JP2004002373A - Maleimide derivatives and their polymers - Google Patents

Abstract

【選択図】　なしA polymer having a liquid crystal group in a side chain is used for an optically anisotropic film, a liquid crystal alignment film, an optical recording material, and the like. Conventionally, a polymer of a liquid crystalline acrylate has been used for such an application, but this polymer has problems in heat resistance, mechanical strength, and the like.
A maleimide derivative represented by the formula (1). Examples of R ¹ include hydrogen, fluorine, chlorine, —NCO, —CF ₃ , —CF ₂ H, —OCF ₃ , —OCF ₂ H, and alkyl or alkoxy having 1 to 12 carbon atoms. Examples of A ^{1 to} A ³ include 1,4-cyclohexylene and 1,4-cyclohexenylene in which arbitrary hydrogen may be replaced by fluorine, and 1,4 in which arbitrary hydrogen may be replaced by halogen. -Phenylene and the like. Examples of Z ¹ to Z ² is a single _{bond, -COO -, - OOC -,} - CF 2 O -, - OCF 2 -, - CH 2 O -, - OCH 2 -, - CH 2 CH 2 -, - C≡C- and the like. m is 1 or 0, and n is an integer of 1 to 20.

[Selection diagram] None

Description

【０００４】
【課題を解決するための手段】
本発明者は、上記の問題を根本的に解決すべく鋭意検討した結果、特定のマレイミド誘導体から得られる重合体が、上記の従来の重合体に比べ、耐熱性、耐光性、硬度、透明性、配向性および基板への塗布性などのいくつかにおいて改良された物性を有することを見いだし、この知見に基づいて本発明を完成した。本発明は下記の構成を有する。なお、本発明において、化学式中に存在する複数の同じ種類の基のうちから、不特定の基を選択する場合に用いる用語「任意の」は、その基の位置だけでなく、個数についても任意であることを示す。
【０００５】
［１］式（１）で表されるマレイミド誘導体。

式（１）において、Ｒ^１は水素、ハロゲン、−ＣＮ、−ＣＦ_３、−ＣＦ_２Ｈ、−ＣＦＨ_２、−ＯＣＦ_３、−ＯＣＦ_２Ｈ、−ＮＣＯ、−ＮＣＳまたは炭素数１〜２０のアルキルであり、このアルキル中の任意の−ＣＨ_２−は、−Ｏ−、−Ｓ−、−ＣＯＯ−、−ＯＣＯ−、−ＣＯ−、−ＣＨ＝ＣＨ−または−Ｃ≡Ｃ−で置き換えられてもよく、このアルキル中の任意の水素はハロゲンまたは−ＣＮで置き換えられてもよい；Ｒ^２およびＲ^３は独立して水素、フェニルまたは炭素数１〜２０のアルキルであり、このアルキル中の任意の−ＣＨ_２−は、−Ｏ−、−Ｓ−、−ＣＯＯ−、−ＯＣＯ−、−ＣＯ−、−ＣＨ＝ＣＨ−、または−Ｃ≡Ｃ−で置き換えられてもよく、このアルキル中の任意の水素はハロゲンまたは−ＣＮで置き換えられてもよく、そしてＲ^２およびＲ^３が共にアルキルの場合には、アルキルの末端が結合して環を形成してもよい；Ａ^１、Ａ^２およびＡ^３は独立して、１，４−シクロへキシレン、少なくとも１つの水素がフッ素で置き換えられた１，４−シクロへキシレン、１，４−シクロヘキセニレン、１，４−フェニレン、少なくとも１つの水素がハロゲン、メチルまたはトリフルオロメチルで置き換えられた１，４−フェニレン、ピリジン−２，５−ジイル、ピリダジン−３，６−ジイル、ピリミジン−２，５−ジイル、ナフタレン−２，６−ジイル、１，２，３，４−テトラヒドロナフタレン−２，６−ジイル、５，６，７，８−テトラヒドロナフタレン−２，６−ジイル、フルオレン−２，７−ジイル、９−メチル−フルオレン−２，７−ジイルまたは１，３−ジオキサン−２，５−ジイルである；Ｚ^１およびＺ^２は独立して単結合または炭素数１〜２０のアルキレンであり、このアルキレン中の任意の−ＣＨ_２−は、−Ｏ−、−ＣＯＯ−、−ＯＣＯ−、−ＣＨ＝ＣＨ−、−ＣＦ＝ＣＦ−、−ＣＦ_２Ｏ−、−ＯＣＦ_２−または−Ｃ≡Ｃ−で置き換えられてもよく、このアルキレン中の任意の水素はハロゲンで置き換えられてもよい；ｍは１または０であり、ｎは１〜２０の整数である。但し、ｍが０であり、Ａ^１およびＡ^２が１，４−フェニレンであり、そしてＺ^１が単結合であるとき、Ｒ^１は−ＣＮではない。
【０００６】
［２］式（１）において、Ｒ^１は水素、フッ素、塩素、−ＮＣＯまたは炭素数１〜２０のアルキルであり、このアルキル中の任意の−ＣＨ_２−は、−Ｏ−、−Ｓ−、−ＣＯＯ−、−ＯＣＯ−または−ＣＯ−で置き換えられてもよく、このアルキル中の任意の水素はハロゲンで置き換えられてもよく；Ｒ^２およびＲ^３は独立して水素、フェニルまたは炭素数１〜４のアルキルであり、Ｒ^２およびＲ^３が共にアルキルの場合には、アルキルの末端が結合して環を形成してもよく；Ａ^１、Ａ^２およびＡ^３は、独立して、１，４−シクロへキシレン、少なくとも１つの水素がフッ素で置き換えられた１，４−シクロへキシレン、１，４−シクロヘキセニレン、１，４−フェニレン、少なくとも１つの水素がハロゲン、メチルまたはトリフルオロメチルで置き換えられた１，４−フェニレン、ピリジン−２，５−ジイル、ピリダジン−３，６−ジイル、ピリミジン−２，５−ジイル、ナフタレン−２，６−ジイル、１，２，３，４−テトラヒドロナフタレン−２，６−ジイル、５，６，７，８−テトラヒドロナフタレン−２，６−ジイル、フルオレン−２，７−ジイル、９−メチル−フルオレン−２，７−ジイルまたは１，３−ジオキサン−２，５−ジイルであり；Ｚ^１およびＺ^２は独立して、単結合、−ＣＯＯ−、−ＯＣＯ−、−ＣＦ_２Ｏ−、−ＯＣＦ_２−、−ＣＨ_２Ｏ−、−ＯＣＨ_２−、−ＣＨ＝ＣＨ−、−ＣＨ_２ＣＨ_２−または−Ｃ≡Ｃ−であり；ｍは１または０であり、そしてｎは１〜２０の整数である、［１］項に記載のマレイミド誘導体。
【０００７】
［３］ｍが０である、［１］または［２］項に記載のマレイミド誘導体。
【０００８】
［４］ｍが１である、［１］または［２］項に記載のマレイミド誘導体。
【０００９】
［５］少なくとも２つの重合性化合物を含有し、その少なくとも１つが［１］項に記載のマレイミド誘導体である重合性組成物。
【００１０】
［６］重合性化合物のすべてが［１］項に記載のマレイミド誘導体である、［５］項に記載の重合性組成物。
【００１１】
［７］［１］項に記載のマレイミド誘導体の少なくとも１つと、これ以外の重合性化合物の少なくとも１つとを含有する、［５］項に記載の重合性組成物。
【００１２】
［８］式（２）で表される構成単位を有する重合体。

式（２）において、Ｒ^１は水素、ハロゲン、−ＣＮ、−ＣＦ_３、−ＣＦ_２Ｈ、−ＣＦＨ_２、−ＯＣＦ_３、−ＯＣＦ_２Ｈ、−ＮＣＯ、−ＮＣＳまたは炭素数１〜２０のアルキルであり、このアルキル中の任意の−ＣＨ_２−は、−Ｏ−、−Ｓ−、−ＣＯＯ−、−ＯＣＯ−、−ＣＯ−、−ＣＨ＝ＣＨ−または−Ｃ≡Ｃ−で置き換えられてもよく、このアルキル中の任意の水素はハロゲンまたは−ＣＮで置き換えられてもよい；Ｒ^２およびＲ^３は独立して水素、フェニルまたは炭素数１〜２０のアルキルであり、このアルキル中の任意の−ＣＨ_２−は、−Ｏ−、−Ｓ−、−ＣＯＯ−、−ＯＣＯ−、−ＣＯ−、−ＣＨ＝ＣＨ−または−Ｃ≡Ｃ−で置き換えられてもよく、このアルキル中の任意の水素はハロゲンまたは−ＣＮで置き換えられてもよく、そしてＲ^２およびＲ^３が共にアルキルの場合には、アルキルの末端が結合して環を形成してもよい；Ａ^１、Ａ^２およびＡ^３は独立して、１，４−シクロへキシレン、少なくとも１つの水素がフッ素で置き換えられた１，４−シクロへキシレン、１，４−シクロヘキセニレン、１，４−フェニレン、少なくとも１つの水素がハロゲン、メチルまたはトリフルオロメチルで置き換えられた１，４−フェニレン、ピリジン−２，５−ジイル、ピリダジン−３，６−ジイル、ピリミジン−２，５−ジイル、ナフタレン−２，６−ジイル、１，２，３，４−テトラヒドロナフタレン−２，６−ジイル、５，６，７，８−テトラヒドロナフタレン−２，６−ジイル、フルオレン−２，７−ジイル、９−メチル−フルオレン−２，７−ジイルまたは１，３−ジオキサン−２，５−ジイルである；Ｚ^１およびＺ^２は独立して、単結合または炭素数１〜２０のアルキレンであり、このアルキレン中の任意の−ＣＨ_２−は、−Ｏ−、−ＣＯＯ−、−ＯＣＯ−、−ＣＨ＝ＣＨ−、−ＣＦ＝ＣＦ−、−ＣＦ_２Ｏ−、−ＯＣＦ_２−または−Ｃ≡Ｃ−で置き換えられてもよく、このアルキレン中の任意の水素はハロゲンで置き換えられてもよい；ｍは１または０であり、そしてｎは１〜２０の整数である。但し、ｍが０であり、Ａ^１およびＡ^２が１，４−フェニレンであり、そしてＺ^１が単結合である場合には、Ｒ^１は−ＣＮではない。
【００１３】
［９］式（２）において、Ｒ^１は水素、フッ素、塩素、−ＮＣＯ、または炭素数１〜２０のアルキルであり、このアルキル中の任意の−ＣＨ_２−は−Ｏ−、−Ｓ−、−ＣＯＯ−、−ＯＣＯ−または−ＣＯ−で置き換えられてもよく、このアルキル中の任意の水素はハロゲンで置き換えられてもよく；Ｒ^２およびＲ^３は独立して水素、フェニルまたは炭素数１〜４のアルキルであり、Ｒ^２およびＲ^３が共にアルキルの場合には、アルキルの末端が結合して環を形成してもよく；Ａ^１、Ａ^２およびＡ^３は独立して、１，４−シクロへキシレン、少なくとも１つの水素がフッ素で置き換えられた１，４−シクロへキシレン、１，４−シクロヘキセニレン、１，４−フェニレン、少なくとも１つの水素がハロゲン、メチルまたはトリフルオロメチルで置き換えられた１，４−フェニレン、ピリジン−２，５−ジイル、ピリダジン−３，６−ジイル、ピリミジン−２，５−ジイル、ナフタレン−２，６−ジイル、１，２，３，４−テトラヒドロナフタレン−２，６−ジイル、５，６，７，８−テトラヒドロナフタレン−２，６−ジイル、フルオレン−２，７−ジイル、９−メチル−フルオレン−２，７−ジイルまたは１，３−ジオキサン−２，５−ジイルであり；Ｚ^１およびＺ^２は独立して、単結合、−ＣＯＯ−、−ＯＣＯ−、−ＣＦ_２Ｏ−、−ＯＣＦ_２−、−ＣＨ_２Ｏ−、−ＯＣＨ_２−、−ＣＨ＝ＣＨ−、−ＣＨ_２ＣＨ_２−または−Ｃ≡Ｃ−であり；ｍは１または０であり、そしてｎは１〜２０の整数である、［８］項に記載の重合体。
【００１４】
［１０］［１］項に記載のマレイミド誘導体の１つを単独重合させて得られる、［８］項に記載の重合体。
【００１５】
［１１］［６］項に記載の重合性組成物から得られる、［８］項に記載の重合体。
【００１６】
［１２］［７］項に記載の重合性組成物から得られる、［８］項に記載の重合体。
【００１７】
［１３］［８］〜［１２］のいずれか１項に記載の重合体を含有する光学補償膜。
【００１８】
［１４］［８］〜［１２］のいずれか１項に記載の重合体を含有する光書き込み記録材料。
【００１９】
［１５］［８］〜［１２］のいずれか１項に記載の重合体を含有する液晶配向膜。
【００２０】
【発明の実施の形態】
以下の説明においては、式（１）で表される本発明のマレイミド誘導体を、化合物（１）で表記することがある。式（２）で表される構成単位を、構成単位（２）で表記することがある。構成単位（２）を有する本発明の重合体を、重合体（２）で表記することがある。そして、下記の基を液晶骨格（１）と称することがある。

【００２１】
化合物（１）および重合体（２）は次の特徴を有する。
（ｉ）化合物（１）は、光や水分などに不安定な基であるアゾ、ジアゾ、アゾキシなどを含まない。
（ｉｉ）化合物（１）は、重合性のマレイミド基と立体的に大きな液晶骨格（１）との間にアルキレン鎖を有する。立体的な込み合いがないので、化合物（１）は高い重合反応性を有する。
（ｉｉｉ）化合物（１）の重合反応性が高いので高分子量の重合体が得られる。その結果、重合体（２）は高い耐熱性を有している。
（ｉｖ）液晶骨格（１）が主鎖から離れており、主鎖の立体的な拘束を受けにくいため、重合体（２）は液晶性を発現しやすい。その結果、重合体（２）は広い液晶相の温度範囲を有している。
（ｖ）化合物（１）が光に安定であるため、これから得られる重合体（２）も耐光性に優れている。
このように重合体（２）は、従来の液晶性アクリレートの重合体にはない優れた性能を有する。
【００２２】
まず、本発明のマレイミド誘導体について説明する。
本発明のマレイミド誘導体は、式（１）で表される。

この式中のＲ^１は、水素、ハロゲン、−ＣＮ、−ＣＦ_３、−ＣＦ_２Ｈ、−ＣＦＨ_２、−ＯＣＦ_３、−ＯＣＦ_２Ｈ、−ＮＣＯ、−ＮＣＳまたは炭素数１〜２０のアルキルである。このアルキルにおいて、任意の−ＣＨ_２−は、−Ｏ−、−Ｓ−、−ＣＯＯ−、−ＯＣＯ−、−ＣＯ−、−ＣＨ＝ＣＨ−または−Ｃ≡Ｃ−で置き換えられてもよく、任意の水素はハロゲンまたは−ＣＮで置き換えられてもよい。
【００２３】
Ｒ^１の好ましい例は、水素、フッ素、塩素、−ＮＣＯまたは炭素数１〜２０のアルキルである。このアルキルにおいて、任意の−ＣＨ_２−は−Ｏ−、−Ｓ−、−ＣＯＯ−、−ＯＣＯ−または−ＣＯ−で置き換えられてもよい。そして、このアルキル中の複数の−ＣＨ_２−が、−Ｏ−、−Ｓ−、−ＣＯＯ−、−ＯＣＯ−、および−ＣＯ−のうちのそれぞれ異なる基で置き換えられてもよい。その一例は、−Ｏ−ＣＨ_２ＣＨ_２−ＣＯＯ−である。しかしながら、連続している２つの−ＣＨ_２−が、−Ｏ−Ｏ−、−Ｏ−Ｓ−または−Ｓ−Ｓ−のように置き換えられることはない。そして、このアルキル中の任意の水素はハロゲンで置き換えられてもよい。ハロゲンは塩素またはフッ素であり、フッ素が好ましい。
【００２４】
Ｒ^１のさらに好ましい例は、水素、フッ素、塩素、−ＮＣＯ、炭素数１〜３のフッ素化アルキル、炭素数１〜３のフッ素化アルキルオキシ、炭素数１〜１２の直鎖のアルキル、および炭素数１〜１２の直鎖のアルコキシである。フッ素化アルキルおよびフッ素化アルキルオキシのうちで特に好ましい基は、−ＣＦ_３、−ＣＦ_２Ｈ、−ＯＣＦ_３および−ＯＣＦ_２Ｈである。アルキルおよびアルコキシのうちで特に好ましい基は、メチル、エチル、プロピル、ブチル、ペンチル、ヘキシル、ヘプチル、オクチル、ノニル、デシル、メトキシ、エトキシ、プロピルオキシ、ブチルオキシ、ペンチルオキシ、ヘキシルオキシ、ヘプチルオキシ、オクチルオキシ、ノニルオキシおよびデシルオキシである。液晶骨格（１）において、Ｒ^１が−ＣＦ_３、−ＯＣＦ_３、−ＮＣＯ、フッ素または塩素であるとき、重合体（２）の誘電率異方性値は正になり易い。
【００２５】
Ｒ^２およびＲ^３は独立して水素、フェニルまたは炭素数１〜２０のアルキルである。このアルキルにおいて、任意の−ＣＨ_２−は−Ｏ−、−Ｓ−、−ＣＯＯ−、−ＯＣＯ−、−ＣＯ−、−ＣＨ＝ＣＨ−または−Ｃ≡Ｃ−で置き換えられてもよく、任意の水素はハロゲンまたは−ＣＮで置き換えられてもよい。Ｒ^２またはＲ^３の好ましい例は、水素、フェニルまたは炭素数１〜４のアルキルである。そして、Ｒ^２およびＲ^３が共にアルキルの場合には、アルキルの末端が結合して環を形成してもよい。Ｒ^１およびＲ^２の特に好ましい例を、マレイミド環と共に次に示す。
【００２６】

【００２７】
式（１）中のＡ^１〜Ａ^３は環構造の２価基である。これらは独立して、１，４−シクロへキシレン、少なくとも１つの水素がフッ素で置き換えられた１，４−シクロへキシレン、１，４−シクロヘキセニレン、１，４−フェニレン、少なくとも１つの水素がハロゲン、メチルまたはトリフルオロメチルで置き換えられた１，４−フェニレン、ピリジン−２，５−ジイル、ピリダジン−３，６−ジイル、ピリミジン−２，５−ジイル、ナフタレン−２，６−ジイル、１，２，３，４−テトラヒドロナフタレン−２，６−ジイル、５，６，７，８−テトラヒドロナフタレン−２，６−ジイル、フルオレン−２，７−ジイル、９−メチル−フルオレン−２，７−ジイルまたは１，３−ジオキサン−２，５−ジイルである。Ａ^１、Ａ^２またはＡ^３の好ましい例を次に示す。
【００２８】

これらの式は、式（１）において左右逆向きに結合してもよい。
【００２９】
式（１）中のＺ^１およびＺ^２は結合基である。これらは独立して単結合または炭素数１〜２０のアルキレンであり、このアルキレン中の任意の−ＣＨ_２−は、−Ｏ−、−ＣＯＯ−、−ＯＣＯ−、−ＣＨ＝ＣＨ−、−ＣＦ＝ＣＦ−、−ＣＦ_２Ｏ−、−ＯＣＦ_２−または−Ｃ≡Ｃ−で置き換えられてもよく、このアルキレン中の任意の水素はハロゲンで置き換えられてもよい。Ｚ^１またはＺ^２の好ましい例は、単結合、−ＣＯＯ−、−ＯＣＯ−、−ＣＦ_２Ｏ−、−ＯＣＦ_２−、−ＣＨ_２Ｏ−、−ＯＣＨ_２−、−ＣＨ＝ＣＨ−、−ＣＨ_２ＣＨ_２−および−Ｃ≡Ｃ−である。Ｚ^１またはＺ^２のより好ましい例は、単結合、−ＣＯＯ−、−ＯＣＯ−、−Ｃ≡Ｃ−、−ＣＦ_２Ｏ−、−ＯＣＦ_２−、−ＣＨ_２Ｏ−、−ＯＣＨ_２−および−ＣＨ_２ＣＨ_２−である。
【００３０】
化合物（１）において、Ｚ^１およびＺ^２の少なくとも１つが、単結合、−ＣＯＯ−、−ＯＣＯ−または−Ｃ≡Ｃ−である場合には、屈折率異方性値の大きな重合体が得られる傾向がある。Ｚ^１およびＺ^２の少なくとも１つが、−ＣＦ_２Ｏ−、−ＯＣＦ_２−、−ＣＨ_２Ｏ−、−ＯＣＨ_２−または−ＣＨ_２ＣＨ_２−である場合には、液晶骨格（１）の柔軟性が増大するので、比較的低い粘性の重合体が得られる傾向がある。そして、ｍは１または０である。但し、ｍが０であり、Ａ^１およびＡ^２が１，４−フェニレンであり、そしてＺ^１が単結合であるとき、Ｒ^１は−ＣＮではない。即ち、本発明の化合物には、液晶骨格（１）がシアノビフェニルである化合物は含まれない。
【００３１】
Ａ^１〜Ａ^３とＺ^１〜Ｚ^２の組み合わせについて説明する。室温において重合体（２）が液晶相を有するためには、液晶骨格（１）においてｍが０であることが好ましい。即ち、次の（１−１）〜（１−１０）である。

これらの式中のＲ^１、Ａ^１およびＡ^２の意味は、前記の通りである。
【００３２】
ｍが１である液晶骨格（１）は３つの環を有する。３環の液晶骨格（１）を有する重合体は、液晶相の上限温度が一般的に高い。３環構造であるとき、Ａ^１〜Ａ^３とＺ^１〜Ｚ^２の好ましい組み合わせは次の通りである。

【００３３】

これらの式中のＲ^１、Ａ^１、Ａ^２およびＡ^３の意味は、前記の通りである。
【００３４】
化合物（１）が重合し易く、その重合によって得られる重合体が液晶相を有するためには、式（１）中のｎは１〜２０の整数であることが好ましい。より好ましいｎは３〜１１である。そして、化合物（１）が１，４−シクロへキシレンまたは１，３−ジオキサン−２，５−ジイルを有する場合には、その立体配置はシス型よりトランス型が好ましい。化合物（１）は、^２Ｈ（重水素）または^１３Ｃなどの同位体元素を自然に存在する割合より多く含んでもよく、その場合でも化合物の物性に大きな差異はない。
【００３５】
次に、化合物（１）の製造方法について説明する。
化合物（１）は、Ｒ^２およびＲ^３が水素の場合には、次のスキームに従って製造することができる。

【００３６】
マレイミドとフランとのＤｉｅｌｓ−Ａｌｄｅｒ反応によって、先ずマレイミドのフラン付加体（ａ）を製造する。液晶骨格（１）を有し末端がヒドロキシル基である化合物とω−ブロモアルカノールとを、塩基を用いてエーテル化することにより、アルコール誘導体（ｂ）を製造する。塩基の例は、水酸化カリウム、水酸化ナトリウム、炭酸カリウム、水素化ナトリウムなどである。マレイミドのフラン付加体（ａ）とアルコール誘導体（ｂ）を光延反応によりＮ−アルキル化した後、ｒｅｔｒｏ−Ｄｉｅｌｓ−Ａｌｄｅｒ反応により熱分解して、化合物（１）を製造する。
【００３７】
Ｒ^２およびＲ^３が独立してフェニルまたは炭素数１〜４のアルキルである場合には、酸無水物（ｃ）とアミノアルコールから製造することができる。Ｒ^２およびＲ^３が共にアルキルであって、アルキルの末端が結合して環を形成した場合についても同様である。

【００３８】
この他、出発物質に目的の末端基、環および結合基を導入する方法は、ホーベン−ワイル（Ｈｏｕｂｅｎ−Ｗｙｌｅ，　Ｍｅｔｈｏｄｓ　ｏｆ　Ｏｒｇａｎｉｃ　Ｃｈｅｍｉｓｔｒｙ，　Ｇｅｏｒｇ　Ｔｈｉｅｍｅ　Ｖｅｒｌａｇ，　Ｓｔｕｔｔｇａｒｔ）、オーガニック・シンセシーズ（Ｏｒｇａｎｉｃ　Ｓｙｎｔｈｅｓｅｓ，　Ｊｏｈｎ　Ｗｉｌｅｙ　＆　Ｓｏｎｓ，　Ｉｎｃ．）、オーガニック・リアクションズ（Ｏｒｇａｎｉｃ　Ｒｅａｃｔｉｏｎｓ，　ＪｏｈｎＷｉｌｅｙ　＆　Ｓｏｎｓ　Ｉｎｃ．）、コンプリヘンシブ・オーガニック・シンセシス（Ｃｏｍｐｒｅｈｅｎｓｉｖｅ　Ｏｒｇａｎｉｃ　Ｓｙｎｔｈｅｓｉｓ，　Ｐｅｒｇａｍｏｎ　Ｐｒｅｓｓ）、新実験化学講座（丸善）などに記載されている。
【００３９】
結合基Ｚ_１またはＺ_２を生成する方法の一例に関して、最初にスキームを示し、次に項（Ｉ）〜項（ＶＩＩ）でスキームを説明する。これらのスキームにおいて、ＭＳＧ^１およびＭＳＧ^２はどちらも、少なくとも１つの環を有する１価の有機基である。スキームに示されている複数のＭＳＧ^１（またはＭＳＧ^２）は、同一であってもよいし、異なってもよい。
【００４０】

【００４１】

【００４２】

【００４３】
（Ｉ）単結合の生成
アリールホウ酸（２１）と公知の方法で合成される化合物（２２）とを、炭酸塩水溶液とテトラキス（トリフェニルホスフィン）パラジウムのような触媒の存在下で反応させて化合物（１Ａ）を合成する。この化合物（１Ａ）は、公知の方法で合成される化合物（２３）にｎ−ブチルリチウムを、次いで塩化亜鉛を反応させ、ジクロロビス（トリフェニルホスフィン）パラジウムのような触媒の存在下で化合物（２２）を反応させることによっても合成される。
【００４４】
（ＩＩ）−ＣＯＯ−と−ＯＣＯ−の生成
化合物（２３）にｎ−ブチルリチウムを、続いて二酸化炭素を反応させてカルボン酸（２４）を得る。化合物（２４）と、公知の方法で合成されるフェノール（２５）とをＤＤＣ（１，３−ジシクロヘキシルカルボジイミド）とＤＭＡＰ（４−ジメチルアミノピリジン）の存在下で脱水させて−ＣＯＯ−を有する化合物（１Ｂ）を合成する。この方法によって、−ＯＣＯ−を有する化合物も合成できる。
【００４５】
（ＩＩＩ）−ＣＦ_２Ｏ−と−ＯＣＦ_２−の生成
化合物（１Ｂ）をローソン試薬のような硫黄化剤で処理して化合物（２６）を得る。化合物（２６）をフッ化水素ピリジン錯体とＮＢＳ（Ｎ−ブロモスクシンイミド）でフッ素化し、−ＣＦ_２Ｏ−を有する化合物（１Ｃ）を合成する。Ｍ．　Ｋｕｒｏｂｏｓｈｉ　ｅｔ　ａｌ．，　Ｃｈｅｍ．　Ｌｅｔｔ．，　１９９２，８２７．を参照。化合物（１Ｃ）は化合物（２６）を（ジエチルアミノ）サルファ　トリフルオリドでフッ素化しても合成される。Ｗｉｌｌｉａｍ　Ｈ．　Ｂｕｎｎｅｌｌｅ　ｅｔ　ａｌ．，　Ｊ．　Ｏｒｇ．　Ｃｈｅｍ．　１９９０，　５５，　７６８．を参照。この方法によって、−ＯＣＦ_２−を有する化合物も合成できる。
【００４６】
（ＩＶ）−ＣＨ＝ＣＨ−の生成
化合物（２３）をｎ−ブチルリチウムで処理した後、Ｎ，Ｎ−ジメチルホルムアミドなどのホルムアミドと反応させてアルデヒド（２８）を得る。公知の方法で合成されるホスホニウム塩（２７）をカリウムｔ−ブトキシドのような塩基で処理して発生させたリンイリドを、アルデヒド（２８）に反応させて化合物（１Ｄ）を合成する。反応条件によってはシス体が生成するので、必要に応じて公知の方法によりシス体をトランス体に異性化する。
【００４７】
（Ｖ）−ＣＨ_２ＣＨ_２−の生成
化合物（１Ｄ）をパラジウム炭素のような触媒の存在下で水素化することにより、化合物（１Ｅ）を合成する。
【００４８】
（ＶＩ）−Ｃ≡Ｃ−の生成
ジクロロパラジウムとハロゲン化銅との触媒存在下で、化合物（２３）に２−メチル−３−ブチン−２−オールを反応させたのち、塩基性条件下で脱保護して化合物（３０）を得る。ジクロロパラジウムとハロゲン化銅との触媒存在下、化合物（３０）を化合物（２２）と反応させて、化合物（１Ｇ）を合成する。
【００４９】
（ＶＩＩ）−ＣＨ_２Ｏ−または−ＯＣＨ_２−の生成
化合物（２８）を水素化ホウ素ナトリウムなどの還元剤で還元して化合物（３２）を得る。これを臭化水素酸などでハロゲン化して化合物（３３）を得る。炭酸カリウムなどの存在下で、化合物（３３）を化合物（２５）と反応させて化合物（１Ｊ）を合成する。
【００５０】
これらの方法により、Ｎｏ．１〜Ｎｏ．１４１の化合物を製造する。

【００５１】

【００５２】

【００５３】

【００５４】

【００５５】

【００５６】

【００５７】

【００５８】

【００５９】

【００６０】

【００６１】

【００６２】

【００６３】
次に、本発明の組成物について説明する。
本発明の組成物は、化合物（１）の少なくとも１つを含有し、これと共重合可能な化合物を含有してもよい重合性組成物である。即ち、含有される重合性化合物のすべてが化合物（１）である重合性組成物、または化合物（１）と化合物（１）以外の重合性化合物とを含有する重合性組成物である。以下の説明では、化合物（１）以外の重合性化合物を他のモノマーと称する。他のモノマーを使用する目的は、化合物（１）との共重合によって得られる共重合体に、皮膜形成性と機械的強度を付与することである。この目的が達成されること以外に、他のモノマーを選択するための条件はない。他のモノマーは、液晶性であっても、そうでなくてもよい。本発明の重合性組成物において、化合物（１）の好ましい含有量は、組成物全量に基づく割合で５〜１００モル％である。そして、この重合性組成物には、重合反応を行うに際し、必要に応じて溶剤や触媒を加えることができる。
【００６４】
次に、本発明の重合体について説明する。
化合物（１）の１つのみを重合させると単独重合体が得られる。重合性化合物として少なくとも２つの化合物（１）を含有する重合性組成物を重合させると、化合物（１）のみの共重合体が得られる。化合物（１）と他のモノマーとを含有する重合性組成物を重合させても共重合体が得られる。これらの単独重合体および共重合体は、どれも下記の構成単位（２）を有する。即ち、重合体（２）は、側鎖に液晶骨格（１）を有するため液晶相を有し易い。構成単位（２）中の記号の意味は、式（１）における場合と同じである。共重合体における構成単位（２）の配列は、ランダム、ブロック、交互、グラフトなどのいずれであってもよい。

【００６５】
重合体（２）は、化合物（１）の１つまたは重合性組成物を熱または光により重合させて製造する。熱重合の反応温度は０〜１５０℃、反応時間は１〜１００時間であり、通常ラジカル重合開始剤を用いる。ラジカル重合開始剤の例は、過酸化ベンゾイル、ジイソプロピルパーオキシジカーボネート、ｔ−ブチルパーオキシ−２−エチルヘキサノエート、ｔ−ブチルパーオキシピバレート、ｔ−ブチルパーオキシジイソブチレート、過酸化ラウロイル、２，２′−アゾビスイソ酪酸ジメチル（ＭＡＩＢ）、ジｔ−ブチルパーオキシド（ＤＴＢＰＯ）、アゾビスイソブチロニトリル（ＡＩＢＮ）、アゾビスシクロヘキサンカルボニトリル（ＡＣＮ）などである。
【００６６】
光または電子線等の照射による重合においては、通常光ラジカル重合開始剤を用いる。光ラジカル重合開始剤の例は、チバ・スペシャリティー・ケミカル（株）の製品のうちから、ダロキュアー１１７３（２−ヒドロキシ−２−メチル−１−フェニルプロパン−１−オン）、イルガキュアー１８４（１−ヒドロキシシクロヘキシルフェニルケトン）、イルガキュアー６５１（２，２−ジメトキシ−１，２−ジフェニルエタン−１−オン）、イルガキュアー５００、イルガキュアー２９５９、イルガキュアー９０７、イルガキュアー３６９、イルガキュアー１３００、イルガキュアー８１９、イルガキュアー１７００、イルガキュアー１８００、イルガキュアー１８５０、ダロキュアー４２６５、イルガキュアー７８４などが挙げられる。
【００６７】
光ラジカル重合開始剤のその他の例は、ｐ−メトキシフェニル−２，４−ビス（トリクロロメチル）トリアジン、２−（ｐ−ブトキシスチリル）−５−トリクロロメチル−１，３，４−オキサジアゾール、９−フェニルアクリジン、９，１０−ベンズフェナジン、ベンゾフェノン／ミヒラーズケトン混合物、ヘキサアリールビイミダゾール／メルカプトベンズイミダゾール混合物、１−（４−イソプロピルフェニル）−２−ヒドロキシ−２−メチルプロパン−１−オン、ベンジルジメチルケタール、２−メチル−１−［４−（メチルチオ）フェニル］−２−モルホリノプロパン−１−オン、２，４−ジエチルキサントン／ｐ−ジメチルアミノ安息香酸メチル混合物などである。
【００６８】
重合体（２）は、アニオン重合法、配位重合法、またはリビング重合法によっても製造することができる。これらの重合法で用いる好ましい開始剤は、ｎ−ブチルリチウム、ｓｅｃ−ブチルリチウム、ｔ−ブチルリチウム、ｔ−ブチルリチウム−トリアルキルアルミニウムなどのアルカリ金属アルキル、アルミニウム化合物、遷移金属化合物などである。
【００６９】
重合反応には溶剤を用いてもよい。好ましい溶剤は、ベンゼン、トルエン、キシレン、メシチレン、ペンタン、ヘキサン、ヘプタン、オクタン、ノナン、デカン、テトラヒドロフラン、１，４−ジオキサン、Ｎ−メチルピロリドン、ジメチルホルムアミド、ジメチルスルホキシドなどである。これらの少なくとも２つを混合した溶剤を用いてもよい。
【００７０】
次に、他のモノマーについて説明する。
他のモノマーのうち液晶性でない重合性化合物の例は、ビニル系単量体、フマル酸ジエステル、マレイミド誘導体などである。これらのうちでは、化合物（１）との共重合性に優れているので、マレイミド誘導体が好ましい。
【００７１】
化合物（１）ではないマレイミド誘導体のうち、非液晶性のマレイミド誘導体の例は、Ｎ−メチルマレイミド、Ｎ−エチルマレイミド、Ｎ−プロピルマレイミド、Ｎ−ブチルマレイミド、Ｎ−ペンチルマレイミド、Ｎ−ヘキシルマレイミド、Ｎ−ヘプチルマレイミド、Ｎ−オクチルマレイミド、Ｎ−ノニルマレイミド、Ｎ−デシルマレイミド、Ｎ−ウンデシルマレイミド、Ｎ−ドデシルマレイミド、Ｎ−オクタデシルマレイミド、Ｎ−イソプロピルマレイミド、Ｎ−（ｓｅｃ−ブチル）マレイミド、Ｎ−（ｔ−ブチル）マレイミド、Ｎ−（１−メチルブチル）マレイミド、Ｎ−（２−メチルブチル）マレイミド、Ｎ−（３−メチルブチル）マレイミド、Ｎ−（ｓｅｃ−ヘキシル）マレイミド、Ｎ−（４−メチル−２−ペンチル）マレイミド、Ｎ−（ｓｅｃ−ヘプチル）マレイミド、Ｎ−（ｓｅｃ−オクチル）マレイミド、Ｎ−シクロプロピルマレイミド、Ｎ−シクロブチルマレイミド、Ｎ−シクロペンチルマレイミド、Ｎ−シクロヘキシルマレイミド、Ｎ−フェニルマレイミド、Ｎ−（２−メチルフェニル）マレイミド、Ｎ−（２−エチルフェニル）マレイミド、Ｎ−（２−イソプロピルフェニル）マレイミド、Ｎ−（２，６−ジメチルフェニル）マレイミド、Ｎ−（２，６−ジエチルフェニル）マレイミド、Ｎ−（２，６−ジイソプロピルフェニル）マレイミド、Ｎ−（２，４，６−トリメチルフェニル）マレイミド、Ｎ−（２−クロロフェニル）マレイミド、Ｎ−（３−メチルフェニル）マレイミド、Ｎ−（３−エチルフェニル）マレイミド、Ｎ−（３−トリフルオロメチルフェニル）マレイミド、Ｎ−（３，５−ジメチルフェニル）マレイミド、Ｎ−ベンジルマレイミド、Ｎ−（４−メチルフェニル）マレイミド、Ｎ−（４−エチルフェニル）マレイミド、Ｎ−（４−プロピルフェニル）マレイミド、Ｎ−（４−イソプロピルフェニル）マレイミド、Ｎ−（４−ブチルフェニル）マレイミド、Ｎ−（４−ペンチルフェニル）マレイミド、Ｎ−トリフルオロメチルマレイミド、Ｎ−〔１−（トリフルオロメチル）エチル〕マレイミド、Ｎ−〔２−（トリフルオロメチル）エチル〕マレイミド、Ｎ−ヘキサフルオロイソプロピルマレイミド、Ｎ−パーフルオロイソプロピルマレイミド、Ｎ−パーフルオロブチルエチルマレイミド、Ｎ−パーフルオロオクチルエチルマレイミド、Ｎ−（２−クロロエチル）マレイミド、Ｎ−（１−ブトキシ−２−プロピル）マレイミド、Ｎ−（メトキシエチル）マレイミド、Ｎ−（トリメチルシリル）マレイミド、Ｎ−（ｔ−ブチルジメチルシリル）マレイミド、Ｎ−（ジメチルトキシシリル）マレイミド、（Ｎ−（２−シアノエチル）マレイミド、Ｎ−（２−ヒドロキシエチル）マレイミド、Ｎ−（３−ヒドロキシプロピル）マレイミド、Ｎ−（４−ヒドロキシブチル）マレイミド、Ｎ−（５−ヒドロキシペンチル）マレイミド、Ｎ−（６−ヒドロキシヘキシル）マレイミド、Ｎ−（７−ヒドロキシヘプチル）マレイミド、Ｎ−（８−ヒドロキシオクチル）マレイミド、Ｎ−（９−ヒドロキシノニル）マレイミド、Ｎ−（１０−ヒドロキシデシル）マレイミドなどである。
【００７２】
光学活性なマレイミド誘導体（ＯＰＭ−１）〜（ＯＰＭ−５）も、化合物（１）の共重合相手として用いることができる。

【００７３】
ビニル系単量体は、重合体（２）に皮膜形成性または透明性を付与することを目的に用いられる。ビニル系単量体を選択するための条件は、この目的を達成できることのみである。好ましいビニル系単量体は、オレフィン、ハロゲン化ビニル、カルボン酸ビニル、芳香族ビニル系単量体、スチレン誘導体、ビニルエーテル、アルキルビニルケトン、ジエン、（メタ）アクリレート、イタコネート、α、β−ビニルナフタレン、Ｎ−ビニルアセトアミドなどである。オレフィンの例は、エチレン、プロピレン、イソブテンなどである。ハロゲン化ビニルの例は、塩化ビニル、フッ化ビニルなどである。カルボン酸ビニルの例は、酢酸ビニル、ピバリン酸ビニル、２，２−ジメチルブタン酸ビニル、２，２−ジメチルペンタン酸ビニル、２−メチル−２−ブタン酸ビニル、プロピオン酸ビニル、ステアリン酸ビニル、２−エチル−２−メチルブタン酸ビニルなどである。芳香族ビニル系単量体の例は、ｐ−ｔ−ブチル安息香酸ビニル、Ｎ，Ｎ−ジメチルアミノ安息香酸ビニル、安息香酸ビニルなどである。スチレン誘導体の例は、スチレン、ｏ−クロロスチレン、ｍ−クロロスチレン、ｐ−クロロスチレン、ｏ−クロロメチルスチレン、ｍ−クロロメチルスチレン、ｐ−クロロメチルスチレン、α−メチルスチレンなどである。
【００７４】
ビニルエーテルの例は、エチルビニルエーテル、ヒドロキシブチルモノビニルエーテル、ｔ−アミルビニルエーテル、シクロヘキサンジメタノールメチルビニルエーテルなどである。アルキルビニルケトンの例は、メチルビニルケトン、イソブチルビニルケトンなどである。ジエンの例は、ブタジエン、イソプレンなどである。（メタ）アクリレートの例は、メチル（メタ）アクリレート、エチル（メタ）アクリレート、ブチル（メタ）アクリレート、２−エチルヘキシル（メタ）アクリレート、フェニル（メタ）アクリレートなどである。イタコネートの例は、ジメチルイタコネート、ジエチルイタコネート、ジブチルイタコネート、ジイソプロピルイタコネートなどである。なお、（メタ）アクリレートは、アクリレートおよびメタクリレートの総称である。
【００７５】
フマル酸ジエステルの例は、フマル酸ジエチル、フマル酸ジイソプロピル、フマル酸ジブチル、フマル酸ジシクロヘキシル、フマル酸ジ（１−フェニル−２−プロピル）、フマル酸ジｓｅｃ−ブチル、フマル酸ジｔ−ブチル、フマル酸ジ２−エチルヘキシル、フマル酸イソプロピル＝エチル、フマル酸イソプロピル＝プロピル、フマル酸イソプロピル＝ブチル、フマル酸イソプロピル＝ｓｅｃ−ブチル、フマル酸イソプロピル＝ｔ−ブチル、フマル酸イソプロピル＝イソアミル、フマル酸イソプロピル＝ｓｅｃ−アミル、フマル酸イソプロピル＝ｓｅｃ−ヘキシル、フマル酸イソプロピル＝４−メチル−２−ペンチル、フマル酸イソプロピル＝２−エチルヘキシル、フマル酸イソプロピル＝オクチル、フマル酸イソプロピル＝シクロヘキシル、フマル酸イソプロピル＝ノニル、フマル酸ｔ−ブチル＝ｓｅｃ−ブチル、フマル酸ｔ−ブチル＝シクロヘキシル、フマル酸ｔ−ブチル＝４−メチル−２−ペンチル、フマル酸ｔ−ブチル＝２−エチルヘキシル、フマル酸イソプロピル＝シクロヘキシル、フマル酸イソプロピル＝シクロペンチル、フマル酸イソプロピル＝２−フェニル−１−エチル、フマル酸イソプロピル＝３−フェニルプロピル、フマル酸イソプロピル＝１−フェニル−２−プロピル、フマル酸イソプロピル＝１−フェニル−１−プロピル、フマル酸イソプロピル＝（トリメチルシリル）プロピル、フマル酸ｔ−ブチル＝（トリメチルシリル）プロピル、フマル酸シクロヘキシル＝（トリメチルシリル）プロピル、フマル酸イソプロピル＝［３−トリス（トリメチルシロキシ）シリル］プロピル、フマル酸イソプロピル＝３−（ペンタメチルジシロキサニル）プロピル、フマル酸Ｎ、Ｎ−ジメチルアミノエチル＝イソプロピル、フマル酸ｔ−ブチル＝１−ブトキシ−２−プロピル、フマル酸２−シアノエチル＝イソプロピル、フマル酸２−ヒドロキシエチル＝イソプロピル、フマル酸グリシジル＝イソプロピル、フマル酸イソプロピル＝ジエチルホスフォメチル、フマル酸２−メチルチオエチル＝イソプロピル、フマル酸イソプロピル＝２−ヒドロキシエチルチオエチル＝イソプロピル、フマル酸パーフルオロオクチルエチル＝イソプロピル、フマル酸トリフルオロメチル＝イソプロピル、フマル酸ペンタフルオロエチル＝イソプロピル、フマル酸ヘキサフルオロイソプロピル＝イソプロピルなどである。
【００７６】
重合体の被膜形成能をより高めるために、多官能アクリレートを添加することもできる。好ましい多官能アクリレートは、１，４−ブタンジオールジアクリレート、１，６−ヘキサンジオールジアクリレート、１，９−ノナンジオールジアクリレート、ネオペンチルグリコールジアクリレート、トリエチレングリコールジアクリレート、ジプロピレングリコールジアクリレート、トリプロピレングリコールジアクリレート、テトラエチレングリコールジアクリレート、トリメチロールプロパントリアクリレート、トリメチロールＥＯ付加トリアクリレート、ペンタエリストールトリアクリレート、トリスアクリロイルオキシエチルフォスフェート、ビスフェノールＡ　ＥＯ付加ジアクリレート、ビスフェノールＡグリジジルエーテルジアクリレート、ポリエチレングリコールジアクリレートなどである。ビスフェノールＡグリジジルエーテルジアクリレートは、大阪有機化学（株）からビスコート７００として市販されている。
【００７７】
これらの液晶性でない他のモノマーを２つ以上用いるときには、同じ種類から２つ以上を選択してもよいし、異なる種類からそれぞれ少なくとも１つを選択してもよい。これらのモノマーの好ましい添加量は、化合物（１）に対する割合で０．５〜５０モル％である。十分な被膜形成力を得るための好ましい割合は、０．５モル％以上である。重合性組成物が液晶性を有するための好ましい割合は、５０モル以下である。
【００７８】
他のモノマーとして、液晶性の骨格を有する重合性化合物を用いてもよい。この重合性化合物の例は、アクリル酸誘導体（ＬＣ−１）、フマル酸誘導体（ＬＣ−２）、ソルビン酸誘導体（ＬＣ−３）、マレイミド誘導体（ＬＣ−４）、クロトン酸誘導体（ＬＣ−５）などである。これらの重合性化合物を用いることにより、得られる重合体の液晶相の温度範囲を調節することができる。
【００７９】
（ＬＣ−１）の例を次に示す。

【００８０】
（ＬＣ−２）の例を次に示す。これらの式中において、Ｒ^２は炭素数１〜１５のアルキルであり、Ｒ^３はメチル、エチル、２−メチルブチル、プロピル、オクチル、イソプロピル、ｔ−ブチル、シクロヘキシル、４−ブチルシクロヘキシル、ノルボルニル、またはアダマンチルであり、ｙは１〜２０の整数である。

【００８１】
次に、（ＬＣ−３）〜（ＬＣ−５）の例を示す。これらの式におけるｙは、１〜２０の整数である。

【００８２】
これらの液晶性の骨格を有する他のモノマーを２つ以上用いるときには、同じ種類から選択してもよいし、異なる種類からそれぞれ少なくとも１つを選択してもよい。重合性組成物におけるこれらのモノマーの好ましい含有量は、組成物全量に基づいて０．５〜９５モル％である。液晶温度範囲の調整が可能であるために好ましい割合は、０．５モル％以上である。そして、共重合体が得られるために好ましい割合は、９５モル％以下である。
【００８３】
重合体（２）が単離される場合には、これを溶剤に溶かして成形することができる。このとき用いる好ましい溶剤は、Ｎ−メチル−２−ピロリドン、ジメチルスルホキシド、Ｎ，Ｎ−ジメチルアセトアミド、Ｎ，Ｎ−ジメチルホルムアミド、Ｎ，Ｎ−ジメチルアセトアミドジメチルアセタール、テトラヒドロフラン、クロロホルム、１，４−ジオキサン、ビス（メトキシエチル）エーテル、γ−ブチロラクトン、テトラメチル尿素、トリフルオロ酢酸、トリフルオロ酢酸エチル、ヘキサフルオロ−２−プロパノールなどである。しかし、使用可能な溶剤はこれらに制限されない。これらの溶剤と、アセトン、ベンゼン、トルエン、ヘプタン、塩化メチレンなどの一般的な有機溶剤との混合物も用いることができる。
【００８４】
重合体（２）は、液晶性を有するので、各種の保護膜、光学補償膜、光書き込み記録材料などへの応用が可能である。光学補償膜の例は位相差フィルムである。重合体（２）は光学異方性薄膜とすることができるので、これを単独で位相差フィルムとして用いるか、または他の位相差フィルムと組み合わせることができる。そしてこの位相差フィルムを、偏光板、円偏光板、楕円偏光板、色補償板、視覚補償板などに応用することができる。偏光板、円偏光板、楕円偏光板、色補償板、視覚補償板なども、光学補償膜の例である。化合物（１）から光重合により得られる重合体は、熱重合により得られる重合体と同様な用途の他、偏光を用いることによって、ラビングレスの配向膜に応用することができる。
【００８５】
液晶ディスプレーに用いられる位相差板は、重合体（２）を有機溶剤に溶解したものを、配向処理した透明基板に塗布し、これをガラス転移点以上の温度に加熱し、次いで放冷することにより、均一に配向した重合体の薄膜（光学異方性薄膜）を形成させて製造する。透明基板は、ガラス板または高分子フィルムである。高分子フィルムの例は、トリアセチルセルロース、ＪＳＲ（株）製の「アートン」、日本ゼオン（株）製の「ゼオネックス」および「ゼオノア」、三井化学（株）製の「アペル」などである。好ましい塗布方法は、マイクログラビアコート法、グラビアコート法、ワイヤーバーコード法、デップコート法、スプレーコート法、メニスカスコート法などである。
【００８６】
光学異方性薄膜の厚さは所望の位相差値により異なり、その位相差値は光学異方性薄膜の複屈折率により異なる。好ましい位相差値は大体０．０５〜５０μｍの範囲であり、より好ましい位相差値は大体０．１〜２０μｍの範囲である。そして、さらに好ましい位相差値は大体０．５〜１０μｍの範囲である。光学異方性薄膜のヘイズ値は、１．５％以下、より好ましくは１．０％以下であり、透過率で８０％以上、より好ましくは８５％以上である。可視光領域で透過率がこれらの割合を満たすことが好ましい。ヘイズ値の範囲１．５％以下は、偏光性能に問題を生じさせないために好ましい条件である。透過率の範囲８０％以上は、この光学異方性薄膜を液晶表示素子に用いるとき、明るさを維持するために好ましい条件である。
【００８７】
【実施例】
以下、実施例により本発明を詳細に説明する。実施例中に記載した相転移温度において、Ｃは結晶、Ｎはネマチック相、Ｃｈはコレステリック相、ＳｍＡはスメクチックＡ相、ＳｍＸは未同定のスメクチック相、Ｉは等方性液体、Ｔｍは重合体の融点を示す。重合体の重量平均分子量（Ｍｗ）、多分散度（Ｍｗ／Ｍｎ）は、ＧＰＣ（ゲル・パーミェーション・クロマトグラフィー）による測定値（排除限界１０００万のカラムを用い、分子量公知の標準ポリスチレンから換算）から算出した。なお、単位記号Ｌはリットル（ｌｉｔｅｒ）を示す。
【００８８】
実施例１
（１−１ａ）マレイミドのフラン付加体［ａ］の製造
マレイミド（２７５ｇ）をジエチルエーテル（３．５Ｌ）に溶解した溶液にフラン（１Ｌ）を加え４８時間還流した。この間、反応が進むに従って反応器の周りに結晶が析出してきた。還流を止めて、室温（２０℃）で１日静置すると結晶がさらに析出した。この結晶を濾過して、減圧下で乾燥することによりマレイミドのフラン付加体［ａ］（４３４ｇ）を得た。
融点：１３０〜１３２℃
（１−１ｂ）テトラヒドロフタルイミド−Ｎ−エチルアルコールの製造
テトラヒドロフタル酸２５ｇのトルエン５０ｍｌ溶液にエタノールアミン１０ｇを加え、還流しながらディーンスタークを用いて共沸して出てくる水を除いた。水が出てこなくなるまで還流したとところで反応を止め。全てのトルエン留去すると３０ｇのテトラヒドロフタルイミド−Ｎ−エチルアルコールが得られた。融点は７０℃であった。
【００８９】
（１−２）　液晶骨格（１）の製造
（ｉ）４−（トランス−４−ｎ−プロピルシクロヘキシル）フェノール（３０ｇ）、６−ブロモヘキサノール（２７．３ｇ）および炭酸カリウム（３９ｇ）をジメチルホルムアミド（３００ｍｌ）に加え、９０℃で３時間攪拌した。反応液を３Ｎの塩酸１Ｌに注ぎ込むことによって析出した白色の結晶を、濾過によって分取した。得られた結晶を水でよく洗浄した後乾燥して、４−（トランス−４−ｎ−プロピルシクロヘキシル）−（６−ヒドロキシヘキシルオキシ）ベンゼン（３２ｇ）を得た。その相転移温度はＣ　６１　ＳｍＸ　６９　Ｉであった。
【００９０】
前記と同様の方法により、以下の化合物を製造した。
（ｉｉ）４−（トランス−４−ｎ−プロピルシクロヘキシル）−（３−ヒドロキシプロピルオキシ）ベンゼン：Ｃ　室温以下　ＳｍＸ　６８　Ｉ
（ｉｉｉ）２−（４−ｎ−ノニルオキシフェニル）−５−（８−ヒドロキシオクチルオキシ）ピリミジン：Ｃ　５３　ＳｍＸ　８７　Ｉ
（ｉｖ）４−（４−ｎ−ペンチルフェニルエチニル）−（６−ヒドロキシヘキシルオキシ）ベンゼン：Ｃ　８２　Ｎ　９２．６　Ｉ
（ｖ）２−（ヒドロキシヘキシルオキシ）−６−（４−ｎ−ペンチルフェニルエチニル）ナフタレン：Ｃ　１１５　Ｎ　１４０　Ｉ
（ｖｉ）２−（６−ヒドロキシヘプチルオキシ）−６−（４−プロピルフェニル）ナフタレン：融点１４７℃
（ｖｉｉ）４−［４−（トランス−４−ｎ−プロピルシクロヘキシル）シクロヘキシル］−１−（６−ヒドロキシヘキシルオキシ）ベンゼン
：Ｃ　１８８　Ｎ　１９９．７　Ｉ
（ｖｉｉｉ）２−（４−ヘキシルフェニル）−５−［４−（６−ヒドロキシヘキシルオキシ）フェニル］ピリジン：　Ｃ　１８０　ＳｍＡ　２００　Ｎ　２０３　Ｉ
【００９１】
（１−３ａ）　マレイミド誘導体の製造１
マレイミドのフラン付加体［ａ］（１５ｇ）、（ｉｉ）の４−（トランス−４−ｎ−プロピルシクロヘキシル）−（３−ヒドロキシプロピルオキシ）ベンゼン（１０ｇ）、トリフェニルフォスフィン（１４．４ｇ）、テトラヒドロフラン（２００ｍｌ）からなる溶液にアゾジカルボン酸ジエチルの４０％トルエン溶液（２７ｍｌ）を０℃で加え、室温で１２時間攪拌した。水（５０ｍｌ）、酢酸エチル（２００ｍｌ）を加えて分液し、有機層を無水硫酸マグネシウムで乾燥した。溶剤を留去して得られた残査にトルエン（２００ｍｌ）を加え１２時間還流した。トルエンを留去して得られた残査をシリカゲルクロマトグラフィーで精製、エタノールで再結晶を行い、７．５ｇのＮ−〔３−［４−（トランス−４−ｎ−プロピルシクロヘキシル）フェニルオキシ］プロピル〕マレイミド（化合物Ｎｏ．３）を得た。

【００９２】
＜プロトンＮＭＲの測定値＞
^１Ｈ−ＮＭＲ（ＣＤＣｌ_３、９０ＭＨｚ）：δ（ｐｐｍ）：０．８９（３Ｈ、ｔ、Ｊ＝６Ｈｚ）１．２１〜２．００（１６Ｈ、ｍ）、３．５２（２Ｈ、ｔ、Ｊ＝６．３Ｈｚ）、３．９０（２Ｈ、ｔ、Ｊ＝６．３Ｈｚ）、６．６７（２Ｈ、ｓ）、６．７９（２Ｈ、ｄ、Ｊ＝９Ｈｚ）、７．１１（２Ｈ、ｄ、Ｊ＝９Ｈｚ）
融点：　９８℃
【００９３】
（１−３ｂ）　マレイミド誘導体の製造２
テトラヒドロフタルイミド−Ｎ−エチルアルコール（１０ｇ）、４−（トランス−４−ｎ−プロピルシクロヘキシル）フェノール（１１ｇ）、トリフェニルフォスフィン（１４．６ｇ）、テトラヒドロフラン（２００ｍｌ）からなる溶液にアゾジカルボン酸ジエチルの４０％トルエン溶液（２７ｍｌ）を０℃で加え、室温で１２時間攪拌した。水（５０ｍｌ）、酢酸エチル（２００ｍｌ）を加えて分液し、有機層を無水硫酸マグネシウムで乾燥した。トルエンを留去して得られた残査をシリカゲルクロマトグラフィーで精製、エタノールで再結晶を行い、６ｇのＮ−〔３−［４−（トランス−４−ｎ−プロピルシクロヘキシル）フェニルオキシ］エチル〕テトラヒドロフタルイミド（化合物Ｎｏ．１２０）を得た。

実施例２
実施例１の方法に準じ、以下のマレイミド誘導体を製造した。
（ｉ）化合物Ｎｏ．８
Ｎ−〔６−［４−（トランス−４−ｎ−プロピルシクロヘキシル）フェニルオキシ］ヘキシル〕マレイミド

^１Ｈ−ＮＭＲ（ＣＤＣｌ_３、９０ＭＨｚ）：δ（ｐｐｍ）：０．８９（３Ｈ、ｔ、Ｊ＝６Ｈｚ）１．２１〜２．００（２２Ｈ、ｍ）、３．５２（２Ｈ、ｔ、Ｊ＝６．３Ｈｚ）、３．９１（２Ｈ、ｔ、Ｊ＝６．３Ｈｚ）、６．６７（２Ｈ、ｓ）、６．７９（２Ｈ、ｄ、Ｊ＝９Ｈｚ）、７．１１（２Ｈ、ｄ、Ｊ＝９Ｈｚ）
融点：　６９℃
【００９４】
（ｉｉ）化合物Ｎｏ．３０
Ｎ−〔８−［２−（４−ノニルオキシフェニル）ピリミジン−５−イルオキシ］オクチル〕マレイミド

^１Ｈ−ＮＭＲ（ＣＤＣｌ_３、９０ＭＨｚ）：δ（ｐｐｍ）：０．８８（３Ｈ、ｔ、Ｊ＝６Ｈｚ）、１．２〜２．０（２６Ｈ、ｍ）、３．５１（２Ｈ、ｔ、Ｊ＝６．３Ｈｚ）、４．０１（２Ｈ、ｔ、Ｊ＝６．３Ｈｚ）、４．１４（２Ｈ、ｔ、Ｊ＝６．３Ｈｚ）、６．６８（２Ｈ、ｓ）、６．９６（２Ｈ、ｄ、Ｊ＝９Ｈｚ）、８．２８（２Ｈ、ｄ、Ｊ＝９Ｈｚ）、８．４２（２Ｈ、ｓ）
融点：７９℃
【００９５】
（ｉｉｉ）化合物Ｎｏ．４４
Ｎ−［６−〔４−（４−ｎ−ペンチルフェニルエチニル）フェニルオキシ〕ヘキシル］マレイミド

^１Ｈ−ＮＭＲ（ＣＤＣｌ_３、９０ＭＨｚ）：δ（ｐｐｍ）：０．８９（３Ｈ、ｔ、Ｊ＝６Ｈｚ）、１．２〜１．９（１４Ｈ、ｍ）、２．６０（２Ｈ、ｔ、Ｊ＝８Ｈｚ）、３．５３（２Ｈ、ｔ、Ｊ＝８Ｈｚ）、３．９５（２Ｈ、ｔ、Ｊ＝８Ｈｚ）、６．６７（２Ｈ、Ｓ）、６．８３（２Ｈ、ｄ、Ｊ＝９．０Ｈｚ）、７．１３（２Ｈ、ｄ、Ｊ＝９．０Ｈｚ）、７．４２（２Ｈ、ｄ、Ｊ＝９．０Ｈｚ）、７．４３（２Ｈ、ｄ、Ｊ＝９．０Ｈｚ）
融点：８２℃
【００９６】
（ｉｖ）化合物Ｎｏ．６５
Ｎ−〔６−［２−（４−プロピルフェニル）ナフタレン−６−イルオキシ］ヘキシル〕マレイミド

^１Ｈ−ＮＭＲ（ＣＤＣｌ_３、９０ＭＨｚ）：δ（ｐｐｍ）：０．９８（３Ｈ、ｔ、Ｊ＝６Ｈｚ）、１．３０〜２．００（１０Ｈ、ｍ）、２．６５（２Ｈ、ｔ、Ｊ＝８Ｈｚ）、３．５４（２Ｈ、ｔ、Ｊ＝８Ｈｚ）、４．０７（２Ｈ、ｔ、Ｊ＝８Ｈｚ）、６．６７（２Ｈ、ｓ）、７．１０〜７．３１（ｍ）、７．５７〜７．９４（ｍ）
融点：１２９℃
【００９７】
（ｖ）化合物Ｎｏ．６６
Ｎ−〔６−〔２−（４−ｎ−ペンチルフェニルエチニル）ナフタレン−６−イルオキシ〕ヘキシル〕マレイミド

^１Ｈ−ＮＭＲ（ＣＤＣｌ_３、９０ＭＨｚ）：δ（ｐｐｍ）：０．８９（３Ｈ、ｔ、Ｊ＝６Ｈｚ）、０．８０〜２．００（１４Ｈ、ｍ）、２．６２（２Ｈ、ｔ、Ｊ＝８Ｈｚ）、３．５４（２Ｈ、ｔ、Ｊ＝８Ｈｚ）、４．０６（２Ｈ、ｔ、Ｊ＝８Ｈｚ）、６．６７（２Ｈ、ｓ）、７．０８〜７．２０（４Ｈ、ｍ）、７．４２〜７．７３（５Ｈ、ｍ）、７．９５（１Ｈ、ｓ）
融点：１０５℃
【００９８】
（ｖｉ）化合物Ｎｏ．７３
Ｎ−〔６−［４−［４−トランス−（トランス−４−ｎ−プロピルシクロヘキシル）シクロヘキシル］フェニルオキシ］ヘキシル〕マレイミド

^１Ｈ−ＮＭＲ（ＣＤＣｌ_３、９０ＭＨｚ）：δ（ｐｐｍ）：０．８７（３Ｈ、ｔ、Ｊ＝６Ｈｚ）、０．８０〜２．００（ｍ）、３．５２（２Ｈ、ｔ、Ｊ＝８Ｈｚ）、３．９０（２Ｈ、ｔ、Ｊ＝８Ｈｚ）、６．６７（２Ｈ、ｓ）、６．８３（２Ｈ、ｄ、Ｊ＝９Ｈｚ）、７．１０（２Ｈ、ｄ、Ｊ＝９Ｈｚ）
融点：１５５．５℃
【００９９】
（ｖｉｉ）化合物Ｎｏ．８３
Ｎ−〔６−〔４−［２−（４−ヘキシルフェニル）ピリジン−５−イル］フェニルオキシ〕ヘキシル〕マレイミド

^１Ｈ−ＮＭＲ（ＣＤＣｌ_３、９０ＭＨｚ）：δ（ｐｐｍ）：０．８８（３Ｈ、ｔ、Ｊ＝６Ｈｚ）、１．２０〜２．００（１６Ｈ、ｍ）、２．６７（２Ｈ、ｔ、Ｊ＝８Ｈｚ）、３．５３（２Ｈ、ｔ、Ｊ＝８Ｈｚ）、３．９９（２Ｈ、ｔ、Ｊ＝８Ｈｚ）、６．６７（２Ｈ、ｓ）、６．９９（２Ｈ、ｄ、Ｊ＝９Ｈｚ）、７．２９（２Ｈ、ｄ、Ｊ＝７．２Ｈｚ）、７．５５（２Ｈ、ｄ、Ｊ＝９Ｈｚ）、７．７７〜７．９９（４Ｈ、ｍ）、８．８８（１Ｈ、Ｊ＝１．３Ｈｚ）
融点：１４８℃
【０１００】
（ｖｉｉｉ）化合物Ｎｏ．８８
Ｎ−［６−〔４−（４’−ｎ−プロピルビフェニルオキシカルボニル）フェニルオキシ〕ヘキシル］マレイミド

^１Ｈ−ＮＭＲ（ＣＤＣｌ_３、９０ＭＨｚ）：δ（ｐｐｍ）：０．９７（３Ｈ、ｔ、Ｊ＝７．３Ｈｚ）、１．２０〜２．００（１０Ｈ、ｍ）、２．６４（２Ｈ、ｔ、Ｊ＝８Ｈｚ）、３．５４（２Ｈ、ｔ、Ｊ＝８Ｈｚ）、４．０４（４Ｈ、ｔ、Ｊ＝８Ｈｚ）、６．６８（２Ｈ、ｓ）、６．９４（２Ｈ、Ｊ＝９Ｈｚ）、７．１５〜７．４０（４Ｈ、ｍ）、７．４０〜７．７５（４Ｈ、ｍ）、８．１５（２Ｈ、Ｊ＝９Ｈｚ）
相転移温度：Ｃ　１２７　Ｎ　１３５．３　Ｉ
【０１０１】
（ｉｘ）化合物Ｎｏ．８９
Ｎ−［６−〔４−（４’−シアノビフェニルオキシカルボニル）フェニルオキシ〕ヘキシル］マレイミド

^１Ｈ−ＮＭＲ（ＣＤＣｌ_３、９０ＭＨｚ）：δ（ｐｐｍ）：１．２０〜２．００（８Ｈ、ｍ）、３．５４（２Ｈ、ｔ、Ｊ＝８Ｈｚ）、４．０４（４Ｈ、ｔ、Ｊ＝８Ｈｚ）、６．６８（２Ｈ、ｓ）、６．９７（２Ｈ、Ｊ＝９Ｈｚ）、７．３１（２Ｈ、Ｊ＝９Ｈｚ）、７．６０（２Ｈ、Ｊ＝９Ｈｚ）、７．７０（４Ｈ、ｍ）、８．１５（２Ｈ、Ｊ＝９Ｈｚ）
相転移温度：Ｃ　１１１　Ｎ　２０２　Ｉ
【０１０２】
実施例３
＜ラジカル重合によるマレイミド重合体の製造＞
（ｉ）化合物Ｎｏ．３の重合
化合物Ｎｏ．３（０．６ｇ）、アゾビスイソブチロニトリル（ＡＩＢＮ；０．００４１ｇ）、テトラヒドロフラン（２ｍｌ）をアンプルにとり、−６０℃に冷却し、真空ポンプで十分脱気を行い、そして封管した。封管したアンプルを７０℃で４８時間反応させた。アンプル内の内容物をテトラヒドロフラン（１０ｍｌ）に溶解し、メタノール（１００ｍｌ）に投入して沈殿させた。この操作を３回行った後、メタノールで十分洗浄し、減圧下で乾燥させ０．４ｇの重合体［Ｐ１］を得た。
重量平均分子量（Ｍ_Ｗ）：３４，０００
多分散度（Ｍｗ／Ｍｎ）：１．４４
相転移温度：Ｔｍ　２００　Ｎ　２５０　Ｉ
重合体［Ｐ１］は、ネマチック液晶相を有する重合体であった。
太陽光に暴露させるために重合体［Ｐ１］を室外に置き、耐光性試験を行ったが、１ヶ月経過後も重合体［Ｐ１］に曇りや色つきはなかった。即ち、太陽光による重合体［Ｐ１］の劣化は確認されなかった。
【０１０３】
（ｉｉ）化合物Ｎｏ．３０の重合
化合物Ｎｏ．３０（２ｇ）、ＡＩＢＮ（０．００２４ｇ）を用い、７０℃で７２時間で反応した以外は、化合物Ｎｏ．３の重合と同様の操作により０．３５ｇの重合体［Ｐ２］を得た。
重量平均分子量（Ｍｗ）：３３，０００
多分散度（Ｍｗ／Ｍｎ）：１．４６
相転移温度：Ｔｍ　６０　ＳｍＸ　１３０　Ｉ
重合体［Ｐ２］は、スメクチック液晶相を有する重合体であった。
【０１０４】
（ｉｉｉ）化合物Ｎｏ．６５の重合
化合物Ｎｏ．６５（０．３４ｇ）、ＡＩＢＮ（０．００１９ｇ）、テトラヒドロフラン（１．５ｍｌ）を用い、７０℃で４８時間で反応した以外は、化合物Ｎｏ．３の重合と同様の操作により、０．２ｇの重合体［Ｐ３］を得た。
重量平均分子量（Ｍｗ）：３６，０００
多分散度（Ｍｗ／Ｍｎ）：１．４３
相転移温度：Ｔｍ　１６５　Ｎ　２１４　Ｉ
重合体［Ｐ３］は、ネマチック液晶相を有する重合体であった。
【０１０５】
（ｉｖ）化合物Ｎｏ．７３の重合
化合物Ｎｏ．７３（０．４ｇ）、ＡＩＢＮ（０．００２ｇ）、テトラヒドロフラン（３ｍｌ）を用い、７０℃で４８時間で反応した以外は、化合物Ｎｏ．３の重合と同様の操作により、０．３１ｇの重合体［Ｐ４］を得た。
重量平均分子量（Ｍｗ）：３８，０００
多分散度（Ｍｗ／Ｍｎ）：１．４０
相転移温度：Ｔｍ　２４０　Ｎ　２８０　Ｉ
重合体［Ｐ４］は、ネマチック液晶相を有する重合体であった。
【０１０６】
（ｖ）化合物Ｎｏ．８３の重合
化合物Ｎｏ．８３（０．４５ｇ）、ＡＩＢＮ（０．００２２ｇ）、テトラヒドロフラン（３ｍｌ）を用い、７０℃で４８時間で反応した以外は、化合物Ｎｏ．３の重合と同様の操作により、０．４ｇの重合体［Ｐ５］を得た。
重量平均分子量（Ｍｗ）：１６，０００
多分散度（Ｍｗ／Ｍｎ）：１．４３
相転移温度：　Ｔｍ　１７５　ＳｍＸ　２９０℃以上　Ｉ
（透明点は、測定機器の測定限界以上で測定できなかった）
重合体［Ｐ５］は、スメクチック相を有する重合体であった。
【０１０７】
実施例４
＜アニオン重合によるマレイミド重合体の製造＞
（ｉ）化合物Ｎｏ．４４の重合
化合物Ｎｏ．４４（０．５ｇ）のテトラヒドロフラン（２ｍｌ）溶液を−１０℃に冷却し、そこへｎ−ブチルリチウムのヘキサン溶液（濃度１．５６ｍｏｌ／ｌ）０．０２７ｍｌを加え、１０℃を保ちながら８時間攪拌した。反応液をメタノール（１００ｍｌ）に注いで反応を止め、メタノール（１００ｍｌ）で２回再沈殿して精製した。２日間減圧下で乾燥し、０．４ｇの重合体［Ｐ６］を得た。重量平均分子量（Ｍ_Ｗ）：３３，０００
多分散度（Ｍｗ／Ｍｎ）：１．２３
相転移温度：Ｔｍ　２１０　Ｎ　２６０　Ｉ
重合体［Ｐ６］は、室温においてネマチック液晶相を有する重合体であった。
【０１０８】
（ｉｉ）化合物Ｎｏ．６６の重合
化合物Ｎｏ．６６（１ｇ）、ｎ−ブチルリチウムのヘキサン溶液（濃度１．５６ｍｏｌ／ｌ）０．０３９ｍｌ、テトラヒドロフラン（６ｍｌ）を用い、−１０℃で８時間で反応した以外は、化合物Ｎｏ．４４の重合と同様の操作により、０．５２ｇの重合体［Ｐ７］を得た。
重量平均分子量（Ｍｗ）：３７，０００
多分散度（Ｍｗ／Ｍｎ）：１．２６
相転移温度：Ｔｍ　２３０　Ｎ　２９０℃以上　Ｉ
（透明点は、測定機器の測定限界以上で測定できなかった）
重合体［Ｐ７］は、ネマチック液晶相を示す重合体であった。
【０１０９】
以上の実施例の結果から判るように、化合物（１）の単独重合により得られる重合体（２）は液晶性の重合体であり、従来のアクリル系重合体よりも高い透明点を示す。このことから、１２０℃以上の透明点を持つ耐熱性重合体が必要とされる位相差板などの材料に、好適に使用できる。
【０１１０】
実施例５
＜共重合によるコレステリック重合体の製造＞
化合物Ｎｏ．６５（０．２ｇ）、光学活性マレイミド（ＯＰＭ−５）（０．０４ｇ）、ＡＩＢＮ（０．００１３ｇ）、テトラヒドロフラン（２ｍｌ）をアンプルにとり、−６０℃に冷却し、真空ポンプで十分脱気を行い、そして封管した。封管したアンプルを７０℃で４８時間反応させた。アンプル内の内容物をテトラヒドロフラン（１０ｍｌ）に溶解し、メタノール（１００ｍｌ）に投入して沈殿させた。この操作を３回行った後、メタノールで十分洗浄し、減圧下で乾燥させ、０．１ｇの重合体［ＣＰ１］を得た。５００ＨｚプロトンＮＭＲの測定により算出した共重合割合は、Ｎｏ．６５：ＯＰＭ−５＝７３：２７であった。
重量平均分子量（Ｍ_Ｗ）：２０，０００
多分散度（Ｍｗ／Ｍｎ）：１．４０
相転移温度：Ｔｍ　１３０　Ｃｈ　１３７　Ｉ
重合体［ＣＰ１］は、コレステリック液晶相を示す重合体であった。
【０１１１】
実施例６
＜光学補償膜の製造＞
実施例３で製造した重合体［Ｐ１］をＮ−メチルピロリドンに溶解し、［Ｐ１］含有率２０重量％の溶液を調製した。この溶液をラビングポリイミド膜を有するガラス基板にスピンコートにより塗布し、溶媒を蒸発させて除去した。その後２２０℃で３０分間熱処理し、熱処理後、冷却して配向を固定化した。得られたガラス基板上のフィルムはラビング方向と同一方向に配向しており、配向欠陥のない均一（０．５μｍ）なフィルムであった。
【０１１２】
実施例７
＜光重合によるマレイミド重合体フィルムの製造＞
化合物Ｎｏ．３（１００ｍｇ）、光重合開始剤２−ヒドロキシ−２−メチル−１−フェニルプロパン−１−オン（４ｍｇ）からなる組成物を調製した。ポリフッ化エチレン製の板とガラス板を、セルギャップが５０ミクロンとなるように張り合わせたセルを作製した。このセルに前記の組成物を１００℃で注入した。高圧水銀灯（１２０Ｗ／ｃｍ^２）を用い、同温度を保持したまま、ガラス面側から１０分間紫外線を照射した。照射後セルを室温に戻し、ガラス板とポリフッ化エチレン製の板を剥離してフィルムを得た。このフィルムはムラがなく透明であった。この重合体の重量平均分子量は５５，０００であった。鉛筆硬度試験では３Ｈを示し、硬度が大きいことが判った。
【０１１３】
実施例８
＜液晶配向膜の製造＞
重合体［Ｐ１］をクロロホルムに溶解して、１重量％の溶液を調製した。この溶液をＩＴＯ膜を有するガラス基板にスピンコートした後、十分乾燥させ薄膜を得た（膜厚３０ｎｍ）。ついでラビングによる配向処理を行い、ツイステッドネマチック用の液晶表示素子を作製した。偏光板を取り付け、液晶配向性、電気応答性を調べた。その結果、液晶が均一に配向しており、本発明の重合体が配向膜として優れていることが判った。また電界に対する光学応答も早く液晶表示素子として優れていることが判った。
【０１１４】
【発明の効果】
本発明のマレイミド誘導体（１）は重合反応性が高く、重合反応により高分子量の重合体を得ることができる。化合物（１）の単独重合体または共重合体である重合体（２）は、液晶性を示し、耐熱性、耐光性、硬度、透明性、配向性および基板への塗布性などのいくつかにおいて改良された物性を有する。重合体（２）は、位相差フィルムなどの光学補償膜、液晶配向膜、光書き込み記録材料などに使用できる。[0001]
TECHNICAL FIELD OF THE INVENTION
The present invention relates to a liquid crystalline maleimide polymer that can be used for an optical compensation film, a liquid crystal alignment film, an optical writing recording material, and the like, and a maleimide derivative that is a raw material thereof.
[0002]
[Prior art]
Polymers having a liquid crystal group in the side chain include optically anisotropic films such as retardation films (Patent Document 1), liquid crystal alignment films (Patent Document 2), polarizing beam splitters (Patent Document 3), and rewritable recording. It is used as an optical recording material such as a medium (Patent Document 4). Conventionally, acrylate polymers that can be easily polymerized have been used for such applications.
[Patent Document 1] Japanese Patent Application Laid-Open No. 9-208957
[Patent Document 2] JP-A-62-70407
[Patent Document 3] JP-A-11-100575
[Patent Document 4] JP-A-10-62739
[0003]
[Problems to be solved by the invention]
However, a homopolymer obtained by polymerizing acrylate (for example, AC1) does not show sufficient values in physical properties such as heat resistance and mechanical strength. Therefore, at present, attempts have been made to improve heat resistance and mechanical strength by a chemical method such as copolymerization with a polyfunctional acrylate or a method such as adding a filler.

[0004]
[Means for Solving the Problems]
The present inventors have conducted intensive studies to fundamentally solve the above-described problems, and as a result, a polymer obtained from a specific maleimide derivative has a higher heat resistance, light resistance, hardness, and transparency than the conventional polymer. The present invention has been found to have improved physical properties in some aspects such as orientation, coatability to a substrate, and the like, and based on this finding, completed the present invention. The present invention has the following configuration. In the present invention, the term “arbitrary” used when selecting an unspecified group from a plurality of groups of the same type present in a chemical formula is not limited to the position of the group, but also to the number of groups. It is shown that.
[0005]
[1] A maleimide derivative represented by the formula (1).

In the formula (1), R ¹ Is hydrogen, halogen, -CN, -CF ₃ , -CF ₂ H, -CFH ₂ , -OCF ₃ , -OCF ₂ H, -NCO, -NCS or alkyl having 1 to 20 carbon atoms, and any -CH in the alkyl ₂ -May be replaced by -O-, -S-, -COO-, -OCO-, -CO-, -CH = CH- or -C≡C-, and any hydrogen in the alkyl is halogen. Or may be replaced by -CN; ² And R ³ Is independently hydrogen, phenyl or alkyl having 1 to 20 carbons, and any -CH in the alkyl is ₂ -May be replaced by -O-, -S-, -COO-, -OCO-, -CO-, -CH = CH-, or -C≡C-, and any hydrogen in the alkyl is May be replaced by halogen or -CN; ² And R ³ When both are alkyl, the ends of the alkyl may combine to form a ring; ¹ , A ² And A ³ Is independently 1,4-cyclohexylene, 1,4-cyclohexylene in which at least one hydrogen is replaced by fluorine, 1,4-cyclohexenylene, 1,4-phenylene, at least one hydrogen is 1,4-phenylene, pyridine-2,5-diyl, pyridazine-3,6-diyl, pyrimidine-2,5-diyl, naphthalene-2,6-diyl, substituted with halogen, methyl or trifluoromethyl , 2,3,4-tetrahydronaphthalene-2,6-diyl, 5,6,7,8-tetrahydronaphthalene-2,6-diyl, fluorene-2,7-diyl, 9-methyl-fluorene-2,7 -Diyl or 1,3-dioxane-2,5-diyl; Z ¹ And Z ² Is independently a single bond or alkylene having 1 to 20 carbon atoms, and any -CH in the alkylene is ₂ -Is -O-, -COO-, -OCO-, -CH = CH-, -CF = CF-, -CF ₂ O-, -OCF ₂ -Or -C≡C- and any hydrogen in the alkylene may be replaced by halogen; m is 1 or 0 and n is an integer from 1 to 20. Where m is 0 and A ¹ And A ² Is 1,4-phenylene, and Z ¹ Is a single bond, R ¹ Is not -CN.
[0006]
[2] In the formula (1), R ¹ Is hydrogen, fluorine, chlorine, -NCO or alkyl having 1 to 20 carbons, and any -CH in the alkyl is ₂ -May be replaced by -O-, -S-, -COO-, -OCO- or -CO-, and any hydrogen in the alkyl may be replaced by halogen; ² And R ³ Is independently hydrogen, phenyl or alkyl having 1 to 4 carbons; ² And R ³ When both are alkyl, the ends of the alkyl may combine to form a ring; ¹ , A ² And A ³ Is independently 1,4-cyclohexylene, 1,4-cyclohexylene in which at least one hydrogen is replaced by fluorine, 1,4-cyclohexenylene, 1,4-phenylene, at least one hydrogen Is substituted with halogen, methyl or trifluoromethyl, pyridine-2,5-diyl, pyridazine-3,6-diyl, pyrimidine-2,5-diyl, naphthalene-2,6-diyl, 1,2,3,4-tetrahydronaphthalene-2,6-diyl, 5,6,7,8-tetrahydronaphthalene-2,6-diyl, fluorene-2,7-diyl, 9-methyl-fluorene-2, Z-diyl or 1,3-dioxane-2,5-diyl; Z ¹ And Z ² Is independently a single bond, -COO-, -OCO-, -CF ₂ O-, -OCF ₂ -, -CH ₂ O-, -OCH ₂ -, -CH = CH-, -CH ₂ CH ₂ -Or -C０C-; m is 1 or 0, and n is an integer of 1 to 20. The maleimide derivative according to item [1].
[0007]
[3] The maleimide derivative according to [1] or [2], wherein m is 0.
[0008]
[4] The maleimide derivative according to [1] or [2], wherein m is 1.
[0009]
[5] A polymerizable composition containing at least two polymerizable compounds, at least one of which is the maleimide derivative according to the item [1].
[0010]
[6] The polymerizable composition according to item [5], wherein all of the polymerizable compounds are the maleimide derivative according to item [1].
[0011]
[7] The polymerizable composition according to item [5], comprising at least one maleimide derivative according to item [1] and at least one other polymerizable compound.
[0012]
[8] A polymer having a structural unit represented by the formula (2).

In the formula (2), R ¹ Is hydrogen, halogen, -CN, -CF ₃ , -CF ₂ H, -CFH ₂ , -OCF ₃ , -OCF ₂ H, -NCO, -NCS or alkyl having 1 to 20 carbon atoms, and any -CH in the alkyl ₂ -May be replaced by -O-, -S-, -COO-, -OCO-, -CO-, -CH = CH- or -C≡C-, and any hydrogen in the alkyl is halogen. Or may be replaced by -CN; ² And R ³ Is independently hydrogen, phenyl or alkyl having 1 to 20 carbons, and any -CH in the alkyl is ₂ -May be replaced by -O-, -S-, -COO-, -OCO-, -CO-, -CH = CH- or -C≡C-, and any hydrogen in the alkyl is halogen. Or -CN and R ² And R ³ When both are alkyl, the ends of the alkyl may combine to form a ring; ¹ , A ² And A ³ Is independently 1,4-cyclohexylene, 1,4-cyclohexylene in which at least one hydrogen is replaced by fluorine, 1,4-cyclohexenylene, 1,4-phenylene, at least one hydrogen is 1,4-phenylene, pyridine-2,5-diyl, pyridazine-3,6-diyl, pyrimidine-2,5-diyl, naphthalene-2,6-diyl, substituted with halogen, methyl or trifluoromethyl , 2,3,4-tetrahydronaphthalene-2,6-diyl, 5,6,7,8-tetrahydronaphthalene-2,6-diyl, fluorene-2,7-diyl, 9-methyl-fluorene-2,7 -Diyl or 1,3-dioxane-2,5-diyl; Z ¹ And Z ² Is independently a single bond or an alkylene having 1 to 20 carbon atoms. ₂ -Is -O-, -COO-, -OCO-, -CH = CH-, -CF = CF-, -CF ₂ O-, -OCF ₂ -Or -C≡C-, any hydrogen in the alkylene may be replaced by halogen; m is 1 or 0, and n is an integer from 1 to 20. Where m is 0 and A ¹ And A ² Is 1,4-phenylene, and Z ¹ Is a single bond, R ¹ Is not -CN.
[0013]
[9] In the formula (2), R ¹ Is hydrogen, fluorine, chlorine, -NCO, or alkyl having 1 to 20 carbons, and any -CH in the alkyl is ₂ -May be replaced by -O-, -S-, -COO-, -OCO- or -CO-, and any hydrogen in the alkyl may be replaced by halogen; ² And R ³ Is independently hydrogen, phenyl or alkyl having 1 to 4 carbons; ² And R ³ When both are alkyl, the ends of the alkyl may combine to form a ring; ¹ , A ² And A ³ Is independently 1,4-cyclohexylene, 1,4-cyclohexylene in which at least one hydrogen is replaced by fluorine, 1,4-cyclohexenylene, 1,4-phenylene, at least one hydrogen is 1,4-phenylene, pyridine-2,5-diyl, pyridazine-3,6-diyl, pyrimidine-2,5-diyl, naphthalene-2,6-diyl, substituted with halogen, methyl or trifluoromethyl, 1 , 2,3,4-tetrahydronaphthalene-2,6-diyl, 5,6,7,8-tetrahydronaphthalene-2,6-diyl, fluorene-2,7-diyl, 9-methyl-fluorene-2,7 -Diyl or 1,3-dioxane-2,5-diyl; Z ¹ And Z ² Is independently a single bond, -COO-, -OCO-, -CF ₂ O-, -OCF ₂ -, -CH ₂ O-, -OCH ₂ -, -CH = CH-, -CH ₂ CH ₂ -Or -C０C-; m is 1 or 0, and n is an integer of 1 to 20. The polymer according to item [8].
[0014]
[10] The polymer according to item [8], obtained by homopolymerizing one of the maleimide derivatives according to item [1].
[0015]
[11] The polymer according to item [8], obtained from the polymerizable composition according to item [6].
[0016]
[12] The polymer according to item [8], obtained from the polymerizable composition according to item [7].
[0017]
[13] An optical compensation film containing the polymer according to any one of [8] to [12].
[0018]
[14] An optical writing recording material containing the polymer according to any one of [8] to [12].
[0019]
[15] A liquid crystal alignment film containing the polymer according to any one of [8] to [12].
[0020]
BEST MODE FOR CARRYING OUT THE INVENTION
In the following description, the maleimide derivative of the present invention represented by the formula (1) may be referred to as a compound (1). The structural unit represented by the formula (2) may be represented by the structural unit (2). The polymer of the present invention having the structural unit (2) is sometimes referred to as a polymer (2). And the following groups may be called liquid crystal skeleton (1).

[0021]
The compound (1) and the polymer (2) have the following characteristics.
(I) The compound (1) does not contain azo, diazo, azoxy and the like, which are groups unstable to light or moisture.
(Ii) The compound (1) has an alkylene chain between the polymerizable maleimide group and the sterically large liquid crystal skeleton (1). Since there is no steric crowding, compound (1) has high polymerization reactivity.
(Iii) Since the polymerization reactivity of the compound (1) is high, a high molecular weight polymer can be obtained. As a result, the polymer (2) has high heat resistance.
(Iv) Since the liquid crystal skeleton (1) is separated from the main chain and is not easily sterically restricted by the main chain, the polymer (2) tends to exhibit liquid crystallinity. As a result, the polymer (2) has a wide liquid crystal phase temperature range.
(V) Since the compound (1) is stable to light, the polymer (2) obtained therefrom is also excellent in light resistance.
As described above, the polymer (2) has excellent performance not available in the conventional liquid crystalline acrylate polymer.
[0022]
First, the maleimide derivative of the present invention will be described.
The maleimide derivative of the present invention is represented by the formula (1).

R in this formula ¹ Is hydrogen, halogen, -CN, -CF ₃ , -CF ₂ H, -CFH ₂ , -OCF ₃ , -OCF ₂ H, -NCO, -NCS or alkyl having 1 to 20 carbons. In this alkyl, any -CH ₂ -May be replaced by -O-, -S-, -COO-, -OCO-, -CO-, -CH = CH- or -C≡C-, and any hydrogen is halogen or -CN. It may be replaced.
[0023]
R ¹ Is preferably hydrogen, fluorine, chlorine, -NCO or alkyl having 1 to 20 carbons. In this alkyl, any -CH ₂ -May be replaced by -O-, -S-, -COO-, -OCO- or -CO-. And a plurality of -CH in this alkyl ₂ -May be replaced by a different group among -O-, -S-, -COO-, -OCO-, and -CO-. One example is -O-CH ₂ CH ₂ —COO—. However, two consecutive -CH ₂ -Is not replaced like -OO-, -OS- or -SS-. Then, any hydrogen in the alkyl may be replaced by halogen. Halogen is chlorine or fluorine, with fluorine being preferred.
[0024]
R ¹ Are more preferably hydrogen, fluorine, chlorine, -NCO, fluorinated alkyl having 1 to 3 carbons, fluorinated alkyloxy having 1 to 3 carbons, linear alkyl having 1 to 12 carbons, and 1 to 12 linear alkoxy. A particularly preferred group of fluorinated alkyl and fluorinated alkyloxy is -CF ₃ , -CF ₂ H, -OCF ₃ And -OCF ₂ H. Particularly preferred groups among alkyl and alkoxy are methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, nonyl, decyl, methoxy, ethoxy, propyloxy, butyloxy, pentyloxy, hexyloxy, heptyloxy, octyl Oxy, nonyloxy and decyloxy. In the liquid crystal skeleton (1), R ¹ Is -CF ₃ , -OCF ₃ , -NCO, fluorine or chlorine, the dielectric anisotropy value of the polymer (2) tends to be positive.
[0025]
R ² And R ³ Is independently hydrogen, phenyl or alkyl having 1 to 20 carbons. In this alkyl, any -CH ₂ -May be replaced by -O-, -S-, -COO-, -OCO-, -CO-, -CH = CH- or -C≡C-, and any hydrogen is replaced by halogen or -CN. You may be. R ² Or R ³ Is preferably hydrogen, phenyl or alkyl having 1 to 4 carbons. And R ² And R ³ When both are alkyl, the terminals of the alkyl may combine to form a ring. R ¹ And R ² Particularly preferred examples of are shown below together with a maleimide ring.
[0026]

[0027]
A in equation (1) ¹ ~ A ³ Is a divalent group having a ring structure. These are independently 1,4-cyclohexylene, 1,4-cyclohexylene wherein at least one hydrogen is replaced by fluorine, 1,4-cyclohexenylene, 1,4-phenylene, at least one hydrogen Is substituted with halogen, methyl or trifluoromethyl, pyridine-2,5-diyl, pyridazine-3,6-diyl, pyrimidine-2,5-diyl, naphthalene-2,6-diyl, 1,2,3,4-tetrahydronaphthalene-2,6-diyl, 5,6,7,8-tetrahydronaphthalene-2,6-diyl, fluorene-2,7-diyl, 9-methyl-fluorene-2, 7-diyl or 1,3-dioxane-2,5-diyl. A ¹ , A ² Or A ³ Preferred examples are shown below.
[0028]

These equations may be combined in the left and right directions in equation (1).
[0029]
Z in equation (1) ¹ And Z ² Is a linking group. These are each independently a single bond or an alkylene having 1 to 20 carbon atoms. ₂ -Is -O-, -COO-, -OCO-, -CH = CH-, -CF = CF-, -CF ₂ O-, -OCF ₂ -Or -C≡C-, and any hydrogen in the alkylene may be replaced by halogen. Z ¹ Or Z ² Are preferably a single bond, -COO-, -OCO-, -CF ₂ O-, -OCF ₂ -, -CH ₂ O-, -OCH ₂ -, -CH = CH-, -CH ₂ CH ₂ -And -C≡C-. Z ¹ Or Z ² Are more preferably a single bond, -COO-, -OCO-, -C≡C-, -CF ₂ O-, -OCF ₂ -, -CH ₂ O-, -OCH ₂ -And -CH ₂ CH ₂ -.
[0030]
In the compound (1), Z ¹ And Z ² Is a single bond, -COO-, -OCO- or -C≡C-, a polymer having a large refractive index anisotropy tends to be obtained. Z ¹ And Z ² At least one of -CF ₂ O-, -OCF ₂ -, -CH ₂ O-, -OCH ₂ -Or -CH ₂ CH ₂ In the case of-, the flexibility of the liquid crystal skeleton (1) increases, so that a polymer having a relatively low viscosity tends to be obtained. And m is 1 or 0. Where m is 0 and A ¹ And A ² Is 1,4-phenylene, and Z ¹ Is a single bond, R ¹ Is not -CN. That is, the compound of the present invention does not include a compound in which the liquid crystal skeleton (1) is cyanobiphenyl.
[0031]
A ¹ ~ A ³ And Z ¹ ~ Z ² Will be described. In order for the polymer (2) to have a liquid crystal phase at room temperature, m is preferably 0 in the liquid crystal skeleton (1). That is, the following (1-1) to (1-10).

R in these formulas ¹ , A ¹ And A ² Has the meaning described above.
[0032]
The liquid crystal skeleton (1) in which m is 1 has three rings. A polymer having a three-ring liquid crystal skeleton (1) generally has a high maximum temperature of a liquid crystal phase. When it has a three ring structure, ¹ ~ A ³ And Z ¹ ~ Z ² Preferred combinations of are as follows.

[0033]

R in these formulas ¹ , A ¹ , A ² And A ³ Has the meaning described above.
[0034]
In the formula (1), n is preferably an integer of 1 to 20 so that the compound (1) is easily polymerized and the polymer obtained by the polymerization has a liquid crystal phase. More preferably, n is 3-11. When the compound (1) has 1,4-cyclohexylene or 1,3-dioxane-2,5-diyl, the steric configuration is preferably a trans type rather than a cis type. Compound (1) is ² H (deuterium) or ¹³ An isotope element such as C may be contained in a higher proportion than naturally occurring, and even in such a case, there is no great difference in physical properties of the compound.
[0035]
Next, a method for producing the compound (1) will be described.
Compound (1) is represented by R ² And R ³ When is hydrogen, it can be produced according to the following scheme.

[0036]
First, a maleimide furan adduct (a) is produced by a Diels-Alder reaction between maleimide and furan. An alcohol derivative (b) is produced by etherifying a compound having a liquid crystal skeleton (1) and having a hydroxyl group at the end with ω-bromoalkanol using a base. Examples of bases are potassium hydroxide, sodium hydroxide, potassium carbonate, sodium hydride and the like. The compound (1) is produced by N-alkylating the furan adduct of maleimide (a) and the alcohol derivative (b) by the Mitsunobu reaction and then thermally decomposing by the retro-Diels-Alder reaction.
[0037]
R ² And R ³ When is independently phenyl or alkyl having 1 to 4 carbon atoms, it can be produced from an acid anhydride (c) and an amino alcohol. R ² And R ³ Are also alkyl, and the same applies to the case where the ends of the alkyl are bonded to form a ring.

[0038]
In addition, methods for introducing a desired terminal group, ring and bonding group into a starting material are described in Houben-Wyle, Methods of Organic Chemistry, Georg Thieme Verlag, Stuttgart, Organic synergy, Organics, Synthesis, Synthesis, Nature, Sciences, Natures. Wiley & Sons, Inc.), Organic Reactions (John Wiley & Sons Inc.), Comprehensive Organic Synthesis (Comprehensive Organic Synthesis, etc.); I have.
[0039]
Linking group Z ₁ Or Z ₂ Regarding an example of a method for producing, a scheme is shown first, and then the scheme is described in terms (I) to (VII). In these schemes, MSG ¹ And MSG ² Are both monovalent organic groups having at least one ring. Multiple MSGs shown in the scheme ¹ (Or MSG ² ) May be the same or different.
[0040]

[0041]

[0042]

[0043]
(I) Formation of a single bond
The compound (1A) is synthesized by reacting the arylboric acid (21) with a compound (22) synthesized by a known method in the presence of an aqueous carbonate solution in the presence of a catalyst such as tetrakis (triphenylphosphine) palladium. This compound (1A) is prepared by reacting compound (23) synthesized by a known method with n-butyllithium and then with zinc chloride in the presence of a catalyst such as dichlorobis (triphenylphosphine) palladium. ) Can also be synthesized.
[0044]
(II) Formation of -COO- and -OCO-
Compound (23) is reacted with n-butyllithium and subsequently with carbon dioxide to obtain carboxylic acid (24). Compound having —COO— by dehydrating compound (24) and phenol (25) synthesized by a known method in the presence of DDC (1,3-dicyclohexylcarbodiimide) and DMAP (4-dimethylaminopyridine) (1B) is synthesized. By this method, a compound having -OCO- can also be synthesized.
[0045]
(III) -CF ₂ O- and -OCF ₂ Generate-
Compound (1B) is treated with a sulfurizing agent such as Lawesson's reagent to give compound (26). Compound (26) is fluorinated with a hydrogen fluoride pyridine complex and NBS (N-bromosuccinimide) to give -CF ₂ Compound (1C) having O— is synthesized. M. Kuroboshi et al. Chem., Chem. Lett. , 1992, 827. See Compound (1C) can also be synthesized by fluorinating compound (26) with (diethylamino) sulfur trifluoride. William H. Bunnelle et al. J. et al. Org. Chem. 1990, 55, 768. See By this method, -OCF ₂ A compound having-can also be synthesized.
[0046]
(IV) Formation of -CH = CH-
The compound (23) is treated with n-butyllithium and then reacted with a formamide such as N, N-dimethylformamide to obtain an aldehyde (28). The compound (1D) is synthesized by reacting the phosphonium salt (27) synthesized by a known method with a base such as potassium t-butoxide and generating phosphorus ylide with an aldehyde (28). Since a cis form is produced depending on the reaction conditions, the cis form is isomerized to a trans form by a known method as necessary.
[0047]
(V) -CH ₂ CH ₂ Generate-
The compound (1E) is synthesized by hydrogenating the compound (1D) in the presence of a catalyst such as palladium on carbon.
[0048]
(VI) Generation of -C≡C-
Compound (23) is reacted with 2-methyl-3-butyn-2-ol in the presence of a catalyst of dichloropalladium and copper halide, and then deprotected under basic conditions to obtain compound (30). . Compound (30) is reacted with compound (22) in the presence of a catalyst of dichloropalladium and copper halide to synthesize compound (1G).
[0049]
(VII) -CH ₂ O- or -OCH ₂ Generate-
Compound (28) is reduced with a reducing agent such as sodium borohydride to obtain compound (32). This is halogenated with hydrobromic acid or the like to obtain a compound (33). Compound (33) is reacted with compound (25) in the presence of potassium carbonate or the like to synthesize compound (1J).
[0050]
By these methods, No. 1 to No. Compound 141 is prepared.

[0051]

[0052]

[0053]

[0054]

[0055]

[0056]

[0057]

[0058]

[0059]

[0060]

[0061]

[0062]

[0063]
Next, the composition of the present invention will be described.
The composition of the present invention is a polymerizable composition containing at least one compound (1) and optionally containing a compound copolymerizable therewith. That is, it is a polymerizable composition in which all of the polymerizable compounds contained are the compound (1), or a polymerizable composition containing the compound (1) and a polymerizable compound other than the compound (1). In the following description, a polymerizable compound other than the compound (1) is referred to as another monomer. The purpose of using other monomers is to impart film-forming properties and mechanical strength to the copolymer obtained by copolymerization with the compound (1). There are no conditions for selecting other monomers other than achieving this purpose. Other monomers may or may not be liquid crystalline. In the polymerizable composition of the present invention, a preferable content of the compound (1) is 5 to 100 mol% based on the total amount of the composition. Then, a solvent or a catalyst can be added to the polymerizable composition as needed when performing the polymerization reaction.
[0064]
Next, the polymer of the present invention will be described.
When only one of the compounds (1) is polymerized, a homopolymer is obtained. When a polymerizable composition containing at least two compounds (1) as a polymerizable compound is polymerized, a copolymer of only the compound (1) is obtained. A copolymer can be obtained by polymerizing a polymerizable composition containing the compound (1) and another monomer. Each of these homopolymers and copolymers has the following structural unit (2). That is, since the polymer (2) has the liquid crystal skeleton (1) in the side chain, the polymer (2) easily has a liquid crystal phase. The meanings of the symbols in the structural unit (2) are the same as those in the formula (1). The arrangement of the structural units (2) in the copolymer may be any of random, block, alternating, graft, and the like.

[0065]
The polymer (2) is produced by polymerizing one of the compounds (1) or the polymerizable composition by heat or light. The reaction temperature of the thermal polymerization is 0 to 150 ° C., the reaction time is 1 to 100 hours, and a radical polymerization initiator is usually used. Examples of the radical polymerization initiator include benzoyl peroxide, diisopropylperoxydicarbonate, t-butylperoxy-2-ethylhexanoate, t-butylperoxypivalate, t-butylperoxydiisobutyrate, and peroxide. Lauroyl, dimethyl 2,2'-azobisisobutyrate (MAIB), di-t-butyl peroxide (DTBPO), azobisisobutyronitrile (AIBN), azobiscyclohexanecarbonitrile (ACN) and the like.
[0066]
In polymerization by irradiation with light or an electron beam, a photoradical polymerization initiator is usually used. Examples of the photo-radical polymerization initiator include Darocur 1173 (2-hydroxy-2-methyl-1-phenylpropan-1-one) and Irgacure 184 (1) among products of Ciba Specialty Chemical Co., Ltd. -Hydroxycyclohexylphenyl ketone), Irgacure 651 (2,2-dimethoxy-1,2-diphenylethan-1-one), Irgacure 500, Irgacure 2959, Irgacure 907, Irgacure 369, Irgacure 1300, Irgac Cure 819, Irgacure 1700, Irgacure 1800, Irgacure 1850, Darocure 4265, Irgacure 784, and the like.
[0067]
Other examples of the photoradical polymerization initiator include p-methoxyphenyl-2,4-bis (trichloromethyl) triazine and 2- (p-butoxystyryl) -5-trichloromethyl-1,3,4-oxadiazole. , 9-phenylacridine, 9,10-benzphenazine, benzophenone / Michler's ketone mixture, hexaarylbiimidazole / mercaptobenzimidazole mixture, 1- (4-isopropylphenyl) -2-hydroxy-2-methylpropan-1-one, Benzyldimethyl ketal, 2-methyl-1- [4- (methylthio) phenyl] -2-morpholinopropan-1-one, 2,4-diethylxanthone / methyl p-dimethylaminobenzoate, and the like.
[0068]
The polymer (2) can also be produced by an anionic polymerization method, a coordination polymerization method, or a living polymerization method. Preferred initiators used in these polymerization methods include alkali metal alkyls such as n-butyllithium, sec-butyllithium, t-butyllithium, t-butyllithium-trialkylaluminum, aluminum compounds, transition metal compounds and the like.
[0069]
A solvent may be used for the polymerization reaction. Preferred solvents are benzene, toluene, xylene, mesitylene, pentane, hexane, heptane, octane, nonane, decane, tetrahydrofuran, 1,4-dioxane, N-methylpyrrolidone, dimethylformamide, dimethylsulfoxide and the like. A solvent in which at least two of these are mixed may be used.
[0070]
Next, other monomers will be described.
Examples of the polymerizable compound that is not liquid crystal among other monomers include a vinyl monomer, a fumaric acid diester, and a maleimide derivative. Of these, maleimide derivatives are preferred because of their excellent copolymerizability with compound (1).
[0071]
Among the maleimide derivatives other than the compound (1), examples of non-liquid crystalline maleimide derivatives include N-methylmaleimide, N-ethylmaleimide, N-propylmaleimide, N-butylmaleimide, N-pentylmaleimide, and N-hexylmaleimide. N-heptylmaleimide, N-octylmaleimide, N-nonylmaleimide, N-decylmaleimide, N-undecylmaleimide, N-dodecylmaleimide, N-octadecylmaleimide, N-isopropylmaleimide, N- (sec-butyl) maleimide N- (t-butyl) maleimide, N- (1-methylbutyl) maleimide, N- (2-methylbutyl) maleimide, N- (3-methylbutyl) maleimide, N- (sec-hexyl) maleimide, N- (4 -Methyl-2-pentyl) maleimide, -(Sec-heptyl) maleimide, N- (sec-octyl) maleimide, N-cyclopropylmaleimide, N-cyclobutylmaleimide, N-cyclopentylmaleimide, N-cyclohexylmaleimide, N-phenylmaleimide, N- (2-methyl Phenyl) maleimide, N- (2-ethylphenyl) maleimide, N- (2-isopropylphenyl) maleimide, N- (2,6-dimethylphenyl) maleimide, N- (2,6-diethylphenyl) maleimide, N- (2,6-diisopropylphenyl) maleimide, N- (2,4,6-trimethylphenyl) maleimide, N- (2-chlorophenyl) maleimide, N- (3-methylphenyl) maleimide, N- (3-ethylphenyl ) Maleimide, N- (3-trifluoromethylf Nyl) maleimide, N- (3,5-dimethylphenyl) maleimide, N-benzylmaleimide, N- (4-methylphenyl) maleimide, N- (4-ethylphenyl) maleimide, N- (4-propylphenyl) maleimide , N- (4-isopropylphenyl) maleimide, N- (4-butylphenyl) maleimide, N- (4-pentylphenyl) maleimide, N-trifluoromethylmaleimide, N- [1- (trifluoromethyl) ethyl] Maleimide, N- [2- (trifluoromethyl) ethyl] maleimide, N-hexafluoroisopropylmaleimide, N-perfluoroisopropylmaleimide, N-perfluorobutylethylmaleimide, N-perfluorooctylethylmaleimide, N- (2 -Chloroethyl) maleimide, N- (1-butoxy-2-propyl) maleimide, N- (methoxyethyl) maleimide, N- (trimethylsilyl) maleimide, N- (t-butyldimethylsilyl) maleimide, N- (dimethylethoxysilyl) maleimide, (N- ( 2-cyanoethyl) maleimide, N- (2-hydroxyethyl) maleimide, N- (3-hydroxypropyl) maleimide, N- (4-hydroxybutyl) maleimide, N- (5-hydroxypentyl) maleimide, N- (6 -Hydroxyhexyl) maleimide, N- (7-hydroxyheptyl) maleimide, N- (8-hydroxyoctyl) maleimide, N- (9-hydroxynonyl) maleimide, N- (10-hydroxydecyl) maleimide, and the like.
[0072]
Optically active maleimide derivatives (OPM-1) to (OPM-5) can also be used as a copolymerization partner of compound (1).

[0073]
The vinyl monomer is used for the purpose of imparting a film-forming property or transparency to the polymer (2). The only condition for selecting a vinyl monomer is that this object can be achieved. Preferred vinyl monomers are olefin, vinyl halide, vinyl carboxylate, aromatic vinyl monomer, styrene derivative, vinyl ether, alkyl vinyl ketone, diene, (meth) acrylate, itaconate, α, β-vinylnaphthalene. , N-vinylacetamide and the like. Examples of olefins are ethylene, propylene, isobutene and the like. Examples of vinyl halides are vinyl chloride, vinyl fluoride and the like. Examples of vinyl carboxylate include vinyl acetate, vinyl pivalate, vinyl 2,2-dimethylbutanoate, vinyl 2,2-dimethylpentanoate, vinyl 2-methyl-2-butanoate, vinyl propionate, vinyl stearate, And vinyl 2-ethyl-2-methylbutanoate. Examples of the aromatic vinyl monomer include pt-butyl vinyl benzoate, N, N-dimethylamino vinyl benzoate, vinyl benzoate and the like. Examples of styrene derivatives include styrene, o-chlorostyrene, m-chlorostyrene, p-chlorostyrene, o-chloromethylstyrene, m-chloromethylstyrene, p-chloromethylstyrene, α-methylstyrene, and the like.
[0074]
Examples of vinyl ethers include ethyl vinyl ether, hydroxybutyl monovinyl ether, t-amyl vinyl ether, cyclohexane dimethanol methyl vinyl ether, and the like. Examples of alkyl vinyl ketones are methyl vinyl ketone, isobutyl vinyl ketone and the like. Examples of dienes are butadiene, isoprene and the like. Examples of (meth) acrylate include methyl (meth) acrylate, ethyl (meth) acrylate, butyl (meth) acrylate, 2-ethylhexyl (meth) acrylate, and phenyl (meth) acrylate. Examples of itaconates are dimethyl itaconate, diethyl itaconate, dibutyl itaconate, diisopropyl itaconate and the like. (Meth) acrylate is a general term for acrylate and methacrylate.
[0075]
Examples of fumaric acid diesters include diethyl fumarate, diisopropyl fumarate, dibutyl fumarate, dicyclohexyl fumarate, di (1-phenyl-2-propyl) fumarate, disec-butyl fumarate, di-t-butyl fumarate, Di-2-ethylhexyl fumarate, isopropyl fumarate ethyl, isopropyl fumarate propyl, isopropyl fumarate butyl, isopropyl fumarate sec-butyl, isopropyl fumarate t-butyl, isopropyl fumarate isoamyl, isopropyl fumarate = Sec-amyl, isopropyl fumarate = sec-hexyl, isopropyl fumarate = 4-methyl-2-pentyl, isopropyl fumarate = 2-ethylhexyl, isopropyl fumarate = octyl, isopropyl fumarate = cyclohexyl Isopropyl nonyl fumarate, t-butyl fumarate = sec-butyl, t-butyl fumarate = cyclohexyl, t-butyl fumarate = 4-methyl-2-pentyl, t-butyl fumarate = 2-ethylhexyl, fumaric acid Isopropyl = cyclohexyl, isopropyl fumarate = cyclopentyl, isopropyl fumarate = 2-phenyl-1-ethyl, isopropyl fumarate = 3-phenylpropyl, isopropyl fumarate = 1-phenyl-2-propyl, isopropyl fumarate = 1-phenyl -1-propyl, isopropyl fumarate = (trimethylsilyl) propyl, t-butyl fumarate = (trimethylsilyl) propyl, cyclohexyl fumarate = (trimethylsilyl) propyl, isopropyl fumarate = [3-tris (trimethylsiloxy) ) Silyl] propyl, isopropyl fumarate = 3- (pentamethyldisiloxanyl) propyl, N-fumarate, N-dimethylaminoethyl = isopropyl, t-butyl fumarate = 1-butoxy-2-propyl, fumaric acid 2 -Cyanoethyl isopropyl, 2-hydroxyethyl fumarate isopropyl, glycidyl fumarate isopropyl, isopropyl fumarate diethylphosphomethyl, 2-methylthioethyl fumarate isopropyl, isopropyl fumarate isopropyl 2-hydroxyethylthioethyl isopropyl Perfluorooctylethyl fumarate = isopropyl, trifluoromethyl fumarate = isopropyl, pentafluoroethyl fumarate = isopropyl, hexafluoroisopropyl fumarate = isopropyl, and the like.
[0076]
In order to further increase the ability of the polymer to form a film, a polyfunctional acrylate may be added. Preferred polyfunctional acrylates are 1,4-butanediol diacrylate, 1,6-hexanediol diacrylate, 1,9-nonanediol diacrylate, neopentyl glycol diacrylate, triethylene glycol diacrylate, dipropylene glycol diacrylate. , Tripropylene glycol diacrylate, tetraethylene glycol diacrylate, trimethylolpropane triacrylate, trimethylol EO-added triacrylate, pentaerythritol triacrylate, trisacryloyloxyethyl phosphate, bisphenol A EO added diacrylate, bisphenol A glycidyl And dialkyl ether diacrylate and polyethylene glycol diacrylate. Bisphenol A glycidyl ether diacrylate is commercially available as Biscoat 700 from Osaka Organic Chemicals, Inc.
[0077]
When two or more of these non-liquid crystalline monomers are used, two or more may be selected from the same type, or at least one may be selected from different types. The preferable addition amount of these monomers is 0.5 to 50 mol% in proportion to the compound (1). A preferable ratio for obtaining a sufficient film forming power is 0.5 mol% or more. A preferable ratio for the polymerizable composition to have liquid crystallinity is 50 mol or less.
[0078]
As another monomer, a polymerizable compound having a liquid crystal skeleton may be used. Examples of the polymerizable compound include an acrylic acid derivative (LC-1), a fumaric acid derivative (LC-2), a sorbic acid derivative (LC-3), a maleimide derivative (LC-4), and a crotonic acid derivative (LC-5). ). By using these polymerizable compounds, the temperature range of the liquid crystal phase of the obtained polymer can be adjusted.
[0079]
An example of (LC-1) is shown below.

[0080]
An example of (LC-2) is shown below. In these formulas, R ² Is an alkyl having 1 to 15 carbons, and R ³ Is methyl, ethyl, 2-methylbutyl, propyl, octyl, isopropyl, t-butyl, cyclohexyl, 4-butylcyclohexyl, norbornyl, or adamantyl, and y is an integer of 1 to 20.

[0081]
Next, examples of (LC-3) to (LC-5) will be described. Y in these formulas is an integer of 1 to 20.

[0082]
When two or more of these other monomers having a liquid crystalline skeleton are used, they may be selected from the same type, or at least one from each of different types. The preferred content of these monomers in the polymerizable composition is 0.5 to 95 mol% based on the total amount of the composition. A preferable ratio is 0.5 mol% or more because the liquid crystal temperature range can be adjusted. A preferable ratio for obtaining a copolymer is 95 mol% or less.
[0083]
When the polymer (2) is isolated, it can be dissolved in a solvent and molded. Preferred solvents used at this time are N-methyl-2-pyrrolidone, dimethyl sulfoxide, N, N-dimethylacetamide, N, N-dimethylformamide, N, N-dimethylacetamide dimethyl acetal, tetrahydrofuran, chloroform, 1,4-dioxane , Bis (methoxyethyl) ether, γ-butyrolactone, tetramethylurea, trifluoroacetic acid, ethyl trifluoroacetate, hexafluoro-2-propanol and the like. However, usable solvents are not limited to these. Mixtures of these solvents with common organic solvents such as acetone, benzene, toluene, heptane and methylene chloride can also be used.
[0084]
Since the polymer (2) has a liquid crystal property, it can be applied to various protective films, optical compensation films, optical writing recording materials, and the like. An example of the optical compensation film is a retardation film. Since the polymer (2) can be an optically anisotropic thin film, it can be used alone as a retardation film or can be combined with another retardation film. Then, this retardation film can be applied to a polarizing plate, a circularly polarizing plate, an elliptically polarizing plate, a color compensating plate, a visual compensating plate and the like. A polarizing plate, a circularly polarizing plate, an elliptically polarizing plate, a color compensator, a visual compensator and the like are also examples of the optical compensation film. The polymer obtained by photopolymerization from the compound (1) can be applied to a rubbingless alignment film by using polarized light in addition to the same uses as the polymer obtained by thermal polymerization.
[0085]
A retardation plate used for a liquid crystal display is prepared by dissolving the polymer (2) in an organic solvent, coating the transparent substrate on which alignment treatment has been performed, heating the glass to a temperature equal to or higher than the glass transition point, and then allowing it to cool. To form a uniformly oriented polymer thin film (optically anisotropic thin film). The transparent substrate is a glass plate or a polymer film. Examples of the polymer film include triacetyl cellulose, "ARTON" manufactured by JSR Corporation, "ZEONEX" and "ZEONOR" manufactured by ZEON CORPORATION, and "APEL" manufactured by Mitsui Chemicals, Inc. Preferred coating methods include a microgravure coating method, a gravure coating method, a wire barcode method, a dip coating method, a spray coating method, and a meniscus coating method.
[0086]
The thickness of the optically anisotropic thin film differs depending on the desired retardation value, and the retardation value varies depending on the birefringence of the optically anisotropic thin film. Preferred retardation values are in the range of about 0.05 to 50 μm, and more preferred retardation values are in the range of about 0.1 to 20 μm. Further, a more preferable retardation value is in a range of about 0.5 to 10 μm. The haze value of the optically anisotropic thin film is 1.5% or less, more preferably 1.0% or less, and the transmittance is 80% or more, more preferably 85% or more. It is preferable that the transmittance satisfies these ratios in the visible light region. A haze value range of 1.5% or less is a preferable condition so as not to cause a problem in polarization performance. When the optically anisotropic thin film is used for a liquid crystal display device, a transmittance range of 80% or more is a preferable condition for maintaining brightness.
[0087]
【Example】
Hereinafter, the present invention will be described in detail with reference to examples. At the phase transition temperatures described in the examples, C is a crystal, N is a nematic phase, Ch is a cholesteric phase, SmA is a smectic A phase, SmX is an unidentified smectic phase, I is an isotropic liquid, and Tm is a polymer. Is shown. The weight average molecular weight (Mw) and polydispersity (Mw / Mn) of the polymer were measured by GPC (gel permeation chromatography) (converted from a standard polystyrene having a known molecular weight using a column having an exclusion limit of 10 million). Calculated from Note that the unit symbol L indicates liter.
[0088]
Example 1
(1-1a) Production of Maleimide Furan Adduct [a]
To a solution of maleimide (275 g) in diethyl ether (3.5 L) was added furan (1 L) and the mixture was refluxed for 48 hours. During this time, crystals were deposited around the reactor as the reaction proceeded. When the reflux was stopped and the mixture was allowed to stand at room temperature (20 ° C.) for 1 day, crystals were further precipitated. The crystals were filtered and dried under reduced pressure to obtain maleimide furan adduct [a] (434 g).
Melting point: 130-132 ° C
(1-1b) Production of tetrahydrophthalimide-N-ethyl alcohol
Ethanolamine (10 g) was added to a solution of tetrahydrophthalic acid (25 g) in toluene (50 ml), and azeotropic distillation was carried out using a Dean Stark while refluxing to remove water. The reaction was stopped when the mixture was refluxed until no more water came out. When all toluene was distilled off, 30 g of tetrahydrophthalimide-N-ethyl alcohol was obtained. The melting point was 70 ° C.
[0089]
(1-2) Production of liquid crystal skeleton (1)
(I) 4- (Trans-4-n-propylcyclohexyl) phenol (30 g), 6-bromohexanol (27.3 g) and potassium carbonate (39 g) were added to dimethylformamide (300 ml) and stirred at 90 ° C. for 3 hours. did. White crystals precipitated by pouring the reaction solution into 1 L of 3N hydrochloric acid were separated by filtration. The obtained crystals were thoroughly washed with water and dried to obtain 4- (trans-4-n-propylcyclohexyl)-(6-hydroxyhexyloxy) benzene (32 g). Its phase transition temperature was C 61 SmX 69 I.
[0090]
The following compounds were produced in the same manner as described above.
(Ii) 4- (trans-4-n-propylcyclohexyl)-(3-hydroxypropyloxy) benzene: C room temperature or less SmX 68 I
(Iii) 2- (4-n-nonyloxyphenyl) -5- (8-hydroxyoctyloxy) pyrimidine: C 53 SmX 87 I
(Iv) 4- (4-n-pentylphenylethynyl)-(6-hydroxyhexyloxy) benzene: C82N92.6I
(V) 2- (hydroxyhexyloxy) -6- (4-n-pentylphenylethynyl) naphthalene: C 115 N 140 I
(Vi) 2- (6-hydroxyheptyloxy) -6- (4-propylphenyl) naphthalene: melting point 147 ° C.
(Vii) 4- [4- (trans-4-n-propylcyclohexyl) cyclohexyl] -1- (6-hydroxyhexyloxy) benzene
: C 188 N 199.7 I
(Viii) 2- (4-hexylphenyl) -5- [4- (6-hydroxyhexyloxy) phenyl] pyridine: C 180 SmA 200 N 203 I
[0091]
(1-3a) Production of maleimide derivative 1
Maleimide furan adduct [a] (15 g), (ii) 4- (trans-4-n-propylcyclohexyl)-(3-hydroxypropyloxy) benzene (10 g), triphenylphosphine (14.4 g) And a solution of tetrahydrofuran (200 ml) at 0 ° C. was added to a 40% toluene solution of diethyl azodicarboxylate at 27 ° C., and the mixture was stirred at room temperature for 12 hours. Water (50 ml) and ethyl acetate (200 ml) were added for liquid separation, and the organic layer was dried over anhydrous magnesium sulfate. Toluene (200 ml) was added to the residue obtained by distilling off the solvent, and the mixture was refluxed for 12 hours. The residue obtained by distilling off toluene was purified by silica gel chromatography and recrystallized from ethanol to give 7.5 g of N- [3- [4- (trans-4-n-propylcyclohexyl) phenyloxy]. Propyl] maleimide (Compound No. 3) was obtained.

[0092]
<Measured value of proton NMR>
¹ H-NMR (CDCl ₃ , 90 MHz): δ (ppm): 0.89 (3H, t, J = 6 Hz) 1.21 to 2.00 (16H, m), 3.52 (2H, t, J = 6.3 Hz), 3 .90 (2H, t, J = 6.3 Hz), 6.67 (2H, s), 6.79 (2H, d, J = 9 Hz), 7.11 (2H, d, J = 9 Hz)
Melting point: 98 ° C
[0093]
(1-3b) Production of maleimide derivative 2
Diethyl azodicarboxylate is added to a solution consisting of tetrahydrophthalimide-N-ethyl alcohol (10 g), 4- (trans-4-n-propylcyclohexyl) phenol (11 g), triphenylphosphine (14.6 g), and tetrahydrofuran (200 ml). Was added at 0 ° C. and stirred at room temperature for 12 hours. Water (50 ml) and ethyl acetate (200 ml) were added for liquid separation, and the organic layer was dried over anhydrous magnesium sulfate. The residue obtained by distilling off toluene was purified by silica gel chromatography and recrystallized from ethanol to give 6 g of N- [3- [4- (trans-4-n-propylcyclohexyl) phenyloxy] ethyl]. Thus, tetrahydrophthalimide (Compound No. 120) was obtained.

Example 2
The following maleimide derivative was produced according to the method of Example 1.
(I) Compound No. 8
N- [6- [4- (trans-4-n-propylcyclohexyl) phenyloxy] hexyl] maleimide

¹ H-NMR (CDCl ₃ , 90 MHz): δ (ppm): 0.89 (3H, t, J = 6 Hz) 1.21 to 2.00 (22 H, m), 3.52 (2H, t, J = 6.3 Hz), 3 .91 (2H, t, J = 6.3 Hz), 6.67 (2H, s), 6.79 (2H, d, J = 9 Hz), 7.11 (2H, d, J = 9 Hz)
Melting point: 69 ° C
[0094]
(Ii) Compound No. 30
N- [8- [2- (4-nonyloxyphenyl) pyrimidin-5-yloxy] octyl] maleimide

¹ H-NMR (CDCl ₃ , 90 MHz): δ (ppm): 0.88 (3H, t, J = 6 Hz), 1.2 to 2.0 (26 H, m), 3.51 (2H, t, J = 6.3 Hz), 4.01 (2H, t, J = 6.3 Hz), 4.14 (2H, t, J = 6.3 Hz), 6.68 (2H, s), 6.96 (2H, d, J = 9 Hz) ), 8.28 (2H, d, J = 9 Hz), 8.42 (2H, s)
Melting point: 79 ° C
[0095]
(Iii) Compound No. 44
N- [6- [4- (4-n-pentylphenylethynyl) phenyloxy] hexyl] maleimide

¹ H-NMR (CDCl ₃ , 90 MHz): δ (ppm): 0.89 (3H, t, J = 6 Hz), 1.2 to 1.9 (14H, m), 2.60 (2H, t, J = 8 Hz), 3. 53 (2H, t, J = 8 Hz), 3.95 (2H, t, J = 8 Hz), 6.67 (2H, S), 6.83 (2H, d, J = 9.0 Hz), 7. 13 (2H, d, J = 9.0 Hz), 7.42 (2H, d, J = 9.0 Hz), 7.43 (2H, d, J = 9.0 Hz)
Melting point: 82 ° C
[0096]
(Iv) Compound No. 65
N- [6- [2- (4-propylphenyl) naphthalen-6-yloxy] hexyl] maleimide

¹ H-NMR (CDCl ₃ , 90 MHz): δ (ppm): 0.98 (3H, t, J = 6 Hz), 1.30 to 2.00 (10H, m), 2.65 (2H, t, J = 8 Hz), 3. 54 (2H, t, J = 8 Hz), 4.07 (2H, t, J = 8 Hz), 6.67 (2H, s), 7.10 to 7.31 (m), 7.57 to 7.5. 94 (m)
Melting point: 129 ° C
[0097]
(V) Compound No. 66
N- [6- [2- (4-n-pentylphenylethynyl) naphthalen-6-yloxy] hexyl] maleimide

¹ H-NMR (CDCl ₃ , 90 MHz): δ (ppm): 0.89 (3H, t, J = 6 Hz), 0.80 to 2.00 (14H, m), 2.62 (2H, t, J = 8 Hz), 3. 54 (2H, t, J = 8 Hz), 4.06 (2H, t, J = 8 Hz), 6.67 (2H, s), 7.08 to 7.20 (4H, m), 7.42 to 7.73 (5H, m), 7.95 (1H, s)
Melting point: 105 ° C
[0098]
(Vi) Compound No. 73
N- [6- [4- [4-trans- (trans-4-n-propylcyclohexyl) cyclohexyl] phenyloxy] hexyl] maleimide

¹ H-NMR (CDCl ₃ , 90 MHz): δ (ppm): 0.87 (3H, t, J = 6 Hz), 0.80 to 2.00 (m), 3.52 (2H, t, J = 8 Hz), 3.90 ( 2H, t, J = 8 Hz), 6.67 (2H, s), 6.83 (2H, d, J = 9 Hz), 7.10 (2H, d, J = 9 Hz)
Melting point: 155.5 ° C
[0099]
(Vii) Compound No. 83
N- [6- [4- [2- (4-hexylphenyl) pyridin-5-yl] phenyloxy] hexyl] maleimide

¹ H-NMR (CDCl ₃ , 90 MHz): δ (ppm): 0.88 (3H, t, J = 6 Hz), 1.20 to 2.00 (16H, m), 2.67 (2H, t, J = 8 Hz), 3. 53 (2H, t, J = 8 Hz), 3.99 (2H, t, J = 8 Hz), 6.67 (2H, s), 6.99 (2H, d, J = 9 Hz), 7.29 ( 2H, d, J = 7.2 Hz), 7.55 (2H, d, J = 9 Hz), 7.77 to 7.99 (4H, m), 8.88 (1H, J = 1.3 Hz)
Melting point: 148 ° C
[0100]
(Viii) Compound No. 88
N- [6- [4- (4'-n-propylbiphenyloxycarbonyl) phenyloxy] hexyl] maleimide

¹ H-NMR (CDCl ₃ , 90 MHz): δ (ppm): 0.97 (3H, t, J = 7.3 Hz), 1.20 to 2.00 (10H, m), 2.64 (2H, t, J = 8 Hz), 3.54 (2H, t, J = 8 Hz), 4.04 (4H, t, J = 8 Hz), 6.68 (2H, s), 6.94 (2H, J = 9 Hz), 7.15- 7.40 (4H, m), 7.40 to 7.75 (4H, m), 8.15 (2H, J = 9 Hz)
Phase transition temperature: C 127 N 135.3 I
[0101]
(Ix) Compound No. 89
N- [6- [4- (4'-cyanobiphenyloxycarbonyl) phenyloxy] hexyl] maleimide

¹ H-NMR (CDCl ₃ , 90 MHz): δ (ppm): 1.20 to 2.00 (8H, m), 3.54 (2H, t, J = 8 Hz), 4.04 (4H, t, J = 8 Hz), 6. 68 (2H, s), 6.97 (2H, J = 9 Hz), 7.31 (2H, J = 9 Hz), 7.60 (2H, J = 9 Hz), 7.70 (4H, m), 8 .15 (2H, J = 9Hz)
Phase transition temperature: C 111 N 202 I
[0102]
Example 3
<Production of maleimide polymer by radical polymerization>
(I) Compound No. Polymerization of 3
Compound No. 3 (0.6 g), azobisisobutyronitrile (AIBN; 0.0041 g) and tetrahydrofuran (2 ml) were placed in an ampoule, cooled to -60 ° C, sufficiently degassed by a vacuum pump, and sealed. The sealed ampule was reacted at 70 ° C. for 48 hours. The contents in the ampoule were dissolved in tetrahydrofuran (10 ml) and poured into methanol (100 ml) to precipitate. After this operation was performed three times, the resultant was sufficiently washed with methanol and dried under reduced pressure to obtain 0.4 g of a polymer [P1].
Weight average molecular weight (M _W ): 34,000
Polydispersity (Mw / Mn): 1.44
Phase transition temperature: Tm 200 N 250 I
The polymer [P1] was a polymer having a nematic liquid crystal phase.
The polymer [P1] was placed outdoors to expose to sunlight, and a light resistance test was conducted. As a result, the polymer [P1] was not cloudy or colored even after one month. That is, deterioration of the polymer [P1] due to sunlight was not confirmed.
[0103]
(Ii) Compound No. 30 polymerizations
Compound No. Compound No. 30 (2 g) and AIBN (0.0024 g) were reacted at 70 ° C. for 72 hours. By the same operation as in the polymerization of 3, 0.35 g of a polymer [P2] was obtained.
Weight average molecular weight (Mw): 33,000
Polydispersity (Mw / Mn): 1.46
Phase transition temperature: Tm 60 SmX 130 I
The polymer [P2] was a polymer having a smectic liquid crystal phase.
[0104]
(Iii) Compound No. 65 polymerization
Compound No. Compound No. 65 (0.34 g), AIBN (0.0019 g), and tetrahydrofuran (1.5 ml) were reacted at 70 ° C. for 48 hours, except that Compound No. 65 was used. By the same operation as in the polymerization of No. 3, 0.2 g of a polymer [P3] was obtained.
Weight average molecular weight (Mw): 36,000
Polydispersity (Mw / Mn): 1.43
Phase transition temperature: Tm 165 N 214 I
The polymer [P3] was a polymer having a nematic liquid crystal phase.
[0105]
(Iv) Compound No. 73 polymerization
Compound No. Compound No. 73 (0.4 g), AIBN (0.002 g), and tetrahydrofuran (3 ml) were reacted at 70 ° C. for 48 hours. By the same operation as in the polymerization of 3, 0.31 g of polymer [P4] was obtained.
Weight average molecular weight (Mw): 38,000
Polydispersity (Mw / Mn): 1.40
Phase transition temperature: Tm 240 N 280 I
The polymer [P4] was a polymer having a nematic liquid crystal phase.
[0106]
(V) Compound No. 83 polymerization
Compound No. Compound No. 83 (0.45 g), AIBN (0.0022 g), and tetrahydrofuran (3 ml) were reacted at 70 ° C. for 48 hours. By the same operation as in the polymerization of 3, 0.4 g of a polymer [P5] was obtained.
Weight average molecular weight (Mw): 16,000
Polydispersity (Mw / Mn): 1.43
Phase transition temperature: Tm 175 SmX 290 ° C or higher I
(The clearing point could not be measured beyond the measurement limit of the measuring instrument)
The polymer [P5] was a polymer having a smectic phase.
[0107]
Example 4
<Production of maleimide polymer by anionic polymerization>
(I) Compound No. Polymerization of 44
Compound No. A solution of 44 (0.5 g) in tetrahydrofuran (2 ml) was cooled to −10 ° C., and 0.027 ml of a hexane solution of n-butyllithium (concentration: 1.56 mol / l) was added thereto, and the temperature was maintained at 10 ° C. for 8 hours. Stirred. The reaction solution was poured into methanol (100 ml) to stop the reaction, and reprecipitated twice with methanol (100 ml) for purification. After drying under reduced pressure for 2 days, 0.4 g of a polymer [P6] was obtained. Weight average molecular weight (M _W ): 33,000
Polydispersity (Mw / Mn): 1.23
Phase transition temperature: Tm 210 N 260 I
The polymer [P6] was a polymer having a nematic liquid crystal phase at room temperature.
[0108]
(Ii) Compound No. Polymerization of 66
Compound No. Compound No. 66 (1 g) was reacted with 0.039 ml of a hexane solution of n-butyllithium (concentration: 1.56 mol / l) and tetrahydrofuran (6 ml) at -10 ° C for 8 hours. By the same operation as in the polymerization of No. 44, 0.52 g of polymer [P7] was obtained.
Weight average molecular weight (Mw): 37,000
Polydispersity (Mw / Mn): 1.26
Phase transition temperature: Tm 230 N 290 ° C or higher I
(The clearing point could not be measured beyond the measurement limit of the measuring instrument)
The polymer [P7] was a polymer exhibiting a nematic liquid crystal phase.
[0109]
As can be seen from the results of the above examples, the polymer (2) obtained by homopolymerization of the compound (1) is a liquid crystal polymer and has a higher clearing point than a conventional acrylic polymer. For this reason, it can be suitably used for a material such as a retardation plate that requires a heat-resistant polymer having a clearing point of 120 ° C. or higher.
[0110]
Example 5
<Production of cholesteric polymer by copolymerization>
Compound No. Take 65 (0.2 g), optically active maleimide (OPM-5) (0.04 g), AIBN (0.0013 g), and tetrahydrofuran (2 ml) in an ampoule, cool to −60 ° C., and sufficiently deaerate with a vacuum pump. Done and sealed. The sealed ampule was reacted at 70 ° C. for 48 hours. The contents in the ampoule were dissolved in tetrahydrofuran (10 ml) and poured into methanol (100 ml) to precipitate. After performing this operation three times, the resultant was sufficiently washed with methanol and dried under reduced pressure to obtain 0.1 g of a polymer [CP1]. The copolymerization ratio calculated from the 500 Hz proton NMR measurement was as follows: 65: OPM-5 = 73: 27.
Weight average molecular weight (M _W ): 20,000
Polydispersity (Mw / Mn): 1.40
Phase transition temperature: Tm 130 Ch 137 I
The polymer [CP1] was a polymer exhibiting a cholesteric liquid crystal phase.
[0111]
Example 6
<Manufacture of optical compensation film>
The polymer [P1] produced in Example 3 was dissolved in N-methylpyrrolidone to prepare a solution having a [P1] content of 20% by weight. This solution was applied to a glass substrate having a rubbing polyimide film by spin coating, and the solvent was removed by evaporation. Thereafter, a heat treatment was performed at 220 ° C. for 30 minutes, and after the heat treatment, the orientation was fixed by cooling. The obtained film on the glass substrate was oriented in the same direction as the rubbing direction, and was a uniform (0.5 μm) film without alignment defects.
[0112]
Example 7
<Production of maleimide polymer film by photopolymerization>
Compound No. 3 (100 mg) and a photopolymerization initiator 2-hydroxy-2-methyl-1-phenylpropan-1-one (4 mg). A cell was prepared by laminating a plate made of polyfluoroethylene and a glass plate so that the cell gap became 50 microns. The above composition was injected into this cell at 100 ° C. High pressure mercury lamp (120W / cm ² ), And ultraviolet rays were irradiated from the glass surface side for 10 minutes while maintaining the same temperature. After the irradiation, the cell was returned to room temperature, and the glass plate and the plate made of polyfluoroethylene were separated to obtain a film. This film was transparent without unevenness. The weight average molecular weight of this polymer was 55,000. The pencil hardness test showed 3H, indicating that the hardness was high.
[0113]
Example 8
<Manufacture of liquid crystal alignment film>
The polymer [P1] was dissolved in chloroform to prepare a 1% by weight solution. This solution was spin-coated on a glass substrate having an ITO film, and then sufficiently dried to obtain a thin film (thickness: 30 nm). Then, an alignment treatment by rubbing was performed to produce a liquid crystal display element for twisted nematic. A polarizing plate was attached, and the liquid crystal orientation and electrical response were examined. As a result, the liquid crystal was uniformly aligned, and it was found that the polymer of the present invention was excellent as an alignment film. It was also found that the optical response to an electric field was fast and that the liquid crystal display element was excellent.
[0114]
【The invention's effect】
The maleimide derivative (1) of the present invention has high polymerization reactivity, and a high molecular weight polymer can be obtained by the polymerization reaction. The polymer (2), which is a homopolymer or a copolymer of the compound (1), exhibits liquid crystallinity, and has several properties such as heat resistance, light resistance, hardness, transparency, orientation, and applicability to a substrate. Has improved physical properties. The polymer (2) can be used for an optical compensation film such as a retardation film, a liquid crystal alignment film, an optical writing recording material, and the like.

Claims (15)

A maleimide derivative represented by the formula (1).

In the formula (1), R ¹ represents hydrogen, halogen, —CN, —CF ₃ , —CF ₂ H, —CFH ₂ , —OCF ₃ , —OCF ₂ H, —NCO, —NCS or C 1-20. alkyl, any _-CH 2 in the alkyl - is, -O -, - S -, - COO -, - OCO -, - CO -, - replaced by CH = CH- or -C≡C- at best, any hydrogen in the alkyl halogen or may be replaced by -CN; alkyl of R ² and R ³ are independently hydrogen, phenyl or 1 to 20 carbon atoms, in the alkyl arbitrary _-CH 2 -, -O -, - S -, - COO -, - OCO -, - CO -, - CH = CH-, or -C≡C-, the alkyl in Is replaced by halogen or -CN At best, and in the case of the alkyl both ^{R 2} and ^{R 3,} the terminal alkyl may combine with each other to form a ^ring; A 1, ^{A 2} and ^{A 3} are independently 1,4 Cyclohexylene, 1,4-cyclohexylene in which at least one hydrogen is replaced by fluorine, 1,4-cyclohexenylene, 1,4-phenylene, at least one hydrogen being replaced by halogen, methyl or trifluoromethyl 1,4-phenylene, pyridine-2,5-diyl, pyridazine-3,6-diyl, pyrimidine-2,5-diyl, naphthalene-2,6-diyl, 1,2,3,4-tetrahydronaphthalene -2,6-diyl, 5,6,7,8-tetrahydronaphthalene-2,6-diyl, fluorene-2,7-diyl, 9-methyl-fluorene-2,7-diyl Or 1,3-dioxane-2,5-diyl; Z ¹ and Z ² are independently a single bond or an alkylene having 1 to 20 carbon atoms, and any -CH _2- in the alkylene is- O—, —COO—, —OCO—, —CH ＝ CH—, —CF ＝ CF—, —CF ₂ O—, —OCF ₂ — or —C≡C—. Any hydrogen may be replaced by halogen; m is 1 or 0 and n is an integer from 1 to 20. Provided that when m is 0, A ¹ and A ² are 1,4-phenylene, and Z ¹ is a single bond, R ¹ is not —CN. In the formula (1), R ¹ is hydrogen, fluorine, chlorine, —NCO or alkyl having 1 to 20 carbon atoms, and any —CH ₂ — in the alkyl is —O—, —S—, —COO -, - OCO- or -CO- may be replaced, and any hydrogen in the alkyl may be replaced by halogen; ^{R 2} and ^{R 3} are independently hydrogen, number phenyl or carbon 1-4 And when R ² and R ³ are both alkyl, the ends of the alkyl may combine to form a ring; A ¹ , A ² and A ³ are independently 1,4- Cyclohexylene, 1,4-cyclohexylene wherein at least one hydrogen is replaced by fluorine, 1,4-cyclohexenylene, 1,4-phenylene, wherein at least one hydrogen is halogen, methyl or trifluoromethyl Substituted 1,4-phenylene, pyridine-2,5-diyl, pyridazine-3,6-diyl, pyrimidine-2,5-diyl, naphthalene-2,6-diyl, 1,2,3,4-tetrahydro Naphthalene-2,6-diyl, 5,6,7,8-tetrahydronaphthalene-2,6-diyl, fluorene-2,7-diyl, 9-methyl-fluorene-2,7-diyl or 1,3-dioxane -1,5-diyl; Z ¹ and Z ² are independently a single bond, —COO—, —OCO—, —CF ₂ O—, —OCF ₂ —, —CH ₂ O—, —OCH ₂ -, - CH = CH -, - CH 2 CH 2 - or a -C≡C-; m is 1 or 0, and n is an integer from 1 to 20, the maleimide derivative according to claim 1 . The maleimide derivative according to claim 1, wherein m is 0. The maleimide derivative according to claim 1, wherein m is 1. A polymerizable composition containing at least two polymerizable compounds, at least one of which is the maleimide derivative according to claim 1. The polymerizable composition according to claim 5, wherein all of the polymerizable compound is the maleimide derivative according to claim 1. 6. The polymerizable composition according to claim 5, comprising at least one of the maleimide derivative according to claim 1 and at least one other polymerizable compound. A polymer having a structural unit represented by the formula (2).

In the formula (2), R ¹ represents hydrogen, halogen, —CN, —CF ₃ , —CF ₂ H, —CFH ₂ , —OCF ₃ , —OCF ₂ H, —NCO, —NCS or C 1-20. alkyl, any _-CH 2 in the alkyl - is, -O -, - S -, - COO -, - OCO -, - CO -, - replaced by CH = CH- or -C≡C- at best, any hydrogen in the alkyl halogen or may be replaced by -CN; alkyl of R ² and R ³ are independently hydrogen, phenyl or 1 to 20 carbon atoms, in the alkyl arbitrary _-CH 2 -, -O -, - S -, - COO -, - OCO -, - CO -, - CH = CH- or -C≡C-, in the alkyl Any hydrogen is replaced by halogen or -CN Even better, and when ^{R 2} and ^{R 3} are alkyl both ends of the alkyl may be bonded to form a ^ring; A 1, ^{A 2} and ^{A 3} are independently 1,4-cyclohexylene Hexylene, 1,4-cyclohexylene, 1,4-cyclohexenylene, 1,4-phenylene, wherein at least one hydrogen is replaced by fluorine, at least one hydrogen is replaced by halogen, methyl or trifluoromethyl 1,4-phenylene, pyridine-2,5-diyl, pyridazine-3,6-diyl, pyrimidine-2,5-diyl, naphthalene-2,6-diyl, 1,2,3,4-tetrahydronaphthalene- 2,6-diyl, 5,6,7,8-tetrahydronaphthalene-2,6-diyl, fluorene-2,7-diyl, 9-methyl-fluorene-2,7-diyl and the like. Or 1,3-dioxane-2,5-diyl; Z ¹ and Z ² are independently a single bond or an alkylene having 1 to 20 carbon atoms, wherein any -CH _2- in the alkylene is , —O—, —COO—, —OCO—, —CH ＝ CH—, —CF ＝ CF—, —CF ₂ O—, —OCF ₂ — or —C≡C—, the alkylene Any hydrogen therein may be replaced by halogen; m is 1 or 0, and n is an integer from 1 to 20. Provided that when m is 0, A ¹ and A ² are 1,4-phenylene, and Z ¹ is a single bond, R ¹ is not —CN. In the formula (2), R ¹ is hydrogen, fluorine, chlorine, —NCO, or alkyl having 1 to 20 carbons, and any —CH ₂ — in the alkyl is —O—, —S—, —COO—. , may be replaced by -OCO- or -CO-, arbitrary in the alkyl hydrogen may be replaced by halogen; ^{R 2} and ^{R 3} are independently hydrogen, phenyl or 1 to 4 carbon atoms When R ² and R ³ are both alkyl, the ends of the alkyl may combine to form a ring; A ¹ , A ² and A ³ are independently 1,4-cycloalkyl Hexylene, 1,4-cyclohexylene in which at least one hydrogen is replaced by fluorine, 1,4-cyclohexenylene, 1,4-phenylene, wherein at least one hydrogen is halogen, methyl or trifluoromethyl Substituted 1,4-phenylene, pyridine-2,5-diyl, pyridazine-3,6-diyl, pyrimidine-2,5-diyl, naphthalene-2,6-diyl, 1,2,3,4- Tetrahydronaphthalene-2,6-diyl, 5,6,7,8-tetrahydronaphthalene-2,6-diyl, fluorene-2,7-diyl, 9-methyl-fluorene-2,7-diyl or 1,3- There dioxane-2,5-diyl; ^{Z 1} and ^{Z 2} are each independently a single _{bond, -COO -, - OCO -,} - CF 2 O -, - OCF 2 -, - CH 2 O -, - OCH _{2 -, - CH = CH -} , - CH 2 CH 2 - or a -C≡C-; m is 1 or 0, and n is an integer from 1 to 20, weight according to claim 8 United. The polymer according to claim 8, which is obtained by homopolymerizing one of the maleimide derivatives according to claim 1. The polymer according to claim 8, obtained from the polymerizable composition according to claim 6. The polymer according to claim 8, obtained from the polymerizable composition according to claim 7. An optical compensation film containing the polymer according to claim 8. An optical writing recording material containing the polymer according to claim 8. A liquid crystal alignment film containing the polymer according to claim 8.