DE9006848U1 - Isolierende Wand für Kühlgeräte - Google Patents
Isolierende Wand für KühlgeräteInfo
- Publication number
- DE9006848U1 DE9006848U1 DE9006848U DE9006848U DE9006848U1 DE 9006848 U1 DE9006848 U1 DE 9006848U1 DE 9006848 U DE9006848 U DE 9006848U DE 9006848 U DE9006848 U DE 9006848U DE 9006848 U1 DE9006848 U1 DE 9006848U1
- Authority
- DE
- Germany
- Prior art keywords
- insulating wall
- refrigerators
- polystyrene
- abs
- plastic plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
111 Il
Die Neuerung bezieht sich auf eine isolierende Wand für Kühlgeräte, bei der zwischen einem Außenblech und
einer tiefgezogenen Kunststoffplatte aus Polystyrol oder ABS ein Polyurethan eingeschäumt ist·..
Derzeit wird bei derartigen Wänden sin Flisc rkohlen-
r wasserstoff (FCKW), wie z.B. Freon, als r treibmittel
tür den Polyurethan-Schaum verendet. Aus Gründen des
.: Umweltschutzes sollte die Verwendung von FCKW
J möglichst bald ein festgut werd<*-i, da hieraus der
: bekannte T-; ibhauseff^t resultiert. Ab 1995 wird die
Verwendung von FCKW für die He?-»cellurkg von PoIy-
urethan-Schaum nicht mehr ^.il^ssig sein. Beim Abgehen
von der Verwendung von Freon als Treibmittel ergibt
M sich das Problem, daß ein Polyurethan-Schaum mit Luft
als Zellgas einen &lgr;-Wert aufweist, welcher je nach
Luftfeuchtigkeit zwischen 28 und 33 Watt * 10~3/mK
liegt, während der entsprechende Wert der Wärmeleitzahl &lgr; für einen Polyurethan-Schaum mit Freon RIl
bei 18 liegt. Eine Lösung dieses Problems ergibt sich durch die Verwendung von Wasser als Treibmittel, da
diese die Entstehung von CO2 als Zellgas zur Folge
hat. Der &Lgr; -Wert für den entstehenden Polyurethan-Schaum beträgt 24.
Bei der Prüfung von Polyurethan-Schäumen mit CO2 als
Zellgas hat sich eine allmähliche Verschlechterung des Wärmedämmverhaltens gezeigt, welche darauf
zurückzuführen ist, daß CO2 nach außen diffundiert und durch Luft ersetzt wird. Um Schäume mit CO2 als
Zellgas zur Herstellung isolierender Wände von Kühlgeräten verwenden zu können, muß ein Weg gefunden
werden, die den Schaum begrenzende tiefgezogene Kunststoffplatte für CO2 undurchlässig zu machen.
34012 - 11/si
Wenn es an sich bekannt ist, daß Copolymere von Ethylenvinylalkohol sich als Sperrschichten gut
eignen, war ihre Verwendung im gegenständlichen Zusammenhang doch nicht naheliegend, da sich die
Koextrusion dieser Kunststoffe mit Polystyrol oder
ABS als schwierig erwies. Die Schwierigkeiten konnten schließlic- durch sorgfältige Kontrolle des Polyethylen-Anteils
im Copolymer überwunden werden.
Neuerungsgemäß ist somit bei einer isolierenden Wand der eingangs charakterisierten Art vorgesehen, daß
das Zellgas des PU-Schaums CC2 ist und daß die Kunststoffplatte
im Inneren eine 0,03 - 0,6 mm dicke Sperrschicht aus einem Copolymer von Polyethylen und
Vinylalkohl(EVOH) mit einem Polyethylenanteil von 32 - 44 mol% aufweist.
Eine Verbindung der EVOH-Schicht mit den benachbarten
Polymeren, Polystyrol, ABS o.a. ist vorzugsweise durch Verwendung eines extrudierbaren,
vinylacetathältigen Haftvermittlers möglich, wodurch die Kunststoffplatte letztendiich aus 5 oder 6
Polymerschichten besteht.
Weitere Einzelheiten der Neuerung werden anschließend anhand der Zeichnung erläutert, welche einen (nicht
maßstabsgetreuen) Querschnitt durch eine neuerungsgemäße Wand für Kühlgeräte zeigt.
Die dargestellte Isolierwand besteht im wesentlichen aus einer Schicht von Polyurethan-Schaum, welche
zwischen einer Kunststoffplatte 1 und dem Außenblech 7 des Gerätes eingeschäumt ist. Das Zellgas des
Polyurethan-Schaums ist CO2, welches als chemische P.eaktion mit Isocyanat, bei Verwendung von Wasser als
Treibmittel zur Herstellung des Polyurethan-Schaums, entsteht. Ees befindet sich in den Zellen 6, deren
Zellwände 5 von Polyurethan gebildet sind. Zweck der Platte 1 ist es unter anderem, den Austausch des
Kohlendioxids in den Zellen 6 gegen Luft zu verhindern. Zu diesem Zweck ist zwischen zwei
Polystyrol- oder ABS-Schichten 4,4' eine 0,03 - 0,6
&Igr;&Ggr;&igr;&Igr;&Ggr;&iacgr;, VOZ-ZUySWcISS etwa 0,3 &idigr;&Ggr;&udiagr;&idigr;&igr; dicke 3p£r"I"3CiilC««t 2 &udiagr;'&udiagr;
Ethylenvinylalkohol angeordnet. Dieses ist ein kristallines Polymer, desr.en Molekülstruktur durch
die folgende Formel charakterisiert ist:
OH
Die Koextrusion mit den Teilplatten 4,4' aus Polystyrol oder ABS hat zu guten Ergebnissen geführt,
wenn der Polyethylenanteil zwischen 32 und 44 mol% liegt und der Schmelzindex (MFI) bei 210'C Werte
zwischen 2 und 8 aufweist (die Angabe bezieht sich ~i«f ** -i *·»-* V*«a*4 -»«&kgr;-*«- «*_««% in U -i «%·*4- &lgr;»» im/1 *-? ■! &agr; OaI aef imn
&zgr;&Lgr;\&Lgr;&Lgr;. CXIl^: I'lCIVUaUI=!. VUJl &Agr; \J l-|±£lUI«Ctl UIlM UA\>
WVJ.UWMII1J
mit dem Gewicht einer Masse von 2160 g). Die Qualität der Platte 1 konnte durch die Verwendung ganz dünner
Schichten 3,3" vinylacetathältiger Haftvermittler verbessert werden, deren MFI, gemessen bei 190'C,
zwischen 3 und 4 lag.
Claims (2)
1. Isolierende Wand für Kühlgeräte, bei der zwischen
einem Außenblech und einer tiefgezogenen Kunststoffplatte
aus Polystyrol oder ABS ein Polyurethan eingescnäumt
ist, dadurch gekennzeichnet, daß das Zellgas des PU-Schaums CO^ ist und daß die Kunststoffplatte (1) im
Inneren eine 0,03 - 0,6 mm dicke Sperrschicht (2) aus
einem Copolymer von Polyethylen und Vinylalkohol (EVOH) mit einem Polyethylenanteil von 32 - 44 mol% aufweist.
2. Isolieionde Wand nach Anspruch 1, dadurch gekennzeichnet,
daß die EVOH-Schicht mit dem benachbarten Polystyrol oder ABS über einen vinylacetathaltigen
Haftvermittler verbunden ist.