JP2001287301A - Composite nonwoven fabric material, bedding cover, fruit protecting bag, food preserving bag, inner sheet of food tray, sheeting mat and cover for child seat - Google Patents
Composite nonwoven fabric material, bedding cover, fruit protecting bag, food preserving bag, inner sheet of food tray, sheeting mat and cover for child seatInfo
- Publication number
- JP2001287301A JP2001287301A JP2000108495A JP2000108495A JP2001287301A JP 2001287301 A JP2001287301 A JP 2001287301A JP 2000108495 A JP2000108495 A JP 2000108495A JP 2000108495 A JP2000108495 A JP 2000108495A JP 2001287301 A JP2001287301 A JP 2001287301A
- Authority
- JP
- Japan
- Prior art keywords
- nonwoven fabric
- bag
- fabric material
- composite nonwoven
- cover
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、複合不織布材並び
にこの複合不織布材を用いてなる寝具カバー、果実保護
用袋、食品保存用袋、食品トレー中敷シート、敷マット
及びチャイルドシート用カバーに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a composite nonwoven material and a bedding cover, a fruit protection bag, a food storage bag, a food tray insole sheet, a mat, and a child sheet cover using the composite nonwoven material.
【０００２】[0002]
【従来の技術】不織布は、天然繊維又は合成繊維の一種
又は複数種を結合したシート状に形成したものである。
シート形成の方法としては、接着剤を用いる方法、機械
的に繊維を交絡させる方法、熱融着性の繊維を原料とし
て熱圧着させる方法が知られている。2. Description of the Related Art A nonwoven fabric is formed in a sheet shape by combining one or a plurality of natural fibers or synthetic fibers.
As a sheet forming method, a method using an adhesive, a method of mechanically entangled fibers, and a method of thermocompression bonding using heat-fusible fibers as a raw material are known.
【０００３】不織布はその特性を生かして種々の用途に
用いられ、抗菌性、難燃性などの機能を付与した不織布
も開発されている。なかでも注目されているのは抗菌性
を付与した製品である。[0003] Nonwoven fabrics are used for various applications by taking advantage of their properties, and nonwoven fabrics having functions such as antibacterial properties and flame retardancy have been developed. Of particular interest are products with antimicrobial properties.
【０００４】抗菌性を有する不織布は、抗菌性を有する
繊維を原材料とするものや抗菌剤を練り込んで製造した
繊維を原材料とするものが知られている。[0004] As the nonwoven fabric having antibacterial properties, there are known those using fibers having antibacterial properties as raw materials and those using fibers produced by kneading an antibacterial agent.
【０００５】[0005]
【発明が解決しようとする課題】亜鉛−アルミニウム擬
合金の溶射被膜が抗菌性を有することが知られている。
しかしながら、亜鉛−アルミニウム擬合金の溶射被膜を
形成した不織布は知られていない。本発明は、亜鉛−ア
ルミニウム擬合金の溶射被膜を有する不織布材を提供す
ることを課題とする。It is known that a sprayed coating of a zinc-aluminum pseudo-alloy has antibacterial properties.
However, a nonwoven fabric formed with a sprayed coating of a zinc-aluminum pseudo-alloy is not known. An object of the present invention is to provide a nonwoven fabric material having a sprayed coating of a zinc-aluminum pseudo alloy.
【０００６】また、本願発明になる不織布材は、抗菌性
・保温性・防臭性などの特性を有しており、このような
特性を利用した各種の製品を提供することができる。Further, the nonwoven fabric material according to the present invention has properties such as antibacterial properties, heat retention properties and deodorant properties, and various products utilizing such properties can be provided.
【０００７】従って、本発明は、抗菌性を有する寝具カ
バーを提供することを課題とする。さらに、本発明は、
抗菌性を有する果実保護用袋を提供することを課題とす
る。さらに、本発明は、抗菌性を有する食品保存用袋を
提供することを課題とする。さらに、本発明は、抗菌性
を有する食品トレー中敷シートを提供することを課題と
する。さらに、本発明は、抗菌性を有する敷マットを提
供することを課題とする。さらに、本発明は、抗菌性を
有するチャイルドシート用カバーを提供することを課題
とする。Therefore, an object of the present invention is to provide a bedding cover having antibacterial properties. Further, the present invention provides
An object of the present invention is to provide an antibacterial fruit protection bag. Furthermore, an object of the present invention is to provide a food storage bag having antibacterial properties. A further object of the present invention is to provide a food tray insole sheet having antibacterial properties. A further object of the present invention is to provide a mat having antibacterial properties. A further object of the present invention is to provide a child seat cover having antibacterial properties.
【０００８】[0008]
【課題を解決するための手段】請求項１に記載の発明
は、少なくとも一方が不織布である２枚の布地の間に亜
鉛−アルミニウム擬合金溶射被膜層を形成してなる複合
不織布材である。The present invention according to claim 1 is a composite nonwoven fabric material in which a zinc-aluminum pseudo-alloy sprayed coating layer is formed between two fabrics, at least one of which is a nonwoven fabric.
【０００９】熱融着性を有する不織布を用いて亜鉛−ア
ルミニウム擬合金溶射被膜を形成すると不織布を損なう
ことなく溶射被膜をきれいに形成することができること
から、不織布としては熱融着性を有する不織布を用いる
のが好ましい。When a zinc-aluminum pseudo-alloy sprayed coating is formed using a heat-fusible nonwoven fabric, the sprayed coating can be formed neatly without damaging the nonwoven fabric. It is preferably used.
【００１０】すなわち、請求項２に記載の発明は、熱融
着性を有する不織布に亜鉛−アルミニウム擬合金溶射被
膜を形成してこれを他の布地と重ねあわせてなる請求項
１に記載の複合不織布材である。That is, the invention according to claim 2 is a composite according to claim 1, wherein a zinc-aluminum pseudo-alloy sprayed coating is formed on a heat-fusible nonwoven fabric and this is laminated with another cloth. It is a non-woven material.
【００１１】不織布と柔軟な木綿布地とを組み合わせる
と、医療用の被覆用品素材として好適な材料を得ること
ができる。ここで、医療用の被覆用品とは、マスク、包
帯、手術後などに用いられる腹帯、丁字帯又は三角布な
どである。また、柔軟な木綿布地としては、晒木綿布地
やガーゼ布地が挙げられる。When a nonwoven fabric and a soft cotton fabric are combined, a material suitable as a medical covering article material can be obtained. Here, the medical covering article is a mask, a bandage, an abdominal band, a T-shaped band, a triangular cloth, or the like used after an operation or the like. Soft cotton fabrics include bleached cotton fabrics and gauze fabrics.
【００１２】すなわち、請求項３に記載の発明は、不織
布と柔軟な木綿布地とを組み合わせてなる請求項１又は
２に記載の複合不織布材である。That is, a third aspect of the present invention is a composite nonwoven fabric material according to the first or second aspect, wherein the nonwoven fabric is combined with a soft cotton fabric.
【００１３】請求項１、２又は３に記載の複合不織布材
は抗菌性・防臭性に優れていることから、寝具、特に病
院において使用される寝具のカバーとして優れている。
すなわち、本願請求項４に記載の発明は、請求項１、２
又は３に記載の複合不織布材を用いてなる寝具カバーで
ある。Since the composite nonwoven fabric material according to the first, second or third aspect is excellent in antibacterial properties and deodorization properties, it is excellent as a cover for bedding, particularly bedding used in hospitals.
That is, the invention described in claim 4 of the present application is equivalent to claims 1 and 2
Or a bedding cover using the composite nonwoven fabric material according to 3.
【００１４】ここで寝具とは、ベッド、敷布団、枕、掛
け布団、毛布等を意味しており、従って、寝具カバーと
は、これらの寝具が汚れるのを防止するために使用され
るカバーであり、具体的には、ベッドシーツ、枕カバ
ー、敷布、掛け布団カバー、毛布カバー等である。病院
やホテルにおいて使用されるこれらの寝具カバーは、従
来はクリーニングして再利用されていた。ところが最近
病院においては、院内感染を防ぐために安価な不織布製
品が使用され、使用済みの寝具カバーは使い捨てとし、
回収して焼却処分されるようになっている。寝具を通し
ての細菌感染を防ぐためである。また、ホテルなどにお
いてもクリーニングするコスト面で有利でありかつ清潔
感が得られることから、不織布製品を使い捨てとする傾
向がある。ところが、寝具カバーは、肌に直接触れるこ
とがあることから、有機系の抗菌剤を練り込んだ製品
は、特に小児用に用いる寝具については使用することが
できなかった。しかるに、本発明になる寝具カバーはア
ルミニウムと亜鉛を使用し、他に有害な成分を使用して
いないので安心して使用することができる。Here, the bedding means a bed, a mattress, a pillow, a comforter, a blanket, and the like. Therefore, the bedding cover is a cover used to prevent these beddings from being stained. Specifically, it is a bed sheet, a pillow cover, a mattress, a comforter cover, a blanket cover, or the like. These bedding covers used in hospitals and hotels have traditionally been cleaned and reused. However, in recent hospitals, inexpensive non-woven products have been used to prevent nosocomial infections, and used bedding covers have been disposable.
Collected and incinerated. This is to prevent bacterial infection through bedding. Also, in hotels and the like, there is a tendency that nonwoven fabric products are disposable because they are advantageous in terms of cleaning costs and can provide a clean feeling. However, since the bedding cover may come into direct contact with the skin, products incorporating an organic antibacterial agent cannot be used, particularly for bedding used for children. However, since the bedding cover according to the present invention uses aluminum and zinc and does not use any other harmful components, it can be used with confidence.
【００１５】また、請求項１又は２に記載の複合不織布
材は抗菌性に優れていることから、果実保護用袋として
優れている。すなわち、請求項５に記載の発明は、請求
項１又は２に記載の複合不織布材を袋状に形成してなる
果実類保護用袋である。Further, the composite nonwoven fabric material according to claim 1 or 2 is excellent in antibacterial properties, and thus is excellent as a bag for protecting fruits. That is, the invention according to claim 5 is a fruit protection bag formed by forming the composite nonwoven fabric material according to claim 1 or 2 into a bag shape.
【００１６】モモ、ナシ、ブドウ、リンゴなどは、害虫
を防ぐために袋かけをしている。従来袋かけ用の袋の材
料としては、新聞紙、ハトロン紙、パラフィン紙が使用
されていたが、これらは抗菌性を有していない。本発明
になる果実保護用袋は、抗菌性を有するため、薬剤散布
を少なくすることができる。[0016] Peach, pear, grape, apple and the like are bagged to prevent pests. Conventionally, as a material for a bag for bagging, newspaper, haptron paper, and paraffin paper have been used, but these do not have antibacterial properties. Since the fruit protection bag according to the present invention has antibacterial properties, it is possible to reduce the application of the medicine.
【００１７】また、請求項１又は２に記載の複合不織布
材は抗菌性に優れていることから、食品保存用袋として
優れている。すなわち、請求項６に記載の発明は、請求
項１又は２に記載の複合不織布材を袋状に形成してなる
食品保存用袋である。Further, the composite nonwoven fabric material according to claim 1 or 2 has excellent antibacterial properties and is therefore excellent as a bag for storing food. That is, the invention according to claim 6 is a food storage bag obtained by forming the composite nonwoven fabric material according to claim 1 or 2 into a bag shape.
【００１８】また、請求項１又は２に記載の複合不織布
材は抗菌性に優れていることから、食品トレー中敷き用
シートとして優れている。すなわち、請求項７に記載の
発明は、請求項１又は２に記載の複合不織布材を用いて
なる食品トレー中敷シートである。Further, the composite nonwoven fabric material according to claim 1 or 2 has excellent antibacterial properties, and thus is excellent as a sheet for laying in a food tray. That is, the invention according to claim 7 is a food tray insole sheet using the composite nonwoven fabric material according to claim 1 or 2.
【００１９】従来、特に生鮮食品用のトレーには、食品
の腐敗を防ぐためにアルコールを含浸させた不織布を中
敷きシートとして用いている。しかしながら、アルコー
ルは揮発性があるため時間の経過とともに効果がなくな
る。本発明になる食品トレー中敷き用シートは不揮発性
の亜鉛−アルミニウムが材料であるので効果に永続性が
ある。Conventionally, a non-woven fabric impregnated with alcohol has been used as an insole sheet especially for trays for fresh foods in order to prevent spoilage of foods. However, alcohol is volatile and loses its effect over time. The food tray insole sheet according to the present invention is made of non-volatile zinc-aluminum, and has a permanent effect.
【００２０】また、請求項１又は２に記載の複合不織布
材は抗菌性に優れていることから、敷マットの芯材とし
て優れている。すなわち、請求項８に記載の発明は、請
求項１又は２に記載の複合不織布材を芯材としてなる敷
マットである。Further, the composite nonwoven fabric material according to claim 1 or 2 is excellent in antibacterial properties, and therefore, is excellent as a core material of a mat. That is, the invention according to claim 8 is a mat that uses the composite nonwoven fabric material according to claim 1 or 2 as a core material.
【００２１】また、請求項１又は２に記載の複合不織布
材は抗菌性及び防臭性に優れていることからチャイルド
シートカバー用芯材として優れている。すなわち、請求
項９に記載の発明は、請求項１又は２に記載の複合不織
布材を芯材としてなるチャイルドシート用カバーであ
る。Further, the composite nonwoven fabric material according to claim 1 or 2 has excellent antibacterial properties and deodorant properties, and thus is excellent as a core material for a child seat cover. That is, the invention according to claim 9 is a child seat cover using the composite nonwoven fabric material according to claim 1 or 2 as a core material.
【００２２】[0022]
【発明の実施の形態】本発明において用いられる不織布
としては特に制限はなく、天然繊維例えば木綿繊維、化
学繊維例えばレーヨン繊維又は合成繊維例えばポリプロ
ピレン繊維などを原材料として、接着剤を使用して、機
械的に交絡させ又は熱的に融着させるなどの手段により
ウェッブ状としたものなどが挙げられる。不織布の厚さ
（通常米坪で表される）については特に制限はなく、市
販されている範囲の厚さ（米坪：４０ｇ〜２５０ｇ／ｍ
２）のものが用途によって適宜選択して使用される。熱
融着性を有する不織布を用いて亜鉛−アルミニウム擬合
金溶射被膜を形成すると不織布を損なうことなく溶射被
膜をきれいに形成することができる。熱融着性を有する
不織布としては、例えば、高融点樹脂と低融点樹脂とを
芯鞘構造やサイドバイサイド構造として組み合わせた複
合繊維を用いた不織布や熱融着性を有しない繊維層と前
記熱融着性を有する繊維層とを複合した不織布（例えば
特開平１０−２８０２６６号公報参照）などが挙げられ
る。BEST MODE FOR CARRYING OUT THE INVENTION The non-woven fabric used in the present invention is not particularly limited, and a natural fiber such as a cotton fiber, a chemical fiber such as a rayon fiber or a synthetic fiber such as a polypropylene fiber is used as a raw material and an adhesive is used. And a web-like material by means such as entanglement or thermal fusion. There is no particular limitation on the thickness of the nonwoven fabric (usually expressed in U.S.P.), and the thickness in the commercially available range (U.S.P .: 40 g to 250 g / m2)
2 ) is appropriately selected and used depending on the application. When a zinc-aluminum pseudo-alloy sprayed coating is formed using a non-woven fabric having heat-fusibility, the sprayed coating can be formed cleanly without damaging the non-woven fabric. Examples of the heat-fusible nonwoven fabric include, for example, a nonwoven fabric using a composite fiber in which a high-melting-point resin and a low-melting-point resin are combined in a core-sheath structure or a side-by-side structure, or a fiber layer having no heat-fusibility. A nonwoven fabric (for example, see Japanese Patent Application Laid-Open No. 10-280266) in which a fiber layer having adhesiveness is compounded is exemplified.
【００２３】亜鉛−アルミニウム擬合金被膜を形成する
ための溶射方法としては、低温で溶射可能であることか
ら、アーク溶射、特に、インバータードライブアーク溶
射装置によるのが好ましい。インバータードライブアー
ク溶射装置は、４００００Ｈｚの高周波電源を用い、減
圧内アーク溶融された溶射材料を高速のエアーにより吹
き付けることで、被溶射面の温度を４０〜５０℃程度で
溶射可能である。そして、溶射材料として亜鉛線とアル
ミニウム線を同時に溶射ガンに供給することにより亜鉛
−アルミニウム擬合金被膜を形成することができるもの
である。As a thermal spraying method for forming a zinc-aluminum pseudo-alloy coating, it is preferable to use arc thermal spraying, particularly, an inverter drive arc thermal spraying apparatus because thermal spraying can be performed at a low temperature. The inverter drive arc spraying apparatus can spray at a temperature of the surface to be sprayed at about 40 to 50 ° C. by using a high-frequency power source of 40000 Hz and spraying a high-pressure air with a sprayed material that has been arc-melted under reduced pressure. Then, a zinc-aluminum pseudo-alloy coating can be formed by simultaneously supplying a zinc wire and an aluminum wire as spray materials to a spray gun.
【００２４】亜鉛−アルミニウム擬合金被膜における亜
鉛とアルミニウムとの組成比は、体積比で亜鉛２０から
８０、アルミニウム８０〜２０の範囲とすることが好ま
しく、亜鉛が４０から６０、アルミニウム６０から４０
とすることがより好ましい。亜鉛−アルミニウム擬合金
被膜における亜鉛とアルミニウムとの組成比は、インバ
ータードライブアーク溶射装置によるときは、亜鉛線と
アルミニウム線の送り速度を調整することにより調整す
るこができるThe composition ratio of zinc to aluminum in the zinc-aluminum pseudo-alloy coating film is preferably in the range of 20 to 80 zinc and 80 to 20 aluminum by volume, with 40 to 60 zinc and 60 to 40 aluminum.
Is more preferable. The composition ratio of zinc and aluminum in the zinc-aluminum pseudo-alloy coating can be adjusted by adjusting the feed speed of the zinc wire and the aluminum wire when using an inverter drive arc spraying device.
【００２５】溶射被膜の付着量については、亜鉛−アル
ミニウム擬合金によりほぼ全面にカバーされて不織布地
が露出していない程度でよく、具体的には、２．０ｇ／
ｍ２程度であればよい。溶射被膜の付着量が少ないと抗
菌性等の効果が劣る傾向がある。The amount of the thermal spray coating is sufficient to cover almost the entire surface with the zinc-aluminum pseudo alloy and not to expose the non-woven fabric. Specifically, 2.0 g / g
m 2 is sufficient. If the amount of the sprayed coating is small, the effects such as antibacterial properties tend to be inferior.
【００２６】亜鉛−アルミニウム擬合金を溶射した不織
布を１枚と溶射被膜を形成しない不織布、又は、他の任
意の布地とを重ね、又は亜鉛−アルミニウム擬合金を溶
射した不織布を２枚重ねて一体化して本発明の複合不織
布材とする。重ね合わせは、芯材として用いる場合を除
き、溶射した面が内側となるようにするのが好ましい。
溶射被膜が脱落して肌、食品などに触れないようにする
ためである。熱融着性の不織布を用いている場合には、
布地を一体化する方法としては加熱ロールによる熱融着
によることができる。例えば、溶射被膜を形成した不織
布と他の不織布とを重ね合わせ、加熱ロールの間を通し
て一体化する。このほか接着剤を用いる方法によること
もできる。なお、果実保護用袋及び食品保存用袋の場合
は例えば所定の寸法に裁断して袋の口となる部分を除い
て周縁をほぼ２〜５ｍｍ程度の幅でシールして袋状に形
成することにより複合不織布材とする。One piece of non-woven fabric sprayed with a zinc-aluminum pseudo-alloy is laminated with a non-woven fabric that does not form a thermal spray coating, or any other fabric, or two non-woven fabrics sprayed with a zinc-aluminum pseudo-alloy are laminated and integrated. Into a composite nonwoven fabric material of the present invention. It is preferable that the superimposition be performed so that the sprayed surface is on the inside, except when used as a core material.
This is to prevent the thermal spray coating from falling off and coming into contact with skin, food, and the like. When using a heat-fusible nonwoven fabric,
As a method of integrating the fabric, heat fusion with a heating roll can be used. For example, the non-woven fabric on which the thermal spray coating is formed and another non-woven fabric are overlapped and integrated by passing between heating rolls. In addition, a method using an adhesive can also be used. In the case of a bag for protecting fruit and a bag for storing food, for example, the bag should be cut into a predetermined size, and the peripheral edge thereof should be sealed in a width of about 2 to 5 mm except for a portion to be a mouth of the bag to form a bag. To form a composite nonwoven material.
【００２７】[0027]
【実施例】実施例１ 幅２０２０ｍｍ、米坪５３．７ｇ／ｍ２の不織布（繊維
材質：ポリエステル・レーヨン・ナイロン混紡＋ポリエ
チレン繊維による熱融着層を形成したもの、日本バイリ
ーン株式会社製を使用）に、溶射材料としてそれぞれ、
直径１．３ｍｍの亜鉛線及びアルミニウム線を用い、高
周波電圧２０Ｖ、電流２７０Ａ、空気圧７ｋｇ／ｃｍ２
の条件でインバータードライブ溶射装置を用いて亜鉛−
アルミニウム擬合金被膜を形成した。溶射被膜の付着量
は、２．８ｇ／ｍ２であった。以下この材料を溶射不織
布とする。同じ材質の不織布を重ね、ロール圧着するこ
とにより複合不織布材を得た。Example 1 Non-woven fabric having a width of 2020 mm and a size of 53.7 gm / m 2 in U.S.A. (fiber material: a polyester / rayon / nylon blended fiber and a heat-sealing layer formed of polyethylene fibers, manufactured by Japan Vilene Co., Ltd.) )
Using a zinc wire and an aluminum wire having a diameter of 1.3 mm, a high-frequency voltage of 20 V, a current of 270 A, and an air pressure of 7 kg / cm 2
Using an inverter drive spraying device under the conditions of
An aluminum pseudoalloy coating was formed. The adhesion amount of the thermal spray coating was 2.8 g / m 2 . Hereinafter, this material is referred to as a sprayed nonwoven fabric. A nonwoven fabric of the same material was stacked and roll-pressed to obtain a composite nonwoven fabric material.
【００２８】作製した複合不織布材から３５×５５ｍｍ
の大きさの試験片を切り出し、繊維製品衛生加工協議会
で制定した抗菌防臭加工製品の加工効果評価試験マニュ
アルの、『II．１ 菌数測定法』に準拠して、黄色ぶど
う状球菌（スタフィロコッカス アウレウス ＡＴＣＣ
６５３８Ｐ）を含む培養液を吸収させ、１８時間室温に
て静置培養した後の生菌数を調べることにより抗菌性を
テストした。その結果を表１に示す。なお表１において
対照例とは溶射被膜を形成しないほかは実施例１と同様
にして作製した複合不織布材を試験片としたものであ
る。35 × 55 mm from the prepared composite nonwoven fabric material
A test piece of the size was cut out, and the processing effect evaluation test manual for antibacterial and deodorized products established by the Textile Sanitary Processing Council, “II. Staphylococcus aureus ATCC
The antibacterial property was tested by absorbing the culture solution containing 6538P) and examining the viable cell count after stationary culture at room temperature for 18 hours. Table 1 shows the results. Note that in Table 1, the control example is a composite nonwoven fabric prepared in the same manner as in Example 1 except that a thermal spray coating was not formed, which was used as a test piece.
【００２９】[0029]
【表１】 [Table 1]
【００３０】実施例２ 実施例１で作製した複合不織布材を１２００×１５００
ｍｍに裁断してシーツとした。このシーツを小児病棟に
おいて使用した。シーツ交換の頻度は３日に１回とし
て、１月間使用した。使用後のシーツを２枚抜き取り、
中央付近を３５×５５ｍｍに裁断し、これをポリオキシ
エチレンソルビタンモノオレート０．２％添加生理食塩
水で洗い出し、普通寒天培地で４８時間培養することに
より付着生菌数を調べた。その結果、付着した生菌数は
２０であった。比較のため、溶射被膜を形成しないほか
は実施例１と同様にして作製した複合不織布材をシーツ
として用いた場合の付着生菌数は３．５×１０８であっ
た。Example 2 The composite nonwoven fabric material prepared in Example 1 was 1200 × 1500
The sheet was cut into mm to obtain a sheet. The sheets were used in a pediatric ward. Sheets were changed once every three days and used for one month. Remove two sheets after use,
The vicinity of the center was cut into a size of 35 × 55 mm, washed with physiological saline containing 0.2% of polyoxyethylene sorbitan monooleate, and cultured on a normal agar medium for 48 hours to determine the number of adherent bacteria. As a result, the number of viable bacteria adhered was 20. For comparison, the viable cell count was 3.5 × 10 8 when the composite nonwoven fabric material prepared in the same manner as in Example 1 was used as a sheet except that no thermal spray coating was formed.
【００３１】実施例３ 実施例１で作製した複合不織布材を、新品の枕のカバー
として、ポマードを整髪料として使用する男性の使用に
供した。枕カバーを毎日取り替えて１月間連続して使用
した後、健常者１０名による臭いテストに枕本体を供し
たところ、臭い不感が９名であり、臭いありが１名であ
った。比較のため、溶射被膜を形成しないほかは実施例
１と同様にして作製した複合不織布材を用いた場合は、
臭い不感が２名であり、臭いありが８名であった。Example 3 The composite nonwoven fabric material prepared in Example 1 was used as a cover for a new pillow and used by men who used Pomade as a hairdressing agent. After continuously using the pillow cover every day for one month after replacing the pillow cover, the pillow body was subjected to an odor test by 10 healthy persons. As a result, 9 persons did not feel odor and 1 person had odor. For comparison, when a composite nonwoven fabric material prepared in the same manner as in Example 1 except that no thermal spray coating was formed was used,
Two people felt no smell and eight people smelled.
【００３２】実施例４ 溶射不織布を２枚、１９０×２１０ｍｍに裁断し、３辺
を熱融着して袋状に形成して果実保護用袋とした。この
果実保護用袋をナシの袋かけに使用した。試験数は１０
個として、袋除去後に罹病した果実はなかった。比較の
ため、溶射被膜を形成しないほか同様にして作製した果
実保護用袋を用いた場合、罹病した果実数は２個であっ
た。Example 4 Two thermally sprayed nonwoven fabrics were cut into a size of 190 × 210 mm, and three sides were heat-sealed to form a bag shape, thereby obtaining a fruit protection bag. This bag for protecting fruits was used for hanging pears. 10 tests
As an individual, there was no diseased fruit after bag removal. For comparison, the number of diseased fruits was 2 when a fruit-protecting bag prepared in the same manner except that no thermal spray coating was formed was used.
【００３３】実施例５ 溶射不織布を２枚、３００×３００ｍｍに裁断し、３辺
を熱融着して袋状に形成して食品保存用袋とした。この
食品保存用袋を用いて、１０℃に保たれた冷蔵庫中にマ
グロ切身を保存した。１週間後に食品の状態を調べた
が、異常なしであった。比較のため、溶射被膜を形成し
ないほか同様にして作製した食品保存用袋を用いた場
合、１週間後には腐敗が始まっていた。Example 5 Two sprayed nonwoven fabrics were cut into 300 × 300 mm, and three sides were heat-sealed to form a bag shape, thereby obtaining a bag for storing food. Using this food storage bag, tuna cuts were stored in a refrigerator kept at 10 ° C. One week later, the condition of the food was checked, and no abnormalities were found. For comparison, in the case of using a food storage bag prepared in the same manner except that no thermal spray coating was formed, decay had started one week later.
【００３４】実施例６ 実施例１で作製した複合不織布材を１５０×５０ｍｍに
裁断して食品トレー中敷き用シートとした。これを発泡
スチロール製食品トレーの中敷きとして使用し、マグロ
切身を置き食品包装用フィルムでラッピングした。これ
を１０℃に保たれた冷蔵庫中に保存した。１週間後に食
品の状態を調べたが、異常なしであった。比較のため、
溶射被膜を形成しないほか同様にして作製した食品トレ
ー中敷き用シートを用いた場合、１週間後には腐敗が始
まっていた。Example 6 The composite nonwoven fabric prepared in Example 1 was cut into a size of 150 × 50 mm to form a sheet for laying in a food tray. This was used as an insole for the food tray made of Styrofoam, and the tuna cut was placed and wrapped with a food packaging film. This was stored in a refrigerator kept at 10 ° C. One week later, the condition of the food was checked, and no abnormalities were found. For comparison,
In the case of using a sheet for laying in a food tray similarly prepared except that a thermal spray coating was not formed, decay had started one week later.
【００３５】実施例７ 実施例１で作製した複合不織布材を芯材とし、パイル地
を表地とするトイレ用マットを作製した。これをトイレ
にて１週間使用した後、便器側の縁中央付近を３５×５
５ｍｍに裁断し、これをポリオキシエチレンソルビタン
モノオレート０．２％添加生理食塩水で洗い出し、普通
寒天培地で４８時間培養することにより付着生菌数を調
べた。その結果、付着した生菌数は１０３個／ｍｌであ
った。比較のため、溶射被膜を形成しないほかは同様に
して作製したトイレ用マットについての付着生菌数は８
×１０５／ｍｌであった。Example 7 A toilet mat having a pile material as a surface material was produced using the composite nonwoven fabric material produced in Example 1 as a core material. After using this in the toilet for one week, 35 × 5
It was cut to 5 mm, washed with physiological saline containing 0.2% polyoxyethylene sorbitan monooleate, and cultured on a normal agar medium for 48 hours to determine the number of adherent bacteria. As a result, the viable cell count adhering was 10 3 / ml. For comparison, the number of viable bacteria on a toilet mat prepared in the same manner except that no thermal spray coating was formed was 8
× 10 5 / ml.
【００３６】実施例８ 実施例１で作製した複合不織布材を芯材とし、メッシュ
地を表裏に用いてチャイルドシートカバーを作製した。
このチャイルドシートカバーをチャイルドシートに装着
して、１日平均１時間、６０日間、１才の男児の乗用に
供した。使用した後、健常者１０名による臭いテストに
供したところ、臭い不感が０名であり、臭いありが１０
名であった。比較のため、溶射被膜を形成しない不織布
を芯材として作製したチャイルドシートカバーを用いた
場合は、臭い不感が３名であり、臭いありが７名であっ
た。Example 8 A child seat cover was manufactured using the composite nonwoven fabric material prepared in Example 1 as a core material and a mesh fabric on both sides.
The child seat cover was attached to the child seat and used for a 1-year-old boy for an average of 1 hour per day for 60 days. After use, when subjected to an odor test by 10 healthy persons, no odor was detected by 0 persons, and 10 persons
Was a name. For comparison, when a child seat cover produced using a nonwoven fabric having no thermal spray coating as a core material was used, three persons had no odor and seven persons had an odor.
【００３７】[0037]
【発明の効果】以上本発明によれば、亜鉛−アルミニウ
ム擬合金の溶射被膜を有する不織布材を提供することが
でき、本願発明になる不織布材は、抗菌性・保温性・防
臭性などの特性を有しており、このような特性を利用し
た寝具カバー、果実保護用袋、食品保存用袋、食品トレ
ー中敷シート、敷マット及びチャイルドシート用カバー
を提供することができる。As described above, according to the present invention, it is possible to provide a non-woven material having a sprayed coating of a zinc-aluminum pseudo-alloy, and the non-woven material according to the present invention has properties such as antibacterial property, heat retention property and deodorant property. It is possible to provide a bedding cover, a bag for protecting fruits, a bag for storing food, a cover for a food tray insole sheet, a mat and a child sheet utilizing such characteristics.
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.7 識別記号 ＦＩ テーマコート゛(参考） Ｄ０４Ｈ 1/54 Ｄ０４Ｈ 1/54 Ｃ ４Ｌ０３１ 5/06 5/06 ４Ｌ０４７ Ｄ０６Ｍ 11/83 Ｄ０６Ｍ 11/00 Ａ Ｆターム(参考） 2B024 FB03 FC04 3B102 BA10 3E064 AA05 BA12 BA30 BA44 BA60 BC18 BC20 EA18 GA01 HN05 4B021 LA15 LA17 LA24 LW03 MC01 MK08 MP10 4F100 AB10C AB18C AB31C BA03 BA07 BA10A BA10B CB03A DG11B DG15A DG15B DG18 EH56C GB15 GB23 GB66 GB71 JC00 JJ02 JL12A 4L031 AA02 AB01 AB34 BA05 CB10 DA00 DA12 DA13 4L047 AA08 AA14 AA23 AA28 BA09 BB01 CA05 CC02 CC16 DA00 EA11 ──────────────────────────────────────────────────続 き Continued on the front page (51) Int.Cl. 7 Identification symbol FI Theme coat ゛ (Reference) D04H 1/54 D04H 1/54 C 4L031 5/06 5/06 4L047 D06M 11/83 D06M 11/00 A F Terms (reference) 2B024 FB03 FC04 3B102 BA10 3E064 AA05 BA12 BA30 BA44 BA60 BC18 BC20 EA18 GA01 HN05 4B021 LA15 LA17 LA24 LW03 MC01 MK08 MP10 4F100 AB10C AB18C AB31C BA03 BA07 BA10A BA10B CB03 GB1 DG11B12 DG11B15 DG11B12 AA02 AB01 AB34 BA05 CB10 DA00 DA12 DA13 4L047 AA08 AA14 AA23 AA28 BA09 BB01 CA05 CC02 CC16 DA00 EA11
Claims (9)
地の間に亜鉛−アルミニウム擬合金溶射被膜層を形成し
てなる複合不織布材。1. A composite non-woven fabric material comprising a zinc-aluminum pseudo-alloy sprayed coating layer formed between two fabrics, at least one of which is a non-woven fabric.
ニウム擬合金溶射被膜を形成してこれを他の布地と重ね
あわせてなる請求項１に記載の複合不織布材。2. The composite non-woven fabric material according to claim 1, wherein a zinc-aluminum pseudo-alloy sprayed coating is formed on a heat-fusible non-woven fabric, and this is laminated with another fabric.
てなる請求項１又は２に記載の複合不織布材。3. The composite nonwoven fabric material according to claim 1, wherein the nonwoven fabric is combined with a soft cotton fabric.
材を用いてなる寝具カバー。4. A bedding cover using the composite nonwoven fabric material according to claim 1.
袋状に形成してなる果実類保護用袋。5. A bag for protecting fruits formed by forming the composite nonwoven fabric material according to claim 1 or 2 into a bag shape.
袋状に形成してなる食品保存用袋。6. A food storage bag formed by forming the composite nonwoven fabric material according to claim 1 into a bag shape.
用いてなる食品トレー中敷シート。7. A food tray insole sheet using the composite nonwoven fabric material according to claim 1 or 2.
芯材としてなる敷マット。8. A mat comprising the composite nonwoven fabric material according to claim 1 or 2 as a core material.
芯材としてなるチャイルドシート用カバー。9. A child seat cover comprising the composite nonwoven fabric material according to claim 1 or 2 as a core material.