solenoid valve are provided. It has a control panel to control.

As shown in FIG. 4, the primary molded product is prepared by using a polystyrene resin particle containing a foaming agent as a raw material, and prefoaming the polystyrene resin particle by a factor of 10 by a bulk ratio into a bead in-mold foam molding method. Is a foamed bead cup having a foaming ratio of 10 times manufactured by the method described in Example 1.
m, bottom 50mm, height 120mm, body thickness 2
mm, and the internal volume is 330 cc. In the method of the present invention, of course, depending on the shape and dimensions of the final foamed resin product,
The shape and dimensions of the primary molded product are appropriately set.

The thickness of the primary molded product is set to be thicker than the final labeled foamed resin product. No lip has been formed on the side surface near the opening. Therefore,
The sides are straight.

The resin constituting the expandable thermoplastic resin as a raw material of the expanded bead cup includes polystyrene resins such as polystyrene, high impact styrene, styrene-maleic anhydride copolymer, styrene-acrylonitrile copolymer and the like. , Polyethylene, polypropylene,
There is no particular limitation as long as the resin can contain a foaming agent and can be subjected to bead foam molding in a mold, such as a polyolefin resin such as an ethylene-vinyl acetate copolymer.

The thickness and the magnification of the primary molded product are determined from the thickness and the magnification of the secondary molded product so that the following equations are satisfied.

The magnification of the primary molded product / the thickness of the primary molded product = the magnification of the secondary molded product / the thickness of the secondary molded product The body thickness of the primary molded product is the body thickness of the final product. In this embodiment, the thickness is set to be twice as large as the body thickness (1 mm) of the secondary molded product.

The molding of the primary molded article is performed according to the time chart in Table 1.

[0025]

[Table 1]

First, open the filling air valve and the steam valve,
At the same time as filling the cavity 3 with the pre-expanded particles, steam is introduced into the steam chamber 1a of the cavity mold 1 and the steam chamber 2a of the core mold 2 and heated. At this time, the drain valve is opened to discharge the condensed water.

Subsequently, the direct heating valve is opened to directly heat the cavity 3. When the foaming is completed, the cooling water valve is opened and the whole is cooled. After cooling, open the exhaust air valve and
The next molded product is transferred to the core mold 2 and discharged. Then, the moving platen 5 is lowered by the ram 6, and the mold is opened.
Take out the primary molded product. The time required from the filling of the raw material to the discharge of the primary molded product is about 13 seconds.

Next, the label 10 (FIG. 4) is set on the primary molded product. That is, a roll film preprinted with display contents such as characters, patterns, and designs is set on a press machine having a Thomson blade and trimmed to produce a fan-shaped label 10 that fits the body of the primary molded product. . The label 10 is spot bonded and temporarily fixed so as to cover the entire side surface of the primary molded product.

In this embodiment, the label 10 is
Although a 200 μm-thick polystyrene roll film was used, a polystyrene-based synthetic paper may be used.
When the resin forming the label 10 and the resin forming the foamed bead cup are the same resin, an adhesive for bonding the two is applied to the back surface of the label 10 because the two are thermally fused during molding. You don't have to. However, when a plastic film such as polypropylene or polyethylene terephthalate or paper or the like, which is difficult to heat seal with the foamed bead cup, is used, the back of the label 10 is used to secure the adhesion to the foamed bead cup. , An adhesive such as vinyl acetate is applied in advance. Note that the thickness of the label 10 is preferably 10 μm to 1 mm.

Next, in the step of manufacturing a secondary molded product as a final foamed product, as shown in FIG. 1, the same press apparatus as described above is used. However, in this step, the cavity 3 has the same shape as the shape of the secondary molded product having the lip.
Is used.

The molding of the secondary molded article is performed according to the time chart in Table 2.

The primary molded product to which the label 10 has been temporarily fixed is set in the cavity mold 1 or the core mold 2 and clamped with the ram 6. In this embodiment, the thickness of the secondary molded product is 1
Since the thickness is smaller than the thickness of the next molded product, the mold clamping force is made stronger than that at the time of manufacturing the primary molded product.

First, the steam valve is opened, and steam is introduced into the steam chamber 1a of the cavity mold 1 and the steam chamber 2a of the core mold 2 and heated. At this time, the drain valve is opened to discharge the condensed water. By heating, the label 10 is fused to the primary molded article as shown in FIG. Then, the cooling water valve is opened and the whole is cooled. After cooling, the discharge air valve is opened, and the primary molded product is transferred to the core mold 2 and discharged. Then ram 6
The moving platen 5 is lowered, the mold is opened, and the secondary molded product is taken out. The time required from heating to discharge of the secondary molded product is about 9 seconds.

[0034]

[Table 2]

The time required in the time chart of the present embodiment is an example of a product having the above-mentioned shape, and when the present invention is carried out, the time is appropriately set according to the shapes and dimensions of the primary molded product and the secondary molded product. Can be set or adjusted.

According to this embodiment, the display of fine characters, the smooth display of gradation changes, and the multi-color superimposition without impairing the high heat retention and cold retention of the foamed bead cup. A foamed bead cup having on its surface a label 10 on which a display such as printing is printed can be manufactured. Further, since the label 10 is firmly fused to the foam bead cup, it is difficult for the label 10 to peel off.

Further, the primary molded product to which the label 10 is temporarily fixed is heated under pressure to produce a labeled foamed resin product as a final product. Therefore, the label 10 is attached to the entire side surface including the lip portion. A foam bead cup can be easily manufactured.

The label 1 is provided on the entire side including the lip.
Since 0 is added, the gas barrier property of the side surface is improved.
Therefore, it is advantageous when used as a food container such as a cup ramen.

That is, in the case of a cup ramen, the upper opening of the foam bead cup is covered with a resin film on which aluminum is deposited. Then, the foamed bead cups are distributed in a state of being stacked in a box. For this reason,
Gas permeation on the top of the foam bead cup is blocked by an aluminum-deposited resin film, gas permeation on the side is blocked by the label 10, and gas permeation on the bottom is deposited with aluminum on the top of the underlying foam bead cup. Blocked by resin film.

In the above embodiment, when the label 10 was set, the label 10 was wrapped around the primary molded product and spot-bonded. However, the polystyrene film was wrapped around a mold having the same shape as the primary molded product and fixed. By doing so, a conical label 10 may be produced, and this may be set in the cavity mold 1 of the above-described press apparatus, and then the primary molded product may be set inside the label 10.

Further, after the label 10 is temporarily attached to the primary molded product, a transparent polypropylene film is further temporarily attached on the label 10 so that the label 10 in the process of manufacturing the secondary molded product can be obtained. Thermal discoloration can be prevented. If a label 10 having a polypropylene film laminated on its surface is prepared in advance, and the label 10 is temporarily attached to a primary molded product, it is convenient to temporarily attach the label once.

In the above embodiment, the label 10 has a two-layer structure basically composed of a base material layer and an adhesive layer made of a heat-sealable resin laminated on the back side of the base material layer. It is preferably a laminated paper strip, such as a three-layer structure in which a paper-like layer is formed on the front surface side, or a multi-layer structure. Such an in-mold label 10 is
Before sticking to the container in the mold, it is in the form of a piece of paper, but after sticking, it is integrated with the container. More specifically, it is preferable to use a label having the following structure.

The in-mold label 10 is usually composed of a base material layer and an adhesive layer, and the material used for the base material layer is polypropylene, high-density polyethylene,
Polyvinyl chloride, polyethylene terephthalate, a thermoplastic resin having a melting point of 135 to 264 ° C. such as polyamide,
A resin film containing 8 to 65% by weight of an inorganic fine powder, a film obtained by coating an inorganic filler-containing latex on the surface of the resin film, or a film obtained by depositing aluminum on the resin film Can be mentioned. Even if such a base material layer is a single layer,
Alternatively, a laminated structure of two or more layers may be used.
When the secondary molded product has a lip portion, it is more preferable that the film has a heat shrinkage sufficient to cope with the lip step.

On the back side of the resin film of the base layer (the side in contact with the resin container), low-density polyethylene, vinyl acetate / ethylene copolymer, ethylene / (meth) acrylic acid copolymer, A film layer made of a heat-sealable resin having a melting point of 85 to 135 ° C., such as a metal salt of an ethylene / (meth) acrylic acid copolymer, is laminated. By laminating the heat-sealable resin film layers, the adhesion between the in-mold label 10 and the resin container can be further strengthened.

The laminated film on which the heat-sealing resin is laminated is stretched in at least one direction. The stretching is usually performed 4 to 12 times, preferably 4 to 8 times in the longitudinal direction, and 4 to 12 times in the transverse direction. The stretching is performed at a temperature lower than the melting point of the resin of the base material layer and at a temperature equal to or higher than the melting point of the heat-sealing resin. Although the base material layer is oriented by this stretching, the heat-sealing resin layer of the adhesive layer is not oriented.

The laminated film (synthetic paper) after the above stretching is
If necessary, the printability and adhesiveness of the surface can be improved by performing corona discharge machining, flame treatment, plasma treatment and the like. Further, the surface side of the substrate layer,
For example, the paper-like layer is usually printed. Examples of such printing include gravure printing, offset printing, flexographic printing, screen printing, etc., which allow product names, manufacturers, sales companies, characters, barcodes,
It can print various designs such as how to use, photos, character display, etc.

The printed container label 10 is separated into labels 10 of a required shape and size by punching. The label 10 may be a partial label attached to a part of the surface of the container, but is usually attached as a blank surrounding the side surface of the cup-shaped container, and is attached to the front and back of the bottle-shaped container in hollow molding. Manufactured as a label.

The method for producing a foamed bead cup with a label 10 according to the present invention is a method for producing a foamed bead cup having a thickness greater than that of a foamed bead cup with a label 10 and having no lip portion on the side by in-mold bead foam molding. , The label 10 on which the display is printed in advance is temporarily fixed so as to cover the entire side surface of the primary molded product, and then the press die having the cavity 3 having the same shape as the foam bead cup with the label 10 After setting the primary molded product to which the above-mentioned label 10 is temporarily fixed in the cavity portion 3 of above, the foamed bead cup with the label 10 is obtained by heating under pressure.

According to this, since there is no lip on the side surface of the primary molded product manufactured by the in-mold bead foam molding method, the label 10 on which the display is printed in advance can be used to cover the entire side surface of the primary molded product. It is easy to temporarily fix to cover. In addition, the primary molded product on which the label 10 is temporarily fixed is heated under pressure to produce the final product, a foamed bead cup with the label 10, so that the label has a lip on the side and covers the entire side including the lip. Label 10 with 10
Can be easily manufactured. Furthermore, the attached label 10 does not protrude from the surface of the foam bead cup, is beautiful, and is hard to peel off. Of course, if the final product does not require a lip, a portion corresponding to the lip is not required in the cavity 3 of the secondary molded product.

[0050]

As described above, the method for producing a foamed resin product with a label according to the present invention comprises the steps of foaming a primary molded product having a greater thickness than a foamed resin product with a label and having no step on the side as described above. After being manufactured by the molding method, the label on which the display is printed in advance is temporarily fixed so as to cover the entire side surface of the primary molded product, and then a press mold having a cavity having the same shape as the foamed resin product with the label is formed. After setting the primary molded product with the above label temporarily fixed in the cavity,
Since a foamed resin product with a label is obtained by heating under pressure, it is easy to temporarily fix the label on which the display is printed in advance so as to cover the entire side surface of the primary molded product. In addition, the final molded product, which is a foamed resin product with a label, is manufactured by heating the primary molded product to which the label is temporarily fixed, so that the label is attached to the entire side including the step. This has the effect that the labeled foamed resin product with a label can be easily manufactured. Further, the attached label does not protrude from the surface of the foamed resin product, is beautiful, and has an effect of being hardly peeled off.

[Brief description of the drawings]

FIG. 1, showing an embodiment of the present invention, is a partial cross-sectional view schematically illustrating a configuration of a press device used for manufacturing a secondary molded product of a foamed bead cup.

FIG. 2 is a longitudinal sectional view of a final foamed bead cup.

FIG. 3 is a partial sectional view showing a schematic configuration of a press device used for manufacturing a primary molded product of a foamed bead cup.

FIG. 4 is a longitudinal sectional view of a primary molded product of a foam bead cup to which a label is temporarily fixed.

[Explanation of symbols]

 DESCRIPTION OF SYMBOLS 1 Cavity type 1a Steam room 2 Core type 2a Steam room 3 Cavity part 4 Fixed plate 5 Moving plate 6 Ram 10 Label

Continuation of the front page (51) Int.Cl. ⁶ Identification code Agency reference number FI Technical display location B29L 22:00 (56) References JP-A-4-331132 (JP, A) JP-A-6-64058 (JP) , A) JP-B-44-20232 (JP, B1) JP-B-53-15419 (JP, B2)

Claims (1)

(57) [Claims] (1) A primary molded product having a thickness greater than that of a foamed resin product with a label and having no step on a side surface is produced by an in-mold bead foam molding method.
The primary molding is temporarily fixed so as to cover the entire side surface of the next molded product, and then the above label is temporarily fixed in the cavity of the press mold having the same shape as the foamed resin product with the label. A method for producing a labeled foamed resin product, comprising: obtaining a foamed resin product with a label by setting and heating the product under pressure.