DE3302368A1 - Heat- and sound-insulating lightweight building block and process for the manufacture thereof

Info

Publication number: DE3302368A1
Application number: DE19833302368
Authority: DE
Inventors: Ferdinand 3062 Bückeburg Preisler
Original assignee: Individual
Current assignee: Individual
Priority date: 1983-01-25
Filing date: 1983-01-25
Publication date: 1984-07-26

Abstract

Lightweight building blocks manufactured from a bulk-porous or porous lightweight aggregate, ground clay and water have a particularly homogeneous structure and show improved compressive strengths.

Description

Wärme- und schalldämmender Leichtbaustein und VerfahrenHeat and sound insulating lightweight building block and process

zu seiner Herstellung. for its manufacture.

Beschreibung Die Erfindung betrifft einen wärme- und schalldämmende^. Description The invention relates to a heat and sound insulating ^.

Leichtbaustein, der im wesentlichen aus Ton und einem haufwerksporigen oder porigen Leichtzuschlag besteht.Lightweight building block, which is essentially made of clay and a pore-like structure or porous lightweight aggregate.

Gebrannte Mauerziegel aus Naturton sind seit langem bekannt. Es sind auch Leichtbausteine bekannt, die aus einem hydraulischen Bindemittel und einem haufwerksporigen Leichtzuschlag hergestellt worden sind. Solche hydraulisch gebundenen Leichtbaustelle, die mit Dampf oder durch Luft getrocknet sein können, schwinden im Verlauf ihrer ca. drei Monate langen Trocknungszeit und weisen sogar danach noch eine häufig zu Rißbildung füt;-rende Restschwindung auf. Leichtbausteine aus Gasbeton bleiben darüber hinaus durch die enthaltenen Kapillaren saugfähig.Fired bricks made of natural clay have been known for a long time. There are also known lightweight building blocks, which consist of a hydraulic binder and a Porous lightweight aggregate have been produced. Such hydraulically bound Lightweight construction sites that can be dried with steam or air are disappearing in the course of their approx. three months long drying time and even afterwards a residual shrinkage that often leads to cracking. Lightweight building blocks made of aerated concrete In addition, they remain absorbent thanks to the capillaries they contain.

In früheren Patentanmeldungen (DE-OS 27 32 581 und unveröffentlichte Deutsche Patentanmeldung P 32 23 805.3-25) des Anmelders wurden verschiedene Anteile an haufwerksporigem oder porigem Leichtzuschlag =:escMagen.Zur'Hersteilung dieser in den genannten älteren Anmeldungen beschriebenen Leichtbausteine wurde als Ton Naturton vorgeschlagen.In previous patent applications (DE-OS 27 32 581 and unpublished German patent application P 32 23 805.3-25) of the applicant were different shares on pore or porous lightweight aggregate =: escMagen.To the production of this Light building blocks described in the earlier applications mentioned was called clay Natural tone suggested.

Es stellte sich heraus, daß in manchen Fällen, insbesondere wenn zur Herstellung sehr leichter Leichtbausteine eine groRe Menge von - Leichtzuschlag mit einer kleinen Menge von plastischem Naturton vermischt werden, die Mischung zwischen Ton und Leichtbauzsuchlag nur schwer homogen herzustellen ist.It turned out that in some cases, especially when for Manufacture of very light lightweight building blocks a large amount of - lightweight aggregate mixed with a small amount of plastic natural clay, the mixture between clay and lightweight construction is difficult to produce homogeneously.

Dies bedeutet, daß der Leichtbauzuschlag, z.B. Blähton, lh manchen Fällen nicht homogen von Naturton umhüllt ist.This means that the lightweight construction surcharge, e.g. expanded clay, lh some Cases is not homogeneously encased in natural clay.

Dies kann so weit führen, daß sich zwischen zwei Blähtonkügelchen nur eine unzureichende Menge von plastischem Ton befindet, so daß die Blähtonkörner nicht optimal miteinander verbunden sind. Dadurch wird der erhaltene Leichtbaustein geschwächt, was sich in einer verringerten Druckfestigkeit auswirkt. Daher muß immer eine relativ große Menge an Naturton mit dem Leicht zuschlag ververmischt werden, um eine zufriedenstellende Festigkeit zu erzielen.This can go so far that there is between two expanded clay pellets only an insufficient amount of plastic clay is located, so that the expanded clay grains are not optimally connected to each other. This becomes the lightweight building block obtained weakened, which results in a reduced compressive strength. Therefore always must a relatively large amount of natural clay is mixed with the light aggregate, to achieve satisfactory strength.

Es stellte sich nun heraus, daß die zum Binden der Körner des Leichtzuschlags benötigte Menge an Ton verringert werden kann, ohne daß sich die Körner direkt berühren und damit die Festigkeit des Leichtbausteins geringer wird, wenn man statt Naturton Tonmehl einsetzt, das mit Wasser zu einer plastischen Masse vermischt wird.It now turned out that the one used to bind the grains of the lightweight aggregate The required amount of clay can be reduced without the grains directly touching one another and thus the strength of the lightweight building block is lower if you use natural clay instead of Clay powder is used, which is mixed with water to form a plastic mass.

Gegenstand der Erfindung ist daher ein Leichtbaustein der eingangs genannten Gattung, der erhältlich ist durch Vermischen von Tonmehl mit dem haufwerksporigen oder porigen Leichtzuschlag und Wasser und anschließendes Verformen, Verdichten, Vortrocknen und Brennen auf an sich bekannter Weise. Beim erfindungsgemäßen Leichtbaustein ist bei gleicher Festigkeit der Tonanteil weiter verringert, so daß der Leichtbaustein noch leichter ist als die bekannten Leichtbausteine, zu deren Herstellung neben de Leichtzuschlag plastischer Naturton verwendet wurde.The invention therefore relates to a lightweight block of the initially named genus, which can be obtained by mixing powdered clay with the pore-like structure or porous lightweight aggregate and water and subsequent shaping, compression, Pre-drying and firing in a known manner. With the lightweight building block according to the invention the clay content is further reduced with the same strength, so that the lightweight building block is even lighter than the well-known lightweight building blocks, in addition to their manufacture de lightweight aggregate plastic natural clay was used.

Gegenstand der Erfindung ist weiterhin ein Verfahren zur Herstellung eines Ton und einen haufwerksorigen oder porigen Leichtzuschlag enthaltenden wärme- und schalldämmenden Leichtbausteins, wobei man Ton mit dem Leichtzuschlag im gewünschten Mischungsverhältnis vermischt und die so erhaltene Mischung verformt, verdichtet, vortrocket und brennt, das dadurch gekennzeichnet ist, daß man als TDn Tonmehl einsetzt, dem man vor dem Vermischen oder während des Vermischens Wasser zusetzt.The invention also relates to a method for production a clay and a haufwerkorigen or porous lightweight aggregate containing heat and sound-absorbing lightweight building block, whereby you can tone with the lightweight aggregate in the desired Mixing ratio mixed and the resulting mixture deformed, compacted, pre-drying and burning, which is characterized in that as TDn Clay powder is used by adding water before or during mixing.

Vorzugsweise wird der vorgeschlagene Leicht baustein aus 70 bis 90 Gew.-% Leichtzuschlag und 30 bis 10 Gew.-° Tonmehl hergestellt. Dabei wird als Leichtzuschlag BlEhton bevorzugt.Preferably, the proposed lightweight building block from 70 to 90 % By weight lightweight aggregate and 30 to 10% by weight clay powder produced. It is used as a light surcharge Bleached clay preferred.

In einer besonders bevorzugten Ausführungsform enthält die Mischung aus Leichtzuschlag und Ton 75 bis 85 Gew.-°,e Blähton als Leichtzuschlag und 25 bis 15 Gew.-% Tonmehl.In a particularly preferred embodiment, the mixture contains from lightweight aggregate and clay 75 to 85% by weight, e expanded clay as lightweight aggregate and 25 up to 15% by weight clay powder.

Als Tonmehl verwendet man dabei getrockneten pulverisierten Ton, wie er z.B. für die Herstellung von Blähton verwendet wird. Dieses Tonmehl stellt bisher ein Produkt dar, das z.B. zum Ausbessern von schadhaften Feuerfest-Auskleidungen und für Tonengaben, Tonglasuren und bedingt für das Töpferhandwerk verwendet wird. Damit dieses Tonmehl nach dem Anrühren mit Wasser die Körner des Leichtzuschlags verbinden kann, muß es wenigstens latent hydraulisch sein. Es darf also nicht bei so hohen Temperaturen gebrannt sein, daß die hydraulischen Eigenschaften permanent verlorengegangen sind, d.h. es darf -ht totgebrannt sein.The powdered clay used is dried powdered clay, such as it is used e.g. for the production of expanded clay. This clay powder represents so far a product that can be used, for example, to repair damaged refractory linings and is used for clay gifts, clay glazes and conditionally for the pottery. So that this clay flour, after being mixed with water, becomes the grains of the lightweight aggregate can connect, it must be at least latently hydraulic. So it mustn't be be burned at such high temperatures that the hydraulic properties are permanent have been lost, i.e. it must not be burned to death.

Als Leichtzuschlag ist z.B. Blähton, Naturbims, Hüttenbis, Blähschiefer, Blähperlit, Schaumlava, Schaumton, Schaunglas, geblähtes Granulat usw. oder Gemische hieraus geeignet; Blähton wird bevorzugt behandelt.Expanded clay, natural pumice, Hüttenbis, expanded slate, Expanded perlite, foam lava, foam clay, foam glass, expanded granules, etc. or mixtures suitable from this; Expanded clay is given preferential treatment.

Entsprechend der Herstellung von Leichtbausteinen aus Zement und Leichtzuschlag werden beim erfindungsgemäßen Verfahren der Vorrat an Tonmehl und an Leichtzuschlag getrennt, z.B. in separaten Silos, gelagert. Zur Herstellung des Leichtbausteins werden aus diesen Silos abgemessene Mengen der Bestandteile auf ein gemeinsames Förderband abgegeben, das die Ausgangsstoffe zu einem Mischwerk führt. In dem Mischwerk werden sie unter Zugabe von Wasser gründlich miteinander vermischt, so daß der Leichtzuschlag vollständig von dem pastösen Tonmehlschlicker umhüllt ist. Es ist auch möglich, das benotig-Wasser dem Tonmehl bereits auf dem Förderband, das zum Mischwerk hinführt, zuzusetzen.Corresponding to the production of lightweight building blocks from cement and lightweight aggregate in the process according to the invention, the supply of powdered clay and light aggregate stored separately, e.g. in separate silos. For the production of the lightweight building block From these silos measured quantities of the constituents are transferred to a common one Conveyor belt delivered, which leads the raw materials to a mixer. In the mixer they will be adding thoroughly mixed with each other by water, so that the lightweight aggregate is completely enveloped by the pasty clay flour slip is. It is also possible to add the necessary water to the clay powder already on the conveyor belt, that leads to the mixer.

Durch die erfindungsgemäße Verwendung von Tonmehl anstelle von Naturton, durch die sich eine innige Vermischung von Ton und Leichtzuschlag selbst bei geringen Zusätzen von Ton erreichen läßt, wird eine vollständige Oberflächenverleimung der Körner des Leichtzuschlags erreicht. Dadurch werden die Leichtzuschlagkörner fest miteinander verbunden, ohne sich vollständig zu berühren.The inventive use of clay powder instead of natural clay, through which there is an intimate mixture of clay and light aggregate even with small amounts Additions of clay can achieve a complete surface gluing of the Grains of light aggregate reached. This makes the lightweight aggregate firm connected to each other without completely touching each other.

Dies führt zu einer weiteren Verringerung der Rohdichte des Leichtbausteins bei genügender Festigkeit.This leads to a further reduction in the bulk density of the lightweight building block with sufficient strength.

Wenn bei der Herstellung der neuen Leichtbausteine Tonmehl und Leichtzuschlag mit Wasser im Mischwerk vermischt worden sind, wird auf an sich bekannter Weise die Mischung zu Leichtbausteinen verformt, und unter Rütteln durch einen Vibrator verdichtet. Anschließend werden die Rohlinge vorgetrocknet, verdichtet und gebrannt.If powdered clay and lightweight aggregate are used in the manufacture of the new lightweight building blocks have been mixed with water in the mixer, is in a known manner the mixture is deformed into lightweight building blocks, and while being shaken by a vibrator condensed. The blanks are then pre-dried, compressed and fired.

Der erfindungsgemäße Leichtbaustein weist ausreichende Druckfestigkeit neben vorzüglicher Wärmedämmeigenschaften auf. Insbesondere bei Verwendung von Blähton als haufwerksporigem Leichtzuschlag werden die vorteilhaften Eigenschaften des Blähtons selbst bei geringen Mengen gegenüber Tonmehl auf den erfindungsgemäßen Leichtbaustein übertragen. Da Blähton keine offenen Kapillaren enthält, ist seine Frostsicherheit vorzüglich. Selbst unter extremen Bedingungen weist Blähton eine äußerst schnelle Feuchteabgabe auf. Außerdem ergibt Blähton eine gute Schalldämmung und garantiert wegen segner niedrigen Kornrohdichte eine optimale Wärmedämmung. Insgesamt geben die neuen Leichtbausteine hervorragende Prüfwerte.The lightweight building block according to the invention has sufficient compressive strength in addition to excellent thermal insulation properties. Especially when using expanded clay The advantageous properties of expanded clay are used as a lightweight aggregate with pores even with small amounts compared to powdered clay on the lightweight building block according to the invention transfer. Since expanded clay does not contain open capillaries, it is frost-proof excellent. Even under extreme conditions, expanded clay exhibits extremely fast Release of moisture. In addition, expanded clay provides good sound insulation and is guaranteed Optimal thermal insulation due to the low bulk grain density. All in all give the new lightweight building blocks have excellent test values.

die über den nach der DIN 105 Blatt 2 und den übrigen mitgeltenden Normen geforderten Werten liegen.those that are also applicable in accordance with DIN 105 sheet 2 and the others Values required by standards.

Die Beispiele erläutern die Erfindung.The examples illustrate the invention.

Beispiel 1 714 kg Naturbims der Körnungsgruppe 0-4 mm werden mit 306 kg Tonmehl t das durch Trocknen und Mahlen von Naturton erhalten worden ist, und mit Wasser in einem Mischer vermischt. Die so erhaltene Mischung wird unter Druck zu Steinrohlingen verpreßt, die nach Vortrocknung bei ca. 1.1000 C gebrannt werden. Beim erhaltenen Leichtbaustein ist die Wärmedämmung entsprechend der Scherbenrohdichte von 1,10 kg/dm3 hervorragend bei ausreichender Druckfestigkeit, die nach DIN 105 in die Nennfestigkeit:-klasse 4 einzuordnen ist. Ein Schwund nach dem Brennen tritt nicht auf.Example 1 714 kg natural pumice of the grain group 0-4 mm are mixed with 306 kg powdered clay t obtained by drying and grinding natural clay, and mixed with water in a mixer. The mixture thus obtained is under pressure pressed into stone blanks which, after pre-drying, are fired at approx. 1.1000 ° C. In the case of the lightweight building block obtained, the thermal insulation is in accordance with the bulk density of the cullet of 1.10 kg / dm3 excellent with sufficient compressive strength, which according to DIN 105 is to be classified in the nominal strength: class 4. There is a loss after burning not on.

Beispiel 2 Das Verfahren gemäß Beispiel 1 wird wiederholt, wobei jedoch ein Gemisch aus 490 kg Blähton mit 210 kg Tonmer und Wasser vermischt wird und bei 960a C gebrannt wird.Example 2 The procedure according to Example 1 is repeated, but with a mixture of 490 kg expanded clay with 210 kg Tonmer and water is mixed and with 960a C.

Die so erhaltenen Steine weisen eine erhöhte Wärmedämv entsprechend einer Scherbenrohdichte von ca. 0,80 kg/d:t bei ausreichender Druckfestigkeit von ca. 5,0 N/mm2 auf. Durch den hohen Gehalt an Blähton - es handelt sic um einen Vollstein ohne Lochung mit lediglich 2 Grifflöchern - ist auch der Schalldämmfaktor hervorragend.The stones obtained in this way have an increased heat insulation accordingly a bulk density of cullet of approx. 0.80 kg / d: t with sufficient compressive strength of approx. 5.0 N / mm2. Due to the high content of expanded clay - it is a solid stone without perforation with only 2 handle holes - the sound insulation factor is also excellent.

Beispiel 3 Während in dem vorangegangenen Beispiel Leichtbausteine aus Blähton der Korngruppe 0 bis 4 mm ohne Lochung herstellt wurden, werden in einem weiteren Versuch Leicht- bausteine mit einem Lochanteil von 15 7o unter Verwendung von Blähton der Korngruppe 0 bis 8 mm hergestellt. Weiverhin wurden Leichtbausteine mit 30 % Lochanteil durch ousatz von Blähton der Korngruppe 0 bis 8 mtn hergestellt.Example 3 While in the previous example lightweight building blocks made of expanded clay of the grain group 0 to 4 mm without perforation are in one further attempt light building blocks with a hole proportion of 15 7o made using expanded clay of the grain group 0 to 8 mm. Weverhin were Lightweight building blocks with 30% perforation through the addition of expanded clay of grain group 0 to 8 mtn manufactured.

Es wurden Gemische aus 490 kg Blähton der Korngruppe 0 bis 8 mm und 210 kg Tonmehl mit Wasser bzw. 690 kg Blähton der Korngruppe 0 bis 16 mit 210 kg Tonmehl und Wasser verwendet. Wie erwartet, waren diese Leiehtbcsteine noch leichter als Ziegelsteine nach den vorangehenden Beispielen bei völlig'ausreichender Druckfestigkeit von 3,0 bis 5,0 N/mm².Mixtures of 490 kg of expanded clay of the grain group 0 to 8 mm and 210 kg clay flour with water or 690 kg expanded clay of grain group 0 to 16 with 210 kg Clay flour and water are used. As expected, these bulbs were even lighter as bricks according to the preceding examples with completely sufficient compressive strength from 3.0 to 5.0 N / mm².

Claims

Heat and sound insulating lightweight building block and process for its Manufacture of claims 1. Heat and sound-insulating lightweight building block, which is im consists essentially of clay and a porous or porous lightweight aggregate, obtainable by mixing clay flour with the lightweight aggregate and water and then Deforming, pre-drying and firing in a manner known per se.

2. Lightweight building block according to claim 1, characterized in that g e -k e n n z e i c h n e t that the mixture is 70 to 90% by weight; Light aggregate and 30 to 10% by weight clay flour contains.

3. Lightweight building block according to claim 2, characterized in that g e -k e n n z e i c h n e t that the mixture contains expanded clay as a lightweight aggregate.

4. Lightweight building block according to claim 3, characterized in that g e -k e n n z e i c h n e t that the mixture contains 75 to 85 wt .-% expanded clay and 25 to 15 wt .-% clay powder.

5. Process for the production of a clay and a porous structure or porous lightweight aggregate containing heat and sound insulating lightweight building blocks, where you can mix clay with porous or porous lightweight aggregate in the desired mixing ratio mixed and the resulting mixture is shaped, compressed, predried and burned, in this way that the clay is used as the clay before it is used adding water to the mixing process or during the mixing process.

6. The method according to claim 5, characterized in that g e k e n n -z e i c h n e t, that the mixture components in a ratio of 70 to 90 wt .-% lightweight aggregate 30 to 10% by weight of powdered clay is used.

7. The method according to claim 6, characterized in that g e k e n n -z e i c h n e t, that expanded clay is used as a lightweight aggregate.

8. The method according to claim 7, characterized in that g e k e n n -z e i c h n e t, that 75 to 85% by weight of expanded clay is mixed with 25 to 15% by weight of powdered clay.