DE29907361U1 - Composite material that can be printed on by computer, in particular for the production of business cards - Google Patents
Composite material that can be printed on by computer, in particular for the production of business cardsInfo
- Publication number
- DE29907361U1 DE29907361U1 DE29907361U DE29907361U DE29907361U1 DE 29907361 U1 DE29907361 U1 DE 29907361U1 DE 29907361 U DE29907361 U DE 29907361U DE 29907361 U DE29907361 U DE 29907361U DE 29907361 U1 DE29907361 U1 DE 29907361U1
- Authority
- DE
- Germany
- Prior art keywords
- composite material
- cards
- information card
- material according
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
PATENTANWÄLTEPATENT ATTORNEYS
WIESBADEN-MÜNCHEN-ALICANTE··"WIESBADEN-MUNICH-ALICANTE··"
Sig232-GBM/luSig232-GBM/lu
MIT COMPUTER BEDRUCKBARES VERBUNDMATERIAL, INSBESONDERE ZUR HERSTELLUNG VON VISITENKARTENCOMPUTER-PRINTABLE COMPOSITE MATERIAL, ESPECIALLY FOR THE PRODUCTION OF BUSINESS CARDS
Sigel GmbH + Co Bäumenheimer Str. D-86690 Mertingen DeutschlandSigel GmbH + Co Bäumenheimer Str. D-86690 Mertingen Germany
European Patent Attorneys European Trademark AttorneysEuropean Patent Attorneys European Trademark Attorneys
Büro/Office MünchenOffice Munich
Dr. Thomas M. Fritzsche Dipl.-Chem. und BiologeDr. Thomas M. Fritzsche Dipl.-Chem. and Biologist
Brienner Straße 52Brienner Strasse 52
D-80333 MünchenD-80333 Munich
Telefon: O 89/5 23 17 09 Telefax: 0 89/52 24 05Telephone: O 89/5 23 17 09 Fax: 0 89/52 24 05
Dr.lng. Jürgen H. Fuchs Dipl.-Ing., B. Com.Dr. Lng. Jürgen H. Fuchs Dipl.-Ing., B. Com.
Dr. rer. nat. Klaus Mehler Dipl.-Phys.Dr. rer. nat. Klaus Mehler Dipl.-Phys.
Dipl.-Ing. Christian WeißDipl.-Ing. Christian Weiß
Dipl.-Ing. Kurt Müller Dipl.-Phys. Werner WitzelDipl.-Ing. Kurt Müller Dipl.-Phys. Werner Witzel
Abraham-Lincoln-Straße D-65189 WiesbadenAbraham-Lincoln-Strasse D-65189 Wiesbaden
Postfach 46 60 D-65036 WiesbadenPO Box 46 60 D-65036 Wiesbaden
Telefon: 06 11/71 42-0 Telefax: 0611/71 42-20Telephone: 06 11/71 42-0 Fax: 0611/71 42-20
e-mail: fuchs-pat@t-online.dee-mail: fuchs-pat@t-online.de
Paseo Explanada de Espana No. 3. 5-dchaPaseo Explanada de Espana No. 3. 5-dcha
ES-03002 Alicante Telefon: +34/96/5 20 01 Telefax: + 34/96/5 20 02ES-03002 Alicante Telephone: +34/96/5 20 01 Fax: + 34/96/5 20 02
USt.-ID-Nr./VAT REG No. DE 130307463VAT ID No./VAT REG No. DE 130307463
Postbank MünchenPostbank Munich
Konto 2403 67-806Account 2403 67-806
(BLZ 700100 80)(Bank code 700100 80)
Volksbank Freudenstadt Konto 12 834 009 (BLZ 642 910 10)Volksbank Freudenstadt Account 12 834 009 (bank code 642 910 10)
• ··
Sig232 TMF/luSig232 TMF/lu
Sigel GmbH + CoSigel GmbH + Co
"Mit Computer bedruckbares Verbundmaterial, insbesondere zur Herstellung von Visitenkarten""Computer printable composite material, particularly for the production of business cards"
Die Erfindung betrifft ein mit Computerdruckern bedruckbares Verbundmaterial aus einem flexiblen Trägermaterial, einem Informationskartenmaterial und einer dazwischen angeordneten Kleberschicht, das insbesondere zur Herstellung von beschrifteten und/oder bebilderten Informationskarten bzw. Schildern wie Visitenkarten, Tischkarten, Post- und Glückwunsch- und Fotokarten sowie Formularen, etc. geeignet ist.The invention relates to a composite material which can be printed with computer printers and consists of a flexible carrier material, an information card material and an adhesive layer arranged therebetween, which is particularly suitable for the production of labelled and/or illustrated information cards or signs such as business cards, place cards, postcards, greeting cards and photo cards as well as forms, etc.
Mit der Verbesserung der Computerdrucker, insbesondere der Laserdrucker und Tintenstrahldrucker können nun auch in Einzelanfertigung Schwarz/Weiß- sowie Farbdrucke von hoher Qualität und in kleinen Auflagen von jedermann mit Hilfe eines Computerprogrammes hergestellt werden. Da früher die Herstellung von optisch sauberen Drucken für beispielsweise Visitenkarten, Tischkarten, Ausweisen, Formularen etc. nur mittels teurer und aufwendig zu bedienender Offset-Druckereien möglich war, bestand daher ein Bedarf, diese kostenintensive Art der Druckerei durch billigere Techniken zu ersetzen. Computerdrucker haben jedoch den Nachteil, daß diese ausschließlich für den Betrieb von genormten Papieren, wie DIN A4, DIN A3, etc. eingestellt sind, Visitenkarten, Formulare, Tischkarten, Ausweise, etc. jedoch eine wesentlich kleinere Form aufweisen, welche von solchen Druckern nicht mehr verarbeitet werden kann.With the improvement of computer printers, particularly laser printers and inkjet printers, anyone can now produce high-quality black and white and color prints in small runs using a computer program. In the past, optically clean prints for business cards, place cards, ID cards, forms, etc. could only be produced using expensive and difficult-to-operate offset printing, so there was a need to replace this costly type of printing with cheaper technology. Computer printers, however, have the disadvantage that they are only set up to work with standardized paper such as DIN A4, DIN A3, etc., while business cards, forms, place cards, ID cards, etc. are much smaller and cannot be processed by such printers.
Es ist daher bereits versucht worden, derartige bedruckbare Papiere bereitzustellen, die zum Bedrucken mit Computerdruckern geeignet sind.Attempts have therefore already been made to provide such printable papers that are suitable for printing with computer printers.
Es sind bereits auf DIN A4-Bögen angeordnete Visiten- und Tischkarten bekannt, die sich nach dem Bedrucken aus dem Papierbogen heraustrennen lassen. Zur Erleichterung des Heraustrennens sind die Ränder der Karten mit einer vorgefertigten Mikroperforation versehen, entlang derer die Visitenkarten vom Bogen abgetrennt werden können. Solche bedruckbaren Kartenbogen werden beispielsweise von der Firma Sigel GmbH + Co, 86690 Mertingen, Deutschland, zusammen mit der entsprechenden Software unter der Bezeichnung "CARDDESIGNER8" vertrieben. Obwohl derartige Mikroperforationen heute unter der Belassung von kleinsten Stanzstegen durchführbar sind, haben sie doch den Nachteil, daß der Eindruck entsteht, die Ränder seien ausgefranst oder uneben. Es besteht daher der Bedarf, bedruckbare Karten bereitzustellen, die keine solchen Stanzstege aufweisen.Business and table cards arranged on DIN A4 sheets are already known and can be torn out of the paper sheet after printing. To make it easier to tear them out, the edges of the cards are provided with a pre-made micro-perforation along which the business cards can be torn off the sheet. Such printable card sheets are sold, for example, by the company Sigel GmbH + Co, 86690 Mertingen, Germany, together with the corresponding software under the name "CARDDESIGNER 8 ". Although such micro-perforations can now be carried out by leaving the smallest of punching bars, they have the disadvantage that they give the impression that the edges are frayed or uneven. There is therefore a need to provide printable cards that do not have such punching bars.
In der DE-A 44 20 027 wird vorgeschlagen, derartige bereits vom restlichen Papierbogen vollständig ausgestanzte Karten mit mindestens einem schmalen, mit einem Haftkleber einseitig beschichteten Klebeband zu versehen, das die linienförmigen Stoßstellen zwischen benachbarten Reihen von Karten und/oder zwischen den Karten und dem restlichen Bogenmaterial (Trägermaterial) überdeckt und dabei die Bestandteile dieses Verbundes aneinander heftet. Derartige Verbundmaterialien haben jedoch den Nachteil, daß das beschichtete Klebeband aus Kunststoff besteht und daher schwer zu recyceln ist. Darüber hinaus besteht die Gefahr, daß sich beim Gebrauch die Klebestellen voneinander lösen.DE-A 44 20 027 proposes that such cards, which have already been completely punched out of the remaining paper sheet, be provided with at least one narrow adhesive tape coated on one side with a pressure-sensitive adhesive, which covers the linear joints between adjacent rows of cards and/or between the cards and the remaining sheet material (carrier material) and thereby attaches the components of this composite to one another. However, such composite materials have the disadvantage that the coated adhesive tape is made of plastic and is therefore difficult to recycle. In addition, there is a risk that the adhesive points will separate from one another during use.
6 -6 -
Eine weitere Vorgehensweise zur Herstellung eines Trägermaterials ist in der EP-A 83 69 53 beschrieben. Dabei ist ein Formular mit einer heraustrennbaren Karte an der Formularrückseite mittels eines Schälleims auf ein Trägermaterial aufgeklebt, das die Karte im Formular hält. Die Karte ist dabei ein durch ein von der Formularvorderseite her zur Trägerschicht hin ausgeführter Stanzling. Nach dem Ablösen vom Trägermaterial ist die Karte frei von irgendwelchem Klebermaterial.Another procedure for producing a carrier material is described in EP-A 83 69 53. In this case, a form with a detachable card on the back of the form is glued to a carrier material using a peeling adhesive, which holds the card in the form. The card is a die-cut piece made from the front of the form to the carrier layer. After being detached from the carrier material, the card is free of any adhesive material.
Die Erfindung hat daher zum Ziel, derartige mit Computerdruckern bedruckbare Verbundmaterialien bereitzustellen, die insbesondere zur Herstellung von Visitenkarten, Tischkarten, Formularen und Ausweisen etc. geeignet sind, und die bereits im Verbund ohne Belassen von Stanzstegen vollumlaufend vorgestanzt sind, aber sich dennoch beim Bedrucken in Computerdruckern nicht vom Trägermaterial ablösen.The invention therefore aims to provide such composite materials which can be printed with computer printers and which are particularly suitable for producing business cards, place cards, forms and ID cards, etc., and which are already pre-punched all the way around in the composite without leaving any punching bars, but which nevertheless do not detach from the carrier material when printed in computer printers.
Dieses Ziel wird erfindungsgemäß durch die Bereitstellung eines bedruckbaren Verbundmaterials zur Herstellung von beschriebenen und/oder bebilderten Informationskarten bzw. -schildern gemäß den Ansprüchen erreicht.This object is achieved according to the invention by providing a printable composite material for producing written and/or illustrated information cards or signs according to the claims.
Das erfindungsgemäße Verbundmaterial umfaßt eine Lage aus einem flexiblen Trägermaterial, eine flächige Lage aus einem die Karten bereits in ausgestanzter Form enthaltenden Kartenmaterial sowie eine dazwischen angeordnete Leimschicht, welche die Lage aus dem Trägermaterial und die Lage aus dem Kartenmaterial in einer beim Bedrucken stabilen, jedoch später wieder lösbaren Weise miteinander laminiert, wobei das Kartenmaterial mindestens eine im Verbundmaterial außenliegende, mit Computerdruckern beschriftbare Seite aufweist, und die Leimschicht zum Trägermaterial eine geringere Adhäsivität aufweist als zurThe composite material according to the invention comprises a layer of a flexible carrier material, a flat layer of a card material containing the cards already in punched form, and an adhesive layer arranged between them, which laminates the layer of the carrier material and the layer of the card material together in a manner that is stable during printing but can be removed again later, wherein the card material has at least one side on the outside of the composite material that can be written on with computer printers, and the adhesive layer has a lower adhesiveness to the carrier material than to the
ftft
O O
ausgestanzten Karte und wobei die Leimschicht beim Ablösen an der Informationskarte haften bleibt und die nach dem Ablösen freiliegende Leimschicht nicht mehr klebrig ist.punched card and where the glue layer remains attached to the information card when removed and the glue layer exposed after removal is no longer sticky.
In einer besonders bevorzugten Ausführungsform bestehen sowohl das flexible Trägermaterial als auch das die spätere Karten, Formulare, etc. bildende Kartenmaterial aus einem recyclingfähigen Material, insbesondere einem Papier. Dabei ist das Kartenmaterial vorzugsweise ein etwas stärkeres Papiermaterial mit einer Grammatur von vorzugsweise 150-250 g/m2 und das Trägermaterial ein dünneres Papier mit einer Grammatur von vorzugsweise 25-80 g/m2, insbesondere 30-60 g/m2, z.B. 40-45 g/m2. Besonders bevorzugt sind dünne, flexible Pergamentpapier oder Naturpapiere.In a particularly preferred embodiment, both the flexible carrier material and the card material that later forms the cards, forms, etc. consist of a recyclable material, in particular paper. The card material is preferably a somewhat stronger paper material with a grammage of preferably 150-250 g/m 2 and the carrier material is a thinner paper with a grammage of preferably 25-80 g/m 2 , in particular 30-60 g/m 2 , eg 40-45 g/m 2 . Thin, flexible parchment paper or natural paper are particularly preferred.
In einer bevorzugten Ausführungsform wird das Trägermaterial mindestens auf der im Verbund inneliegenden, zur Klebeschicht und zum die Karten und Formulare enthaltenden Informationsträger zugewandten Seite wenigstens im Bereich der abzulösenden Karten mit einem Release-Coat beschichtet, so daß die innere Oberfläche des Trägermaterials zur angrenzenden Leimschicht eine geringere Adhäsivität aufweist als die innere Oberfläche des Kartenmaterials. Bevorzugte Release-Coats sind silikonisierte Beschichtungen.In a preferred embodiment, the carrier material is coated with a release coat at least on the side inside the composite facing the adhesive layer and the information carrier containing the cards and forms, at least in the area of the cards to be detached, so that the inner surface of the carrier material has a lower adhesiveness to the adjacent glue layer than the inner surface of the card material. Preferred release coats are siliconized coatings.
Besonders zweckmäßig sind Release-Coats, die ein Gemisch aus einem mittels einem Leimwerk, vorzugsweise einem Druckwerk, wie einem Flexodruckwerk, auftragbaren Lack umfassen. Bevorzugte Lacke sind Acrylate sowie Mischungen davon, insbesondere von di- und polyfunktionalen Acrylaten. Vorzugsweise weisen sie einen die Polymerisationsreaktion startenden Fotoinitiator auf. Typische Fotoinitiatoren sind dem Fachmann bekannt. BesondersParticularly useful are release coats which comprise a mixture of a varnish which can be applied by means of a gluing unit, preferably a printing unit such as a flexographic printing unit. Preferred varnishes are acrylates and mixtures thereof, in particular of di- and polyfunctional acrylates. They preferably have a photoinitiator which starts the polymerization reaction. Typical photoinitiators are known to the person skilled in the art. Particularly
geeignet sind vergilbungsfreie Fotoinitiatoren. Derart typische radikalische Fotoinitiatoren sind 2,2-Dimethoxy-l,2-diphenylethanon-[Benzyl-Mono(dimethylketal)], (l-Hydroxycyclohexyl)phenylmethanon, 2-Hydroxy-2-Methyl-l-Phenyl-l-Propanon oder auch &agr;,&agr;-Diethoxyacetophenon (DEAP). Weitere Fotoinitiatoren sind Benzoinmethylether und 2-t-Butylanthrachinon. Die Konzentration des Fotoinitiators im UV-härtbaren Lack ist im allgemeinen von der Lichtintensität der verwendeten UV-Lampe und der Verweildauer hierunter abhängig. Mit üblichen Auftrag- und Reaktionsmaschinen haben sich Konzentrationen von 2-10 Gew.-%, insbesondere 4-8, vorzugsweise 5-7 Gew.-% als zweckmäßig erwiesen. Der Fotolack enthält gegebenenfalls weitere Hilfsmittel sowie geeignete Lösungsmittel. Dem UV-Lack wird zweckmäßigerweise ein Abstoßungsmittel, üblicherweise ein Silierungsmittel zugesetzt. Zweckmäßige Mittel sind Siloxane und Siloxene, insbesondere Dimethylsiloxene, wie Polydimethylsiloxen. Diese sind in der aus Abstoßungsmittel und Lack gebildeten Release-Coat-Mischung üblicherweise in einer Menge von 9-15 Gew.-%, vorzugsweise 11-14 Gew.-% vorhanden.Non-yellowing photoinitiators are suitable. Typical radical photoinitiators of this type are 2,2-dimethoxy-l,2-diphenylethanone-[benzyl mono(dimethyl ketal)], (l-hydroxycyclohexyl)phenylmethanone, 2-hydroxy-2-methyl-l-phenyl-l-propanone or α,α-diethoxyacetophenone (DEAP). Other photoinitiators are benzoin methyl ether and 2-t-butylanthraquinone. The concentration of the photoinitiator in the UV-curable varnish generally depends on the light intensity of the UV lamp used and the residence time under it. With conventional application and reaction machines, concentrations of 2-10% by weight, in particular 4-8, preferably 5-7% by weight have proven to be appropriate. The photoresist optionally contains other auxiliaries and suitable solvents. A repellant, usually a silage agent, is expediently added to the UV varnish. Useful agents are siloxanes and siloxenes, especially dimethylsiloxenes, such as polydimethylsiloxene. These are usually present in the release coat mixture formed from the repellant and the lacquer in an amount of 9-15% by weight, preferably 11-14% by weight.
Bevorzugte Fotoinitiatoren sind solche, die bei einer Wellenlänge von 200-380 nm aktiviert werden. Eine zweckmäßige Strahlungshärtung beträgt 0,5-5 Joule/cm3, vorzugsweise 0,5-1,5 Joule/cm3. Vorzugsweise werden Mischungen von mindestens 2, zweckmäßigerweise 3-5, insbesondere 4 Fotoinitoren verwendet.Preferred photoinitiators are those which are activated at a wavelength of 200-380 nm. A suitable radiation curing is 0.5-5 joules/cm 3 , preferably 0.5-1.5 joules/cm 3 . Preferably, mixtures of at least 2, suitably 3-5, in particular 4 photoinitiators are used.
Der Leim zum Verkleben der beiden Lagen ist vorzugsweise aus Klebstoffen ausgewählt, die zum Verkleben von saugfähigen Materialien verwendet werden. Bevorzugt sind insbesonders Heißsiegelkleber, die einen Erweichungspunkt von mindestens 55°C und eine Siegeltemperatur von mindestens 75, vorzugsweise mindestens 1200C aufweisen. EineThe glue for bonding the two layers is preferably selected from adhesives used for bonding absorbent materials. Particularly preferred are hot-seal adhesives which have a softening point of at least 55°C and a sealing temperature of at least 75, preferably at least 120 0 C.
Siegeltemperatur oberhalb von 2800C ist zwar möglich, jedoch nicht bevorzugt. Zweckmäßigerweise liegt die Siegeltemperatur unterhalb 200°C. Temperaturen im Bereich von 130-1600C sind besonders geeignet. Allerdings können bei der Herstellung auf Maschinen mit hohen Bandlaufgeschwindigkeiten Siegeltemperaturen von über 3000C eingesetzt werden.Sealing temperatures above 280 0 C are possible, but not preferred. The sealing temperature is preferably below 200°C. Temperatures in the range of 130-160 0 C are particularly suitable. However, sealing temperatures of over 300 0 C can be used during production on machines with high belt speeds.
Als besonders zweckmäßig haben sich Polyacrylatmischungen sowie Polyester und Polyurethane sowie Mischungen davon erwiesen. Bevorzugt sind Polyester-Polyurethanmischungen, die in Form wässriger Dispersionen im Handel erhältlich sind. Durch Zugabe unterschiedlicher Härtermengen und unterschiedlicher Härterarten kann die Siegeltemperatur derartiger Kunstharzleime stufenlos über weite Bereiche hin eingestellt werden. Üblicherweise werden die Härter in einer Menge von 0,5-6 Gew.-%, vorzugsweise 1-4 Gew.-% zur Heißsiegelklebermischung zugesetzt, wobei die Siegeltemperatur erhöht wird.Polyacrylate mixtures, polyesters and polyurethanes, and mixtures thereof, have proven to be particularly useful. Polyester-polyurethane mixtures, which are commercially available in the form of aqueous dispersions, are preferred. By adding different amounts of hardeners and different types of hardeners, the sealing temperature of such synthetic resin adhesives can be continuously adjusted over a wide range. The hardeners are usually added to the hot-seal adhesive mixture in an amount of 0.5-6% by weight, preferably 1-4% by weight, whereby the sealing temperature is increased.
Derartige Klebstoffe werden so eingestellt, daß die mit ihnen hergestellten Leimschichten transparent sind und eine stumpfe Oberfläche aufweisen. Für eine stumpfe Oberfläche werden insbesondere Dispersionen mit Teilchen einer Größe £0,01 um, vorzugsweise >0,05 um und insbesondere 2:0,1 um verwendet. Die obere Teilchengrenze liegt üblicherweise bei 1 \im, insbesondere bei 0,5 um. Besonders bevorzugte Teilchengrößen sind 0,2 &mgr;&igr;&agr;. Such adhesives are adjusted so that the glue layers produced with them are transparent and have a dull surface. For a dull surface, dispersions with particles of a size of £0.01 µm, preferably >0.05 µm and in particular 2:0.1 µm are used in particular. The upper particle limit is usually 1 µm, in particular 0.5 µm. Particularly preferred particle sizes are 0.2 µm.
übliche Härter für Polyester-Polyurethanmischungen sind Isocyanate, insbesondere Polyisocyanate.Common hardeners for polyester-polyurethane mixtures are isocyanates, especially polyisocyanates.
üblicherweise werden die Dispersionskleber derart aufgetragen, daß sie nach dem Auftragen ein Trockengewicht von 6-8 g/m2 aufweisen. Das Naßauftraggewicht liegtUsually, the dispersion adhesives are applied in such a way that they have a dry weight of 6-8 g/m 2 after application. The wet application weight is
- 10 -- 10 -
üblicherweise bei 15-30, insbesondere bei 18-22 g/m2, wobei 20 g/m2 besonders bevorzugt sind.usually 15-30, especially 18-22 g/m 2 , with 20 g/m 2 being particularly preferred.
Üblicherweise wird der Kleber vollflächig in Form eines Filmes aufgetragen. In einer bevorzugten Ausführungsform wird im Bereich der ablösbaren Karten eine geringere Menge Leim aufgetragen als im übrigen Bereich. In einer weiteren bevorzugten Ausführungsform weist der Bereich um die den Umfang bzw. den Kartenrand definierenden Stanzlinien herum eine stärkere Leimschicht auf, beispielsweise dadurch, daß der Leim dort dicker aufgetragen ist. üblicherweise ist die verstärkte Leimschicht etwa 3-15 mm, insbesondere 5-10 mm breit. In der Mitte der Karte kann dann der Leim dünner aufgetragen sein.The adhesive is usually applied over the entire surface in the form of a film. In a preferred embodiment, a smaller amount of glue is applied in the area of the removable cards than in the rest of the area. In a further preferred embodiment, the area around the punch lines defining the circumference or edge of the card has a thicker layer of glue, for example by applying the glue more thickly there. The reinforced layer of glue is usually about 3-15 mm, in particular 5-10 mm wide. The glue can then be applied more thinly in the middle of the card.
In einer besonderen Ausführungsform wird der Kleber gerastert aufgetragen. Dabei wird der Kleber üblicherweise mittels Näpfchen in Form von Klebstoffpünktchen aufgetragen. Die Klebstoffpünktchen können sowohl gleichförmig über die gesamte Fläche als auch mit Bereichen unterschiedlicher Dichte aufgetragen werden. Es hat sich als besonders zweckmäßig erwiesen, die Klebstoffpünktchen im Bereich der Stanzschnitte dichter aufzutragen, und zwar vorzugsweise in den zur Druckereinzugsrichtung quer verlaufenden Schnitten. Im mittleren Bereich der Karten bzw. des Informationsträgers, der von den Stanzschnitten weiter entfernt liegt, ist es möglich, das Raster nur dünn aufzutragen. Dadurch verbleibt die Visitenkarte an den beim Bedrucken problematischen Randbereichen besser haften, läßt sich jedoch weiterhin gut ablösen. Eine solche Punkterasterung läßt sich beispielsweise mittels Dosiersystemen wie Bubble-Jet, Magnetventil, Piezo-Inject Aktoren auftragen.In a special embodiment, the adhesive is applied in a grid pattern. The adhesive is usually applied using cups in the form of adhesive dots. The adhesive dots can be applied evenly over the entire surface or in areas of varying density. It has proven particularly useful to apply the adhesive dots more densely in the area of the die cuts, preferably in the cuts that run perpendicular to the printer feed direction. In the middle area of the cards or the information carrier, which is further away from the die cuts, it is possible to apply the grid thinly. This means that the business card adheres better to the edge areas that are problematic when printing, but can still be removed easily. Such a dot grid can be applied, for example, using dosing systems such as bubble jets, solenoid valves, piezo inject actuators.
- 11 -- 11 -
Das zuvor beschriebenen Verbundmaterial ist beispielsweise dadurch erhältlich, daß man aus einer ersten flächenförmigen, eine äußere und eine innere Oberfläche aufweisenden Bahn oder Lage aus einem flexiblen Trägermaterial und aus einer zweiten flächenförmigen, eine äußere und eine innere Oberfläche aufweisenden Bahn bzw. Lage aus einem bedruckbaren Kartenmaterial mittels einer zwischen den beiden Bahnen angeordneten Leimschicht ein flächiges Verbundmaterial laminiert. Das Verkleben bzw. Laminieren wird erfindungsgemäß dadurch erreicht, daß man mittels einem auf die äußeren Oberflächen der beiden Bahnen druckausübenden Walzwerk die inneren zueinanderweisenden Bahnenoberflächen fest zusammenpreßt, daß sie durch die Leimschicht fest aneinander haften. Nach dem Laminieren wird das Verbundmaterial von der äußeren Oberfläche des bedruckbaren Kartenmaterials in vorbestimmte, die späteren bedruckbaren Karten definierende Bereiche bestanzt. Der Stanzvorgang wird derart durchgeführt, daß der die Karten bzw. Schilder bildende Bereich durch das Stanzen vollständig durchtrennt wird, ohne daß dabei Stanzstege belassen bleiben. Auf diese Weise werden nach dem Ablösen der Karte aus dem Verbundmaterial glatte, saubere Seitenkanten erhalten. Das Stanzen wird zwar vorzugsweise bis in die Leimschicht hinein, nicht jedoch so tief ausgeführt, daß die darunter liegende Trägerschicht ihre Stabilität verliert. Vor dem Laminieren wird dann auf die innere Oberfläche des flexiblen Trägermaterials und/oder des flexiblen Kartenmaterials zumindest in den die bedruckbaren Karten definierende Bereiche der zuvor definierte Release-Coat aufgetragen, getrocknet und auf zumindest einer der beiden inneren Oberflächen mittels eines Druckwerkes ein Leim aufgetragen. Nach dem Laminieren wird der Leim getrocknet und/oder gehärtet. Der Leim wird erfindungsgemäß in einer solchen Menge und Art aufgetragen, daß der Verbund beim Bedrucken fest aneinanderThe composite material described above can be obtained, for example, by laminating a flat composite material from a first sheet-like web or layer made of a flexible carrier material, which has an outer and an inner surface, and a second sheet-like web or layer made of a printable card material, which has an outer and an inner surface, using a layer of glue arranged between the two webs. The bonding or lamination is achieved according to the invention by firmly pressing the inner web surfaces facing each other together using a roller that exerts pressure on the outer surfaces of the two webs, so that they adhere firmly to one another thanks to the layer of glue. After lamination, the composite material is punched from the outer surface of the printable card material into predetermined areas that define the later printable cards. The punching process is carried out in such a way that the area forming the cards or signs is completely severed by the punching, without leaving any punching webs. In this way, smooth, clean side edges are obtained after the card has been removed from the composite material. The punching is preferably carried out into the glue layer, but not so deep that the underlying carrier layer loses its stability. Before lamination, the previously defined release coat is then applied to the inner surface of the flexible carrier material and/or the flexible card material, at least in the areas defining the printable cards, dried and a glue is applied to at least one of the two inner surfaces by means of a printing unit. After lamination, the glue is dried and/or hardened. According to the invention, the glue is applied in such an amount and manner that the composite adheres firmly to one another during printing.
- 12 -- 12 -
haftet, die ausgestanzten Karten sich jedoch aus dem Verbundmaterial zerstörungsfrei herauslösen lassen. Dabei wird bei der Herstellung der Leim derart getrocknet und/oder ausgehärtet, daß die verbleibende Leimschicht nach dem Ablösen der ausgestanzten Karten aus dem Verbundmaterial nicht mehr klebrig ist. Vorzugsweise wird die Stanzung mittels eines um seine Längsachse rotierenden Stanzzylinders ohne Belassen von Stanzstegen durchgeführt.adheres, but the punched-out cards can be removed from the composite material without causing damage. During production, the glue is dried and/or hardened in such a way that the remaining glue layer is no longer sticky after the punched-out cards have been removed from the composite material. Preferably, the punching is carried out using a punching cylinder rotating about its longitudinal axis without leaving any punching webs.
Derartige Verbundmaterialien werden zur Herstellung von beschriebenen und/oder bebilderten Informationskarten bzw. Schildern verwendet. Derartige Karten und Schilder sind vorzugsweise Visitenkarten, Firmenausweise, insbesondere temporäre Firmenausweise, Post-, Glückwunsch- und Einladungskarten sowie Tischkarten, Fotokarten und Fotobilder, insbesondere für die digitale Fotographie, sowie Einsteckschilder für Regale, Hängemappen, Ordner und Namensschilder für Seminare etc. Auch zur Herstellung von Einlegern für Behälter für Datenträger, wie für CD-Boxen, sog. Tool-Boxen, ZIP-Träger, Disketten, Schallplatten und ähnlichem sind die erfindungsgemäßen Verbundmaterialien verwendbar. Die Karten weisen vorzugsweise die gängigen Größen wie DIN-A6 oder DIN-A7, übliche Visitenkartengrößen sowie die üblichen Fotogrößen 10x15, 9x13 bzw. 12x18 cm auf.Such composite materials are used to produce written and/or illustrated information cards or signs. Such cards and signs are preferably business cards, company IDs, in particular temporary company IDs, postcards, greeting cards and invitation cards as well as place cards, photo cards and photo images, in particular for digital photography, as well as insert signs for shelves, hanging files, folders and name tags for seminars etc. The composite materials according to the invention can also be used to produce inserts for containers for data storage media, such as for CD boxes, so-called tool boxes, ZIP carriers, diskettes, records and the like. The cards preferably have the usual sizes such as DIN A6 or DIN A7, usual business card sizes and the usual photo sizes 10x15, 9x13 or 12x18 cm.
Die Erfindung soll am folgenden Beispiel näher erläutert werden.The invention will be explained in more detail using the following example.
Fig. 1 zeigt einen erfindungsgemäßen Bogen von seiner bedruckbaren Vorderseite. Dabei sind zehn vorgestanzte Karten nebeneinander in Längsrichtung derart angeordnet, daß zwischen ihnen ein Verstärkungssteg stehen bleibt. Die in Einzugsrichtung längs verlaufenden Stanzstege, welche die schmalen Kartenseiten definieren, laufen bis zumFig. 1 shows a sheet according to the invention from its printable front side. Ten pre-punched cards are arranged next to each other in the longitudinal direction in such a way that a reinforcing web remains between them. The punched webs running lengthwise in the feed direction, which define the narrow sides of the card, run up to the
Blattende durch und erleichtern nach dem Bedrucken das Abknicken bzw. das Herauslösen der Karten. Die quer zur Einzugsrichtung verlaufenden Stanzlinien sind nicht volldurchlaufend, so daß jeweils links und rechts der Karte ein Bogensteg verbleibt, der einem scharfen Abknikken beim Einzug in den Drucker entgegenwirkt, so daß die quer verlaufenden Kartenseiten sich nicht so leicht ablösen.The punch lines run perpendicular to the feed direction and make it easier to bend or remove the cards after printing. The punch lines running perpendicular to the feed direction are not continuous, so that a web remains on the left and right of the card, which counteracts sharp bending when it is fed into the printer, so that the perpendicular card sides do not come off so easily.
Bei der Herstellung eines derartigen Bogens wird von einer ersten Endlosbahn ein Trägerpapier mit einer Grammatur von 45 g/m2 abgerollt und in einem Leimauftrag mittels einem Druckwerk mit einem Flexolack, der 12% eines Silikons (Polydimethylxyloxen) als Abstoßungsmittel oder Repellent und 36% eines difunktionellen Monoacrylacrylats sowie 45% eines polyfunktionellen Acrylats zusammen mit 5% eines Fotoinitiators aufweist, in einer Konzentration von ca. 20g/m2 Naßgewicht aufgetragen und anschließend mittels einer UV-Lampe gehärtet. Nach dem Trocknen wird ein mit einer das Silikonrepellant enthaltende Trennschicht beschichtetes erstes Endlospapier erhalten, das in einem weiteren Arbeitsgang mit einer den späteren Informationsträger bildenden zweiten, ebenfalls endlosen Kartonbahn mit einer Grammatur von 185 g/m2 in einer Zweibahnmaschine zusammengeführt, d. h. naß kaschiert wird. Vor dem Kaschieren wird diese zweite Endlosbahn mittels einem Kunstharzleim bestehend aus einer Polyesterpolyurethan-Dispersion in einer Menge von ca. 20 g/m2 naß beschichtet (entsprechend 8g/m2 Trockengewicht)· Nach dem Zusammenführen dieser beiden Bahnen in der zuvor genannten Zweibahnenmaschine wird das erhaltene Verbundmaterial mittels einem Infrarottrockner bei ca. 1500C erwärmt, wobei ggf. vorliegender Härter aktiviert wird und der Disperionsklebstoff aushärtet und gleichzeitig getrocknet wird. Danach werden mittels einer Schnittstanzung dieIn the production of such a sheet, a carrier paper with a grammage of 45 g/m 2 is unrolled from a first continuous web and is applied in a glue application by means of a printing unit with a flexo varnish containing 12% of a silicone (polydimethylxyloxene) as a repellant or repellent and 36% of a difunctional monoacrylic acrylate and 45% of a polyfunctional acrylate together with 5% of a photoinitiator in a concentration of approx. 20 g/m 2 wet weight and then hardened using a UV lamp. After drying, a first continuous paper coated with a separating layer containing the silicone repellent is obtained, which in a further operation is combined with a second, also continuous cardboard web with a grammage of 185 g/m 2 in a two-web machine, i.e. wet laminated. Before lamination, this second continuous web is wet coated with a synthetic resin glue consisting of a polyester polyurethane dispersion in an amount of approx. 20 g/m 2 (corresponding to 8 g/m 2 dry weight). After these two webs are brought together in the two-web machine mentioned above, the resulting composite material is heated using an infrared dryer at approx. 150 0 C, whereby any hardener present is activated and the dispersion adhesive hardens and is dried at the same time. The
• ····
Karten etc. aus dem Endlosverbund ausgestanzt und die Bahn in DIN-gerechte Papierbögen geschnitten bzw. gestanzt. Mit solchen Bögen hergestellte Visitenkarten weisen den Vorteil auf, daß sie nach dem Herauslösen aus dem Verbund auch von der Rückseite her mittels normalen Kugelschreibern oder Füllern beschriftbar sind, aber durch den aufgetragenen anhaftenden Leim gegen Verschmutzung geschützt sind, und zwar auch dann noch, wenn der Leim nur in Punktrastern aufgetragen worden ist.Cards etc. are punched out of the continuous composite and the web is cut or punched into DIN-compliant paper sheets. Business cards made with such sheets have the advantage that they can be written on from the back using normal ballpoint pens or fountain pens after they have been removed from the composite, but are protected from dirt by the adhesive that has been applied, even if the glue has only been applied in dot grids.
In einer weiteren bevorzugten Ausführungsform kann auch die Vorderseite der Visitenkarten noch mit einem dünnen Leimauftrag versehen werden, der das Bedrucken mittels Tintenstrahl- und Laserdruckern nicht behindert.In a further preferred embodiment, the front of the business cards can also be provided with a thin layer of glue, which does not hinder printing using inkjet and laser printers.
• ··
• ··
Claims (9)