GB834303A - Improvements in metallizing ceramics - Google Patents

Improvements in metallizing ceramics

Info

Publication number
GB834303A
GB834303A GB12396/57A GB1239657A GB834303A GB 834303 A GB834303 A GB 834303A GB 12396/57 A GB12396/57 A GB 12396/57A GB 1239657 A GB1239657 A GB 1239657A GB 834303 A GB834303 A GB 834303A
Authority
GB
United Kingdom
Prior art keywords
reducing atmosphere
molybdenum
molybdenum trioxide
mixture
metallized
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB12396/57A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
General Electric Co
Original Assignee
General Electric Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by General Electric Co filed Critical General Electric Co
Publication of GB834303A publication Critical patent/GB834303A/en
Expired legal-status Critical Current

Abstract

The surface of a ceramic member is metallized by applying thereto, e.g. by dipping, a mixture, suspended in a volatile liquid such as acetone, consisting of 50-90% by weight of molybdenum trioxide and the remainder manganese powder, and then heating in a reducing atmosphere at 1200-1400 DEG C. at which temperature the molybdenum trioxide is reduced to molybdenum. The reducing atmosphere may be hydrogen.ALSO:The surface of a ceramic member is metallized by applying thereto a mixture consisting of 50-90% by weight of molybdenum trioxide and the remainder manganese powder, and then heating in a reducing atmosphere at 1200 DEG -1400 DEG C. at which temperature the molybdenum trioxide is reduced to molybdenum. The mixture is preferably applied as a suspension in a volatile liquid such as acetone. The reducing atmosphere may be hydrogen.
GB12396/57A 1956-05-14 1957-04-16 Improvements in metallizing ceramics Expired GB834303A (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
US834303XA 1956-05-14 1956-05-14

Publications (1)

Publication Number Publication Date
GB834303A true GB834303A (en) 1960-05-04

Family

ID=22178275

Family Applications (1)

Application Number Title Priority Date Filing Date
GB12396/57A Expired GB834303A (en) 1956-05-14 1957-04-16 Improvements in metallizing ceramics

Country Status (1)

Country Link
GB (1) GB834303A (en)

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3215555A (en) * 1962-03-29 1965-11-02 Rca Corp Methods and materials for metallizing ceramic or glass bodies
GB2209292A (en) * 1987-08-31 1989-05-10 Gen Electric Application of conductive metallic film to a glass ceramic support surface

Cited By (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3215555A (en) * 1962-03-29 1965-11-02 Rca Corp Methods and materials for metallizing ceramic or glass bodies
GB2209292A (en) * 1987-08-31 1989-05-10 Gen Electric Application of conductive metallic film to a glass ceramic support surface

Similar Documents

Publication Publication Date Title
GB885618A (en) Glass body having a semi-crystalline surface layer and method of making the same
GB834303A (en) Improvements in metallizing ceramics
SE305780B (en)
SE305779B (en)
GB1027116A (en) Improvements in or relating to enamel coatings
GB801279A (en) Improvements in or relating to the manufacture of ceramic materials
GB827638A (en) Preparation of citraconic anhydride
CA522682A (en) Manufacture of thiourea by the thermal conversion of ammonium thiocyanate
CA534546A (en) Treatment of glass surfaces with organosilicon compounds
AU120342B2 (en) Improvements in the production of compositions of or containing organic polysulphides and articles produced therefrom
GB624967A (en) Improved enamelling process
CA524056A (en) Increasing the useful life of porcelain enameled metal articles
FR1216042A (en) Process for the manufacture of briefcases, and cases, cases and similar articles manufactured by this process
CA532480A (en) Condensation of metallic vapors
GB562225A (en) Improvements in the application of vitreous enamels
CA525939A (en) Compositions of matter useful as coating materials
GB873438A (en) Improvements in or relating to production of graphite
GB696209A (en) Improvements in or relating to coatings for glass envelopes and the like
AU228127B2 (en) Siloxane compositions capable of curing at elevated temperature
AU257620B2 (en) Impprovements in or relating to the production of ceramic materials
CA522681A (en) Manufacture of thiourea by the thermal conversion of ammonia thiocyanate
AU245035B2 (en) Improvements in or relating tothe manufacture of asbestos cement articles
AU211942B2 (en) Improvements in or relating tothe heating of glass bodies
AU3027457A (en) Siloxane compositions capable of curing at elevated temperature
FR1150012A (en) Improvements to the heating of glass parts