DE2702663A1 - Silicone rubber elastomer seal for inker-head opening - contains hardener e.g. di:cumyl peroxide and opt. an organic amine hardening retarder

Info

Publication number: DE2702663A1
Application number: DE19772702663
Authority: DE
Inventors: Wolfgang Ing Grad Drescher; Ehrenfried Dipl Chem Loock; Cornelis Van Dipl Ph Raamsdonk
Original assignee: Olympia Werke AG
Current assignee: Olympia Werke AG
Priority date: 1977-01-24
Filing date: 1977-01-24
Publication date: 1978-07-27
Also published as: DE2702663B2

Abstract

An elastomer, esp. a silicone rubber, is used to seal openings of an inker-heat filled with an aq. liquid. The viscous elastic flow behaviour of the elastomer is made use of to fill the smallest cavities and interspaces in the sealed inker-head surface. A pref. silicone rubber consists of (i) 10 pts. wt. silicone rubber, crosslinked at room temp. with 1 pt. wt. crosslinking agent, or of (ii) silicone rubber crosslinked with 0.5-1% crosslinking agent, esp. dicumyl peroxide, at 180 degrees C for 20 mins. Elastomer flow is limited and coating can be removed without leaving residues on inker-head surface or in nozzles. Coating adhesion is reversible.

Description

Verwendung eines Elastomers, insbesondere eines Silikon-Use of an elastomer, especially a silicone

kautschuks zum Verschließen von oeffnungen an einem Tintenschreibkopf und Silikonkautschuk zu dieser Verwendung Die Erfindung betrifft die Verwendung eines Elastomers, insbesondere eines Silikonkautschuks zum Verschließen von tiffnungen an einem Tintenschreibkopf. Der Tintenschreibkopf ist zum Schreiben mit Tinte oder mit einer anderen, beispielsweise neutralen, wäßrigen Flüssigkeit für den Transport und seine Lagerung gefüllt. Zum Verschlienen der nffnungen soll nicht nur das elastische Verhalten, sondern im besonderen das viskoselastische (Fließ-) Verhalten des Elastomers zum Auffüllen kleinster Hohl- und Zwischenräume im Bereich der verschlossenen Kopffläche genutzt werden. Und die Erfindung betrifft einen Silikonkautschuk als ein dementsprechendes Elastomer zur Verwendung als Abdeckmittel beim Verschließen der Öffnungen.rubber for closing openings on an ink recording head and silicone rubber for this use. The invention relates to the use an elastomer, in particular a silicone rubber, for closing openings on an ink recording head. The ink recording head is for writing with ink or with another, for example neutral, aqueous liquid for transport and its storage filled. To seal the openings, not only the elastic Behavior, but in particular the visco-elastic (flow) behavior of the elastomer for filling up the smallest of cavities and spaces in the area of the closed top surface be used. And the invention relates to a silicone rubber as a corresponding one Elastomer for use as a covering means in closing the openings.

Der Düsenbereich von Tintenschreibköpfen ist empfindlich gegen Verschmutzungen, wie sie z. B. durch Papierfasern und Anhäufungen von Staub hervorgerufen werden. Verschmutzungen im Düsenbereich führen mit ihren Folgeerscheinungen zu veränderter Düsengeometrie, so daß aus der Düse abzugebende Tropfen in Größe, Form und in Geschwindigkeit stark beeinflußt werden. Bei längerem Stillstand zwischen den Schreibphasen, bei Transport und Lagerung der Schreibwerke, die mit solchen Schreibköpfen bestückt sind, mun weiterhin vermieden werden, daß Tinte in den dffnungsbereichen der Düse zu stark eindickt und daß Tinte oder eine entsprechende Flüssigkeit durch Transportstöße ausläuft bzw. das Luft mit dieser in den Schreibkopf zurückgesaugt wird.The nozzle area of inkjet heads is sensitive to dirt, how they z. B. caused by paper fibers and accumulations of dust. Soiling in the nozzle area and their consequences lead to changes Nozzle geometry, so that the size, shape and speed of drops to be dispensed from the nozzle are strongly influenced. If there is a long standstill between the writing phases, at Transport and storage of the writing units equipped with such writing heads to avoid getting ink in the orifice areas of the nozzle thickens too much and that ink or a corresponding liquid from transport impacts leaks or the air is sucked back into the write head with it.

In der Aufzeichnungseinrichtung nach der US-PS 3,039,438 wird in Nicht-Schreibzeiten ein aus einem Tintentank getränktes Kissen gegen die Uffnung eines Tinte auf einen Aufzeichnungsträger übertragenden Schreibstiftes gelegt. Durch das Kissen wird die Tinte in dem Schreibstift feucht gehalten.In the recording device according to US-PS 3,039,438 in non-writing times a pad soaked from an ink tank against the opening of an ink on one Put the recording medium transferring pen. The pillow becomes the Ink kept moist in the pen.

Tintenreste von vorangegangenen Aufzeichnungen werden zwar angelöst, diese werden, wie auch die Schmutzpartikel der bereits genannten Art, beim Abheben des Kissens nicht abgonommen.Ink residues from previous recordings are dissolved, these, like the dirt particles of the type already mentioned, are released when the vehicle is lifted off of the pillow not removed.

Mit der Abdeckeinrichtung nach der DT-AS 25 19 160 wird in Nicht-Schreibzeiten ein Kissen gegen die Düsenöffnungen eines Tintenschreibkopfes gelegt. Das Kissen ist mit einem Silikonöl getränkt. Durch die Wischbewegung des Kissens werden Tintenreste und Schmutzpartikel entfernt. Es tritt jedoch hierbei Silikonöl in die Düsen ein, die sich zwischen die dort vorhandene Tinte und die Düsenwandung schiebt und so zu Veränderungen der Randwinkel in den Düsen und den Düsenbereichen führt. Hierdurch besteht im vermehrtem Maße die Möglichkeit, daß Luft eingesogen wird und der Tintenschreibkopf ausfällt.With the covering device according to the DT-AS 25 19 160 is in non-writing times a pad placed against the nozzle orifices of an ink recording head. The pillow is impregnated with a silicone oil. The wiping motion of the pad removes ink residue and dirt particles removed. However, silicone oil enters the nozzles here, which pushes itself between the ink there and the nozzle wall and so on leads to changes in the contact angle in the nozzles and the nozzle areas. Through this there is an increased possibility that air is sucked in and the ink recording head fails.

In der US-PS 3,346,869 wird in einer Ausführung ein mit einem Silikonöl benetztes Polster und in einer zweiten Ausführung eine Nylonnadel gegen die tiffnung einer Düse gebracht. Neben den bei Verwendung eines Silikonöls bereits beschriebenen nachteiligen Begleiterscheinungen muß die Nylonabdeckung sehr genau geführt werden, um den Verschleiß und ein Aufweiten der Düsenöffnung in geringen Grenzen zu halten. Bei Verwendung von Nylon oder derartigen Kunststoffen können kleinste Hohlräume zwischen dem Abdeckmaterial und der abzudeckenden Schreibkopffläche nicht aufgefüllt werden.In US Pat. No. 3,346,869, in one embodiment, a silicone oil is used wet upholstery and, in a second version, a nylon needle against the opening brought to a nozzle. In addition to those already described when using a silicone oil disadvantageous side effects, the nylon cover must be guided very precisely, in order to keep the wear and a widening of the nozzle opening within low limits. When using nylon or such plastics, the smallest cavities can be created not filled between the cover material and the writing head surface to be covered will.

Demgegenüber ist die Aufgabe der Erfindung darin zu sehen einen Werkstoff zu finden zum Abdichten insbesondere der Düsen und der an diese angrenzenden Bereiche an einem Tintenschreibkopf.In contrast, the object of the invention is to see a material to be found for sealing in particular the nozzles and the areas adjoining them on an ink recording head.

Mit diesem Werkstoff sollen die abgedeckten Bereiche während der Nicht-Schreibzeiten vor dem Einfluß der Umwelt geschützt sein und die während des Betriebes hier angesammelten Fremdpartikel und Tintenreste entfernt werden. Im besonderen soll der sich während des Schreibens einstellende Betriebszustand der Düsenbereiche hinsichtlich deren Benetzungsverhaltens und die Schreibbereitschaft der Düsen auch über länger an -dauernde Nicht-Schreibzeiten mit dem Abdeckmaterial erhalten bleiben.With this material, the covered areas should be used during non-writing times be protected from the influence of the environment and those accumulated here during operation Foreign particles and ink residues are removed. In particular, the should during of the writing adjusting operating state of the nozzle areas with respect to their Wetting behavior and the readiness of the nozzles to write even over longer periods of time Non-writing times are preserved with the masking material.

Diese Aufgabe wird gelöst durch die Verwendung eines Elastomers, insbesondere eines Silikonkautschuks, mit dem die Öffnungen an einem mit einer wäßrigen Flüssigkeit gefüllten Tintenschreibkopf verschlossen und unter Ausnutzung des viskos-elastischen (Fließen) Verhalten des Elastomers kleinste Hohl- und Zwischenräume im Bereich der verschlossenen Schreibkopffläche aufgefüllt werden sollen. Die weiteren Ansprüche beziehen sich auf bevorzugte Zusammensetzungen vernetzbarer Silikonkautschuke.This object is achieved through the use of an elastomer, in particular a silicone rubber with which the openings are connected to an aqueous liquid filled ink writing head closed and taking advantage of the viscous-elastic (Flow) Behavior of the elastomer smallest voids and spaces in the area of the sealed writing head surface should be filled. The other claims relate to preferred compositions of crosslinkable silicone rubbers.

Die Vorteile der Erfindung bestehen im besonderen darin, daß das Fließen des Elastomers begrenzt ist, so daß dieses nur so tief in die Oeffnungen einzudringen vermag, daß die Abdeckung abnehmbar ist, ohne Rückstände auf der Schreibkopffläche oder in den Düsen zu hinterlassen. Die gewünschte Oberflächenklebrigkeit der Abdeckung ist reversibel. Die durch den elastischen Anteil des Elastomers infolge von Druckbelastung sich bildende Oberflächenverformung (Oberflächennegativ der abgedeckten Fläche) bildet sich zumindest zum Teil zurück und die benutzten Abdeckbereiche können erneut gegen den Tintenschreibkopf gelegt werden. Auch lassen sich korrosionshemmende Mittel zum Vcrmeiden von Passungsrost und keimtötende Mittel zum Fernhalten von Mikroorganismen von der Düsenöffnung in das Gemisch aus der Grundsubstanz und dem Vernetzer vor dem Vernetzen eingeben, ohne das plastische Verhalten des Abdeckmaterials zu beeinträchtigen. Zur Abdichtung des Öffnungsbereiches am Schreibkopf wird ein nur geringer Druck benötigt, da sich das Elastomer der Kopfform bzw. der Form der bedeckten Fläche oder der Flächenteile auch durch Fließen anpaßt; bei Verwendung eines kaltvernetzenden Elastomers erfolgt eine sehr genaue Anpassung.The advantages of the invention are in particular that the flow of the elastomer is limited so that it can only penetrate so deeply into the openings is capable of removing the cover without leaving any residue on the writing head surface or to leave in the nozzles. The desired surface tack of the cover is reversible. The result of the elastic component of the elastomer as a result of pressure loads forming surface deformation (surface negative of the covered area) at least partially regresses and the used ones Coverage areas can be placed against the inkjet head again. Corrosion-inhibiting Means to prevent fretting corrosion and germicides to keep away Microorganisms from the nozzle opening into the mixture of the basic substance and the Enter crosslinker before crosslinking, without the plastic behavior of the cover material to affect. To seal the opening area on the write head, a only low pressure is required, as the elastomer is the shape of the head or the shape of the also adapts the covered area or parts of the area by flowing them; Using a cold-curing elastomer is a very precise match.

Im folgenden soll die Erfindung anhand von Ausführungsbeispielen und unter bezug auf die zeichnerische Darstellung beschrieben werden. Es zeigen: Figur 1 einen in Zeilenrichtung bewegbaren Tinten-Schreibkopf mit einer auf Abstand zur Düsenaustrittsfläche am Schreibkopf gehaltenen Abdeckung.In the following, the invention is based on exemplary embodiments and are described with reference to the graphic representation. They show: figure 1 an ink writing head movable in the line direction with a distance to the Nozzle exit surface on the print head held cover.

Figur 2 einen Querschnitt in einer starken Vergrößerung von dem Schreibkopf und der gegen die Düsenaustrittsfläche ohne Anpreßkraft gelegten Abdeckung, Figur 3 einen Querschnitt in starker Vergrößerung von dem Schreibkopf und der gegen die Dusenaustrittsfläche gepreßten Abdeckung und Figur 4 einen Querschnitt in starker Vergrößerung von dem Schreibkopf und der Abdeckung kurz nach dem Entfernen der Abdeckung von der Düsenaustrittsfläche. FIG. 2 shows a cross-section in a large enlargement of the writing head and the cover placed against the nozzle outlet surface without any contact pressure, FIG 3 shows a cross-section in high enlargement of the writing head and the one against the Noise outlet area pressed cover and Figure 4 shows a cross-section in greater detail Enlargement of the print head and cover shortly after removing the cover from the nozzle exit surface.

Zu den Elastomeren zählen Werkstoffe mit gummielastischen Eigenschaften. Diese Materialien dienen zur Herstellung von Kraft speichern, Dichtungselementen, Walzen und Transportbändern und zu Isoliermaterial und Schläuchen.The elastomers include materials with rubber-elastic properties. These materials are used to produce power stores, sealing elements, Rollers and conveyor belts and to insulating material and hoses.

Neben der elastischen Verformung tritt beim Uberschreiten eines bestimmten Mindestdruckes bei Elastomeren eine plastische Verformung ein, die durch viskoses Fließen hervorgerufen wird.In addition to elastic deformation occurs when a certain value is exceeded Minimum pressure in elastomers a plastic deformation caused by viscous Flow is caused.

Anhand von Versuchsaufbauten wurde beobachtet, daß durch das Fließen feinste Rauheiten in der Oberfläche eines mit einem derartigen Material abgedeckten Schreibkopfes aufgefüllt werden können. Zum Herstellen geeigneter Werkstoffe für Abdeckungen wurden bekannte Methoden der heiß- und kaltvernetzenden Art angewandt. Prinzipiell lassen sich auch andere Elastomere wie beispielsweise Polyurethan mit den entsprechenden Eigenschaften als Ersatz für Silikonkautschuk verwenden. Neben der neuen Anwendung haben sich überraschende Effekte ergeben, auch solche, die darin bestehen, daß ohne weitere Zusätze und ohne hohen Kraftaufwand Öffnungen, Spalte und sonstige Hohlräume auch in kapillaren Abmessungen verschlossen werden können.Using experimental set-ups, it was observed that the flow very fine roughness in the surface of one covered with such a material Print head can be filled. For the production of suitable materials for Known hot and cold curing methods have been used for covers. In principle, other elastomers such as polyurethane can also be used use the appropriate properties as a substitute for silicone rubber. Next to the new application has resulted in surprising effects, including those in it exist that, without further additives and without great effort, openings, gaps and other cavities can also be closed in capillary dimensions.

Für die Herstellung eines Abdeckmaterials ergaben sich folgende beispielshafte Verfahrensschritte: 1. Beispiel Es wurde HTV-Silikonkautschuk Grundmasse in Druckformen bei Temperaturen bis 1800 ohne weitere Zusatzstoffe verarbeitet.The following examples resulted for the production of a cover material Process steps: 1st example HTV silicone rubber base material was used in printing forms processed at temperatures up to 1800 without further additives.

Das Aufheizen erfolgte über etwa eine Stunde. Hierbei zeigt sich, daß die Grenzflächen gegen Luft, Metall und Teflonlack sich nicht immer gleichmäßig aushärten. Durch Nachbearbeitung, wie Abschaben der noch weichen Schicht, ließ sich das Material verwenden.The heating took about an hour. This shows that the interfaces with air, metal and Teflon lacquer are not always uniform Harden. Post-processing, such as scraping off the still soft layer, could use the material.

2. Beispiel Zu der Grundsubstanz HTV-Silikonkautschuk wurde als Zusatz ein Vernetzer aus Dicumylperoxid verwendet. Dieser Vernetzer wurde mit o,5 bis 1 % Gewichtsanteilen in den Kautschuk eingeknetet, bis die Masse homogen war. Die Aushärtung erfolgte in einer Stahl form, deren Innenseite mit Teflon beschichtet war, wobei eine Temperatur von 1600 etwa 15 Minuten lang auf das Gemisch einwirkte. Das der Form entnommene Material war durchgehend vernetzt mit leicht klebriger Oberfläche.2nd example To the basic substance HTV silicone rubber was added as an additive a crosslinker made from dicumyl peroxide is used. This crosslinker was rated 0.5 to 1 % By weight kneaded into the rubber until the mass was homogeneous. the Curing took place in a steel mold, the inside of which was coated with Teflon where a temperature of 1600 was applied to the mixture for about 15 minutes. The material removed from the mold was crosslinked throughout with a slightly sticky surface.

3. Beispiel Zu der Grundsubstanz Kautschuk wurde 0,5 bis 1 % Gewichtsanteilen Vernetzer und 0,5 bis 1 % Gewichtsanteilen Diäthanolamin zugesetzt und in den Kautschuk eingeknetet. Die Aushärtung erfolgte wie bei Beispiel 2. Das Ausgangsmaterial war wesentlich weicher als das Material nach Beispiel 2 und besaß eine stärkere Oberflächenklebrigkeit, mit deren Hilfe Verschmutzungen vom Kopf leicht und vollständig abgenommen werden konnten. Das Material paßt sich Feinkonturen schnell an. Eine bereits benutzte Abdeckstelle kann mit diesem Material mehrfach kurz hintereinander benutzt werden, da die alten Abdrücke, die bei Anlage an dem Kopf durch die bestehenden Kopfformen entstanden waren, wieder verschwanden.3rd Example The basic substance rubber was added by 0.5 to 1% by weight Crosslinker and 0.5 to 1% parts by weight of diethanolamine are added and added to the rubber kneaded. The curing took place as in Example 2. The starting material was much softer than the material according to example 2 and had a stronger surface tack, with the help of which dirt can be easily and completely removed from the head could. The material adapts to fine contours quickly. A covering point that has already been used can be used several times in quick succession with this material, as the old Imprints that were created by the existing head shape when it was placed on the head were, disappeared again.

Der heiß-vernetzende Silikonkautschuk ist im Handel unter der Bezeichnung R 800/40 C 1 der Firma Wacker Chemie erhältlich.The hot-crosslinking silicone rubber is commercially available under the name R 800/40 C 1 available from Wacker Chemie.

4. Beispiel Es wurde ein Silikonkautschuk mit der Handelsbezeichnung IC 347/1 mit einem Vernetzer mit der handelsüblichen Bezeichnung IC 347/B der Perennator Werke im Verhältnis 10:1 verrührt. Die Vernetsungszeit betrug an der Luft bei Zl=sertemperatur etwa 7 Stunden. Dieser Zweikomponenten-additionsvernetzende Kautschuk ist auch in geschlossenen Formen zu verarbeiten. Das Endprodukt ist ein chemisch weitgehend inaktiver Silikonkautschuk.Example 4 A silicone rubber with the trade name IC 347/1 with a crosslinker with the commercial name IC 347 / B the Perennator Works mixed in a ratio of 10: 1. The crosslinking time was in the air at cylinder temperature approximately 7 hours. This two-component addition-curing rubber is also available in closed Process shapes. The end product is a chemically largely inactive silicone rubber.

5. Beispiel Durch die Erhöhung der Temperatur des unter Beispiel 4 genannten Gemisches auf etwa 100° konnte dann die Vernetzungszeit von etwa 7 Stunden auf etwa eine Zeit von 5 Minuten herabgesetzt werden. Das aus Grundsubstanz und Vernetzer vermischte Material wurde in einer Dicke von 0,1 mm auf eine Folie aufgerak,elt. Zur Erhöhung der Haftfähigkeit des Silikonkautschuks auf des Träger wurde auf diesen zuvor ein Silikonkleber aufgetragen.5th example By increasing the temperature of the example 4 said mixture to about 100 ° then the crosslinking time of about 7 hours can be reduced to about 5 minutes. That from basic substance and Material mixed with crosslinkers was raked onto a film in a thickness of 0.1 mm. In order to increase the adhesion of the silicone rubber to the carrier, it was applied to the carrier previously applied a silicone adhesive.

Einigen Silikonkautschuk-Gemischen wurde von vornherein korrosionshemmende Mittel wie z. B. Cydo-hexylamin-chromat bzw. DicyclohZrylaminchromat-nitrit und als keirnhemmendes Mittel Biozide in geringsten Mengen beigefügt, um für längere Abdeckseiten sogenannten Passungsrost wie auch Mikroorganismen von den DUsenilindungen fernzuhalten.Some silicone rubber compounds were initially anti-corrosive Means such as B. Cydo-hexylamine-chromate or DicyclohZrylaminchromat-nitrite and As a germ inhibitor, biocides added in the smallest amounts to last for longer So-called fretting rust covers as well as microorganisms from the DUsenilindings keep away.

Die in geschlossenen Formen oder zu Folien verarbeiteten Bilikonkautschuke wurden zu Abdeckungen von insbesondere Düsen öffnungen an einem Tintenschreibkopf verwendet. Derartige DU-senschreibköpfe sind beispielsweise bekannt aus der DT-AS 21 64 614 und der DT-AS 22 33 469. In Figur 1 ist ein solcher, in Zeilenrichtung bewegbarer Tintenschreibkopf 1 in eine Position bringbar, in der eine Abdeckung 2 aus einem Silikonkautschuk gegen ihn legbar ist. Die Dosen 3 sind ebenso wie di. Hohlräume des Tintenschreibkopfes nach seinem Einbau in das Schreibgerät mit Tinte gefüllt. Die Tinte bildet einen negativen Meniskus 4 (Figur 2) als Grenzfläche gegen die Atmosphäre. Die gegen den Tintenschreibkopf legbare Abdeckfläche 5 der Abdeckung 2 weist eine nahezu glatte Oberfläche auf, die jedoch nicht unbedingt eben ist. Wird nun die Abdeckung, wie es in der Figur 2 dargestellt worden ist, gegen den Tintenschreibkopf 1 herangeführt, erfolgt eine Anpassung des Abdeckmaterials an die Kopfform in der Weise, daß insbesondere auch durch Oberflächenunebenheiten von Abdeckmaterial und insbesondere durch Bearbeitungsverfahren am Tintenschreibkopf hervorgerufene Riefen, stark vergrößerte Kapillare 9 entstehen, in denen Tinte bzw. Tintenreste 10 und Luft verbleiben. Da das Abdeckmaterial unter geringer Andruckkraft gegen den Tintenschreibkopf gedrückt worden ist, kommt es zu einem viskos-elastischen Fließen des Materials, so daß selbst diese kleinen Hohlräume 9 zwischen der abzudeckenden Fläche und dem Abdeckmaterial aufgefüllt werden. Hierbei konnte beobachtet werden, daß Tinte 10 in geringen Mengen und vor allem Luft aus dem Abdeckbereich in den Grenzbereich Kopf-Abdeckung-Atmosphäre 6 transportiert wurde.The bilicon rubbers processed into closed molds or foils became covers of, in particular, nozzle openings on an ink recording head used. Such DU write heads are known, for example, from the DT-AS 21 64 614 and the DT-AS 22 33 469. In Figure 1 is such, in line direction movable ink writing head 1 can be brought into a position in which a cover 2 made of a silicone rubber can be placed against him. The cans 3 are just like di. Cavities of the ink recording head with ink after it has been installed in the writing instrument filled. The ink forms one negative meniscus 4 (Figure 2) as an interface with the atmosphere. The cover surface that can be placed against the ink recording head 5 of the cover 2 has an almost smooth surface, but this is not necessarily the case is even. If now the cover, as it has been shown in Figure 2, brought up against the ink recording head 1, an adaptation of the cover material takes place to the shape of the head in such a way that, in particular, by surface unevenness of masking material and in particular by processing methods on the ink recording head evoked grooves, greatly enlarged capillaries 9 arise in which ink or Ink residue 10 and air remain. Since the cover material is under low pressure has been pressed against the ink recording head, it comes to a viscous-elastic Flow of the material, so that even these small cavities 9 between the to be covered Surface and the covering material are filled. Here it could be observed that ink 10 in small amounts and especially air from the cover area into the Border area head-cover-atmosphere 6 was transported.

In Figur 3 ist das Abdeckmaterial unter erhöhtem Druck gegen den Tintenschreibkopf gedrückt worden. Der Grenzbereich aus Kopf-Abdeckmaterial und Atmosphäre ist mit 6 positioniert.In Figure 3, the cover material is under increased pressure against the ink recording head been pressed. The border area between head cover material and atmosphere is with 6 positioned.

Dieses Bild zeigt desweiteren das Eindringen des Abdeckmaterials 2 in die Düse 3, in dem es eine konvexe Form annimmt.This picture also shows the penetration of the cover material 2 into the nozzle 3, in which it assumes a convex shape.

Die Eindringtiefe innerhalb der Düse 3 ist begrenzt. Das Fließen des Abdeckmaterials reicht jedoch aus die Hohlräume 9 (Figur 2) aufzufüllen.The depth of penetration within the nozzle 3 is limited. The flow of the However, covering material is sufficient to fill up the cavities 9 (FIG. 2).

Mit der Figur 4 soll im wesentlichen der Unterschied zwischen der elastischen und der plastischen Verformung des AMeckmaterials gezeigt werden. Die Abdecken¢ 2 ist so dargestellt worden, als befände sie sich noch vor dem Tinten-Schreibkopf 1.With the figure 4 is essentially the difference between the elastic and plastic deformation of the A-corner material shown will. The cover [2] has been shown as if it were still in front of it the ink print head 1.

Die Verformungen als Folge der Anlage der Abdeckung an der abzudeckenden Fläche des Tinten-Schreibkopfes bestehen im wesentlichen aus den elastisch verformten Bereichen 7 und den plastisch verformten Bereichen 8. Während sich die elastischen Deformierungen zurückbilden, bleiben Restverformungen in den Bereichen zurück, die durch plastische Verformungen bzw. durch viskos-elastisches Fließen deformiert wurden. Die in den Grenzbereichen 6 angesammelte und eingedickte oder ausgetrocknete Tinte 10 wird von dem Abdeckmaterial ebenso aufgenommen wie Staub- und Schmutzpartikel, die sich im Bereich des Tintenschreibkopfes auf der abgedeckten Fläche angesammelt haben. Der sich im Betrieb einstellende Benetzungsgrad im Düsenbereich konnte durch eine solche Abdeckmaßnahme erhalten werden.The deformations as a result of the installation of the cover on the one to be covered Surface of the ink recording head consist essentially of the elastically deformed Areas 7 and the plastically deformed areas 8. While the elastic If deformations recede, residual deformations remain in the areas that were deformed by plastic deformations or by viscous-elastic flow. The ink accumulated and thickened or dried out in the boundary areas 6 10 is absorbed by the covering material as well as dust and dirt particles, which accumulates in the area of the ink recording head on the covered surface to have. The degree of wetting in the nozzle area that set in during operation was able to pass through such a covering measure can be obtained.

L e e r s e i t eL e r s e i t e

Claims

Claims 1. Use of an elastomer, in particular one Silicone rubber for closing openings on one with an aqueous liquid Filled ink recording head utilizing the viscous-elastic (flow) behavior of the elastomer to fill the smallest liohl- and gaps in the area of the closed Writing head surface.

2. silicone rubber for use according to claim 1, d a d u r c h e k e k e n n n nz e i c h n e t that it consists of 10 parts by weight of the basic substance Silicone rubber and one part by weight crosslinker and the crosslinking at Room temperature has taken place.

3. silicone rubber for use according to claim 1, d a d u r c h e k e k e n n n n e i c h n e t that it consists of the basic substance silicone rubber and 0.5 to 1% parts by weight crosslinker, consisting essentially of dicumyl peroxide and the crosslinking at a temperature below 1800 within a time of took less than 20 minutes.

4. silicone rubber according to one or more of the preceding claims, d a d u r c h e k e n n n z e i c h -n e t that to brake the networking of the Silicone rubber -Crosslinker mixture to start crosslinking 0.5 to 1% by weight of an organic amine has been added.

5. silicone rubber according to one or more of the preceding claims, d a d u r c h e k e n n n z e i c h -n e t that the silicone rubber crosslinker mixture At the beginning of the crosslinking, a corrosion-inhibiting agent, in particular dicyclohexylamine-chromate-nitrite has been added.

6. silicone rubber according to claim 3, d a d u r c h g e -k e n n z E i c h n e t that to avoid nucleation the silicone rubber crosslinker mixture Biocides have been added at the beginning of the crosslinking process.