GB1404388A - Processes for the production of grain-oriented steel sheet - Google Patents

Processes for the production of grain-oriented steel sheet

Info

Publication number
GB1404388A
GB1404388A GB3271373A GB3271373A GB1404388A GB 1404388 A GB1404388 A GB 1404388A GB 3271373 A GB3271373 A GB 3271373A GB 3271373 A GB3271373 A GB 3271373A GB 1404388 A GB1404388 A GB 1404388A
Authority
GB
United Kingdom
Prior art keywords
separator
july
final
subjected
grain
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
GB3271373A
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Steel Corp
Original Assignee
Nippon Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Corp filed Critical Nippon Steel Corp
Publication of GB1404388A publication Critical patent/GB1404388A/en
Expired legal-status Critical Current

Abstract

1404388 Making sheets NIPPON STEEL CORP 10 July 1973 [10 July 1972] 32713/73 Heading B3A [Also in Division C7] Silicon steel containing acid-soluble Al is hot rolled, continuously annealed at 950- 1200‹ C. and cooled rapidly while aluminium nitride precipitates. It is then subjected to one or two cold rolling stages, the one stage or final stage giving a reduction of 81-95% and subjected to final annealing while coated with a separator incorporating Sb in elemental or compound form. Preferably the antimony content of the separator is 0À1-15% by wt., added as oxide, silicate or hydroxide the separator being based on MgO n or Al 2 O 3 . A preferred steel composition includes C 0À025- 0À085%, Si 2-4, and Al 0À01-0À065% and the final anneal may be at 1200‹ C. for 20 hours, possibly preceded by decarburization.
GB3271373A 1972-07-10 1973-07-10 Processes for the production of grain-oriented steel sheet Expired GB1404388A (en)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
JP6889172A JPS5037129B2 (en) 1972-07-10 1972-07-10

Publications (1)

Publication Number Publication Date
GB1404388A true GB1404388A (en) 1975-08-28

Family

ID=13386715

Family Applications (1)

Application Number Title Priority Date Filing Date
GB3271373A Expired GB1404388A (en) 1972-07-10 1973-07-10 Processes for the production of grain-oriented steel sheet

Country Status (8)

Country Link
JP (1) JPS5037129B2 (en)
BE (1) BE802120A (en)
BR (1) BR7305144D0 (en)
DE (1) DE2334739C3 (en)
FR (1) FR2192180B1 (en)
GB (1) GB1404388A (en)
IT (1) IT991092B (en)
SE (1) SE384228B (en)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2152537A (en) * 1984-01-09 1985-08-07 Nippon Steel Corp Progress for producing grain-oriented electrical steel sheet having both improved magnetic properties and properties of glass film

Families Citing this family (5)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
IT1127263B (en) * 1978-11-28 1986-05-21 Nippon Steel Corp SEPARATION SUBSTANCE TO BE USED IN THE ANNEALING PHASE OF ORIENTED GRAINS OF SILICON STEEL
JPS60177132A (en) * 1984-02-24 1985-09-11 Nippon Steel Corp Manufacturing method of high magnetic flux density unidirectional electrical steel sheet with excellent magnetic properties
US4582547A (en) * 1984-05-07 1986-04-15 Allegheny Ludlum Steel Corporation Method for improving the annealing separator coating on silicon steel and coating therefor
EP0390160B2 (en) † 1989-03-30 2001-02-07 Nippon Steel Corporation Process for producing a grain-oriented electrical steel sheet by means of rapid quench-solidification process
DE69515892T3 (en) † 1994-11-16 2005-10-20 Nippon Steel Corp. METHOD FOR PRODUCING AN ELECTRIC DIRECTIVE PLATE WITH GOOD GLASS STABILITY AND EXCELLENT MAGNETIC PROPERTIES

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB2152537A (en) * 1984-01-09 1985-08-07 Nippon Steel Corp Progress for producing grain-oriented electrical steel sheet having both improved magnetic properties and properties of glass film

Also Published As

Publication number Publication date
JPS4927423A (en) 1974-03-11
FR2192180A1 (en) 1974-02-08
BR7305144D0 (en) 1974-08-15
DE2334739C3 (en) 1975-07-24
DE2334739B2 (en) 1974-12-12
FR2192180B1 (en) 1975-08-22
DE2334739A1 (en) 1974-01-31
JPS5037129B2 (en) 1975-12-01
BE802120A (en) 1973-11-05
IT991092B (en) 1975-07-30
SE384228B (en) 1976-04-26

Similar Documents

Publication Publication Date Title
GB1403271A (en) Process of producing cube-on-edge oriented silicon-iron from cast slabs
US3873381A (en) High permeability cube-on-edge oriented silicon steel and method of making it
GB1063046A (en) Process for producing single-oriented silicon steel sheets having a high magnetic induction
GB1434213A (en) Processing of electrical steels
GB1506029A (en) Method of making a low yield point coldreduced steel sheet by continuous annealing process
GB1481967A (en) Process for the manufacture of steel sheet with oriented grains for magnetic applications and products obtained therefrom
GB878819A (en) Improvements in or relating to oriented steel sheets or the like
GB1404388A (en) Processes for the production of grain-oriented steel sheet
GB1449975A (en) Production of grain-oriented electrical steel sheets
GB1478948A (en) Method of manufacturing a grain orientated steel sheet
GB1466517A (en) Manufacture of dynamo and electrical bands
US3281286A (en) Double-stepped annealing for improvement of super-deep drawing property of steel sheet
GB1386162A (en) Steel alloys and processes for their preparation
GB1197800A (en) Production of Cube-On-Edge Oriented Silicon-Iron.
JPS54107415A (en) Cold rolled steel plate with baking hardenability for deep drawing
GB1322135A (en) Method of producing a minimum-ridging type
GB1366353A (en) Process for the production of thin aluminium strip of sheet
JPS6462417A (en) Production of grain oriented electrical steel sheet having metallic luster
GB1341503A (en)
GB1464232A (en) Method of making cold-reduced al-killed steel strip for press- forming by continuous casting and continuous annealing process
GB1145408A (en) Process for annealing iron silicon magnetic alloys
GB1057124A (en) Method for producing a cold rolled rimmed steel sheet or strip
GB1142552A (en) Grain-oriented iron and steel and method of making same
GB2046785A (en) Manufacture of sheet or foil silicon steel having a Goss texture
GB911660A (en) Double oriented iron-silicon magnetic sheets

Legal Events

Date Code Title Description
PS Patent sealed
PE20 Patent expired after termination of 20 years

Effective date: 19930709