JP2009298985A - Method for producing aqueous self-dispersive polymer dispersion, aqueous ink composition, ink set and image forming method - Google Patents

Abstract

A method for producing an aqueous dispersion of a self-dispersing polymer having excellent dispersion stability is provided.
A method for producing an aqueous dispersion of a self-dispersing polymer includes a copolymer comprising a hydrophilic constituent unit and a hydrophobic constituent unit derived from a monomer having an ethylenically unsaturated bond, and the copolymer A step of obtaining a copolymer solution containing a mixed solvent containing an organic good solvent that dissolves the organic solvent and an organic poor solvent that does not dissolve the copolymer, a dispersion step of adding water to the copolymer solution, It is set as the manufacturing method containing.
[Selection figure] None

Description

  The present invention relates to a method for producing a self-dispersing polymer aqueous dispersion, an aqueous ink composition, an ink set, and an image forming method.

  The ink jet recording method performs recording by ejecting ink droplets from a large number of nozzles formed on an ink jet head, and the noise during the recording operation is low, the running cost is low, and various recording media are used. On the other hand, it is widely used because it can record high-quality images.

By the way, carbon black pigment is used for black ink in inkjet ink, but water-soluble dye is central in color ink, and improvement of weather resistance (light resistance, ozone resistance, water resistance) is required. It has been. In particular, when considering application to the printing field, improvement in weather resistance is particularly important. The pigment is inherently high in fastness due to its high crystallinity, and has excellent light resistance and water resistance compared to dyes. However, there are problems such as dischargeability due to clogging of the nozzle part, storage stability such as coagulation sedimentation, and further fixing of printed matter such as abrasion resistance and glossiness due to particles remaining on the surface of the recording medium. It is left.
Under such circumstances, an object of the present invention is to improve the dischargeability and fixability of inkjet ink.

  Self-water dispersibility obtained by copolymerizing an unsaturated monomer having an aliphatic hydrocarbon group having 14 to 20 carbon atoms, a benzyl methacrylate monomer, and a styrene monomer as a fixability improving technique An aqueous inkjet recording liquid that uses a copolymer resin in the form of a hydrosol or an emulsion in an aqueous inkjet recording liquid is disclosed (for example, see Patent Document 1). This recording liquid has good storage stability, maintains a high printing density and printing quality even when it is given quick drying by osmotic drying, and is also excellent in friction resistance and water resistance.

  In addition, a water-based ink for ink jet recording containing self-dispersing pigments and self-emulsifying polymer particles containing a structural unit derived from an aromatic group-containing monomer is disclosed (for example, see Patent Document 2). The ink is said to be excellent in gloss when printed on special paper while satisfying a high printing density.

Furthermore, the basic technique regarding the manufacturing method of an aqueous emulsion polymer is disclosed (for example, refer patent document 3). According to the production method, an emulsified dispersion having excellent dispersion stability is obtained.
JP 2002-88285 A JP 2006-283003 A JP 53-39387 A

  However, in the production method described in Patent Document 1 or Patent Document 2, the polarity of the solvent changes suddenly during the phase inversion from the oil phase to the aqueous phase, and the association between the hydrophilic groups of the resin and the hydrophobic groups In some cases, the precipitation of the resin and the fusion of the particles are promoted by the mutual interaction and the like, making it difficult to form stable fine particles. In addition, only an aqueous dispersion having poor dispersion stability can be obtained, and the stability of the aqueous ink composition containing the aqueous dispersion inevitably tends to be low.

  Furthermore, in the method for producing an aqueous emulsion polymer described in Patent Document 3, isopropyl alcohol is used as a polymerization solvent and a phase inversion solvent. By adopting this method, particles having relatively high dispersion stability can be obtained. However, since isopropyl alcohol is used at the time of polymerization, it can be applied only to a combination of monomers having a high affinity with the solvent, and is not versatile. In some cases, it cannot be applied to a polymer containing a structural unit.

  The present invention has been made in view of such circumstances, and a method for producing an aqueous dispersion of a self-dispersing polymer excellent in dispersion stability, and an ink composition and ink having good fixability containing the aqueous dispersion. An object of the present invention is to provide a set and an image recording method using the ink composition or the ink set.

Specific means for solving the above problems are as follows.
<1> A copolymer containing a hydrophilic constituent unit and a hydrophobic constituent unit, derived from a monomer having an ethylenically unsaturated bond, an organic good solvent for dissolving the copolymer, and the copolymer A method for producing a self-dispersing polymer aqueous dispersion, comprising: a step of obtaining a copolymer solution containing a mixed solvent containing an organic poor solvent that does not dissolve; and a dispersion step of adding water to the copolymer solution.

<2> The organic good solvent is at least one selected from a ketone solvent, an ether solvent, and an ester solvent, and the organic poor solvent is an alcohol solvent, according to <1>. A method for producing an aqueous dispersion of a self-dispersing polymer.
<3> The method for producing an aqueous self-dispersing polymer dispersion according to <1> or <2>, wherein the mixed solvent has a content of the organic poor solvent of 30% by mass or more and 70% by mass or less.
<4> Any one of <1> to <3>, further including a solvent removal step of setting the content of the organic poor solvent to 0.05% by mass or more and 10% by mass or less of the copolymer after the dispersion step. A process for producing an aqueous dispersion of a self-dispersing polymer according to claim 1.
<5> The method for producing an aqueous self-dispersing polymer dispersion according to any one of <1> to <4>, wherein at least one of the hydrophilic structural units is a structural unit having a carboxyl group.
<6> At least one of the hydrophobic structural units is a structural unit derived from at least one of an acrylic ester monomer and a methacrylic ester monomer, and any one of the above <1> to <5> A process for producing an aqueous dispersion of a self-dispersing polymer as described in 1.

<7> Water-insoluble colored particles containing a colorant, and a self-dispersing polymer aqueous dispersion produced by the method for producing an aqueous self-dispersing polymer dispersion according to any one of <1> to <6>, A water-based ink composition containing
<8> An ink set comprising at least one water-based ink composition according to <7>.
<9> Image formation including an ink application step of applying the aqueous ink composition onto a recording medium using the aqueous ink composition according to <7> or the ink set according to <8>. Method.

  According to the present invention, there are provided a method for producing an aqueous dispersion of a self-dispersing polymer excellent in dispersion stability, an ink composition and an ink set containing the aqueous dispersion and having good fixability, and the ink composition. Alternatively, an image recording method using the ink set can be provided.

  Hereinafter, a method for producing a self-dispersing polymer aqueous dispersion, an aqueous ink composition, an ink set, and an image recording method according to the present invention will be described in detail. First, the manufacturing method of this polymer aqueous dispersion of this invention is demonstrated.

<Method for producing aqueous dispersion of self-dispersing polymer>
The method for producing an aqueous dispersion of a self-dispersing polymer of the present invention comprises a copolymer comprising a hydrophilic constituent unit derived from a monomer having an ethylenically unsaturated bond, and a hydrophobic constituent unit having an ethylenically unsaturated bond; A step of obtaining a copolymer solution comprising an organic good solvent that dissolves the copolymer and an organic poor solvent that does not dissolve the copolymer, and water is added to the copolymer solution And a dispersing step.
The aqueous dispersion of a self-dispersing polymer produced by such a production method becomes an aqueous dispersion having a fine particle size because phase inversion to an aqueous system is performed under a mild polarity change condition, and has excellent dispersion stability. is doing.

The self-dispersing polymer in the present invention is a copolymer comprising a hydrophilic structural unit derived from a monomer having an ethylenically unsaturated bond and a hydrophobic structural unit derived from a monomer having an ethylenically unsaturated bond. In the absence of a surfactant, it refers to a water-insoluble polymer that can be dispersed in an aqueous medium by a hydrophilic functional group (preferably a dissociable group or a salt thereof) of the polymer itself. In addition, the dispersion state here means an emulsified state (emulsion) in which a water-insoluble polymer is dispersed in an aqueous medium, and a dispersion state (suspension) in which a water-insoluble polymer is dispersed in an aqueous medium. ) Including both states.
The self-dispersing polymer is preferably a self-dispersing polymer that can be in a dispersed state in which a water-insoluble polymer is dispersed in a solid state, for example, from the viewpoint of ink fixability when contained in an aqueous ink composition.

  In the present invention, the dispersion state of the self-dispersing polymer means a solution in which 30 g of a water-insoluble polymer is dissolved in 70 g of an organic solvent (for example, methyl ethyl ketone), a neutralizing agent that can neutralize 100% of the dissociable group of the water-insoluble polymer ( After the salt-forming group is anionic, sodium hydroxide, acetic acid if it is cationic) and 200 g of water are mixed and stirred (apparatus: stirring apparatus with stirring blades, rotation speed 200 rpm, 30 minutes, 25 ° C.) It means a state in which even after removing the organic solvent from the mixed solution, it can be visually confirmed that the dispersed state exists stably at 25 ° C. for at least one week.

  The water-insoluble polymer means a polymer having a dissolution amount of 10 g or less when the polymer is dried at 105 ° C. for 2 hours and then dissolved in 100 g of water at 25 ° C., and the dissolution amount is preferable. Is 5 g or less, more preferably 1 g or less. The dissolution amount is the dissolution amount when neutralized with sodium hydroxide or acetic acid 100% according to the type of dissociable group of the water-insoluble polymer.

In the method for producing an aqueous dispersion of a self-dispersing polymer of the present invention, the mixed solvent is at least one organic good solvent that dissolves the copolymer and at least one organic poor solvent that does not dissolve the copolymer. It is characterized by including these. By using a mixed solvent, an aqueous dispersion having excellent dispersion stability can be obtained.
Here, the organic good solvent that dissolves the copolymer means an organic solvent in which the solubility of the self-dispersing polymer (copolymer) in the present invention is 10% by mass or more. Moreover, the organic poor solvent which does not melt | dissolve the said copolymer means the organic solvent whose solubility of the self-dispersing polymer (copolymer) in this invention is less than 10 mass%.

Examples of the organic good solvent in the present invention include ketone solvents such as methyl ethyl ketone and acetone, ether solvents such as 1,3-dioxane, 1,4-dioxane, 1,3-oxolane and tetrahydrofuran, and esters such as ethyl acetate. And amide solvents such as dimethylacetamide, dimethylformamide, N-methylpyrrolidone, and the like. In the present invention, at least one selected from ketone solvents, ether solvents, and ester solvents is preferable, and at least one selected from ketone solvents, ether solvents, and ester solvents having a boiling point of 100 ° C. or less. It is more preferable that it is at least one selected from methyl ethyl ketone, acetone, 1,3-dioxane, 1,4-dioxane, tetrahydrofuran and ethyl acetate.
The organic good solvents may be used alone or in combination of two or more.

Examples of the organic poor solvent in the present invention include alcohol solvents such as ethanol, isopropyl alcohol, n-butanol, s-butanol, t-butanol, and 2-ethylhexanol. Especially, it is preferable that it is an alcohol solvent whose boiling point is 100 degrees C or less, and it is more preferable that it is at least 1 sort (s) chosen from ethanol, isopropyl alcohol, and t-butanol.
The organic poor solvent may be used alone or in combination of two or more.

As the mixed solvent for dissolving the self-dispersing polymer resin in the present invention, from the viewpoint of dispersion stability of the self-dispersing polymer aqueous dispersion, the content of the organic poor solvent is preferably 30 to 70% by mass, and 30 to 60%. More preferably, it is mass%.
It can suppress that self-dispersing polymer resin precipitates from a mixed solvent because the content rate of an organic poor solvent is 70 mass% or less. Moreover, when the content of the organic poor solvent is 30% by mass or more, the polarity of the solvent can be prevented from changing abruptly during the phase inversion from the oil phase to the water phase. It is possible to effectively suppress the precipitation of the resin and the fusion of the particles due to the association between each other and the interaction between the hydrophobic groups, thereby enabling more stable formation of fine particles. That is, when the content is 30% by mass or more and 70% by mass or less, the phase inversion from the oil phase to the aqueous phase is smoothly performed, and a self-dispersing polymer aqueous dispersion having more excellent dispersion stability can be prepared.

Furthermore, in the present invention, from the viewpoint of dispersion stability of the self-dispersing polymer aqueous dispersion, the mixed solvent is an alcohol solvent having a content of 30 to 70% by mass and a good organic solvent having a content of 70 to 70%. It is preferably at least one selected from 30% by mass of a ketone solvent, an ether solvent, and an ester solvent, and the organic poor solvent is an alcohol solvent having a boiling point of 100 ° C. or lower with a content of 30 to 60% by mass. More preferably, the organic good solvent is at least one selected from a ketone solvent, an ether solvent, and an ester solvent having a content of 70 to 40% by mass and a boiling point of 100 ° C. or less.
Particularly preferably, the organic good solvent is at least one selected from methyl ethyl ketone, acetone, 1,3-dioxane, 1,4-dioxane, tetrahydrofuran and ethyl acetate, and the organic poor solvent is ethanol, isopropyl alcohol, t-butanol. It is a mixed solvent which is at least one selected from

The step of obtaining the copolymer solution is not particularly limited as long as the copolymer solution in which the copolymer is dissolved in the mixed solvent can be prepared, and is a mixed solvent containing an organic good solvent and an organic poor solvent. After preparing the copolymer, the copolymer may be dissolved in the mixed solvent to form a copolymer solution, or the copolymer may be dissolved in an organic good solvent and then mixed with an organic poor solvent to form a copolymer solution. .
In this invention, it is preferable that it is the process of mixing an organic poor solvent after melt | dissolving a copolymer in an organic good solvent.

The copolymer solution may further contain at least one neutralizing agent.
The neutralizing agent is used to neutralize some or all of the dissociable groups that the copolymer (self-dispersing polymer) may have, and the self-dispersing polymer forms a stable dispersion state in an aqueous medium. .

  When the self-dispersing polymer in the present invention has an anionic dissociative group as a dissociable group, examples of the neutralizing agent used include basic compounds such as organic amine compounds, ammonia, and alkali metal hydroxides. Examples of organic amine compounds include monomethylamine, dimethylamine, trimethylamine, monoethylamine, diethylamine, triethylamine, monopropylamine, dipropylamine, monoethanolamine, diethanolamine, triethanolamine, N, N-dimethyl-ethanolamine, N, N-diethyl-ethanolamine, 2-dimethylamino-2-methyl-1-propanol, 2-amino-2-methyl-1-propanol, N-methyldiethanolamine, N-ethyldiethanolanine, monoisopropanolamine, di Examples include isopropanolamine and triisopropanolamine. Examples of the alkali metal hydroxide include lithium hydroxide, sodium hydroxide, and potassium hydroxide. Among these, sodium hydroxide, potassium hydroxide, triethylamine, and triethanolamine are preferable from the viewpoint of stabilizing the dispersion of the self-dispersing polymer particles of the present invention in water.

  These neutralizing agents (preferably, basic compounds) are preferably used in an amount of 5 to 120 mol%, more preferably 10 to 110 mol%, based on 100 mol% of the dissociable group. More preferably, it is mol%. By making it 15 mol% or more, the effect of stabilizing the dispersion of particles in water is remarkably exhibited, and by making it 100 mol% or less, there is an effect of remarkably reducing the water-soluble component in the dispersed state.

  The dispersion step in the present invention is preferably a step of preparing an aqueous dispersion by mixing and stirring while adding at least water to the copolymer solution. By adding water to the copolymer solution dissolved in the mixed solvent in this way, a self-dispersing polymer aqueous dispersion having better dispersion stability can be obtained without requiring a strong shearing force.

In the present invention, the method of mixing and stirring is not particularly limited, and a generally used mixing and stirring device, or a dispersing machine such as an ultrasonic dispersing machine or a high-pressure homogenizer can be used as necessary.
In the present invention, at least water is added to the copolymer solution, but in addition to water, a neutralizing agent or an organic solvent (preferably an organic poor solvent) may be further added.

The method for producing an aqueous self-dispersing polymer dispersion of the present invention preferably includes a solvent removal step after the dispersion step. The solvent removal step is not particularly limited as long as at least a part of the mixed solvent can be removed, and a commonly used method such as distillation, distillation under reduced pressure, or the like can be applied.
In the present invention, a self-dispersing polymer aqueous dispersion having better dispersion stability can be obtained by including a solvent removal step.

  In the solvent removal step of the present invention, at least a part of the mixed solvent is removed. The content ratio of the organic good solvent and the organic poor solvent in the mixed solvent to be removed is not particularly limited, and a part of the water may be removed together with the mixed solvent.

In the present invention, the solvent removal step is performed by adding a mixed solvent so that the content of the organic poor solvent in the aqueous dispersion of the self-dispersing polymer is 0.05% by mass or more and 10% by mass or less of the solid content mass of the copolymer. It is preferable that it is the process of removing, and it is more preferable that they are 0.08 mass% or more and 8 mass% or less. The organic poor solvent is preferably an alcohol solvent.
The content of the organic poor solvent (preferably an alcohol solvent) contained in the aqueous self-dispersing polymer dispersion is 0.05% by mass or more of the solid content mass of the copolymer. The film-forming property in the aqueous ink composition containing the dispersion is improved, and the ink fixing property is further improved. Moreover, the fall of dispersion stability can be suppressed because it is 10 mass% or less, and the fall of the water resistance of the ink in a water-based ink composition can be suppressed.

After the solvent removal step in the present invention, the organic poor solvent contained in the self-dispersing polymer aqueous dispersion may be (a) an organic poor solvent in a mixed solvent in which the self-dispersing polymer resin is dissolved, or (b) An organic poor solvent newly added after substantially removing the organic solvent from the self-dispersing polymer aqueous dispersion may be used.
Among these, from the viewpoint of simplifying the production process and reducing foaming during solvent removal, (a) an organic poor solvent in a mixed solvent in which the self-dispersing polymer resin is dissolved is preferable.

  The average particle size of the self-dispersing polymer particles in the aqueous dispersion of the self-dispersing polymer in the present invention is preferably in the range of 10 to 100 nm, more preferably 10 to 80 nm, and further preferably 10 to 60 nm. Manufacturability is improved when the average particle diameter is 10 nm or more. Moreover, storage stability improves by setting it as an average particle diameter of 100 nm or less. On the other hand, when the thickness is less than 10 nm, the amount of components dissolved in water increases and the viscosity becomes high, which is not suitable for a water-based ink composition from the viewpoint of ejection properties. On the other hand, if it exceeds 100 nm, the fusion between polymer particles and the number of micron-sized coarse particles increase, and it becomes difficult to maintain a stable dispersion state.

In the present invention, the particle size distribution of the self-dispersing polymer particles is not particularly limited, and may have a wide particle size distribution or a monodispersed particle size distribution. Moreover, two or more kinds of self-dispersing polymer resins (copolymers) may be mixed and contained.
The average particle size and particle size distribution of the self-dispersing polymer particles can be measured using, for example, a dynamic light scattering method.

  The self-dispersing polymer in the present invention contains at least one hydrophobic constituent unit derived from a monomer having an ethylenically unsaturated bond. At least one of the hydrophobic structural units is preferably an acrylic ester and / or a methacrylic ester monomer.

  Acrylic esters, specifically, methyl acrylate, ethyl acrylate, n-propyl acrylate, isopropyl acrylate, n-butyl acrylate, isobutyl acrylate, sec-butyl acrylate, tert-butyl acrylate, amyl acrylate, hexyl acrylate, 2- Ethylhexyl acrylate, octyl acrylate, tert-octyl acrylate, 2-chloroethyl acrylate, 2-bromoethyl acrylate, 4-chlorobutyl acrylate, cyanoethyl acrylate, 2-acetoxyethyl acrylate, benzyl acrylate, methoxybenzyl acrylate, 2-chlorocyclohexyl acrylate , Cyclohexyl acrylate, furfuryl acrylate, tetrahydrofur Furyl acrylate, phenyl acrylate, 2-phenoxyethyl acrylate, 5-hydroxypentyl acrylate, 2,2-dimethyl-3-hydroxypropyl acrylate, 2-methoxyethyl acrylate, 3-methoxybutyl acrylate, 2-ethoxyethyl acrylate, 2- Butoxyethyl acrylate, 2- (2-methoxyethoxy) ethyl acrylate, 2- (2-butoxyethoxy) ethyl acrylate, glycidyl acrylate, 1-bromo-2-methoxyethyl acrylate, 1,1-dichloro-2-ethoxyethyl acrylate 2,2,2-tetrafluoroethyl acrylate, 1H, 1H, 2H, 2H-perfluorodecyl acrylate and the like.

  Methacrylic acid esters, specifically, methyl methacrylate, ethyl methacrylate, n-propyl methacrylate, isopropyl methacrylate, n-butyl methacrylate, isobutyl methacrylate, sec-butyl methacrylate, tert-butyl methacrylate, amyl methacrylate, hexyl methacrylate, cyclohexyl methacrylate , Benzyl methacrylate, chlorobenzyl methacrylate, octyl methacrylate, stearyl methacrylate, 2- (3-phenylpropyloxy) ethyl methacrylate, furfuryl methacrylate, tetrahydrofurfuryl methacrylate, phenyl methacrylate, 2-phenoxyethyl methacrylate, cresyl methacrylate, naphthyl methacrylate 2-Hido Xylethyl methacrylate, 4-hydroxybutyl methacrylate, triethylene glycol monomethacrylate, dipropylene glycol monomethacrylate, 2-methoxyethyl methacrylate, 3-methoxybutyl methacrylate, 2-ethoxyethyl methacrylate, methoxydiethylene glycol methacrylate, 2-iso-propoxyethyl Methacrylate, 2-butoxyethyl methacrylate, 2- (2-methoxyethoxy) ethyl methacrylate, 2- (2-ethoxyethoxy) ethyl methacrylate, 2- (2-butoxyethoxy) ethyl methacrylate, 2-acetoxyethyl methacrylate, 2-acetate Acetoxyethyl methacrylate, allyl methacrylate, glycidyl methacrylate, 2,2,2-tetra Le Oro methacrylate, 1H, 1H, 2H, 2H- perfluoro decyl methacrylate, and the like.

The self-dispersing polymer in the present invention contains at least one hydrophilic structural unit derived from a monomer having an ethylenically unsaturated bond. The hydrophilic structural unit is not particularly limited as long as it is derived from a hydrophilic group-containing monomer, and even if it is derived from one kind of hydrophilic group-containing monomer, it contains two or more hydrophilic groups. It may be derived from a monomer. The hydrophilic group is not particularly limited, and may be a dissociable group or a nonionic hydrophilic group.
In the present invention, the hydrophilic group is preferably a dissociable group and more preferably an anionic dissociable group from the viewpoint of promoting self-dispersion and the stability of the formed emulsified or dispersed state. Examples of the dissociable group include a carboxyl group, a phosphoric acid group, and a sulfonic acid group, and among them, a carboxyl group is preferable from the viewpoint of fixability when an aqueous ink composition is formed.

The hydrophilic group-containing monomer in the present invention is preferably a dissociable group-containing monomer from the viewpoint of self-dispersibility, and is preferably a dissociable group-containing monomer having a dissociable group and an ethylenically unsaturated bond. .
Examples of the dissociable group-containing monomer include an unsaturated carboxylic acid monomer, an unsaturated sulfonic acid monomer, and an unsaturated phosphoric acid monomer.

Specific examples of the unsaturated carboxylic acid monomer include acrylic acid, methacrylic acid, crotonic acid, itaconic acid, maleic acid, fumaric acid, citraconic acid, and 2-methacryloyloxymethyl succinic acid. Specific examples of the unsaturated sulfonic acid monomer include styrene sulfonic acid, 2-acrylamido-2-methylpropane sulfonic acid, 3-sulfopropyl (meth) acrylate, and bis- (3-sulfopropyl) -itaconate. It is done. Specific examples of unsaturated phosphoric acid monomers include vinylphosphonic acid, vinyl phosphate, bis (methacryloxyethyl) phosphate, diphenyl-2-acryloyloxyethyl phosphate, diphenyl-2-methacryloyloxyethyl phosphate, dibutyl-2- Examples include acryloyloxyethyl phosphate.
Among the dissociable group-containing monomers, unsaturated carboxylic acid monomers are preferable and acrylic acid and methacrylic acid are more preferable from the viewpoints of dispersion stability and ejection stability.

The molecular weight range of the self-dispersing polymer in the present invention is preferably 3000 to 200,000, more preferably 5000 to 150,000, and still more preferably 10,000 to 100,000 in terms of weight average molecular weight. By setting the weight average molecular weight to 3000 or more, the amount of water-soluble components can be effectively suppressed. Moreover, self-emulsification stability can be improved by making a weight average molecular weight or less into 200,000.
The weight average molecular weight can be measured by gel permeation chromatography (GPC).

  Specific examples of the self-dispersing polymer are listed below as exemplary compounds B-01 to B-10, but the present invention is not limited thereto. In addition, the parenthesis represents the mass ratio of the copolymer component.

B-01: Methyl methacrylate / methoxyethyl acrylate / benzyl methacrylate / methacrylic acid copolymer (44/15/35/6)
B-02: Methyl methacrylate / benzyl acrylate / phenoxyethyl methacrylate / acrylic acid copolymer (50/15/30/5)
B-03: Methyl methacrylate / phenoxyethyl acrylate / acrylic acid copolymer (45/50/5)
B-04: Isobutyl methacrylate / phenoxyethyl acrylate / benzyl methacrylate / methacrylic acid copolymer (43/16/35/6)
B-05: Methyl methacrylate / phenoxyethyl methacrylate / benzyl methacrylate / methacrylic acid copolymer (45/23/26/6)
B-06: Methyl methacrylate / benzyl methacrylate / methacrylic acid copolymer (39/55/6)
B-07: benzyl acrylate / methyl methacrylate / acrylic acid copolymer (55/40/5)
B-08: Phenoxyethyl methacrylate / benzyl acrylate / methacrylic acid copolymer (45/47/8)
B-09: Styrene / phenoxyethyl acrylate / butyl methacrylate / acrylic acid copolymer (5/48/40/7)
B-10: benzyl methacrylate / isobutyl methacrylate / cyclohexyl methacrylate / methacrylic acid copolymer (35/30/30/5)

The method for synthesizing the self-dispersing polymer in the present invention is not particularly limited, and it can be synthesized by copolymerizing the monomer mixture by a known polymerization method such as a solution polymerization method or a bulk polymerization method. Among these polymerization methods, the solution polymerization method is preferable from the viewpoint of droplet ejection stability when an aqueous ink composition is used. For example, a self-dispersing polymer can be synthesized by copolymerizing a mixture containing a monomer mixture and, if necessary, an organic solvent and a radical polymerization initiator in an inert gas atmosphere.
The synthesized self-dispersing polymer can be converted into a self-dispersing polymer aqueous dispersion by the method for producing an aqueous self-dispersing polymer dispersion of the present invention.

The aqueous self-dispersing polymer dispersion produced by the method for producing an aqueous self-dispersing polymer dispersion of the present invention has excellent dispersion stability. Therefore, for example, an ink composition containing the aqueous self-dispersing polymer dispersion can exhibit excellent storage stability and can exhibit better ink fixing properties. Further, by applying the ink composition to an ink jet ink composition, excellent ejection stability can be exhibited in addition to storage stability and ink fixability.
The aqueous self-dispersing polymer dispersion in the present invention may be used alone or in combination of two or more.

<Water-based ink composition>
The aqueous ink composition of the present invention contains at least one kind of water-insoluble colored particles containing a colorant and at least one kind of the above-mentioned self-dispersing polymer aqueous dispersion. By containing the self-dispersing polymer aqueous dispersion, the storage stability of the ink composition is excellent, and the fixability of the formed image is improved.

  The water-based ink composition of the present invention can be used not only for monochromatic image formation but also for full-color image formation. In order to form a full color image, a magenta color ink, a cyan color ink, and a yellow color ink can be used, and a black color ink may be further used to adjust the color tone. Further, red, green, blue, and white inks other than yellow, magenta, and cyan color inks, and so-called special color inks (for example, colorless) in the printing field can be used.

  The method for recording an image using the water-based ink composition of the present invention is not particularly limited, and a known image recording method can be used. For example, the image is coated by means such as an inkjet method, a copying method, a printing method, and the like. Examples thereof include a method of applying a water-based ink composition to a recording medium.

(A) Water-insoluble colored particles The water-insoluble colored particles in the present invention contain at least one colorant. As the colorant, known dyes, pigments and the like can be used without particular limitation. Among these, from the viewpoint of ink colorability, a colorant that is almost insoluble or hardly soluble in water is preferable. Specific examples include various pigments, disperse dyes, oil-soluble dyes, dyes forming J aggregates, and the like, and pigments are more preferable.
In the present invention, the water-insoluble pigment itself or the pigment surface-treated with a dispersant can be used as water-insoluble colored particles.

  There is no restriction | limiting in particular as a pigment in this invention, A conventionally well-known organic and inorganic pigment can be used. For example, polycyclic pigments such as azo lakes, azo pigments, phthalocyanine pigments, perylene and perinone pigments, anthraquinone pigments, quinacridone pigments, dioxazine pigments, diketopyrrolopyrrole pigments, thioindigo pigments, isoindolinone pigments, quinophthaloni pigments, basic Examples include dye lakes such as dye-type lakes and acid dye-type lakes, organic pigments such as nitro pigments, nitroso pigments, aniline black, and daylight fluorescent pigments, and inorganic pigments such as titanium oxide, iron oxide, and carbon black. Any pigment not described in the color index can be used as long as it can be dispersed in the aqueous phase. Further, it is of course possible to use a pigment obtained by surface-treating the above pigment with a surfactant, a polymer dispersing agent or the like, or graft carbon. Among the above pigments, it is particularly preferable to use an azo pigment, a phthalocyanine pigment, an anthraquinone pigment, a quinacridone pigment, or a carbon black pigment.

Specific examples of the organic pigment used in the present invention are shown below.
Examples of organic pigments for orange or yellow include C.I. I. Pigment orange 31, C.I. I. Pigment orange 43, C.I. I. Pigment yellow 12, C.I. I. Pigment yellow 13, C.I. I. Pigment yellow 14, C.I. I. Pigment yellow 15, C.I. I. Pigment yellow 17, C.I. I. Pigment yellow 74, C.I. I. Pigment yellow 93, C.I. I. Pigment yellow 94, C.I. I. Pigment yellow 128, C.I. I. Pigment yellow 138, C.I. I. Pigment yellow 151, C.I. I. Pigment yellow 155, C.I. I. Pigment yellow 180, C.I. I. And CI Pigment Yellow 185.

  Examples of organic pigments for magenta or red include C.I. I. Pigment red 2, C.I. I. Pigment red 3, C.I. I. Pigment red 5, C.I. I. Pigment red 6, C.I. I. Pigment red 7, C.I. I. Pigment red 15, C.I. I. Pigment red 16, C.I. I. Pigment red 48: 1, C.I. I. Pigment red 53: 1, C.I. I. Pigment red 57: 1, C.I. I. Pigment red 122, C.I. I. Pigment red 123, C.I. I. Pigment red 139, C.I. I. Pigment red 144, C.I. I. Pigment red 149, C.I. I. Pigment red 166, C.I. I. Pigment red 177, C.I. I. Pigment red 178, C.I. I. Pigment red 222C. I. Pigment violet 19 and the like.

Examples of organic pigments for green or cyan include C.I. I. Pigment blue 15, C.I. I. Pigment blue 15: 2, C.I. I. Pigment blue 15: 3, C.I. I. Pigment blue 15: 4, C.I. I. Pigment blue 16, C.I. I. Pigment blue 60, C.I. I. Pigment Green 7 and siloxane-crosslinked aluminum phthalocyanine described in U.S. Pat. No. 4,311,775.
Examples of organic pigments for black include C.I. I. Pigment black 1, C.I. I. Pigment black 6, C.I. I. Pigment black 7 and the like.

-Dispersant-
When the colorant in the present invention is a pigment, it is preferably dispersed in an aqueous solvent by a dispersant. The dispersant may be a polymer dispersant or a low molecular surfactant type dispersant. The polymer dispersant may be either a water-soluble dispersant or a water-insoluble dispersant.
The low molecular surfactant type dispersant (hereinafter sometimes referred to as “low molecular dispersant”) may be added for the purpose of stably dispersing the organic pigment in an aqueous solvent while keeping the ink at a low viscosity. it can. The low molecular dispersant herein is a low molecular dispersant having a molecular weight of 2000 or less. Moreover, 100-2000 are preferable and, as for the molecular weight of a low molecular dispersing agent, 200-2000 are more preferable.

  The low molecular weight dispersant has a structure including a hydrophilic group and a hydrophobic group. In addition, the hydrophilic group and the hydrophobic group may be independently contained in one molecule or more, and may have a plurality of types of hydrophilic groups and hydrophobic groups. In addition, a linking group for linking a hydrophilic group and a hydrophobic group can be appropriately included.

Examples of the hydrophilic group include an anionic group, a cationic group, a nonionic group, and a betaine type combining these.
The anionic group is not particularly limited as long as it has a negative charge, but may be a phosphate group, phosphonic acid group, phosphinic acid group, sulfuric acid group, sulfonic acid group, sulfinic acid group or carboxylic acid group. Preferably, it is a phosphoric acid group or a carboxylic acid group, more preferably a carboxylic acid group.

The cationic group is not particularly limited as long as it has a positive charge, but is preferably an organic cationic substituent, more preferably a cationic group containing nitrogen or phosphorus, and nitrogen. More preferably, it is a cationic group. Among these, a pyridinium cation or an ammonium cation is particularly preferable.
The nonionic group is not particularly limited as long as it has no negative or positive charge. For example, a polyalkylene oxide, polyglycerin, a part of sugar unit, etc. are mentioned.

In the present invention, the hydrophilic group is preferably an anionic group from the viewpoint of dispersion stability and aggregation of the pigment.
Moreover, when a low molecular weight dispersing agent has an anionic hydrophilic group, it is preferable that the pKa is 3 or more from a viewpoint of making it contact with an acidic process liquid and promoting aggregation reaction. The pKa of the low molecular dispersant in the present invention is determined experimentally from a titration curve by titrating a solution of 1 mol / L of the low molecular dispersant in tetrahydrofuran-water = 3: 2 (V / V) solution with an acid or alkaline aqueous solution. It is the calculated value.
Theoretically, if the pKa of the low molecular dispersant is 3 or more, 50% or more of the anionic groups are in a non-dissociated state when in contact with a treatment solution having a pH of about 3. Accordingly, the water solubility of the low molecular weight dispersant is remarkably lowered, and an agglomeration reaction occurs. That is, the aggregation reactivity is improved. From this viewpoint, it is preferable that the low molecular dispersant has a carboxylic acid group as an anionic group.

  On the other hand, the hydrophobic group may have any structure such as hydrocarbon-based, fluorocarbon-based, and silicone-based, but is particularly preferably hydrocarbon-based. Further, these hydrophobic groups may have a linear structure or a branched structure. The hydrophobic group may have a single chain structure or two or more chain structures, and may have a plurality of types of hydrophobic groups in the case of a structure having two or more chains.

  The hydrophobic group is preferably a hydrocarbon group having 2 to 24 carbon atoms, more preferably a hydrocarbon group having 4 to 24 carbon atoms, and further preferably a hydrocarbon group having 6 to 20 carbon atoms.

  Among the polymer dispersants in the present invention, a hydrophilic polymer compound can be used as the water-soluble dispersant. For example, natural hydrophilic polymer compounds include plant polymers such as gum arabic, tragan gum, guar gum, karaya gum, locust bean gum, arabinogalactone, pectin, quince seed starch, seaweeds such as alginic acid, carrageenan and agar. Examples include molecules, animal polymers such as gelatin, casein, albumin and collagen, and microorganism polymers such as xanthene gum and dextran.

  In addition, as hydrophilic polymer compounds chemically modified from natural products, fiber polymers such as methyl cellulose, ethyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, carboxymethyl cellulose, sodium starch glycolate, sodium starch phosphate, etc. And seaweed polymers such as alginic acid propylene glycol ester.

  Synthetic water-soluble polymer compounds include vinyl polymers such as polyvinyl alcohol, polyvinyl pyrrolidone, and polyvinyl methyl ether, acrylic polymers such as polyacrylamide, polyacrylic acid or alkali metal salts thereof, and water-soluble styrene acrylic resins. Resin, water-soluble styrene maleic acid resin, water-soluble vinyl naphthalene acrylic resin, water-soluble vinyl naphthalene maleic resin, polyvinyl pyrrolidone, polyvinyl alcohol, alkali metal salt of β-naphthalene sulfonic acid formalin condensate, quaternary ammonium, amino group, etc. And a polymer compound having a cationic functional group salt in the side chain.

  Among these, from the viewpoint of dispersion stability of the pigment, a polymer compound containing a carboxyl group is preferable. For example, an acrylic resin such as a water-soluble styrene acrylic resin, a water-soluble styrene maleic acid resin, a water-soluble vinyl naphthalene acrylic resin, A polymer compound containing a carboxyl group such as a water-soluble vinyl naphthalene maleic resin is particularly preferable.

  As the water-insoluble dispersant among the polymer dispersants, a polymer having both a hydrophobic part and a hydrophilic part can be used. For example, styrene- (meth) acrylic acid copolymer, styrene- (meth) acrylic acid- (meth) acrylic acid ester copolymer, (meth) acrylic acid ester- (meth) acrylic acid copolymer, polyethylene glycol ( Examples thereof include a meth) acrylate- (meth) acrylic acid copolymer and a styrene-maleic acid copolymer.

  The weight average molecular weight of the polymer dispersant in the present invention is preferably 3,000 to 200,000, more preferably 5,000 to 100,000, still more preferably 5,000 to 80,000, and particularly preferably 10,000. 000-60,000.

  Further, the mixing mass ratio of the pigment and the dispersant (pigment: dispersant) is preferably in the range of 1: 0.06 to 1: 3, more preferably in the range of 1: 0.125 to 1: 2. Preferably it is 1: 0.125 to 1: 1.5.

In the present invention, when a dye is used as the colorant, a water-insoluble carrier can be used as a water-insoluble colored particle. As the dye, known dyes can be used without particular limitation. For example, the dyes described in JP-A-2001-115066, JP-A-2001-335714, JP-A-2002-249677 and the like can be used in the present invention. It can be used suitably. The carrier is not particularly limited as long as it is insoluble in water or hardly soluble in water, and inorganic materials, organic materials, and composite materials thereof can be used. Specifically, the carriers described in JP-A-2001-181549, JP-A-2007-169418, etc. can be suitably used in the present invention.
The carrier holding the dye (water-insoluble colored particles) can be used as an aqueous dispersion using a dispersant. As the dispersant, the above-described dispersants can be suitably used.

  The water-insoluble colored particles in the present invention preferably contain a pigment and a dispersant, more preferably contain an organic pigment and a polymer dispersant, from the viewpoint of light resistance and quality of the image, and the organic pigment and the carboxyl group. It is particularly preferable to include a polymer dispersant.

In the present invention, the average particle size of the water-insoluble colored particles is preferably 10 to 200 nm, more preferably 10 to 150 nm, and still more preferably 10 to 100 nm. When the average particle size is 200 nm or less, the color reproducibility is good, and in the case of the ink jet method, the droplet ejection characteristics are good. Moreover, light resistance becomes favorable because an average particle diameter is 10 nm or more.
The particle size distribution of the water-insoluble colored particles is not particularly limited, and may be either a wide particle size distribution or a monodisperse particle size distribution. Further, two or more kinds of water-insoluble colored particles having a monodisperse particle size distribution may be mixed and used.
The average particle size and particle size distribution of the water-insoluble colored particles can be measured using, for example, a light scattering method.

In the present invention, the water-insoluble colored particles may be used alone or in combination of two or more.
Further, the content of the water-insoluble colored particles is preferably 1 to 25% by mass, more preferably 2 to 20% by mass, and more preferably 5 to 20% by mass with respect to the aqueous ink composition from the viewpoint of image density. % Is more preferable, and 5 to 15% by mass is particularly preferable.

The solid content of the self-dispersing polymer in the aqueous ink composition of the present invention is preferably 1 to 30% by mass with respect to the aqueous ink composition from the viewpoint of image glossiness, and 5 to 15%. More preferably, it is mass%.
In addition, the content ratio of the water-insoluble colored particles to the water-insoluble particles (water-insoluble colored particles / water-insoluble particles) in the water-based ink composition of the present invention is 1 / 0.5 to from the viewpoint of image scratch resistance. 1/10 is preferable, and 1/1 to 1/4 is more preferable.

-Water-soluble organic solvent-
The water-based ink composition of the present invention contains water as a solvent, but can further contain a water-soluble organic solvent. The water-soluble organic solvent can be contained as a drying inhibitor and a penetration enhancer.
The anti-drying agent can effectively prevent nozzle clogging that may occur due to drying of ink at the ink ejection port, particularly when the aqueous ink composition of the present invention is applied to an image recording method using an ink jet method. .

  The drying inhibitor is preferably a water-soluble organic solvent having a vapor pressure lower than that of water. Specific examples of the drying inhibitor include ethylene glycol, propylene glycol, diethylene glycol, polyethylene glycol, thiodiglycol, dithiodiglycol, 2-methyl-1,3-propanediol, 1,2,6-hexanetriol, Polyhydric alcohols represented by acetylene glycol derivatives, glycerin, trimethylolpropane, etc., polyvalent alcohols such as ethylene glycol monomethyl (or ethyl) ether, diethylene glycol monomethyl (or ethyl) ether, triethylene glycol monoethyl (or butyl) ether Lower alkyl ethers of alcohols, 2-pyrrolidone, N-methyl-2-pyrrolidone, 1,3-dimethyl-2-imidazolidinone, heterocyclic rings such as N-ethylmorpholine, sulfolane, dimethyls Sulfoxide, sulfur-containing compounds such as sulfolane, diacetone alcohol, polyfunctional compounds such as diethanolamine, and urea derivatives. Of these, polyhydric alcohols such as glycerin and diethylene glycol are preferred as the drying inhibitor. Moreover, said drying inhibitor may be used independently or may be used together 2 or more types. These drying inhibitors are preferably contained in the ink in an amount of 10 to 50% by mass.

  Further, the penetration accelerator is preferably used for the purpose of allowing the ink to penetrate better into the recording medium (printing paper). Specific examples of penetration enhancers include alcohols such as ethanol, isopropanol, butanol, di (tri) ethylene glycol monobutyl ether, 1,2-hexanediol, sodium lauryl sulfate, sodium oleate, and nonionic surfactants. Etc. can be used suitably. These penetration enhancers exhibit a sufficient effect when contained in the ink composition in an amount of 5 to 30% by mass. Further, it is preferable that the penetration enhancer is used within a range of an addition amount that does not cause printing bleeding and paper loss (print through).

In addition to the above, the water-soluble organic solvent can be used for adjusting the viscosity. Specific examples of water-soluble organic solvents that can be used to adjust the viscosity include alcohols (eg, methanol, ethanol, propanol, isopropanol, butanol, isobutanol, sec-butanol, t-butanol, pentanol, hexanol, Cyclohexanol, benzyl alcohol), polyhydric alcohols (for example, ethylene glycol, diethylene glycol, triethylene glycol, polyethylene glycol, propylene glycol, dipropylene glycol, polypropylene glycol, butylene glycol, hexanediol, pentanediol, glycerin, hexanetriol, Thiodiglycol), glycol derivatives (eg, ethylene glycol monomethyl ether, ethylene glycol monoethyl ether) Ter, ethylene glycol monobutyl ether, diethylene glycol monomethyl ether, diethylene glycol monobutyl ether, propylene glycol monomethyl ether, propylene glycol monobutyl ether, dipropylene glycol monomethyl ether, triethylene glycol monomethyl ether, ethylene glycol diacetate, ethylene glycol monomethyl ether acetate, Triethylene glycol monomethyl ether, triethylene glycol monoethyl ether, ethylene glycol monophenyl ether), amine (eg, ethanolamine, diethanolamine, triethanolamine, N-methyldiethanolamine, N-ethyldiethanolamine, morpholine, N-ethylmorpholine, Tylenediamine, diethylenetriamine, triethylenetetramine, polyethyleneimine, tetramethylpropylenediamine) and other polar solvents (eg, formamide, N, N-dimethylformamide, N, N-dimethylacetamide, dimethylsulfoxide, sulfolane, 2-pyrrolidone, N-methyl-2-pyrrolidone, N-vinyl-2-pyrrolidone, 2-oxazolidone, 1,3-dimethyl-2-imidazolidinone, acetonitrile, acetone).
In addition, a water-soluble organic solvent may be used independently and may use 2 or more types together.

-Other additives-
Examples of other additives in the present invention include, for example, antifading agents, emulsion stabilizers, penetration enhancers, ultraviolet absorbers, preservatives, antifungal agents, pH adjusters, surface tension adjusters, antifoaming agents, and viscosity adjusters. Well-known additives, such as an agent, a dispersing agent, a dispersion stabilizer, a rust preventive agent, a chelating agent, are mentioned. These various additives may be added directly after the aqueous ink composition is prepared, or may be added when the aqueous ink composition is prepared.

  The ultraviolet absorber is used for the purpose of improving image storability. Examples of ultraviolet absorbers include benzotriazoles described in JP-A Nos. 58-185677, 61-190537, JP-A-2-782, JP-A-5-97075, JP-A-9-34057, and the like. Compounds, benzophenone compounds described in JP-A No. 46-2784, JP-A No. 5-194433, US Pat. No. 3,214,463, etc., JP-B Nos. 48-30492, 56-211141, Cinnamic acid compounds described in, for example, Kaihei 10-88106, JP-A-4-298503, 8-53427, 8-239368, 10-182621, JP-A-8- No. 501291, etc., triazine compounds, Research Disclosure No. Compounds described in No. 24239, compounds that emit fluorescence by absorbing ultraviolet rays typified by stilbene-based and benzoxazole-based compounds, so-called fluorescent brighteners, can also be used.

  The anti-fading agent is used for the purpose of improving image storage stability. As the antifading agent, various organic and metal complex antifading agents can be used. Organic anti-fading agents include hydroquinones, alkoxyphenols, dialkoxyphenols, phenols, anilines, amines, indanes, chromans, alkoxyanilines, heterocycles, etc. Complex, zinc complex and the like. More specifically, Research Disclosure No. No. 17643, Nos. VII to I, J; 15162, ibid. No. 18716, page 650, left column, ibid. No. 36544, page 527, ibid. No. 307105, page 872, ibid. The compounds described in the patent cited in Japanese Patent No. 15162 and the compounds included in the general formulas and compound examples of typical compounds described on pages 127 to 137 of JP-A-62-215272 can be used.

Examples of the antifungal agent include sodium dehydroacetate, sodium benzoate, sodium pyridinethione-1-oxide, p-hydroxybenzoic acid ethyl ester, 1,2-benzisothiazolin-3-one and salts thereof. These are preferably used in the water-based ink composition in an amount of 0.02 to 1.00% by mass.
As the pH adjuster, a neutralizer (organic base, inorganic alkali) can be used. For the purpose of improving the storage stability of the aqueous ink composition, the pH adjuster is preferably added so that the aqueous ink composition has a pH of 6 to 10, and more preferably added to have a pH of 7 to 10. .

Examples of the surface tension adjusting agent include nonionic surfactants, cationic surfactants, anionic surfactants, betaine surfactants, and the like.
The addition amount of the surface tension adjusting agent is preferably an addition amount for adjusting the surface tension of the water-based ink composition to 20 to 60 mN / m in order to achieve good droplet ejection by the ink jet method, and is adjusted to 20 to 45 mN / m. The addition amount to be adjusted is more preferable, and the addition amount adjusted to 25 to 40 mN / m is more preferable. On the other hand, when ink is applied by a method other than the inkjet method, a range of 20 to 60 mN / m is preferable, and a range of 30 to 50 mN / m is more preferable.
The surface tension of the water-based ink composition can be measured using, for example, a plate method.

Specific examples of surfactants include fatty acid salts, alkyl sulfate esters, alkylbenzene sulfonates, alkyl naphthalene sulfonates, dialkyl sulfosuccinates, alkyl phosphate esters, naphthalene sulfonate formalin condensation in hydrocarbons Products, anionic surfactants such as polyoxyethylene alkyl sulfates, polyoxyethylene alkyl ethers, polyoxyethylene alkyl allyl ethers, polyoxyethylene fatty acid esters, sorbitan fatty acid esters, polyoxyethylene sorbitan fatty acid esters, polyoxy Nonionic surfactants such as ethylene alkylamine, glycerin fatty acid ester and oxyethyleneoxypropylene block copolymer are preferred. Further, SURFYNOLS (Air Products & Chemicals), which is an acetylene-based polyoxyethylene oxide surfactant, is also preferably used. An amine oxide type amphoteric surfactant such as N, N-dimethyl-N-alkylamine oxide is also preferred.
Furthermore, pages (37) to (38) of JP-A-59-157636, Research Disclosure No. The surfactants described in 308119 (1989) can also be used.
Also, fluorine (fluorinated alkyl) surfactants, silicone surfactants, and the like described in JP-A Nos. 2003-322926, 2004-325707, and 2004-309806 are disclosed. By using, the abrasion resistance can be improved.
These surface tension modifiers can also be used as antifoaming agents, and fluorine compounds, silicone compounds, chelating agents represented by EDTA, and the like can also be used.

The viscosity of the aqueous ink composition of the present invention is preferably in the range of 1 to 30 mPa · s, and in the range of 1 to 20 mPa · s, from the viewpoint of droplet ejection stability and agglomeration speed when ink is applied by an inkjet method. Is more preferable, the range of 2 to 15 mPa · s is more preferable, and the range of 2 to 10 mPa · s is particularly preferable.
In addition, when ink is applied by a method other than the inkjet method, a range of 1 to 40 mPa · s is preferable, and a range of 5 to 20 mPa · s is more preferable.
The viscosity of the water-based ink composition can be measured using, for example, a Brookfield viscometer.

<Ink set>
The ink set of the present invention includes at least one water-based ink composition. The ink set of the present invention is used in a recording method using the aqueous ink composition described above, and is particularly preferable as an ink set used in an ink jet recording method. Further, the ink set of the present invention can be used as an ink cartridge in which these are integrally or independently accommodated, and is preferable from the viewpoint of easy handling. An ink cartridge including an ink set is known in the art, and can be formed into an ink cartridge by appropriately using a known method.

<Image forming method>
The image forming method of the present invention includes an ink application step of applying the water-based ink composition onto a recording medium using the water-based ink composition or the ink set.
The water-based ink composition and ink set of the present invention can be used for general writing instruments, recorders, pen plotters, and the like, but are particularly preferably used for inkjet recording methods. The ink jet recording method in which the ink set or the ink cartridge of the present invention can be used includes any recording method in which the ink composition is ejected as droplets from a thin nozzle and the droplets are attached to a recording medium. Specific examples of the ink jet recording method in which the aqueous ink composition of the present invention can be used will be described below.

  The first method is a method called an electrostatic attraction method. In the electrostatic suction method, a strong electric field is applied between the nozzle and the acceleration electrode arranged in front of the nozzle, and droplet-like ink is continuously ejected from the nozzle, and the ink droplet passes between the deflection electrodes. In the meantime, by supplying a printing information signal to the deflection electrode, the ink droplets are blown toward the recording medium and the ink is fixed on the recording medium, or the image is recorded, or the ink droplets are not deflected, In this method, an image is fixed on a recording medium by ejecting ink droplets from a nozzle onto the recording medium in accordance with a print information signal. The ink set or ink cartridge of the present invention is preferably used in a recording method using this electrostatic suction method.

  The second method is a method for forcibly ejecting ink droplets from the nozzles by applying pressure to the ink liquid with a small pump and mechanically vibrating the ink jet nozzles with a quartz vibrator or the like. The ink droplet ejected from the nozzle is charged at the same time as it is ejected, and while the ink droplet passes between the deflection electrodes, a print information signal is given to the deflection electrode to fly the ink droplet toward the recording medium, This is a method for recording an image on a recording medium. The ink set or ink cartridge of the present invention is preferably used for this recording method.

  The third method is a method (piezo) in which an image is recorded on a recording medium by simultaneously applying a pressure and a printing information signal to the ink liquid by a piezoelectric element and ejecting ink droplets from a nozzle toward the recording medium. The ink set or ink cartridge of the present invention is preferably used for this recording method.

  In the fourth method, the ink liquid is heated and foamed using microelectrodes according to the print signal information, and the bubbles are expanded to eject the ink liquid from the nozzle toward the recording medium, thereby forming an image on the recording medium. This is a recording method (Bubble Jet (registered trademark)). The ink set or ink cartridge of the present invention is preferably used for this recording method.

  The recording medium in the present invention is not particularly limited, and examples thereof include plain paper, high-quality paper, and coated paper.

  The ink set or ink cartridge of the present invention is particularly preferable as an ink composition used when an image is recorded on a recording medium using an image recording method based on an ink jet recording method including the four methods described above. The recorded matter recorded using the ink set of the present invention has excellent image quality and is excellent in ink fixability.

  EXAMPLES Next, although an Example demonstrates this invention still in detail, this invention is not limited to a following example. Unless otherwise specified, “part” and “%” are based on mass.

[Preparation of aqueous dispersion of self-dispersing polymer]
<Example 1>
360.0 g of methyl ethyl ketone was charged into a 2-liter three-necked flask equipped with a stirrer, a thermometer, a reflux condenser, and a nitrogen gas inlet tube, and the temperature was raised to 75 ° C. While maintaining the temperature in the reaction vessel at 75 ° C., 158.4 g of methyl methacrylate, 54.0 g of methoxyethyl acrylate, 126.0 g of benzyl methacrylate, 21.6 g of methacrylic acid, 72 g of methyl ethyl ketone, and “V-601” (Wako Pure Chemical ( A mixed solution consisting of 1.44 g) was added dropwise at a constant speed so that the addition was completed in 2 hours. After completion of the dropwise addition, a solution consisting of 0.72 g of “V-601” and 36.0 g of methyl ethyl ketone was added. After stirring at 75 ° C. for 2 hours, a solution consisting of 0.72 g of “V-601” and 36.0 g of methyl ethyl ketone was further added. After stirring at 75 ° C. for 2 hours, the temperature was raised to 85 ° C., and stirring was further continued for 2 hours. The weight average molecular weight (Mw) of the obtained copolymer was 66000 (calculated in terms of polystyrene by gel permeation chromatography (GPC), and the columns used were TSKgel SuperHZM-H, TSKgel SuperHZ4000, TSKgel SuperHZ200 (manufactured by Tosoh Corporation)). there were.

  Next, 668.3 g of the polymerization solution was weighed, 388.3 g of isopropanol and 145.7 ml of 1 mol / L NaOH aqueous solution were added, and the temperature in the reaction vessel was raised to 80 ° C. Next, 720.1 g of distilled water was added dropwise at a rate of 20 ml / min to disperse in water. Thereafter, the temperature in the reaction vessel was maintained at 80 ° C. for 2 hours, 85 ° C. for 2 hours, and 90 ° C. for 2 hours under atmospheric pressure, and then the reaction vessel was depressurized, and isopropanol, methyl ethyl ketone, and distilled water totaled 913. 7 g was distilled off to obtain an aqueous dispersion (B-01Lx) of a self-dispersing polymer (B-01) having a solid content concentration of 28.0%. In addition, the number of each structural unit of the following compound example (B-01) represents mass ratio. Hereinafter, the same applies to each structural formula.

<Examples 2 to 5>
In the synthesis of (B-01) in Example 1, instead of methyl methacrylate, methoxyethyl acrylate, benzyl methacrylate, and methacrylic acid, the type and mixing ratio of each monomer were changed so that the mass ratio of the following exemplary compounds was obtained. Except that the neutralized base species and amount were changed as shown in Table 1, the same self-dispersing polymers (B-02) to (B-05) as shown below were obtained in the same manner as in Example 1, and these were obtained. Were used to obtain aqueous dispersions of self-dispersing polymers (B-02Lx) to (B-05Lx), respectively. The physical properties of the obtained self-dispersing polymer aqueous dispersions (B-02Lx) to (B-05Lx) are shown in Table 1.

<Examples 6 to 11>
In the process of obtaining the aqueous dispersion of (B-01) in Example 1 (phase inversion process), the phase inversion solvent was changed so that the solvent type and amount ratio shown in Table 1 were used instead of methyl ethyl ketone and isopropanol. As shown in Table 1, the self-dispersing polymer was changed to the following Exemplified Compounds (B-06) to (B-10) and the Exemplified Compound (B-03), and the neutralized base species and amount were as shown in Table 1. Except having changed, it carried out similarly to Example 1, and obtained the self-dispersion polymer aqueous dispersion (B-06Lx)-(B-11Lx). Table 1 shows the physical properties of the obtained self-dispersing polymer aqueous dispersions (B-06Lx) to (B-11Lx).

<Example 12>
In the synthesis of (B-01) in Example 1, instead of methyl methacrylate 158.4 g, methoxyethyl acrylate 54.0 g, benzyl methacrylate 126.0 g, and methacrylic acid 21.6 g, 324.0 g of styrene and 36. The following exemplary compound (BH-04) was obtained in the same manner as in Example 1 except that the amount was changed to 0 g. An aqueous dispersion (B-12Lx) was obtained in the same manner as in Example 1 using the obtained exemplary compound (BH-04). Table 1 shows the physical properties of the aqueous dispersion (B-12Lx) obtained.

<Comparative Example 1>
In the process of obtaining the aqueous dispersion of (B-01) of Example 1 (phase inversion process), instead of methyl ethyl ketone and isopropanol, the phase inversion solvent was changed so as to have the kind and amount ratio shown in Table 1. And the self-dispersing polymer aqueous dispersion was the same as in Example 1 except that the self-dispersing polymer species were changed as shown in Table 1, and the neutralizing base species and amount were changed as shown in Table 1. (BH-01Lx) was obtained. Table 1 shows the physical properties of the obtained (BH-01Lx).

<Comparative Example 2>
According to the production example of the self-emulsifying polymer particles described in paragraph No. [0041] of JP-A-2006-283003, all the same procedures except that the neutralized base species and amount are changed as shown in Table 1, and the following examples are given. Compound (BH-01) was obtained. In the following exemplified compounds, AS-6S is a trade name of styrene macromer (manufactured by Toagosei Co., Ltd.), and NK ESTER EH-4G is a trade name of polyethylene glycol methacrylate 2-ethylhexyl ether (Shin Nakamura Chemical Co., Ltd.). ). The physical properties of the aqueous dispersion (BH-03Lx) of the obtained exemplary compound (BH-01) are shown in Table 1.

<Comparative Example 3>
The following exemplary compound (BH-02) was obtained according to the production example of the copolymer resin liquid described in paragraph No. [0098] of JP-A-2002-88285. The physical properties of the aqueous dispersion (BH-04Lx) of the obtained exemplary compound (BH-02) are shown in Table 1.

<Comparative example 4>
An aqueous dispersion (BH-05Lx) containing a self-dispersing polyester (BH-03) was obtained according to the self-dispersing polyester aqueous dispersion production example described in paragraph Nos. [0073] and [0080] of JP-A-2007-277495. . Table 1 shows the physical properties of the aqueous dispersion (BH-05Lx) of the obtained self-dispersing polyester (BH-03).
The composition of the self-dispersing polyester (BH-03) is such that the acid component has a molar ratio of terephthalic acid / isophthalic acid / trimetic acid = 48/48/4, and the glycol component has a molar ratio of ethylene glycol / 2-methyl- It was 1,3-propanediol = 85/15.

<Comparative Example 5>
In the synthesis of (B-01) in Example 1, polymerization was carried out in the same manner as in Example 1 except that the solvent at the time of polymerization was changed from methyl ethyl ketone to isopropyl alcohol. After 5 hours from the start of the reaction, stirring was impossible, and an aqueous self-dispersing polymer dispersion could not be obtained.

Abbreviations in Table 1 are as follows.
MEK: methyl ethyl ketone EtOH: ethyl alcohol IPA: isopropyl alcohol t-BuOH: t-butyl alcohol Acetone: acetone NaOH: sodium hydroxide Amm: aqueous ammonia (2.8% solution)
TEA: Triethylamine TEDA: Triethylenediamine

  In Table 1, the particle diameter is a volume average particle diameter measured using a dynamic scattering method, and is a value measured by a conventional method using Microtrac UPA EX-150 (manufactured by Nikkiso Co., Ltd.). Moreover, in any of B-01Lx to B-12Lx and BH-05Lx, the residual alcohol solvent was present in the system in such a manner that the organic poor solvent for dissolving the self-dispersing polymer remained. In Table 1, the alcohol solvent content is a mass ratio (%) to the total solid content of the self-dispersing polymer.

<Example 11>
[Preparation of water-based ink composition]
<< Preparation of Cyan Ink C-1 >>
(Preparation of cyan dispersion as water-insoluble colored particles)
In a reaction vessel, 6 parts of styrene, 11 parts of stearyl methacrylate, 4 parts of styrene macromer AS-6 (manufactured by Toa Gosei), 5 parts of Blenmer PP-500 (manufactured by NOF Corporation), 5 parts of methacrylic acid, 0.05 of 2-mercaptoethanol A mixed solution of 24 parts of methyl ethyl ketone was prepared.
On the other hand, 14 parts of styrene, 24 parts of stearyl methacrylate, 9 parts of styrene macromer AS-6 (manufactured by Toa Gosei), 9 parts of Blenmer PP-500 (manufactured by NOF Corporation), 10 parts of methacrylic acid, 0.13 part of 2-mercaptoethanol, A mixed solution consisting of 56 parts of methyl ethyl ketone and 1.2 parts of 2,2′-azobis (2,4-dimethylvaleronitrile) was prepared and placed in a dropping funnel.

  Next, under a nitrogen atmosphere, the mixed solution in the reaction vessel was heated to 75 ° C. while stirring, and the mixed solution in the dropping funnel was gradually dropped over 1 hour. 2 hours after the completion of the dropwise addition, a solution prepared by dissolving 1.2 parts of 2,2′-azobis (2,4-dimethylvaleronitrile) in 12 parts by mass of methyl ethyl ketone was added dropwise over 3 hours, and further at 75 ° C. for 2 hours. And aged at 80 ° C. for 2 hours to obtain a polymer dispersant solution.

  A part of the obtained polymer dispersant solution was isolated by removing the solvent, the obtained solid content was diluted to 0.1% by mass with tetrahydrofuran, and the weight average molecular weight was measured by GPC. As a result, the isolated solid had a polystyrene equivalent weight average molecular weight of 25,000.

  Moreover, 5.0 g of the obtained polymer dispersant solution in terms of solid content, 10.0 g of cyan pigment pigment blue 15: 3 (manufactured by Dainichi Seika), 40.0 g of methyl ethyl ketone, 8.0 g of 1 mol / L sodium hydroxide, Ion-exchanged water 82.0 g and 0.1 mm zirconia beads 300 g were supplied to the vessel and dispersed with a ready mill disperser (manufactured by Imex) at 1000 rpm for 6 hours. The obtained dispersion was concentrated under reduced pressure using an evaporator until methyl ethyl ketone could be sufficiently distilled off, and concentrated until the pigment concentration became 10%, and a cyan dispersion C1 as water-insoluble colored particles was prepared. The average particle diameter of the obtained cyan dispersion liquid C1 was 77 nm.

  Then, using cyan dispersion C1 as water-insoluble colored particles and B-01Lx as a self-dispersing polymer aqueous dispersion, ink was prepared so as to have the following ink composition. After the preparation, coarse particles were removed with a 5 μm filter, and cyan ink C-1 was prepared as an aqueous ink composition.

<Ink composition of cyan ink C-1>
・ Cyan pigment (Pigment Blue 15: 3) manufactured by Dainichi Seika Co., Ltd. 4%
・ Polymer dispersant 2%
・ B-01Lx (Solid content conversion) 8%
・ Diethylene glycol (Wako Pure Chemical Industries) 10%
・ Glycerin 20%
・ Orphine E1010 (Nisshin Chemical) 1%
・ Ion-exchanged water added to make the total 100%

<< Preparation of Cyan Inks C-2 to 12, CH-1, CH-3 to CH-5, CH-7 >>
A water-based ink was prepared in the same manner as in the cyan ink C-1, except that the self-dispersing polymer aqueous dispersion B-01Lx shown in the following Table 2 was used instead of the self-dispersing polymer aqueous dispersion B-01Lx in the cyan ink C-1. Cyan inks C-2 to 12, CH-1, CH-3 to CH-5, and CH-7 of the composition were prepared, respectively. In addition, CH-7 was prepared without adding a self-dispersing polymer aqueous dispersion.
Table 2 shows the physical property values of the cyan ink obtained above immediately after preparation.

In Table 2, the term of viscosity is described according to the following evaluation criteria.
~Evaluation criteria~
○: Less than 6.5 mPa · s Δ ... 6.5 mPa · s or more and less than 10 mPa · s ×… 10 mPa · s or more

[Evaluation]
Each cyan ink prepared as described above (hereinafter sometimes simply referred to as “ink”) was subjected to an ink stability test over time, a droplet ejection test, and an image fixability test. The ink aging stability test is an evaluation of the stability of the particle size and viscosity before ink is ejected, that is, when the ink is stored in the ink storage tank (or cartridge). When discharging from the droplet ejection nozzle of the ink jet apparatus, problems such as clogging of the droplet ejection nozzle occur. Further, the droplet ejection test is an evaluation relating to the ejection directionality. When the ink viscosity is high, the nozzles are clogged, resulting in a directionality defect.

(Ink stability test over time)
10 mL of each ink was sealed in a 15 mL glass bottle, and the average particle size and viscosity were measured after (1) leaving at 60 ° C. for 14 days and (2) leaving at 40 ° C. for 3 months. Change rate of average particle size before and after standing [(average particle size after leaving-average particle size before leaving) / average particle size before leaving] and change rate of viscosity [(viscosity after leaving-before leaving) Viscosity) / viscosity before standing] was calculated. The evaluation criteria are as follows.
~Evaluation criteria~
A: The change rate of the average particle diameter or the change rate of the viscosity was less than 5%.
Δ: The change rate of the average particle diameter or the change rate of the viscosity was 5% or more and less than 10%.
X: The change rate of the average particle diameter or the change rate of the viscosity was 10% or more.
And evaluation of x was judged to be unusable. The results are shown in Table 3.

(Drip droplet stability test)
The droplet ejection stability test was conducted as follows. On Tokishi double-sided art N (Mitsubishi Paper), droplets were ejected using a Ricoh GELJETG717 printer head so that the resolution was 1200 × 600 dpi and the ink ejection amount was 12 pL. The droplet ejection stability was evaluated by observing the state after 5 hours of continuous hitting. Table 3 shows the droplet ejection stability test results. The evaluation criteria for the droplet ejection stability test in Table 3 are as follows. In addition, it was judged that evaluation of x was unusable.
~Evaluation criteria~
○: No discharge failure and no direction failure.
○ △: There was no ejection failure and a little direction failure occurred.
Δ: Almost no ejection failure and some direction failure occurred.
×: There were many ejection failures.

(Fixability test)
The ink was refilled into a cartridge of GELJETG717 manufactured by Ricoh, and an image printed with GELJETG717 was printed on Tokishi double-sided art N (Mitsubishi Paper), and the printed sample was dried at room temperature for 24 hours or more after printing. After drying, the sample was further left to stand at 60 ° C. for 1 hour in PDR-3KP manufactured by heating oven ESPEC Co., Ltd., and the fixability of the sample left for 12 hours was evaluated. The results are shown in Table 3. The evaluation criteria for the fixability test in Table 3 are as follows. Cellotape (registered trademark) (manufactured by Nichiban) and mending tape (3M) were applied to the coated sample so that the tape adhered to the entire surface, and then immediately peeled off. The color transfer to the peeled tape was evaluated according to the following evaluation criteria.
~Evaluation criteria~
○: No transfer of color was observed for both cello tape (registered trademark) and mending tape.
○ △: Slight color transfer was observed on at least one of the cello tape (registered trademark) and the mending tape.
Δ: Color transfer was observed in at least one of Cellotape (registered trademark) or Mending tape.
X: Color transfer was observed on both the cello tape (registered trademark) and the mending tape.

  First, as can be seen from Table 1, the self-dispersing polymer aqueous dispersions B-01Lx to B-10Lx and B-12Lx of the present invention were prepared by using an organic good solvent and an organic poor solvent as phase inversion solvents. Since the average particle size is as small as 15 to 80 nm, BH-01Lx and BH-03Lx to BH-05Lx of comparative self-dispersing polymer aqueous dispersions are as large as 95 nm or more. This result suggests that the dispersion stability of the self-dispersing polymer aqueous dispersion of the present invention is superior. This is reflected in the ink viscosity shown in Table 2, and it can be seen that the ink viscosity of the comparative example tends to be high while the ink viscosity of the present invention is low.

Further, as can be seen from Table 3, the ink of the present invention is excellent in stability over time. On the other hand, CH-1, CH-3 to CH-5, which have low dispersion stability and high ink viscosity, tended to increase in viscosity and particle size over time.
In addition, since all of the inks of the present invention have a low ink viscosity, there is no ejection failure and excellent droplet ejection stability, whereas self-dispersed polyester with high ink viscosity and low dispersion stability. The droplet ejection stability of CH-1, CH-3 to CH-5 and CH-7 containing the aqueous dispersion was low.

Further, the fixing properties of the inks C-1 to C-12 of the present invention containing a self-dispersing polymer aqueous dispersion containing an alcohol solvent are very good, but a self-dispersing polymer aqueous dispersion containing no alcohol solvent is used. The fixability of the contained CH-1, CH-3 to CH-5 was deteriorated by one rank. This is a result suggesting that, when the aqueous dispersion contains a small amount of an alcohol-based solvent, the film-forming property of the aqueous ink composition is improved and the ink fixing property is enhanced.
The fixability of the ink CH-7 containing no self-dispersing polymer aqueous dispersion was extremely deteriorated.
As described above, by using the ink containing the self-dispersing polymer aqueous dispersion of the present invention characterized by the production method, it is possible to provide an ink composition having unprecedented stable ejection properties and good fixing properties. I understand.

Claims (9)

A copolymer derived from a monomer having an ethylenically unsaturated bond, comprising a hydrophilic structural unit and a hydrophobic structural unit, an organic good solvent that dissolves the copolymer, and an organic that does not dissolve the copolymer A step of obtaining a copolymer solution containing a mixed solvent containing a poor solvent;
A dispersion step of adding water to the copolymer solution;
A process for producing an aqueous dispersion of a self-dispersing polymer comprising   The self-dispersing polymer aqueous solution according to claim 1, wherein the good organic solvent is at least one selected from a ketone solvent, an ether solvent, and an ester solvent, and the organic poor solvent is an alcohol solvent. A method for producing a dispersion.   The said mixed solvent is a manufacturing method of the self-dispersion polymer aqueous dispersion of Claim 1 or Claim 2 whose content rate of the said organic poor solvent is 30 mass% or more and 70 mass% or less.   The solvent removal process which makes content of the said organic poor solvent 0.05 mass% or more and 10 mass% or less of the said copolymer after the said dispersion | distribution process is included in any one of Claims 1-3. A process for producing the aqueous dispersion of a self-dispersing polymer as described.   The method for producing an aqueous self-dispersing polymer dispersion according to any one of claims 1 to 4, wherein at least one of the hydrophilic structural units is a structural unit having a carboxyl group.   6. The self according to claim 1, wherein at least one of the hydrophobic structural units is a structural unit derived from at least one of an acrylate monomer and a methacrylate monomer. A method for producing a dispersion polymer aqueous dispersion.   An aqueous solution comprising water-insoluble colored particles containing a colorant and a self-dispersing polymer aqueous dispersion produced by the method for producing a self-dispersing polymer aqueous dispersion according to any one of claims 1 to 6. Ink composition.   An ink set comprising at least one water-based ink composition according to claim 7.   An image forming method including an ink application step of applying the aqueous ink composition onto a recording medium using the aqueous ink composition according to claim 7 or the ink set according to claim 8.