JP2009190310A - Method for producing moisture-proof plywood and floor board using the moisture-proof plywood - Google Patents

Abstract

A method of manufacturing a moisture-proof plywood having excellent water resistance and moisture resistance, less warpage and twisting, and having dimensional stability, and a surface of the moisture-proof plywood obtained by the method as a base material. Provide a moisture barrier floor board.
A method for manufacturing a plywood in which a plurality of single plates 1, 2, 3, 4, 5 are heated and pressed in the presence of an adhesive T, wherein a moisture-proof sheet 6 is provided between the single plates. , 7 are disposed so as to be positioned symmetrically in the vertical direction, and the moisture-proof plywood A is manufactured by attaching the moisture-proof sheets 6 and 7 and laminating the single plates 1, 2, 3, 4, and 5 at the same time. Method. And a moisture-proof floor board C comprising the moisture-proof plywood A as a base material.
[Selection] Figure 1

Description

  The present invention relates to a method for manufacturing a plywood, and more particularly to a method for manufacturing a moisture-proof plywood that is manufactured by interposing a moisture-proof sheet between single plates constituting the plywood. Furthermore, it is related with the moisture-proof floor board obtained using this moisture-proof plywood.

  In recent years, the depletion of timber resources has progressed, making it difficult to obtain solid timber, and the price is also rising. Therefore, wood composite materials are widely used in which surface decorative materials such as veneer are attached to various wood base materials such as plywood, laminated wood, medium density fiberboard (MDF), and particle board, and the surface is designed with good appearance. is doing. However, since the above-mentioned wood composite material is essentially fibrous, it has the property that the moisture content changes according to changes in temperature and humidity. Therefore, when it is used as an interior material, there is a problem that when the indoor temperature and the indoor humidity are repeatedly changed, the whole wood composite material is warped or twisted or distorted due to a dimensional change.

  In order to solve the above problem, Japanese Patent Application Laid-Open No. 2000-43196 discloses that a moisture-coated moisture-proof resin layer is formed on at least the back side of a wooden board, and a decorative sheet is attached to the front side of the wooden board. A wood veneer is disclosed. And as said moisture-proof resin layer, thermoplastic resin such as polyolefin resin such as ethylene-vinyl acetate copolymer, butyral resin, polyethylene, ethylene-ethyl acrylate copolymer, polyamide resin composed of dimer acid and ethylenediamine, polyester resin, etc. A resin layer formed by melting and coating a hot melt adhesive or the like is shown.

And in the wooden decorative board disclosed in the above-mentioned known technology, the moisture-proof resin layer formed by melt-coating the hot melt adhesive on the wooden board prevents moisture and moisture from entering and leaving the wooden board. Therefore, it is described that, when the above-mentioned wooden decorative board is used for a door face material, for example, it is possible to prevent the door from warping and twisting.
JP 2000-43196 A

  Among the above-mentioned plywood, laminated wood, medium density fiberboard (MDF), particle board, and other woody base materials, in particular, plywood is excellent in strength, has good workability, and is easily available. It is widely used in fields such as flooring, wall materials and ceiling materials. However, it is difficult to say that the technique of directly forming the moisture-proof resin layer by melt-coating the above-mentioned hot melt adhesive directly on the wood base material can be applied to plywood.

  The present invention has been made in view of the above-described background art, and its purpose is excellent in water resistance and moisture resistance, has no warpage or twisting with respect to changes in temperature and humidity, and has dimensional stability. It is providing the manufacturing method of a moisture-proof plywood. It is another object of the present invention to provide a moisture-proof floor board obtained by using the moisture-proof plywood obtained by the method as a base material and making up the surface thereof.

  In order to solve the above-mentioned problem, the method for manufacturing a moisture-proof plywood according to the first aspect of the present invention is a method for manufacturing a plywood obtained by heating and pressing a plurality of single plates in the presence of an adhesive. In addition, the moisture-proof sheet is interposed between the single plates so as to be positioned vertically symmetrically, and the moisture-proof sheet is adhered and the single plates are laminated at the same time.

  As the adhesive for adhering the veneer, for example, a known emulsion adhesive that can be applied with a spreader as an aqueous emulsion, such as vinyl acetate, vinyl chloride-vinyl acetate copolymer, ethylene-vinyl acetate copolymer resin, is preferable. Used.

  The invention according to claim 2 of the present application is the method for manufacturing a moisture-proof plywood according to claim 1, wherein the moisture-proof sheet is interposed between the uppermost layer of the single plate constituting the plywood and the second layer from the top. The plywood is interposed between the lowermost layer of the single plate and the second layer from the bottom.

  The invention according to claim 3 of the present application is characterized in that, in the method for manufacturing a moisture-proof plywood according to claim 1, the moisture-proof sheet has a sandwich structure in which paper is attached to both surfaces of a plastic sheet. Yes. The plastic sheet is not particularly limited as long as it can be processed into a film. Polyolefin resins such as polyethylene and vinyl chloride, and polyester resins such as polyethylene terephthalate are preferably used. Among these, a polyethylene film is preferably used. Further, as paper, paraffin paper, thin paper, Japanese paper, high-quality paper and the like can be used without any particular limitation.

  The invention according to claim 4 of the present application is characterized in that, in the moisture-proof plywood manufacturing method according to claim 1, as the moisture-proof sheet, a sheet having a sandwich structure in which paper is pasted on both surfaces of a metal foil is used. . Aluminum foil is preferably used as the metal foil. Similarly to the above, the paper can be used without any particular limitation, such as paraffin paper, thin paper, Japanese paper, high-quality paper, and the like.

  In the moisture-proof floor board according to the second aspect of the present invention, a plurality of single boards are heated and pressurized in the presence of an adhesive so that the moisture-proof sheets are positioned vertically symmetrically between the single boards. It is characterized in that a veneer is stuck as a surface decorative material on a moisture-proof plywood obtained by interposing and sticking the moisture-proof sheet and laminating a single plate at the same time.

  In the moisture-proof plywood manufacturing method according to the first aspect of the present invention, in particular, a plurality of single plates are interposed in the presence of an adhesive so that the moisture-proof sheets are positioned symmetrically between the single plates. In addition, since the moisture-proof sheet is adhered and laminated together, the plywood can be manufactured and the moisture-proof property can be imparted to the plywood at the same time. be able to.

  In the manufacturing method of the moisture-proof plywood according to the invention of claim 2 of the present application, in particular, the moisture-proof sheet includes the uppermost layer of the single plate constituting the plywood and the second layer from the top, the lowermost layer of the single plate and the lower layer. In order to intervene between the first and second layers, when used as a base material for both the front and back sides, for example, as a base material for a floor board, in addition to preventing moisture penetration from the floor side and moisture penetration from the bottom side It can be carried out.

  In the method for producing a moisture-proof plywood according to the invention of claim 3 of the present application, in particular, as the moisture-proof sheet, a plastic sheet, for example, by using a sandwich structure in which paper is attached to both surfaces of a plastic sheet, for example, By using a polyethylene film, it is possible to prevent moisture penetration and moisture penetration. In addition, the porous nature of the paper makes it easier for the adhesive to penetrate, and the plastic sheet can be easily bonded to a single plate. Further, the hygroscopicity of the paper itself can be used.

  In the method of manufacturing a moisture-proof plywood according to the invention of claim 4 of the present application, in particular, as the moisture-proof sheet, a metal foil, for example, a sandwich structure in which paper is attached to both sides of an aluminum foil, In addition to preventing penetration, it is possible to prevent moisture from entering. In addition, the porous nature of the paper makes it easier for the adhesive to penetrate and the metal foil can be easily bonded to a single plate. Further, the hygroscopicity of the paper itself can be used.

  In the moisture-proof floor board according to the invention of claim 5 of the present application, a plurality of veneers are interposed between the veneer layers in the presence of an adhesive so that the moisture-proof sheets are positioned vertically symmetrically. A veneer is attached as a surface decorative material to a moisture-proof plywood obtained by carrying out wearing and laminating a single board at the same time, so it has the same appearance as natural wood, and is a toilet, kitchen, and washbasin It can be advantageously used for floors around water such as in places. In addition, since the moisture-proof sheet is interposed between the layers of the veneer, it is possible to suppress the transpiration of moisture from the veneer and maintain an appropriate moisture content, and prevent warping and twisting due to drying, It is possible to prevent the floor boards from warping and to prevent a gap between the floor boards.

  Hereinafter, an embodiment of a method for manufacturing a moisture-proof plywood according to the first invention of the present application will be described in detail with reference to the drawings. There are two types of plywood: a parallel plywood that laminates a plurality of single plates cut thin with a rotary cutter so that the grain is parallel, and a cross plywood that is laminated so that the grain is orthogonal, but in this embodiment, it is dry. The form which gives moisture-proof property to the crossing plywood which crosses and laminates | stacks the single board | plate which carried out 5 sheets is demonstrated.

  FIG. 1 is a process diagram schematically showing an embodiment of a method for producing a moisture-proof plywood according to the first invention of the present application. As shown in FIG. 1, the second-ply single plate 2 and the fourth-ply single plate 4 to which the adhesive T has been applied on both sides by the first double-sided coating spreader S <b> 1 are connected to the third-ply (center) single plate 3. Adhere to both surfaces to form the core layer B. Next, the moisture-proof sheet 6 is attached to the front side of the core layer B, that is, the upper surface of the single plate 2, and at the same time, the moisture-proof sheet 7 is attached to the back side of the core layer B, that is, the lower surface of the single plate 4.

  Next, the first-ply single plate 1 and the fifth-ply single plate 5 in which the adhesive is applied on both sides by the second double-side coating spreader S2 on both surfaces of the three-layer core layer B that has been moisture-proofed as described above. Are laminated and pressed. By doing so, the moisture-proof sheet 6 is adhered between the first and second plies, and the two single plates 1 and 2 of the first and second plies are laminated. Similarly, the lamination of the single plates 4 and 5 of the fourth ply and the fifth ply and the adhesion of the moisture-proof sheet 7 are performed simultaneously. Thus, moisture-proof plywood A waterproofed on the front side and the back side can be obtained with good workability by simultaneously performing moisture-proofing and bonding of the single plates.

  FIG. 2 is a cross-sectional view showing the configuration of the moisture-proof sheets 6 and 7 used in the present embodiment. As shown in FIG. 2, as the moisture-proof sheet 6 (7), a sandwich-type moisture-proof sheet is used in which paper is attached to both surfaces of a polyethylene sheet (PE) used as a plastic sheet by a tackifier such as rosin. . The polyethylene sheet (PE) is durable against moisture and excellent in moisture impermeability, and the paper is excellent in adhesiveness to a single plate, and thus can be laminated firmly. Furthermore, since the paper itself has a hygroscopic property, the moisture resistance of the moisture-proof plywood A can be improved.

  FIG. 3 is an enlarged sectional view showing the moisture-proof plywood A. As shown in FIG. As shown in FIG. 3, the moisture-proof sheets 6 and 7 are interposed between the first ply board 1 and the second ply board 2 of the cross plywood having five layers, and the fifth ply of the lowermost layer. It is interposed between the single plate 5 and the single plate 4 of the fourth ply. In this way, when used as a floorboard around the water in toilets, kitchens, washrooms, etc., with surface makeup applied, it prevents the water that spills on the floor from entering the floorboard and causing the plywood to delaminate. In addition, moisture can be prevented from entering under the floor.

  FIG. 4 is a perspective view showing a moisture-proof floor board C according to the second invention of the present application obtained by sticking the veneer 8 to the surface of the moisture-proof plywood A manufactured as described above. As shown in FIG. 4, the moisture-proof floorboard C uses the moisture-proof plywood A as a base material, and thus has a good appearance similar to that of natural wood, such as a toilet, kitchen, toilet, etc. It is preferably used for the construction and renovation of floors around water.

  The surface of the veneer 8 is coated with a transparent paint, an ultraviolet curable paint, such as an acrylic resin paint, an amino alkyd resin paint, or a urethane resin paint, and is irradiated with ultraviolet rays to provide a clear or semi-clear paint. A film may be formed. This coating film functions as a protective layer and is excellent in moisture resistance, and even when tableware is dropped, the moisture-proof floor board C having excellent impact resistance that does not easily scratch the surface can be obtained.

  In addition, when the floor heating device which is applied to a living room other than the above-mentioned water-split area and has been popular in recent years is constructed, the moisture-proof sheets 6 and 7 are interposed between the single-plate layers. It is possible to suppress the transpiration of water from the water and maintain an appropriate water content. Therefore, it is possible to prevent warpage and twisting due to room air dried by floor heating, suppress warpage of the floor boards, and prevent gaps between the floor boards.

  In addition, although embodiment mentioned above described the example which interposed the moisture-proof sheet | seat in the plywood which consists of 5 single board | plates, it is not restricted to 5 sheets, You may use 7 single sheets or 9 sheets. The present invention can also be applied to the case where three single plates are used. Thus, the manufacturing method of the moisture-proof plywood according to the present invention can be freely changed in design, and belongs to the technical scope of the present invention unless departing from the scope of the claims.

Process drawing which shows typically embodiment of the manufacturing method of the moisture-proof plywood concerning 1st invention of this application. Sectional drawing which shows the structure of the moisture-proof sheet | seat used in embodiment of the manufacturing method of the moisture-proof plywood concerning this-application 1st invention. Sectional drawing which expands and shows the moisture-proof plywood shown in the said FIG. The perspective view which shows the moisture-proof floor board which concerns on this-application 2nd invention obtained by sticking a veneer on the surface of the moisture-proof plywood manufactured by this-application 1st invention.

Explanation of symbols

A Moisture-proof plywood according to the first invention of the present application B Core layer C according to the first invention of the present application Moisture-proof floor board S1 according to the second invention of the present application S1 First double-sided coating spreader S2 Second double-sided coating spreader T Adhesive 1 First ply single plate 2 2 ply veneer 3 3 ply veneer 4 4 ply veneer 5 5 ply veneer 6 moisture proof sheet 7 moisture proof sheet 8 veneer

Claims (5)

  A method for producing a plywood by heating and pressing a plurality of veneers in the presence of an adhesive, wherein a moisture-proof sheet is interposed between the layers of the veneer so as to be vertically symmetrical, The manufacturing method of a moisture-proof plywood characterized by performing sticking and lamination | stacking of a single board simultaneously.   The moisture-proof sheet is interposed between the uppermost layer of the single plate constituting the plywood and the second layer from the top, and is interposed between the lowermost layer of the single plate constituting the plywood and the second lower layer. A method for producing the moisture-proof plywood according to 1.   The method for producing a moisture-proof plywood according to claim 1, wherein the moisture-proof sheet uses a sandwich structure in which paper is adhered to both surfaces of a plastic sheet.   The method for producing a moisture-proof plywood according to claim 1, wherein the moisture-proof sheet is a sandwich structure in which paper is attached to both surfaces of a metal foil.   A plurality of veneers are heated and pressed in the presence of an adhesive, and moisture-proof sheets are interposed between the layers of the veneers so as to be positioned vertically symmetrically. A moisture-proof floor board obtained by attaching a veneer as a surface decorative material to a moisture-proof plywood obtained simultaneously.