DE3038248C2 - Verfahren zur Auskleidung der Lauffläche eines Lagerringes - Google Patents

Verfahren zur Auskleidung der Lauffläche eines Lagerringes

Info

Publication number
DE3038248C2
DE3038248C2 DE19803038248 DE3038248A DE3038248C2 DE 3038248 C2 DE3038248 C2 DE 3038248C2 DE 19803038248 DE19803038248 DE 19803038248 DE 3038248 A DE3038248 A DE 3038248A DE 3038248 C2 DE3038248 C2 DE 3038248C2
Authority
DE
Germany
Prior art keywords
running surface
plastic
lining
bearing ring
bearing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE19803038248
Other languages
English (en)
Other versions
DE3038248A1 (de
Inventor
Hartmut 4800 Bielefeld Elges
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HELMUT ELGES KG 4800 BIELEFELD DE
Original Assignee
HELMUT ELGES KG 4800 BIELEFELD DE
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HELMUT ELGES KG 4800 BIELEFELD DE filed Critical HELMUT ELGES KG 4800 BIELEFELD DE
Priority to DE19803038248 priority Critical patent/DE3038248C2/de
Publication of DE3038248A1 publication Critical patent/DE3038248A1/de
Application granted granted Critical
Publication of DE3038248C2 publication Critical patent/DE3038248C2/de
Expired legal-status Critical Current

Description

Die vorliegende Erfindung betrifft ein Verfahren zur Auskleidung der Lauffläche eines Ls^errin^es, insbesondere des Außenringes eines Gelenk-Axiallagers, mit einer Kunststoffschicht, wobei auf die Lauffläche gemahlener oder pulverisierter, besonders gleitfähiger Kunststoff, vermischt mit einem Bindemittel, aufgetragen und unter Zuführung von Wärme und Druck gegen die Lauffläche verdichtet wird.
Ein Verfahren der gattungsgemäßen Art ist aus der DE-OS 19 66 881 bekannt.
Bei dem in der DE-OS 19 66 881 beschriebenen Verfahren werden '.hsrmoplastische Bindemittel, vorzugsweise aus Tetrafluoräthylen und Hexafluorpropylen, verwendet. Erfahrungsgemäß eriordern derartige Bindemittel eine Verarbeitungstemperatur von etwa 165°C. In der DE-OS 19 66 881 is; ausgeführt, daß die Haftvermittlerschicht aus den erwähnten Bindemitteln auf den Lagerrücken gebracht und aufgesintert wird und daß auf die aufgesinterte Haftvermittlerschicht eine weitere Schicht aus Polytetrafluoräthylenteilchen und gegebenenfalls Metallteiichen in Mischung mit einem Copolymer porös aufgesintert oder eine poröse gesinterte Folie, gegebenenfalls gefüllt mit Metallteiichen, aufgelegt wird und unter Druck und Temperatur zur Bildung einer einheitlichen Lagerlaufschicht in die Haftvermittlerschicht hineingedrückt und verdichtet wird.
Der vorliegenden Erfindung liegt die Aufgabe zugrunde, das Verfahren der gattungsgemäßen Art dahingehend zu vereinfachen, daß eine gute Verbindung und Verdichtung des Kunststoffs unter allen Umständen ermöglicht wird.
Diese Aufgabe wird erfindungsgemäß gelöst durch die Verwendung von gesintertem, gleitfähigem Kunststoffmaterial in Verbindung mit einer Nitrilkautschuk-Phenolverbindung oder einem Vinyl-Phenolharz als Bindemittel.
Die angegebenen Bindemittel erlauben eine im Vergleich zum vorbekannten Stand der Technik erheblich niedrigere Verarbeitungstemperatur. Die angegebenen Bindemittel können gegebenenfalls bei Temperaturen um 200C verarbeitet werden. Durch eine Verarbeitung bei höheren Temperaturen, aber noch deutlich unter dem Niveau der bisher verwendeten Bindemittel, wird eine deutliche Verbesserung der Klebefestigkeit erreicht. Bei Verarbeitungstemperaturen von etwa 80—900C erfüllen die erfindungsgemäß vorgeschlagenen Bindemittel höchste Anforderungen.
Durch die relativ niedrigen Verarbeitungstemperaturen wird die Verwendung von Gleitkunststoff aus bereits gesintertem Material ermöglicht, so daß die Kosten für die Auskleidung der Lauffläche eines Lagerringes gegenüber dem bekannten Stand der Technik beträchtlich gesenkt werden können.
In den Zeichnungen ist ein nach dem erfindungsgemäßen Verfahren behandelter Außenring eines Gelenk-Axiallagers dargestellt, und anhand der Figuren soll das erfindungsgemäße Verfahren noch einmai ausführlich erläutert werden. Es zeigt im einzelnen
F i g. 1 einen Schnitt durch ein komplettes Gelenk-Axiallager,
F i g. 2 einen Schnitt durch den Außenring des Lagers nach F ig. 1,
Fig.3 einen Teilschnitt nach der Linie IH-IH in cig-2,
F i g. 4 eine Ansicht des Lagerringes in Richtung des Pfeiles IVin Fig.2.
Wie insbesondere die F i g. 1 und 2 sehr deutlich zeigen, ist die Lauffläche 1 des Außenringes 2 mit Kunststoff ausgekleidet. Dies wird nach dem erfindungsgemäßen Verfahren dadurch erreicht, daß auf die Lauffläche 1 gemahlener oder pulverisierter Kunststoff aufgetragen und derselbe anschließend unter Zuführung von Wärme und Druck verdichtet und mit der Lauffläche 1 fest verbunden wird. Wie die F i g. 3 und 4 sehr deutlich zeigen, ist die Lauffläche 1 des Außenringes 2 aufgerauht, und zwar sind im dargestellten Ausführungsbeispiel radial verlaufende Riefen 3 angebracht. Durch diese Aufrauhung der Lauffläche 1 wird die Haftfähigkeit des Kunststoffes am Außenring 2 wesentlich verbessert.
Als Gleitkunststoff wird bereits gesintertes Material in gemahlener oder pulverisierter Form verwendet. Da sich für wartungsfreie Lager bislang Polytetrafluorethylen mit entsprechenden Beimengungen recht gut bewährt hat, ist in erster Linie ein derartiger Kunststoff vorgesehen, es können aber sämtliche anderen Kunststoffe Verwendung finden, die gleiche oder noch bessere Eigenschaften aufweisen. Dies gilt ebenso hinsichtlich der Beimengungen, die dem Kunststoff zugefügt werden, um die speziellen Anforderungen, wie beispielsweise Trockenschmiereigenschaften c, dgl., zu verbessern. Damit das auf die Lauffläche 1 aufgebrachte Kunststoffpulver während des Verdichtungsvorganges nicht ausweichen kann, ist es zweckmäßig, sowohl am unteren wie auch am oberen Rand der Lauffläche 1 Haltevorrichtungen vorzusehen, die ein Ausweichen des Kunststoffpulvers verhindern. Dies könnte beispielsweise dadurch geschehen, daß entsprechend geformte Zusatzringe in den Außenring 2 eingeschoben bzw. auf denselben aufgelegt werden. Die Haltekanten könnten aber auch direkt an den Außenring 2 angedreht sein.
Als Bindemittel wird eine Nilrilkautschuk-Phenolverbindung oder ein Vinyl-Phenolharz verwendet. Diese Bindemittel erlauben Verarbeitungstemperaturen zwischen 200C und 900C, so daß das bereits gesinterte Kunststoffmaterial einwandfrei mit der Lauffläche des Lagerringes verbunden wird.
Das verwendete Bindemittel gewährleistet eine gute Verbindung und Verdichtung des schon einmal gesinterten Kunststoffpulvers sowie ein einwandfreies Verkleben desselben.
Um die Laufeigenschaften der Beschichtung zu verbessern, das heißt, insbesondere deren Lebensdauer und Belastungsfähigkeit zu erhöhen, kann dem Kunststoffpulver eine PTFE-Po!yestermischung beigemengt werden.
Zur Herabsetzung oder vollständigen Veränderung des Kaliflusses kann dem Kunsistoffpulver eine Beimi-
schung von Glaspulver, MoS2, PTFE-Molekülen, gereckten PTFE-BaumwolI-, Glasseide- und/oder Polyester-Fasern beigegeben werden.
Hierzu 2 Blatt Zeichnungen
10
15
20
30
35
40
50
55
60

Claims (1)

  1. Patentanspruch:
    Verfahren zur Auskleidung der Lauffläche eines Lagerringes, insbesondere des Außenringes eines Gelenk-Axiallagers, mit einer Kunststoffschicht, wobei auf die Lauffläche gemahlener oder pulverisierter, besonders gleitfähiger Kunststoff, vermischt mit einem Bindemittel, aufgetragen und unter Zuführung von Wärme und Druck gegen die Lauffläche verdichtet wird, gekennzeichnet durch die Verwendung von gesintertem, gleitfähigem Kunststoffmaterial in Verbindung mit einer Nitrilkautschuk-PhenoIverbindung oder einem Vinyl-Phenolharz als Bindemittel
DE19803038248 1980-10-10 1980-10-10 Verfahren zur Auskleidung der Lauffläche eines Lagerringes Expired DE3038248C2 (de)