JP2000282338A - Mass-colored crimped polyamide yarn and carpet - Google Patents
Mass-colored crimped polyamide yarn and carpetInfo
- Publication number
- JP2000282338A JP2000282338A JP11086597A JP8659799A JP2000282338A JP 2000282338 A JP2000282338 A JP 2000282338A JP 11086597 A JP11086597 A JP 11086597A JP 8659799 A JP8659799 A JP 8659799A JP 2000282338 A JP2000282338 A JP 2000282338A
- Authority
- JP
- Japan
- Prior art keywords
- yarn
- carpet
- polyamide
- crimped yarn
- origin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明はポリアミド原着捲縮
糸およびカーペットに関するものである。さらに詳しく
は、耐候性、耐摩耗性、ポイント性に優れ、かつ風合い
や製糸性に優れたポリアミド原着捲縮糸およびこのポリ
アミド原着捲縮糸から作られ、特に玄関マットや足拭き
マットなどの用途に好ましく適用されるカーペットに関
するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a crimped yarn and a carpet. More specifically, it is made of a polyamide crimped yarn excellent in weather resistance, abrasion resistance, point properties, and excellent in texture and spinnability, and made from this polyamide crimped yarn. The present invention relates to a carpet that is preferably applied to the use of a carpet.
【０００２】[0002]
【従来の技術】ナイロン６６マルチフィラメントの嵩高
捲縮糸は、その優れた耐候性、耐摩耗性などを生かし
て、従来からカーペットに代表される種々のインテリア
用途素材として用いられている。そして、近年では、カ
ーペット用途の多様化に伴い、カーペットを店舗や事務
所むけの玄関マットや足拭きマットへ展開する技術も進
んでいる。2. Description of the Related Art A bulky crimped yarn of nylon 66 multifilament has been conventionally used as a material for various interior applications represented by carpets, taking advantage of its excellent weather resistance and abrasion resistance. In recent years, with the diversification of carpet applications, the technology of developing carpets into entrance mats and foot-wiping mats for stores and offices has also been advanced.
【０００３】従来、玄関マットや足拭きマットは、泥落
としを主目的としたものであり、金網、プラスチックシ
ートを素材とするものが一般的であったが、金網やプラ
スチックシートでは、高級感を持った雰囲気を提供する
には限界があり、特に店舗や事務所の玄関を演出するに
は不適であった。しかも、金網やプラスチックシートを
素材とする玄関マットや足拭きマットでは、比較的大き
い泥を落とすに点では泥落とし性能に優れているもの
の、比較的小さな泥、埃、塵を捕捉することは不向きで
あった。Conventionally, entrance mats and foot-wiping mats have been mainly used for removing mud, and are generally made of wire mesh or plastic sheet. There was a limit in providing a unique atmosphere, and it was particularly unsuitable for producing a store or office entrance. In addition, door mats and foot wiping mats made of wire mesh or plastic sheets have excellent mud-dropping performance in terms of dropping relatively large mud, but are not suitable for catching relatively small mud, dust, and dust. Met.
【０００４】また、金網やプラスチックシートを素材と
する玄関マットや足拭きマットは、その構成からわかる
ように、いわゆるカーペットに比較してクッション性が
明らかに劣るものであった。さらに、玄関マットや端拭
きマットは、建物の入り口に設置されることから太陽光
にさらされるため、紫外線に対する耐候性が要求され、
またその設置環境から多くの人が足でふみつけられるば
かりか、汚れを落とすために繰り返し洗濯して使用され
るため、優れた耐久性が要求される。[0004] Further, as can be seen from the configuration, the entrance mat and the foot wiping mat made of a wire net or a plastic sheet have a cushioning property that is clearly inferior to that of a so-called carpet. In addition, door mats and end wipes are exposed to sunlight because they are installed at the entrance of the building, so weather resistance to ultraviolet light is required,
In addition, because of the installation environment, not only many people can touch with their feet, but also they are repeatedly washed and used to remove dirt, so that excellent durability is required.
【０００５】一方、カーペットの耐候性能向上を目的と
した原着ポリアミド捲縮糸の方法については、すでにい
くつかの提案がなされており、例えば特開平２−１６９
７３６号公報には、特定の顔料添加および銅添加により
耐候性能にすぐれた原着ポリアミド捲縮糸を製造する方
法が開示されている。[0005] On the other hand, there have already been proposed several methods for producing a so-called crimped polyamide yarn for the purpose of improving the weather resistance of a carpet.
Japanese Patent Publication No. 736 discloses a method for producing a soaked polyamide crimped yarn having excellent weatherability by adding a specific pigment and copper.
【０００６】しかしながら、上記特開平２−１６９７３
６号公報に記載の方法では、ナイロン６６特有の問題で
ある球晶成長の問題が解決されていないことから、他の
顔料組成物を使用する場合には製糸性が悪く安定に生産
できないという問題があり、このことはさらに多色展開
が難しいという問題にもつながっていた。[0006] However, Japanese Patent Application Laid-Open No. Hei 2-16973 discloses the above.
In the method described in JP-A No. 6-2006, the problem of spherulite growth, which is a problem peculiar to nylon 66, has not been solved. This led to the problem that multicolor development was more difficult.
【０００７】また、特表平５−５０４３８５号公報に
は、ポリヘキサメチレンアジパミドの球晶を抑制し延伸
性を向上させることを目的として、ポリヘキサメチレン
アジパミド中にカプロアミドを５〜３０重量％共重合さ
せるか、もしくはポリカプロアミド５〜３０重量％を有
意の共重合をおこすことなくブレンドする方法が提案さ
れている。Further, Japanese Patent Application Laid-Open No. 5-504385 discloses that, in order to suppress the spherulites of polyhexamethylene adipamide and to improve the stretchability, caproamide is added to polyhexamethylene adipamide. Methods have been proposed in which 30% by weight are copolymerized or 5 to 30% by weight of polycaproamide are blended without significant copolymerization.
【０００８】上記特表平５−５０４３８５号公報に記載
の方法では、確かにポリヘキサメチレンアジパミドホモ
ポリマーに比較すると球晶抑制効果は確実に認められる
ものの、このポリマーに顔料を添加し製糸する上では、
共重合あるいはブレンド各々の単独効果による球晶抑制
効果が小さく、球晶抑制効果を得るためにはブレンドあ
るいは共重合成分の量が２０重量％を上回ることが必要
となる。つまり、ポリヘキサメチレンアジパミドが８０
重量％を下回ることが確実となるため、ポリヘキサメチ
レンアジパミド特有のポリマー特性を得ることが困難と
なり、延伸性が良好で耐候性、耐摩耗性に優れた糸が得
られにくいという問題があった。In the method described in JP-A-5-504385, although a spherulite-inhibiting effect is definitely observed as compared with polyhexamethylene adipamide homopolymer, a pigment is added to this polymer to form a yarn. In doing so,
The spherulite-inhibiting effect of the copolymer or the blend alone is small, and the amount of the blend or copolymer component must be more than 20% by weight in order to obtain the spherulite-inhibiting effect. That is, polyhexamethylene adipamide is 80
%, It is difficult to obtain the polymer characteristics unique to polyhexamethylene adipamide, and it is difficult to obtain a yarn having good stretchability and excellent weather resistance and abrasion resistance. there were.
【０００９】また、玄関マットや足拭きマットのカーペ
ット形態としては、サキソニー調のカットパイルカーペ
ットが一般的に普及している。これは、高級感を演出
し、かつ形状の特徴を活かした上に、優れた泥落とし性
能を発現させるためである。そして、このサキソニー調
のカットパイルカーペットにおいては、ポイント性が高
いことが要求される。すなわち、玄関マットや足拭きマ
ットの場合には、特に過酷な使用環境ゆえに、カーペッ
トとして使い込むにつれ撚り止め処理があまくなり、カ
ーペットとしての外観が低下するからである。As a carpet form of a door mat or a foot-wiping mat, a cut-pile carpet having a saxony tone has been widely used. This is for producing a sense of quality and utilizing the characteristics of the shape, as well as exhibiting excellent mud removal performance. The saxony-style cut pile carpet is required to have high points. That is, in the case of a door mat or a foot-wiping mat, since the use environment is particularly severe, as the carpet is used as a carpet, the twist-prevention treatment is increased, and the appearance of the carpet is deteriorated.
【００１０】なお、ここでいうポイント性とは、カーペ
ット表糸先端の撚り止め処理がきれいに締まっている状
態、つまり収束性が良好であることを意味し、ポイント
性が劣るカーペットでは、カーペット表糸先端の撚りが
容易に解けてしまう。しかるに、上記した二つの提案に
よるカーペットは、ポイント性の向上については何ら考
慮されていないことから、カットパイルカーペットとし
ては不十分であり、玄関マットや足拭きマットとしての
要求性能を十分に満たすものではなかった。[0010] The point property here means that the twisting treatment at the tip of the carpet surface yarn is tightly tightened, that is, the convergence is good. The twist at the tip is easily unwound. However, the carpets according to the above two proposals are not sufficient as cut pile carpets because no consideration is given to the improvement of point properties, and the carpets that sufficiently satisfy the required performance as entrance mats and foot wipe mats are not considered. Was not.
【００１１】さらに、特公平６−３７７４１号公報に
は、繊維の中空率を５〜４０％とし、かつ１個以上の中
空部を形成することにより、カーペット表糸先端のポイ
ント性を改善する提案がなされている。しかしながら、
中空部を形成することによるポイント性の向上効果は考
え難く不明瞭であり、またこの中空糸は断面形状が複雑
なことから、均一冷却が難しいことによる球晶成長、お
よび原着剤を添加することなどの要因が加味されること
による延伸性の低下などの不具合が招かれることが容易
に予想できる。Furthermore, Japanese Patent Publication No. Hei 6-37741 proposes that the hollowness of the fiber is set to 5 to 40% and at least one hollow portion is formed to improve the point property of the tip end of the carpet yarn. Has been made. However,
The effect of improving the point property by forming the hollow portion is inconceivable and unclear, and since the hollow fiber has a complicated cross-sectional shape, spherulite growth due to difficulty in uniform cooling, and addition of a soaking agent It can be easily expected that a drawback such as a decrease in stretchability due to the addition of such factors is caused.
【００１２】また、上記の中空糸をカットパイルカーペ
ットに用いた場合には、断面が切断されることにより中
空部にゴミなどが入り込み容易に取ることができず、カ
ーペットとしての品位を著しく低下せるため、カットパ
イルカーペットとしては不適である。Further, when the above hollow fiber is used for a cut pile carpet, the cross section is cut, so that dust or the like can enter the hollow portion and cannot be easily removed, and the quality of the carpet is significantly reduced. Therefore, it is not suitable as a cut pile carpet.
【００１３】さらにまた、特公昭６２−１４６５３号公
報には、構成単繊維を部分的に融着させることにより、
カーペット表糸先端のポイント性を改善する提案がなさ
れている。しかし、この方法では、構成単繊維を部分的
に融着させることにより、確かにポイント性は向上する
ものの、構成単繊維を融着させることは、すなわち劣化
を促進させていることであり、耐候性が低下するため
に、玄関マットや足拭きマットのカーペットとしては不
適である。Furthermore, Japanese Patent Publication No. 62-14653 discloses that the constituent monofilaments are partially fused to each other.
Proposals have been made to improve the pointability of the carpet yarn end. However, in this method, although the point property is certainly improved by partially fusing the constituent single fibers, fusing the constituent single fibers means that the deterioration is accelerated, and It is not suitable as a carpet for an entrance mat or a foot-wiping mat because of its reduced properties.
【００１４】このように、従来の技術では、耐候性、耐
摩耗性、ポイント性、かつ風合いや製糸性をすべて同時
に達成するカーペット用原着捲縮糸は提案されておら
ず、いまだに多くの課題を残したものとなっていた。As described above, in the prior art, there has not been proposed an original crimped yarn for carpet which simultaneously achieves all of weather resistance, abrasion resistance, point properties, texture and yarn-making properties, and there are still many problems. Had been left.
【００１５】[0015]
【発明が解決しようとする課題】本発明は、上述した従
来技術における問題点を解消するため検討し達成したも
のである。したがって本発明の課題は、耐候性、耐摩耗
性、ポイント性に優れ、かつ風合いや製糸性に優れたポ
リアミド原着捲縮糸およびこのポリアミド原着捲縮糸か
ら作られ、特に玄関マットや足拭きマットなどの用途に
好ましく適用されるカーペットを提供することにある。SUMMARY OF THE INVENTION The present invention has been achieved by studying to solve the problems in the prior art described above. Accordingly, an object of the present invention is to prepare a polyamide-origin crimped yarn having excellent weather resistance, abrasion resistance, point properties, and excellent texture and yarn-making properties, and a polyamide-origin crimped yarn, particularly a doormat or foot. An object of the present invention is to provide a carpet that is preferably applied to uses such as a wiping mat.
【００１６】[0016]
【課題を解決するための手段】上記の課題を解決するた
めに、本発明のポリアミド原着捲縮糸は、主として次の
構成を有する。すなわち、構成成分の８０重量％以上が
ヘキサメチレンアジパミド単位からなるポリアミドの原
着捲縮糸であって、単繊維繊度が１０〜３０デニール、
沸騰水処理後の捲縮伸長率が１０〜３０％、耐候処理後
の強度が１．５ｇ／ｄ以上であることを特徴とするポリ
アミド原着捲縮糸である。Means for Solving the Problems In order to solve the above-mentioned problems, the polyamide-origin crimped yarn of the present invention mainly has the following constitution. That is, 80% by weight or more of the constituent components are the original crimped yarns of polyamide comprising hexamethylene adipamide units, and the single fiber fineness is 10 to 30 deniers.
It is a polyamide-origin crimped yarn characterized in that the crimp elongation after boiling water treatment is 10 to 30% and the strength after weathering treatment is 1.5 g / d or more.
【００１７】本発明の原着捲縮糸においては、以下の
（１）〜（４）が好ましい条件であり、これらの条件の
適用により一層すぐれた効果の取得を期待することがで
きる。 （１）ポリアミドが、共重合成分としてカプロラクタム
を２〜１０重量％含有し、かつブレンド成分としてポリ
カプラミドを２〜１０重量％含有していること、（２）
単繊維断面変形度が２．５〜３．８のトライローバル型
であること、（３）銅を銅原子として３０〜２００ｐｐ
ｍ含むこと、（４）総繊度が８００〜２０００デニール
であること。In the original crimped yarn of the present invention, the following conditions (1) to (4) are preferable conditions, and it is expected that a more excellent effect can be obtained by applying these conditions. (1) the polyamide contains 2 to 10% by weight of caprolactam as a copolymer component and 2 to 10% by weight of a polycapramide as a blend component; (2)
Trilobal type having a single fiber cross-sectional deformation degree of 2.5 to 3.8, (3) 30 to 200 pp using copper as a copper atom
(4) The total fineness is 800 to 2000 denier.
【００１８】また、本発明のカーペットは、主として次
の構成を有する。すなわち、上記ポリアミド原着捲縮糸
に下撚りを施した後、その２本または３本に上撚りを施
した撚糸が、フェースヤーンの８０重量％以上であるこ
とを特徴とするカーペットである。なお、本発明のカー
ペットは、カットパイルカーペットであり、玄関マット
または足拭きマットとして使用されることが好ましい。The carpet of the present invention mainly has the following configuration. That is, the carpet is characterized in that two or three of the above-mentioned polyamide-originally crimped yarns are firstly twisted and then two or three twisted yarns are 80% by weight or more of the face yarn. The carpet of the present invention is a cut pile carpet, and is preferably used as an entrance mat or a foot-wiping mat.
【００１９】[0019]
【発明の実施の形態】以下本発明を詳細に説明する。本
発明のポリアミド原着捲縮糸は、これを構成するポリア
ミドの８０重量％以上がヘキサメチレンアジパミド単位
からなることが必須である。DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described below in detail. In the present invention, it is essential that at least 80% by weight of the polyamide constituting the crimped yarn is composed of hexamethylene adipamide units.
【００２０】すなわち、このことは、耐候性、耐摩耗性
などのポリマ特性を活かすために不可欠であり、ヘキサ
メチレンアジパミド単位が８０重量％以下では、ポリヘ
キサメチレンアジパミドの特性である耐候性、耐摩耗性
が低下し、目的とするカーペット用途には不適となる。That is, this is indispensable to make use of polymer properties such as weather resistance and abrasion resistance. When hexamethylene adipamide unit is 80% by weight or less, it is a property of polyhexamethylene adipamide. The weather resistance and the abrasion resistance are reduced, and it is not suitable for the intended use of carpet.
【００２１】本発明におけるポリアミド原着捲縮糸は、
原着糸であることが必要である。耐候性向上のため染料
の検討、染色後の処理などさまざまな検討がなされてい
るが、これらの方法で得られるポリアミド染色捲縮糸
は、顔料によるポリアミド原着捲縮糸にくらべて、耐候
処理後の変退色が著しいため、目的とするカーペット用
途での使用は不適である。The polyamide-origin crimped yarn in the present invention comprises:
It is necessary that the yarn be an original yarn. Various studies have been made on dyes and post-dyeing treatments to improve weather resistance.However, polyamide dyed crimped yarns obtained by these methods are more resistant to weathering than pigmented polyamide crimped yarns. Since the subsequent discoloration is remarkable, it is unsuitable for use in the intended carpet application.
【００２２】なお、ここでいう原着捲縮糸とは、顔料を
予めポリアミドの紡糸工程以前にチップに含有させて紡
糸して得られた捲縮糸であり、通常の顔料濃度は捲縮糸
中にて５重量％以下、さらには３重量％以下であること
が好ましい。糸中の顔料濃度がかかる好ましい範囲の場
合、球晶核としての作用が顕在化することはなく、延伸
時に単繊維切れが発生することもない。本発明で使用す
る顔料としては、有機顔料でも無機顔料でも特に制限が
ない。The term “dipped crimped yarn” as used herein refers to a crimped yarn obtained by incorporating a pigment in a chip before the spinning step of polyamide and spinning the resulting yarn. The content is preferably 5% by weight or less, more preferably 3% by weight or less. When the pigment concentration in the yarn is in such a preferable range, the action as a spherulite nucleus does not appear, and a single fiber break does not occur during stretching. The pigment used in the present invention is not particularly limited, whether it is an organic pigment or an inorganic pigment.
【００２３】本発明のポリアミド原着捲縮糸は、単繊維
繊度を１０〜３０デニール、好ましくは１３〜２５／デ
ニールの範囲にするものである。単繊維繊度が１０デニ
ール未満では、流体捲縮加工において十分な捲縮が得ら
れず、またカーペットの風合いも柔らかすぎるものとな
るばかりか、摩耗しやすく、さらにはカーペット使用中
にピリングと呼ばれる糸玉が生じやすくなる。また、単
繊維繊度が３０デニールを越えると、紡糸時の冷却が不
足し球晶成長が増大して延伸時の単繊維切れ原因とな
り、またカーペットとしての風合いが硬くなってしま
う。The polyamide-origin crimped yarn of the present invention has a single fiber fineness of 10 to 30 denier, preferably 13 to 25 / denier. If the single fiber fineness is less than 10 denier, sufficient crimping cannot be obtained in the fluid crimping process, and the texture of the carpet is not only too soft but also easily worn, and furthermore, a yarn called pilling during use of the carpet. Balls tend to form. On the other hand, if the single fiber fineness exceeds 30 denier, cooling during spinning is insufficient, spherulite growth is increased, and single fiber breakage occurs during stretching, and the texture as a carpet becomes hard.
【００２４】また、本発明のポリアミド原着捲縮糸にお
いては、後述の実施例の欄において定義する方法で測定
した沸騰水処理後の捲縮伸長率を１０〜３０％、好まし
くは１５〜２５％の範囲とするものである。沸騰水処理
後の伸長率が１０％未満では、捲縮糸の特徴である嵩高
性が不足し、また沸騰水処理後の伸長率が３０％を越え
ると、捲縮糸の風合いが堅くなり柔軟性を損なう。Further, in the crimped yarn of the present invention, the crimp elongation after boiling water treatment measured by the method defined in the section of Examples described later is 10 to 30%, preferably 15 to 25. %. If the elongation after boiling water treatment is less than 10%, the bulkiness characteristic of the crimped yarn will be insufficient, and if the elongation after boiling water treatment exceeds 30%, the hand of the crimped yarn will become hard and flexible. Impair the nature.
【００２５】さらに、本発明のポリアミド原着捲縮糸に
おいては、下記に定義する方法で測定した耐候処理後の
強度を１．５ｇ／ｄ以上、好ましくは２．０ｇ／ｄ以上
とするものである。耐候処理後の強度が１．５ｇ／ｄに
満たないと、カーペットとしての外観維持が困難とな
り、例えば繊維切れやピリングと呼ばれる糸玉が生じ、
設置場所の環境悪化や高級感が失われるなど、使用に耐
えがたいものとなる。Further, in the crimped yarn of the present invention, the strength after weathering treatment, measured by the method defined below, is 1.5 g / d or more, preferably 2.0 g / d or more. is there. If the strength after the weathering treatment is less than 1.5 g / d, it becomes difficult to maintain the appearance as a carpet, and for example, fiber breaks or thread balls called pilling occur,
It is difficult to use, such as deterioration of the environment of the installation location and loss of luxury.
【００２６】なお、本発明において、耐候処理後の強度
とは、捲縮糸にサンシャインウェーザーメーターにより
ブラックパネル温度８３℃でカーボンアークを１００時
間照射し、かつ１２０分間に１８分の頻度で水を噴霧す
る雰囲気中で耐候処理した後に、ＪＩＳ Ｌ １０９０
に基づいて測定した捲縮糸の強度をいう。In the present invention, the strength after the weathering treatment means that the crimped yarn is irradiated with a carbon arc for 100 hours at a black panel temperature of 83 ° C. by a sunshine weatherer meter, and water is applied at a frequency of 18 minutes every 120 minutes. JIS L 1090 after weathering treatment in an atmosphere in which
Refers to the strength of the crimped yarn measured based on
【００２７】本発明のポリアミド原着捲縮糸において
は、単繊維断面変形度が２．８〜３．８、さらには３．
０〜３．６の範囲にあるトライローバル糸とすることが
好ましい。単繊維断面変形度がかかる好ましい範囲のト
ライローバル糸である場合には、耐候性、耐摩耗性、ポ
イント性、延伸性を優れたものとしつつ、カーペットと
して好適なバルキー性を得ることができ、また製造工程
において延伸切れが発生することもない。The crimped yarn of the present invention has a single fiber cross-sectional deformation of 2.8 to 3.8, and more preferably 3.
It is preferable to use a trilobal yarn in the range of 0 to 3.6. In the case of a trilobal yarn having a single fiber cross-sectional deformation degree in such a preferable range as described above, weather resistance, abrasion resistance, point properties, and stretchability can be excellent, and bulkiness suitable as a carpet can be obtained. Also, there is no occurrence of stretch breakage in the manufacturing process.
【００２８】さらに、本発明のポリアミド原着捲縮糸に
おいては、共重合成分を２〜１０重量％含有し、かつブ
レンド成分としてポリカプラミドを２〜１０重量％含有
していることがより好ましい。Further, it is more preferable that the polyamide-origin crimped yarn of the present invention contains 2 to 10% by weight of a copolymer component and 2 to 10% by weight of a polycapramide as a blend component.
【００２９】このように共重合することおよびブレンド
成分を導入することを併用するのは、ポリヘキサメチレ
ンアジパミド特有の問題である球晶と呼ばれる結晶部の
成長を抑えるために有効な手法であり、上記した本発明
のポリアミド原着捲縮糸における単繊維繊度のような、
単孔吐出量が多く冷却速度が小さい工程で製造されるポ
リアミド捲縮糸の場合には、ことから球晶成長による延
伸切れ問題を解消するための有効な手段となるからであ
る。The combination of the copolymerization and the introduction of the blend component is an effective method for suppressing the growth of a crystal part called spherulite which is a problem peculiar to polyhexamethylene adipamide. Yes, such as the single fiber fineness in the above-mentioned polyamide original crimped yarn of the present invention,
This is because, in the case of a polyamide crimped yarn produced in a process in which the single hole discharge amount is large and the cooling rate is low, this is an effective means for solving the problem of breakage due to spherulite growth.
【００３０】本発明における共重合成分は特に限定はさ
れず、例えばテトラメチレンアジパミド、ヘキサメチレ
ンセバカミド、ヘキサメチレンテレフタルアミド、ヘキ
サメチレンイソフタルアミド、およびキシリレンフタル
アミドなどを使用することができるが、そのなかでも特
にカプロアミドの使用が好ましい。The copolymerization component in the present invention is not particularly limited. For example, tetramethylene adipamide, hexamethylene sebacamide, hexamethylene terephthalamide, hexamethylene isophthalamide, xylylene phthalamide and the like can be used. Of these, caproamide is particularly preferred.
【００３１】本発明におけるブレンド成分は特に限定は
されず、ナイロン１１、ナイロン１２、およびナイロン
６・１０などを使用できるが、そのなかでも特にナイロ
ン６であるポリカプロアミドを使用するのが好ましい。The blend component in the present invention is not particularly limited, and nylon 11, nylon 12, nylon 6, and the like can be used. Among them, polycaproamide, which is nylon 6, is particularly preferable.
【００３２】本発明のポリアミド原着捲縮糸において
は、銅を銅原子として糸中に３０〜２００ｐｐｍ存在さ
せることが好ましい。もちろん耐候性を高めるために
は、つまり耐候処理後の強度を１．５ｇ／ｄ以上にする
ためには、紡糸条件や後加工条件を最適化したり、各種
耐候処理を施すことが考えられるが、なかでも銅を含有
させることがより好ましい手段として挙げられる。銅化
合物の添加量をかかる好ましい範囲とすればその耐候性
向上効果を十分発揮することができ、延伸時に単繊維切
れを起こすこともない。In the present invention, it is preferable that 30 to 200 ppm of copper as a copper atom be present in the yarn. Of course, in order to increase the weather resistance, that is, to increase the strength after the weathering treatment to 1.5 g / d or more, it is conceivable to optimize spinning conditions and post-processing conditions or to perform various weathering treatments. Above all, a more preferable means is to contain copper. When the addition amount of the copper compound is in such a preferable range, the effect of improving the weather resistance can be sufficiently exhibited, and the single fiber does not break during drawing.
【００３３】本発明で使用する銅化合物としては、例え
ば酢酸第二銅、沃化第一銅、臭化第一銅、臭化第二銅、
フタル酸銅、ステアリン酸銅、燐酸銅、ピロリン酸銅お
よび各種銅塩などが挙げられる。また、必要に応じて非
水溶性銅塩を溶液として添加するために、ハロゲン化ア
ルカリ金属の高濃度水溶液を溶媒として使用することも
可能である。The copper compounds used in the present invention include, for example, cupric acetate, cuprous iodide, cuprous bromide, cupric bromide, and the like.
Examples include copper phthalate, copper stearate, copper phosphate, copper pyrophosphate, and various copper salts. In addition, in order to add the water-insoluble copper salt as a solution if necessary, it is also possible to use a high-concentration aqueous solution of an alkali metal halide as a solvent.
【００３４】ポリアミドに対し銅化合物を含有させて、
耐候処理後の強伸度低下を抑制することにより、カーペ
ットにした場合に単繊維切れやピリングなどが発生する
という問題が効果的に解消されると共に、耐候性がきわ
めて優れたカーペットを得ることができる。なお、本発
明の効果を損なわない範囲であれば、銅化合物以外の他
の添加物を添加しても差し支えない。A copper compound is added to the polyamide,
By suppressing the drop in strength and elongation after the weathering treatment, the problem of breakage of single fibers or pilling when carpet is formed can be effectively solved, and a carpet having extremely excellent weather resistance can be obtained. it can. Note that other additives other than the copper compound may be added as long as the effects of the present invention are not impaired.
【００３５】本発明のポリアミド原着捲縮糸は、カーペ
ットとしての高次加工の取り扱いを考慮して、その総繊
度が８００〜２０００デニール、特に１８００〜２００
０デニールであることが好ましい。総繊度をかかる好ま
しい範囲とすればは、撚糸セット工程やタフト工程での
生産効率を良好に保ちつつ、目的とするカーペットが要
求するポイント性を容易に得ることができ、通常２本な
いし３本撚り合わせて使用する場合でも、実用上取り扱
い難くなることはない。The polyamide-origin crimped yarn of the present invention has a total fineness of 800 to 2,000 denier, particularly 1,800 to 200, in consideration of the handling of higher-order processing as a carpet.
It is preferably 0 denier. When the total fineness is set in such a preferable range, it is possible to easily obtain the point property required by the target carpet while maintaining good production efficiency in the twist setting process and the tuft process, and usually 2 to 3 yarns. Even when they are used in a twisted manner, there is no practical difficulty in handling.
【００３６】本発明のカーペットにおいては、上記のポ
リアミド原着捲縮糸に下撚りを施した後、その２本また
は３本に上撚りを施した撚糸が、フェースヤーンの８０
重量％以上とするものである。フェースヤーンとは、カ
ーペット表面のパイル糸を意味する。In the carpet of the present invention, the above-mentioned polyamide-origin crimped yarn is subjected to ply twisting, and then two or three of the twisted yarns are twisted to form a face yarn of 80%.
% By weight or more. Face yarn means pile yarn on the carpet surface.
【００３７】ポリアミド原着捲縮糸の２本または３本を
上撚りにて撚り合わせることにより、カットパイルカー
ペットとして好適に使用することができる。なお、この
とき必要に応じて熱セットを施すことは何ら差し支えな
い。By twisting two or three of the original polyamide crimped yarns by twisting, they can be suitably used as a cut pile carpet. At this time, heat setting may be performed as needed.
【００３８】本発明のカーペットにおいては、前記した
ポリアミド原着捲縮糸に下撚りを施した後、その２本ま
たは３本に上撚りを施した撚糸を、フェースヤーンの８
０重量％以上とするものである。撚糸がフェースヤーン
の８０重量％未満では、該捲縮糸の特徴である耐候性、
耐摩耗性、ポイント性、かつ風合い等を十分に発揮した
カーペットを得ることができない。In the carpet according to the present invention, after the above-described polyamide-originally crimped yarn is subjected to priming and then two or three of the twisted yarns are subjected to ply twisting, the face yarn 8
0% by weight or more. When the twisted yarn is less than 80% by weight of the face yarn, the weather resistance characteristic of the crimped yarn,
It is not possible to obtain a carpet sufficiently exhibiting abrasion resistance, point properties, and texture.
【００３９】以下に、本発明の耐候性・耐摩耗性、ポイ
ント性に優れ、かつ風合いや製糸性に優れたポリアミド
原着捲縮糸およびこの捲縮糸を用いたカーペットの代表
的な製造方法について説明する。The following is a typical method of producing a polyamide-origin crimped yarn of the present invention which is excellent in weather resistance, abrasion resistance and point properties, and which is excellent in texture and yarn formability, and a carpet using this crimped yarn. Will be described.
【００４０】本発明のポリアミド原着捲縮糸は、基本的
に公知の溶融紡糸、冷却、給油、延伸、捲縮付与の各工
程からなる通常の溶融紡糸法によって製造される。本発
明で用いる溶融紡糸装置は、エクストルーダー型紡糸機
およびプレッシャー型紡糸機のどちらも使用可能である
が、製品の均一性および製糸工程における収率の点から
前者が好ましい。特に原着ポリマーを用いる場合はエク
ストルーダー型紡糸機が有利である。The polyamide-origin crimped yarn of the present invention is produced by an ordinary melt-spinning method basically comprising known steps of melt spinning, cooling, oil supply, drawing and crimping. As the melt spinning device used in the present invention, both an extruder type spinning machine and a pressure type spinning machine can be used, but the former is preferable in terms of product uniformity and yield in the spinning process. In particular, an extruder-type spinning machine is advantageous when a soaked polymer is used.
【００４１】まず、耐候性を高めるためにその８０重量
％以上がヘキサメチレンアジパミド単位から構成される
ポリアミドを準備する。このポリアミドに対する共重合
成分はあらかじめ重合時に添加させておくことが好まし
い。また、ポリアミドに対するブレンド成分は、ポリヘ
キサメチレンアジパミドとの反応性が低い場合は重合時
のブレンドが可能である。通常はチップ重合後、乾燥時
やあるいは紡糸の直前にブレンドされる。紡糸直前にブ
レンドする場合には、上述のようにエクストルーダータ
イプの紡糸機を使用すると混合がより均一になり好まし
い。First, a polyamide whose hexamethylene adipamide unit is 80% by weight or more is prepared to improve the weather resistance. It is preferable that a copolymer component for the polyamide is added in advance at the time of polymerization. In addition, the blend component for polyamide can be blended during polymerization when the reactivity with polyhexamethylene adipamide is low. Usually, after chip polymerization, it is blended at the time of drying or immediately before spinning. In the case of blending immediately before spinning, it is preferable to use an extruder-type spinning machine as described above because the mixing becomes more uniform.
【００４２】また、本発明のポリアミド原着捲縮糸は、
顔料をあらかじめチップに混合して紡糸する原着糸であ
るので、この顔料を含有させたマスターチップをブレン
ド成分と同一にすることも可能である。具体的には、顔
料を混合するマスターチップをポリカプラミドとするこ
とは、本発明において適用される好例となる。なお、耐
候剤として銅化合物などを糸中に存在させる場合にも、
それらの添加は紡糸前行われるが、その添加方法は添加
する化合物の種類や特性に応じて決定すればよい。The polyamide-origin crimped yarn of the present invention is
Since the dyed yarn is a spun yarn in which the pigment is previously mixed with the chip and spun, the master chip containing the pigment can be the same as the blend component. Specifically, the use of polycapramide as the master chip for mixing the pigment is a good example applied in the present invention. In addition, even when a copper compound or the like is present in the yarn as a weathering agent,
These additions are performed before spinning, and the addition method may be determined according to the type and characteristics of the compound to be added.
【００４３】さらに、ポリアミド原着捲縮糸の糸断面
を、上述した単繊維断面変形度と単繊維繊度にするため
には、溶融吐出する際の口金の吐出孔形状と吐出量、引
き取り速度などの紡糸条件を、目的に合わせて調節すれ
ばよい。溶融紡糸された糸条には、冷却、給油の後、必
要に応じて延伸、熱固定が施される。Further, in order to make the cross section of the original crimped yarn of the polyamide into the above-mentioned single fiber cross-section deformation and single fiber fineness, the shape and amount of the discharge hole of the die at the time of melting and discharging, the take-up speed, etc. May be adjusted according to the purpose. The melt-spun yarn is subjected to drawing and heat setting as necessary after cooling and refueling.
【００４４】延伸に際しては、補助的に延伸点を固定す
るなどの目的で、スチーム処理装置などを併用してもよ
い。本発明のポリアミド原着捲縮糸は、ポリヘキサメチ
レンアジパミドを基本構成とするものであり、後の工程
で高い捲縮を付与するためには、ある程度の配向と結晶
化が必要であるので、通常は２倍から５倍の倍率の延伸
を行うことが好ましい。At the time of stretching, a steam processing device or the like may be used in combination for the purpose of auxiliaryly fixing the stretching point. The polyamide-origin crimped yarn of the present invention is based on polyhexamethylene adipamide, and requires a certain degree of orientation and crystallization in order to impart a high crimp in a later step. Therefore, it is usually preferable to perform stretching at a magnification of 2 to 5 times.
【００４５】次いで、それぞれの延伸糸について、別々
に捲縮付与装置によって個別に捲縮を付与する。捲縮は
通常の加熱流体加工処理により付与すればよく、例え
ば、ジェットノズルタイプ、ジェットスタッファタイ
プ、さらにはギヤ方式など各種の捲縮付与方法が採用さ
れ得るが、高い捲縮付与とその顕在化を達成するために
はジェットノズル方式が好ましく、例えば米国特許第
３，７８１，９４９号明細書に記載の捲縮ノズルなどが
好ましく使用される。なお、この場合には、捲縮を固定
する目的から、例えば特開平５−３２１０５８号公報に
記載のごとく、冷却装置、さらにはロータリーフィルタ
を組み合わせてもよい。Next, each of the drawn yarns is individually crimped individually by a crimping device. The crimp may be applied by a normal heating fluid processing process. For example, various crimping methods such as a jet nozzle type, a jet stuffer type, and a gear system may be adopted. The jet nozzle method is preferable in order to achieve the formation, and for example, a crimp nozzle described in US Pat. No. 3,781,949 is preferably used. In this case, for the purpose of fixing the crimp, for example, as described in JP-A-5-31058, a cooling device and a rotary filter may be combined.
【００４６】溶融紡糸、延伸および捲縮付与は、途中で
巻取らずに連続して行ってもよいし、未延伸糸段階ある
いは延伸糸段階で一旦巻取ってもよい。耐候処理後の強
度を得るためには、単繊維繊度や断面形状、あるいは耐
候剤として添加した化合物の添加量や性能に合わせて、
捲縮付与条件を適宜設定すればよい。本発明において
は、その工程通過性や捲縮特性をコントロールする目的
のために、捲縮ノズルに導入する糸条に予め原糸交絡を
付与しても差し支えない。The melt spinning, drawing and crimping may be performed continuously without winding in the middle, or may be once wound in an undrawn yarn stage or a drawn yarn stage. In order to obtain the strength after weathering treatment, according to the single fiber fineness and cross-sectional shape, or the amount and performance of the compound added as a weathering agent,
The crimping conditions may be set as appropriate. In the present invention, the yarn introduced into the crimping nozzle may be entangled in advance with the yarn for the purpose of controlling the processability and the crimping property.
【００４７】このようにして得られたポリアミド原着捲
縮糸は、玄関マットや足拭きマットに使用される場合
に、捲縮の耐久性や靴の汚れ除去性能の向上のために、
サキソニー調として使用されることが多い。この場合に
は、目的に応じて撚りおよび熱処理が施されるが、いず
れも公知の方法を採りうる。使用目的に応じ、２プライ
あるいは３プライとして使用される。The polyamide-origin crimped yarn thus obtained is used for a door mat or a foot-wiping mat, in order to improve the durability of the crimp and the performance of removing stains of shoes.
Often used as a saxony tone. In this case, twisting and heat treatment are performed depending on the purpose, and any known method can be employed. It is used as two plies or three plies depending on the purpose of use.
【００４８】タフトは公知の方法で行うことが可能であ
る。本発明におけるポリアミド原着捲縮糸は、カットパ
イルとしてタフトされたときに特に優れた効果を発現す
るため、カットが可能なタフトマシンを使用する。The tufting can be performed by a known method. In the present invention, the crimped yarn is a tuft machine capable of cutting, since it exhibits particularly excellent effects when tufted as a cut pile.
【００４９】また、カーペットの意匠性を高めるため
に、カットアンドループなどの規格とすることもでき
る。パイルハイは、用途により適宜設定すればよいが、
３ｍｍから３０ｍｍ、好ましくは１０ｍｍから２０ｍｍ
が選択される。このとき、カーペットの制電性を高めた
り、さらには意匠性を高めるなどの目的で、本発明の効
果を損ねない程度に制電糸あるいはモノフィラメントや
他の糸を混織することは何ら差し支えない。Further, in order to enhance the design of the carpet, a standard such as cut-and-loop may be used. The pile high may be set appropriately depending on the application,
3 to 30 mm, preferably 10 to 20 mm
Is selected. At this time, for the purpose of enhancing the antistatic property of the carpet, and further enhancing the design, it is possible to mix antistatic yarns or monofilaments or other yarns to the extent that the effect of the present invention is not impaired. .
【００５０】次いで、公知の方法により、バッキングが
施される。この場合に、必要に応じ、シャーリングを実
施することはより好ましい手法として推奨される。ま
た、防汚性を高めるために、防汚剤を塗布することも何
ら差し支えない。Next, backing is performed by a known method. In this case, it is recommended to perform shearing as necessary as a more preferable technique. Further, in order to enhance the antifouling property, application of an antifouling agent may be performed at all.
【００５１】本発明のポリアミド原着捲縮糸およびこれ
を用いたカットパイルカーペットは、パイル先端の耐候
性、耐摩耗性、ポイント性に優れた特性を活かし、特に
店舗、事務所向けの玄関マットや足拭きマットとして適
しているが、その奏する効果の活用を必要とする場合で
あれば、車両用マットや家庭用マットなどの用途にも利
用可能である。The polyamide-origin crimped yarn of the present invention and the cut pile carpet using the same take advantage of the excellent weather resistance, abrasion resistance and point properties of the pile tip, and are particularly suitable for entrance mats for stores and offices. It is suitable for use as a foot mat or a foot-wiping mat, but can be used for applications such as a vehicle mat and a home mat if it is necessary to utilize the effect of the mat.
【００５２】[0052]
【実施例】以下、実施例にて本発明をさらに説明する。
なお、上述および以下に説明する実施例中の物性値は次
の方法により求めた値である。 ［総繊度］ＪＩＳ Ｌ １０９０により測定した。 ［単繊維繊度］上記にて測定した総繊度を単繊維数で徐
して求めた。 ［単繊維断面変形度］単繊維断面を切断後、光学顕微鏡
を用いて単繊維凸部を外接円の直径（Ａ）と単繊維凹部
の内接円の直径（Ｂ）を測定し、Ａ／Ｂにより算出し
た。 ［沸騰水処理後の捲縮伸長率］捲縮糸に無荷重下で９８
℃×５分間の沸騰水処理をした後、風乾し、初荷重とし
て２ｍｇ／ｄをかけて測定した場合の長さＬ1と、次い
で定荷重（１００ｍｇ／ｄ）をかけて測定した場合の長
さＬ2から、｛（Ｌ2−Ｌ1）／Ｌ1｝×１００により算出
した。 ［耐候処理後の強度］サンシャインウェザーメーターを
使用して、ブラックパネル温度８３℃±５℃、カーボン
アーク処理１００時間、かつ１２０分間に１８分の頻度
で水を噴霧した条件にて処理を行ったのち、オリエンテ
ック社製テンシロン引っ張り試験機を用い、ＪＩＳ Ｌ
１０９０により、試長２５０ｍｍ、引張り速度３００
ｍｍ／分の条件で測定した。 ［製糸性］延伸に起因する製糸切れを評価し、◎‥きわ
めて良好、○‥良好、△‥若干不良、×‥不良４段階に
区分した。 ［風合い］カーペットを足で踏んだときの風合を官能評
価し、◎…最もソフトで弾力間のあるもの、○‥風合良
好、△‥風合若干不良、×‥最も風合不良の４段階に区
分した。 ［耐候性］上記した耐候処理後の強度が、２．５ｇ／ｄ
以上のものを「◎」、２．０ｇ／ｄ以上２．５ｇ／ｄ未
満のものを「○」、１．５ｇ／ｄ以上２．０ｇ／ｄ未満
のものを「△」、１．５ｇ／ｄ未満のものを「×」とし
た。 ［耐摩耗性］１０万人実用テスト法を参考に、テスト後
の表糸の摩耗の程度を、使用前のものと比較し、目視に
よる官能評価により、◎‥きわめて良好、○‥良好、△
‥若干の摩耗がみられるものの目立たない程度、×‥不
良の４段階に程度を区分した。 ［ポイント性］上記耐耐摩耗性テストを実施した後の表
糸の撚りの解け程度を、目視による官能評価により、◎
‥きわめて良好、○‥良好、△‥若干の解けが見えるも
のの目立たない程度、×‥不良の４段階に程度区分し
た。 ［硫酸相対粘度］ポリマ試料を９８％硫酸に１重量％の
濃度で溶解し、オストワルド粘度計を用いて２５℃で測
定した。The present invention will be further described below with reference to examples.
The physical property values in the examples described above and below are values obtained by the following methods. [Total fineness] Measured according to JIS L 1090. [Single fiber fineness] The total fineness measured as described above was gradually obtained based on the number of single fibers. [Degree of Single Fiber Cross Section Deformation] After cutting the single fiber cross section, the diameter (A) of the circumscribed circle of the single fiber convex part and the diameter (B) of the inscribed circle of the single fiber concave part were measured using an optical microscope, and A / B was calculated. [Crimp elongation rate after boiling water treatment] 98
After treatment with boiling water at 5 ° C. × 5 minutes, air-dried, the length L 1 when measured with an initial load of 2 mg / d, and the length when measured with a constant load (100 mg / d) from the L 2, it was calculated by {(L 2 -L 1) / L 1} × 100. [Strength after weathering treatment] Using a sunshine weather meter, the treatment was carried out under the condition that water was sprayed at a black panel temperature of 83 ° C ± 5 ° C, a carbon arc treatment of 100 hours, and a frequency of 18 minutes every 120 minutes. Then, using Orientec Tensilon tensile tester, JIS L
1090, test length 250mm, pulling speed 300
It was measured under the condition of mm / min. [Yarn-making properties] The yarn breakage caused by the stretching was evaluated, and classified into four stages of ‥‥ very good, ‥‥ good, △ ‥ slightly poor, and × ‥ bad. [Hand feeling] Sensory evaluation of hand feeling when stepping on the carpet, ◎: softest and most elastic, ○ ‥ good feeling, △ slightly poor feeling, × ‥ most poor feeling 4 It was divided into stages. [Weather resistance] The strength after the above weather treatment is 2.5 g / d.
“以上” indicates the above, “○” indicates the value of 2.0 g / d to less than 2.5 g / d, “△” indicates the value of 1.5 g / d to less than 2.0 g / d, and 1.5 g / d Those with less than d were rated "x". [Abrasion resistance] Referring to the practical test method for 100,000 people, the degree of abrasion of the face yarn after the test was compared with that before use, and the sensory evaluation by visual observation showed ◎ ‥ very good, ○ ‥ good, △
‥ Several abrasion was observed but not noticeable. [Pointability] The degree of untwisting of the face yarn after the abrasion resistance test was performed was evaluated by visual sensory evaluation.
‥ Excellent, ○ ‥ Good, △ ‥ Slightly unmelted but inconspicuous, × ‥ Poor poor. [Sulfuric acid relative viscosity] A polymer sample was dissolved in 98% sulfuric acid at a concentration of 1% by weight, and measured at 25 ° C using an Ostwald viscometer.
【００５３】（実施例１）ポリヘキサメチレンアジパミ
ドにカプロラクタムを５重量％共重合し、さらに銅成分
を糸中にて８０ｐｐｍとなるように添加した硫酸相対粘
度２．９０のナイロン６６／６ベースポリマーチップに
対し、酸化鉄系およびカーボンブラックを適宜混合した
顔料を１０重量％含有する硫酸相対粘度３．４０のポリ
カプロアミドマスターチップを、それぞれ９５：５の混
合重量比にて機械的ブレンドした後、エクストルダー型
紡糸機で溶融し、公知のトライローバル型口金より紡糸
した。紡糸部より得た糸条に先ず油剤を付着せしめ、続
いて引き取りロールで引き取り、１８０℃以上の加熱延
伸ロールにて３．０倍で延伸した後、連続して加熱流体
捲縮加工装置にて２３０℃以上での加熱蒸気処理を行
い、捲縮を付与した。次いで、捲縮がへたらない程度に
引き伸ばし、最後に０．０８ｇ／ｄ程度の巻取張力で巻
き取ることにより、１３００デニール６８フィラメント
のポリアミド原着捲縮糸を得た。この際、製糸性を評価
するとともに、得られたポリアミド原着捲縮糸の耐候処
理後の強度を測定した。また、上記にて得られたポリア
ミド原着捲縮糸を、下撚り（１８０Ｔ／ｍ）し、それを
２本用いて上撚り（１８０Ｔ／ｍ）で撚り合わせ、乾熱
１３０℃で撚り止め処理を施した後、カットパイルカー
ペットとしてタフトし、得られたカーペットの風合い・
耐候性・耐摩耗性・ポイント性について評価した。この
結果を表１に示した。表１の結果から明らかなように、
優れた延伸加工性、風合い、耐候性、耐摩耗性、ポイン
ト性を有すると共に、耐候処理後の強度が１．５ｇ／ｄ
以上のきわめて優れたカーペット用ポリアミド原着捲縮
糸およびカーペットが得られた。Example 1 Nylon 66/6 having a relative viscosity of 2.90 of sulfuric acid obtained by copolymerizing 5% by weight of caprolactam with polyhexamethylene adipamide and further adding a copper component to 80 ppm in the yarn. A mechanical blend of a polycaproamide master chip having a relative viscosity of sulfuric acid of 3.40 and a weight ratio of 95: 5 containing 10% by weight of a pigment obtained by appropriately mixing an iron oxide type and carbon black with a base polymer chip was performed. After that, the mixture was melted by an extruder type spinning machine and spun from a known trilobal type spinneret. First, an oil agent is adhered to the yarn obtained from the spinning section, subsequently taken up by a take-up roll, stretched at a ratio of 3.0 with a hot stretch roll at 180 ° C. or higher, and then continuously heated with a fluid crimping device. A heating steam treatment at 230 ° C. or higher was performed to impart crimp. Next, it was stretched to such an extent that the crimp was not loosened, and finally wound up with a winding tension of about 0.08 g / d to obtain a 1300 denier 68-filament polyamide-origin crimped yarn. At this time, the yarn formability was evaluated, and the strength of the obtained polyamide-dipped crimped yarn after weathering treatment was measured. In addition, the polyamide-origin crimped yarn obtained above is subjected to a bottom twist (180 T / m), two of them are twisted together by a top twist (180 T / m), and a twist preventing treatment is performed at a dry heat of 130 ° C. And then tufted as a cut pile carpet,
The weather resistance, abrasion resistance and point properties were evaluated. The results are shown in Table 1. As is clear from the results in Table 1,
It has excellent stretchability, texture, weather resistance, abrasion resistance and point properties, and has a strength of 1.5 g / d after weathering treatment.
The above-mentioned extremely excellent crimped yarn and carpet on polyamide for carpet were obtained.
【００５４】[0054]
【表１】 [Table 1]
【００５５】（実施例２）ポリヘキサメチレンアジパミ
ドにカプロラクタムを５重量％共重合し、さらに銅成分
を糸中にて８０ｐｐｍとなるように添加した硫酸相対粘
度２．９０のベースチップと、酸化鉄系およびカーボン
ブラックを適宣混合した顔料を１０重量％含有する硫酸
相対粘度３．４０のポリカプロアミドマスターチップ
を、それぞれ９０：１０の混合重量比にて機械的ブレン
ドし、実施例１と同様に紡糸し、カットパイルカーペッ
トを作製して、評価を行った。この結果を表１に併記し
た。表１の結果から明らかなように、極めて優れた延伸
加工性を有し、また優れた風合いおよびポイント性を有
する優れたカーペット用原着捲縮糸およびカーペットが
得られた。Example 2 Caprolactam was copolymerized with polyhexamethylene adipamide in an amount of 5% by weight, and a copper component was added so as to be 80 ppm in the yarn. Example 1 A polycaproamide master chip containing sulfuric acid having a relative viscosity of 3.40 and containing 10% by weight of a pigment appropriately mixed with iron oxide and carbon black was mechanically blended at a mixing weight ratio of 90:10. Spinning was performed in the same manner as described above, and a cut pile carpet was prepared and evaluated. The results are shown in Table 1. As is clear from the results shown in Table 1, excellent crimped yarns and carpets for carpet having extremely excellent drawability and excellent texture and point properties were obtained.
【００５６】（実施例３）表１に示した単繊維繊度とな
るように、９０ホールトライローバル型紡糸口金を用い
た以外は、実施例１に同様にして紡糸し、カットパイル
カーペットを作製して、評価を行ない、この結果を表１
に併記した。表１の結果から明らかなように、極めて優
れた風合い、ポイント性を有し、また優れた延伸加工性
を有するカーペット用原着捲縮糸およびカーペットが得
られた。(Example 3) Spinning was carried out in the same manner as in Example 1 except that a 90-hole trilobal spinneret was used so as to obtain the single fiber fineness shown in Table 1, thereby producing a cut pile carpet. Table 1 shows the results.
It was also described in. As is evident from the results in Table 1, original crimped yarns and carpets for carpets having extremely excellent texture and point properties and excellent stretchability were obtained.
【００５７】（実施例４）表１に示した沸騰水処理後の
伸長率となるように、加熱延伸ロール温度をにコントロ
ールした以外は、実施例１に同様にして紡糸し、カット
パイルカーペットを作製して、評価を行ない、この結果
を表１に併記した。表１の結果から明らかなように、優
れた延伸加工性、耐候性、耐摩耗性風を有するカーペッ
ト用原着捲縮糸およびカーペットが得られた。(Example 4) Spinning was performed in the same manner as in Example 1 except that the temperature of the hot drawing roll was controlled so that the elongation rate after the boiling water treatment shown in Table 1 was attained. It was prepared and evaluated, and the results are shown in Table 1. As is clear from the results in Table 1, the original crimped yarn for carpet and the carpet having excellent stretchability, weather resistance and abrasion-resistant wind were obtained.
【００５８】（比較例１）ポリヘキサメチレンアジパミ
ドにカプロラクタム２０重量％共重合し、さらに銅成分
を糸中にて８０ｐｐｍとなるように添加した硫酸相対粘
度２．９０のナイロン６６／６ベースチップと、酸化鉄
系およびカーボンブラックとを適宣混合した顔料を１０
重量％含有する硫酸相対粘度３．４０のポリカプロアミ
ドマスターチップとを、９０：５の混合重量比にて機械
的ブレンドし、実施例１と同様に紡糸・評価を行ない、
この結果を表２に示した。表２の結果から明らかなよう
に、優れた延伸加工性を有するものの、耐候性、耐摩耗
性が極めて劣位であった。Comparative Example 1 Nylon 66/6 base having a relative viscosity of 2.90 and a sulfuric acid obtained by copolymerizing 20% by weight of caprolactam with polyhexamethylene adipamide and further adding a copper component to 80 ppm in the yarn. 10 parts of a pigment that is a suitable mixture of iron oxide and carbon black
A polycaproamide master chip having a relative viscosity of sulfuric acid of 3.40 and containing by weight was mechanically blended at a mixing weight ratio of 90: 5, and spun and evaluated in the same manner as in Example 1.
The results are shown in Table 2. As is clear from the results in Table 2, although having excellent stretchability, the weather resistance and the abrasion resistance were extremely inferior.
【００５９】[0059]
【表２】 [Table 2]
【００６０】（比較例２）ポリヘキサメチレンアジパミ
ドにカプロラクタム５重量％共重合し、さらに銅成分を
糸中にて８０ｐｐｍとなるように添加した硫酸相対粘度
２．９０のナイロン６６／６ベースチップと、酸化鉄系
およびカーボンブラックを適宣混合した顔料を２．５重
量％含有する硫酸相対粘度３．４０のポリカプロアミド
マスターチップとを、８０：２０の混合重量比にて機械
的ブレンドし、実施例１と同様に紡糸・評価を行ない、
この結果を表２に併記した。表２の結果から明らかなよ
うに、優れた延伸加工性を有するものの、耐候性、耐摩
耗性が極めて劣位であった。(Comparative Example 2) Nylon 66/6 base having a relative viscosity of 2.90 of sulfuric acid obtained by copolymerizing 5% by weight of caprolactam with polyhexamethylene adipamide and further adding a copper component to 80 ppm in the yarn. A mechanical blend of the chips and a polycaproamide master chip having a relative viscosity of sulfuric acid of 3.40 and containing 2.5% by weight of a pigment appropriately mixed with iron oxide and carbon black in a mixing weight ratio of 80:20. Then, spinning and evaluation were performed in the same manner as in Example 1.
The results are shown in Table 2. As is clear from the results in Table 2, although having excellent stretchability, the weather resistance and the abrasion resistance were extremely inferior.
【００６１】（比較例３〜４）実施例１において、表２
に示した単繊維繊度となるよう、１８０ホールトライロ
ーバル型口金（比較例３）、４０ホールトライローバル
型紡糸口金（比較例４）を用いた以外は、実施例１と同
様に紡糸・評価を行ない、この結果を表２に併記した。
表２の結果から明らかなように、比較例３では、優れた
風合いを有するものの、延伸加工性が生産困難なレベル
であり、さらに耐候性、耐摩耗性も劣位であった。ま
た、比較例４では、優れた耐候性、耐摩耗性を有するも
のの、延伸加工性が生産困難なレベルであり、さらに風
合いが粗剛であった。(Comparative Examples 3 and 4)
The spinning / evaluation was performed in the same manner as in Example 1 except that the 180-hole trilobal spinneret (Comparative Example 3) and the 40-hole trilobal spinneret (Comparative Example 4) were used so as to have the single fiber fineness shown in Table 1. The results are shown in Table 2.
As is evident from the results in Table 2, Comparative Example 3 had an excellent texture, but the stretchability was at a level where production was difficult, and the weather resistance and abrasion resistance were also inferior. In Comparative Example 4, although excellent weather resistance and wear resistance were obtained, the stretchability was at a level at which production was difficult, and the texture was rough and rigid.
【００６２】（比較例５〜６）実施例１において、表２
に示した沸騰水処理後の伸長率となるように、加熱延伸
ロール温度をコントロールをした以外は、実施例１と同
様に紡糸・評価を行ない、この結果を表２に併記した。
表２の結果から明らかなように、比較例５では、優れた
風合いを有するものの、ポイント性が極めて劣位であっ
た。また、比較例６では、優れたポイント性を有するも
のの、風合いが粗剛であった。(Comparative Examples 5 to 6)
The spinning and evaluation were carried out in the same manner as in Example 1 except that the temperature of the hot stretching roll was controlled so as to obtain the elongation rate after the boiling water treatment shown in Table 2. The results are also shown in Table 2.
As is clear from the results in Table 2, Comparative Example 5 had an excellent texture, but the point property was extremely inferior. In Comparative Example 6, the texture was rough and rigid, although it had excellent point properties.
【００６３】[0063]
【発明の効果】本発明のポリアミド原着捲縮糸は、耐候
性、耐摩耗性、ポイント性に優れ、かつ風合いや製糸性
に優れているため、特にカットパイルカーペット用材料
として好適に使用することができる。また、上記のポリ
アミド原着捲縮糸から作られる本発明のカーットは、上
記の優れた特性を生かして、特に玄関マットや足拭きマ
ットなどの用途に好ましく適用される。Industrial Applicability The crimped yarn of the present invention is excellent in weather resistance, abrasion resistance and pointability, and is excellent in texture and yarn-making properties. Therefore, it is preferably used as a material for cut pile carpet. be able to. Further, the cart of the present invention made from the above-described polyamide-originated crimped yarn is preferably applied to applications such as door mats and foot-wiping mats, taking advantage of the above-mentioned excellent properties.
───────────────────────────────────────────────────── フロントページの続き Ｆターム(参考） 3B120 AA15 BA30 EA03 EA04 EB16 EB18 4L035 AA09 BB89 BB91 CC05 CC20 DD02 DD20 EE08 EE20 FF08 JJ04 JJ10 LC03 LC05 4L036 MA06 MA20 MA33 PA01 PA03 PA19 PA26 PA41 PA49 RA04 ──────────────────────────────────────────────────続 き Continued on the front page F term (reference) 3B120 AA15 BA30 EA03 EA04 EB16 EB18 4L035 AA09 BB89 BB91 CC05 CC20 DD02 DD20 EE08 EE20 FF08 JJ04 JJ10 LC03 LC05 4L036 MA06 MA20 MA33 PA01 PA03 PA19 PA26 PA41 PA49 RA04
Claims (8)
レンアジパミド単位からなるポリアミド原着捲縮糸であ
って、単繊維繊度が１０〜３０デニール、沸騰水処理後
の捲縮伸長率が１０〜３０％、耐候処理後の強度が１．
５ｇ／ｄ以上であることを特徴とするポリアミド原着捲
縮糸。1. A polyamide-origin crimped yarn comprising at least 80% by weight of a hexamethylene adipamide unit, having a single fiber fineness of 10 to 30 denier and a crimp elongation after boiling water treatment. 10-30%, strength after weathering treatment is 1.
A polyamide-origin crimped yarn characterized by being at least 5 g / d.
ラクタムを２〜１０重量％含有し、かつブレンド成分と
してポリカプラミドを２〜１０重量％含有していること
を特徴とする請求項１に記載のポリアミド原着捲縮糸。2. The polyamide raw material according to claim 1, wherein the polyamide contains 2 to 10% by weight of caprolactam as a copolymer component and 2 to 10% by weight of a polycapramide as a blend component. Crimped yarn.
ライローバル型であることを特徴とする請求項１または
２に記載のポリアミド原着捲縮糸。3. The crimp yarn according to claim 1, wherein the crimp yarn is a trilobal type having a single fiber cross-sectional deformation degree of 2.5 to 3.8.
むことを特徴とする請求項１〜３のいずれかに記載のポ
リアミド原着捲縮糸。4. The polyamide-origin crimped yarn according to claim 1, wherein copper is contained in an amount of 30 to 200 ppm as a copper atom.
ることを特徴とする請求項１〜４のいずれかに記載のポ
リアミド原着捲縮糸。5. The polyamide-origin crimped yarn according to claim 1, wherein the total fineness is 800 to 2,000 denier.
ミド原着捲縮糸に下撚りを施した後、その２本または３
本に上撚りを施した撚糸が、フェースヤーンの８０重量
％以上であることを特徴とするカーペット。6. The polyamide-origin crimped yarn according to any one of claims 1 to 5, which is subjected to ply-twisting, and then two or three of them.
A carpet, wherein the twisted yarn obtained by twisting the book is 80% by weight or more of the face yarn.
徴とする請求項６に記載のカーペット。7. The carpet according to claim 6, wherein the carpet is a cut pile carpet.
用されることを特徴とする請求項６または７に記載のカ
ーペット。8. The carpet according to claim 6, wherein the carpet is used as an entrance mat or a foot wipe mat.