DE29920722U1 - One-component PUR sealing compound - Google Patents
One-component PUR sealing compoundInfo
- Publication number
- DE29920722U1 DE29920722U1 DE29920722U DE29920722U DE29920722U1 DE 29920722 U1 DE29920722 U1 DE 29920722U1 DE 29920722 U DE29920722 U DE 29920722U DE 29920722 U DE29920722 U DE 29920722U DE 29920722 U1 DE29920722 U1 DE 29920722U1
- Authority
- DE
- Germany
- Prior art keywords
- pur
- sealant
- sealing compound
- prepolymers
- pur sealant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
ARNE MISSLING Dipl.-ing. PATENTANWALT ARNE MISSLING Dipl.-Ing. PATENT ATTORNEY
&bgr; (06 41) 9 74 60-0, D-35390 Giessen&bgr; (06 41) 9 74 60-0, D-35390 Giessen
25. November 1999 Mi-Gr/Fa99.160GMNovember 25, 1999 Mi-Gr/Fa99.160GM
Weiss Chemie + Technik GmbH & Co. KG Hansastraße 2 D-35708 HaigerWeiss Chemie + Technik GmbH & Co. KG Hansastrasse 2 D-35708 Haiger
Die Erfindung betrifft eine einkomponentige PUR-Dichtmasse.The invention relates to a one-component PUR sealant.
Eine derartige PUR-Dichtmasse kann dazu verwendet werden, Löcher oder Risse in Dichtbahnen auszubessern. Solche Dichtbahnen werden im Allgemeinen dazu verwendet, Dächer gegenüber von außen eindringende Feuchtigkeit abzudichten und zugleich auch Schwitzfeuchtigkeit aus dem Inneren des Hauses durch die Dichtbahn nach außen zu transportieren. Dazu weisen die Dichtbahnen eine Vlies- und eine Membranschicht auf. Die Dichtbahnen werden auf einem Dach quer zu den Sparren über die gesamte EJreite des Daches ausgelegt. Dabei wird an dem unteren Ende der Sparren mit einer ersten Dichtbahn begonnen, an welche sich weitere Dichtbahnen anschließen, wobei sich diese Dichtbahnen in ihren Randbereichen überlappen. Die Befestigung der Dichtbahnen erfolgt durch Festklammern oder -nageln der Dichtbahnen im Bereich der darunter liegenden Sparren. Dadurch entstehen Löcher in den Dichtbahnen, durch welche Feuchtigkeit bzw. Wasser in das Innere des Daches bzw. Hauses transportiert werden kann. Außerdem kön-Such a PUR sealant can be used to repair holes or cracks in sealing sheets. Such sealing sheets are generally used to seal roofs against moisture penetrating from the outside and at the same time to transport moisture from the inside of the house to the outside through the sealing sheet. The sealing sheets have a fleece and a membrane layer for this purpose. The sealing sheets are laid out on a roof across the rafters over the entire width of the roof. A first sealing sheet is laid at the lower end of the rafters, followed by further sealing sheets, with these sealing sheets overlapping in their edge areas. The sealing sheets are attached by clamping or nailing the sealing sheets in the area of the rafters below. This creates holes in the sealing sheets through which moisture or water can be transported into the interior of the roof or house. In addition,
nen bei den Arbeiten der Dachdecker auf dem Dach Löcher oder Risse in den Dichtbahnen entstehen. Auch durch diese wird dann, falls diese Löcher oder Risse nicht repariert werden, Feuchtigkeit vom Äußeren ins Innere des Hauses transportiert.When roofers work on the roof, holes or cracks can appear in the waterproofing membranes. If these holes or cracks are not repaired, moisture can then be transported from the outside to the inside of the house.
Derzeit werden zum Abdichten der durch das Festklammern oder -nageln der Dichtbahnen auf den Sparren entstandenen Löcher Butylkautschukbänder verwendet, welche mit einer beidseitigen Klebeschicht versehen sind. Diese Butylkautschukbänder werden auf die Sparren aufgeklebt und anschließend die Dichtbahnen auf die mit den Butylkautschukbändern versehenen Sparren aufgelegt und auf diesen festgenagelt bzw. -geklammert. Die Butylkautschukbänder sollen die durch sie hindurchtretenden Nägel und Klammern so fest manschettenartig umschließen, dass ein Durchtritt von Feuchtigkeit bzw. Wasser durch die Nagellöcher unmöglich wird. Dieser dichtende Effekt erfolgt jedoch leider nicht in einem zufriedenstellenden Maße.Currently, butyl rubber tapes with an adhesive layer on both sides are used to seal the holes created by clamping or nailing the sealing strips to the rafters. These butyl rubber tapes are glued to the rafters and then the sealing strips are placed on the rafters with the butyl rubber tapes and nailed or clamped to them. The butyl rubber tapes are designed to enclose the nails and staples that pass through them so tightly like a cuff that it is impossible for moisture or water to pass through the nail holes. Unfortunately, this sealing effect is not satisfactory.
Die Reparatur der Dichtbahnen erfolgt ebenfalls überwiegend mit Butylkautschukflicken. In diesem Fall sind die Butylkautschukflicken jedoch mit einer einseitigen Klebeschicht versehen und werden nachträglich von außen auf die Vlies- und/oder Gewebeschicht der Dichtbahn geklebt, so dass der Riss oder das Loch überdeckt wird. Auf den ersten Blick mag diese Art der Abdichtung zwar ausreichend erscheinen, jedoch ist es möglich, dass Wasser, welches von der Vlies- und/oder Gewebeschicht der Dichtbahn aufgesogen ist, an die reparierte Stelle kriecht. Da die Butylkautschukflicken in der Regel keine ausreichende Viskosität aufweisen, um in die Vlies- und/oder Gewebeschicht einzudringen und sie derart zu durchdringen, dass in der Vlies- und/oder Gewebeschicht ein geschlossener und für die Kriechfeuchtigkeit undurchdringlicher Bereich rund um das Loch oder den Riss entsteht, in dem das Butylkautschukflicken mit der auf der Unterseite der Dichtbahn befindlichen Membranschicht verbunden ist, kann die Feuchtigkeit zwischen dem Butylkautschukflicken und der Membranschicht durch die Vlies- und/oder Gewebeschicht hindurchkriechen und im Weiteren durch das LochThe repair of the sealing membranes is also mainly carried out using butyl rubber patches. In this case, however, the butyl rubber patches are provided with an adhesive layer on one side and are subsequently glued from the outside to the fleece and/or fabric layer of the sealing membrane so that the tear or hole is covered. At first glance, this type of sealing may seem sufficient, but it is possible that water that has been absorbed by the fleece and/or fabric layer of the sealing membrane will creep into the repaired area. Since the butyl rubber patches generally do not have sufficient viscosity to penetrate the fleece and/or fabric layer and penetrate it in such a way that a closed area impenetrable to creeping moisture is created in the fleece and/or fabric layer around the hole or crack in which the butyl rubber patch is connected to the membrane layer on the underside of the sealing sheet, the moisture can creep through the fleece and/or fabric layer between the butyl rubber patch and the membrane layer and then through the hole
oder den Riss in das Innere des Daches bzw. Hauses eindringen. Durch Veränderung der Klebstoffviskosität der Butylkautschukbänder können zwar Optimierungen erreicht werden. Diese gehen jedoch zu Lasten der Trennfestigkeit, speziell der Scherfestigkeit des Butylkautschukflickens. Bei der Verarbeitung solcher Bänder muss daher besonders auf eine gute Verklebung mit der darunter befindlichen Vlies- und/oder Gewebeschicht geachtet werden. Da jedoch nur in speziellen Konstruktionen mit einer Hartunterdachung eine derart ausreichende Verklebung möglich ist, kann eine zufriedenstellende Verklebung bzw. Abdichtung der Reparaturstelle nur in den seltensten Fällen erfolgen. In der Regel entfällt nämlich eine Hartunterdachung, und die Dichtbahnen werden nur über die Sparren gespannt. In den Räumen zwischen den Sparren drückt sich daher die Dichtbahn durch, so bald der Dachdecker versucht, den Butylkautschukflicken unter Druck fest auf der Vlies- und/oder Gewebeschicht zu fixieren.or penetrate the crack into the interior of the roof or house. Optimizations can be achieved by changing the adhesive viscosity of the butyl rubber tapes. However, this comes at the expense of the separation strength, especially the shear strength of the butyl rubber patch. When processing such tapes, particular attention must be paid to ensuring good adhesion to the fleece and/or fabric layer underneath. However, since such sufficient adhesion is only possible in special constructions with a hard roof underlay, satisfactory bonding or sealing of the repair site can only be achieved in the rarest of cases. As a rule, there is no hard roof underlay and the sealing sheets are only stretched over the rafters. In the spaces between the rafters, the sealing sheet therefore pushes through as soon as the roofer tries to firmly fix the butyl rubber patch to the fleece and/or fabric layer under pressure.
Der Erfindung liegt daher die Aufgabe zugrunde, ein Ersatz für die Butylkautschukbänder zu finden, welcher einfach zu verarbeiten ist und eine ausreichende Abdichtung gegen von außen eindringende Feuchtigkeit in das Innere eines Daches bietet und dabei insbesondere durch die Nagellöcher und Reparaturstellen eintretende Kriechfeuchtigkeit aufgrund der Dochtwirkung unterbindet.The invention is therefore based on the object of finding a replacement for the butyl rubber tapes, which is easy to process and offers sufficient sealing against moisture penetrating from the outside into the interior of a roof and, in particular, prevents creeping moisture entering through nail holes and repair points due to the wicking effect.
Diese Aufgabe wird erfindungsgemäß durch den kennzeichnenden Teil des Anspruches 1 gelöst.This object is achieved according to the invention by the characterizing part of claim 1.
Die erfindungsgemäße einkomponentige PUR-Dichtmasse ist insbesondere aufgrund der während des Auftragens der PUR-Dichtmasse auf die Vlies- und/oder Gewebeschicht vorhandenen niedrigen Viskosität dazu geeignet, die Löcher oder Risse - so auch die Nagellöcher - in ausreichend zufriedenstellendem Maße abzudichten. Die PUR-Dichtmasse kann so in die Vlies- und/oder Gewebeschicht eindringen, sie vollständig durchdringen, bis sie mit der auf der Unterseite der Vlies- und/oder Gewebeschicht angebrachten Membranschicht verbunden ist. Dadurch kann ein in der Vlies- und/oder Ge-The one-component PUR sealant according to the invention is particularly suitable for sealing the holes or cracks - including nail holes - to a sufficiently satisfactory extent due to the low viscosity present during the application of the PUR sealant to the fleece and/or fabric layer. The PUR sealant can thus penetrate into the fleece and/or fabric layer, completely penetrating it until it is connected to the membrane layer attached to the underside of the fleece and/or fabric layer. This allows a gap in the fleece and/or fabric layer to be formed.
webeschicht entstehender dichtender „Ring" aus der PUR-Dichtmasse um die abzudichtende Stelle gelegt werden. Die auf der Oberfläche der Vlies- und/oder Gewebeschicht verbleibende PUR-Dichtmasse wird so im Bereich der Reparaturstelle verteilt, dass sich ein dichtender Überzug über dem Nagelloch, Riss oder Loch bildet, wobei die Ränder dieses dichtenden Überzuges im Bereich des in der Vlies- und/oder Gewebeschicht ausgebildeten Ringes liegen. Das Eindringverhalten der PUR-Dichtmasse in die Vlies- und/oder Gewebeschicht wird durch die niedrige Viskosität erreicht. Die leichte Thixotropie der PUR-Dichtmasse gewährleistet bei Rissen eine Spaltlochüberdeckung. Nachdem die PUR-Dichtmasse in die Vlies- und/oder Gewebeschicht eingedrungen ist und der Überzug auf der Oberfläche der Vlies- und/oder Gewebeschicht gebildet wurde, härtet die PUR-Dichtmasse, insbesondere durch Feuchtigkeitseinwirkung, aus. Dabei kann die Umgebungsfeuchte ausreichend sein, jedoch sollte vorteilhaft mittels eines Zerstäubers Wasser auf die PUR-Dichtmasse aufgesprüht werden, um somit das ausreichende Schäumverhalten zu gewährleisten.A sealing "ring" of the PUR sealant created by the fleece and/or fabric layer is placed around the area to be sealed. The PUR sealant remaining on the surface of the fleece and/or fabric layer is distributed in the area of the repair site in such a way that a sealing coating is formed over the nail hole, crack or hole, with the edges of this sealing coating lying in the area of the ring formed in the fleece and/or fabric layer. The penetration behavior of the PUR sealant into the fleece and/or fabric layer is achieved by the low viscosity. The slight thixotropy of the PUR sealant ensures that gaps are covered in the event of cracks. After the PUR sealant has penetrated into the fleece and/or fabric layer and the coating has been formed on the surface of the fleece and/or fabric layer, the PUR sealant hardens, particularly through the action of moisture. The ambient humidity can be sufficient, but water should preferably be sprayed onto the PUR sealant must be sprayed on to ensure sufficient foaming behavior.
Vorteilhafte Bereiche für die in der PUR-Dichtmasse enthaltenen Stoffe sind (in Gew-%)Advantageous ranges for the substances contained in the PUR sealant are (in % by weight)
95 - 98 % Prepolymere,
1-3 % Weichmacher,95 - 98 % prepolymers,
1-3% plasticizer,
0,5 - 2 % Stabilisierungsmittel,
0,2 - 1 % PUR-Beschleuniger und0.5 - 2 % stabilizing agent,
0.2 - 1 % PUR accelerator and
0 - 0,75 % Farbpigmente oder Farbpasten.0 - 0.75% color pigments or color pastes.
Eine besonders vorteilhafte Zusammensetzung der PUR-Dichtmasse weist folgende Anteile der Stoffe auf (in Gew-%):A particularly advantageous composition of the PUR sealant has the following proportions of the substances (in % by weight):
96 % Prepolymere,
2 % Weichmacher,96 % prepolymers,
2 % plasticizer,
1 % Stabilisierungsmittel,
0,7 % PUR-Beschleuniger und1% stabiliser,
0.7 % PUR accelerator and
0,3 % Farbpigmente/Farbpasten.0.3% color pigments/color pastes.
Das in der PUR-Dichtmasse enthaltene Prepolymer kann vorteilhaft die folgende Zusammensetzung (in Gew-% der gesamten PUR-Dichtmasse) haben: The prepolymer contained in the PUR sealant can advantageously have the following composition (in weight % of the total PUR sealant):
34 - 42 % Polyole und34 - 42 % polyols and
35 - 63 % lsocyanat.35 - 63 % isocyanate.
Eine besonders vorteilhafte Zusammensetzung des Prepolymeres v/eistA particularly advantageous composition of the prepolymer is
38 % Polyole und
59 % lsocyanat38 % polyols and
59 % isocyanate
(bezogen auf das Gesamtgewicht der PUR-Dichtmasse) auf.(based on the total weight of the PUR sealant).
Gemäß der Erfindung können die Polyole aus einem oder mehreren Diolen bestehen, insbesondere zu gleichen Teilen aus Diolen mit einem Molekulargewicht von 1000 und 2000.According to the invention, the polyols may consist of one or more diols, in particular equal parts of diols having a molecular weight of 1000 and 2000.
Gemäß der Erfindung kann das lsocyanat vorteilhaft ein modifiziertes Roh-4,4'-Methylendiphenylisocyanatsein. According to the invention, the isocyanate can advantageously be a modified crude 4,4'-methylenediphenyl isocyanate.
Vorteilhaft ist es, wenn der Weichmacher Diisobutylphtalat und das Stabilisierungsmittel Diethylmalonat ist und der PUR-Beschleuniger Dibutylzinndilanat und Dimorpholindiethylether enthält.It is advantageous if the plasticizer is diisobutyl phthalate and the stabilizer is diethyl malonate and the PUR accelerator contains dibutyltin dilanate and dimorpholine diethyl ether.
Die PUR-Dichtmasse sollte so eingestellt sein, dass aufgrund der Feuchtigkeitseinwirkung während des Aushärtens die PUR-Dichtmasse aufschäumt, wobei der gebildete Schaum zähelastisch ist. Dieses verbessert die dichtenden Eigenschaften der PUR-Dichtmasse. Ebenfalls wird vorteilhaft die Viskosität der PUR-Dichtmasse zu Beginn des Aushärtens ansteigen.The PUR sealant should be adjusted in such a way that the PUR sealant foams up due to the effect of moisture during curing, whereby the foam formed is viscoelastic. This improves the sealing properties of the PUR sealant. The viscosity of the PUR sealant will also advantageously increase at the beginning of curing.
Ein Beispiel für die Verwendung der erfindungsgemäßen PUR-Dichtmasse ist anhand der Zeichnungen näher beschrieben. Darin zeigenAn example of the use of the PUR sealing compound according to the invention is described in more detail with reference to the drawings.
Fig. 1 die Draufsicht auf einen mit einer PUR-Dichtmasse ausgebesserten Riss bzw. ein Loch undFig. 1 the top view of a crack or hole repaired with a PUR sealant and
Fig. 2 einen Querschnitt durch den ausgebesserten Riss bzw. das Loch gemäß Fig. 1.Fig. 2 shows a cross-section through the repaired crack or hole according to Fig. 1.
Die in Fig. 1 dargestellte Dichtbahn 1, welche eine Vliesschicht 11 und eine Membranschicht 12 aufweist, weist einen Riss bzw. Loch 3 auf. Dieser Riss bzw. Loch 3 ist mit einer einkomponentigen PUR-Dichtmasse 2 abgedichtet worden. Dazu wurde die PUR-Dichtmasse 2 auf eine Vliesschicht 11 der Dichtbahn 1 aufgetragen. Aufgrund der niedrigen Viskosität der PUR-Dichtmasse 2 dringt diese während und unmittelbar nach dem Auftragen in das Gewebe der Vliesschicht 11 ein. Die Vliesschicht 11 wird vollständig von der PUR-Dichtmasse 2 durchdrungen, wobei die PUR-Dichtmasse 2 durch das Gewebe bis zu einer Membranschicht auf der Unterseite der Dichtbahn 1 durchdringt (Fig. 2) und an dieser dichtend anhaftet. Der übrige Teil der PUR-Dichtmasse 2 verbleibt außerhalb der Vliesschicht 11 erhaben leicht thixotrop auf der Oberfläche der Dichtbahn 1 bzw. sickert zumindest teilweise durch den Riss bzw. das Loch 3 in der Dichtbahn 1 hindurch. Dadurch ergibt sich eine vollständige Spaltüberdeckung des Risses 3 der Dichtbahn 1. Von außen auf die abgedichtete Stelle auftreffende Feuchtigkeit kann nunmehr nicht durch die Abdichtung hindurchtreten. Selbst Wasser, welches in die Vliesschicht 11 aufgrund der Dochtwirkung transportiert wird, gelangt immer nur bis an die Grenze des Bereiches der Vliesschicht 11, in den die PUR-Dichtmasse 2 eingedrungen ist. Während des Aushärtens durch Feuchtigkeit schäumt die PUR-Dichtmasse 2 zähelastisch auf und der Schaum dichtet dadurch zusätzlich den Riss, das Loch 3 bzw. Fremdkörper wie Nägel ab. Damit ist für die Verbundfähigkeit und die weitere Dichtigkeit nach dem Aufnageln einer Konterlattung gesorgt. Eine erfindungsgemäße PUR-Dichtmasse ist witterungs- und alterungsbeständig.The sealing sheet 1 shown in Fig. 1, which has a fleece layer 11 and a membrane layer 12, has a crack or hole 3. This crack or hole 3 has been sealed with a one-component PUR sealant 2. For this purpose, the PUR sealant 2 was applied to a fleece layer 11 of the sealing sheet 1. Due to the low viscosity of the PUR sealant 2, it penetrates into the fabric of the fleece layer 11 during and immediately after application. The fleece layer 11 is completely penetrated by the PUR sealant 2, with the PUR sealant 2 penetrating through the fabric to a membrane layer on the underside of the sealing sheet 1 (Fig. 2) and adhering to it in a sealing manner. The remaining part of the PUR sealant 2 remains outside the fleece layer 11, raised slightly thixotropic on the surface of the sealing sheet 1 or at least partially seeps through the crack or hole 3 in the sealing sheet 1. This results in a complete gap coverage of the crack 3 in the sealing sheet 1. Moisture hitting the sealed area from the outside can no longer penetrate through the seal. Even water that is transported into the fleece layer 11 due to the wicking effect only ever reaches the edge of the area of the fleece layer 11 into which the PUR sealant 2 has penetrated. As it hardens due to moisture, the PUR sealant 2 foams up in a viscoelastic manner and the foam also seals the crack, hole 3 or foreign bodies such as nails. This ensures the bonding ability and further tightness after nailing on counter battens. A PUR sealant according to the invention is weather- and ageing-resistant.
1 Dichtbahn1 sealing membrane
11 Vliesschicht11 Fleece layer
12 Membranschicht12 Membrane layer
2 PUR-Dichtmasse2 PUR sealant
3 Riss bzw. Loch3 Crack or hole
Claims (13)
50-98% Prepolymere,
50-50% Pigmente/Füllstoffe,
0-10% Thixotropiermittel,
0-10% Feuchtigkeitsbindemittel,
0-5% Stabilisierungsmittel,
0-5% PUR-Beschleuniger und
100-5% Farbpigmente/ Farbpasten
enthält und dass die Prepolymere einen Überschuss an Isocyanat aufweisen. 1. One-component PUR sealant, characterized in that the PUR sealant (in % by weight)
50-98% prepolymers,
50-50% pigments/fillers,
0-10% thixotropic agent,
0-10% moisture binder,
0-5% stabilizing agent,
0-5% PUR accelerator and
100-5% color pigments/ color pastes
and that the prepolymers contain an excess of isocyanate.
95-98% Prepolymere,
1-3% Weichmacher,
0,5-2% Stabilisierungsmittel,
0,2-1% PUR-Beschleuniger und
0-0,75% Farbpigmente oder Farbpasten
enthält. 2. PUR sealing compound according to claim 1, characterized in that the PUR sealing compound (in % by weight)
95-98% prepolymers,
1-3% plasticizer,
0.5-2% stabilizing agent,
0.2-1% PUR accelerator and
0-0.75% color pigments or color pastes
contains.
96% Prepolymere,
2% Weichmacher,
1% Stabilisierungsmittel,
0,7% PUR-Beschleuniger und
0,3% Farbpigmente/Farbpasten
enthält. 3. PUR sealing compound according to claim 1 or 2, characterized in that the PUR sealing compound (in % by weight)
96% prepolymers,
2% plasticizer,
1% stabilizing agent,
0.7% PUR accelerator and
0.3% colour pigments/colour pastes
contains.
34-42% Polyole und
55-63% Isocyanat
enthalten. 4. PUR sealing compound according to one of claims 1 to 3, characterized in that the prepolymers (in % by weight)
34-42% polyols and
55-63% isocyanate
contain.
38% Polyole und
59% Isocyanat
enthalten. 5. PUR sealing compound according to one of claims 1 to 4, characterized in that the prepolymers (in % by weight)
38% polyols and
59% Isocyanate
contain.