GB2160470A - The manufacture of lightweight extruded structural profile

Info

Publication number: GB2160470A
Application number: GB08511763A
Authority: GB
Inventors: Michael John Hewitt
Original assignee: Individual
Current assignee: Individual
Priority date: 1984-05-09
Filing date: 1985-05-08
Publication date: 1985-12-24
Also published as: GB8511763D0

Description

SPECIFICATION The manufacture of lightweight extruded structural profile This invention is concerned with the manufacture of lightweight extruded structural profile, particularly but not exclusively profile suitable for use in the building or joinery industries instead of timber, for example in the construction of window and door frames and the like, but also for floor boards, joists, rafters and other building components.

In International patent specification No. WO 81/ 00588 there is described a method of manufacturing window and door frames from cored extruded plastics profiles in which the core material may be of high quality plywood or other suitable material (for example a cement-bonded fibrous material such as cement-bonded chipboard orcement-bonded glass fibres) provided with a cladding of plastics material e. g. polyvinylchloride.

For such frames the core material is required to possess a high degree of dimensional and shape stability and to be of adequate strength to bearthe loads encountered by the frames in use in various weather conditions. Furthermore, as a timber substitute it may be desirable that the core material should possess good screw-holding properties. in U. K. Patent specification No. 2 028 406 B there is disclosed a method of manufacturing an extruded construction strip which is suitable for use in the manufacture of frames for windows and the like and which comprises a tubular section of thermosoftening plastics material (specifical'ly PVC) filled with a matrix of methylmethacrylate with hollow silicate spherules as a filler. As described, the construction strip may incorporate within the matrix a number of filaments (specifically glass rovings) extending lengthwise of the strip for reinforcement purposes. In manufacturing the strip the plastics sheath forming the hollow section is extruded by a first extruding machine and the sheath is filled by extruding thereinto (by a second extruding machine) the plastics matrix of methylmethacrylate incorporating the silicate spherules, being extruded in the cold state into the hollow sheath whilst the latter is still hot. The glass rovings are drawn into the matrix during its extrusion by some means not disclosed.

Curing of the matrixtakes place as the strip is fed through a sizing bush of considerable length. It is apparent that the matrix must comprise a relatively high proportion of resin (methylmethacrylate) enabling the matrix to flow freely under pressure to fill the hollow section.

Furthermore, there is described in International patent specification No. WO 82/03243 a method of making somewhat similar structural profile, in which method: (i) a core comprising an unsaturated polyester resin incorporating a silicate filler and an additional mineral filler, thoroughly mixed and tight ly compacted together, is extruded through a die, (ii) a sheath of a plastics material is extruded around the core, and (iii) the sheathed core is cured by means of heat, so as to effect curing of the core and crosslinking between the core and the sheath. The preferred silicate filler for that process as described therein, is in the form of lightweight hollow microspheres, and an acrylic coating is preferred for the plastics sheath.

According to the process described in specification No. WO 82/03243, a very close packing of the selected fillers could be achieved, resulting in a considerable reduction in the amount of resin required. However, a further reduction in the resin content can be desirable. Furthermore, there could be an advantage in using, at least as the primary filler for the core of such structural profile, a readily-manufacturable material that could reduce the dependence on commercially supplied filles.

There are known, and described for example in European patent specification No. 0 096 489 (A1), rigid inorganic foams of cellular structure comprising one or more layer minerals (hereinafter referred to as layer mineral foams). The term"layer minerals"includes vermiculite, kaolinite, kaolincontaining clays such as ball clays, china clays and fire clays, montmorillonite and sepiolite. Mixtures of layer minerals may be employed in making foams, as also may mixtures of one or more layer minerals with one or more materials other than layer minerals. Where the foam comprises at least a major proportion of clays (hereinafter referred to as a clay foam) it may be sintered to confer improved strength and water-stabiiity.

Such rigid foams have been proposed for various uses, including insulation uses and the fireprotection of substrates. Whilst often produced in the form of extruded board or slab-stock, the foams are also produced in a coarse particulate extruded form known as prills, the prills comprising short extruded strands of the foam materials. Production of such foams can be effected utilising readily available materials and relatively simple machinery.

It is an object of the present invention to provide an improved method of manufacturing lightweight extruded structural profile and according to the invention, in one of its aspects, in such a method there is formed in an extrusion process a core comprising closely compacted and bonded layer mineral foam in a coarse particulate form.

It is to be clearly understood that any reference herein to extrusion (e. g. to an extrusion process, and to the core and profile being extruded) are intended to be read broadly as applicable to a pultrusion process, in which it may be that only pulling forces are applied to move the profile, in formation, through the die.

The coarse particulate layer mineral foam can conveniently be in the form of short extruded strands ("prills"). An additional filler, being of a less coarse particulate form, can be introduced; a preferred such additional filler comprises (primarily if not exclusively) a silicate filler in the form of hollow microspheres.

The densities and strengths of layer mineral foams can vary over a wide range but can be readily controlled. Their use in accordance with the invention, together with careful selection of secondary fillers as appropriate, affords a corresponding versatility in determining the properties of structural profile so manufactured.

In a technique developed for the purpose of enabling loose particulate layer mineral foam (i. e. not pre-mixed with liquid resin) to be introduced into an extrusion die in an efficient manner, applied vacuum is utilised to draw in and packthe filler. Such a vacuum packing technique can enable particularly high packing densities to be achieved where the filler comprises a relatively fine free-ftowing additional filler (such as hollow silicate microspheres), the additional filler being drawn in separately to occupy interstices in previously packed primary filler.

For certain products it might be desirable to arrange to have filler of a higher specific gravity towards the outside of the core than in the middle.

This could be achieved by first packing by vacuum the heavierfiller againstthe walls ofthe die and thereafter packing (also by means of vacuum) lighter filler into the middle.

The manufacturing method can advantageously employ a pultrusion process similarto that described in U. K. patent specification No. 2 143 768 A.

That is to say, glass fibre rovings, or equivalent materials, can be provided trapped between outer surfaces of a body of packed filler and walls of the extrusion die, the rovings being pulled with the packed fillerthrough the die as the profile is extruded. Such use of glass fibre rovings can be of particular benefit in easing the extrusion process, serving to keep down the back pressure in the die with a consequent saving of wear in the apparatus generally and minimising any breakdown of the filler by crushing owing to excessive pressures. The fibres may provide a complete-resin-bonded sheath forthe core. If required, a plastics coating can be applied to the outside of the fibre-clad core, again as referred to in patent specification No. 2 143 768 A, though with suitable resins and pigments this may be unneces- sary to provide finished profile with a fully satisfactory outer surface.

In a preferred method, after the loose filler has been packed within the extrusion die a bonding resin is caused to permeate interstices of the packed filler (and the surrounding sheath of fibres, if present) the resin thereafter being caused or allowed to cure or set. Advantage may be gained from at least the surface of the filler being at an elevated temperature when the bonding resin is introduced.

Preferably, after initial packing the packed filler is progressed through a convergent portion of the extrusion die to achieve further consolidation of the packed filler. Introduction of a bonding resin into the packed filler preferably occurs as the filler is progressed through the convergent portion.

In another of its aspects the invention provides lightweight extruded structural profile comprising a core comprising closely compacted and bonded layer mineral foam in a coarse particulate form.

There now follows a detailed description, to be read with reference to the accompanying drawings, of a method of making lightweight extruded structural profile, which method and which profile illustrate the invention by way of example.

In the accompanying drawings: Figure 1 is a diagrammatic illustration. for a packing section of pultrusion apparatus for producing extruded profile ; Figure 2 is a diagrammatic cross-sectional view of the apparatus on the line ll-ll of Figure 1; and Figure 3 is a schematic illustration of the apparatus as a whole.

In the manufacture of lightweight extruded structural profile comprising a core of closely compacted resin-bonded particulate filler within a sheath of resin-bonded reinforcing fibres, an extrusion die 10 lined with continuously supplied reinforcing fibres in the form of glass rovings 12 is packed from one end with loose particulate filler, from feeding means comprising a conduit 14, as the rovings are continuously drawn through the die (in the direction of the arrow E in Figure 1). Reference can be made to U. K. patent specification No. 2 143 768 Afor a further example of the manufacture of extruded profile comprising a fibre-sheathed core in such a pultrusion process.

A nose portion 16 of the conduit 14 is received within an entry portion 18 of the die 10 and is shaped similarlyto the interior cross-section of the die in that region to define a suitable gap (all around the nose portion) to permit and control introduction of the glass rovings 12 on to the wall surfaces defining the die cavity 20. The glass rovings are fed in, in continuous lengths, from supply drums 21 (Figure 3) and are caused to line the die cavity 20 substantially uniformly over all its wall surfaces.

A generally annular array of airways, comprising fine radial bores 22 in the walls 24 of the die 10, connectthe die cavity 20 with the interiors of low pressure manifolds 26. The manifolds are connected to a vacuum pump 27, whereby air can be drawn from the manifolds to reduce air pressure within the die cavity. By this means, particulate filler supplied to the die cavity from the feeding means through the conduit 14 can be vacuumed into a packing region 28 of the cavity (within the array of airways) and so packed within the sheath of glass rovings 12 in that region. The sheath of rovings itself serves to some extent as a filter preventing filler particles from entering or obstructing the airways 22, but additional filtering means (not shown) can be provided to preventthe passage of fine fiiier particies.

In the construction shown in Figures 1 and 2, a resin feeding tube 30 of resin feeding means extends longitudinally through the conduit 14 and the die cavity 20 substantially to the limit of the packing region 28 (which is to say, it extends to the limit of, or very slightly beyond, that portion of the die 10 provided with the bores 22). Alternatively, and as indicated in Figure 3, resin can be introduced through a feeding tube 31 through the die wall to a feeding channel 33 in the die wall extending in a loop around the die cavity.

At the start of operation, a plug 32 (Figure 1) is positioned to occupy the die cavity 20 immediately beyond the packing region 28. The plug 32 is shaped similarly to the interior cross-section of the die in that region to define a suitable gap to accommodate and hold the glass rovings 12 against the interior die wall surfaces. The plug provides, in effect, a dummy section of core which together with the sheath of rovings around it blocks the die to permit initial vacuum packing of the filler. Once filler has been packed by vacuum into the packing region 28, continuous formation of profile can commence by withdrawal (in the forwards direction) of the plug 32 at normal extrusion speed. The plug is of a compressible foam material which permits it to be drawn through the convergent die. The plug is drawn from the die in a similar manner to that in which the profile will thereafter be drawn through and from the die, which is to say by applying a pulling force in the direction of extrusion to the glass rovings 12 held to the plug/core (in a similar manner to that described in U. K. patent specification No. 2 143 768 A, hereinbefore referred to). Liquid resin is fed through the feeding tube 30 or 31 to permeate the packed filler and the glass rovings 12, the resin thereafter being caused or allowed to cure or set to provide an extruded body of predetermined cross-section of sheathed resin-bonded filler.

More or less immediately following the packing region 28, there is a compressing region 34 within the die 10 in which a convergence of the die walls causes compression and further consolidation of the core as it passes to a final forming region 36 of the die.

With particular reference to Figure 3, the feeding means for supplying particulate fillerto the extrusion die 10 comprises two feed shutes 38 and 40 leading into the feed conduit 14. Each of the shutes is valved to enable measured portions of filler materials to be delivered into the conduit 14 as required.

The vacuum pump 27 in operation draws an air stream through the conduit 14, and heating means 42 within an entry portion of the conduit enables the air to be heated if required. Resin is supped to the resin feeding tube 30 or 31 by means of a supply pump 44. The resin supply can be controlled by monitoring the pressure in the feeding tube. Profile drawing means 46, of a kind well known in the pultrusion art, acts continuously to draw the glass rovings 12 (and the profile core) through the extrusion die 10.

The particulate filler comprises layer mineral foam in a coarse particulate form as a primaryfiller.

Suitable clay foam prills (being short extruded strands) are as promoted in the U. K, by Imperial Chemical Industries PLC as"K4 Inorganic Foam".

The prills may, for example, have a mean extruded length of around 5 mm and a diameter of about 2 mm, and theirspecific gravity can fall (at choice) anywhere within as wide a range as 0.1 to 0.6; partly reflecting that, the proportion (by weight) of filler in the resin-bonded product can vary between, say, 25% and 80% (depending also on the type of resin used).

Whilstthe particulate layer mineral foam alone may constitute the filler, it is usually preferably that a suitable secondary filler be incorporated. This additional filler should be a realtively fine filler, and to permit efficient incorporation by the vacuum packing technique it should be a free-flowing material. A preferred secondary filler comprises (at least as the primary constituent) silicate material in the form of hollow microspheres; such material is widely known as a filler and is available commercially either as recovered from power station waste or as manufactured"glass bubble"filler.

Chopped glass strands may also be introduced in addition to the foam clay and hollow silicate filles.

Employing the vacuum packing technique (hereinbefore described) the primary and secondary fillers are introduced into the extrusion die separately in discrete measured portions. A first of the feed shutes 38 is used to supply the primary filler (the prills), and the second feed shute 40 is used to supply the secondary filler (the microspheres), measured portions of the two fillers being supplied alternately. Accordingly, a portion of primary filler is first released from the first feed shute 38, and the filler is drawn by vacuum into the packing region 28 of the extrusion die. A portion of secondary filler is then released from the second feed shute 40 and drawn into the packing region 28 and into the interstices of the packed portion of primary filler. A next measured portion of primary filler can be released from the first feed shute 38 at a suitable time, bearing in mind that extrusion is taking place continuously, with the glass rovings 12 being drawn continuously through the die 10 by means of the profile drawing means 46.

Further consolidation of the initially vacuum packed primary and secondary fillers occurs as the core material is progressed next through the compressing region 34 of the die 10. With the resin-feeding arrangement as shown in Figure 3, a bonding resin is introduced through the feeding tube 31 shortly before the end of the compressing region of the die.

The resin (whether introduced at the centre of the packed filler as from the tube 30 in Figures 1 and 2, or at the periphery as from the tube 31) permeates the remaining interstices of the packed filler (and the glass fibre rovings 12) by capillary attraction and the effects of increasing pressure as the material moves through the die. A non-foaming phenolic resin system which has been successfully in one available in the U. K. from BP Chemicals under the trade marks Celloband J25/425L resin and Phencat 10 catalyst.

Typically, in use of that resin system, with about 5% of the catayst, the heating means 42 is utilised to result in the foam clay filler having a surface temperature of around 70 C when the resin (i. e. mixed resin and catalyst) is introduced, the extruding die 10 itself being at a temperature ranging from not more than about 90 C at its entry end to around 130 C towards its outlet end.

In the finished profile the proporation of the constituents (by volume) can be within the following ranges: Layer mineral foam (primary filler) : 50%=0% 51 Hollow silicate filler (additional filler) : 28%-32.5% resin: 12%-17.5% The finished sheath thickness may typically be 0.5 mm to 0. 75 mm.

Claims

CLAIMS 1. A method of manufacturing lightweight extruded structural profile in which there is formed in an extrusion process a core comprising closely compacted and bonded layer mineral foam in a coarse particu late form.
2. A method according to claim 1 in which the layer mineral foam is in the form of short extruded strands.
3. A method according to either of claims 1 and 2 in which the filler comprises also relatively fine additional filler.
4. A method according to claim 3 in which the additional filler comprises (primarily if not exclusively) a silicate filler in the form of hollow microspheres.
5. A method according to either of claims 3 and 4 in which by volume the core is constituted by from 50% to 60% layer mineral foam in a coarse particulate form, from 28% to 32.5% additional filler, and from 12% to 17.5% a bonding resin.
6. A method according to any one of claims 1 to 5 in which loose particulate filler is packed into an extrusion die and progressed through the die to become bonded in formation of the core.
7. A method according to claim 6 in which the filler is packed within a sheath of reinforcing fibres within the extrusion die, the sheath and the packed filler together being progressed through the die.
8. A method according to claim 7 in which the sheath and the packed filler together are drawn through the die by means of a pulling force exterted on the fibres in the direction of extrusion.
9. A method according to either of claims 6 and 7 in which the reinforcing fibres are of glass.
10. A method according to claim 6 in which a bonding resin is caused to permeatethe packed filler as the packed filler is progressed through the die, the resin thereafter being caused or allowed to cure or set.
11. A method according to claim 10 in which the filler is packed within a sheath of reinforcing fibres within the extrusion die and the bonding resin is caused to permeate also the sheath of fibres.
12. A method according to either of claims 10 and 11 in which the resin is introduced into the packed filler when the filler has an elevated surface temperature.
13. Lightweight extruded structural profile comprising a core comprising closely compacted and bonded layer mineral foam in a coarse particulate form.
14. Profile according to claim 13 in which the layer mineral foam is in the form of short extruded strands.
15. Profile according to either of claims i 3 and 14 in which the filler comprises also relatively fine additional filler.
16. Profile according to claim 15 in which the additional filler comprises (primarily if not exclusive ly) a silicate filler in the form of hollow microspheres.
17. Profile according to either of claims 15 and 16 in which by volume the core is constituted by from 50% to 60% layer mineral foam in a coarse particu- late form, from 28% to 32.5% additional filler, and from 12% to 17.5% a bonding resin.
18. Profile according to any one of claims 13 to 17 in which the core is encased within a sheath of bonded reinforcing fibres.
19. Profile according to claim 18 in which the fibres are of glass.
20. Lightweight extruded structural profile sub- stantially as hereinbefore described.