JP2000015752A - Decorative sheet - Google Patents
Decorative sheetInfo
- Publication number
- JP2000015752A JP2000015752A JP10191105A JP19110598A JP2000015752A JP 2000015752 A JP2000015752 A JP 2000015752A JP 10191105 A JP10191105 A JP 10191105A JP 19110598 A JP19110598 A JP 19110598A JP 2000015752 A JP2000015752 A JP 2000015752A
- Authority
- JP
- Japan
- Prior art keywords
- resin emulsion
- emulsion
- ethylene
- decorative sheet
- vinyl acetate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は、合成樹脂エマルジ
ョンによる装飾模様を形成してなる装飾シートに関する
ものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a decorative sheet having a decorative pattern formed of a synthetic resin emulsion.
【０００２】[0002]
【従来の技術】従来より、建築物の壁装材等の装飾シー
トとして、紙（壁材用裏打紙）や布帛類等の基材上に、
合成樹脂製の発泡又は／及び非発泡の模様を形成した装
飾シートが使用されている。また、このような装飾シー
トの一つとして、合成樹脂エマルジョンによる装飾模様
を形成したものが知られている。そして、本発明出願人
は、上記のような合成樹脂エマルジョンによる装飾模様
を形成した装飾シートとして、特開平６−４７８７５号
公報にあるような、アクリル樹脂エマルジョンとエチレ
ン−酢酸ビニル共重合体エマルジョンを混合したエマル
ジョンにより装飾模様を形成した装飾シートを提案し
た。2. Description of the Related Art Conventionally, decorative sheets such as wall coverings for buildings have been used on paper (backing paper for wall materials) or base materials such as fabrics.
A decorative sheet formed of a synthetic resin foamed or / and non-foamed pattern is used. As one of such decorative sheets, a decorative sheet formed with a synthetic resin emulsion is known. The applicant of the present invention has proposed an acrylic resin emulsion and an ethylene-vinyl acetate copolymer emulsion as disclosed in JP-A-6-47875 as a decorative sheet on which a decorative pattern is formed by the synthetic resin emulsion as described above. A decorative sheet having a decorative pattern formed by the mixed emulsion was proposed.
【０００３】[0003]
【発明が解決しようとする課題】ところで、上記の提案
（以下、「先提案」という）においては、アクリル樹脂
エマルジョンとエチレン−酢酸ビニル共重合体エマルジ
ョンとを略等量或いはエチレン−酢酸ビニル共重合体エ
マルジョンの方がやや多くなるように混合したものが好
適であるとされている。すなわち、従来より通常使用さ
れているアクリル樹脂エマルジョンを使用した場合に
は、エンボス適性、表面性状（表面のべたつき感、汚れ
の付着性等）の面において、商品化に耐え得るものを得
るために、アクリル樹脂エマルジョンとエチレン−酢酸
ビニル共重合体エマルジョンとを３０：７０〜５０：５
０の範囲で混合したものが特に好適であるというのであ
る。In the above-mentioned proposal (hereinafter referred to as "prior proposal"), an acrylic resin emulsion and an ethylene-vinyl acetate copolymer emulsion are prepared in substantially equal amounts or ethylene-vinyl acetate copolymer emulsion. It is said that a mixture in which the coalesced emulsion is slightly increased is preferable. That is, in the case of using an acrylic resin emulsion conventionally used conventionally, in order to obtain a product which can withstand commercialization in terms of embossing suitability and surface properties (stickiness of surface, adhesion of dirt, etc.). , An acrylic resin emulsion and an ethylene-vinyl acetate copolymer emulsion in a ratio of 30:70 to 50: 5.
A mixture in the range of 0 is particularly suitable.
【０００４】本発明は、上記のようなアクリル樹脂エマ
ルジョンとエチレン−酢酸ビニル共重合体エマルジョン
とを混合した合成樹脂エマルジョンを使用して装飾模様
を形成した装飾シートにおいて、アクリル樹脂エマルジ
ョン及びエチレン−酢酸ビニル共重合体エマルジョンと
して特定のものを使用することにより、アクリル樹脂エ
マルジョンの混合割合を低く抑えてもエンボス適性が悪
化するようなことがなく、かつ、表面性状も良好な装飾
シートを提供し得ることを見出し、完成するに至ったも
のである。[0004] The present invention relates to a decorative sheet formed with a synthetic pattern obtained by mixing the above-mentioned acrylic resin emulsion and an ethylene-vinyl acetate copolymer emulsion to form a decorative pattern. By using a specific vinyl copolymer emulsion, even if the mixing ratio of the acrylic resin emulsion is kept low, the embossing suitability does not deteriorate, and a decorative sheet having good surface properties can be provided. It was found that it was completed.
【０００５】[0005]
【課題を解決するための手段】上記の課題を解決するた
めになされた本発明の装飾シートは、乾燥皮膜の引張試
験を行なったときに降伏値を有するアクリル樹脂エマル
ジョンと、乾燥皮膜の引張試験を行なったときに弾性変
形するエチレン−酢酸ビニル共重合体エマルジョンとを
混合した合成樹脂エマルジョンにより装飾模様を形成し
たことを特徴とするものである。Means for Solving the Problems A decorative sheet of the present invention made in order to solve the above-mentioned problems has an acrylic resin emulsion having a yield value when a tensile test of a dry film is performed, and a tensile test of a dry film. The decorative pattern is formed by a synthetic resin emulsion obtained by mixing an ethylene-vinyl acetate copolymer emulsion which is elastically deformed when performing the above.
【０００６】本発明において使用するアクリル樹脂エマ
ルジョンは、モノマーとして、２−エチルヘキシルアク
リレート、ブチルアクリレート、エチルアクリレート等
のアクリル酸エステルモノマー；メチルメタクリレート
等のメタクリル酸エステルモノマー；アクリル酸モノマ
ー；メタクリル酸モノマー；等から選ばれる一種以上の
アクリル系モノマー、或いはこれらのアクリル系モノマ
ーに、エチレンやスチレン等のビニル基を有するモノマ
ーを用い、これらのモノマーを、乳化剤（界面活性剤）
を用いて乳化重合させたものが使用できる。The acrylic resin emulsion used in the present invention comprises, as monomers, acrylate monomers such as 2-ethylhexyl acrylate, butyl acrylate and ethyl acrylate; methacrylate monomers such as methyl methacrylate; acrylic monomers; methacrylic monomers; One or more acrylic monomers selected from the above, or a monomer having a vinyl group, such as ethylene or styrene, is used as an emulsifier (surfactant).
What emulsion-polymerized using is used.
【０００７】本発明においては、上記のモノマーを乳化
重合させて得られるアクリル樹脂エマルジョンの中から
選ばれる、乾燥皮膜の引張試験を行なったときに降伏値
を有するアクリル樹脂エマルジョンが使用される。尚、
ここでいう降伏値を示すアクリル樹脂エマルジョンと
は、当該エマルジョンの乾燥皮膜の引張試験を行なった
とき、微小伸びの範囲で一旦抗張力の極大値を示し、更
なる伸長が継続される再び応力が増大して破断点を迎え
るという挙動を示すものである。また、本発明において
好ましくは、伸度が３〜５％の範囲で降伏値を示すアク
リル樹脂エマルジョンである。In the present invention, an acrylic resin emulsion selected from among acrylic resin emulsions obtained by emulsion polymerization of the above-mentioned monomers and having a yield value when a dry film is subjected to a tensile test is used. still,
The acrylic resin emulsion showing a yield value here indicates a maximum value of tensile strength once within a range of minute elongation when a dry film of the emulsion is subjected to a tensile test, and further elongation is continued. At the break point. Further, in the present invention, an acrylic resin emulsion showing a yield value in a range of elongation of 3 to 5% is preferable.
【０００８】一方、本発明において、上記のアクリル樹
脂エマルジョンと混合するエチレン−酢酸ビニル共重合
体エマルジョンは、乾燥皮膜の引張試験を行なったとき
に弾性変形するエチレン−酢酸ビニル共重合体エマルジ
ョン、すなわち、乾燥皮膜の引張試験を行なったときに
降伏値を示さないエチレン−酢酸ビニル共重合体エマル
ジョンである。On the other hand, in the present invention, the ethylene-vinyl acetate copolymer emulsion mixed with the acrylic resin emulsion is an ethylene-vinyl acetate copolymer emulsion which elastically deforms when a tensile test is performed on a dry film, that is, And an ethylene-vinyl acetate copolymer emulsion which does not show a yield value when a dry film is subjected to a tensile test.
【０００９】また、エチレン−酢酸ビニル共重合体エマ
ルジョンは、ポリビニルアルコールを保護コロイドとし
て重合させたものと、乳化剤（界面活性剤）を用いて乳
化重合させたものとに大別されるが、本発明において好
ましくは、成膜性に優れるポリビニルアルコールを保護
コロイドとして重合させたエチレン−酢酸ビニル共重合
体エマルジョンである。[0009] Ethylene-vinyl acetate copolymer emulsions are roughly classified into those obtained by polymerizing polyvinyl alcohol as a protective colloid and those obtained by emulsion polymerization using an emulsifier (surfactant). In the present invention, an ethylene-vinyl acetate copolymer emulsion obtained by polymerizing polyvinyl alcohol having excellent film-forming properties as a protective colloid is preferable.
【００１０】本発明の装飾シートは、上記のアクリル樹
脂エマルジョン及びエチレン−酢酸ビニル共重合体エマ
ルジョンを混合して用いるが、これらの混合割合として
好ましくは、重量比で２０：８０〜３０：７０の範囲で
ある。合成樹脂エマルジョン中に含まれる上記のアクリ
ル樹脂エマルジョンの混合割合が高くなりすぎると、折
り曲げ時に亀裂やひび割れ等の発生することが懸念さ
れ、アクリル樹脂エマルジョンの混合割合が低すぎる
と、エンボス適性や表面性状が悪化する。The decorative sheet of the present invention is used by mixing the acrylic resin emulsion and the ethylene-vinyl acetate copolymer emulsion described above. The mixing ratio thereof is preferably 20:80 to 30:70 by weight. Range. If the mixing ratio of the above acrylic resin emulsion contained in the synthetic resin emulsion is too high, there is a concern that cracks and cracks may occur at the time of bending, and if the mixing ratio of the acrylic resin emulsion is too low, the embossing suitability and surface The properties deteriorate.
【００１１】本発明の装飾シートにおいて使用される合
成樹脂エマルジョンは、上記のアクリル樹脂エマルジョ
ンとエチレン−酢酸ビニル共重合体エマルジョンとを混
合したものをであるが、得られる装飾シートの諸特性を
損なわない範囲であれば、上記のアクリル樹脂エマルジ
ョン及びエチレン−酢酸ビニル共重合体エマルジョン
に、上記以外の合成樹脂エマルジョンを混合しても差し
支えない。この合成樹脂エマルジョンとしては、例え
ば、上記以外のアクリル樹脂エマルジョンやエチレン−
酢酸ビニル共重合体エマルジョン、エチレン−酢酸ビニ
ル−アクリル共重合体エマルジョン、ポリエステルエマ
ルジョン等が挙げられる。The synthetic resin emulsion used in the decorative sheet of the present invention is a mixture of the above acrylic resin emulsion and an ethylene-vinyl acetate copolymer emulsion, but impairs the properties of the decorative sheet obtained. If it is not in the range, a synthetic resin emulsion other than the above may be mixed with the acrylic resin emulsion and the ethylene-vinyl acetate copolymer emulsion. Examples of the synthetic resin emulsion include acrylic resin emulsions other than those described above and ethylene-
Examples include a vinyl acetate copolymer emulsion, an ethylene-vinyl acetate-acryl copolymer emulsion, and a polyester emulsion.
【００１２】上記の合成樹脂エマルジョンには、従来よ
り使用されている合成樹脂エマルジョンに通常添加され
る各種添加剤、例えば、無機質粉体、マイクロカプセル
型熱膨張材、熱分解型発泡剤、分散剤、消泡剤、粘度調
整剤、印刷適性改良剤、乾燥遅延剤、粘着防止剤、抗菌
・防カビ剤、消臭剤、顔料等の着色剤等を必要に応じて
添加することができる。特に、本発明における合成樹脂
エマルジョン中には、従来よりこの種装飾シートに使用
されている合成樹脂エマルジョンと同様、原材料のコス
トダウン、得られる装飾シートへの難燃性付与等を目的
とし、水酸化アルミニウム、水酸化マグネシウム、酸化
チタン、炭酸カルシウム、炭酸マグネシウム等の無機質
粉体を添加するのが一般的である。The above-mentioned synthetic resin emulsion contains various additives usually added to conventionally used synthetic resin emulsions, such as inorganic powder, microcapsule type thermal expansion material, thermal decomposition type foaming agent, and dispersant. If necessary, a defoaming agent, a viscosity adjusting agent, a printability improving agent, a drying retarder, an antiadhesive, an antibacterial / antifungal agent, a deodorant, a coloring agent such as a pigment, and the like can be added. In particular, in the synthetic resin emulsion of the present invention, as in the case of the synthetic resin emulsion conventionally used for this type of decorative sheet, water is used for the purpose of reducing the cost of raw materials, imparting flame retardancy to the obtained decorative sheet, and the like. It is common to add inorganic powders such as aluminum oxide, magnesium hydroxide, titanium oxide, calcium carbonate, magnesium carbonate and the like.
【００１３】また、装飾模様を発泡模様とする場合に
は、上記のマイクロカプセル型熱膨張材又は／及び熱分
解型発泡剤を添加したものを使用し、これを適宜の手段
で塗布或いは印刷し、これを乾燥させた後、発泡させ
る。尚、本発明の装飾シートにおいて、装飾模様を発泡
模様とするためには、マイクロカプセル型熱膨張材を使
用するのが望ましい。すなわち、熱分解型発泡剤を使用
した場合には、マイクロカプセル型熱膨張材を使用した
場合に比して、より高温に加熱する必要があるため、装
飾模様が黄変するといったことが懸念される等の問題が
あり、従って、１４０〜２００℃の温度でも充分な発泡
倍率を確保し得るマイクロカプセル型熱膨張材を使用す
るのが望ましいのである。When the decorative pattern is a foamed pattern, the microcapsule type thermal expansion material and / or the thermally decomposable foaming agent is used, and is applied or printed by an appropriate means. After it is dried, it is foamed. In the decorative sheet of the present invention, it is desirable to use a microcapsule type thermal expansion material in order to make the decorative pattern a foamed pattern. That is, when a pyrolytic foaming agent is used, it is necessary to heat it to a higher temperature than when a microcapsule-type thermal expansion material is used. Therefore, it is desirable to use a microcapsule type thermal expansion material that can secure a sufficient expansion ratio even at a temperature of 140 to 200 ° C.
【００１４】上記のマイクロカプセル型熱膨張材は、低
沸点炭化水素等を熱可塑性高分子材料の殻中に封入した
ものである。このマイクロカプセルの殻を構成する熱可
塑性高分子材料としては、熱可塑性で、かつ、ガスバリ
ヤ性に優れることが要求され、具体的には、塩化ビニリ
デンとアクリロニトリルの共重合体を主体とする重合体
や、アクリロニトリルと（メタ）アクリル酸エステルの
共重合体を主体とする重合体等を使用することができ
る。また、このマイクロカプセル型熱膨張材の熱膨張温
度は、殻中に封入される低沸点炭化水素等の種類や殻を
構成する熱可塑性高分子材料の種類等によって変わり、
このような中から適宜の熱膨張温度のものを選定して使
用する。尚、熱膨張温度が異なる二種以上を併用しても
よい。The above-mentioned microcapsule type thermal expansion material is obtained by encapsulating a low-boiling hydrocarbon or the like in a shell of a thermoplastic polymer material. The thermoplastic polymer material constituting the shell of the microcapsule is required to be thermoplastic and have excellent gas barrier properties. Specifically, a polymer mainly composed of a copolymer of vinylidene chloride and acrylonitrile is required. Alternatively, a polymer mainly composed of a copolymer of acrylonitrile and (meth) acrylic acid ester can be used. In addition, the thermal expansion temperature of the microcapsule-type thermal expansion material varies depending on the type of low-boiling hydrocarbons and the like sealed in the shell and the type of thermoplastic polymer material forming the shell,
Among them, a material having an appropriate thermal expansion temperature is selected and used. Incidentally, two or more kinds having different thermal expansion temperatures may be used in combination.
【００１５】本発明装飾シートにおける合成樹脂エマル
ジョンによる装飾模様の形成は、従来の装飾シートと同
様、スクリーンプリンター、ロータリースクリーンプリ
ンター、グラビアプリンター等の適宜のプリンター、或
いは、ドクターナイフコーター、ロールコーター、コン
マドクターコーター、エアーナイフコーター等のコータ
ーを使用して、合成樹脂エマルジョンを印刷もしくは塗
布し、乾燥し、必要に応じて発泡させることにより行な
われる。勿論、発泡させた後、エンボス加工によって装
飾模様を形成することも可能である。The decorative pattern of the decorative sheet of the present invention is formed by a synthetic resin emulsion, as in the case of the conventional decorative sheet, by a suitable printer such as a screen printer, a rotary screen printer, a gravure printer, or a doctor knife coater, a roll coater, a comma. Using a coater such as a doctor coater or an air knife coater, the synthetic resin emulsion is printed or applied, dried and, if necessary, foamed. Of course, after foaming, it is also possible to form a decorative pattern by embossing.
【００１６】また、本発明装飾シートの表面には、必要
に応じて、表面の艶調整、防汚性付与、表面強度向上等
を目的とした表面処理を施したり、通常の印刷インキを
用いてのプリント模様等を形成することもできる。The surface of the decorative sheet of the present invention may be subjected to a surface treatment for the purpose of adjusting the gloss of the surface, imparting antifouling properties, improving the surface strength, etc., if necessary, or using a normal printing ink. Can be formed.
【００１７】[0017]
【実施例】以下に、本発明の具体例を挙げるが、本発明
は以下に示す実施例に限定されるものではない。EXAMPLES Specific examples of the present invention will be described below, but the present invention is not limited to the following examples.
【００１８】〔試験例１〜４〕表１に示す配合からなる
合成樹脂エマルジョンを、ロータリースクリーンプリン
ターを用いて壁紙用裏打紙上に印刷し、１２０℃のオー
ブン中で９０秒間乾燥させた。次いで、１５０℃のオー
ブン中で６０秒間加熱して発泡させた後、エンボス加工
を施して装飾シートを得た。Test Examples 1-4 Synthetic resin emulsions having the formulations shown in Table 1 were printed on a backing paper for wallpaper using a rotary screen printer, and dried in an oven at 120 ° C. for 90 seconds. Next, after heating in a 150 ° C. oven for 60 seconds to foam, embossing was performed to obtain a decorative sheet.
【００１９】得られた装飾シートについて、室温で折り
曲げたときの亀裂やひび割れ発生の有無、エンボス適性
及び表面性状を以下の基準で評価した。 （１）亀裂・ひび割れ発生の有無 ○：亀裂・ひび割れの発生無し ×：亀裂・ひび割れの発生有り （２）エンボス適性 ○：エンボスによる絞が深く、かつ鮮明に入っている △：エンボスによる絞がやや浅く、かつやや不鮮明であ
るが、商品化可能 ×：エンボスによる絞が浅く、不鮮明 （３）表面性状 ○：ドライタッチでべたつき等なし、汚れも付着し難い ×：表面にべたつき感があり、汚れが付着し易いThe obtained decorative sheet was evaluated for the occurrence of cracks and cracks when bent at room temperature, suitability for embossing, and surface properties according to the following criteria. (1) Presence or absence of cracks / cracks ○: No occurrence of cracks / cracks ×: Presence of cracks / cracks (2) Suitability for embossing ○: Deep and clear embossing △: Embossing narrow Slightly shallow and somewhat unclear, but commercializable ×: Shallow squeezing by embossing, unclear (3) Surface properties ○: No stickiness due to dry touch, dirt is hard to adhere ×: There is sticky feeling on the surface, Easy to get dirty
【００２０】[0020]
【表１】 [Table 1]
【００２１】以上の結果から明らかなように、アクリル
樹脂エマルジョンとして、明確な降伏値を示さないもの
を使用したもの（試験例３）では、エンボス適性及び表
面性状において劣り、また、降伏値を示すアクリル樹脂
エマルジョンを使用しても、その混合割合が大きいもの
（試験例４）では、折り曲げたときに亀裂やひび割れが
発生するといった問題がある。一方、アクリル樹脂エマ
ルジョンとして、明確な降伏値を示すものを用い、その
混合割合を適当範囲としたもの（試験例１、２）では、
折り曲げたときに亀裂やひび割れ等が発生することがな
く、また、エンボス適性や表面性状の面でも優れている
ことがわかる。As is apparent from the above results, the acrylic resin emulsion which does not show a clear yield value (Test Example 3) is inferior in embossability and surface properties and shows a yield value. Even if an acrylic resin emulsion is used, a mixture having a large mixing ratio (Test Example 4) has a problem that cracks and cracks occur when bent. On the other hand, an acrylic resin emulsion having a clear yield value was used, and the mixing ratio thereof was set to an appropriate range (Test Examples 1 and 2).
It can be seen that no cracks, cracks or the like are generated when the sheet is bent, and that it is excellent in terms of embossability and surface properties.
【００２２】[0022]
【発明の効果】以上詳述したように、本発明の装飾シー
トは、装飾模様を形成する合成樹脂エマルジョンとして
特定の性状のアクリル樹脂エマルジョン及びエチレン−
酢酸ビニル共重合体エマルジョンを使用しているので、
アクリル樹脂エマルジョンの混合割合が極少量であって
も、エンボス適性や表面性状に優れるものである。As described in detail above, the decorative sheet of the present invention can be used as a synthetic resin emulsion for forming a decorative pattern.
Because we use vinyl acetate copolymer emulsion,
Even if the mixing ratio of the acrylic resin emulsion is extremely small, it is excellent in embossability and surface properties.
Claims (3)
装飾模様を形成してなる装飾シートであって、 合成樹脂エマルジョンが、乾燥皮膜の引張試験を行なっ
たときに降伏値を有するアクリル樹脂エマルジョンと、
乾燥皮膜の引張試験を行なったときに弾性変形するエチ
レン−酢酸ビニル共重合体エマルジョンとを混合した合
成樹脂エマルジョンである装飾シート。1. A decorative sheet formed by forming a decorative pattern of a synthetic resin emulsion on a base material, the synthetic resin emulsion comprising an acrylic resin emulsion having a yield value when a dry film is subjected to a tensile test. ,
A decorative sheet that is a synthetic resin emulsion mixed with an ethylene-vinyl acetate copolymer emulsion that elastically deforms when a dry film tensile test is performed.
酢酸ビニル共重合体エマルジョンとの混合比率が、重量
比で２０：８０〜３０：７０である請求項１記載の装飾
シート。2. An acrylic resin emulsion and ethylene-
The decorative sheet according to claim 1, wherein the mixing ratio with the vinyl acetate copolymer emulsion is 20:80 to 30:70 by weight.
ョンが、ポリビニルアルコールを保護コロイドとするエ
チレン−酢酸ビニル共重合体エマルジョンである請求項
１又は２記載の装飾シート。3. The decorative sheet according to claim 1, wherein the ethylene-vinyl acetate copolymer emulsion is an ethylene-vinyl acetate copolymer emulsion containing polyvinyl alcohol as a protective colloid.