JP2003270440A - Method for producing polarizer, polarizer, polarizing plate and image display device - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a method for manufacturing a polarizer comprising a polyvinylalcohol film dyed with iodine and uniaxially stretched in an aqueous solution of boric acid, by which a drying process can be easily carried out without decreasing optical characteristics. <P>SOLUTION: The method for manufacturing a polarizer features that an unstretched polyvinylalcohol film is subjected to dyeing with iodine, then to uniaxial stretching in an aqueous solution of boric acid, to impregnation treatment with iodine ion and further to immersion treatment in an alcohol liquid. <P>COPYRIGHT: (C)2003,JPO

Description

Detailed Description of the Invention

[0001]

TECHNICAL FIELD The present invention relates to a method for producing a polarizer and a polarizer obtained by the production method. Further, the present invention provides a polarizing plate using the polarizer, and further a liquid crystal display device, an organic EL display device, a PD using the polarizing plate.
The present invention relates to image display devices such as P and CRT.

[0002]

2. Description of the Related Art As a polarizer used for a liquid crystal display device or the like, a polyvinyl alcohol film dyed with iodine is used because it has both a high transmittance and a polarization degree. In addition, the polarizer is usually used as a polarizing plate having a protective film such as a triacetyl cellulose film attached to one side or both sides thereof. The polarizing plate for displaying images in such a liquid crystal display device is required to have optical characteristics such that white display becomes whiter and black display becomes blacker as color display characteristics.

Conventionally, the above-mentioned polarizer has been produced, for example, by subjecting an unstretched polyvinyl alcohol film to an iodine dyeing treatment, and then uniaxially stretching it in a boric acid aqueous solution. When the above-mentioned optical characteristics of the polarizing plate are produced by the wet treatment as described above, the iodine ion concentration in the treatment bath affects the optical characteristics of the polarizer, and the drying treatment after the treatment also results in the optical characteristics of the polarizer. Affect the properties. In particular, a polarizer produced by a wet process has a large change in hue when the water content is high, and therefore the water content of the polarizer is usually 1 or less.
Drying is performed so as to be 0 to 30% by weight. Generally 3
Heat treatment at 0 to 50 ° C. is performed. However, when the heat treatment is performed, the hue of the polarizer becomes yellow in white display and red in black display due to the influence of heat during drying. On the other hand, if you do not heat treatment and room temperature drying, it takes time to dry,
Moreover, since the water content of the polarizer cannot be sufficiently reduced, the problem of hue change cannot be solved.

[0004]

DISCLOSURE OF THE INVENTION The present invention is a method for producing a polarizer composed of a polyvinyl alcohol film dyed with iodine and uniaxially stretched in an aqueous boric acid solution, without impairing the optical characteristics. It is an object of the present invention to provide a method for producing the above-mentioned polarizer, which can be easily dried. Another object is to provide a polarizer obtained by the manufacturing method, a polarizing plate using the polarizer, and an image display device using the polarizing plate.

[0005]

Means for Solving the Problems As a result of intensive studies to solve the above-mentioned problems, the present inventors have found that the above-mentioned object can be achieved by the method for producing a polarizer described below, and thus the present invention is completed. I arrived.

That is, according to the present invention, an unstretched polyvinyl alcohol film is subjected to an iodine dyeing treatment, then uniaxially stretched in a boric acid aqueous solution, then subjected to an iodine ion impregnation treatment, and further subjected to an alcohol liquid immersion treatment. A method of manufacturing a polarizer, comprising:

In the above-mentioned method for producing a polarizer of the present invention, since it has an alcohol solution immersion treatment, the subsequent drying treatment of the polarizer can be completed at a low temperature in a short time, and the polarizer is desired. The water concentration can be adjusted. Since the drying treatment of the polarizer can be performed at 30 ° C. or lower,
There is no problem of the hue change of the polarizer due to the heat treatment. Further, the water content of the polarizer can be adjusted to 20% by weight or less in a short time. The water content of the polarizer is 6 to 20% by weight, especially 6 to 12
It is preferable to adjust the content to the weight% because there is little change in hue.

Further, in the above-mentioned method for producing a polarizer, after uniaxially stretching treatment in a boric acid aqueous solution, iodine ion impregnation treatment is carried out, and then alcohol solution immersion treatment is further carried out. It is preferable to perform the iodine ion impregnation treatment from the viewpoint of optical characteristics such as the orthogonal transmittance of the polarizer and the degree of polarization, and it is particularly preferable to perform the iodine ion impregnation treatment at the above stage from the viewpoint of controlling the hue of the polarizer. .

The present invention also relates to the polarizer obtained by the above manufacturing method. The present invention also relates to a polarizing plate in which a transparent protective layer is provided on at least one surface of the polarizer. Furthermore, the present invention relates to an image display device using at least one of the polarizing plates.

[0010]

BEST MODE FOR CARRYING OUT THE INVENTION Polyvinyl alcohol or its derivative is used as the material of the polyvinyl alcohol film applied to the polarizer of the present invention. Examples of the derivative of polyvinyl alcohol include polyvinyl formal, polyvinyl acetal, and the like, olefins such as ethylene and propylene, acrylic acid, methacrylic acid, unsaturated carboxylic acids such as crotonic acid, and alkyl esters thereof.
Examples include those modified with acrylamide. Polyvinyl alcohol having a degree of polymerization of about 1000 to 10,000 and a degree of saponification of about 80 to 100 mol% is generally used.

The polyvinyl alcohol-based film may contain additives such as a plasticizer. Examples of the plasticizer include polyols and condensates thereof, such as glycerin, diglycerin, and triglycerin. Examples thereof include ethylene glycol, propylene glycol and polyethylene glycol. The amount of the plasticizer used is not particularly limited, but is 20 in the polyvinyl alcohol film.
It is preferable that the content is not more than wt%.

The polyvinyl alcohol film (unstretched film) is first subjected to iodine dyeing treatment.
The iodine dyeing treatment is generally performed by immersing the polyvinyl alcohol film in an iodine solution. When an aqueous iodine solution is used as the iodine solution, an aqueous solution containing iodine and iodine as a dissolution aid such as potassium iodide is used. The iodine concentration is about 0.01 to 0.5% by weight, preferably 0.1.
02-0.4% by weight, and the potassium iodide concentration is 0.
It is preferable to use about 01 to 10% by weight, more preferably 0.02 to 8% by weight.

In the iodine dyeing treatment, the temperature of the iodine solution is usually about 20 to 50 ° C, preferably 25 to 40 ° C.
Is. The immersion time is usually about 10 to 300 seconds, preferably 20 to 240 seconds. The content of iodine in the polyvinyl alcohol-based film (stretched film) is usually about 1 to 4% by weight, preferably 1.5 to 3.5% by weight so that the polarizer exhibits a good degree of polarization. It is preferable to adjust so that In the iodine dyeing treatment, the iodine content in the polyvinyl alcohol-based film is adjusted to be in the above range by adjusting the conditions such as the concentration of the iodine solution, the immersion temperature of the polyvinyl alcohol-based film in the iodine solution, and the immersion time. Is preferred.

Next, uniaxial stretching treatment is performed in a boric acid aqueous solution. The boric acid concentration in the boric acid aqueous solution is 2 to 15% by weight.
It is about 3 to 10% by weight, preferably. Iodine ions can be added to the boric acid aqueous solution by potassium iodide. A boric acid aqueous solution containing potassium iodide can give a polarizer with little coloring, that is, a so-called neutral gray polarizer having an almost constant absorbance over almost the entire wavelength range of visible light.

The temperature of the boric acid aqueous solution is, for example, 50 ° C. or higher,
It is preferably in the range of 50 to 85 ° C. The immersion time is usually 100 to 1200 seconds, preferably 150 to 600 seconds.
Seconds, more preferably about 200 to 500 seconds.

The uniaxial stretching method in the boric acid aqueous solution is not particularly limited, and a roll stretching method, a tenter stretching method and the like can be adopted. The stretching can be performed in multiple stages. Normal,
An unstretched film having a thickness of about 30 to 150 μm is used. The stretch ratio of the stretched film can be appropriately set according to the purpose, but the stretch ratio is about 2 to 7 times, preferably 3 to
It is desirable to set it to 6.5 times, more preferably 3.5 to 6 times. The thickness of the stretched film is preferably about 5 to 40 μm.

Next, it is preferable to carry out an iodine ion impregnation treatment. For the iodine ion impregnation treatment, for example, an aqueous solution containing iodine ions with potassium iodide or the like is used. The potassium iodide concentration is preferably about 0.5 to 10% by weight, more preferably 1 to 8% by weight. In the iodine ion impregnation treatment, the temperature of the aqueous solution is usually 1
It is about 5 to 60 ° C, preferably 25 to 40 ° C. The immersion time is usually about 1 to 120 seconds, preferably 3 to 90 seconds.

Then, an alcohol solution immersion treatment is performed. For the alcohol liquid immersion treatment, for example, liquid alcohol or an aqueous solution containing the liquid alcohol is used.
In the case of an aqueous alcohol solution, its concentration is about 5% by weight or more. The liquid alcohol is preferably a volatile hydrophilic alcohol at room temperature (25 ° C.), particularly one that can be mixed with water at an arbitrary ratio. Examples of such alcohols include methanol, ethanol, isopropyl alcohol, butanol, propanol and the like. The temperature of the aqueous solution in the alcohol liquid immersion treatment is usually about 5 to 50 ° C, preferably 5 to 40 ° C.
Is. The immersion time is usually about 1 to 300 seconds, preferably 3 to 120 seconds.

The polyvinyl alcohol film (stretched film) that has been subjected to each of the above-mentioned treatments is dried to be a polarizer. Drying treatment of the polarizer is 30 ° C. or lower,
It is preferably 10 to 25 ° C. The drying time is generally about 0.5 to 10 minutes, preferably 0.5 to 5 minutes.

The obtained polarizer can be used as a polarizing plate having a transparent protective layer on at least one surface thereof according to a conventional method. The transparent protective layer can be provided as a coating layer made of a polymer or as a laminated layer of a film. As the transparent polymer or film material for forming the transparent protective layer, an appropriate transparent material can be used, but a material having excellent transparency, mechanical strength, thermal stability, moisture barrier property and the like is preferably used. Examples of the material for forming the transparent protective layer include polyester polymers such as polyethylene terephthalate and polyethylene naphthalate, cellulose polymers such as cellulose diacetate and cellulose triacetate, acrylic polymers such as polymethylmethacrylate, polystyrene and acrylonitrile. Examples thereof include styrene polymers such as styrene copolymers (AS resin) and polycarbonate polymers. Also, polyethylene, polypropylene, polyolefins having a cyclo or norbornene structure, polyolefin polymers such as ethylene / propylene copolymers, vinyl chloride polymers, amide polymers such as nylon and aromatic polyamide, imide polymers, sulfone polymers. , Polyether sulfone polymer, polyether ether ketone polymer, polyphenylene sulfide polymer,
Vinyl alcohol-based polymers, vinylidene chloride-based polymers, vinyl butyral-based polymers, arylate-based polymers, polyoxymethylene-based polymers, epoxy-based polymers, and blends of the aforementioned polymers are also examples of polymers forming the transparent protective layer. .

The surface of the transparent protective film on which the polarizer is not adhered (the surface on which the coating layer is not provided) has been subjected to a treatment for the purpose of hard coat layer, antireflection treatment, sticking prevention, diffusion or antiglare. May be

The hard coat treatment is carried out for the purpose of preventing scratches on the surface of the polarizing plate. For example, a hardened film excellent in hardness and sliding characteristics made of an appropriate ultraviolet curable resin such as acrylic or silicone is used. It can be formed by a method of adding to the surface of the transparent protective film.
The antireflection treatment is performed for the purpose of preventing reflection of external light on the surface of the polarizing plate, and can be achieved by forming an antireflection film or the like according to the conventional method. Further, the sticking prevention treatment is performed for the purpose of preventing adhesion with an adjacent layer.

The anti-glare treatment is carried out for the purpose of preventing external light from being reflected on the surface of the polarizing plate and obstructing the visual recognition of the light transmitted through the polarizing plate. For example, a sand blasting method or an embossing method is used to roughen the surface. It can be formed by imparting a fine concavo-convex structure to the surface of the transparent protective film by an appropriate method such as a surface-rendering method or a method of blending transparent particles. The fine particles to be contained in the formation of the surface fine uneven structure are, for example, conductive particles made of silica, alumina, titania, zirconia, tin oxide, indium oxide, cadmium oxide, antimony oxide having an average particle size of 0.5 to 50 μm. In some cases, transparent fine particles such as inorganic fine particles and organic fine particles made of a crosslinked or uncrosslinked polymer are used. When forming the surface fine uneven structure, the amount of the fine particles used is generally about 2 to 50 parts by weight based on 100 parts by weight of the transparent resin forming the surface fine uneven structure.
25 parts by weight is preferred. The anti-glare layer may also serve as a diffusion layer (such as a viewing angle enlarging function) for diffusing the light transmitted through the polarizing plate and enlarging the viewing angle.

The antireflection layer, the antisticking layer, the diffusion layer, the antiglare layer and the like can be provided on the transparent protective film itself, or as an optical layer separately from the transparent protective layer. it can.

An adhesive is used for the adhesion treatment between the polarizer and the transparent protective film. Examples of the adhesive include isocyanate adhesives, polyvinyl alcohol adhesives, gelatin adhesives, vinyl latex adhesives, and water-based polyesters. The adhesive is usually used as an adhesive composed of an aqueous solution, and is usually 0.5 to 60% by weight.
Of solid content.

The polarizing plate of the present invention is produced by laminating the transparent protective film and the polarizer with the adhesive. The adhesive may be applied to either the transparent protective film or the polarizer, or to both. After the bonding, a drying step is performed to form an adhesive layer composed of a coating and drying layer. The lamination of the polarizer and the transparent protective film can be performed with a roll laminator or the like.
The thickness of the adhesive layer is not particularly limited, but is usually 0.1 to 5
It is about μm.

In practical use, the polarizing plate of the present invention can be used as an optical film laminated with another optical layer.
Although the optical layer is not particularly limited, for example, for forming a liquid crystal display device such as a reflection plate, a semi-transmission plate, a retardation plate (including a wavelength plate such as 1/2 or 1/4), and a viewing angle compensation film. One or two or more optical layers that may be used can be used. In particular, a reflective polarizing plate or a semi-transmissive polarizing plate obtained by further laminating a reflective plate or a semi-transmissive reflective plate on the polarizing plate of the present invention, an elliptic polarizing plate or a circularly polarized light having a retardation plate further laminated on the polarizing plate. A wide viewing angle polarizing plate in which a viewing angle compensation film is further laminated on a plate or a polarizing plate, or a polarizing plate in which a brightness improving film is further laminated on the polarizing plate is preferable.

The reflective polarizing plate is a polarizing plate provided with a reflective layer, and is for forming a liquid crystal display device of the type that reflects incident light from the viewing side (display side) to display. Further, there is an advantage that it is possible to omit the incorporation of a light source such as a backlight and to easily reduce the thickness of the liquid crystal display device. The reflective polarizing plate can be formed by an appropriate method such as a method in which a reflective layer made of metal or the like is attached to one surface of the polarizing plate via a transparent protective layer or the like, if necessary.

Specific examples of the reflection type polarizing plate include a transparent protective film which is mat-treated if necessary, and a foil or vapor deposition film made of a reflective metal such as aluminum is attached to one surface to form a reflective layer. can give. Further, by incorporating fine particles into the transparent protective film to form a surface fine uneven structure,
There is also one having a reflective layer having a fine concavo-convex structure thereon. The reflective layer having the fine concavo-convex structure has the advantage that diffused incident light is diffused to prevent directivity and glare, and uneven brightness can be suppressed. Further, the transparent protective film containing fine particles also has an advantage that incident light and reflected light thereof are diffused when they pass therethrough to further suppress uneven brightness. The reflective layer having a fine concavo-convex structure reflecting the surface fine concavo-convex structure of the transparent protective film is formed by, for example, a vacuum deposition method, an ion plating method,
It can be performed by a method of directly attaching a metal to the surface of the transparent protective layer by an appropriate method such as a vapor deposition method such as a sputtering method or a plating method.

The reflection plate may be used as a reflection sheet in which a reflection layer is provided on an appropriate film according to the transparent film, instead of the method of directly applying to the transparent protective film of the polarizing plate. Since the reflective layer is usually made of a metal, the use form in which the reflective surface is covered with a transparent protective film, a polarizing plate, or the like prevents the reduction of the reflectance due to oxidation, and thus the long-lasting initial reflectance. It is more preferable from the viewpoint of avoiding the additional provision of the protective layer.

The semi-transmissive polarizing plate can be obtained by using a semi-transmissive reflective layer such as a half mirror that reflects and transmits light in the reflective layer. The semi-transmissive polarizing plate is usually provided on the back side of the liquid crystal cell, and when the liquid crystal display device is used in a relatively bright atmosphere,
An image is displayed by reflecting incident light from the viewing side (display side), and in a relatively dark atmosphere, an image is displayed using a built-in light source such as a backlight built into the back side of the semi-transmissive polarizing plate. It is possible to form a liquid crystal display device of the type that displays That is, the semi-transmissive polarizing plate can save energy for use of a light source such as a backlight in a bright atmosphere, and is useful for forming a liquid crystal display device of a type that can be used with a built-in light source even in a relatively dark atmosphere. is there.

An elliptical polarizing plate or a circular polarizing plate in which a retardation plate is further laminated on the polarizing plate will be described. A phase difference plate or the like is used when changing linearly polarized light to elliptically polarized light or circularly polarized light, changing elliptically polarized light or circularly polarized light to linearly polarized light, or changing the polarization direction of linearly polarized light. In particular, a so-called ¼ wavelength plate (also called a λ / 4 plate) is used as a retardation plate that changes linearly polarized light into circularly polarized light or changes circularly polarized light into linearly polarized light. A half-wave plate (also called a λ / 2 plate) is usually used to change the polarization direction of linearly polarized light.

The elliptically polarizing plate compensates (prevents) coloring (blue or yellow) caused by the birefringence of the liquid crystal layer of a spurts twisted nematic (STN) type liquid crystal display device, and is used for black and white display without the coloring. Used effectively. Further, the one in which the three-dimensional refractive index is controlled is preferable because it can also compensate (prevent) coloring that occurs when the screen of the liquid crystal display device is viewed from an oblique direction. The circularly polarizing plate is effectively used, for example, when adjusting the color tone of an image in a reflective liquid crystal display device in which an image is displayed in color, and also has a function of preventing reflection.
Specific examples of the retardation plate described above include polycarbonate, polyvinyl alcohol, polystyrene, polymethylmethacrylate, polypropylene and other polyolefins, polyarylate, and a birefringent film obtained by subjecting a film made of a suitable polymer such as polyamide to a stretching treatment. And a liquid crystal polymer oriented film, a liquid crystal polymer oriented layer supported by a film, and the like. The retardation plate may be one having an appropriate retardation according to the purpose of use, such as various wavelength plates or one for the purpose of compensating for the viewing angle and the like due to birefringence of the liquid crystal layer, and may be two or more kinds. It may be one in which retardation plates are laminated to control optical properties such as retardation.

The elliptically polarizing plate or the reflective elliptically polarizing plate is a laminate of a polarizing plate or a reflective elliptically polarizing plate and a retardation plate in an appropriate combination. Such an elliptically polarizing plate or the like can be formed by sequentially stacking them separately in the manufacturing process of a liquid crystal display device so as to form a combination of a (reflection type) polarizing plate and a retardation plate. An optical film such as a polarizing plate is excellent in stability of quality, workability of lamination, and the like, and has an advantage that manufacturing efficiency of a liquid crystal display device can be improved.

The viewing angle compensating film is a film for widening the viewing angle so that the image can be seen relatively clearly even when the screen of the liquid crystal display device is viewed from a slightly oblique direction, not perpendicular to the screen. Such a viewing angle compensating retardation plate includes, for example, a retardation film, an orientation film of a liquid crystal polymer or the like, or a transparent substrate on which an orientation layer of a liquid crystal polymer or the like is supported. The ordinary retardation film is a birefringent polymer film uniaxially stretched in the plane direction, whereas the retardation plate used as the viewing angle compensation film is biaxially stretched in the plane direction. A polymer film having birefringence, or a bidirectionally stretched film such as a polymer or a tilt-oriented film having a birefringence in which the refractive index in the thickness direction stretched uniaxially in the plane direction and also stretched in the thickness direction is controlled. Used. Examples of the tilted oriented film include those obtained by adhering a heat-shrinkable film to a polymer film and subjecting the polymer film to stretching treatment and / or shrinking treatment under the action of the shrinkage force caused by heating, and those obtained by obliquely orienting a liquid crystal polymer. Can be mentioned. The raw material polymer of the retardation plate is the same as the polymer explained in the previous retardation plate, which prevents coloration due to the change of the viewing angle due to the phase difference due to the liquid crystal cell and enlarges the viewing angle for good viewing. An appropriate one can be used for the purpose such as.

Further, from the viewpoint of achieving a wide viewing angle with good visibility, an optically anisotropic layer comprising an alignment layer of a liquid crystal polymer, particularly an inclined alignment layer of a discotic liquid crystal polymer, is supported by a triacetyl cellulose film. A compensation retardation plate can be preferably used.

The polarizing plate in which the polarizing plate and the brightness enhancement film are bonded together is usually used by being provided on the back side of the liquid crystal cell. The brightness enhancement film has a property of reflecting linearly polarized light of a predetermined polarization axis or circularly polarized light of a predetermined direction when natural light is incident due to reflection from a backlight of a liquid crystal display device or the back side, and transmits other light. A polarizing plate in which a brightness enhancement film is laminated with a polarizing plate allows light from a light source such as a backlight to enter and obtain transmitted light in a predetermined polarization state, and light other than the predetermined polarization state is reflected without being transmitted. It The light reflected by the surface of the brightness enhancement film is inverted through a reflection layer or the like provided on the rear side of the brightness enhancement film to be re-incident on the brightness enhancement film, and part or all of the light is transmitted as light in a predetermined polarization state to achieve brightness. The brightness can be improved by increasing the amount of light transmitted through the improvement film and by supplying polarized light that is difficult to be absorbed by the polarizer to increase the amount of light that can be used for liquid crystal display image display and the like. That is,
When light is input from the back side of the liquid crystal cell through a polarizer without using a brightness enhancement film, almost all light with a polarization direction that does not match the polarization axis of the polarizer is reflected by the polarizer. It is absorbed and does not pass through the polarizer. That is, although depending on the characteristics of the polarizer used, about 50% of light is absorbed by the polarizer, and the amount of light that can be used for liquid crystal image display and the like is reduced accordingly, and the image becomes dark. The brightness enhancement film allows light having a polarization direction that is absorbed by the polarizer to be reflected once by the brightness enhancement film without being incident on the polarizer, and then inverted through a reflection layer or the like provided behind it. The light-increasing film transmits only the polarized light whose polarization direction is such that the light reflected and inverted between the two can pass through the polarizer. Since the light is supplied to the polarizer, light from a backlight or the like can be efficiently used for displaying an image on the liquid crystal display device, and the screen can be brightened.

A diffusion plate may be provided between the brightness enhancement film and the reflective layer or the like. The light in the polarization state reflected by the brightness enhancement film goes to the reflection layer and the like, but the installed diffusion plate uniformly diffuses the light passing therethrough, and at the same time, cancels the polarization state and becomes a non-polarization state. That is, the diffuser plate returns the polarized light to the original natural light state. The light in the non-polarized state, that is, the light in the natural light state, is repeatedly directed to the reflection layer and the like, reflected through the reflection layer and the like, again passes through the diffuser plate, and is incident again on the brightness enhancement film. Thus, between the brightness enhancement film and the reflective layer, while maintaining the brightness of the display screen by providing a diffuser that returns the polarized light to the original natural light state, at the same time, reduce the unevenness of the brightness of the display screen, It is possible to provide a uniform and bright screen. It is considered that by providing such a diffusion plate, the number of repetitions of reflection of the first incident light is moderately increased, and it is possible to provide a uniform bright display screen in combination with the diffusion function of the diffusion plate.

The above-mentioned brightness enhancement film is, for example, a multilayer thin film of a dielectric or a multilayer stack of thin films having different refractive index anisotropies, transmits linearly polarized light of a predetermined polarization axis and reflects other light. Those that exhibit the characteristics of, such as an oriented film of a cholesteric liquid crystal polymer or an oriented liquid crystal layer supported on a film substrate, reflect either left-handed or right-handed circularly polarized light and transmit other light. Appropriate materials such as those exhibiting characteristics can be used.

Therefore, in the brightness enhancement film of the type which transmits the linearly polarized light of the above-mentioned predetermined polarization axis, the transmitted light is directly incident on the polarizing plate with the polarization axis aligned to suppress the absorption loss by the polarizing plate. It can be efficiently transmitted. On the other hand, in the case of a type of brightness enhancement film that drops circularly polarized light such as a cholesteric liquid crystal layer, it can be directly incident on the polarizer, but from the viewpoint of suppressing absorption loss, the circularly polarized light is linearly polarized through a retardation plate. It is preferable that the light is incident on the polarizing plate. By using a ¼ wavelength plate as the retardation plate, circularly polarized light can be converted into linearly polarized light.

The retardation plate functioning as a quarter-wave plate in a wide wavelength range such as a visible light region is, for example, a retardation layer functioning as a quarter-wave plate and another phase difference for a light color light having a wavelength of 550 nm. It can be obtained by a method of superposing a retardation layer exhibiting characteristics, for example, a retardation layer functioning as a half-wave plate. Therefore, the retardation plate disposed between the polarizing plate and the brightness enhancement film may be composed of one layer or two or more retardation layers.

Regarding the cholesteric liquid crystal layer,
Two layers or three layers with different reflection wavelengths
By arranging the layers so as to overlap each other, it is possible to obtain an element that reflects circularly polarized light in a wide wavelength range such as a visible light region, and based on that, it is possible to obtain transmitted circularly polarized light in a wide wavelength range.

Further, the polarizing plate may be formed by laminating a polarizing plate and two or three or more optical layers, like the above-mentioned polarization separation type polarizing plate. Therefore, it may be a reflective elliptical polarizing plate or a semi-transmissive elliptical polarizing plate in which the above reflective polarizing plate or semi-transmissive polarizing plate is combined with a retardation plate.

The optical film in which the optical layer is laminated on the polarizing plate can be formed by a method of sequentially laminating separately in the manufacturing process of a liquid crystal display device, etc. Has an advantage that it is excellent in quality stability and assembling work and can improve the manufacturing process of a liquid crystal display device or the like. Appropriate adhesion means such as an adhesive layer may be used for lamination. In adhering the above-mentioned polarizing plate and other optical films, the optical axes thereof can be set at an appropriate arrangement angle according to the intended retardation characteristics and the like.

At least one polarizing plate or at least one polarizing plate is used.
A pressure-sensitive adhesive layer for adhering to another member such as a liquid crystal cell may be provided on the laminated optical film. The pressure-sensitive adhesive forming the pressure-sensitive adhesive layer is not particularly limited, but for example, acrylic polymer, silicone polymer, polyester,
It is possible to appropriately select and use a polymer having a base polymer such as polyurethane, polyamide, polyether, or a polymer of fluorine type or rubber type. In particular, an acrylic pressure-sensitive adhesive, which has excellent optical transparency, exhibits appropriate wettability, cohesiveness and adhesiveness, and has excellent weather resistance and heat resistance, can be preferably used.

In addition to the above, prevention of foaming phenomenon or peeling phenomenon due to moisture absorption, deterioration of optical characteristics due to thermal expansion difference or the like, prevention of warpage of liquid crystal cells, and further formation of a liquid crystal display device having high quality and excellent durability, etc. From this point of view, an adhesive layer having a low moisture absorption rate and excellent heat resistance is preferable.

The adhesive layer is made of, for example, natural or synthetic resins, in particular, tackifying resins, fillers, pigments, colorants, and oxidizers made of glass fibers, glass beads, metal powder, other inorganic powders and the like. It may contain an additive such as an inhibitor that is added to the adhesive layer. Further, it may be an adhesive layer containing fine particles and exhibiting light diffusion property.

The adhesive layer may be attached to one side or both sides of the polarizing plate or the optical film by an appropriate method. As an example thereof, a pressure-sensitive adhesive solution of about 10 to 40% by weight in which a base polymer or a composition thereof is dissolved or dispersed in a solvent composed of a single solvent or a mixture of appropriate solvents such as toluene and ethyl acetate is prepared, A method in which it is directly attached on the polarizing plate or the optical film by an appropriate developing method such as a casting method or a coating method, or an adhesive layer is formed on the separator according to the above and the adhesive layer is formed on the polarizing plate or the optical film. There is a method of transferring to the top.

The pressure-sensitive adhesive layer may be provided on one side or both sides of the polarizing plate or the optical film as a layer in which different compositions or types are laminated. Further, when it is provided on both surfaces, an adhesive layer having different composition, type and thickness may be provided on the front and back of the polarizing plate or the optical film. The thickness of the adhesive layer can be appropriately determined according to the purpose of use, adhesive strength, etc., and is generally 1 to
500 μm, preferably 5 to 200 μm, particularly 1
0 to 100 μm is preferable.

The exposed surface of the pressure-sensitive adhesive layer is temporarily covered with a separator for the purpose of preventing contamination and the like until it is put into practical use. As a result, it is possible to prevent contact with the adhesive layer in the usual handling state. As a separator,
Except for the above thickness conditions, for example, a plastic film, a rubber sheet, a paper, a cloth, a non-woven fabric, a net, a foamed sheet or a metal foil, an appropriate thin sheet such as a laminated body thereof, a silicone type or a long mirror alkyl type may be used as necessary. It is possible to use an appropriate one according to the prior art, such as one coated with an appropriate release agent such as fluorine-based or molybdenum sulfide.

In the present invention, each layer such as a polarizer, a transparent protective film, an optical film, etc. forming the above-mentioned polarizing plate, and each layer such as an adhesive layer may be, for example, a salicylic acid ester compound, a benzophenol compound, a benzotriazole compound. Alternatively, it may be one having an ultraviolet absorbing ability by a method such as a method of treating with an ultraviolet absorber such as a cyanoacrylate compound or a nickel complex salt compound.

The polarizing plate or optical film of the present invention can be preferably used for forming various devices such as liquid crystal display devices. The liquid crystal display device can be formed in a conventional manner. That is, a liquid crystal display device is generally formed by appropriately assembling a liquid crystal cell, a polarizing plate or an optical film, and if necessary, components such as an illumination system and incorporating a drive circuit. There is no particular limitation except that the polarizing plate or the optical film according to the invention is used, and the conventional method can be applied. The liquid crystal cell may be of any type such as TN type, STN type, and π type.

It is possible to form an appropriate liquid crystal display device such as a liquid crystal display device in which a polarizing plate or an optical film is arranged on one side or both sides of a liquid crystal cell or a liquid crystal display device using a backlight or a reflector in an illumination system. In that case, the polarizing plate or the optical film according to the present invention can be installed on one side or both sides of the liquid crystal cell. When a polarizing plate or an optical film is provided on both sides, they may be the same or different. Further, when forming the liquid crystal display device, for example, a diffusion plate, an anti-glare layer, an antireflection film, a protective plate, a prism array, a lens array sheet, a light diffusion plate, a backlight, and other appropriate components are provided at appropriate positions in a single layer or Two or more layers can be arranged.

Next, an organic electroluminescence device (organic EL display device) will be described. Generally, in an organic EL display device, a transparent electrode, an organic light emitting layer, and a metal electrode are sequentially laminated on a transparent substrate to form a light emitting body (organic electroluminescent light emitting body). Here, the organic light emitting layer is a laminate of various organic thin films, for example, a laminate of a hole injection layer made of a triphenylamine derivative or the like and a light emitting layer made of a fluorescent organic solid such as anthracene, Alternatively, a structure having various combinations such as a laminated body of such a light emitting layer and an electron injection layer formed of a perylene derivative, or a laminated body of these hole injection layer, light emitting layer, and electron injection layer is known. Has been.

In the organic EL display device, holes and electrons are injected into the organic light emitting layer by applying a voltage to the transparent electrode and the metal electrode, and energy generated by the recombination of these holes and electrons is fluorescent. It emits light based on the principle that a substance is excited and the excited fluorescent substance emits light when returning to the ground state. The mechanism of recombination in the middle is similar to that of a general diode, and as can be expected from this, the current and the emission intensity show a strong nonlinearity with rectification with respect to the applied voltage.

In an organic EL display device, at least one electrode must be transparent in order to extract light emitted from the organic light emitting layer.
A transparent electrode formed of a transparent conductor such as O) is used as an anode. On the other hand, it is important to use a substance having a small work function for the cathode in order to facilitate electron injection and increase the luminous efficiency, and a metal electrode such as Mg-Ag or Al-Li is usually used.

In the organic EL display device having such a structure, the organic light emitting layer is formed of an extremely thin film having a thickness of about 10 nm. For this reason, the organic light emitting layer transmits light almost completely like the transparent electrode. As a result, when entering from the surface of the transparent substrate during non-light emission, the light transmitted through the transparent electrode and the organic light emitting layer and reflected by the metal electrode goes out to the surface side of the transparent substrate again, when viewed from the outside, The display surface of the organic EL display device looks like a mirror surface.

In an organic EL display device including an organic electroluminescent light-emitting body having a transparent electrode on the front surface side of an organic light-emitting layer which emits light when a voltage is applied and a metal electrode on the back surface side of the organic light-emitting layer, A polarizing plate can be provided on the surface side of the electrode, and a retardation plate can be provided between the transparent electrode and the polarizing plate.

Since the retardation plate and the polarizing plate have a function of polarizing the light which is incident from the outside and reflected by the metal electrode, there is an effect that the mirror surface of the metal electrode is not visually recognized from the outside by the polarization action. Especially, the phase difference plate is 1/4.
The mirror surface of the metal electrode can be completely shielded by using a wave plate and adjusting the angle between the polarization directions of the polarizing plate and the retardation plate to π / 4.

That is, of the external light incident on the organic EL display device, only the linearly polarized light component is transmitted by the polarizing plate. This linearly polarized light is generally elliptically polarized by the retardation plate, but it is circularly polarized when the retardation plate is a 1/4 wavelength plate and the polarization direction between the polarizing plate and the retardation plate is π / 4. .

This circularly polarized light passes through the transparent substrate, the transparent electrode and the organic thin film, is reflected by the metal electrode, again passes through the organic thin film, the transparent electrode and the transparent substrate and becomes linearly polarized light again on the retardation plate. . Since this linearly polarized light is orthogonal to the polarization direction of the polarizing plate, it cannot pass through the polarizing plate. as a result,
The mirror surface of the metal electrode can be completely shielded.

[0062]

EXAMPLES The present invention will be specifically described below with reference to Examples and Comparative Examples. In addition,% in each example is% by weight.

Example 1 A polyvinyl alcohol film having a thickness of 80 μm (average degree of polymerization: 2400, saponification degree: 99.9%) was placed in an aqueous iodine solution having a potassium iodide concentration of 0.3% and an iodine concentration of 0.05%. Dip at 60 ° C for 60 seconds to dye, and then stretch to 5.5 times while soaking in a boric acid aqueous solution having a boric acid concentration of 4% at 50 ° C for 60 seconds, and then add 30% to an aqueous solution of potassium iodide having a concentration of 4%. It was immersed at 5 ° C for 5 seconds. Furthermore, 99.5
% Ethanol for 5 minutes. Then, at 25 ℃ 4
After drying for a minute, a polarizer was obtained. A 80 μm thick triacetyl cellulose film having a saponified surface was attached to both sides of the polarizer with a polyvinyl alcohol-based adhesive and then dried at 60 ° C. for 4 minutes to obtain a polarizing plate.

Comparative Example 1 A polyvinyl alcohol film having a thickness of 80 μm (average degree of polymerization: 2400, saponification degree: 99.9%) was put in an aqueous iodine solution having a potassium iodide concentration of 0.3% and an iodine concentration of 0.05%. It was immersed at 60 ° C. for 60 seconds for dyeing, and then stretched to 5.5 times while being immersed for 60 seconds in an aqueous solution of boric acid concentration 4% and potassium iodide concentration 4% at 50 ° C. Then, it dried at 50 degreeC for 4 minutes. Further, it was dried at 50 ° C. for 4 minutes to obtain a polarizer. A 80 μm thick triacetyl cellulose film having a saponified surface was attached to both sides of the polarizer with a polyvinyl alcohol-based adhesive and then dried at 60 ° C. for 4 minutes to obtain a polarizing plate.

Comparative Example 2 A polyvinyl alcohol film having a thickness of 80 μm (average degree of polymerization: 2400, saponification degree: 99.9%) was placed in an aqueous iodine solution having a potassium iodide concentration of 0.3% and an iodine concentration of 0.05%. It was immersed at 60 ° C. for 60 seconds for dyeing, and then stretched to 5.5 times while being immersed for 60 seconds in an aqueous solution of boric acid concentration 4% and potassium iodide concentration 4% at 50 ° C. Then, it dried at 50 degreeC for 4 minutes. Further, it was dried at 30 ° C. for 4 minutes to obtain a polarizer. A 80 μm thick triacetyl cellulose film having a saponified surface was attached to both sides of the polarizer with a polyvinyl alcohol-based adhesive and then dried at 60 ° C. for 4 minutes to obtain a polarizing plate.

(Evaluation) The optical characteristics of the polarizers and polarizing plates prepared in Examples and Comparative Examples were evaluated. The results are shown in Table 1.
Shown in.

(Moisture Content of Polarizer) The weight of the initial polarizer is W
_0, a polarizer weight for 2 hours drying at a temperature of 120 ° C. and W _120, wherein: a polarizer moisture content _{(%) = {(W 0} -W
₁₂₀ ) / W ₀ } × 100.

(Optical Properties of Polarizer) For the transmittance, a single transmittance of one polarizer was measured using a spectrophotometer (CMS-500 manufactured by Murakami Color Research Laboratory Co., Ltd.). In addition,
The transmittance of the polarizer is a Y value which is adjusted in luminosity by the 2 degree visual field (C light source) of JISZ8701. The a value and the b value are the a value and the b value in the Hunter color system.

(Change in Hue of Polarizing Plate) The change Δab in parallel and orthogonal hues when the polarizing plate was left under the condition of 80 ° C. for 240 hours was determined. The change Δab in the orthogonal hue represents the initial parallel and orthogonal chromaticities (a _P0 , b _p0 ), (a _C0 , b
_c0 ), and the parallel and orthogonal chromaticities when left for 240 hours at 80 ° C. (a _p240 , b _P240 ), (a
_c240 , b _c240 ), the change in the parallel color and the change in the orthogonal color are represented by the formula: _{Δab P} = √ {(a _P240 −a _P0 ) ² +
(A _P240 −b _P0 ) ² }, formula: _{Δab c} = √ {(a _c240 −
It is a value obtained from a _c0 ) ² + (a _c240 −b _c0 ) ² }. The a value and the b value are the a value and the b value in the Hunter color system.

[0070]

[Table 1] In Comparative Example 1, the moisture content of the polarizer can be reduced to some extent, but since it is dried by heating, the initial hue has a yellowish tint, and the hue change after being left at 80 ° C. is large.
In Comparative Example 2, the decrease in the water content of the polarizer is small, the initial hue is yellowish, and the hue change after being left at 80 ° C. is large. In the examples, it is understood that the water content of the polarizer can be effectively reduced by the low temperature drying by performing the immersion treatment with the alcohol solution. It can be seen that by reducing the water content of the polarizer without applying heat to the polarizer, the initial yellowness of the polarizer is reduced and the hue changes little even when exposed to a heating environment.

─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. ⁷ Identification code FI theme code (reference) H05B 33/14 H05B 33/14 A // C08L 29:04 C08L 29:04 Z (72) Inventor Saiki Yuji, 1-2, Shimohozumi, Ibaraki-shi, Osaka Prefecture Nitto Denko Corporation (72) Inventor Yoichiro Sugino 1-2-1, Shimohozumi, Ibaraki-shi, Osaka Prefecture Nitto Denko Corporation (72) Inventor Seri Kondo Nitto Denko Co., Ltd. 1-2 1-2 Shimohozumi, Ibaraki-shi, Osaka (72) Inventor Iida Shomori 1-2 1-2 Shimohozumi, Ibaraki-shi, Osaka Nitto Denko Corporation F-term (reference) 2H049 BA02 BA06 BA25 BA26 BB33 BB43 BB54 BB63 BC03 BC14 BC22 2H091 FA08X FA08Z FB02 FB12 FC05 FC08 FC25 GA16 LA30 3K007 AB17 BB06 DB03 4F073 AA24 AA26 BA17 BA52 BB01 EA01 EA21 EA56 EA75 5C032 EE03 EE17

Claims (4)

[Claims] 1. An unstretched polyvinyl alcohol film is subjected to an iodine dyeing treatment, then uniaxially stretched in a boric acid aqueous solution, then subjected to an iodine ion impregnation treatment, and then subjected to an alcohol liquid immersion treatment. And a method for manufacturing a polarizer. 2. A polarizer obtained by the manufacturing method according to claim 1. 3. A polarizing plate having a transparent protective layer provided on at least one surface of the polarizer according to claim 2. 4. An image display device using at least one polarizing plate according to claim 3.