Verfahren zur Herstellung von Verbundblöcken Es ist bekannt, Verbundblöcke herzustellen, indem in der Kokille ein oder mehrere in festem Zustand befindliche Stahlblöcke mit flüssigem Stahl anderer Festigkeit umgossen und mit Gas behandelt werden, worauf die so erhaltenen Rohblöcke durch Weiterbearbeitung in die gewünschte endgültige Form übergeführt werden.Method of making composite blocks It is known to use composite blocks to produce by one or more in the solid state in the mold Steel blocks cast around with liquid steel of a different strength and treated with gas whereupon the rough blocks obtained in this way are converted into the desired final form to be transferred.

Die dabei Verwendung findenden Gase dienen bisher jedoch ausschließlich dem Zweck, das Umgießen des flüssigen Stahles um die festen Stahlblöcke im Beisein einer Schutzschicht erfolgen zu lassen, um eine. Oxydation der Oberfläche der Stahlblöcke zu verhindern, weshalb stets reduzierende oder neutrale Grase gewählt werden.The gases used for this purpose have so far only been used the purpose of pouring the liquid steel around the solid steel blocks in the presence a protective layer to allow a. Oxidation of the surface of the steel blocks to prevent, which is why reducing or neutral grasses are always chosen.

Demgegenüber besteht der Zweck der Erfindung vor allem darin, bei der beschriebenen Art der Herstellung von Verbundblöcken eine innige Verschweißung der zur Verwendung kommenden Stahlsorten zu erzielen, die für das fertige Erzeugnis umbedingt erforderlich ist, bisher aber häufig nicht möglich war.In contrast, the purpose of the invention is above all to the type of production of composite blocks described, an intimate weld the steel grades used to achieve that for the finished product is absolutely necessary, but was often not possible up to now.

Erfindungsgemäß wird das mit Sicherheit dadurch erreicht, daß als Gas Preßluft oder mit Sauerstoff angereichertes Gas Verwendung findet, das dicht über dem steigenden Flüssigkeitsspiegel gegen die mit flüssigem Metall zu umgießenden, hocherhitzten Stahlblöcke geleitet wird. Der Zweck dieser Maßnahme ist, die Temperatur des eingesetzten Blockes zu steigern und außerdem die an ihm sitzenden Unreinigkeiten, Oxyde u. dgl., durch den Preßluft- oder Gasstrom fortzublasen, so daß eine innige Verbindung der beiden Stahlsorten möglich ist. Die Oxyde und Unreinigkeiten werden von dem flüssigen Stahl fortgeschwemmt. Um das Fortschwemtnen dieser Stoffe mit größerer Sicherheit zu bewirken, ist es vorteilhaft, den flüssigen Werkstoff von unten her in die Kokille einzuführen, also durch steigenden Guß. Das Reinigen und Temperaturerhöhen der Oberfläche des eingesetzten Blockes geschieht deshalb dicht über dem Flüssigkeitsspiegel des hinzuzugießenden Stahles, damit keine neue Oxydation oder nicht wieder eine Temperaturabnahme des Blockes stattfindet. Zusammen mit dem Preßluft- oder Gasstrom können erfindungsgemäß noch solche Stoffe gleichzeitig auf den hocherhitzten Block geschleudert werden, die entweder die Temperaturerhöhung oder die Reinigung der Oberfläche unterstützen oder die beides bewirken. Naturgemäß sind solche Stoffe zu bevorzugen, die zusammen mit den abgeblasenen Oxyden eine leichtflüssige, auf dem steigenden Flüssigkeitsspiegel schwimmende Schlacke erzeugen.According to the invention this is achieved with certainty that as Gas compressed air or oxygen-enriched gas is used, which is tight above the rising liquid level against those to be poured with liquid metal, highly heated steel blocks is conducted. The purpose of this measure is the temperature of the inserted block and also to increase the impurities sitting on it, Oxides and the like, blown away by the compressed air or gas stream, so that an intimate Connection of the two types of steel is possible. The oxides and impurities will be swept away by the molten steel. About the floating away of these substances To bring about greater security, it is advantageous to use the liquid material from to be introduced into the mold from below, that is, by increasing casting. The cleaning and Raising the temperature of the surface of the block used therefore takes place tightly above the liquid level of the steel to be poured in, so that no new oxidation occurs or the temperature of the block does not decrease again. Together with the According to the invention, compressed air or gas stream can also simultaneously apply such substances the highly heated block will be thrown, which will either increase the temperature or support the cleaning of the surface or do both. Naturally those substances are to be preferred, which together with the blown oxides a generate light slag floating on the rising liquid level.

Die Zuführung des Gases bzw. der Zusatzstoffe erfolgt .erfindungsgemäß mittels eines auf und ab beweglichen, stets unmittelbar über dem Metallbade befindlichen Ringes, der sich der Form des Stahlblockes anpaßt.The supply of the gas or the additives takes place according to the invention by means of a movable up and down, always located directly above the metal bath Ring that adapts to the shape of the steel block.

Auf dem Flüssigkeitsspiegel schwimmende Ringe sind beider Herstellung von Verbundblöcken zwar bekannt, doch dienen sie ausschließlich dazu, die freie Oberfläche des Bades vor Oxydation zu schützen.Rings floating on the liquid level are both manufactured known from composite blocks, but they are used exclusively to, to protect the free surface of the bath from oxidation.

Bei der Erfindung besitzt der Ring an :der dem Block zugewandten Seite kleine Öffnungen für den Austritt des in den Ring durch ein Rohr o. dgl. eingeführten Gases.In the invention, the ring has: the side facing the block small openings for the exit of the one introduced into the ring through a tube or the like Gas.

Das Wesen des neuen Verfahrens ist auf der Zeichnung beispielsweise verdeutlicht. -Es zeigt Abb. i einen Längsschnitt durch die Kokille mit eingesetztem Block und Abb. 2 die Draufsicht. In die Kokille a ist der hocherhitzte Stahlblock b eingesetzt. (Anzustreben isst es, den Block möglichst schweißwarm oder wenigstens hellgelb glühend einzusetzen.) Unter Vermittlung des Trichters c wird der flüssige Zusatzstahl von unten in die Kokille eingeführt. Dicht über dem Flüssigkeitsspiegel d und mit ihm steigend befindet sich -der Ring e, der an der dem Block b zugewandten Seite mit kleinen öffnungen f für den Austritt der in den Ring durch Schlauch g und Rohr h eingeführten Preßluft versehen ist. Der Ring $chtniegt sich dicht der Form des Blockes b an, damit der ganze Umfang des Blockes und mit großer Kraft von der Preßluft bestrichen werden kann.The essence of the new process is on the drawing for example made clear. -It shows Fig. I a longitudinal section through the mold with inserted Block and Fig. 2 the top view. The highly heated steel block is in the mold a b used. (The aim is to eat the block as warm as possible, or at least light yellow glowing.) With the intermediary of the funnel c, the liquid Additional steel introduced into the mold from below. Just above the liquid level d and rising with it is the ring e on the one facing the block b Side with small openings f for the exit into the ring through hose g and pipe h introduced compressed air is provided. The ring fits tightly to the Shape of the block b at, so that the whole circumference of the block and with great force of the compressed air can be coated.

Claims

PATENT CLAIMS: i. Process for the production of composite blocks, in which one or more solid steel blocks with liquid Steel cast around and treated with gas, characterized in that as a gas Bounce air or oxygen-enriched gas is used, which is just above. the rising "liquid level against those to be poured with liquid metal highly heated steel blocks is conducted.

2. The method according to claim i, characterized in that that at the same time with the baffle air or gas stream such substances are supplied that allow either the cleaning effect or the temperature or both to be increased.

3. embodiment of the method according to claim i or 2, characterized by- the use of an upward and downward moving ring that follows the shape of the or or blocks inserted into the mold and the supply of the treatment agent permitted over the entire circumference of the block or blocks.