JP2004169237A - Aramid combined filament yarn - Google Patents

Aramid combined filament yarn Download PDF

Info

Publication number
JP2004169237A
JP2004169237A JP2002338891A JP2002338891A JP2004169237A JP 2004169237 A JP2004169237 A JP 2004169237A JP 2002338891 A JP2002338891 A JP 2002338891A JP 2002338891 A JP2002338891 A JP 2002338891A JP 2004169237 A JP2004169237 A JP 2004169237A
Authority
JP
Japan
Prior art keywords
yarn
aramid
component
rubber
multifilament
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2002338891A
Other languages
Japanese (ja)
Other versions
JP4324901B2 (en
Inventor
Kazuto Miwa
和人 三輪
Minoru Shiojima
実 塩島
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toray Textiles Inc
Original Assignee
Toray Textiles Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toray Textiles Inc filed Critical Toray Textiles Inc
Priority to JP2002338891A priority Critical patent/JP4324901B2/en
Publication of JP2004169237A publication Critical patent/JP2004169237A/en
Application granted granted Critical
Publication of JP4324901B2 publication Critical patent/JP4324901B2/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

<P>PROBLEM TO BE SOLVED: To provide a new aramid combined filament yarn having remarkably improved adhesion to rubbers and usable as a reinforcing material for rubbers and plastics without using an adhesion improving treatment for some uses. <P>SOLUTION: The aramid combined filament yarn is at least composed of an aramid multifilament yarn A and a multifilament yarn B and has loops and loosened parts on the surface of the yarn. <P>COPYRIGHT: (C)2004,JPO

Description

【0001】
【発明の属する技術分野】
本発明は、2種類のマルチフィラメント糸からなり、少なくとも1成分がアラミドフィラメント糸であるアラミド混繊糸に関するものである。
【0002】
【従来の技術】
従来から、アラミドマルチフィラメント糸は、高弾性、高強力、耐熱性の特性を活用して、ゴムやプラスチックの補強剤として使用されている。
【0003】
該用途においては、アラミドフィラメント糸は、ゴムやプラスチックと接着される必要があるが、アラミドフィラメント自体はゴムとの接着性が悪く、このゴムとの接着性を向上させるために、例えば、別途に予め、接着性向上処理を行う必要があった。
【0004】
すなわち、例えば、ゴムとの接着性が改良されたポリエステル繊維およびアラミド繊維を得るため、該繊維を特定の接着剤で被覆するという接着性向上処理法が提案されている(特許文献1)。
【0005】
しかしながら、このような方法は、接着性向上のための処理を行うことが必要であることから製造工程が複雑になり、コスト高になるという問題があった。
【0006】
【特許文献1】特開2001−146686号公報
【0007】
【発明が解決しようとする課題】
本発明の目的は、従来技術の上記課題を解決せんとするものであって、ゴムとの接着性が著しく向上されていて、用途によっては接着性向上処理なしでも、ゴムやプラスチックの補強剤として使用することのできる新規なアラミド混繊糸を提供することにある。
【0008】
【課題を解決するための手段】
前述した目的を達成するため、本発明のアラミド混繊糸は、以下の構成からなるものである。
【0009】
すなわち、少なくともアラミドマルチフィラメント糸A成分とマルチフィラメント糸B成分で構成され、かつ糸表面にループやタルミを有することを特徴とするアラミド混繊糸である。
【0010】
かかる本発明のアラミド混繊糸において、用途に応じて好ましくは、マルチフィラメント糸B成分が非熱可塑性繊維であるものであり、あるいは、他の用途に応じて好ましくは、マルチフィラメント糸B成分が熱可塑性繊維であるものである。
【0011】
また、好ましくは、下記式で表される糸長差が0%より大きく、20%以下であるものである。
【0012】
糸長差(%)={〔YL(B)―YL(A)〕/YL(A)}×100
YL(A):アラミド混繊糸の単位長さ当たりに含まれるアラミドマルチフィラメント糸A成分の長さ
YL(B):アラミド混繊糸の単位長さ当たりに含まれるマルチフィラメント糸B成分の長さ
【0013】
【発明の実施の形態】
以下、更に詳しく本発明のアラミド混繊糸について説明をする。
【0014】
本発明のアラミド混繊糸は、成分A糸と成分B糸を少なくとも含んでなる混繊糸であって、ここで、成分A糸たるアラミドマルチフィラメント糸と、成分B糸たるマルチフィラメント糸とを含んで基本的に構成されてなるものである。
【0015】
本発明において、マルチフィラメント糸とは、フィラメントが複数本集まった繊維束を称する。
【0016】
また、本発明において、成分A糸たるアラミドマルチフィラメント糸は、アラミド繊維からなるマルチフィラメント糸をいい、メタ系アラミドマルチフィラメント糸と、パラ系アラミドマルチフィラメント糸のいずれでも良いが、用途に応じて、これらメタ系アラミドマルチフィラメント糸と、パラ系アラミドマルチフィラメント糸を適宜に区別して用いることができ、特に、高強度、高弾性の点でパラ系アラミドマルチフィラメント糸であることが好ましい。
【0017】
なお、本発明でいうアラミド繊維とは、芳香族環がアミド結合で結合された繰り返し単位が全体の少なくとも80%以上を占める重合体からなる繊維を意味する。これらの重合体または共重合体からなるアラミド繊維の代表例としては、ポリパラフェニレンテレフタラミド繊維、ポリメタフェニレンテレフタラミド繊維およびコポリパラフェニレン−3,4’−オキシジフェニレンテレフタラミド繊維などがある。
【0018】
また、本発明の成分B糸たるマルチフィラメント糸は、用途に応じて非熱可塑性繊維または熱可塑性繊維を適宜選択して用いることができる。高弾性、高強力、耐熱性を重視する場合は、非熱可塑性繊維を選択するのがよい。一方、混繊糸に適度な熱収縮率を付与したい場合には熱可塑性繊維を選択するのがよい。
【0019】
非熱可塑性繊維の例としては、メタ系アラミド繊維、パラ系アラミド繊維がある。高強度、耐熱性をともに重視する場合は、パラ系アラミド繊維をB糸として選択するのがよい。耐熱性のみを重視する場合はメタ系アラミドをB糸として選択するのがよい。
【0020】
該成分B糸たるマルチフィラメント糸として使用することのできる熱可塑性繊維の例としては、ポリエステル、またはナイロンマルチフィラメント糸がある。
【0021】
本発明者らの知見によれば、特にゴムとの接着性を重視する場合は、ナイロンマルチフィラメント糸を選択することが好ましい。
【0022】
本発明においては、好ましくは、下記式で表される糸長差が0%より大きく、20%以下のものであり、より好ましくは5%以上、15%以下であるものである。すなわち、このような糸長差を有する本発明にかかるアラミド混繊糸をゴムなどの補強材として用いた場合、該アラミド混繊糸とゴムとを接着した際に、ゴムが成分B糸によって生じたタルミやループの隙間に回り込んで投錨効果を発揮することにより、ゴムとの接着性が向上するからである。一方、糸長差が0%のときは成分Bによるタルミやループの発生がほとんどなく、ゴムの投錨効果を発揮させることが難しく、接着性が著しく劣ることとなる。
【0023】
また、糸長差が20%を越えると、成分Bにより生じたループやタルミが大きくなりすぎて、糸のパッケージからの解舒性が悪くなり、解舒中に糸破壊を起こる場合があり使用しずらくなる傾向を示すので好ましくない。
【0024】
本発明のアラミド混繊糸の好ましい繊度範囲は60〜8000デシテックスであり、該糸の用途に応じて適宜に変更するのが好ましい。例えば、自動車用ホースの補強糸に使用する場合は500〜2000デシテックスが好ましい。
【0025】
また、アラミドマルチフィラメント糸A成分の繊度範囲は、好ましくは30〜4000デシテックス、マルチフィラメント糸B成分の繊度範囲は、好ましくは30〜4000デシテックスの範囲内である。
【0026】
また、成分A、B共に単繊維繊度は0.3〜20デシテックスの範囲内のものが好ましく、混繊時の加工性を考慮すると、特に1〜6デシテックスの範囲内のものが好ましい。
【0027】
アラミドマルチフィラメント糸A成分とマルチフィラメント糸B成分の混繊範囲(重量比)は、A/B=20/80〜80/20 の範囲内が好ましく、
成分Aの高強度、高弾性の特性を生かすために、特にA/B=30/70〜70/30の範囲内が好ましい。
【0028】
本発明に用いられるマルチフィラメントの断面形状は特に限定はされなく、丸断面、異形断面、中空断面等のいずれもが使用できる。また、マルチフィラメント内のフィラメント間で、太さや断面形状等が異なっていてもよい。
【0029】
本発明のアラミド混繊糸を製造するには、成分Aフィラメント糸と、成分Bフィラメント糸を混繊することが必要であり、該混繊をするには、例えば、成分AをフィードローラーA、成分BをフィードローラーBの別々のフィードローラーから混繊ノズルに供給し、混繊ノズルから出た糸をデリベリーローラーで送り出し、巻き取りローラーで巻き取れば良い。このときに糸表面にループやタルミを有せしめるには、フィードローラーの速度をデリベリーローラーの速度より早くすればよい。また、糸長差を0%より大きく、20%以下とするためには、フィードローラーBの速度を該糸長差に対応した分だけフィードローラーAの速度より速くすればよい。現実に速くする割合は、実際に後述の糸長差測定法により糸長差を測定して調節するのがよい。
【0030】
ここで、混繊ノズルは整流交絡ノズル、乱流交絡ノズルなどを使用することができる。中でもより好ましくはループやタルミが発生しやすい乱流交絡ノズルを使用することである。
【0031】
混繊ノズルに供給する圧縮空気の圧力は、特に限定されるものではないが、本発明者らの知見によれば、0.2〜1.2MPaが好ましく、より好ましくは0.4〜1.0MPaである。圧力は混繊糸の強度を測定し、適宜調節すればよい。また、ループやタルミの形成力を向上させるために、混繊ノズルに供給する直前に一方の成分または両方の成分に水を付与すること等も適宜に選択できる。さらに、ループおよびタルミの表面処理を行うためにデリベリーローラーと巻き取りローラーの間にセットヒーターを適宜設けることもできる。
【0032】
図1と図2は、いずれも本発明のアラミド混繊糸を説明するための糸形態の一例を示した糸外観概略モデル図である。
【0033】
図1に示した本発明のアラミド混繊糸は、アラミドフィラメント糸A成分が芯部を構成し、アラミドフィラメント糸B成分糸が鞘部を構成している形態を図示したものである。
【0034】
図2に示した本発明のアラミド混繊糸は、アラミドフィラメント糸A成分が芯部を構成し、ポリエステルフィラメント糸B成分糸が鞘部を構成している形態を図示したものである。
【0035】
本発明のアラミド混繊糸は、ゴム資材の補強剤用途に用いるのが適しているものである。
【0036】
ゴム資材としては、各種ホース、ベルト、タイヤ、シートなどがあるが、中でも耐熱性を要求されるブレーキホース等の自動車用ホースが好ましい。アラミド繊維の耐熱性、高強力等の各種特性を利用することができるからである。
【0037】
【実施例】
以下、実施例によって本発明を説明するが、本発明はこれらの実施例に限定されるものではない。実施例中に記載の特性の評価方法は次の通りである。
<ゴムとの接着力の評価>
剥離テスト1:
タイヤコードで使用することを想定して、糸7本を未加硫のゴムブロックに糸が重ならないように表層近くに埋め、160℃で30分間加硫を行って糸とゴムを接着し、長さ250mm×幅30mmの試料とする。次に、引張試験機で両端の2本を除く糸5本をゴムブロックから引張速度100mm/minで剥離するときの剥離力(N/5本)を測定した。
【0038】
剥離テスト2:
ゴムホースの補強糸として使用することを想定して、糸を未加硫のゴムブロックに隙間なく並べて表層近くに埋め、160℃で30分間加硫を行って糸とゴムを接着し、長さ250mm×幅30mmの試料とする。次に引張試験機で20mm幅の糸を引張速度100mm/minで剥離するときの剥離力(N/20mm)を測定した。
<糸長差>
糸に荷重2.94mN/dtexを掛け、検撚機に長さ5cmで固定する。このときに糸に撚りが入っている場合は検撚機を回して、撚りをほどいておく。
【0039】
荷重を外して、検撚機に糸を固定したまま、A成分とB成分を丁寧に分離する。このときに針、ピンセットなどの補助具を使うと分離しやすいので極力使用する。
【0040】
再び荷重2.94mN/dtexを掛ける。A成分は張力が掛かり張った状態になり、B成分はA成分より糸長が長いので、張力が掛からず弛んだ状態になる。 この状態の糸長を測定する。この値をYL(A)とする。次にA成分を鋏で切断する。今度はB成分に張力が掛かり張った状態になる。この状態の糸長を測定する。この値をYL(B)とする。
【0041】
次式に従い、糸長差を計算する。小数点以下は四捨五入する。
【0042】
糸長差(%)={〔YL(B)―YL(A)〕/YL(A)}×100
試験は、一試料糸からランダムに試験サンプル糸を計3本採取して合計3回の測定を行い、該3つの測定値を平均して糸長差とする。
実施例1
成分Aのパラ系アラミドマルチフィラメント糸(800デシテックス、490フィラメント)、成分Bのパラ系アラミドマルチフィラメント糸(800デシテックス、490フィラメント)を流体乱流ノズルで混繊し、糸長差10%の混繊糸を得た。
【0043】
被着ゴムとしてタイヤ用SBR系ゴムを用いて得られた糸についての剥離テスト1を行った。
【0044】
また、被着ゴムとしてブレーキホース用EPDM系ゴムを用いて、得られた糸についての剥離テスト2を行った。結果を表1に示す。
実施例2
成分Aのパラ系アラミドマルチフィラメント糸(800デシテックス、490フィラメント)、成分Bのポリエステルマルチフィラメント糸(800デシテックス、140フィラメント)を流体乱流ノズルで混繊し、糸長差10%の混繊糸を得た。
【0045】
被着ゴムとしてタイヤ用SBR系ゴムを用いて、得られた糸についての剥離テスト1を行った。
【0046】
また、被着ゴムとしてブレーキホース用EPDM系ゴムを用いて、得られた糸についての剥離テスト2を行った。結果を表1に示す。
実施例3
成分Aのパラ系アラミドマルチフィラメント糸(800デシテックス、490フィラメント)、成分Bのナイロンマルチフィラメント糸(800デシテックス、120フィラメント)を流体乱流ノズルで混繊し、糸長差10%の混繊糸を得た。 被着ゴムとしてタイヤ用SBR系ゴムを用いて、得られた糸についての剥離テスト1を行った。
【0047】
また、被着ゴムとしてブレーキホース用EPDM系ゴムを用いて、得られた糸についての剥離テスト2を行った。結果を表1に示す。
実施例4
成分Aのパラ系アラミドマルチフィラメント糸(800デシテックス、490フィラメント)、成分Bのパラ系アラミドマルチフィラメント糸(800デシテックス、490フィラメント)を流体乱流ノズルで混繊し、糸長差3%の混繊糸を得た。
【0048】
被着ゴムとしてタイヤ用SBR系ゴムを用いて得られた糸についての剥離テスト1を行った。
【0049】
また、被着ゴムとしてブレーキホース用EPDM系ゴムを用いて、得られた糸についての剥離テスト2を行った。結果を表1に示す。
実施例5
成分Aのパラ系アラミドマルチフィラメント糸(800デシテックス、490フィラメント)、成分Bのパラ系アラミドマルチフィラメント糸(800デシテックス、490フィラメント)を流体乱流ノズルで混繊し、糸長差18%の混繊糸を得た。
【0050】
被着ゴムとしてタイヤ用SBR系ゴムを用いて得られた糸についての剥離テスト1を行った。
【0051】
また、被着ゴムとしてブレーキホース用EPDM系ゴムを用いて、得られた糸についての剥離テスト2を行った。結果を表1に示す。
比較例1
成分Aのパラ系アラミドマルチフィラメント糸(800デシテックス、490フィラメント)、成分Bのパラ系アラミドマルチフィラメント糸(800デシテックス、490フィラメント)を混繊せず、引きそろえて、糸長差0%のタルミおよびループのない糸を得た。被着ゴムとしてタイヤ用SBR系ゴムを用いて、得られた糸についての剥離テスト1を行った。
【0052】
また、被着ゴムとしてブレーキホース用EPDM系ゴムを用いて、得られた糸についての剥離テスト2を行った。結果を表1に示す。
比較例2
成分Aのパラ系アラミドマルチフィラメント糸(800デシテックス、490フィラメント)、成分Bのパラ系アラミドマルチフィラメント糸(800デシテックス、490フィラメント)を混繊せず、引きそろえて、糸長差0%のタルミおよびループのない糸を得た。得られた糸を第1処理液(エポキシ系接着液)に浸した後、150℃で3分間乾燥させ、さらに200℃で2分の熱処理を行った。
【0053】
次に、第2処理液(一般的なVP/SBRラテックスを使用したレゾルシン・ホルマリン・ラテックスを使用)に浸漬した後、150℃で3分間乾燥させ、さらに、200℃で2分熱処理して接着性向上処理糸を得た。
【0054】
被着ゴムとしてタイヤ用SBR系ゴムを用いて、得られた接着性向上処理糸についての剥離テスト1を行った。
【0055】
また、被着ゴムとしてブレーキホース用EPDM系ゴムを用いて、得られた糸についての剥離テスト2を行った。結果を表1に示す。
【0056】
【表1】

Figure 2004169237
【0057】
実施例1〜5は比較例1と比べてゴムとの接着性が高くなっていることがわかる。
【0058】
また、実施例1は接着性向上処理を行った比較例2と比較しても、同等以上の剥離力が得られている。
【0059】
すなわち、本発明のアラミド混繊糸をゴムの補強糸として使用する場合、接着性向上処理をしなくても、接着性が高く補強糸として高い性能が得られることがわかる。
【0060】
【発明の効果】
本発明によれば、ゴムとの接着性が著しく向上され、用途によっては接着性向上処理なしでも、ゴムやプラスチックの補強剤として使用することのできる新規なアラミド混繊糸が提供される。また、適宜に接着性向上処理を施して用いれば、より一層の高い接着強さを実現することができる。
【図面の簡単な説明】
【図1】本発明のアラミド混繊糸の糸形態の一例を示す概念図である。
【図2】本発明のアラミド混繊糸の糸形態の他の一例を示す概念図である。[0001]
BACKGROUND OF THE INVENTION
The present invention relates to an aramid mixed yarn comprising two types of multifilament yarns and at least one component being an aramid filament yarn.
[0002]
[Prior art]
Conventionally, aramid multifilament yarn has been used as a reinforcing agent for rubbers and plastics by utilizing the properties of high elasticity, high strength, and heat resistance.
[0003]
In this application, the aramid filament yarn needs to be bonded to rubber or plastic, but the aramid filament itself has poor adhesion to rubber, and in order to improve the adhesion to this rubber, for example, separately It was necessary to perform an adhesion improvement process in advance.
[0004]
That is, for example, in order to obtain a polyester fiber and an aramid fiber having improved adhesion to rubber, an adhesion improving treatment method in which the fiber is coated with a specific adhesive has been proposed (Patent Document 1).
[0005]
However, such a method has a problem that a manufacturing process becomes complicated and costs increase because it is necessary to perform a treatment for improving adhesiveness.
[0006]
[Patent Document 1] Japanese Patent Application Laid-Open No. 2001-146686
[Problems to be solved by the invention]
The object of the present invention is to solve the above-mentioned problems of the prior art, and the adhesiveness with rubber is remarkably improved, and depending on the use, it can be used as a reinforcing agent for rubber or plastics even without an adhesive improvement treatment. The object is to provide a novel aramid blended yarn that can be used.
[0008]
[Means for Solving the Problems]
In order to achieve the above-described object, the aramid mixed yarn of the present invention has the following configuration.
[0009]
That is, it is an aramid mixed yarn characterized in that it is composed of at least an aramid multifilament yarn A component and a multifilament yarn B component, and has a loop or a tarmi on the yarn surface.
[0010]
In the aramid mixed yarn of the present invention, the multifilament yarn B component is preferably a non-thermoplastic fiber depending on the use, or the multifilament yarn B component is preferably used according to other uses. It is a thermoplastic fiber.
[0011]
Preferably, the yarn length difference represented by the following formula is greater than 0% and 20% or less.
[0012]
Yarn length difference (%) = {[YL (B) −YL (A)] / YL (A)} × 100
YL (A): Length of aramid multifilament yarn A component contained per unit length of aramid blended yarn YL (B): Length of multifilament yarn B component contained per unit length of aramid blended yarn [0013]
DETAILED DESCRIPTION OF THE INVENTION
Hereinafter, the aramid mixed yarn of the present invention will be described in more detail.
[0014]
The aramid mixed yarn of the present invention is a mixed yarn comprising at least a component A yarn and a component B yarn. Here, an aramid multifilament yarn as a component A yarn and a multifilament yarn as a component B yarn are used. It is basically configured by including.
[0015]
In the present invention, the multifilament yarn refers to a fiber bundle in which a plurality of filaments are collected.
[0016]
In the present invention, the aramid multifilament yarn as the component A yarn refers to a multifilament yarn made of an aramid fiber, which may be either a meta aramid multifilament yarn or a para aramid multifilament yarn, depending on the application. These meta-aramid multifilament yarns and para-aramid multifilament yarns can be appropriately distinguished and used, and para-aramid multifilament yarns are particularly preferred in terms of high strength and high elasticity.
[0017]
In addition, the aramid fiber as used in the field of this invention means the fiber which consists of a polymer for which the repeating unit with which the aromatic ring was couple | bonded by the amide bond occupies at least 80% or more. Typical examples of the aramid fibers made of these polymers or copolymers include polyparaphenylene terephthalamide fibers, polymetaphenylene terephthalamide fibers, and copolyparaphenylene-3,4'-oxydiphenylene terephthalamide fibers. and so on.
[0018]
In addition, the multifilament yarn as the component B yarn of the present invention can be used by appropriately selecting non-thermoplastic fibers or thermoplastic fibers according to the application. When high elasticity, high strength, and heat resistance are important, it is better to select non-thermoplastic fibers. On the other hand, when it is desired to impart an appropriate heat shrinkage rate to the mixed yarn, it is preferable to select a thermoplastic fiber.
[0019]
Examples of non-thermoplastic fibers include meta-aramid fibers and para-aramid fibers. When both high strength and heat resistance are emphasized, it is preferable to select para-aramid fibers as B yarns. If only heat resistance is important, meta-aramid should be selected as the B yarn.
[0020]
Examples of the thermoplastic fiber that can be used as the multifilament yarn as the component B yarn include polyester or nylon multifilament yarn.
[0021]
According to the knowledge of the present inventors, it is preferable to select a nylon multifilament yarn, particularly when importance is attached to adhesion to rubber.
[0022]
In the present invention, the yarn length difference represented by the following formula is preferably greater than 0% and not more than 20%, more preferably not less than 5% and not more than 15%. That is, when the aramid mixed yarn according to the present invention having such a yarn length difference is used as a reinforcing material such as rubber, the rubber is generated by the component B yarn when the aramid mixed yarn and the rubber are bonded. This is because the adhesiveness with the rubber is improved by wrapping around the gap between the talmi and the loop and exerting the anchoring effect. On the other hand, when the yarn length difference is 0%, there is almost no occurrence of tarmi and loops due to the component B, it is difficult to exert the rubber throwing effect, and the adhesiveness is remarkably inferior.
[0023]
In addition, if the yarn length difference exceeds 20%, the loop and the tarmi generated by the component B become too large, the unwinding property from the yarn package becomes worse, and the yarn breakage may occur during unwinding. Since it tends to be difficult, it is not preferable.
[0024]
The preferred fineness range of the aramid mixed yarn of the present invention is 60 to 8000 dtex, and it is preferable to change it appropriately according to the use of the yarn. For example, 500-2000 dtex is preferable when used as a reinforcing thread for automobile hoses.
[0025]
Further, the fineness range of the aramid multifilament yarn A component is preferably 30 to 4000 decitex, and the fineness range of the multifilament yarn B component is preferably within a range of 30 to 4000 decitex.
[0026]
In addition, both the components A and B preferably have a single fiber fineness in the range of 0.3 to 20 dtex, and in consideration of processability at the time of fiber mixing, those in the range of 1 to 6 dtex are particularly preferable.
[0027]
The mixed fiber range (weight ratio) of the aramid multifilament yarn A component and the multifilament yarn B component is preferably within the range of A / B = 20/80 to 80/20,
In order to take advantage of the high strength and high elasticity characteristics of Component A, A / B = 30/70 to 70/30 is particularly preferable.
[0028]
The cross-sectional shape of the multifilament used in the present invention is not particularly limited, and any of a round cross section, an irregular cross section, a hollow cross section, and the like can be used. Moreover, thickness, cross-sectional shape, etc. may differ between the filaments in a multifilament.
[0029]
In order to produce the aramid mixed yarn of the present invention, it is necessary to mix the component A filament yarn and the component B filament yarn. To mix the components, for example, the component A is fed to the feed roller A, The component B may be supplied from separate feed rollers of the feed roller B to the blending nozzle, and the yarn discharged from the blending nozzle may be sent out by the deli berry roller and wound up by the winding roller. At this time, in order to make the surface of the yarn have loops and tarmi, the speed of the feed roller may be made faster than the speed of the delivery roller. Further, in order to make the yarn length difference larger than 0% and 20% or less, the speed of the feed roller B may be made faster than the speed of the feed roller A by an amount corresponding to the yarn length difference. The actual speed increase rate may be adjusted by actually measuring the yarn length difference by the yarn length difference measurement method described later.
[0030]
Here, a rectification entanglement nozzle, a turbulent entanglement nozzle, etc. can be used for the fiber mixing nozzle. Among them, it is more preferable to use a turbulent entanglement nozzle that is liable to generate a loop or a tarmi.
[0031]
Although the pressure of the compressed air supplied to a blend fiber nozzle is not specifically limited, According to the knowledge of the present inventors, 0.2-1.2 MPa is preferable, More preferably, 0.4-1. 0 MPa. The pressure may be adjusted as appropriate by measuring the strength of the mixed yarn. Moreover, in order to improve the formation power of a loop or a talmi, providing water to one component or both components just before supplying to a fiber mixing nozzle can also be selected suitably. Furthermore, in order to perform the surface treatment of the loop and the tarmi, a set heater can be appropriately provided between the delivery roller and the take-up roller.
[0032]
FIG. 1 and FIG. 2 are each a schematic diagram of a yarn appearance showing an example of a yarn form for explaining the aramid mixed yarn of the present invention.
[0033]
The aramid mixed yarn of the present invention shown in FIG. 1 illustrates a form in which an aramid filament yarn A component constitutes a core portion and an aramid filament yarn B component yarn constitutes a sheath portion.
[0034]
The aramid mixed yarn of the present invention shown in FIG. 2 illustrates a form in which an aramid filament yarn A component constitutes a core portion and a polyester filament yarn B component yarn constitutes a sheath portion.
[0035]
The aramid mixed yarn of the present invention is suitable for use as a reinforcing agent for rubber materials.
[0036]
Examples of the rubber material include various hoses, belts, tires, and seats. Among them, automobile hoses such as brake hoses that require heat resistance are preferable. This is because various properties such as heat resistance and high strength of aramid fiber can be used.
[0037]
【Example】
EXAMPLES Hereinafter, although an Example demonstrates this invention, this invention is not limited to these Examples. The evaluation methods of the characteristics described in the examples are as follows.
<Evaluation of adhesive strength with rubber>
Peel test 1:
Assuming use with tire cords, 7 yarns were buried near the surface so that they would not overlap the unvulcanized rubber block, and vulcanized at 160 ° C. for 30 minutes to bond the yarn and rubber, A sample having a length of 250 mm and a width of 30 mm is used. Next, the peeling force (N / 5) was measured when 5 yarns excluding 2 at both ends were peeled from the rubber block at a tensile speed of 100 mm / min with a tensile tester.
[0038]
Peel test 2:
Assuming that it will be used as a reinforcing thread for rubber hoses, the thread is lined up in an unvulcanized rubber block without any gaps and buried near the surface layer, vulcanized at 160 ° C for 30 minutes to bond the thread and rubber, and a length of 250 mm X A sample with a width of 30 mm. Next, the peeling force (N / 20 mm) when peeling a 20 mm wide yarn at a tensile speed of 100 mm / min was measured with a tensile tester.
<Thread length difference>
A load of 2.94 mN / dtex is applied to the yarn, and the yarn is fixed to a tester with a length of 5 cm. If the yarn is twisted at this time, turn the tester to untwist the yarn.
[0039]
Remove the load and carefully separate the A component and the B component while the yarn is fixed to the inspection machine. At this time, use auxiliary tools such as needles and tweezers as much as possible because they are easy to separate.
[0040]
Again apply a load of 2.94 mN / dtex. The A component is tensioned and the B component is longer than the A component, so the tension is not applied and the component A is slack. The yarn length in this state is measured. This value is YL (A). Next, the A component is cut with scissors. This time, the tension is applied to the B component. The yarn length in this state is measured. This value is YL (B).
[0041]
The yarn length difference is calculated according to the following formula. Round off to the next decimal place.
[0042]
Yarn length difference (%) = {[YL (B) −YL (A)] / YL (A)} × 100
In the test, a total of three test sample yarns are collected from one sample yarn, a total of three measurements are performed, and the three measured values are averaged to obtain a yarn length difference.
Example 1
Component A para-aramid multifilament yarn (800 dtex, 490 filament) and component B para-aramid multifilament yarn (800 dtex, 490 filament) are mixed using a fluid turbulent nozzle and mixed with a yarn length difference of 10%. A yarn was obtained.
[0043]
A peel test 1 was performed on yarns obtained using SBR rubber for tires as the rubber to be adhered.
[0044]
Moreover, the peeling test 2 was performed about the obtained thread | yarn using EPDM type rubber | gum for brake hoses as adherend rubber. The results are shown in Table 1.
Example 2
Component A para-aramid multifilament yarn (800 dtex, 490 filament) and component B polyester multifilament yarn (800 dtex, 140 filament) are mixed with a fluid turbulent nozzle, and the yarn length difference is 10%. Got.
[0045]
Using an SBR rubber for tires as a rubber to be adhered, a peel test 1 was performed on the obtained yarn.
[0046]
Moreover, the peeling test 2 was performed about the obtained thread | yarn using EPDM type rubber | gum for brake hoses as adherend rubber. The results are shown in Table 1.
Example 3
Component A para-aramid multifilament yarn (800 dtex, 490 filament) and component B nylon multifilament yarn (800 dtex, 120 filament) are mixed with a fluid turbulent nozzle, resulting in a yarn length difference of 10%. Got. Using an SBR rubber for tires as a rubber to be adhered, a peel test 1 was performed on the obtained yarn.
[0047]
Moreover, the peeling test 2 was performed about the obtained thread | yarn using EPDM type rubber | gum for brake hoses as adherend rubber. The results are shown in Table 1.
Example 4
Component A para-aramid multifilament yarn (800 dtex, 490 filament) and component B para-aramid multifilament yarn (800 dtex, 490 filament) are mixed using a fluid turbulent nozzle and mixed with a yarn length difference of 3%. A yarn was obtained.
[0048]
A peel test 1 was performed on yarns obtained using SBR rubber for tires as the rubber to be adhered.
[0049]
Moreover, the peeling test 2 was performed about the obtained thread | yarn using EPDM type rubber | gum for brake hoses as adherend rubber. The results are shown in Table 1.
Example 5
Component A para-aramid multifilament yarn (800 dtex, 490 filament) and component B para-aramid multifilament yarn (800 dtex, 490 filament) are mixed with a fluid turbulent nozzle, and the yarn length difference is 18%. A yarn was obtained.
[0050]
A peel test 1 was performed on yarns obtained using SBR rubber for tires as the rubber to be adhered.
[0051]
Moreover, the peeling test 2 was performed about the obtained thread | yarn using EPDM type rubber | gum for brake hoses as adherend rubber. The results are shown in Table 1.
Comparative Example 1
Para-aramid multifilament yarn of component A (800 dtex, 490 filaments) and para-aramid multifilament yarn of component B (800 dtex, 490 filaments) are not mixed and aligned, and the tarmi has a yarn length difference of 0%. And a loop-free yarn was obtained. Using an SBR rubber for tires as a rubber to be adhered, a peel test 1 was performed on the obtained yarn.
[0052]
Moreover, the peeling test 2 was performed about the obtained thread | yarn using EPDM type rubber | gum for brake hoses as adherend rubber. The results are shown in Table 1.
Comparative Example 2
Para-aramid multifilament yarn of component A (800 dtex, 490 filaments) and para-aramid multifilament yarn of component B (800 dtex, 490 filaments) are not mixed and aligned, and the tarmi has a yarn length difference of 0%. And a loop-free yarn was obtained. The obtained yarn was immersed in the first treatment liquid (epoxy adhesive liquid), dried at 150 ° C. for 3 minutes, and further subjected to heat treatment at 200 ° C. for 2 minutes.
[0053]
Next, after immersing in the second treatment liquid (using resorcin / formalin latex using general VP / SBR latex), it is dried at 150 ° C. for 3 minutes, and further heat-treated at 200 ° C. for 2 minutes for adhesion. Yield improved yarn was obtained.
[0054]
Using the SBR rubber for tires as the rubber to be adhered, a peel test 1 was performed on the obtained adhesive improvement treated yarn.
[0055]
Moreover, the peeling test 2 was performed about the obtained thread | yarn using EPDM type rubber | gum for brake hoses as adherend rubber. The results are shown in Table 1.
[0056]
[Table 1]
Figure 2004169237
[0057]
It can be seen that Examples 1 to 5 have higher adhesion to rubber than Comparative Example 1.
[0058]
Moreover, even if Example 1 is compared with the comparative example 2 which performed the adhesive improvement process, the peeling force more than equivalent is acquired.
[0059]
That is, when the aramid mixed yarn of the present invention is used as a rubber reinforcing yarn, it can be seen that high adhesiveness and high performance can be obtained without performing an adhesive improvement treatment.
[0060]
【The invention's effect】
ADVANTAGE OF THE INVENTION According to this invention, the adhesiveness with rubber | gum is improved remarkably, and the novel aramid mixed yarn which can be used as a reinforcing agent of rubber | gum or a plastic is provided even if there is no adhesiveness improvement process depending on a use. Moreover, if an adhesive improvement process is suitably performed, it can implement | achieve much higher adhesive strength.
[Brief description of the drawings]
FIG. 1 is a conceptual diagram showing an example of a yarn form of an aramid mixed yarn of the present invention.
FIG. 2 is a conceptual diagram showing another example of the yarn form of the aramid mixed yarn of the present invention.

Claims (5)

少なくともアラミドマルチフィラメント糸A成分とマルチフィラメント糸B成分で構成され、かつ糸表面にループやタルミを有することを特徴とするアラミド混繊糸。An aramid blended yarn comprising at least an aramid multifilament yarn A component and a multifilament yarn B component, and having a loop or a tarmi on the yarn surface. マルチフィラメント糸B成分が、非熱可塑性繊維であることを特徴とする請求項1記載のアラミド混繊糸。The aramid mixed yarn according to claim 1, wherein the multifilament yarn B component is a non-thermoplastic fiber. マルチフィラメント糸B成分が、熱可塑性繊維であることを特徴とする請求項1記載のアラミド混繊糸。The aramid mixed yarn according to claim 1, wherein the multifilament yarn B component is a thermoplastic fiber. 糸長差が0%より大きく、20%以下であることを特徴とする請求項1、2または3記載のアラミド混繊糸。
糸長差(%)={〔YL(B)―YL(A)〕/YL(A)}×100
YL(A):アラミド混繊糸の単位長さ当たりに含まれるアラミドマルチフィラメント糸A成分の長さ
YL(B):アラミド混繊糸の単位長さ当たりに含まれるマルチフィラメント糸B成分の長さ
4. The aramid mixed yarn according to claim 1, wherein the yarn length difference is greater than 0% and 20% or less.
Yarn length difference (%) = {[YL (B) −YL (A)] / YL (A)} × 100
YL (A): Length of the aramid multifilament yarn A component included per unit length of the aramid blended yarn YL (B): The length of the multifilament yarn B component included per unit length of the aramid blended yarn The
ゴム補強用繊維糸として用いられることを特徴とする請求項1、2、3または4記載のアラミド混繊糸。The aramid mixed yarn according to claim 1, 2, 3, or 4, which is used as a fiber yarn for rubber reinforcement.
JP2002338891A 2002-11-22 2002-11-22 Aramid blended yarn Expired - Lifetime JP4324901B2 (en)