JP2001226145A - Plate glass for image reader - Google Patents
Plate glass for image readerInfo
- Publication number
- JP2001226145A JP2001226145A JP2000042755A JP2000042755A JP2001226145A JP 2001226145 A JP2001226145 A JP 2001226145A JP 2000042755 A JP2000042755 A JP 2000042755A JP 2000042755 A JP2000042755 A JP 2000042755A JP 2001226145 A JP2001226145 A JP 2001226145A
- Authority
- JP
- Japan
- Prior art keywords
- group
- image reading
- polydimethylsiloxane
- sample
- plate glass
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、原稿自動送り機構
付き複写機若しくはスキャナー又はこれに類するもの
（以下、画像読取り装置と言う。）に使用する板ガラ
ス、特に画像読取り装置で問題となるコピー上の汚れ対
策や紙詰り対策を施した板ガラスに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a plate glass used for a copying machine or a scanner having an automatic document feeding mechanism or the like (hereinafter, referred to as an image reading device), and particularly to a copy glass which is problematic in an image reading device. The present invention relates to a sheet glass provided with a countermeasure against dirt and paper jam.
【０００２】[0002]
【従来の技術】原稿自動送り機構を備えた画像読取り装
置の問題点として、原稿に、粘着テープ、接着剤、半乾
きの油性インクが付着している場合、この様な原稿を自
動で送ると板ガラスが汚れることがある。粘着テープ、
接着剤又は油性インクが原稿から板ガラスに移るからで
ある。この汚れを放置したままで原稿を読取り、複写を
実行すると、コピーに陰や筋が写り、コピーの品質が低
下する。2. Description of the Related Art A problem with an image reading apparatus provided with an automatic document feed mechanism is that when a document has an adhesive tape, an adhesive, or semi-dry oil-based ink, such a document is automatically fed. The glass sheet may become dirty. Adhesive tape,
This is because the adhesive or the oil-based ink transfers from the original to the plate glass. If the original is read and the copy is executed with the dirt left untouched, shadows and streaks appear in the copy, and the quality of the copy deteriorates.
【０００３】一方、複写機天板に関する改良技術とし
て、特開昭６２−２９３２３６号公報「潤滑性と帯電
防止性を有する複写機用天板」や、特開平７−３０６
４７８号公報「複写機用天板及びその製造方法」などが
提案されている。すなわち、上記は、それの特許請求
の範囲によれば、透明板上に、透明導電層を有する。こ
の透明導電層上に、ポリフルオロアルキル基を含有する
化合物からなる保護潤滑層を有することを特徴とする。On the other hand, as an improved technique relating to a copier top plate, Japanese Patent Application Laid-Open No. Sho 62-293236, "A copier top plate having lubricity and antistatic properties", and Japanese Patent Application Laid-Open No. 7-306.
No. 478, “Top plate for copier and method for producing same” is proposed. That is, the above, according to the claims, has a transparent conductive layer on a transparent plate. On this transparent conductive layer, a protective lubricating layer comprising a compound containing a polyfluoroalkyl group is provided.
【０００４】また、上記は、それの請求項１によれ
ば、表面に潤滑層が形成された複写機用天板において、
前記潤滑層は側鎖がアミノ基（モノアルミノアルキル基
およびジアミノアルキル基を含む）、カルボキシル基、
またはカルビノール基で変性されたポリジメチルシロキ
サンを含有することを特徴とする。According to the first aspect of the present invention, there is provided a copier top plate having a lubricating layer formed on a surface thereof.
The lubricating layer has an amino group (including a monoaluminoalkyl group and a diaminoalkyl group), a carboxyl group,
Alternatively, it is characterized by containing a polydimethylsiloxane modified with a carbinol group.
【０００５】[0005]
【発明が解決しようとする課題】上記を実行したとこ
ろ、１万枚程度の複写を実行すると、紙詰りが目立つよ
うになった。原因を推定すれば、ポリフルオロアルキル
基を主成分とする潤滑層が用紙に触れたときに、ごく微
量ではあるが削られ、保護潤滑層が実質的に消失したと
思われる。潤滑機能が低下すれば、紙の流れが滞り、つ
いには紙詰りとなると考えられる。As a result of executing the above, when about 10,000 copies are executed, paper jams become noticeable. If the cause is presumed, it is considered that when the lubricating layer containing a polyfluoroalkyl group as a main component touches the paper, the protective lubricating layer is substantially eliminated, though it is removed in a very small amount. If the lubricating function is reduced, it is considered that the flow of the paper is stagnated, and eventually the paper is jammed.
【０００６】また、上記を実行したところ、数千枚レ
ベルの複写を実施するとコピーに汚れが発生することが
分かった。原因を推定すれば原稿に付着していた粘着テ
ープ、接着剤等がガラスに付着することにより、コピー
に影が写ったものと考えられる。[0006] In addition, it has been found that when the above operation is performed, a copy is stained when a copy of several thousand sheets is performed. If the cause is presumed, it is considered that the adhesive tape, the adhesive or the like attached to the document adheres to the glass, and a shadow appears on the copy.
【０００７】「紙詰り」と「コピー汚れ」は複写機等の
画像読取り装置の信頼性を著しく低下させる。そこで、
本発明の目的は紙詰りと汚れの両方を解消することので
きる画像読取り装置用板ガラスを提供することにある。[0007] "Paper jam" and "copy dirt" significantly lower the reliability of an image reading apparatus such as a copying machine. Therefore,
SUMMARY OF THE INVENTION It is an object of the present invention to provide a plate glass for an image reading apparatus which can eliminate both paper jams and stains.
【０００８】[0008]
【課題を解決するための手段】上記目的を達成するため
に請求項１は、板ガラスの表面に透明導電層を形成し、
この透明導電層上に汚れ防止層を形成した画像読取り装
置用板ガラスにおいて、前記汚れ防止層は、パーフルオ
ロ・アルキルポリエーテルと、側鎖がモノアミノアルキ
ル基またはジアミノアルキル基を含むアミノ基で変成さ
れたポリジメチルシロキサンと、を含有することを特徴
とする。To achieve the above object, a first aspect of the present invention is to form a transparent conductive layer on a surface of a sheet glass,
In the plate glass for an image reading apparatus having an antifouling layer formed on the transparent conductive layer, the antifouling layer is modified with a perfluoroalkylpolyether and an amino group having a side chain containing a monoaminoalkyl group or a diaminoalkyl group. And polydimethylsiloxane.
【０００９】パーフルオロ・アルキルポリエーテルは、
Ｆ（ふっ素）を多く含むため化学的に不活性になり、こ
れにより防汚性に富む。一方、アミノ基で変性されたポ
リジメチルシロキサンはアミノ基の作用により、透明導
電層又は板ガラスに対する吸着性が強く、耐久性に富
む。そのためアミノ基で変性されたポリジメチルシロキ
サンを含む汚れ防止層は多数の通紙にも摩滅することが
ない。すなわち、パーフルオロ・アルキルポリエーテル
の防汚機能を発揮し、アミノ基で変成されたポリジメチ
ルシロキサンは低摩擦性能を発揮させ続けることができ
る。従って、請求項１によれば複写機等の画像読取り装
置は、汚れのない綺麗な複写が行え且つ紙詰りのない円
滑な複写作業が行える。[0009] The perfluoroalkyl polyether is
Since it contains a large amount of F (fluorine), it becomes chemically inert, and thus has high antifouling properties. On the other hand, polydimethylsiloxane modified with an amino group has a strong adsorptivity to a transparent conductive layer or a sheet glass due to the action of the amino group, and has high durability. Therefore, the antifouling layer containing the amino group-modified polydimethylsiloxane is not worn away even when a large number of papers are passed. That is, the anti-fouling function of the perfluoroalkyl polyether is exhibited, and the polydimethylsiloxane modified with the amino group can continue to exhibit low friction performance. Therefore, according to the first aspect, the image reading apparatus such as a copying machine can perform a clean copy without dirt and can perform a smooth copy operation without paper jam.
【００１０】請求項２は、板ガラスの表面に汚れ防止層
を形成した画像読取り装置用板ガラスにおいて、汚れ防
止層は、パーフルオロ・アルキルポリエーテルと、側鎖
がモノアミノアルキル基またはジアミノアルキル基を含
むアミノ基で変成されたポリジメチルシロキサンと、を
含有することを特徴とする。According to a second aspect of the present invention, there is provided a plate glass for an image reading apparatus in which a stain preventing layer is formed on a surface of the sheet glass, wherein the stain preventing layer comprises a perfluoroalkylpolyether and a monoaminoalkyl group or a diaminoalkyl group having a side chain. And polydimethylsiloxane modified with an amino group.
【００１１】パーフルオロ・アルキルポリエーテルは防
汚機能を発揮し、アミノ基で変成されたポリジメチルシ
ロキサンは低摩擦性能を発揮する。従って、請求項２に
よれば複写機等の画像読取り装置は、汚れのない綺麗な
複写が行え且つ紙詰りのない円滑な複写作業が行える。
加えて、請求項２は、透明導電層を含まぬ分、構造が簡
単で画像読取り装置用板ガラスの低コスト化を図ること
ができる。The perfluoroalkyl polyether exhibits an antifouling function, and the polydimethylsiloxane modified with an amino group exhibits low friction performance. Therefore, according to the second aspect, the image reading apparatus such as a copying machine can perform a clean copy without dirt and can perform a smooth copy operation without paper jam.
In addition, according to the second aspect, since the transparent conductive layer is not included, the structure is simple and the cost of the plate glass for an image reading device can be reduced.
【００１２】請求項３では、パーフルオロ・アルキルポ
リエーテルは、下記式で示されるとともに、ｎが７〜１
５０であることを特徴とする。According to a third aspect of the present invention, the perfluoroalkyl polyether is represented by the following formula and n is 7 to 1
50.
【００１３】[0013]
【数２】 (Equation 2)
【００１４】ｎが７未満であれば、原稿を通したときの
耐久性が不十分となる。また、ｎが１５０を超えると、
塗布液にしたときの液の粘度が高くなり過ぎて、塗布作
業に支障をきたす。ｎを７〜１５０の範囲から選択すれ
ば、汚れ防止層の耐久性を高めることと、塗布作業を円
滑にすることとの双方を満足させることができる。If n is less than 7, the durability when the document is passed will be insufficient. Also, when n exceeds 150,
The viscosity of the coating liquid becomes too high, which hinders the coating operation. When n is selected from the range of 7 to 150, it is possible to satisfy both the enhancement of the durability of the stain prevention layer and the smoothness of the coating operation.
【００１５】請求項４では、パーフルオロ・アルキルポ
リエーテルとポリジメチルシロキサンとの混合比は、体
積比で１：４〜４：１としたことを特徴とする。According to a fourth aspect of the present invention, the mixing ratio of the perfluoroalkyl polyether and the polydimethylsiloxane is 1: 4 to 4: 1 by volume.
【００１６】混合比が１：４を下回ると、パーフルオロ
・アルキルポリエーテルが不足し、汚れ防止層の耐久性
が著しく低下し、数千枚の複写を実施した後に、汚れ防
止層が失われ、結果として汚れが発生するようになる。
一方、混合比が４：１を超えると、ポリジメチルシロキ
サンが不足して摩擦係数が増加し、紙詰りを誘起する。
混合比を、体積比で１：４〜４：１にすれば、汚れ防止
と紙詰り防止の双方をより効果的に達成することができ
る。If the mixing ratio is less than 1: 4, the perfluoroalkylpolyether becomes insufficient, and the durability of the antifouling layer is remarkably reduced. After performing thousands of copies, the antifouling layer is lost. As a result, dirt is generated.
On the other hand, when the mixing ratio exceeds 4: 1, the polydimethylsiloxane becomes insufficient, the friction coefficient increases, and paper jam is induced.
When the mixing ratio is 1: 4 to 4: 1 in volume ratio, both the prevention of stains and the prevention of paper jam can be more effectively achieved.
【００１７】[0017]
【発明の実施の形態】本発明の実施の形態を添付図に基
づいて以下に説明する。図１は本発明に係る画像読取り
装置用板ガラス（第１実施例）の要部拡大図であり、画
像読取り装置用板ガラス１０は、板ガラス１１の表面に
透明導電層１２を形成し、この透明導電層１２上に汚れ
防止層１３を形成したものである。帯電によるトナーの
付着を防ぐため板ガラス１１の裏面にも透明導電層１２
を設けてもよい。Embodiments of the present invention will be described below with reference to the accompanying drawings. FIG. 1 is an enlarged view of a main part of a glass sheet for an image reading device according to the present invention (first embodiment). A glass sheet 10 for an image reading device has a transparent conductive layer 12 formed on the surface of a glass sheet 11 and has a transparent conductive layer. The anti-smudge layer 13 is formed on the layer 12. The transparent conductive layer 12 is also provided on the back surface of the sheet glass 11 to prevent toner from adhering due to charging.
May be provided.
【００１８】前記透明導電層１２は図示せぬアース線を
介して静電気を除去するところの帯電防止のために設け
たものであり、例えば酸化錫、酸化インジウム、錫ドー
プインジウムなどの被膜をスパッタリング法、化学的気
相成長法、蒸着法などで形成したものである。The transparent conductive layer 12 is provided for preventing static electricity from being removed through a ground wire (not shown). For example, a coating such as tin oxide, indium oxide, or tin-doped indium is formed by sputtering. Formed by a chemical vapor deposition method, a vapor deposition method, or the like.
【００１９】前記汚れ防止層１３は、摩擦係数を下げる
ことで紙詰りを防止するために設けたものであり、パー
フルオロ・アルキルポリエーテルと、側鎖がモノアミノ
アルキル基またはジアミノアルキル基を含むアミノ基で
変成されたポリジメチルシロキサンとを含有する化合物
を、エタノール、メタノール、プロパノールなどのアル
コール類、ヘキサン、ｎ−ヘキサン等の脂肪族炭化水
素、又はこれらに類する溶剤に分散させる。溶剤は任意
のものを採用することができるが、労働環境の面からは
エタノールが望ましい。The stain prevention layer 13 is provided for preventing paper jam by lowering the friction coefficient, and includes a perfluoroalkyl polyether and a side chain containing a monoaminoalkyl group or a diaminoalkyl group. A compound containing a polydimethylsiloxane modified with an amino group is dispersed in an alcohol such as ethanol, methanol and propanol, an aliphatic hydrocarbon such as hexane and n-hexane, or a solvent similar thereto. Although any solvent can be used, ethanol is desirable from the viewpoint of the working environment.
【００２０】この場合、前記化合物は、エタノールに実
質不溶であるから、０．１〜１．０重量％で混合したも
のを強く攪拌して機械的に分散させたものを塗布液とし
て用いる。In this case, since the compound is substantially insoluble in ethanol, a mixture of 0.1 to 1.0% by weight and vigorously stirred and mechanically dispersed is used as a coating solution.
【００２１】ここで、前記パーフルオロ・アルキルポリ
エーテルは、下記式で示されるとともに、ｎが７〜１５
０であることが望ましい。Here, the perfluoroalkylpolyether is represented by the following formula and n is 7 to 15:
Desirably, it is 0.
【００２２】[0022]
【数３】 (Equation 3)
【００２３】ｎが７未満であれば、原紙（原稿）を通し
たときの耐久性が不十分となる。また、ｎが１５０を超
えると、塗布液にしたときの液の粘度が高くなり過ぎ
て、塗布作業に支障をきたす。汚れ防止層１３の耐久性
を高めることと、塗布作業を円滑にすることとの双方を
満足するにはｎは７〜１５０の範囲に留めるべきであ
る。If n is less than 7, the durability when passing the base paper (original) becomes insufficient. On the other hand, if n exceeds 150, the viscosity of the coating liquid becomes too high, which hinders the coating operation. In order to satisfy both the enhancement of the durability of the stain prevention layer 13 and the smoothness of the coating operation, n should be kept in the range of 7 to 150.
【００２４】なお、溶剤として、クロロフルオロカーボ
ン或いはこれの代替品を使用すれば、前記化合物は完全
に溶解させることができる。しかし、クロロフルオロカ
ーボン或いはこれの代替品は、フロン規制対象物であ
り、環境に対する配慮から使用は避けたい。If chlorofluorocarbon or a substitute thereof is used as a solvent, the compound can be completely dissolved. However, chlorofluorocarbons or their substitutes are substances subject to the regulation of chlorofluorocarbons, and their use should be avoided because of environmental considerations.
【００２５】また、パーフルオロ・アルキルポリエーテ
ルとポリジメチルシロキサンとの混合比は、体積比で
１：４〜４：１とすることが望ましい。前記混合比が
１：４を下回ると、パーフルオロ・アルキルポリエーテ
ルが不足し、汚れ防止層１３の耐久性が著しく低下し、
数千枚の複写を実施した後に、汚れ防止層１３が失わ
れ、結果として汚れが発生するようになる。一方、混合
比が４：１を超えると、ポリジメチルシロキサンが不足
して摩擦係数が増加し、紙詰りを誘起する。従って、汚
れ防止と紙詰り防止の双方を満足させるには、パーフル
オロ・アルキルポリエーテルとポリジメチルシロキサン
との混合比は、体積比で１：４〜４：１とすることが有
効である。The mixing ratio between the perfluoroalkyl polyether and the polydimethylsiloxane is desirably 1: 4 to 4: 1 by volume. If the mixing ratio is less than 1: 4, the perfluoroalkyl polyether becomes insufficient, and the durability of the stain prevention layer 13 is significantly reduced,
After thousands of copies have been made, the stain prevention layer 13 is lost, resulting in stains. On the other hand, when the mixing ratio exceeds 4: 1, the polydimethylsiloxane becomes insufficient, the friction coefficient increases, and paper jam is induced. Therefore, in order to satisfy both stain prevention and paper jam prevention, it is effective that the mixing ratio of perfluoroalkyl polyether and polydimethylsiloxane is 1: 4 to 4: 1 by volume.
【００２６】図２は本発明に係る画像読取り装置用板ガ
ラス（第２実施例）の要部拡大図であり、画像読取り装
置用板ガラス１０Ｂは、板ガラス１１の表面上に汚れ防
止層１３を形成したものである。第１実施例から透明導
電層を除いたところの簡易型画像読取り装置用板ガラス
であり、製造コストを下げることができる。原稿自動送
り機構での送り速度がそれほど大きくない場合、又は帯
電防止策を板ガラス１１外に別途設ける場合に適用でき
る。また、帯電によるトナーの付着を防ぐため板ガラス
１１の裏面にも透明導電層１２を設けてもよい。FIG. 2 is an enlarged view of a main part of a glass sheet for an image reading apparatus according to the present invention (second embodiment). A glass sheet 10B for an image reading apparatus has a stain prevention layer 13 formed on the surface of a glass sheet 11. Things. This is a plate glass for a simplified image reading device in which the transparent conductive layer is removed from the first embodiment, and the manufacturing cost can be reduced. The present invention can be applied to a case where the feeding speed of the automatic document feeding mechanism is not so high or a case where an antistatic measure is separately provided outside the plate glass 11. Further, a transparent conductive layer 12 may be provided on the back surface of the plate glass 11 in order to prevent the toner from adhering due to charging.
【００２７】前記汚れ防止層１３は、第１実施例で使用
したものと同じものを使用する。説明が重複するが再度
記載する。すなわち、汚れ防止層１３は、摩擦係数を下
げることで紙詰りを防止するために設けたものであり、
パーフルオロ・アルキルポリエーテルと、側鎖がモノア
ミノアルキル基またはジアミノアルキル基を含むアミノ
基で変成されたポリジメチルシロキサンとを含有する化
合物を、エタノール、メタノール、プロパノールなどの
アルコール類、ヘキサン、ｎ−ヘキサン等の脂肪族炭化
水素、又はこれらに類する溶剤に分散させる。溶剤は任
意のものを採用することができるが、労働環境の面から
はエタノールが望ましい。As the stain prevention layer 13, the same one as used in the first embodiment is used. Although the description is duplicated, it will be described again. That is, the stain prevention layer 13 is provided to prevent paper jam by lowering the coefficient of friction.
A compound containing a perfluoroalkyl polyether and a polydimethylsiloxane in which the side chain is modified with an amino group containing a monoaminoalkyl group or a diaminoalkyl group is converted into an alcohol such as ethanol, methanol, propanol, hexane, n -Dispersed in an aliphatic hydrocarbon such as hexane or a similar solvent. Although any solvent can be used, ethanol is desirable from the viewpoint of the working environment.
【００２８】この場合、前記化合物は、エタノールに実
質不溶であるから、０．１〜１．０重量％で混合したも
のを強く攪拌して機械的に分散させたものを塗布液とし
て用いる。In this case, since the compound is substantially insoluble in ethanol, a mixture of 0.1 to 1.0% by weight, which is vigorously stirred and mechanically dispersed, is used as a coating solution.
【００２９】ここで、前記パーフルオロ・アルキルポリ
エーテルは、下記式で示されるとともに、ｎが７〜１５
０であることが望ましい。Here, the perfluoroalkyl polyether is represented by the following formula and n is 7 to 15:
Desirably, it is 0.
【００３０】[0030]
【数４】 (Equation 4)
【００３１】ｎが７未満であれば、原紙（原稿）を通し
たときの耐久性が不十分となる。また、ｎが１５０を超
えると、塗布液にしたときの液の粘度が高くなり過ぎ
て、塗布作業に支障をきたす。汚れ防止層１３の耐久性
を高めることと、塗布作業を円滑にすることとの双方を
満足するにはｎは７〜１５０の範囲に留めるべきであ
る。If n is less than 7, the durability when passing the base paper (original) becomes insufficient. On the other hand, if n exceeds 150, the viscosity of the coating liquid becomes too high, which hinders the coating operation. In order to satisfy both the enhancement of the durability of the stain prevention layer 13 and the smoothness of the coating operation, n should be kept in the range of 7 to 150.
【００３２】なお、溶剤として、クロロフルオロカーボ
ン或いはこれの代替品を使用すれば、前記化合物は完全
に溶解させることができる。しかし、クロロフルオロカ
ーボン或いはこれの代替品は、フロン規制対象物であ
り、環境に対する配慮から使用は避けたい。When chlorofluorocarbon or a substitute thereof is used as a solvent, the compound can be completely dissolved. However, chlorofluorocarbons or their substitutes are substances subject to the regulation of chlorofluorocarbons, and their use should be avoided because of environmental considerations.
【００３３】また、パーフルオロ・アルキルポリエーテ
ルとポリジメチルシロキサンとの混合比は、体積比で
１：４〜４：１とすることが望ましい。前記混合比が
１：４を下回ると、パーフルオロ・アルキルポリエーテ
ルが不足し、汚れ防止層１３の耐久性が著しく低下し、
数千枚の複写を実施した後に、汚れ防止層１３が失わ
れ、結果として汚れが発生するようになる。一方、混合
比が４：１を超えると、ポリジメチルシロキサンが不足
して摩擦係数が増加し、紙詰りを誘起する。従って、汚
れ防止と紙詰り防止の双方を満足させるには、パーフル
オロ・アルキルポリエーテルとポリジメチルシロキサン
との混合比は、体積比で１：４〜４：１とすることが有
効である。The mixing ratio between the perfluoroalkyl polyether and the polydimethylsiloxane is desirably 1: 4 to 4: 1 by volume. If the mixing ratio is less than 1: 4, the perfluoroalkyl polyether becomes insufficient, and the durability of the stain prevention layer 13 is significantly reduced,
After thousands of copies have been made, the stain prevention layer 13 is lost, resulting in stains. On the other hand, when the mixing ratio exceeds 4: 1, the polydimethylsiloxane becomes insufficient, the friction coefficient increases, and paper jam is induced. Therefore, in order to satisfy both stain prevention and paper jam prevention, it is effective that the mixing ratio of perfluoroalkyl polyether and polydimethylsiloxane is 1: 4 to 4: 1 by volume.
【００３４】[0034]
【実施例】本発明に係る実験例（実験１，２）を次に説
明する。なお、本発明は以下に述べる実験例に限定され
るものではない。DESCRIPTION OF THE PREFERRED EMBODIMENTS Experimental examples (Experiments 1 and 2) according to the present invention will be described below. The present invention is not limited to the experimental examples described below.
【００３５】［実験１］実験１は、試料の作製と汚れ確
認実験と摩擦係数計測実験とからなり、これらを順に説
明する。[Experiment 1] Experiment 1 is composed of a sample preparation, a soil confirmation experiment, and a friction coefficient measurement experiment, and these will be described in order.
【００３６】（試料の作製）：図３は本発明に係る実験
１を実施するための試料の作製フロー図であり、ＳＴ×
×はステップ番号を示す。 ＳＴ０１：３５０ｍｍ×４６ｍｍ×３ｍｍの寸法の板ガ
ラスを準備する。 ＳＴ０２：この板ガラスの上表面に蒸着法により、錫ド
ープインジウム膜からなり、厚さが約１０ｎｍ、面抵抗
が約２００Ω／ｃｍ2である透明導電層を形成する。(Preparation of Sample) FIG. 3 is a flow chart of preparing a sample for carrying out Experiment 1 according to the present invention.
X indicates a step number. ST01: A sheet glass having a size of 350 mm × 46 mm × 3 mm is prepared. ST02: A transparent conductive layer made of a tin-doped indium film, having a thickness of about 10 nm and a sheet resistance of about 200 Ω / cm 2 is formed on the upper surface of the glass sheet by vapor deposition.
【００３７】ＳＴ０３：一方、パーフルオロ・アルキル
ポリエーテルであるデュポン社製クライトックス１５２
５（以下「クライトックス」と略記する。）を注射器に
よりＡｃｍ3を採取する。さらに、アミノ基で変成され
たポリジメチルシロキサンであるアミノ変性シリコンオ
イル（信越シリコーン社製ＫＦ−８５９（以下「シリコ
ンオイルＫＦ−８５９」と略記する。））を注射器によ
りＢｃｍ3を採取する。採取したクライトックスＡｃｍ3
とアミノ変性シリコンオイルＢｃｍ3とを試薬瓶に注入
する。このときの溶媒は４００ｃｍ3のエタノールであ
る。なお、Ａｃｍ3＋Ｂｃｍ3＝１．０ｃｍ3とし、Ａと
Ｂの比率は後述する。ST03: On the other hand, Krytox 152 manufactured by DuPont, which is a perfluoroalkyl polyether
Acm 3 of 5 (hereinafter abbreviated as “Crytox”) is collected with a syringe. Further, Bcm 3 is sampled with an amino-modified silicone oil (KF-859 manufactured by Shin-Etsu Silicone Co., Ltd. (hereinafter abbreviated as “silicon oil KF-859”)), which is polydimethylsiloxane modified with an amino group, using a syringe. Krytox Acm 3 collected
And amino-modified silicone oil Bcm 3 are poured into a reagent bottle. The solvent at this time is 400 cm 3 of ethanol. Acm 3 + Bcm 3 = 1.0 cm 3, and the ratio of A to B will be described later.
【００３８】ＳＴ０４：上記混合液を磁石攪拌式混合機
（マグネチックスターラ）にて攪拌混合する。 ＳＴ０５：これで、防汚液が準備できた。ST04: The above liquid mixture is stirred and mixed by a magnetic stirring type mixer (magnetic stirrer). ST05: The antifouling liquid is now ready.
【００３９】ＳＴ０６：ＳＴ０２で準備した板ガラス上
の導電層上に、ＳＴ０５で準備した防汚液を少量垂ら
す。 ＳＴ０７：そして、ベンコットンクリーンルーム用ワイ
ピングクロスで防汚液を塗り広げる。 ＳＴ０８：次に、ワイピングクロスを巻いたスポンジブ
ロックで空拭き仕上げをする。ST06: A small amount of the antifouling solution prepared in ST05 is dripped on the conductive layer on the plate glass prepared in ST02. ST07: Then, the antifouling liquid is spread with a wiping cloth for Ben Cotton clean room. ST08: Next, dry wiping is performed with a sponge block around which a wiping cloth is wound.
【００４０】ＳＴ０９：ＳＴ０３におけるＡを０、Ｂを
１することで得た試料を「試料１」とする。同様に、Ａ
＝０．２，Ｂ＝０．８での試料を「試料２」、Ａ＝０．
３３，Ｂ＝０．６７での試料を「試料３」、Ａ＝０．
５，Ｂ＝０．５での試料を「試料４」、Ａ＝０．６７，
Ｂ＝０．３３での試料を「試料５」、Ａ＝０．８，Ｂ＝
０．２での試料を「試料６」、Ａ＝１，Ｂ＝０での試料
を「試料７」とする。この様にして、複数個の試料を製
作する。なお、上記したフローは１例を示したに過ぎ
ず、順序を変える、ステップを増減することは差支えな
い。例えばＳＴ０３は、ＳＴ０１より前に実施すること
は差支えない。ST09: A sample obtained by setting A to 0 and B to 1 in ST03 is referred to as "Sample 1". Similarly, A
= 0.2, B = 0.8, "Sample 2", A = 0.
33, the sample at B = 0.67 was designated as “Sample 3”, and A = 0.
5, the sample at B = 0.5 is “Sample 4”, A = 0.67,
The sample at B = 0.33 was designated as “Sample 5,” A = 0.8, B =
The sample at 0.2 is referred to as “sample 6”, and the sample at A = 1 and B = 0 as “sample 7”. In this way, a plurality of samples are manufactured. It should be noted that the above-described flow is merely an example, and the order may be changed or the number of steps may be increased or decreased. For example, ST03 may be performed before ST01.
【００４１】（汚れ確認実験）：試料１を、複写機に装
着し、多数枚の原稿を送りつつ複写を実施し、コピーに
発生が予想される線汚れの有無を調べる。試料２〜７に
ついても同様の実験を行う。その結果は後述の表１に示
す。(Stain Confirmation Experiment): The sample 1 is mounted on a copying machine, copying is performed while a large number of originals are fed, and the presence or absence of a line stain expected to occur in the copy is examined. The same experiment is performed for Samples 2 to 7. The results are shown in Table 1 below.
【００４２】（摩擦係数計測実験）：摩擦係数が小さい
ほど紙詰りが起こりにくいと言える。そこで、複写機に
装着し、多数枚の原稿を送りつつ複写を実施した試料１
を対象に、それの原稿の接触面における動摩擦係数を計
測する。この計測は、試料１にコピー用紙を載せ、この
コピー用紙に重りを載せ、この様なコピー用紙の一端を
ばね秤で引張り、動き始めた後の定常状態に達したとき
引張り力を読む。そして、この読みに基づいて動摩擦係
数を割出す。(Friction coefficient measurement experiment): It can be said that paper jam is less likely to occur as the friction coefficient is smaller. Therefore, sample 1 was mounted on a copier and copied while sending many originals.
, The coefficient of kinetic friction on the contact surface of the original is measured. In this measurement, a copy sheet is placed on the sample 1, a weight is placed on the copy sheet, one end of such a copy sheet is pulled by a spring scale, and when a steady state is reached after the copy sheet is started, the tensile force is read. Then, the dynamic friction coefficient is determined based on the reading.
【００４３】[0043]
【表１】 [Table 1]
【００４４】表１は実験１における汚れ確認実験の結
果、摩擦係数計測実験の結果をまとめた表であり、左か
ら試料番号、構造、試薬体積比（ＳＡはクライトック
ス、ＳＢはシリコーンオイルＫＦ−８５９）、通紙テス
ト時の線汚れ発生数、動摩擦係数、結果及び評価を記載
した。なお、線汚れ発生数は、５×１０3枚、２０×１
０3枚、６０×１０3枚、１００×１０3枚について調べ
た。動摩擦係数は１０×１０3枚を通紙した時点で調べ
た。Table 1 summarizes the results of the soil confirmation experiment and the friction coefficient measurement experiment in Experiment 1. From the left, the sample number, structure, and reagent volume ratio (SA is Krytox, SB is silicone oil KF- 859), the number of line stains generated during the paper passing test, the coefficient of kinetic friction, the results and the evaluation were described. The number of line stains generated was 5 × 10 3 sheets, 20 × 1
0 3 sheets, 60 × 10 3 sheets were examined for 100 × 10 3 sheets. The coefficient of kinetic friction was examined when 10 × 10 3 sheets were passed.
【００４５】試料１は、ＳＡ（クライトックス）が０で
あるから、実質的にＳＢ（シリコンオイルＫＦ−８５
９）のみで汚れ防止層を形成したものであり、通紙５×
１０3枚で早くも１本の線汚れが発生し、２０×１０3枚
で６本、１００×１０3枚で２０本もの線汚れが発生し
た。動摩擦係数は０．０５と十分に低いため、紙詰りは
発生しなかった。しかし、結果としては汚れが酷く、評
価は「×」であった。Sample 1 has substantially no SB (silicone oil KF-85) because SA (Crytox) is 0.
9) alone, a stain prevention layer was formed, and paper passing 5 ×
As early as 10 3 sheets, one line stain occurred, 20 × 10 3 sheets caused 6 lines, and 100 × 10 3 sheets caused 20 lines of stain. Since the kinetic friction coefficient was sufficiently low at 0.05, paper jam did not occur. However, as a result, the stain was severe and the evaluation was "x".
【００４６】試料２は、ＳＡ（クライトックス）１に対
してＳＢ（シリコンオイルＫＦ−８５９）４を混合した
防汚液を採用したが、通紙１００×１０3枚での線汚れ
は２本に留った。数本であれば使用上許容できるので、
結果としては良好と言える。また、動摩擦係数は０．０
５と十分に低いため、紙詰りは発生しなかった。従っ
て、評価は「○」である。[0046] Sample 2, SA (Krytox) SB (silicone oil KF-859) with respect to 1 but 4 employs the antifouling solution obtained by mixing, line dirt in the sheet passing 100 × 10 3 sheets 2 Stayed. If several are acceptable for use,
The result is good. The dynamic friction coefficient is 0.0
5 was sufficiently low, so that paper jam did not occur. Therefore, the evaluation is “○”.
【００４７】試料３は、ＳＡ（クライトックス）１に対
してＳＢ（シリコンオイルＫＦ−８５９）２を混合した
防汚液を採用したが、通紙１００×１０3枚で線汚れが
認められなかった。結果としては極めて良好と言える。
また、動摩擦係数は０．０６と十分に低いため、紙詰り
は発生しなかった。従って、評価は「◎」である。For Sample 3, an antifouling liquid in which SB (silicone oil KF-859) 2 was mixed with SA (Crytox) 1 was used, but no line stain was observed on 100 × 10 3 sheets. Was. The result is extremely good.
Further, since the coefficient of kinetic friction was sufficiently low at 0.06, paper jam did not occur. Therefore, the evaluation is “◎”.
【００４８】試料４は、ＳＡ（クライトックス）１に対
してＳＢ（シリコンオイルＫＦ−８５９）１を混合した
防汚液を採用したが、通紙１００×１０3枚での線汚れ
は１本に留ったので、結果としては良好と言える。ま
た、動摩擦係数は０．０６と十分に低いため、紙詰りは
発生しなかった。従って、評価は「○」である。[0048] Sample 4, SA (Krytox) 1 is adopted SB antifouling solution obtained by mixing (silicone oil KF-859) 1 against, the line dirt in the sheet passing 100 × 10 3 sheets one The result is good. Further, since the coefficient of kinetic friction was sufficiently low at 0.06, paper jam did not occur. Therefore, the evaluation is “○”.
【００４９】試料５は、ＳＡ（クライトックス）２に対
してＳＢ（シリコンオイルＫＦ−８５９）１を混合した
防汚液を採用したが、通紙１００×１０3枚での線汚れ
は２本に留った。数本であれば使用上許容できるので、
結果としては良好と言える。また、動摩擦係数は０．０
７と十分に低いため、紙詰りは発生しなかった。従っ
て、評価は「○」である。[0049] Sample 5, SA (Krytox) SB (silicone oil KF-859) with respect to 2 is adopted 1 antifouling solution obtained by mixing, line dirt in the sheet passing 100 × 10 3 sheets 2 Stayed. If several are acceptable for use,
The result is good. The dynamic friction coefficient is 0.0
7, the paper jam did not occur. Therefore, the evaluation is “○”.
【００５０】試料６は、ＳＡ（クライトックス）４に対
してＳＢ（シリコンオイルＫＦ−８５９）１を混合した
防汚液を採用したが、通紙１００×１０3枚での線汚れ
は３本に留った。数本であれば使用上許容できるので、
結果としては良好と言える。また、動摩擦係数は０．０
６と十分に低いため、紙詰りは発生しなかった。従っ
て、評価は「○」である。[0050] Sample 6, SA (Krytox) 4 was adopted SB (silicone oil KF-859) antifouling solution 1 were mixed with respect to, the line dirt in the sheet passing 100 × 10 3 sheets three Stayed. If several are acceptable for use,
The result is good. The dynamic friction coefficient is 0.0
6, the paper jam did not occur. Therefore, the evaluation is “○”.
【００５１】試料７は、ＳＢ（シリコンオイルＫＦ−８
５９）が０であるから、実質的ＳＡ（クライトックス）
のみで汚れ防止層を形成したものであり、通紙１００×
１０ 3枚での線汚れは１本であるから、汚れについては
問題なかった。しかし、通紙途中での紙詰りが目立ち、
動摩擦係数を測ったところ０．３０であった。従って、
評価は「×」であった。Sample 7 was made of SB (silicone oil KF-8).
59) is 0, so substantial SA (Krytox)
Only with a dirt prevention layer formed,
10 ThreeSince there is only one line stain on a sheet,
There was no problem. However, paper jams in the middle of passing are noticeable,
It was 0.30 when the dynamic friction coefficient was measured. Therefore,
The evaluation was "x".
【００５２】以上の実験１から、ＳＡ（クライトック
ス）にＳＢ（シリコンオイルＫＦ−８５９）を適量混合
した防汚液で形成した汚れ防止層を使用した試料２〜６
は、紙詰り防止と汚れ防止の双方の機能を発揮し得るこ
とが確認できた。From the above Experiment 1, Samples 2 to 6 using the antifouling layer formed by the antifouling liquid obtained by mixing an appropriate amount of SB (silicone oil KF-859) with SA (Crytox) were used.
It can be confirmed that can perform both functions of paper jam prevention and stain prevention.
【００５３】なお、この様な好ましい結果を得ることが
できたのは、パーフルオロ・アルキルポリエーテルは、
Ｆ（ふっ素）を多く含むため化学的に不活性になり、こ
れにより防汚性に富む。一方、アミノ基で変性されたポ
リジメチルシロキサンはアミノ基の作用により、透明導
電層又は板ガラスに対する吸着性が強く、耐久性に富
む。そのためアミノ基で変性されたポリジメチルシロキ
サンを含む汚れ防止層は多数の通紙にも摩滅することが
ない。すなわち、パーフルオロ・アルキルポリエーテル
の防汚機能を発揮し、アミノ基で変成されたポリジメチ
ルシロキサンは低摩擦性能を発揮させ続けることができ
る。It should be noted that such a favorable result was obtained because the perfluoroalkyl polyether was
Since it contains a large amount of F (fluorine), it becomes chemically inert, and thus has high antifouling properties. On the other hand, polydimethylsiloxane modified with an amino group has a strong adsorptivity to a transparent conductive layer or a sheet glass due to the action of the amino group, and has high durability. Therefore, the antifouling layer containing the amino group-modified polydimethylsiloxane is not worn away even when a large number of papers are passed. That is, the anti-fouling function of the perfluoroalkyl polyether is exhibited, and the polydimethylsiloxane modified with the amino group can continue to exhibit low friction performance.
【００５４】［実験２］実験２も、試料の作製と汚れ確
認実験と摩擦係数計測実験とからなる。しかし、実験２
は前記図２の構成の試料を対象に実施したものである。[Experiment 2] Experiment 2 also consists of a sample preparation, a stain confirmation experiment, and a friction coefficient measurement experiment. However, Experiment 2
Is carried out on a sample having the configuration shown in FIG.
【００５５】図４は本発明に係る実験２を実施するため
の試料の作製フロー図であり、図３からＳＴ０２を削除
したものであるから、図３の説明を準用することにし
て、図の説明は省略する。ただし、ＳＴ０９で得た試料
は、試料１１，１２，１３，１４，１５からなる５個と
した。FIG. 4 is a flow chart of the preparation of a sample for carrying out Experiment 2 according to the present invention. Since ST02 is omitted from FIG. 3, the description of FIG. 3 shall be applied mutatis mutandis. Description is omitted. However, the number of samples obtained in ST09 was five including samples 11, 12, 13, 14, and 15.
【００５６】[0056]
【表２】 [Table 2]
【００５７】表２は実験２における汚れ確認実験の結
果、摩擦係数計測実験の結果をまとめた表であり、表の
構成及び読み方は表１のものを参照することで、ここで
は詳しく述べないが、ＳＢのみである試料１１並びにＳ
Ａのみである試料１５は表１同様に評価は×である。一
方、試料１２，１３，１４は、汚れ発生数が表１より若
干多くなっているが、その本数は許容できる値であり、
動摩擦係数も若干大きくなっているが、紙詰りを発生す
るほどではないので、評価は○である。Table 2 is a table summarizing the results of the soil confirmation experiment and the friction coefficient measurement experiment in Experiment 2. The constitution and reading of the table are shown in Table 1, and will not be described in detail here. , SB only sample 11 and S
In the case of Sample 15 having only A, the evaluation was x as in Table 1. On the other hand, in Samples 12, 13, and 14, the number of stains generated is slightly larger than in Table 1, but the number is an acceptable value.
The coefficient of kinetic friction was slightly increased, but was not so large as to cause paper jam.
【００５８】以上の実験２から、ＳＡ（クライトック
ス）にＳＢ（シリコンオイルＫＦ−８５９）を適量混合
した防汚液で形成した汚れ防止層を使用した試料１２〜
１４は、紙詰り防止と汚れ防止の双方の機能を発揮し得
ることが確認できた。From Experiment 2 described above, it was found that samples 12 to 12 using the antifouling layer formed of an antifouling liquid obtained by mixing an appropriate amount of SB (silicone oil KF-859) with SA (Crytox) were obtained.
It was confirmed that Sample No. 14 can exhibit both functions of preventing paper jam and dirt.
【００５９】実験１に比較して実験２の方が、テスト後
の動摩擦係数がやや劣る。これは、実験１の試料は透明
導電層を有し、この透明導電層の表面に凹凸を有し、こ
の凹凸に防汚液を好ましく保持するため、動摩擦係数の
点で優れ、反対に実験２の試料は透明導電層が無いた
め、動摩擦係数が劣ることになったと考えられる。In Experiment 2, the dynamic friction coefficient after the test is slightly inferior to that in Experiment 1. This is because the sample of Experiment 1 has a transparent conductive layer, and the surface of the transparent conductive layer has irregularities. Since the antifouling liquid is preferably retained on the irregularities, the sample is excellent in dynamic friction coefficient. It is probable that the sample No. had no transparent conductive layer, so that the dynamic friction coefficient was inferior.
【００６０】尚、実験及びその結果は省略するが、パー
フルオロ・アルキルポリエーテルとしてダイキン工業製
デムナムを試し、又、側鎖がモノアミノアルキル基また
はモノアミノアルキル基を含むアミノ基で変成されたポ
リシロキサンとして、信越シリコーン製ＫＦ−８６５を
試したところ、上述の実験１，２と同様の結果を確認す
ることができた。従って、防汚液を構成するパーフルオ
ロ・アルキルポリエーテル並びにアミノ基で変成された
ポリシロキサンは、実験例のクライトックス並びにシリ
コーンオイルＫＦ−８５９に限定するものではない。Although experiments and results are omitted, Daikin Industries Demnum was tried as a perfluoroalkyl polyether, and the side chain was modified with a monoaminoalkyl group or an amino group containing a monoaminoalkyl group. When KF-865 made by Shin-Etsu Silicone was tried as a polysiloxane, the same results as in Experiments 1 and 2 described above could be confirmed. Accordingly, the perfluoroalkyl polyether and the polysiloxane modified with an amino group constituting the antifouling liquid are not limited to Krytox and silicone oil KF-859 of the experimental examples.
【００６１】[0061]
【発明の効果】本発明は上記構成により次の効果を発揮
する。請求項１は、板ガラスの表面に透明導電層を形成
し、この透明導電層上に汚れ防止層を形成した画像読取
り装置用板ガラスにおいて、前記汚れ防止層は、パーフ
ルオロ・アルキルポリエーテルと、側鎖がモノアミノア
ルキル基またはジアミノアルキル基を含むアミノ基で変
成されたポリジメチルシロキサンと、を含有することを
特徴とし、パーフルオロ・アルキルポリエーテルは防汚
機能を発揮し、アミノ基で変成されたポリジメチルシロ
キサンは低摩擦性能を発揮する。According to the present invention, the following effects are exhibited by the above configuration. Claim 1 is a plate glass for an image reading device in which a transparent conductive layer is formed on the surface of a plate glass, and a stain prevention layer is formed on the transparent conductive layer, wherein the stain prevention layer comprises a perfluoroalkyl polyether and a side surface. A polydimethylsiloxane whose chain is modified with an amino group containing a monoaminoalkyl group or a diaminoalkyl group, and wherein the perfluoroalkylpolyether exhibits an antifouling function and is modified with an amino group. Polydimethylsiloxane exhibits low friction performance.
【００６２】従って、請求項１によれば複写機等の画像
読取り装置は、汚れのない綺麗な複写が行え且つ紙詰り
のない円滑な複写作業が行える。Therefore, according to the first aspect, the image reading apparatus such as a copying machine can perform a clean copy without dirt and can perform a smooth copy operation without paper jam.
【００６３】請求項２は、板ガラスの表面に汚れ防止層
を形成した画像読取り装置用板ガラスにおいて、汚れ防
止層は、パーフルオロ・アルキルポリエーテルと、側鎖
がモノアミノアルキル基またはジアミノアルキル基を含
むアミノ基で変成されたポリジメチルシロキサンと、を
含有することを特徴とし、パーフルオロ・アルキルポリ
エーテルは防汚機能を発揮し、アミノ基で変成されたポ
リジメチルシロキサンは低摩擦性能を発揮する。According to a second aspect of the present invention, there is provided a plate glass for an image reading apparatus in which a stain preventing layer is formed on the surface of the sheet glass. Containing polydimethylsiloxane modified with amino group, containing perfluoroalkyl polyether exhibits antifouling function, and polydimethylsiloxane modified with amino group exhibits low friction performance .
【００６４】従って、請求項２によれば複写機等の画像
読取り装置は、汚れのない綺麗な複写が行え且つ紙詰り
のない円滑な複写作業が行える。加えて、請求項２は、
透明導電層を含まぬ分、構造が簡単で画像読取り装置用
板ガラスの低コスト化を図ることができる。Therefore, according to the second aspect, the image reading apparatus such as a copying machine can perform a clean copy without dirt and can perform a smooth copy operation without paper jam. In addition, claim 2
Since the transparent conductive layer is not included, the structure is simple and the cost of the plate glass for an image reading device can be reduced.
【００６５】請求項３では、パーフルオロ・アルキルポ
リエーテルは、下記式で示されるとともに、ｎが７〜１
５０であることを特徴とする。In the third aspect, the perfluoroalkyl polyether is represented by the following formula and n is 7 to 1
50.
【００６６】[0066]
【数５】 (Equation 5)
【００６７】ｎが７未満であれば、原稿を通したときの
耐久性が不十分となる。また、ｎが１５０を超えると、
塗布液にしたときの液の粘度が高くなり過ぎて、塗布作
業に支障をきたす。ｎを７〜１５０の範囲から選択すれ
ば、汚れ防止層の耐久性を高めることと、塗布作業を円
滑にすることとの双方を満足させることができる。If n is less than 7, the durability when the document is passed becomes insufficient. Also, when n exceeds 150,
The viscosity of the coating liquid becomes too high, which hinders the coating operation. When n is selected from the range of 7 to 150, it is possible to satisfy both the enhancement of the durability of the stain prevention layer and the smoothness of the coating operation.
【００６８】請求項４では、パーフルオロ・アルキルポ
リエーテルとポリジメチルシロキサンとの混合比は、体
積比で１：４〜４：１としたことを特徴とする。According to a fourth aspect of the present invention, the mixing ratio of the perfluoroalkyl polyether and the polydimethylsiloxane is 1: 4 to 4: 1 by volume.
【００６９】混合比が１：４を下回ると、パーフルオロ
・アルキルポリエーテルが不足し、汚れ防止層の耐久性
が著しく低下し、数千枚の複写を実施した後に、汚れ防
止層が失われ、結果として汚れが発生するようになる。
一方、混合比が４：１を超えると、ポリジメチルシロキ
サンが不足して摩擦係数が増加し、紙詰りを誘起する。
混合比を、体積比で１：４〜４：１にすれば、汚れ防止
と紙詰り防止の双方をより効果的に達成することができ
る。If the mixing ratio is less than 1: 4, the perfluoroalkylpolyether becomes insufficient, and the durability of the stain preventing layer is remarkably reduced. After the thousands of copies are made, the stain preventing layer is lost. As a result, dirt is generated.
On the other hand, when the mixing ratio exceeds 4: 1, the polydimethylsiloxane becomes insufficient, the friction coefficient increases, and paper jam is induced.
When the mixing ratio is 1: 4 to 4: 1 in volume ratio, both the prevention of stains and the prevention of paper jam can be more effectively achieved.
【図１】本発明に係る画像読取り装置用板ガラス（第１
実施例）の要部拡大図FIG. 1 shows a sheet glass for an image reading apparatus according to the present invention (first glass sheet).
Example) Enlarged view of main part
【図２】本発明に係る画像読取り装置用板ガラス（第２
実施例）の要部拡大図FIG. 2 is a view illustrating a plate glass for an image reading apparatus according to the present invention (second embodiment);
Example) Enlarged view of main part
【図３】本発明に係る実験１を実施するための試料の作
製フロー図FIG. 3 is a flow chart of preparing a sample for performing Experiment 1 according to the present invention.
【図４】本発明に係る実験２を実施するための試料の作
製フロー図FIG. 4 is a flow chart of preparing a sample for carrying out Experiment 2 according to the present invention.
１０，１０Ｂ…画像読取り装置用板ガラス、１１…板ガ
ラス、１２…透明導電層、１３…汚れ防止層。10, 10B: plate glass for image reading device, 11: plate glass, 12: transparent conductive layer, 13: stain prevention layer.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｈ０４Ｎ 1/04 Ｈ０４Ｎ 1/12 Ｚ ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) H04N 1/04 H04N 1/12 Z
Claims (4)
この透明導電層上に汚れ防止層を形成した画像読取り装
置用板ガラスにおいて、前記汚れ防止層は、パーフルオ
ロ・アルキルポリエーテルと、側鎖がモノアミノアルキ
ル基またはジアミノアルキル基を含むアミノ基で変成さ
れたポリジメチルシロキサンと、を含有することを特徴
とする画像読取り装置用板ガラス。1. A transparent conductive layer is formed on a surface of a sheet glass,
In the plate glass for an image reading apparatus having an antifouling layer formed on the transparent conductive layer, the antifouling layer is modified with a perfluoroalkylpolyether and an amino group having a side chain containing a monoaminoalkyl group or a diaminoalkyl group. A sheet glass for an image reading device, comprising:
画像読取り装置用板ガラスにおいて、前記汚れ防止層
は、パーフルオロ・アルキルポリエーテルと、側鎖がモ
ノアミノアルキル基またはジアミノアルキル基を含むア
ミノ基で変成されたポリジメチルシロキサンと、を含有
することを特徴とする画像読取り装置用板ガラス。2. A plate glass for an image reading apparatus in which a stain preventing layer is formed on a surface of a sheet glass, wherein the stain preventing layer is composed of a perfluoroalkylpolyether and an amino group having a side chain containing a monoaminoalkyl group or a diaminoalkyl group. A plate glass for an image reading device, comprising: polydimethylsiloxane modified with a group.
ルは、下記式で示されるとともに、ｎが７〜１５０であ
ることを特徴とした請求項１又は請求項２記載の画像読
取り装置用板ガラス。 【数１】 3. The glass sheet for an image reading device according to claim 1, wherein the perfluoroalkyl polyether is represented by the following formula, and n is 7 to 150. (Equation 1)
ルとポリジメチルシロキサンとの混合比は、体積比で
１：４〜４：１としたことを特徴とする請求項３記載の
画像読取り装置用板ガラス。4. The plate glass for an image reading device according to claim 3, wherein the mixing ratio of the perfluoroalkyl polyether and polydimethylsiloxane is 1: 4 to 4: 1 by volume.