GB1142334A - Aqueous phenoplast-aminoplast resin binder for mineral fibers - Google Patents
Aqueous phenoplast-aminoplast resin binder for mineral fibersInfo
- Publication number
- GB1142334A GB1142334A GB18538/66A GB1853866A GB1142334A GB 1142334 A GB1142334 A GB 1142334A GB 18538/66 A GB18538/66 A GB 18538/66A GB 1853866 A GB1853866 A GB 1853866A GB 1142334 A GB1142334 A GB 1142334A
- Authority
- GB
- United Kingdom
- Prior art keywords
- parts
- aqueous
- phenoplast
- formaldehyde
- binder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
1,142,334. Aqueous phenoplast-aminoplast composition. WEST VIRGINIA PULP & PAPER CO. 27 April, 1966 [10 May, 1965], No. 18538/66. Heading C3R. [Also in Division D1] A binder for mineral fibres comprises an aqueous solution of (a) 20 to 60 parts by weight of a thermosetting resin consisting of (i) 10 to 50 wt. per cent dicyandiamide-formaldehyde and (ii) 50 to 90% phenol-formaldehyde; (b) 16 to 50 parts of the free acid form of alkali lignin and (c) 12 to 50 parts of urea, (a), (b) and (c) totalling 100 parts and (c) not exceeding 5 times (a) (i). Excess formaldehyde in the composition may be neutralized with ammonia to form hexamine and additional hexamine may be added. Antioxidants such as phosphates, borates and antimonates may be added to enhance fire resistance. The mineral fibres which may be bonded into mats with the resin may be constituted by various combinations of silica, magnesia, alumina, soda and lime. The binder may be used as an aqueous solution of pH from 7 to 10.
Applications Claiming Priority (1)
| Application Number | Priority Date | Filing Date | Title |
|---|---|---|---|
| US45467765A | 1965-05-10 | 1965-05-10 |
Publications (1)
| Publication Number | Publication Date |
|---|---|
| GB1142334A true GB1142334A (en) | 1969-02-05 |
Family
ID=23805617
Family Applications (1)
| Application Number | Title | Priority Date | Filing Date |
|---|---|---|---|
| GB18538/66A Expired GB1142334A (en) | 1965-05-10 | 1966-04-27 | Aqueous phenoplast-aminoplast resin binder for mineral fibers |
Country Status (3)
| Country | Link |
|---|---|
| DK (1) | DK117132B (en) |
| GB (1) | GB1142334A (en) |
| SE (1) | SE308800B (en) |
Cited By (3)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| FR2495628A1 (en) * | 1980-12-04 | 1982-06-11 | Johns Manville | FIBROUS INSULATION AND PROCESS FOR PRODUCING THE SAME WITH A FLAME FREE COMBUSTION TANK |
| WO2002026653A1 (en) * | 2000-09-27 | 2002-04-04 | Mahieuxe, Bruno | Mineral wool with enhanced durability |
| CN114656605A (en) * | 2022-03-23 | 2022-06-24 | 吉林大学 | Nano SiO2Preparation method of/LPF composite material |
-
1966
- 1966-04-27 GB GB18538/66A patent/GB1142334A/en not_active Expired
- 1966-05-09 DK DK237166A patent/DK117132B/en unknown
- 1966-05-10 SE SE641166A patent/SE308800B/xx unknown
Cited By (4)
| Publication number | Priority date | Publication date | Assignee | Title |
|---|---|---|---|---|
| FR2495628A1 (en) * | 1980-12-04 | 1982-06-11 | Johns Manville | FIBROUS INSULATION AND PROCESS FOR PRODUCING THE SAME WITH A FLAME FREE COMBUSTION TANK |
| WO2002026653A1 (en) * | 2000-09-27 | 2002-04-04 | Mahieuxe, Bruno | Mineral wool with enhanced durability |
| CN114656605A (en) * | 2022-03-23 | 2022-06-24 | 吉林大学 | Nano SiO2Preparation method of/LPF composite material |
| CN114656605B (en) * | 2022-03-23 | 2024-04-12 | 吉林大学 | Nano SiO 2 Preparation method of LPF composite material |
Also Published As
| Publication number | Publication date |
|---|---|
| DK117132B (en) | 1970-03-16 |
| SE308800B (en) | 1969-02-24 |
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| PL294477A1 (en) | Method of obtaining phenolic binder, phenolic binder as such and method of making products consisting of mineral fibres | |
| GB963462A (en) | Resin binder | |
| GB1226731A (en) | ||
| MX169174B (en) | PRODUCTION OF PARTICULATE LINKED MATERIAL ARTICLES AND BINDING COMPOSITIONS FOR USE THEREOF | |
| DK533379A (en) | PAPER MANUFACTURING | |
| GB1439027A (en) | Manufacture of glass wool | |
| AR247241A1 (en) | Binder and sizing based on it for inorganic fibres | |
| GB1142334A (en) | Aqueous phenoplast-aminoplast resin binder for mineral fibers | |
| BG46750A3 (en) | FORMALDEHYDE COMPOSITION | |
| GB1482939A (en) | Method of the cold adhesion of wood glues | |
| GB1293744A (en) | Fibreglass resin lignin coating | |
| GB1333470A (en) | Binders for glass fibre insulation | |
| ES8606832A1 (en) | PROCEDURE FOR THE MANUFACTURE OF GLASS AND MINERAL FIBER PRODUCTS AGGLUTINATED WITH PHENOLIC RESINS. | |
| GB1166380A (en) | Refractory Insulating Compositions. | |
| GB1328493A (en) | Refractory insulating compositions | |
| GB905393A (en) | Modified phenol formaldehyde resinous binder for vitreous fibres | |
| GB1402120A (en) | Flameproof materials | |
| GB1286661A (en) | Guanamine/formaldehyde resins | |
| GB1157397A (en) | Phenolic Resin Composition and Paper Impregnated Therewith | |
| GB1308934A (en) | Alkylated amine copolymers | |
| ATE61258T1 (en) | BINDER MIXTURE FOR CONSOLIDATION. | |
| GB1160864A (en) | Refractory Heat-Insulating Compositions | |
| GB986711A (en) | Improved lignin-extended phenolic resins | |
| GB1312383A (en) | Pressboard made from fibrous material and a binding substance | |
| BG48695A3 (en) | METHOD OF OBTAINING UREA-FORMALDEHYDE GLUE |