JP2004035603A - Image fastness improver, recorded matter, method for improving image fastness, method for producing recorded matter, kit for improving image fastness - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide an image fastness improver which obtains superior resistance to gas fastness and a feeling of high quality level gloss, its recorded product, and a method of improving image fastness using the same. <P>SOLUTION: The image fastness improver is imparted to a recorded product obtained by forming an image by a coloring agent on an ink receptive layer of a porous structure and mainly contains a monovalent saturated aliphatic alcohol ester of a polybasic acid having a molecular weight of ≥300. <P>COPYRIGHT: (C)2004,JPO

Description

【００２７】
【化２】

【００２８】
上記式中、ｔ−Ｃ_４Ｈ_９はｔｅｒｔ−ブチル基を、ｔ−Ｃ_８Ｈ_１７はｔｅｒｔ−オクチル基をそれぞれ表す。
【００２９】
Ｂ：被記録媒体
本発明に用い得る被記録媒体としては、多孔質層のインク受容層を有し、インクが付着することで記録を行う被記録媒体であればいずれのものでも使用することができる。しかし、本発明では被記録媒体に画像堅牢性向上剤を含浸させるため、画像堅牢性向上剤が裏抜けしない媒体であることが好ましい。本発明にかかる被記録媒体は、特に、インク受容層の多孔質構造が微粒子から形成され、且つ、該微粒子に色材が吸着するような被記録媒体がインクジェット法を利用する場合に特に好適である。このようなインクジェット用の被記録媒体としては支持体上のインク受容層に形成された間隙によりインクを吸収するいわゆる吸収タイプであることが好ましい。吸収タイプのインク受容層は、微粒子を主体とし、必要に応じて、バインダーやその他の添加剤を含有する多孔質構造を有する。
【００３０】
微粒子の例としては、シリカ、クレー、タルク、炭酸カルシウム、カオリン、アルミナあるいはアルミナ水和物等の酸化アルミニウム、珪藻土、酸化チタン、ハイドロタルサイト、酸化亜鉛等の無機顔料や尿素ホルマリン樹脂、エチレン樹脂、スチレン樹脂等の有機顔料が挙げられ、これらの１種以上が使用される。バインダーとして好適に使用されているものには水溶性高分子やラテックスを挙げることができる。例えば、ポリビニルアルコールまたはその変性体、澱粉またはその変性体、ゼラチンまたはその変性体、アラビアゴム、カルボキシメチルセルロース、ヒドロキシエチルセルロース、ヒドロキシプロピルメチルセルロースなどのセルロース誘導体、ＳＢＲラテックス、ＮＢＲラテックス、メチルメタクリレート−ブタジエン共重合体ラテックス、官能基変性重合体ラテックス、エチレン酢酸ビニル共重合体などのビニル系共重合体ラテックス、ポリビニルピロリドン、無水マレイン酸またはその共重合体、アクリル酸エステル共重合体などが使用され、これらから選択した１種、あるいは必要に応じて２種以上を組み合せて用いることができる。
【００３１】
インク受容層には、その他の添加剤を使用することもでき、例えば、必要に応じて分散剤、増粘剤、ｐＨ調整剤、潤滑剤、流動性変性剤、界面活性剤、消泡剤、離型剤、蛍光増白剤、紫外線吸収剤、酸化防止剤などを挙げることができる。
【００３２】
本発明にかかる特に好適な被記録媒体は、上述の微粒子として、平均粒子径が１μｍ以下の微粒子を主体として、インク受容層を形成したものが好ましい。上記の微粒子として、特に好ましいものは、例えばシリカまたは酸化アルミニウム微粒子等が挙げられる。酸化アルミニウム微粒子、シリカにおいて特に効果的な理由としては以下の様に考えられる。即ち、酸化アルミニウム微粒子、シリカに吸着された色材は、ＮＯ_Ｘ、ＳＯ_Ｘ、オゾン等のガスによる色材の褪色を受け易いことが判ったが、これらの微粒子はガスを引き寄せやすく、色材の近傍にガスが存在することになり色材が褪色し易くなるためと思われる。シリカ微粒子として好ましいものは、コロイダルシリカに代表されるシリカ微粒子である。コロイダルシリカ自体も市場より入手可能なものであるが、特に好ましいものとして、例えば特許第２８０３１３４号、同２８８１８４７号公報に掲載されたものを挙げることができる。酸化アルミ微粒子として好ましいものとしては、アルミナ水和物微粒子を挙げることができる。このようなアルミナ系顔料の一つとして下記一般式により表されるアルミナ水和物を好適なものとして挙げることができる。
【００３３】
Ａｌ_２Ｏ_３−ｎ（ＯＨ）_２ｎ・_ｍＨ_２Ｏ
上記式中、ｎは１、２または３の整数のいずれかを表し、ｍは０〜１０、好ましくは０〜５の値を表す。但し、ｍとｎは同時には０にはならない。ｍＨ_２Ｏは、多くの場合ｍＨ_２Ｏ結晶格子の形成に関与しない脱離可能な水相をも表すものである為、ｍは整数または整数でない値を取ることもできる。またこの種の材料を加熱するとｍは０の値に達することがありうる。
【００３４】
アルミナ水和物は一般的には、米国特許第４２４２２７１号、米国特許第４２０２８７０号に記載されているようなアルミニウムアルコキシドの加水分解やアルミン酸ナトリウムの加水分解のような、また特公昭５７−４４６０５号公報に記載されているアルミン酸ナトリウム等の水溶液に硫酸ナトリウム、塩化アルミニウム等の水溶液を加えて中和を行う方法などの公知の方法で製造されたものを使用したものが好適である。
【００３５】
更に、これらのアルミナ水和物を使用したインクジェット用被記録媒体は、本発明にかかる画像堅牢性向上剤との親和性、吸収性、定着性が優れる上、前述したような写真画質を実現するために必要とされる光沢、透明性および染料等の記録液中の色材の定着性等が優れていることより、本発明を適用するのに更に好適である。
【００３６】
本発明に用いられるインクジェット用被記録媒体の微粒子と前記のバインダーの混合比は、重量比で、１：１〜１００：１の範囲にあることが好ましい。バインダーの量を上記範囲とすることで、インク受容層への画像堅牢性向上剤の含浸に好適な細孔容積の維持が可能となる。酸化アルミニウム微粒子またはシリカ微粒子のインク受容層中の好ましい含有量としては、５０重量％以上、より好ましくは７０重量％以上、更に好ましくは、８０重量％以上であり、９９重量％以下であることが最も好適である。インク受容層の塗工量としては、画像堅牢性向上剤の含浸性を良好とするために乾燥固形分換算で１０ｇ／ｍ^２以上であることが好ましく、１０〜６０ｇ／ｍ^２が最も好適である。
【００３７】
本発明に用いられる被記録媒体は上記したインク受容層を支持するための支持体を有することが好ましいが、支持体としては、特段の制限がなく、上記した多孔質構造のインク受容層の形成が可能であって、且つインクジェットプリンタ等の搬送機構によって搬送可能な剛度を与えるものであれば、いずれのものでも使用できる。例えば、支持体とインク受容層の間に硫酸バリウム、酸化チタン、酸化亜鉛等の無機顔料等をバインダーと共に塗工して形成した多孔質層を有するものや、支持体にレジンコート紙を用いても良い。そして、上記支持体とインク受容層の間に多孔質層を有する被記録媒体は、前記した本発明のより好ましい態様である、「画像形成領域が、インク受容層の厚さ方向に存在する孔部の全てあるいは実質的に全てが画像堅牢性向上剤によって充填されている部分を有する記録物」に用いられた場合により効果がある。つまり、インク受容層の厚さ方向に存在する孔部の全てあるいは実質的に全てが画像堅牢性向上剤によって充填されている記録物を、高温・高湿環境下に長時間放置したような場合であっても、記録物表面への画像堅牢性向上剤の染み出しなどによる表面のべたつきなどが生じることを極めて有効に抑制でき、保管性においても極めて優れた記録物とすることができる。
【００３８】
上記したような効果が得られる理由は明らかでないが、インク受容層の厚さ方向に存在する孔部の全てあるいは実質的に全てを充填するために供給された画像堅牢性向上剤は透気度の低い、例えば、バライタ層を通り抜け難い為、画像堅牢性向上剤による孔部の充填が確実に行われ、さらにまた、インク受容層中の孔部に存在している空気や水分が、図３に模式的に示した様に、堅牢性向上剤の孔部への充填処理に伴って、多孔質層（１３０１）に移行し、或いは吸着されて、インク受容層中への空気や水分の残留を抑制もしくは防止することができる為であると考えられる。
【００３９】
Ｃ：記録物の製造方法および画像堅牢性向上方法
本発明にかかる記録物とは、支持体（１０００）表面に、微粒子（１００５）を含む多孔質構造のインク受容層（１００３）を備え、該微粒子の表面に吸着した色材（１００９）により画像が形成されている領域を有する記録物であって、該領域に上記した画像堅牢性向上剤（以下、向上剤）１００１が付与されたものである。
【００４０】
そして、例えば、図２に示すよう、該画像が形成されている領域が、インク受容層の厚さ方向に分布している色材の全てまたは実質的に全てが画像堅牢性向上剤中にある部分を有する、あるいは、インク受容層の厚さ方向に分布している孔部の全てまたは実質的に全てが画像堅牢性向上剤によって充填されている態様がより好ましく、画像堅牢性はさらに向上する。また、本発明にかかる記録物のインク受容層は多孔質構造であれば、特に微粒子を含むものに限定されるものではない。
【００４１】
上記した本発明のより好ましい態様の場合に、受容層を有する被記録媒体に形成したインク等による記録物（プリント物）の色味の改善や耐ガス性の驚異的な向上が達成される理由は以下のようなメカニズムによるものと考えられる。
【００４２】
図１は、紙などからなる支持体上に微粒子からなる多孔質構造のインク受容層を備える、いわゆるコート紙の断面構造を模式的に示している。図１において、１０００は支持体、１００３は、支持体１０００に保持されているインク受容層である。インク受容層１００３は、微粒子１００５を含む多孔質構造を形成しており、微粒子は、結着剤（バインダー）１００７によって固定されている。そしてこのようなコート紙に付与されたインク滴は、インク受容層１００３に染み込んでいく過程において、インクに含まれる色材１００９が微粒子１００５の表面に吸着され、画像が形成される。
【００４３】
このようにして記録の為されたコート紙の表面に、画像堅牢性向上剤１００１を供給した後、インク受容層の比較的深部にある色材をも向上剤中にあらしめるために、例えば、インク供給後にラビング処理を行うと、画像堅牢性向上剤は、インク受容層１００３中の孔部、ここでは微粒子１００５の隙間（間隙）１０１１を充填していく。向上剤は、非水系の物質であることから、粒子間にトラップされている水性インクの水性媒体を次々と置換していき、微粒子表面に吸着している色材の周囲も被覆していく。そして、最終的に図２に示した様に、間隙１０１１が向上剤１００１で充填され、インク受容層の厚さ方向に分布している色材の全てまたは実質的に全てが画像堅牢性向上剤中にある、あるいは、インク受容層の厚さ方向に存在する孔部の全てあるいは実質的に全てを該向上剤によって充填させると、色材１００９は大気中のＳＯ_ＸやＮＯ_Ｘなどのガスあるいはそれらを含む水分との接触を断たれることとなる。その結果、インク受容層中の色材の劣化が抑制され、画像の堅牢性の向上がさらに図られるものと考えられる。また、本発明による画像の堅牢性向上効果と共に得られる色味の改善、印字濃度向上、光沢度の向上の効果は、インク受容層を形成している物質と孔部（空気）、ここでは微粒子と間隙（空気）との屈折率の差によって生じていたインク受容層表面および内部における光の乱反射が、該間隙が画像堅牢性向上剤で充填されることによって抑制される為であると考えられる。
【００４４】
本発明にかかる画像堅牢性向上剤は、好ましくは液体の状態でインク受容層に付与される。そのため、インク受容層への浸透が容易に行われ、かつインク受容層内の多孔質構造の形状に対応して変形し、画像堅牢性向上剤中への色材の取り込み効果を十分に発揮することが可能である。しかも、液体としてインク受容層内に保持されることで、記録物に許容できる変形を生じさせた場合において、インク受容層の多孔質構造、例えば間隙の内壁や微粒子が含有されている場合における微粒子の外壁との画像堅牢性向上剤の接触状態が良好に維持される。
【００４５】
一方、画像堅牢性向上剤を、ワックスなどの通温において固形状態の形態とした場合は、インク受容層への浸透に圧力を必要としたり、均一な浸透状態が得られ難いなどの問題がある。更に、揮発性溶剤により希釈された状態で適用され、適用後に固化するもの、あるいは液体で適用された後に固化する成分を含むものなどの形態とした場合は、固化する過程で水分や気泡の取り込みによる向上剤の相の白濁化が生じる場合があり、更に、固化する際の体積減少が生じた場合には、向上剤の相と多孔質構造との間に空隙が生じ、色材の保護機能が減少するおそれがある。インク受容層の局所的な熱分析等の方法により、物質溶解時の熱挙動（吸熱、発熱）がないことを確認することによって、インク受容層中に液体状態で保持されていることを確認することが可能である。
【００４６】
本発明で用いる、ラビング処理とは、堅牢性向上剤をインク受容層中の孔部に積極的に充填させるための拭き取りおよび研磨の少なくとも一方の処理を示す。
【００４７】
（１）第１の実施態様
本発明にかかる記録物の製造方法あるいは画像堅牢性向上方法の一実施態様としては、上記したように、多孔質構造のインク受容層を備え、該インク受容層へのインク或いはインク滴の付与によって、文字や絵等の画像が記録されている記録シートの、該インク受容層表面に、前記した画像堅牢性向上剤を供給し、その後にラビング処理を行なう方が挙げられる。ここで、向上剤は、記録シートの画像記録部分の少なくとも一部にのみ供給し、塗り込んでもよいが、記録シートの全面に塗りこむことが最も好ましい。これによってインク受容層中の色材が、オゾン等のガスによって攻撃されることをより確実に抑制することができる。
【００４８】
また、前記したように、本発明のより好ましい態様は、インク受容層の厚さ方向に存在する孔部の全て或いは実質的に全てが画像堅牢性向上剤で充填されているものである。この場合、画像堅牢性向上剤の供給量は、塗りこみの手間等を考慮すると、孔部が完全に充填される量と、塗布部材への吸収分などを考慮した量とするのが適当である。ここで、孔部が完全に充填される量とは、例えば、微粒子からなるインク受容層の場合はインク受容層の間隙度（吸油量など）などから考慮する。このような量の画像堅牢性向上剤を供給し、塗り込むことで、インク受容層の孔部をほぼ確実に画像堅牢性向上剤で充填することができる。
【００４９】
具体的には、例えば、吸油量が０．３ｃｃである記録媒体に形成されてなる画像の堅牢性を向上させる為には、約０．３ｇ程度の画像堅牢性向上剤を付与し、ラビング処理することで十分な堅牢性の向上効果を得ることができる。このことは、インク受容層の表面部分を覆うだけではなく、画像堅牢性向上剤がインク受容層の孔部を充填することによって、本発明の効果が達成されるものであることを表すものである。
【００５０】
ここで該画像堅牢性向上剤の塗布方法については、刷毛塗り、スプレー塗り、ローラー塗り、へら塗り、スポンジ塗布等特に制限されないが、具体的な方法として、例えば、図５に示した様に、適当量の画像堅牢性向上剤をインク受容層表面に一定量を供給可能な機能５００１（スプレーやポンプなど）を備えた容器５００３（ディスペンサー等）に該向上化剤を含むものとラビング用の部材とがセットとなった画像堅牢性向上化キットを用いることで実現可能である。
【００５１】
また他の実施態様としては、図４（ａ）及び（ｂ）に示した様な、画像堅牢性向上剤を含んでいる画像堅牢性向上化剤貯蔵部４００１と、画像堅牢性向上剤の塗布部材４００２とが一体化され、該貯蔵部内の画像堅牢性向上剤が該塗布部材表面に滲出可能に構成されているアプリケータを用いて、画像堅牢性向上剤の供給とラビング処理とを同時に行うようにしてもよい。尚、塗布部材４００２の画像堅牢性向上剤が少なくなってきた場合に、画像堅牢性向上化剤貯蔵部４００１に圧力をかけることにより、塗布部材に画像堅牢性向上剤がしみ込むような構成であっても良い。４００３は４００２の蓋である。本発明にかかる方法で画像堅牢性に優れた記録物を得るために、上記被記媒体と上記画像記録性向上剤とのセットを用いることで、簡便に堅牢性の高い画像をえることができる。
【００５２】
（２）他の実施態様
本発明にかかる記録物の製造方法あるいは画像堅牢性向上方法の他の実施態様として、記録装置内で人手を介在させること無しに処理する方法を挙げることができる。図６は、画像堅牢性に優れた記録物を得るための装置の概略断面図であり、インクジェット法による記録媒体への画像の記録と、形成された画像への堅牢性付与の処理とを行う手段を各々備えている。図６において、２５は筐体であり、１は積層された未使用の記録媒体で、サプライトレイ（給紙用カセット）２に略水平に載置されている。
【００５３】
３は吸盤で、吸盤移動機構（不図示）により、図中ａの位置から積層された未使用の記録紙１の最上部の１枚に接する位置ｂに移動し、最上位の用紙を吸引して持ち上げることができる。この際、吸引機構（不図示）により、吸盤３が記録紙に接した状態で吸盤３の内部の圧力を減少させて記録紙１の最上部の１枚を吸着して、その記録紙を他の記録紙から分離させる。その状態で吸盤移動機構により図中ｃの位置に移動し、その分離した１枚の記録紙の先端を搬送ローラ４，５の間に差し込むことができる。その後、吸引機構による吸引動作を停止させて吸盤３の吸着力を解除し、吸盤３による記録紙の拘束を解くことができる。
【００５４】
搬送用ローラ４，５は、搬送用モータ（不図示）等の駆動源によりクラッチ機構（不図示）等を介して回転駆動される。６，７はガイド板で、所定の間隔を持って対向して配置されており、搬送用ローラ４，５の回転により搬送される記録紙の供給経路を形成している。これらガイド板６，７で形成される供給経路の断面形状は略半円形であり、搬送用ローラ４，５近傍から上方の副走査用ローラ８，９に至っている。これら副走査用ローラ８，９は、図中左方向に平行に配置された第２の副走査用ローラ対１０，１１と共に、搬送されてきた記録紙を挟持し、後述する制御部（不図示）などの制御の下に紙送りを行っている。１５は副走査用ローラ８，９，１０，１１の間での記録紙の位置を規制するガイド板である。１２は記録ヘッド（インクジェットヘッド）で、記録紙１の搬送方向に複数のインク吐出用ノズルが配されている。尚、この記録ヘッド１２は、それぞれが異なる色のインクを吐出する複数のインクジェットヘッドを備えていても良い。１３は記録ヘッド１２に供給するインクを収容しているインクタンクである。記録ヘッド１２とインクタンク１３はキャリッジに載置されており、副走査用ローラ８〜１１の回転軸と略平行に配置されたキャリッジガイドにより、記録紙の搬送方向に略直交する方向に移動可能に保持されている。
【００５５】
１６は、上方の記録紙収容部に積層して収容された未使用の第２の記録紙である。１７は積層収納された記録紙１６を載置し、分離ローラ１８方向に適宜押圧する圧板である。１９，２０はガイド板で、分離ローラ１８により取り出された１枚の記録紙の先端を副走査用ローラ８，９に導くための第２の供給経路を形成している。
【００５６】
２１，２２，２３，２４は、例えば特開平１−２６４８７９号公報で開示されている各記録紙１，１６の有無及びその紙質を検知する手段である。２１，２３はそれぞれ記録紙１，１６の表面に所定波長の光を照射する光源、２２，２４は、その光源から照射された光が記録紙表面から反射された光を受光する光検出器である。
【００５７】
このような反射光による記録紙の紙質の検知は、記録紙の種類に応じて表面の粗さが異なり、それに伴って光の拡散の程度が異なってくることに起因してなされるものである。例えば普通紙の表面は微視的にみれば繊維の絡み合ったもので表面の拡散は大きく、従って検出器２２，２４の出力は小さくなる。一方、表面が平滑で、光の拡散の程度の低いシートの場合、検出器２２，２４の出力が大きくなる。このような光による検出手段を用いて、吸盤３を使用した第１の分離機構、或は分離ローラ１８を使用した第２の分離機構に対応する記録紙がそれぞれ対応するカセットに装填されているか、又は記録に適した記録紙が装着されているかなどが判断可能となる。
【００５８】
２６，２７は記録ヘッド１２による記録終了後、副走査ローラ１０，１１の回転に伴って排出される記録紙を後述の工程に導くための搬送路を形成するガイド板である。ガイド板には面状のヒータ（不図示）が取り付けられており、ガイド板２６，２７で形成された搬送路内の記録紙を加熱し、その記録紙上に吐出されたインクの乾燥を促進する。
【００５９】
こうして得られた記録物の記録面に対して、画像堅牢性向上剤を供給し、該記録物のインク受容層に、画像堅牢性向上剤が充填された領域を形成する。
【００６０】
液体５２は、本発明にかかる画像堅牢性向上剤であり、容器５１にタンク（不図示）から供給装置（不図示）にて供給され、常に容器５１内における液面の高さが所定の範囲内になるように自動的に供給・制御されている。５３は堅牢性向上剤塗布用ローラで、その表面部５３ａは堅牢性向上剤５２が浸透可能なスポンジ状の構造となっており、その一部が容器５１内の堅牢性向上剤５２に接していて、液体塗布用ローラ５３が不図示の駆動源の駆動により回転することにより、その表面部５３ａに一様に堅牢性向上剤５２を浸潤させることができる。５４は塗布用ローラ５３との協動により記録媒体を挟持して搬送する搬送用ローラである。尚、この搬送用ローラ５４は、その表面に堅牢性向上剤５２が付着しないように、記録媒体が挟持されていない時は塗布用ローラ５３と離間し、記録媒体が介在している場合にのみ塗布用ローラ５３と搬送用ローラ５４と接触して記録媒体を挟持するのが望ましい。５５は乾燥用ヒータで、堅牢性向上剤５２が塗布された記録紙を乾燥させるのに使用される。
【００６１】
以上の構成により、記録ヘッド１２による記録が終了した後、その記録紙の後端が第２の副走査ローラ対１０，１１から離れる以前に記録媒体の先端が搬送用ローラ５４，塗布用ローラ５３の位置にまで到達する。そして、搬送用ローラ５４と塗布用ローラ５３との間に記録媒体が挟持され、これらローラ５３，５４の回転に伴って記録媒体の片方の面に堅牢性向上剤５２が一様に供給され、またラビングされて、インク受容層の間隙に充填される。この液体が充填された記録紙は、必要に応じて更なるラビング処理を施した後、排紙用ローラ３３の回転により３４の排紙口から装置外に排出される。
【００６２】
なお、図６では、インクジェット記録と画像堅牢性向上剤の充填とが、同一の装置内で処理される形態の画像記録装置を説明したが、これに限定されず、画像記録部と堅牢性向上液の充填部とを分離した構成の画像記録装置、更には、堅牢性向上液の充填部を、画像形成部と独立させた、画像堅牢性向上液の塗布装置もまた、本発明の範囲内のものである。
【００６３】
【実施例】
以下、実施例および比較例により本発明を更に説明する。
【００６４】
（画像堅牢性向上剤の調製）
下記に示す多塩基酸の１価飽和脂肪族アルコールの部分エステル化物と、添加剤すなわち紫外線吸収剤を表２に示した割合で混合することによって実施例１から８で用いた画像堅牢性向上剤を用意した。
【００６５】
グループＡ．多塩基酸と１価飽和脂肪族アルコールの部分エステル化物
Ａ−１．化合物名：アジピン酸モノ−２−ヘプチルウンデシル
分子量：３９７
【００６６】
【化３】

Ａ−２．化合物名：フタル酸モノデシル
分子量：３０６
【００６７】
【化４】

Ａ−３．化合物名：トリメリット酸ジ２−エチルヘキシル
分子量：４３４
【００６８】
【化５】

グループＢ：添加剤
Ｂ−１．商品名：アデカスタブＬＡ−６３Ｐ（旭電化株式会社製）
【００６９】
【化６】

【００７０】
比較例１および２
比較例１は画像堅牢性向上化剤を用いない場合である。
比較例２の処理剤として、Ｃ−１．アクリル樹脂溶液アクリル樹脂系エマルジョン商品名：ボンコート４００１大日本インキ化学工業株式会社製）を用いた場合である。
【００７１】
（被記録媒体の製造例）
先ず、下記のようにして基材を作製した。濾水度４５０ｍｌＣＳＦ（Ｃａｎａｄｉａｎ　Ｓｔａｎｄａｒａｄ　Ｆｒｅｅｎｅｓｓ）の、広葉樹晒しクラフトパルプ（ＬＢＰＫ）８０質量部、濾水度４８０ｍｌＣＳＦの、針葉樹晒しクラフトパルプ（ＮＢＰＫ）２０質量部からなるパルプスラリーに、カチオン化澱粉０．６０質量部、重質炭酸カルシウム１０質量部、軽質炭酸カルシウム１５質量部、アルキルケテンダイマー０．１０質量部、カチオン性ポリアクリルアミド０．０３質量部、硫酸バンド０．４０質量部を添加して紙料を調整後、長網抄紙紙で抄造し、３段のウエットプレスを行って、多筒式ドライヤーで乾燥した。その後、サイズプレス装置で、酸化澱粉水溶液を固形分で１．０ｇ／ｍ^２となるように含浸し、乾燥後、マシンカレンダー仕上げをし、坪量１５５ｇ／ｍ^２、ステキヒトサイズ度１００秒、透気度５０秒、ベック平滑度３０秒、ガーレー剛度１１．０ｍＮの基材を得た。
【００７２】
次に、上記で得た基材上に、以下のようにして下塗り層を形成した。先ず、下塗り層の形成に使用する塗工液として、カオリン（ウルトラホワイト９０、Ｅｎｇｅｌｈａｒｄ社製）／酸化亜鉛／水酸化アルミニウムの、重量比６５／１０／２５からなる填量１００質量部と、市販のポリアクリル酸系分散剤０．１質量部とからなる固形分濃度７０％のスラリーに、市販のスチレン−ブタジエン系ラテックス７質量部を添加して、固形分６０％になるように調整して組成物を得た。次に、この組成物を、乾燥塗工量が１５ｇ／ｍ^２になるように、ブレードコータで、基材の両面に塗工し、乾燥した。その後、マシンカレンダー仕上げをし（線圧１５０ｋｇｆ／ｃｍ）、坪量１８５ｇ／ｍ^２、ステキヒトサイズ度３００秒、透気度３，０００秒、ベック平滑度２００秒、ガーレー剛度１１．５ｍＮの下塗り層付き基材を得た。下塗り層付き基材の白色度は、断裁されたＡ４サイズ５枚のサンプルに対して各々測定し、その平均値として求めた。その結果、Ｌ^＊：９５、ａ^＊：０、ｂ^＊：−２であった（ＪＩＳ　Ｚ　８７２９の色相として求めた）。
【００７３】
次に、インク受容層を形成したが、上記の第二の表面処理工程での塗工後、即ち、塗工液が下塗り層に含浸されてすぐに、そのまま下塗り層上にインク受容層を形成した。その際の、インク受容層の形成に用いた塗工液及び塗工方法等は、以下の通りである。
【００７４】
塩化アルミニウムの４重量％溶液中にアルミン酸ソーダを加えｐＨを４に調整した。その後、攪拌をしながら９０℃まで昇温し、しばらく攪拌を行った。その後、再びアルミン酸ソーダを加えてｐＨを１０に調整し、その温度を保持しながら４０時間熟成反応を行った。その後、室温に戻し、ｐＨを７〜８に調整した。この分散液に対して脱塩処理を行い、その後酢酸により解膠処理を行ってコロイダルゾルを得た。このアルミナ水和物のコロイダルゾルを濃縮して１７重量％の溶液を得た。ポリビニルアルコール　ＰＶＡ１１７（商品名：クラレ社製）を純水に溶解して９重量％の溶液を得た。上記アルミナ水和物のコロイダルゾルとポリビニルアルコール溶液を、アルミナ水和物固形分とポリビニルアルコール固形分が重量比で１０：１になるように混合攪拌して、分散液を得た。これをダイコータで乾燥塗工量で３５ｇ／ｍ^２になるように毎分３０ｍで塗工した。そして、１７０℃で乾燥してインク受容層を形成した。この被記録媒体のインク受容層表面にリウエットキャストコーターを用いて、熱湯を用いたリウエットキャスト処理を行い被記録媒体を得た。被記録媒体の吸油量は約２１ｃｃ／ｍ^２であった。
【００７５】
（記録物の作成および堅牢化処理）
上記で作成した被記録媒体に、下記の方法で画像を記録した記録物を作成し、その記録物に対して、実施例１から６の画像堅牢性向上化剤及び比較例２の化合物を用いて、下記の方法▲１▼〜▲５▼に従って各種の画像堅牢性試験を行った。また、何も処理しなかった記録物を比較例１として同様に評価を行った。
【００７６】
インクジェット方式を用いたフォト用プリンタ（商品名：ＢＪ−Ｆ８７０キヤノン製）に当該プリンタに純正のインクタンク（商品名：ＢＣＩ−６ＢＫ、ＢＣＩ−６Ｙ、Ｍ、Ｃ、ＢＣＩ−６ＰＭ、ＢＣＩ−６ＰＣ）を装着し、上記で得た被記録媒体の記録面に、単色として、ブラック、シアン、マゼンタ及びイエロー、コンポジットカラーとして、コンポジットブラック、葉緑色、肌色および空色の各色について、１００％、８０％、６０％、４０％、２０％及び１０％の各濃度のベタパッチを印字して記録物を作成した。なお、印字に用いたインクは、上記プリンタ純正品であって、全て水溶性染料を含んでいる水性インクである。次いで、この記録物のインク受容層表面に、１２６ｍｍ×８９ｍｍの面積あたり約０．３ｇの割合で、上述した種々の画像堅牢性向上剤、及び比較例２の化合物を付与し、天然コットン素材のラビング部材で画像全面に亘ってラビング処理を行って、実施例１から８、及び比較例２の記録物を得た。そして各記録物について、各色Ｏ．Ｄが約１．０のパッチを選んで、以下の画像堅牢性試験に用いた。
耐光性および耐ガス性の評価方法：上記の記録物の試験前の画像濃度と試験後の画像濃度とを分光光度計・スペクトリノ（グレタグマクベス社製）を用いて測定した。耐光性および耐ガス性評価は、以下に記述する判定基準に基づき判定し、結果は表１に示した。
【００７７】
（試験方法）
▲１▼耐光性試験１
以下の試験条件に従って、キセノンフェードメーターを用いて、耐光暴露試験を行った。本試験は、室内における窓越し太陽光の影響を考慮した画像堅牢性試験である。
試験条件；
照射光量：５０ｋｌｕｘ
試験時間：１００時間
試験槽内温湿度条件：３０℃・４５％ＲＨ
フィルタ：（アウター）ソーダライム、（インナー）ボロシリケート
【００７８】
耐光性評価：
ＩＳＯ１０９７７（１９９３）の基準を参考に耐光暴露試験後の反射濃度残存率（ΔＥ）データより評価した。具体的には、単色のインクによる記録部に関しては、試験後の記録部が示す反射濃度残存率を測定し、下記表１の基準に従って評価した。一方、複数色のインクを重ねて形成したコンポジットカラーの記録部に関しては、試験後の各記録部の反射濃度残存率に加えて、各コンポジットカラー記録部を構成している複数の構成色それぞれの耐光暴露試験後の反射濃度残存率を測定し、得られた反射濃度残存率の差を算出し、表１に示す基準に従って評価した。コンポジットカラー記録部の評価に、該コンポジットカラー記録部を構成する構成色の反射濃度残存率の差を加えた理由は、コンポジットカラー記録部の画像堅牢性は記録部自体の反射濃度残存率だけでなく、コンポジットカラー記録部を構成している複数の構成色のそれぞれの褪色の程度も視覚上の画質に大きな影響を及ぼすからである。つまり、例えコンポジットカラーの記録部自体の反射濃度残存率が大きい場合であっても、コンポジットカラーを構成している構成色の何れか１つでも、試験前後で反射濃度が大きく変化している場合には、目視におけるカラーバランスが崩れ、視覚的に退色が大きい様に感じることがある為である。
【００７９】
表１において、例えば、濃度残存率が９０％以上というのは、ブラック、シアン、マゼンタ、イエロー、コンポジットブラック、葉緑色、肌色および空色の各記録部の反射濃度残存率の内、最も低い値でも９０％以上であることを示す。また、例えば、濃度残存率の差が５％未満というのは、上記した４色のコンポジットカラー記録部において、各コンポジットカラー記録部を構成している構成色それぞれの試験前の反射濃度残存率の値の差のうちの最大値が、５％未満の場合である。濃度残存率の差が５％以上１０％未満というのは、該４色コンポジットカラー記録部のそれぞれを構成している構成色それぞれの反射濃度残存率の差のうちの最大値が５％以上１０％未満の場合である。
【００８０】
【表１】

評価結果を表２に示す。
【００８１】
▲２▼耐光性試験２
以下の試験条件に従って、蛍光灯耐光性試験機を用いて、耐光暴露試験を行った。本試験は、室内における蛍光灯光の影響を考慮した画像堅牢性試験である。
試験条件；
照射光量：６０ｋｌｕｘ
試験時間：４８０時間
試験層内温湿度条件：３０℃・４５％ＲＨ
フィルタ：ソーダライム
耐光性評価；
ＩＳＯ１０９７７（１９９３）の基準を参考に耐光暴露試験後の濃度残存率データより耐光性を上記▲１▼と同様の評価基準を用いて評価した。結果を表２に示す。
【００８２】
▲３▼耐ガス性試験
オゾン試験装置（スガ試験機社製、商品名：オゾンウエザオメーター）を用いて、オゾン暴露試験を行った。
試験条件；
暴露ガス組成：Ｏ_３３ｐｐｍ
試験時間：６時間
試験層内温湿度条件：４５℃、５５％ＲＨ
耐ガス性評価；
オゾン暴露試験後の濃度残存率データを上記▲１▼の評価と同様の評価基準を用いて評価した。結果を表２に示す。
【００８３】
▲４▼黄変試験
（試験方法および評価方法）
未印字の被記録媒体に対して、実施例１から６の画像堅牢性向上剤、比較例１から２の化合物の各々を上記と同様にして付与し、ラビング処理して実施例１から６、比較例２のサンプルを調製し、比較例１としての未処理のサンプルを加えて、以下の環境の中に各サンプルを放置し、試験前後の記録面の色味を比較した。結果は表２に示した。
試験条件；
試験層温湿度条件：５０℃、８０％ＲＨ
試験時間：２４０時間
【００８４】
【表２】

【００８５】
▲５▼光沢度試験
未印字の被記録媒体に対して、新たに実施例１および６の各々を上記と同様に付与して、ラビング処理してサンプルを調整し、また、比較例１として未処理のサンプルを用意した。これら３サンプルを常温で２４時間保存した後の各々の光沢度をＪＩＳ−Ｚ−８７４１に規定される方法で測定した。その結果を表３に示す。
【００８６】
【表３】

【００８７】
新たに実施例１および６の記録物（１００％ベタパッチ）と比較例１の記録物（１００％ベタパッチ）を▲１▼で用いたサンプルと同様に調製し、常温で２４時間保存した後の、各々の画像の濃度をグレタグスペクトロイノ（グレタグマクベス製）で測定した。その結果を表４に示す。
【００８８】
【表４】

【００８９】
【発明の効果】
本発明によって、インクジェット記録画像の堅牢性が向上し、特に、インクジェット記録画像を家庭やオフィス等の通常の室内環境で展示する用途に使用しても画像の褪色を劇的に防止することができる。又、本発明は、記録画像の記録品位を低下させることなく画像堅牢性を向上することが可能である。
ある。
【図面の簡単な説明】
【図１】本発明に用いられる被記録媒体の断面構造を模式的に示す概略断面図である。
【図２】本発明にかかる画像堅牢性の向上方法の概略説明図であり、インク受容層中の間隙に向上剤が充填された状態を示す概略断面図である。
【図３】被記録媒体の支持体として、インク受容層側の表面に緻密な多孔質層があるものを用いたときの、インク受容層中の水分子の挙動の説明図である。
【図４】本発明にかかるアプリケータの一実施態様である。（ａ）は、使用時の形態を示す概略斜視図であり、（ｂ）は収納や携帯に適する、塗布部が蓋で保護された形態を示す概略斜視図である。
【図５】本発明にかかるアトマイザの概略断面図である。
【図６】本発明にかかるインクジェット記録装置の概略断面図である。
【符号の説明】
１０００　　支持体
１００１　　画像堅牢性向上剤
１００３　　インク受容層
１００５　　微粒子
１００７　　結着剤
１００９　　色材
１０１１　　インク受容層中の間隙
１３０１　　多孔質層
４００１　　画像堅牢性向上剤貯蔵部
４００２　　画像堅牢性向上剤塗布部
４００３　　蓋
５００１　　ディスペンス手段（スプレー部）
５００３　　画像堅牢性向上化剤貯蔵部[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention relates to an image fastness improver which can obtain more excellent gas fastness, high quality gloss, and high image density for a recorded matter having an image formed on the ink receiving layer having a porous structure. The present invention relates to a recorded matter using an image fastness improving agent, a method for improving image fastness and a method for producing a recorded matter, and an image fastness improving kit including such an image fastness improving agent.
[0002]
[Prior art]
Among various image recording methods, the ink jet recording method has been widely spread at present and is expected to be further spread in the future. Currently required image characteristics are high-quality images at the same level as silver halide photographic images, specifically, high print density, excellent water fastness, light fastness, no feathering and bleeding, It is a high quality image having gas fastness and high quality glossiness. In particular, it is required to maintain a high-quality image equivalent to a silver halide photographic image for a long period of time, that is, to have excellent robustness against deterioration due to gas in the air and deterioration due to water or moisture.
[0003]
To date, many studies have been made to improve the image fastness. For example, as disclosed in JP-A-07-314882, an antioxidant is added to a porous ink receiving layer of an ink jet recording medium to improve the gas fastness of the recording medium. Further, as disclosed in Japanese Patent Application Laid-Open No. 09-48180, a method of protecting a printed matter by coating a printed material with a water-based ink with a protective agent made of a specific resin is disclosed. Further, as described in JP-A-06-301441, after recording is performed on a recording sheet provided with a porous layer made of alumina hydrate on a base material, the porous layer is impregnated with the cured composition. There has been proposed a recording method for curing and making the recording transparent.
[0004]
[Problems to be solved by the invention]
However, for example, the fading phenomenon that occurs when a recorded image is displayed in a room is various such as that the entire image is reddish, greenish, and the non-printed portion is yellowed. . In addition, the factor causing the problem is not limited to light alone, but various factors such as various gases in the air, and the effects of temperature and humidity can be considered, and it is not sufficient to simply add an antioxidant to the recording medium for inkjet recording. In some cases, image fastness could not be obtained. In particular, it has sometimes been difficult to dramatically improve the gas fastness. In addition, the method of coating the printed matter with the protective agent has a problem that the glossiness of the printed matter surface may not be sufficiently obtained. Japanese Patent Application Laid-Open No. 9-48180 does not disclose any application of a protective agent to a printed material formed using a recording medium having an ink receiving layer having a porous structure. Does not suggest anything. Furthermore, in the technique of impregnating the inorganic porous layer with the cured composition and curing and making the composition transparent, the printing surface may be non-uniformly transparent and unevenness may occur because curing does not proceed uniformly. There was a problem.
[0005]
Therefore, the present inventor can provide a recording medium on which an image has been recorded with more excellent gas fastness than ever, and at the same time, have a glossy high-quality image equivalent to a silver halide photographic image, and a high image quality. Various approaches have been studied for obtaining the concentration. As a result, it was found that by providing a monovalent saturated aliphatic alcohol ester compound of a polybasic acid having a molecular weight of 300 or more, the robustness of an image, in particular, the fastness to gas, was remarkably improved. Was.
[0006]
[Means for Solving the Problems]
The image fastness improver of a recorded matter according to the present invention is an image fastness improver of a recorded matter having an ink receiving layer having a porous structure and having an image formed on the ink receiving layer by a coloring material. And a polybasic acid monovalent saturated aliphatic alcohol ester compound having a molecular weight of 300 or more.
[0007]
The recorded matter according to the present invention is a recorded matter provided with an ink receiving layer having a porous structure, and the ink receiving layer has a region where an image is formed by a coloring material, and the image having the above-described structure is formed in the region. It is characterized by having a fastness improver.
[0008]
The method for improving the image fastness of a recorded matter according to the present invention includes improving the image fastness of a recorded matter provided with an ink receiving layer having a porous structure, and wherein the ink receiving layer has a region where an image is formed by a coloring material. A method, characterized in that an image fastness improver having the above structure is applied to the region.
[0009]
The method for producing a recorded matter according to the present invention is a method for producing a recorded matter comprising an ink receiving layer having a porous structure, and the ink receiving layer having a region where an image is formed by a coloring material,
(I) applying ink to the ink receiving layer to obtain a region where an image is formed by a coloring material contained in the ink;
(Ii) a step of applying the image fastness improver having the above structure to the ink receiving layer;
It is characterized by having.
[0010]
The kit for improving the image fastness of a recorded matter according to the present invention is characterized by comprising a recording medium having an ink receiving layer having a porous structure, and an image fastness improver having the above-described configuration.
[0011]
By using the image fastness improver of the recorded matter of the present invention, the fastness of a recorded matter having an image formed by an aqueous ink or the like on a recording medium having a porous ink receiving layer such as coated paper, especially ozone It is possible to surprisingly improve the fastness to gases such as, and to add further depth to the color itself of an image. Japanese Patent Application Laid-Open No. 56-77154 discloses that the voids of an ink-jet sheet having a porous structure are filled with a non-volatile substance. However, there is no disclosure of a specific technique according to the present invention. Absent.
[0012]
BEST MODE FOR CARRYING OUT THE INVENTION
Hereinafter, the image fastness improver according to the present invention and its use will be described.
[0013]
A: Image fastness improver First, the image fastness improver of the present invention will be described in detail.
[0014]
In a recording medium having an ink receiving layer provided on at least one surface of a base material, a monovalent saturated fatty acid of a polybasic acid having a molecular weight of 300 or more is added to the ink receiving layer as an image fastness improver after image recording by ink jet recording or the like. An image fastness improver mainly containing an aliphatic alcohol ester compound is applied, and more preferably thereafter, the porous ink receiving layer is impregnated with the image fastness improver to record from various physical or chemical changes. The image is protected, and the recorded image is provided with high gas fastness, high quality glossiness and high image density equivalent to silver halide photographic images.
[0015]
As the image fastness improver, those which are in a liquid state at normal temperature (15 to 30 ° C.) and normal pressure and have low volatility are preferable. The image fastness improver according to the present invention mainly contains a monovalent saturated aliphatic alcohol ester compound of a polybasic acid having a molecular weight of 300 or more, and is used for various purposes for various purposes as long as the effects of the present invention are not impaired. May be contained. Here, "mainly contains" means that the content is the largest among the components in the image fastness improver, preferably 50% or more, more preferably 80%, and more preferably 80% or more. Is 90% or more, and the case where the image fastness improver is composed of only this ester compound is also included.
[0016]
As the ester compound, specifically, a partial ester compound of a polybasic acid and a monovalent saturated aliphatic alcohol can be used. Here, the polybasic acid means an acid in which the number of hydrogen atoms that can be substituted with a metal atom or a positive group (that is, basicity) is 2 or more among the hydrogen atoms contained in one molecule of the acid, The compound means an ester compound in which the ratio of the molar amount of the carboxylic acid esterified with the monovalent saturated aliphatic alcohol to the molar amount of all the carboxylic acids of the polybasic acid is less than 1. When a partially esterified product is used as the ester compound used in the present invention, the partial esterification ratio is preferably in the range of 10 to 90%. The definition of the partial esterification rate is based on the following formula.
[0017]
(Equation 1)
Partial esterification rate (%)
= [1- (mol amount of carboxylic acid group in ester compound / mol amount of carboxylic acid group of polybasic acid before esterification)] × 100
Examples of the partially esterified product of a polybasic acid and a monovalent saturated aliphatic alcohol include a polybasic acid that is an aliphatic alkyl polybasic acid having 3 to 18 carbon atoms or an aromatic polybasic acid and a monohydric acid having 2 to 30 carbon atoms. A partially esterified product with a monovalent saturated aliphatic alcohol which is a saturated aliphatic alcohol can be mentioned as a preferred partial esterified product.
[0018]
The ester compound used in the present invention has a very low volatility because it has a molecular weight of 300 or more, so that it is difficult for the improver to evaporate after being impregnated in the porous layer and generate a void in the porous layer.
[0019]
The reason why the image fastness is improved when the image fastness improver is applied is not clear, but for example, the inorganic porous layer constituting the porous ink receiving layer is composed of boehmite particles. In such a case, a hydrogen bond occurs between the boehmite particles and mainly the carboxylic acid group of the ester compound, and the ester compound is easily adsorbed to the boehmite particles due to its chemical structure, and thus is adsorbed to the boehmite particles. It is assumed that the dye molecules existing in the vicinity of the dye molecules and boehmite particles are protected from the adsorption of gas molecules, and as a result, the gas fastness at room temperature and the gas fastness in a high temperature and high humidity environment are improved. You.
[0020]
The molecular weight of the ester compound is preferably 2000 or less. The reason is that when the molecular weight is larger than 2,000, the viscosity at normal temperature and normal pressure becomes extremely high, and tends to be solid.
[0021]
Specific examples of the partially esterified product in which the molecular weight of the polybasic acid and the monovalent saturated aliphatic alcohol is 300 or more include mono-2-heptylundecyl adipate, monoisodecyl adipate, monotridecyl phthalate, mono-2-ethylhexyl phthalate, Monoisononyl phthalate, monodecyl phthalate, di-2-ethylhexyl trimellitate, diisodecyl trimellitate, and the like are included.
[0022]
According to a further preferred embodiment of the present invention, when at least one of an antioxidant and an ultraviolet absorber is further contained, gas resistance and light resistance are further improved.
[0023]
The antioxidant is not particularly limited as long as a predetermined effect can be obtained. For example, thiourea-based compounds such as N, N-diethylthiourea, thiuram-based compounds such as tetramethylthiuram disulfide and tetraethylthiuram disulfide, and 2-methyl- Thiazoles such as 5-chlorobenzothiazole, 2-methyl-5-bromobenzothiazole, 2-mercaptobenzothiazole, and 1,2,2,6,6-pentamethyl-4-piperidyl 1,2,3,4-butane Hindered amines such as tetracarboxylate, 1,2,2,6,6-pentamethyl-4-tridecyl 1,2,3,4-butanetetracarboxylate, 2- (2H-benzotriazol-2-yl) -p -Benzotriazoles such as cresol, O, O'-dioctadecylpentaerythritol bis Examples include phosphites such as phosphite, trisnonylphenyl phosphite, and phenyldiisodecyl phosphite; and dithiocarbamate salts such as zinc diethyldithiocarbamate, sodium dimethyldithiocarbamate, and sodium diethyldithiocarbamate. Seeds can be used.
[0024]
The ultraviolet absorber is not particularly limited as long as it can obtain a predetermined effect. For example, 6,6′-di-t-butyl-4,4′-butylidenedi-m-cresol, 3,3 ′, Hindered phenols such as 3 ″, 5,5 ′, 5 ″ -hexa-t-butyl-α, α ′, α ″-(mesitylene-2,4,6-triyl) tri-p-cresol , 2- (3,5-di-t-pentyl-2-hydroxyphenyl) -2H-benzotriazole, 2- (3,5-di-t-butyl-2-hydroxyphenyl) -2H-benzotriazole, etc. Benzotriazole, 1,2,2,6,6-pentamethyl-4-piperidyl 1,2,3,4-butanetetracarboxylate, 1,2,2,6,6-pentamethyl-4-tridecyl 1,2 , 3,4-butanetetracarboxylate Hindered amines, benzophenones such as 2,4-dihydroxybenzophenone, 2-hydroxy-4-methoxybenzophenone, and 4-dodecyloxy-2-hydroxybenzophenone, and salicylic acids such as phenyl salicylate, and at least one of these is used. be able to.
[0025]
Examples of the ultraviolet absorber further include, for example, those represented by the following structural formulas (9) to (16).
[0026]
Embedded image

[0027]
Embedded image

[0028]
In the above formula, tC ₄ H ₉ represents a tert-butyl group, and tC ₈ H ₁₇ represents a tert-octyl group.
[0029]
B: Recording Medium As the recording medium that can be used in the present invention, any recording medium that has a porous ink receiving layer and performs recording by attaching ink can be used. it can. However, in the present invention, since the recording medium is impregnated with the image fastness improver, it is preferable that the medium does not show through the image fastness improver. The recording medium according to the present invention is particularly suitable when the recording medium in which the porous structure of the ink receiving layer is formed of fine particles and the coloring material is adsorbed on the fine particles uses an ink jet method. is there. Such a recording medium for inkjet is preferably a so-called absorption type in which ink is absorbed by a gap formed in an ink receiving layer on a support. The absorption type ink receiving layer has a porous structure mainly composed of fine particles and optionally containing a binder and other additives.
[0030]
Examples of the fine particles include silica, clay, talc, calcium carbonate, kaolin, aluminum oxide such as alumina or alumina hydrate, diatomaceous earth, titanium oxide, hydrotalcite, inorganic pigments such as zinc oxide, urea formalin resin, and ethylene resin. And organic pigments such as styrene resin. One or more of these are used. Water-soluble polymers and latexes are preferably used as the binder. For example, polyvinyl alcohol or a modified product thereof, starch or a modified product thereof, gelatin or a modified product thereof, gum arabic, cellulose derivatives such as carboxymethylcellulose, hydroxyethylcellulose, hydroxypropylmethylcellulose, SBR latex, NBR latex, methyl methacrylate-butadiene copolymer Copolymer latex, functional group-modified polymer latex, vinyl copolymer latex such as ethylene-vinyl acetate copolymer, polyvinylpyrrolidone, maleic anhydride or its copolymer, acrylate ester copolymer, etc. are used. One selected type or a combination of two or more types can be used as needed.
[0031]
In the ink receiving layer, other additives can also be used, for example, if necessary, a dispersant, a thickener, a pH adjuster, a lubricant, a fluidity modifier, a surfactant, an antifoaming agent, Release agents, fluorescent brighteners, ultraviolet absorbers, antioxidants and the like can be mentioned.
[0032]
A particularly suitable recording medium according to the present invention is preferably a medium in which an ink receiving layer is formed mainly of fine particles having an average particle diameter of 1 μm or less. Particularly preferred examples of the fine particles include silica or aluminum oxide fine particles. The reason that the aluminum oxide fine particles and silica are particularly effective is considered as follows. That is, the coloring material adsorbed to the fine particles of aluminum oxide, _silica, NO X, SO _X, it was found that susceptible to fading of the colorant by gas such as ozone, these fine particles are easy to attract gas, colorant It is considered that a gas is present in the vicinity of, and the coloring material is easily discolored. Preferred as silica fine particles are silica fine particles represented by colloidal silica. Colloidal silica itself is also commercially available, but particularly preferred are those described in, for example, Japanese Patent Nos. 2803134 and 2881847. Preferred examples of the aluminum oxide fine particles include alumina hydrate fine particles. As one of such alumina-based pigments, alumina hydrate represented by the following general formula can be mentioned as a preferable one.
[0033]
Al ₂ O _3-n (OH) _2n · _m H ₂ O
In the above formula, n represents an integer of 1, 2 or 3, and m represents a value of 0 to 10, preferably 0 to 5. However, m and n do not become 0 at the same time. mH 2 _O, since it represents also often does not participate in the formation of mH 2 _O crystal lattice eliminable aqueous phase, m can take a value not an integer or an integer. In addition, m can reach a value of 0 when this type of material is heated.
[0034]
Alumina hydrate is generally used, such as the hydrolysis of aluminum alkoxide and sodium aluminate as described in U.S. Pat. Nos. 4,242,271 and 4,202,870, and JP-B-57-44605. It is preferable to use a solution produced by a known method such as a method of adding an aqueous solution of sodium sulfate, aluminum chloride or the like to an aqueous solution of sodium aluminate or the like described in Japanese Patent Application Laid-Open Publication No. H11-15064.
[0035]
Further, the recording medium for inkjet using these alumina hydrates has excellent affinity, absorptivity and fixability with the image fastness improver according to the present invention, and realizes the photographic image quality as described above. It is more suitable for applying the present invention because of its excellent glossiness, transparency and fixing property of a coloring material in a recording liquid such as a dye.
[0036]
The mixing ratio of the fine particles of the ink jet recording medium used in the present invention and the binder is preferably in the range of 1: 1 to 100: 1 by weight. By setting the amount of the binder in the above range, it is possible to maintain a pore volume suitable for impregnating the ink receiving layer with the image fastness improver. The content of the aluminum oxide fine particles or the silica fine particles in the ink receiving layer is preferably 50% by weight or more, more preferably 70% by weight or more, and still more preferably 80% by weight or more and 99% by weight or less. Most preferred. The coating amount of the ink receiving layer, is preferably 10 g / m ² or more on a dry solid basis for the impregnation of image fastness enhancing agent good, 10 to 60 g / m ² is most preferred is there.
[0037]
The recording medium used in the present invention preferably has a support for supporting the ink receiving layer described above, but the support is not particularly limited, and the ink receiving layer having the porous structure described above may be formed. Any material can be used as long as it can provide a stiffness that can be transported by a transport mechanism such as an inkjet printer. For example, a support having a porous layer formed by applying an inorganic pigment such as barium sulfate, titanium oxide, and zinc oxide together with a binder between the support and the ink receiving layer, or using a resin-coated paper for the support Is also good. The recording medium having a porous layer between the support and the ink receiving layer is a recording medium according to a more preferred embodiment of the present invention described above, wherein "the image forming region is located in the thickness direction of the ink receiving layer. It is more effective when used in a "recorded matter having a portion in which all or substantially all of the portion is filled with an image fastness improver". That is, when a recorded matter in which all or substantially all of the holes existing in the thickness direction of the ink receiving layer are filled with the image fastness improver is left for a long time in a high-temperature and high-humidity environment, Even in this case, it is possible to extremely effectively suppress the occurrence of stickiness of the surface due to the exudation of the image fastness improving agent onto the surface of the recorded material, and it is possible to obtain a recorded material having extremely excellent storability.
[0038]
Although it is not clear why the above-mentioned effects can be obtained, the image fastness improver supplied to fill all or substantially all of the holes existing in the thickness direction of the ink receiving layer has an air permeability. For example, since it is difficult to pass through the baryta layer, the holes are reliably filled with the image fastness improver. Further, air and moisture existing in the holes in the ink receiving layer are reduced as shown in FIG. As schematically shown in FIG. 7, the filling of the pores with the solidity improver causes the porous layer (1301) to move or be adsorbed, and the air or moisture remaining in the ink receiving layer. Is considered to be able to suppress or prevent.
[0039]
C: Method for Producing Recorded Material and Method for Improving Image Fastness The recorded material according to the present invention comprises a support (1000) having a porous ink receiving layer (1003) containing fine particles (1005) on the surface thereof. A recorded matter having an area in which an image is formed by a coloring material (1009) adsorbed on the surface of fine particles, wherein the above-described image fastness improver (hereinafter referred to as an improver) 1001 is applied to the area. is there.
[0040]
Then, for example, as shown in FIG. 2, all or substantially all of the color material distributed in the thickness direction of the ink receiving layer is in the image fastness improving agent in the region where the image is formed. It is more preferable that all or substantially all of the holes distributed in the thickness direction of the ink receiving layer are filled with the image fastness improver, and the image fastness is further improved. . Further, the ink receiving layer of the recorded matter according to the present invention is not particularly limited to one containing fine particles as long as it has a porous structure.
[0041]
In the above-described more preferred embodiment of the present invention, the reason why the tint of the recorded matter (printed matter) by the ink or the like formed on the recording medium having the receiving layer and the surprising improvement in the gas resistance are achieved. Is considered to be due to the following mechanism.
[0042]
FIG. 1 schematically shows a cross-sectional structure of a so-called coated paper provided with a porous ink receiving layer made of fine particles on a support made of paper or the like. In FIG. 1, reference numeral 1000 denotes a support, and 1003 denotes an ink receiving layer held by the support 1000. The ink receiving layer 1003 has a porous structure including fine particles 1005, and the fine particles are fixed by a binder 1007. In the process of permeating the ink droplets applied to such coated paper into the ink receiving layer 1003, the coloring material 1009 contained in the ink is adsorbed on the surface of the fine particles 1005, and an image is formed.
[0043]
After supplying the image fastness improver 1001 to the surface of the coated paper on which recording has been performed in this manner, in order to make the coloring material relatively deep in the ink receiving layer into the improver, for example, When the rubbing treatment is performed after the supply of the ink, the image fastness improver fills the pores in the ink receiving layer 1003, here, the gaps 1011 between the fine particles 1005. Since the enhancer is a non-aqueous substance, it gradually replaces the aqueous medium of the aqueous ink trapped between the particles, and also covers the periphery of the coloring material adsorbed on the fine particle surface. Finally, as shown in FIG. 2, the gap 1011 is filled with the improver 1001, and all or substantially all of the color material distributed in the thickness direction of the ink receiving layer is used as the image fastness improver. When all or substantially all of the pores present or present in the thickness direction of the ink receiving layer are filled with the improver, the coloring material 1009 becomes a gas such as SO _X or NO _X in the atmosphere or The contact with moisture containing them will be cut off. As a result, it is considered that the deterioration of the coloring material in the ink receiving layer is suppressed, and the robustness of the image is further improved. In addition, the effect of improving the color tone, improving the print density, and improving the glossiness obtained together with the effect of improving the image fastness according to the present invention is based on the substance forming the ink receiving layer and the pores (air), It is considered that the irregular reflection of light on the surface and inside of the ink receiving layer caused by the difference in the refractive index between the ink and the gap (air) is suppressed by filling the gap with the image fastness improver. .
[0044]
The image fastness improver according to the present invention is preferably applied to the ink receiving layer in a liquid state. Therefore, the ink is easily penetrated into the ink receiving layer, and is deformed in accordance with the shape of the porous structure in the ink receiving layer, so that the effect of incorporating the coloring material into the image fastness improver is sufficiently exhibited. It is possible. Moreover, when the recorded matter is allowed to deform by being held in the ink receiving layer as a liquid, the porous structure of the ink receiving layer, e.g. The contact state of the image fastness improver with the outer wall of the film is kept good.
[0045]
On the other hand, when the image fastness improver is in the form of a solid in the passage of a temperature such as wax, there are problems such as the need for pressure to penetrate the ink receiving layer and the difficulty of obtaining a uniform permeation state. . Furthermore, when applied in a state diluted with a volatile solvent and solidified after application, or in a form that contains a component that solidifies after being applied in a liquid form, it takes in moisture and bubbles during the solidification process May cause clouding of the phase of the improver, and furthermore, if the volume is reduced upon solidification, a void is formed between the phase of the improver and the porous structure, thereby protecting the coloring material. May decrease. By confirming that there is no thermal behavior (endothermic or exothermic) at the time of material dissolution by a method such as local thermal analysis of the ink receiving layer, it is confirmed that the ink receiving layer is kept in a liquid state in the ink receiving layer. It is possible.
[0046]
The rubbing treatment used in the present invention means at least one of wiping and polishing for positively filling the pores in the ink receiving layer with the fastness improver.
[0047]
(1) First Embodiment As one embodiment of the method for producing a recorded matter or the method for improving image fastness according to the present invention, as described above, the ink receiving layer having a porous structure is provided. It is more preferable to supply the above-mentioned image fastness improver to the surface of the ink receiving layer of the recording sheet on which an image such as a character or a picture is recorded by applying the ink or the ink droplet, and then to perform a rubbing treatment. No. Here, the improver may be supplied and applied to at least a part of the image recording portion of the recording sheet, but is most preferably applied to the entire surface of the recording sheet. This makes it possible to more reliably prevent the color material in the ink receiving layer from being attacked by a gas such as ozone.
[0048]
Further, as described above, in a more preferred embodiment of the present invention, all or substantially all of the holes existing in the thickness direction of the ink receiving layer are filled with the image fastness improver. In this case, the supply amount of the image fastness improver is suitably set to an amount that completely fills the holes and an amount that takes into consideration the amount absorbed into the application member, in consideration of the time and labor required for application. is there. Here, the amount by which the holes are completely filled is taken into consideration, for example, in the case of an ink receiving layer composed of fine particles, from the degree of porosity (such as oil absorption) of the ink receiving layer. By supplying and applying such an amount of the image fastness improver, the pores of the ink receiving layer can be almost certainly filled with the image fastness improver.
[0049]
Specifically, for example, in order to improve the robustness of an image formed on a recording medium having an oil absorption of 0.3 cc, about 0.3 g of an image fastness improver is applied, and a rubbing treatment is performed. By doing so, a sufficient effect of improving the robustness can be obtained. This means that the effect of the present invention is achieved not only by covering the surface portion of the ink receiving layer, but also by filling the holes of the ink receiving layer with the image fastness improver. is there.
[0050]
Here, the method of applying the image fastness improver is not particularly limited, such as brush coating, spray coating, roller coating, spatula coating, sponge coating, but as a specific method, for example, as shown in FIG. A container 5003 (dispenser, etc.) provided with a function 5001 (spray, pump, etc.) capable of supplying an appropriate amount of an image fastness improver to the surface of the ink receiving layer, and a rubbing member This can be realized by using an image robustness improvement kit that is a set of (1) and (2).
[0051]
As another embodiment, as shown in FIGS. 4A and 4B, an image fastness improving agent storage section 4001 containing an image fastness improving agent, and application of the image fastness improving agent. The supply of the image fastness improver and the rubbing treatment are simultaneously performed by using an applicator in which the image fastness improver in the storage section is integrated with the member 4002 so that the image fastness improver can leak out to the surface of the application member. You may do so. When the amount of the image fastness improving agent of the coating member 4002 is reduced, the image fastness improving agent is impregnated into the coating member by applying pressure to the image fastness improving agent storage section 4001. May be. Reference numeral 4003 denotes a lid of 4002. In order to obtain a recorded matter excellent in image fastness by the method according to the present invention, by using a set of the recording medium and the image-recording property improving agent, an image having high fastness can be easily obtained. .
[0052]
(2) Other Embodiment As another embodiment of the method for producing a recorded matter or the method for improving the image fastness according to the present invention, a method of performing processing without intervention of a manual in a recording apparatus can be cited. FIG. 6 is a schematic cross-sectional view of an apparatus for obtaining a recorded matter having excellent image fastness, which performs recording of an image on a recording medium by an inkjet method and processing for imparting fastness to a formed image. Means. In FIG. 6, reference numeral 25 denotes a housing, and 1 denotes a stacked unused recording medium, which is placed substantially horizontally on a supply tray (sheet feeding cassette) 2.
[0053]
Reference numeral 3 denotes a suction cup, which is moved by a suction cup moving mechanism (not shown) from a position a in the figure to a position b in contact with one of the uppermost sheets of the unused unused recording sheets 1, and sucks the topmost sheet. Can be lifted. At this time, the pressure inside the suction cup 3 is reduced by the suction mechanism (not shown) while the suction cup 3 is in contact with the recording paper, and the uppermost sheet of the recording paper 1 is sucked, and the recording paper 1 From the recording paper. In this state, the suction cup moving mechanism moves to the position c in the figure, and the leading end of the separated recording sheet can be inserted between the transport rollers 4 and 5. Thereafter, the suction operation of the suction mechanism is stopped to release the suction force of the suction cup 3, and the constraint of the recording paper by the suction cup 3 can be released.
[0054]
The transport rollers 4 and 5 are rotationally driven by a drive source such as a transport motor (not shown) via a clutch mechanism (not shown) or the like. Reference numerals 6 and 7 denote guide plates which are arranged to face each other at a predetermined interval, and form a supply path for recording paper conveyed by rotation of the conveying rollers 4 and 5. The cross-sectional shape of the supply path formed by the guide plates 6 and 7 is substantially semicircular, and extends from the vicinity of the transport rollers 4 and 5 to the upper sub-scan rollers 8 and 9. These sub-scanning rollers 8 and 9, together with a second pair of sub-scanning rollers 10 and 11 arranged in parallel in the left direction in the figure, sandwich the conveyed recording paper, and a control unit (not shown) ), Etc., the paper is fed. Reference numeral 15 denotes a guide plate for regulating the position of the recording paper between the sub-scanning rollers 8, 9, 10, and 11. Reference numeral 12 denotes a recording head (ink-jet head) in which a plurality of ink ejection nozzles are arranged in the direction in which the recording paper 1 is conveyed. The recording head 12 may include a plurality of ink jet heads each of which ejects a different color ink. An ink tank 13 stores ink to be supplied to the recording head 12. The recording head 12 and the ink tank 13 are mounted on a carriage, and can be moved in a direction substantially perpendicular to the recording paper conveyance direction by a carriage guide disposed substantially parallel to the rotation axes of the sub-scanning rollers 8 to 11. Is held in.
[0055]
Reference numeral 16 denotes an unused second recording sheet stacked and accommodated in the upper recording sheet accommodation section. Reference numeral 17 denotes a pressure plate on which the stacked recording papers 16 are placed and which is appropriately pressed toward the separation roller 18. Reference numerals 19 and 20 denote guide plates, which form a second supply path for guiding the leading end of one sheet of recording paper taken out by the separation roller 18 to the sub-scanning rollers 8 and 9.
[0056]
21, 22, 23, and 24 are means for detecting the presence or absence and the quality of each of the recording sheets 1 and 16 disclosed in, for example, Japanese Patent Laid-Open No. 1-264879. Reference numerals 21 and 23 denote light sources for irradiating the surface of the recording paper 1 and 16 with light of a predetermined wavelength, respectively, and reference numerals 22 and 24 denote photodetectors for receiving light reflected from the surface of the recording paper. is there.
[0057]
Such detection of the paper quality of the recording paper by the reflected light is performed because the surface roughness differs according to the type of the recording paper, and the degree of light diffusion changes accordingly. . For example, the surface of plain paper is microscopically entangled with fibers and the diffusion of the surface is large, so that the outputs of the detectors 22 and 24 are small. On the other hand, in the case of a sheet having a smooth surface and a low degree of light diffusion, the outputs of the detectors 22 and 24 increase. Whether the recording paper corresponding to the first separation mechanism using the suction cup 3 or the second separation mechanism using the separation roller 18 is loaded in the corresponding cassette by using such a light detecting means. Or whether a recording sheet suitable for recording is mounted.
[0058]
Reference numerals 26 and 27 denote guide plates which form a conveyance path for guiding recording paper discharged with the rotation of the sub-scanning rollers 10 and 11 to a process described later after the recording by the recording head 12 is completed. A planar heater (not shown) is attached to the guide plate, and heats the recording paper in the transport path formed by the guide plates 26 and 27 to promote drying of the ink discharged on the recording paper. .
[0059]
An image fastness improving agent is supplied to the recording surface of the recording thus obtained, and a region filled with the image fastness improving agent is formed in the ink receiving layer of the recording.
[0060]
The liquid 52 is an image fastness improver according to the present invention, and is supplied to the container 51 from a tank (not shown) by a supply device (not shown), and the height of the liquid level in the container 51 is always within a predetermined range. It is automatically supplied and controlled to be inside. Reference numeral 53 denotes a roller for applying a fastness improving agent, and a surface portion 53a has a sponge-like structure through which the fastness improving agent 52 can penetrate, and a part thereof is in contact with the fastness improving agent 52 in the container 51. By rotating the liquid applying roller 53 by driving of a drive source (not shown), the surface improving portion 52a can uniformly infiltrate the rigidity improver 52. Reference numeral 54 denotes a transport roller for nipping and transporting the recording medium in cooperation with the application roller 53. The transport roller 54 is separated from the application roller 53 when the recording medium is not clamped so that the robustness improver 52 does not adhere to the surface thereof, and is only provided when the recording medium is interposed. Desirably, the recording medium is nipped by contacting the application roller 53 and the transport roller 54. Reference numeral 55 denotes a drying heater which is used to dry the recording paper to which the fastness improver 52 has been applied.
[0061]
With the above configuration, after the recording by the recording head 12 is completed, the leading end of the recording medium is moved by the conveying roller 54 and the coating roller 53 before the trailing edge of the recording paper separates from the second pair of sub-scanning rollers 10 and 11. To the position of. Then, the recording medium is sandwiched between the transport roller 54 and the application roller 53, and with the rotation of these rollers 53, 54, the robustness improver 52 is uniformly supplied to one surface of the recording medium, It is also rubbed and filled in the gap between the ink receiving layers. The recording paper filled with the liquid is further subjected to a rubbing treatment as needed, and then discharged from the discharge port of the apparatus by the rotation of the discharge roller 33.
[0062]
FIG. 6 illustrates an image recording apparatus in which the inkjet recording and the filling of the image fastness improver are performed in the same apparatus. However, the present invention is not limited to this. The image recording apparatus having a configuration in which the liquid filling section is separated from the liquid recording section, and further, the application section of the image fastness improving liquid in which the filling section of the fastness improving liquid is independent of the image forming section are also within the scope of the present invention. belongs to.
[0063]
【Example】
Hereinafter, the present invention will be further described with reference to Examples and Comparative Examples.
[0064]
(Preparation of image fastness improver)
The image fastness improver used in Examples 1 to 8 by mixing a partial esterified product of a monobasic saturated aliphatic alcohol of a polybasic acid shown below with an additive, that is, an ultraviolet absorber, in the proportions shown in Table 2. Was prepared.
[0065]
Group A. Partially esterified product of polybasic acid and monovalent saturated aliphatic alcohol A-1. Compound name: mono-2-heptylundecyl adipate Molecular weight: 397
[0066]
Embedded image

A-2. Compound name: monodecyl phthalate Molecular weight: 306
[0067]
Embedded image

A-3. Compound name: di-2-ethylhexyl trimellitate Molecular weight: 434
[0068]
Embedded image

Group B: additive B-1. Product name: ADK STAB LA-63P (made by Asahi Denka Co., Ltd.)
[0069]
Embedded image

[0070]
Comparative Examples 1 and 2
Comparative Example 1 is a case where no image fastness improving agent was used.
As the treating agent of Comparative Example 2, C-1. Acrylic resin solution An acrylic resin emulsion (trade name: Boncoat 4001 manufactured by Dainippon Ink and Chemicals, Inc.) was used.
[0071]
(Example of manufacturing recording medium)
First, a substrate was prepared as described below. A pulp slurry consisting of 80 parts by mass of bleached bleached kraft pulp (LBPK) having a freeness of 450 ml CSF (Canadian Standard Freeness) and 20 parts by mass of softwood bleached kraft pulp (NBPK) having a freeness of 480 ml CSF was added with 0.60 cationized starch. Paper mass by adding 10 parts by mass, heavy calcium carbonate 10 parts by mass, light calcium carbonate 15 parts by mass, alkyl ketene dimer 0.10 part by mass, cationic polyacrylamide 0.03 part by mass, and sulfuric acid band 0.40 part by mass. After the preparation, the paper was made with Fourdrinier paper, subjected to three-stage wet pressing, and dried with a multi-cylinder dryer. Then, with a size press device, impregnated with an oxidized starch aqueous solution so as to have a solid content of 1.0 g / m ^2, and after drying, machine calendering was completed, and the basis weight was 155 g / m ² . A substrate having an air permeability of 50 seconds, a Beck smoothness of 30 seconds and a Gurley stiffness of 11.0 mN was obtained.
[0072]
Next, an undercoat layer was formed on the base material obtained as described above as follows. First, 100 parts by mass of a kaolin (Ultra White 90, manufactured by Engelhard) / zinc oxide / aluminum hydroxide having a weight ratio of 65/10/25 as a coating liquid used for forming an undercoat layer, 7 parts by mass of a commercially available styrene-butadiene latex were added to a slurry having a solid content concentration of 70% composed of 0.1 parts by mass of a polyacrylic acid-based dispersant, and adjusted to have a solids content of 60%. A composition was obtained. Next, this composition was coated on both surfaces of a substrate with a blade coater and dried so that the dry coating amount was 15 g / m ² . Thereafter, machine calendering is finished (linear pressure: 150 kgf / cm), basis weight: 185 g / m ² , Steckigt size: 300 seconds, air permeability: 3,000 seconds, Beck smoothness: 200 seconds, Gurley stiffness: 11.5 mN A layered substrate was obtained. The whiteness of the substrate with an undercoat layer was measured for each of five cut A4 size samples, and the average value was obtained. As a result, L ^{* was} 95, a ^{* was} 0, and b ^* was -2 (determined as a hue according to JIS Z 8729).
[0073]
Next, the ink receiving layer was formed. After the coating in the second surface treatment step, that is, immediately after the coating liquid was impregnated into the undercoat layer, the ink receiving layer was formed on the undercoat layer as it was. did. The coating liquid and the coating method used for forming the ink receiving layer at that time are as follows.
[0074]
Sodium aluminate was added to a 4% by weight solution of aluminum chloride to adjust the pH to 4. Thereafter, the temperature was raised to 90 ° C. while stirring, and stirring was performed for a while. Thereafter, sodium aluminate was added again to adjust the pH to 10, and the aging reaction was performed for 40 hours while maintaining the temperature. Then, it returned to room temperature and adjusted pH to 7-8. This dispersion was subjected to a desalting treatment, and then a peptizing treatment with acetic acid to obtain a colloidal sol. This colloidal sol of alumina hydrate was concentrated to obtain a 17% by weight solution. Polyvinyl alcohol PVA117 (trade name, manufactured by Kuraray Co., Ltd.) was dissolved in pure water to obtain a 9% by weight solution. The colloidal sol of the alumina hydrate and the polyvinyl alcohol solution were mixed and stirred so that the weight ratio of the solid content of the alumina hydrate and the solid content of the polyvinyl alcohol was 10: 1 to obtain a dispersion. This was applied by a die coater at a rate of 30 m / min to a dry coating amount of 35 g / m ² . Then, it was dried at 170 ° C. to form an ink receiving layer. The surface of the ink receiving layer of the recording medium was subjected to a rewet cast treatment using hot water using a rewet cast coater to obtain a recording medium. The oil absorption of the recording medium was about 21 cc / m ² .
[0075]
(Record creation and hardening processing)
On the recording medium prepared above, a recorded matter in which an image was recorded by the following method was produced, and the recorded matter was prepared using the image fastness improvers of Examples 1 to 6 and the compound of Comparative Example 2. Various image fastness tests were conducted according to the following methods (1) to (5). In addition, a recorded material that had not been subjected to any processing was similarly evaluated as Comparative Example 1.
[0076]
A genuine ink tank (trade name: BCI-6BK, BCI-6Y, M, C, BCI-6PM, BCI-6PC) is attached to a photo printer (trade name: manufactured by BJ-F870 Canon) using an inkjet method. Is mounted on the recording surface of the recording medium obtained above, as black, cyan, magenta, and yellow as a single color, and as composite colors, 100%, 80% for each of composite black, leaf green, flesh color, and sky blue. A solid patch of each density of 60%, 40%, 20% and 10% was printed to produce a recorded matter. The ink used for printing is a genuine product of the printer, and is an aqueous ink containing a water-soluble dye. Next, the above-mentioned various image fastness improvers and the compound of Comparative Example 2 were applied to the surface of the ink receiving layer of the recorded matter at a ratio of about 0.3 g per area of 126 mm × 89 mm, and a natural cotton material was obtained. Rubbing treatment was performed on the entire surface of the image with a rubbing member to obtain recorded materials of Examples 1 to 8 and Comparative Example 2. For each recorded matter, each color O.D. A patch with a D of about 1.0 was selected and used in the following image fastness test.
Evaluation method of light fastness and gas fastness: The image density of the above recorded matter before the test and the image density after the test were measured using a spectrophotometer / Spectrino (manufactured by Gretag Macbeth). The light fastness and gas fastness were evaluated based on the criteria described below, and the results are shown in Table 1.
[0077]
(Test method)
(1) Light fastness test 1
Under the following test conditions, a light resistance exposure test was performed using a xenon fade meter. This test is an image fastness test that considers the influence of sunlight through a window in a room.
Test condition;
Irradiation light amount: 50klux
Test time: 100 hours Temperature and humidity conditions in test chamber: 30 ° C, 45% RH
Filter: (outer) soda lime, (inner) borosilicate
Light fastness rating:
It was evaluated from the reflection density residual ratio (ΔE) data after the light resistance exposure test with reference to the standard of ISO10977 (1993). Specifically, for the recording portion using a single color ink, the reflection density residual ratio of the recording portion after the test was measured and evaluated according to the criteria in Table 1 below. On the other hand, for a composite color recording portion formed by superimposing a plurality of color inks, in addition to the reflection density residual ratio of each recording portion after the test, each of the plurality of constituent colors constituting each composite color recording portion was tested. The reflection density residual ratio after the light resistance exposure test was measured, and the difference between the obtained reflection density residual ratios was calculated and evaluated according to the criteria shown in Table 1. The reason for adding the difference in the reflection density residual ratio of the constituent colors constituting the composite color recording unit to the evaluation of the composite color recording unit is that the image fastness of the composite color recording unit is determined only by the reflection density residual ratio of the recording unit itself. In other words, the degree of fading of each of a plurality of constituent colors constituting the composite color recording section greatly affects the visual image quality. In other words, even if the residual ratio of the reflection density of the composite color recording unit itself is large, the reflection density of any one of the constituent colors constituting the composite color significantly changes before and after the test. The reason for this is that the visual color balance may be lost and visual fading may be large.
[0079]
In Table 1, for example, the fact that the density remaining ratio is 90% or more means that even the lowest value among the reflection density remaining ratios of the recording portions of black, cyan, magenta, yellow, composite black, leaf green, skin color and sky blue is used. 90% or more. Further, for example, the difference of the residual density of less than 5% means that in the above-described four-color composite color recording section, the reflection density residual rate of each of the constituent colors constituting each composite color recording section before the test is measured. The case where the maximum value among the value differences is less than 5%. The difference between the residual densities of 5% or more and less than 10% means that the maximum value among the differences between the residual densities of the reflection densities of the constituent colors constituting each of the four-color composite color recording sections is 5% or more and 10% or less. %.
[0080]
[Table 1]

Table 2 shows the evaluation results.
[0081]
(2) Light fastness test 2
A light resistance exposure test was performed using a fluorescent lamp light resistance tester under the following test conditions. This test is an image fastness test that considers the influence of fluorescent light in a room.
Test condition;
Irradiation light amount: 60klux
Test time: 480 hours Temperature / humidity condition in test layer: 30 ° C / 45% RH
Filter: Soda lime lightfastness evaluation;
The light resistance was evaluated from the residual density data after the light resistance exposure test using the same evaluation criteria as the above (1) with reference to the standard of ISO 10977 (1993). Table 2 shows the results.
[0082]
(3) Gas resistance test An ozone exposure test was performed using an ozone test apparatus (trade name: ozone weatherometer manufactured by Suga Test Instruments Co., Ltd.).
Test condition;
Exposure gas composition: O ₃ 3ppm
Test time: 6 hours Temperature and humidity conditions in test layer: 45 ° C, 55% RH
Gas resistance evaluation;
The residual concentration data after the ozone exposure test was evaluated using the same evaluation criteria as in the above evaluation (1). Table 2 shows the results.
[0083]
4) Yellowing test (test method and evaluation method)
To an unprinted recording medium, each of the image fastness improvers of Examples 1 to 6 and the compounds of Comparative Examples 1 and 2 was applied in the same manner as described above, and rubbed to give Examples 1 to 6, A sample of Comparative Example 2 was prepared, an untreated sample as Comparative Example 1 was added, each sample was allowed to stand in the following environment, and the color of the recording surface before and after the test was compared. The results are shown in Table 2.
Test condition;
Test layer temperature and humidity conditions: 50 ° C, 80% RH
Testing time: 240 hours
[Table 2]

[0085]
{Circle around (5)} The glossiness test was performed by newly applying each of Examples 1 and 6 to the recording medium on which no printing was performed in the same manner as described above, and rubbing the sample to prepare a sample. Processing samples were prepared. The glossiness of each of these three samples after storage at room temperature for 24 hours was measured by the method specified in JIS-Z-8741. Table 3 shows the results.
[0086]
[Table 3]

[0087]
The recorded matter (100% solid patch) of Examples 1 and 6 and the recorded matter of Comparative Example 1 (100% solid patch) were newly prepared in the same manner as the sample used in (1), and stored at room temperature for 24 hours. The density of each image was measured with Gretag Spectroino (Gretag Macbeth). Table 4 shows the results.
[0088]
[Table 4]

[0089]
【The invention's effect】
According to the present invention, the robustness of an ink-jet recorded image is improved, and in particular, even when the ink-jet recorded image is used for display in a normal indoor environment such as a home or office, image fading can be dramatically prevented. . Further, the present invention can improve the image fastness without deteriorating the recording quality of the recorded image.
is there.
[Brief description of the drawings]
FIG. 1 is a schematic sectional view schematically showing a sectional structure of a recording medium used in the present invention.
FIG. 2 is a schematic explanatory view of a method for improving image fastness according to the present invention, and is a schematic sectional view showing a state in which a gap in an ink receiving layer is filled with an improving agent.
FIG. 3 is an explanatory diagram of the behavior of water molecules in the ink receiving layer when a support having a dense porous layer on the surface on the ink receiving layer side is used as a support of the recording medium.
FIG. 4 is an embodiment of an applicator according to the present invention. (A) is a schematic perspective view showing a form at the time of use, and (b) is a schematic perspective view showing a form suitable for storage and carrying, in which an application unit is protected by a lid.
FIG. 5 is a schematic sectional view of an atomizer according to the present invention.
FIG. 6 is a schematic sectional view of an ink jet recording apparatus according to the present invention.
[Explanation of symbols]
1000 Support 1001 Image fastness improver 1003 Ink receiving layer 1005 Fine particles 1007 Binder 1009 Colorant 1011 Gap in ink receiving layer 1301 Porous layer 4001 Image fastness improver storage section 4002 Image fastness improver application section 4003 Lid 5001 Dispensing means (spray part)
5003 Image fastness improver storage

Claims (12)

A monovalent saturated fatty acid of a polybasic acid having a molecular weight of 300 or more, comprising an ink receiving layer having a porous structure, and an image fastness improver for a recorded matter in which an image is formed on the ink receiving layer by a coloring material. An image fastness improver comprising mainly an aliphatic alcohol ester compound. The image fastness improver according to claim 1, wherein the ester compound is a partially esterified product of a polybasic acid and a monovalent saturated aliphatic alcohol. The polybasic acid monovalent saturated aliphatic alcohol ester compound is a polybasic acid which is an aliphatic alkyl polybasic acid having 3 to 18 carbon atoms or an aromatic polybasic acid; The image fastness improver according to claim 2, which is an ester compound with an aliphatic alcohol. The image fastness improver according to any one of claims 1 to 3, wherein the image fastness improver further contains at least one of an antioxidant and an ultraviolet absorber. The image fastness improver according to any one of claims 1 to 4, wherein the content of the ester compound is 50% or more. The image according to any one of claims 1 to 5, which is a recorded matter including an ink receiving layer having a porous structure, and the ink receiving layer has a region where an image is formed by a coloring material, and the region has an image formed thereon. A recorded matter, which is provided with a fastness improver. An image fastness improver according to any one of claims 1 to 5, wherein all or substantially all of the holes existing in the thickness direction of the ink receiving layer in at least a part of the region are filled. The recorded matter according to claim 6, wherein 6. A method for improving the image fastness of a recorded matter comprising an ink receiving layer having a porous structure, and wherein the ink receiving layer has an area where an image is formed by a coloring material, wherein the area comprises: A method for improving image fastness, which comprises adding the image fastness improver according to any one of the above. 9. The image fastness improvement according to claim 8, wherein all or substantially all of the holes existing in the thickness direction of the ink receiving layer in at least a part of the region are filled with the image fastness improver. Method. A method for producing a recorded matter comprising an ink receiving layer having a porous structure, and wherein the ink receiving layer has a region where an image is formed by a coloring material,
(I) applying ink to the ink receiving layer to obtain a region where an image is formed by a coloring material contained in the ink;
(Ii) a step of applying the image fastness improver according to any one of claims 1 to 5 to the ink receiving layer;
A method for producing a recorded matter, comprising: (Iii) further comprising a step of filling all or substantially all of the holes distributed in the thickness direction of the ink receiving layer with the image fastness improving agent in a region where the image is formed. The method for producing a recorded matter according to item 1. An image fastness improving kit comprising a recording medium having an ink receiving layer having a porous chamber structure and the image fastness improving agent according to any one of claims 1 to 5.

Images