HK1155695B - Compositions for use in three dimensional model printing - Google Patents

Description

FIELD OF THE INVENTION

The present invention relates to three-dimensional (3-D) modeling in general and to methods and compositions for use in 3-D printing of complex structures in particular.

BACKGROUND OF THE INVENTION

3-D printing, which works by building parts in layers, is a process used for the building up of 3-D models. 3-D printing is relatively speedy and flexible, allowing for the production of prototype parts and tooling directly from a CAD model, for example.

3-D printing enables the manufacturer to obtain a full 3-D model of any proposed product before tooling, thereby possibly substantially reducing the cost of tooling and leading to a better synchronization between design and manufacturing. A lower product cost and improved product quality can also be obtained.

Various systems have been developed for computerized 3-D printing. In US Patent No. 6,259,962 to the Assignees of the present application, there is described an apparatus and a method for 3-D model printing. U.S. Patent No. 6,259,962 describes apparatus including a printing head having a plurality of nozzles, a dispenser connected to the printing head for selectively dispensing interface material in layers, and curing means for optionally curing each of the layers deposited.. The depth of each deposited layer is controllable by selectively adjusting the output from each of the plurality of nozzles.

In US Patent No: 6,658,314 to the Assignees of the present invention, there is described an apparatus and a method for 3-D model printing. U.S. Patent 6,658,314 describes a system and a method for printing complex 3-D models by using interface materials having different hardness or elasticity and mixing the interface material from each of the printing heads to control the hardness of the material forming the 3-D model. The construction layers of the model are formed from interface material having a different (harder) modulus of elasticity than the material used to form the release (and support) layers, thereby allowing for the forming of complex shapes.

Radiation curable inks are disclosed in U.S. Patent Nos. 4,303,924 , 5,889,084 , and 5,270,368 , U.S. Patent No. 4,303,924 discloses radiation curable compositions for jet-drop printing containing multifunctional ethylenically unsaturated material, monofunctional ethylenically unsaturated material, a reactive synergist, a dye colorant and an oil soluble salt U.S. Patent No. 5,889,084 discloses a radiation curable ink composition for ink-jet printing which comprises a cationically photoreactive epoxy or vinyl ether monomer or oligomer, a cationic photo-initiator and a coloring agent. U.S. Patent No. 5,270,368 discloses a UV curable ink composition for ink-jet printing comprising a resin formulation having at least two acrylate components, a photo-initiator and an organic carrier..

The ink compositions disclosed in these references are formulated for use in ink-jet printing. Compositions for ink-jet printing are formulated differently from compositions for building 3-D models, and thus have different properties. For example, high viscosity at room temperature is a desirable property for 3-D objects, and thus compositions for building 3-D models are designed to have a high viscosity at room temperature. In contrast, compositions for ink-jet printing are designed to have low viscosity at room temperature in order to function well in the printing process. None of the above-mentioned references disclose compositions that are especially formulated for 3-D printing. Radiation curable inks for 3-D objects are disclosed in U.S. Patent No. 5,705,316 . U.S. 5,705,316 discloses compounds having at least one vinyl ether group, which also contain in the molecule at least one other functional group such as an epoxy or an acrylate group; compositions comprising these compounds; and methods of producing 3-D objects using these compositions. The compounds of U.S. 5,705,316 are complex molecules that are not readily available and thus need to be especially synthesized, which incurs additional time and costs.

None of the above mentioned references provides simple, easily obtainable curable compositions that are suitable for use in 3-D printing. In addition, the above mentioned references do not provide compositions for use in supporting and/or releasing a 3-D model during construction. Finally, the above mentioned references do not provide methods for 3-D printing, by using interface materials having different hardness or elasticity and by mixing the interface materials to control the hardness of the material forming the 3-D model.

A thermopolymer material adapted for use in thermal stereolithography is disclosed in U.S. Patent No. 5,855,836 . The thermopolymer of U.S. 5,855,836 comprises a mixture of a low shrinkage polymer resin, a low viscosity material such as paraffin wax, at least one microcrystalline wax, a toughening polymer and a plasticizer. These wax-like materials are solid at room temperature.

Thus, there is a need for simple, easily obtainable curable compositions, that are specially formulated to construct a 3-D model. There is further a need for simple, easily obtainable curable compositions, that are specially formulated to provide support to a 3-D, by forming support/and or release layers around a 3-D object during construction. Lastly, there is a need for methods of constructing a 3-D model by using the above mentioned compositions.

SUMMARY OF THE INVENTION

The present invention relates to compositions according to claim 1 for use in the manufacture of 3 D objects and for use as support and/or release material in the manufacture of said 3-D objects.

The present invention relates to a

• composition suitable for support in building a three dimensional object by a method of selective dispensing, said composition comprising: a non-reactive and low toxicity component;a reactive component;a photoinitiator;a surface active agent for reducing surface tension to around 30 mN/m (30 dyne/cm),a bubble releasing substance able to produce gas upon exposure to water or to an alkaline or acidic water solution; anda stabilizer,wherein said composition has a first viscosity greater than 80 mPa·s (cps) at ambient temperature and a second viscosity lower than 20 mPa·s (cps) at a second temperature higher than 60°C and after irradiation, said composition results in a solid material.

In accordance with an embodiment of the present invention, there is thus provided an interface material composition suitable for use in support layers for three-dimensional objects by a method of selective dispensing. The composition comprises:

• at least one (meth)acrylic reactive component;
• at least one non-reactive and low toxicity component;
• wherein the non-reactive component is not reactive with the (meth)acrylic reactive component,
• at least one free radical photo-initiator;
• at least one surface active agent; and
• at least one stabilizer;

The composition has a first viscosity at room temperature, and a second viscosity compatible with ink-jet printers at a second temperature, wherein said second temperature is higher than room temperature;

The composition is irradiated or cured resulting in a semi-solid form.

In accordance with an embodiment of the present invention, the composition further comprises a molecule having one or more vinyl ether substituents, a water miscible component that is, after curing, capable of swelling upon exposure to water or to an alkaline or acidic water solution, or a combination thereof. In another embodiment, the water miscible component is a (meth)acrylated urethane oligomer derivative of polyethylene glycol, a partially (meth)acrylated polyol oligomer, a (meth)acrylated oligomer having hydrophilic substituents, polyethylene glycol mono or di (meth)acrylated, or any combination thereof.

Furthermore, in accordance with an embodiment of the present invention, the non-reactive component is polyethylene glycol, methoxy polyethylene glycol, glycerol, ethoxylated polyol, or propylene glycol or any combination thereof. Furthermore, in accordance with the present invention, the first viscosity of the composition is greater than 80 cps. In one embodiment, the first viscosity is between 80 and 300 cps. In another embodiment, the first viscosity is around 200 cps.

Furthermore, in accordance with the present invention, the second viscosity of the composition is lower than 20 cps at a second temperature, which is greater than 60°C. In another embodiment, the second viscosity is between 8 arid 15 cps at the second temperature, which is greater than 60°C. In another embodiment, the second viscosity is about 11 cps at a temperature around 85°C.

Furthermore, in accordance with the present invention, the second interface composition further comprising a component able to produce gas upon exposure to water or to an alkaline or acidic solution. In an embodiment, the component able to produce gas upon exposure to water or to an alkaline or acidic solution is sodium bicarbonate.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention will be understood and appreciated more fully from the following detailed description taken in conjunction with the appended drawings in which:

• Fig. 1 is a schematic illustration of an embodiment of a 3-D printing system, described in US Patent No: 6,658,314, assigned to the Assignees of the present application; and
• Fig. 2 is an elevational view of a 3-D object, constructed in accordance with an embodiment of the present Invention.

DETAILED DESCRIPTION OF THE PRESENT INVENTION

The present invention relates to compositions for use as a support and/release material in the manufacture of 3-D objects. The present specification further relates to a method for the preparation of a 3-D object by 3-D printing, using the above-mentioned compositions, and to a 3-D object obtained by said method.

A composition for use in the manufacture of the 3-D objects comprises at least one reactive component, at least one photo-Initiator, at least one surface-active agent and at least one stabilizer. The composition is formulated so as to be compatible for use with ink-jet printers and to have a viscosity at room temperature above 50 cps.

The composition for use as a support and/or second interface material in the manufacture of the 3-D objects comprises at least one non-reactive and low-toxicity component, at least one surface-active agent and at least one stabilizer. The composition may further contain at least one reactive component and at least one photo-initiator The composition is formulated so as to be compatible for use with ink-jet printers and to have a viscosity at room temperature above 50 cps.

The compositions will be described in further detail below.

The 3-D object described in the present specification can be built using a 3-D printing system similar to the one described in US Patent No. 6,658,314 . assigned to the Assignees of the present application. The 3-D printing system is shown in Fig 1, to which reference is now made. Fig 1 is an illustration of a 3-D printing system, generally designated 10, which includes one or more printing heads, referenced 12, and at least two dispensers generally referenced 14 and individually referenced 14a and 14b, containing interface materials, generally referenced 16 and individually referenced 16a and 16b, respectively.

Printing head 12 has a plurality of ink-jet type nozzles 18, through which interface materials 16a and 16b are jetted. In one embodiment, first dispenser 14a is connected to a first set of nozzles, referenced 18a, and second dispenser 14b is connected to a second set of nozzles, referenced 18b. Thus first interface material 16a is jetted through nozzles 18a, and second interface material 16b is jetted through nozzles 18b. Alternatively, in another embodiment (not shown), the 3-D printing system may comprise at least two printing heads. The first printing head is connected to first dispenser 14a and is used to jet first interface material 16a; and the second printing head is connected to second dispenser 14b is used to jet second interface material 16b.

The 3-D printing system 10 further includes a controller 20, a Computer Aided Design (CAD) system 22, curing unit 24, and optionally a positioning apparatus 26. The controller 20 is coupled to the CAD system 22, curing unit 24, positioning apparatus 26, printing head 12 and each of the dispensers 14. The 3-D object being produced (28) is built in layers, the depth of each layer being controllable by selectively adjusting the output from each of the ink-jet nozzles 18.

By combining or mixing materials from each of the dispensers, wherein each dispenser contains interface material having a different hardness, it is possible to adjust and control the hardness of the material forming the 3-D object being produced. Thus, by combining the interface material being output from each of the dispensers, different parts of the 3-D object having a different modulus of elasticity and a different strength can be produced.

As used hereinafter, the term "strength" is used as a relative term to Indicate the difference in modulus of elasticity among interface materials. The strength of a material may be described by reference to its modulus of elasticity, which may be defined as: "the ratio of stress to its corresponding strain under given conditions of load, for materials that deform elastically, according to Hooke's law".

The first dispenser 14a contains a first interface material 16a, referred to hereinafter as the "first interface material", and the second dispenser 14b contains a second interface material 16b, referred to hereinafter as the "second interface material". The first interface material has a different (harder) modulus of elasticity and a greater strength than the second interface material. By combining the first interface material and the second interface material, different layers of the 3-D object having a different modulus of elasticity and a different strength can be produced, such as, for example, a construction layer, a support layer and a release layer, as defined hereinbelow..

For example, combining the first interface material and the second interface material forms a multiplicity of construction layers, which are defined as the layers constituting the 3-D object. Multiplicity, as used hereinafter, refers to a number which is one or greater.

Further, combining the first interface material and the second interface material forms a multiplicity of support layers, which are defined as the layers supporting the 3-D object, and not constituting the 3-D object.

Further, combining the first interface material and the second interface material forms a multiplicity of release layers, which are defined as the layers (not constituting the 3-D object) for separating the 3-D object layer from layers such as the support layers. The release layers have a lower modulus of elasticity and a lower strength than the construction layers and the support layers.

in one case, the support layers are designed exactly as the construction layers, and thus have the same modulus of elasticity and the same strength as the construction layers. In this way, the construction layers form a core, and the support layers look like the negative printing of the core. The release layers are positioned between the construction layers and the support layers, and are used to separate the construction layers from the support layers.

In another case, the support layers have a lower modulus of elasticity and a lower strength than the construction layers. The support layers may be separated from the construction layers by taking advantage of their weaker properties, as will be explained In detail below. Alternatively, the support layers may be separated from the construction layers by positioning release layers between the construction layers and the support layers.

In order to more clearly define the present invention, reference is now made to Fig 2, which is a 3-D model of a wineglass, generally referenced 30. This 3-D model is printed using the ink-jet type printing system of Fig 1. Combining the first interface material and the second interface material form a multiplicity of construction layers 32 which make up wine glass 30.

The construction layers 32 of wineglass 30 need to be supported externally, such as in the area referenced 34. Furthermore, an internal void, referenced 36, needs to be formed during printing. Thus a multiplicity of support layers 38, formed by combining the first interface material and the second interface material, are printed.

Furthermore, combination of the first interface material and the second interface material forms a multiplicity of release layers 40. In some cases release layers 40 are positioned between construction layers 32 and support layers 38. Generally, release layers 40 have a different (lower) modulus of elasticity than support layers 38 and construction layers 32. Thus release layers 40 can be used to separate support layers 38 from construction layers 32.

The present invention, which will now be described in detail, provides compositions according to claim 1 suitable for use as the the second interface material.

The second interface material of the present invention are especially designed and formulated for building a 3-D object using 3-D printing. Accordingly, the interface materials are designed to have increased viscosity at room temperature, which is defined as about 20-30C. The second interface material has a viscosity greater than 80 cps at room temperature, more preferably between 80 and 300 cps. In a preferred embodiment, the second interface material have a viscosity of around 300 cps at room temperature,

Further, the second interface material have a second viscosity compatible with ink-jet printing, at a second temperature which is higher than room temperature. A composition compatible with ink-jet printing has low viscosity, preferably below 20 cps at the printing temperature, in order to function properly In the printing process. The second interface material, upon heating, has a viscosity below 20 cps at a second temperature higher than 60°C, enabling the construction of the 3-D object under heat. The temperature typically used to build the 3-D model described in the present specification is higher than 60C, preferably about 85C. In one embodiment, the second interface materials has a viscosity of 8-15 cps at a temperature greater than 60C. In another embodiment, the second interface materials has a viscosity of 11 cps at a temperature of about 85C.

Having this viscosity, the second interface material is distinguished from prior art formulations designed for ink-jet printing, which have low viscosity at room temperature, the temperature at which the printing is conducted.. High viscosity at room temperature is a desirable property for 3-D objects, a feature that is lacking in the prior art formulations.

SECOND INTERFACE MATERIAL

The second interface material is formulated to form a release layer to permit a manual easy cleaning of the 3-D model from its support. The second interface material may be one of two different principle kinds: 1) a liquid material lacking any curable groups that remains liquid even after irradiation In one embodiment, the liquid is water miscible and is easily washed out by water; and 2) a solid or semi-solid material that is formulated as a very weak, curable material that, when cured, is capable of swelling in water or in alkaline or acidic water. Thus, when cured, the second interface material swells and almost breaks upon exposure to water, with minimum manual work required, i.e. a semi-solid form material. In both cases the second interface material is formulated so as to permit fast, easy and efficient removal of the support and release construction layers and cleaning of the 3-D model.

The second interface material according to claim 1 of the present invention comprises: at least one non-reactive and low toxicity compound; at least one surface-active agent; and at least one stabilizer. The non-reactive component of the second interface material is a non-reactive and low toxicity compound, preferably a water miscible once.

The term "non-reactive" refers to compounds of the second interface composition that do not undergo a curing process, therefor remain in a liquid form after irradiation. The non-reactive component is chosen to reduce the mechanical strength of the second interface material and/or enhance its water-swelling rate. High water diffusion rate is desirable in order to minimize the time needed for the water cleaning process of the 3-D model. Examples of non-reactive components for the present invention are polyethylene glycol marketed by Aldrich under the trade name PEG 400, methoxypolyethylene glycol marketed by Aldrich under the trade name methoxycarbowax 500 and 1000, and propylene glycol. Other examples are ethoxylated polyols and glycerol.

In the present invention, the second interface material further comprises at least one reactive component and at least one photo-initiator. The second interface material is formulated as a curable composition that is capable of solidifying upon radiation exposure. The reactive components may be similar to those used in the first interface material, but may be chosen specifically to give a hydrophillic cured resin, with very weak mechanical properties. Thus, upon curing, a solid composition is formed that is very weak and can be easily pulverized by hand or using water.

The reactive component is at least one of an acrylic component, a molecule having one or more vinyl ether substituents, or a water miscible component that is, after curing, capable of swelling upon exposure to water or to an alkaline or acidic water solution.

The acrylic component is an acrylic monomer or an acrylic oligomer, and may be any one of the examples defined hereinabove. Examples of acrylic components for use in the second interface material of the present invention are polyethylene glycol monoacrylate, marketed by Laporte under the trade name Bisomer PEA6, and polyethylene glycol diacrylate, marketed by Sartomer under the trade name SR-610, methoxypolyethyleneglycole 550 monomethacrylate, and the like.

The reactive component of the second interface material can also be a water miscible component that is, after curing, capable of swelling upon exposure to water or to an alkaline or acidic water solution. Examples of water miscible components for the present invention are an acrylated urethane oligomer derivative of polyethylene glycol - polyethylene glycol urethane diacrylate, a partially acrylated polyol oligomer, an acrylated oligomer having hydrophillic substituents, or any combination thereof. The hydrophilic substituents are acidic substituents, amino substituents, hydroxy substituents, or any combination thereof An example of an acrylated monomer with hydrophillic substituents is betha-carboxyethyl acrylate, which contains acidic substituents The reactive component of the second interface material can also be a molecule having one or more vinyl ether substituents, which may be any of the compounds as defined hereinabove. An example of vinyl ether for the second interface material is 1,4-cyclohexane dimethanol divinyl ether, marketed by ISP under the trade name CHVE.

In one embodiment, the reactive component of the second interface material is an acrylic oligomer. In another embodiment, the reactive component of the second interface material is a combination of an acrylic component as defined hereinabove and a water miscible component as defined hereinabove. In another embodiment, the reactive component of the present invention is a combination of an acrylic component as defined hereinabove and a molecule having one or more vinyl ether substituents, as defined hereinabove. In another embodiment, the reactive component of the present invention is a combination of a water miscible component as defined hereinabove, and a molecule having one or more vinyl ether substituents, as defined hereinabove. When the second interface material comprises a reactive material, the second interface material further comprises a photo-initiator. The photo-initiator can be any photo-initiator, as defined above.

Besides swelling, another characteristic of the solid support upon exposure to water or to an alkaline or acidic water solution may be the ability to break down during exposure to water or to an alkaline or acidic water solution. Because the second interface material is made of hydrophillic components, during the swelling process, internal forces appear and cause fractures and breakdown of the cured second interface material.

In addition, the second interface material may be at least partially water-soluble. At least part of the second interface material is completely water soluble/miscible During the removal of the support and/or release layers, the water soluble/miscible components are extracted out with water.

In addition the second interface material liberates bubbles upon exposure to water or to an alkaline water or acidic water solution. The bubbles are intended to help in the process of removal of the support and/or release layers from the construction layers.

The bubbles are liberated by a bubble releasing substance (BRS) that is present in the water solution that is used to clean out the 3-D object, Such a substance may be a carbonate or bicarbonate, for example sodium bicarbonate (SBC). During the swelling process, at least part of the SBC is introduced or absorbed into the second interface material, where it is transformed into carbon dioxide gas (CO2) and a water-soluble salt. The trigger for the production of CO2 may be the reaction of the SBC with an acid functionality present in the second interface material. Such acid functionality may be introduced as part of the second interface material formulation or introduced later, after curing, using an acid water solution. For example, the first step may be to put the 3-D object with its support in a water solution containing a SBC, then to place the same object in an acidic solution The acid will start to decompose the SBC and product gas (bubbles).

The substance that liberates gas is already present in the formulation of the second interface material. For example, the second interface material may contain calcium bicarbonate as a solid pigment. In that case, the trigger is the introduction of the second interface material in a water or acidic solution.

It should be clear that a BRS is not limited to a sodium bicarbonate or calcium bicarbonate and an acidic water solution. Other chemical reagents and reactions may be used to achieve the same result - the production of bubbles inside the matrix of the second interface material. For example, the SBC may be any alkaline metal or alkaline earth metal carbonate or bicarbonate Examples of preferred formulations of the second Interface material outside the scope of claim 1 are provided hereinbelow in Table 5 and Table 6, to which reference is now made. Tables 5 and 6 display various formulations that are suitable for use as the second interface material.

	Trade Name	Chemical Type	Function in the formulation	Supplier
A	SR-610	Polyethylene Glycole (600) Diacrylate	Oligomer	Sartomer
B	Bisomer PEA6	Polyethylene Glycole monoacrylate	Water swelling/ sensitive Oligomer	Laport
C	PEG 400	Polyethylene Glycole 400	Polymer (hydrophilic and palsticizer)	Aldrich
D	Irgacure 907	alpha-Amino Ketone	Free radical photo-initiator type I	Ciba Specialties Chemical Inc.
E	BP	Benzophenone	Free radical photo-initiator Type II	Satomer
F	Triethanol Amine	Ternary Amine	Free radical Coinitiator for Type II photo-initiator	Aldrich
G	Byk 307	Silicone Surface Additive	Surface agent	Byk Chemie
H	MEHQ	4-Methoxy phenol	Inhibitor (thermal stabilizer)	Sigma
I	PEG UA	Polyethylene glycol urethane diacrylate	Water swelling/sensiti ve oligomer	Home made
J	AP	Partially acrylated polyol	Water swelling/ sensitive oligomer	Home made
K	Betha-CEA	Betha-caboxyethyl acrylate	Acidic monomer
M	CHVE	1,4-Cyclohexane dimethanol divinyl ether	Vinyl ether monomer	ISP
N	Tone polyol 0301	Caprolactone polyol	Polyol (plasticizer)	Union Cabide
P	methoxycarbo wax 500 and 1000	methoxypolyethylene glycol	Polymer (hydrophilic and palsticizer)

Example	A	B	C	D	E	F	G	H	I	J	K	L	M	N
1	X	X	X	X	X
2	X	X	X	X	X	X
3	X	X	X	X	X
4	X	X	X	X	X	X
5	X	X	X	X	X	X
6	X	X	X	X	X	X	X
7	X	X	X	X
8	X	X	X	X	X
9	X	X	X	X	X	X
10	X	X	X	X	X
11	X	X	X	X
12	X	X	X	x	X	X
13	X	X	X	X	X	X
14	X	X	X	X	X	X	X	X	X	X

A particularly preferred formulation of the second interface material is presented in entry No. 3 of Table 6. According to this particularly preferred embodiment of the present invention, the second interface material comprises: a water swelling oligomer, which can be any water swelling oligomer as defined hereinabove, and which is preferably polyethylene glycole monoacrylate; a non-reactive component, which can be any non-reactive component as defined hereinabove, and which is preferably polyethylene glycole; a radical photo-initiator, which can be any radical photo-initiator as defined hereinabove, and which is preferably alpha-amino ketone; a surface agent, which is preferably a silicone surface additive; and an inhibitor, which is preferably 4-methoxyphenol.

Another particularly preferred formulation of the second interface material is presented in entry No.. 4 of Table 6. According to this particularly preferred embodiment of the present invention, the second interface material comprises: a water swelling oligomer, which can be any water swelling oligomer as defined hereinabove, and which is preferably polyethylene glycole monoacrylate; a non-reactive component, which can be any non-reactive component as defined hereinabove, and which is preferably polyethylene glycole; a radical photo-initiator, which can be any radical photo-initiator as defined hereinabove, and which is preferably benzophenone; a co-initiator, which can be any co-initiator as defined hereinabove, and which is preferably triethanolamine; a surface agent, which is preferably a silicone surface additive; and an inhibitor, which is preferably 4-methoxyphenol.

The first interface material and the second interface material are suitable for use in the method for 3-D printing which is described in U.S. Patent 6,658,314 , assigned to the Assignees of the present application.

Briefly, the method comprises: dispensing a first interface material from a printing head; dispensing a second interface material from said printing head; and combining the first interface material and the second interface material in pre-determined proportions to a produce a multiplicity of construction layers for forming the three-dimensional model.

The method further comprises the step of curing the first interface material. Further, when the second interface material comprises a reactive component, the method may further comprise the step of curing the second interface material. Curing may be carried out as described in U.S. Patent 6,658,314 . For example, the curing method is by radiation, such as Ultraviolet (UV) and/or Visible (Vis) and/or Infra Red (IR) and/or UV-Vis radiation. Preferably the curing method is UV-Vis radiation.

In operation, in order to obtain layers of different modulus of elasticity and a different strength, the first interface material and the second interface material are combined in predetermined proportions. For example, in order to obtain layers having a higher modulus of elasticity and a higher strength such as the construction layers, a suitable combination that contains mostly the first interface material is used. Further, in order to obtain layers having a lower modulus of elasticity arid a lower strength such as the release layers, a suitable combination that includes mostly the second interface material is used.

By way of example, in order to produce the construction layers and/or the support layers, a combination that includes 90-100% of the first interface material and 0-10% of the second interface material is used. Further, in order to produce the release layers, a combination that includes 0-10% of the first interface material and 90-100% of the second interface material is used. In another embodiment, in order to produce support layers that have a lower modulus of elasticity and a lower strength than the construction layers, a combination that includes 30-70% of the first interface material and 70-30% of the second interface material is used.

Thus a 3-D object is produced which is comprised of a core consisting of a multiplicity of construction layers. The construction layers are formed by combining predetermined proportions of the first interface material and the second interface material.

The 3-D object may further comprise a multiplicity of support layers for supporting the core. The support layers are prepared by combining pre-determined proportions of the first interface material and the second interface material. The support layers may be designed exactly like to construction layers, or may be designed to be weaker (lower modulus of elasticity) than the construction layers.

The 3-D object may further comprise a multiplicity of release layers for releasing the support layers from the construction layers. Preferably, the release layers are positioned between the support layers and the construction layers. The release layers are prepared by combining pre-determined proportions of the first interface material and the second interface material.

It will be appreciated by persons skilled in the art that the present invention is not limited by what has been particularly shown and described herein above and that numerous modifications, all of which fall within the scope of the present invention, exist. Rather, the scope of the invention is defined by the claims which follow:

Claims (15)

1. A composition suitable for support in building a three dimensional object by a method of selective dispensing, said composition comprising:

   a non-reactive and low toxicity component;

   a reactive component;

   a photoinitiator;

   a surface active agent for reducing surface tension to around 30 mN/m (30 dyne/cm);

   a bubble releasing substance able to produce gas upon exposure to water or to an alkaline or acidic water solution; and

   a stabilizer,

   wherein said composition has a first viscosity greater than 80 mPa·s (cps) at ambient temperature and a second viscosity lower than 20 mPa·s (cps) at a second temperature higher than 60°C and after irradiation, said composition results in a solid material.
2. The composition of claim 1, wherein said bubble releasing substance is sodium bicarbonate or calcium carbonate.
3. The composition of any preceding claim, wherein said non-reactive component is polyethylene glycol, methoxypolyethylene glycol, glycerol, propylene glycol or an ethoxylated polyol.
4. The composition of any preceding claim, wherein said reactive component is an acrylic monomer or an acrylic oligomer.
5. The composition of any one of claims 1 to 3, wherein said reactive component is polyethylene glycol monoacrylate, polyethylene glycol diacrylate or methoxypolyethylene glycol 550 monomethacrylate.
6. The composition of any one of claims 1 to 3, wherein said reactive component is a water miscible component that after curing is capable of swelling upon exposure to water or to an alkaline or acidic water solution.
7. The composition of claim 6, wherein the water miscible component is an acrylated urethane oligomer derivative of polyethylene glycol-plolyethylene glycol urethane diacrylate, a partially acrylated polyol oligomer, an acrylate oligomer having hydrophilic substituents, or any combination thereof.
8. The composition of claim 7, wherein said hydrophilic substituents comprise acidic substituents, amino substituents, hydroxy substituents, or any combination thereof.
9. The composition of claim 6, wherein the water miscible component is polyethylene glycol monoacrylate.
10. The composition of any one of claims 1 to 3, wherein said reactive component is a molecule having one or more vinyl ether substituents.
11. The composition of any preceding claim, wherein the material resulting from irradiation swells, breaks down or dissolves upon exposure to water or to an alkaline or acidic water solution.
12. The composition of any one of claims 1 to 10, wherein the material resulting from irradiation is formulated as a hydrophilic cured resin with weak mechanical properties that can be easily pulverized by hand or using water.
13. The composition of any one of claims 1 to 3, wherein the reactive component is polyethylene glycol monoacrylate and the non-reactive component is polyethylene glycol.
14. The composition of any preceding claim, for use in a three-dimensional printing system to build a support construction for a three-dimensional object.
15. A solid composition formed by curing the composition of any one of claims 1 to 14.