DE2757560A1 - Perforated cutter foil for dry electric razors - has hard metal layer on inside surface, and is made by electroforming - Google Patents
Perforated cutter foil for dry electric razors - has hard metal layer on inside surface, and is made by electroformingInfo
- Publication number
- DE2757560A1 DE2757560A1 DE19772757560 DE2757560A DE2757560A1 DE 2757560 A1 DE2757560 A1 DE 2757560A1 DE 19772757560 DE19772757560 DE 19772757560 DE 2757560 A DE2757560 A DE 2757560A DE 2757560 A1 DE2757560 A1 DE 2757560A1
- Authority
- DE
- Germany
- Prior art keywords
- foil
- hard metal
- metal layer
- nickel
- deposited
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
Verfahren zur Herstellung einer nur auf der Innenseite mit Hart-Process for the production of an only on the inside with hard
metall beschichteten Scherfolie für einen elektrisch betriebenen Trockenrasierapparat Die Erfindung bezieht sich auf ein Verfahren zur Herstellung einer nur an der Innenseite mit Hartmetall beschichteten Scherfolie für einen elektrisch betriebenen Trockenrasierapparat.metal-coated shaving foil for an electrically operated dry shaver the Invention relates to a method for producing one only on the inside with hard metal coated shaving foil for an electrically operated dry shaver.
Der Vorteil einer solchen Scherfolie ist, daß diese einen höheren Verschleißwiderstand und eine geringere Reibungskraft gegenüber einem bewegten Messer aufweist.The advantage of such a shaving foil is that it has a higher Wear resistance and a lower frictional force compared to a moving knife having.
Dies ist besonders bei Kammfolien von Bedeutung. Infolge ihrer sehr starken Krümmung werden hohe Anforderungen an die Biegsamkeit gestellt. Sie müssen deshalb aus weicherem Nickel mit einer Härte von maximal 400 HV hergestellt werden. Die Folge ist eine sehr geringe Verschleißbeständigkeit; nach nur kurzer Benutzungsdauer erfolgt Bruch.This is particularly important with comb slides. As a result of their very strong curvature, high demands are placed on flexibility. You need to therefore made of softer nickel with a hardness of max. 400 HV. The result is very poor wear resistance; after only a short period of use fracture occurs.
Es ist bekannt, Scherfolien nachträglich zu vernickeln oder zu verchromen.It is known that shaving foils can be subsequently nickel-plated or chrome-plated.
Ein Nachteil dieses bekannten Verfahrens ist, daß die Schneidkanten verrunden, mit der Folge einer mangelnden Schneidleistung und schlechter Hautschonung. Ein weiterer Nachteil ist, daß die Scherfolie, als deren Material bekanntermaßen nur schwefelhaltiges Nickel geeignet ist, durch diese Behandlung infolge Entwicklung atomaren Wasserstoffes versprödet und die sogenannte Wasserstoffbrüchigkeit zeigt.A disadvantage of this known method is that the cutting edges round, with the result of inadequate cutting performance and poor skin protection. Another disadvantage is that the shaving foil is known as its material only sulphurous nickel is suitable due to this treatment as a result of development atomic hydrogen embrittles and shows the so-called hydrogen brittleness.
Die Erfindung hat es sich zur Aufgabe gemacht, ein Verfahren zur Herstellung einer nur an der Innenseite mit Hartmetall beschichteten Scherfolie für einen elektrisch betriebenen Trockenrasierapparat zur Verfügung zu stellen, welches die geschilderten Nachteile behebt und in wirtschaftliche Weise die Serienproduktion in großen Stückzahlen in einwandfreier Qualität ermöglicht.It is an object of the invention to provide a method for production a shaving foil only coated with hard metal on the inside for an electrical one operated dry shaver available, which the described Eliminates disadvantages and mass production in large numbers in an economical manner in perfect quality.
Die Erfindung löst die Aufgabe durch ein galvanoplastisches Verfahren auf einer entsprechend dem Muster des Scheröffnungsbildes elektrisch nicht leitend und des Stegbildes elektrisch leitend auf ihrer Oberfläche ausgebildeten Platte, wobei die Scherfolie auf einer Hartmetallschicht abgeschieden wird.The invention solves the problem by means of an electroforming process electrically non-conductive on one corresponding to the pattern of the shear opening image and the web image is electrically conductive on its surface plate, wherein the shear foil is deposited on a hard metal layer.
In einer Weiterausbildung wird die Hartmetallschicht auf die elektrisch leitend ausgebildeten Stellen der Platte aufgebracht.In a further training, the hard metal layer is applied electrically applied conductive formed areas of the plate.
In einer Fortentwicklung werden die elektrisch leitend ausgebildeten Stellen der Platte passiviert.In a further development, the electrically conductive Make the plate passivated.
In einer vorteilhaften Weiterausbildung wird die Hartmetallschicht auf eine an der Platte galvanisch abgeschiedenen Metallzwischenfolie, insbesondere Nickelfolie, aufgebracht.In an advantageous further development, the hard metal layer on an intermediate metal foil that is electrodeposited on the plate, in particular Nickel foil applied.
In einer Fortentwicklung wird die Metallzwischenfolie vor Aufbringung der Hartmetallschicht passiviert.In a further development, the intermediate metal foil is used before application the hard metal layer passivated.
In einer anderen Fortentwicklung wird auf die passivierte Metallzwischenfolie vor Aufbringung der Hartmetallschicht elektrolytisch eine Nickelschicht in einer Dicke von weniger als 1 Mikrometer abgeschieden.Another further development focuses on the passivated intermediate metal foil before applying the hard metal layer electrolytically a nickel layer in one Thickness of less than 1 micron deposited.
Vorteilhafterweise wird die Hartmetallschicht vor Abscheidung der Scherfolie aktiviert.Advantageously, the hard metal layer is deposited before the Shaving foil activated.
Bevorzugterweise ist die Hartmetallschicht aus Nickel oder Chrom. Die Hartmetallschicht kann galvanisch oder nicht galvanisch aufgebracht werden.The hard metal layer is preferably made of nickel or chromium. The hard metal layer can be applied galvanically or not galvanically.
Nach Beendigung des Verfahrens wird die Scherfolie von der Metallzwischenfolie in an sich bekannter Weise getrennt.When the process is complete, the shaving foil is removed from the intermediate metal foil separated in a manner known per se.
In den folgenden Beispielen wird die Erfindung noch näher erläutert.The invention is explained in more detail in the following examples.
Beispiel 1 Eine elektrisch leitende Metallplatte wird durch Bedrucken mit dem gewünschten Muster mit einem an sich bekannten nicht elektrisch leitenden Lack an den den Stegen der Scherfolie entsprechenden Stellen abgedeckt und geätzt. Danach werden die Lackinseln in an sich bekannter Weise entfernt und die durch das Ätzen erhaltenen Vertiefungen mit dem elektrisch nicht leitenden Lack beschichtet. Example 1 An electrically conductive metal plate is made by printing with the desired pattern with a non-electrically conductive known per se Lacquer covered and etched at the points corresponding to the webs of the shaving foil. Then the paint islands are removed in a known manner and the Etching obtained depressions coated with the electrically non-conductive paint.
Aus einem wässerigen Bad enthaltend je Liter 300 g Chromtrioxyd und 1 g 0 Schwefelsäure wird bei 55 C innerhalb 10 Minuten bei einer Stromdichte von 50 A/dm2 Hartchrom an den den Stegen entsprechenden Stellen abgeschieden. Darauf wird aus einem Bad enthaltend je Liter 70 g Nickel als Sulfamat, 10 g Nickel als Chlorid, 40 g Borsäure und 0,2 g Benzoesäuresulfimid-Natriumsalz bei 500C und einer Stromdichte von 4 A/dm2 eine Nickelfolie abgeschieden. Diese verwächst mit der Hartchromabscheidung. Nach erfolgter Abtrennung erhält man eine an der Innenseite mit Hartchrom beschichteten Scherfolie.From an aqueous bath containing 300 g of chromium trioxide and per liter 1 g 0 sulfuric acid is at 55 C within 10 minutes at a current density of 50 A / dm2 hard chrome deposited at the points corresponding to the bars. Thereon is obtained from a bath containing 70 g of nickel per liter as sulfamate, 10 g of nickel as Chloride, 40 g boric acid and 0.2 g benzoic acid sulfimide sodium salt at 500C and one Current density of 4 A / dm2 deposited a nickel foil. This grows together with the hard chrome deposition. After the separation has taken place, one that is coated on the inside with hard chrome is obtained Shaving foil.
Beispiel 2 Auf einer Messingplatte wird ein Photolack aufgebracht, durch ein Negativdiapositiv in dem Muster des Lochfeldes belichtet und entwickelt. Example 2 A photoresist is applied to a brass plate, exposed and developed through a negative slide in the pattern of the hole field.
Es verbleiben Lackinseln an den Stellen, die den Öffnungen der Scherfolie entsprechen. Mit einer Lösung enthaltend 1 g Chromsäure je Liter wird passiviert. Eine Nickelzwischenfolie wird in einem Bad enthaltend je Liter 70 g Nickel als Sulfamat, 10 g Nickel als Chlori d, 40 g Borsäure und 0,2 g Benzoesäuresulfimid-Natriumsalz bei 500C und einer Stromdichte 2 von 4 A/dm in 26 Minuten in einer Dicke von ca. 30 Mikrometer abgeschieden. Es wird nun mit einer Lösung enthaltend 20 g Chromsäure je Liter passiviert. Aus einem Bad enthaltend je Liter 250 g Chromsäure 0 2 und 2,5 g Schwefelsäure wird bei 50 C und einer Stromdichte von 60 A/dm auf die passivierte Nickelfolie in 5 Minuten eine Hartchromschicht abgeschieden. Aus einem Bad der Zusammensetzung wie für die Abscheidung der Nickelzwischenfolie wird auf der Hartchromschicht bei 500C und einer 2 Stromdichte von 4 A/dm in 40 Minuten eine Nickelfolie abgeschieden.There remain paint islands at the points, which the openings of the shaving foil correspond. Passivation is carried out with a solution containing 1 g of chromic acid per liter. An intermediate nickel foil is contained in a bath per liter 70 g nickel as sulfamate, 10 g nickel as chloride, 40 g boric acid and 0.2 g benzoic acid sulfimide sodium salt at 500C and a current density 2 of 4 A / dm in 26 minutes in a thickness of approx. 30 microns deposited. It is now with a solution containing 20 g of chromic acid passivated per liter. From a bath containing 250 g of chromic acid 0 2 and per liter 2.5 g of sulfuric acid is passivated at 50 ° C. and a current density of 60 A / dm Nickel foil deposited a hard chrome layer in 5 minutes. From a bath of composition as for the deposition of the intermediate nickel foil is on the hard chrome layer at 500C and a current density of 4 A / dm in 40 minutes, a nickel foil is deposited.
Diese verwächst mit der Hartchromschicht. Erfolgt nun die Trennung von der Nickelzwischenfolie in an sich bekannter Weise, so verbleibt die Hartchromschicht an der Nickelfolie und man erhält eine nur an der Innenseite mit Hartchrom beschichtete Scherfolie.This grows together with the hard chrome layer. The separation now takes place from the intermediate nickel foil in a manner known per se, the hard chrome layer remains on the nickel foil and you get one coated with hard chrome only on the inside Shaving foil.
Beispiel 3 Eine Nickeizwischenfol ie wird abgeschieden und passiviert, wie in Beispiel t beschrieben. Aus einem Bad, enthaltend je Liter 20 g Nickelchlorid, 10 g Natrium dihydrogenphosphit, 20 g Milchsäure und 2 g Propionsäure wird bei einem PH von 4,6 in 15 Minuten eine Hartnickelschicht auf der Nickelzwischenfolie und darauf, wie in Beispiel 2 beschrieben, eine Nickelfolie abgeschieden. Nach der Trennung von der Nickelzwischenfolie erhält man eine nur an der Innenseite mit Hartnickel beschichtete Scherfolie. Example 3 An intermediate nickel film is deposited and passivated, as described in example t. From a bath containing 20 g of nickel chloride per liter, 10 g sodium dihydrogen phosphite, 20 g lactic acid and 2 g propionic acid is used in one PH of 4.6 in 15 minutes a hard nickel layer on the intermediate nickel foil and thereupon, as described in Example 2, deposited a nickel foil. After the separation one of the intermediate nickel foil is only obtained on the inside with hard nickel coated shaving foil.
Beispiel 4 Wie in Beispiel 1 beschrieben, wird eine Nickelzwischenfolie abgeschieden. Example 4 As described in Example 1, an intermediate nickel foil is used deposited.
Diese wird durch Behandlung mit einer Lösung enthaltend je Liter 0,5 g Chromsäure während einer Minute passiviert. Es wird nun durch Kurzzeitelektrolyse aus dem beschriebenen Nickel bad eine Nickelschicht in einer Dicke von weniger als 1 Mikrometer aufgebracht. Auf diese wird, wie in Beispiel 3 beschrieben, eine Hartnickelfolie und eine Nickelfolie abgeschieden.This is achieved by treatment with a solution containing 0.5 per liter g chromic acid passivated for one minute. It is now made by short-term electrolysis from the described nickel bath a nickel layer with a thickness of less than 1 micron applied. As in Example 3 described, deposited a hard nickel foil and a nickel foil.
Nach der Abtrennung erhält man eine nur an der Innenseite mit Hartnickel beschichtete Scherfolie, die noch eine hauchdünne Schicht Weichnickel aufweist. Eine Beeinträchtigung der Funktion ist nicht gegeben, da diese Weichnickelschicht im Betrieb sofort abgerieben wird und dann die Hartnickelschicht der Gleitpartner ist.After the separation you get one with hard nickel only on the inside coated shaving foil, which still has a very thin layer of soft nickel. The function is not impaired because this soft nickel layer is rubbed off immediately during operation and then the hard nickel layer of the sliding partner is.
Beispiel 5 Wie in Beispiel t beschrieben, wird eine Nickelzwischenfolie abgeschieden. Example 5 As described in Example t, an intermediate nickel foil is used deposited.
Mit einer Lösung enthaltend 11 g Chromsäure je Liter wird passiviert und eine Hartnickelschicht wie in Beispiel 3 beschrieben abgeschieden. Diese Hartnickelschicht wird in einer 10 Volum teigen Salzsäurelösung eine Minute bei einer Stromdichte von 5 A/dm2 aktiviert und, wie in Beispiel 1, beschrieben,eine Nickelfolie abgeschieden. Nach Abtrennung von der Nickelzwischenfolie erhält man eine nur an der Innenseite mit Hartnickel beschichtete Scherfolie.Passivation is carried out with a solution containing 11 g of chromic acid per liter and a hard nickel layer as described in Example 3 is deposited. This hard nickel layer is dough in a 10 volume hydrochloric acid solution for one minute at a current density activated by 5 A / dm2 and, as described in Example 1, deposited a nickel foil. After separation from the intermediate nickel foil, one is only obtained on the inside shaving foil coated with hard nickel.
Beispiel 6 Wie in Beispiel ~ beschrieben wird eine Nickelzwischenfolie abgeschieden und passiviert und eine Nickel schicht in einer Dicke von weniger als 1 Mikrometer aufgebracht. Es wird nun, wie in Beispiel t beschrieben, eine Hartchromschicht abgeschieden. Es wird nun während drei Minuten in einem mit Salzsäure auf ein PH von 1,5 eingestelltem Bad enthaltend je Liter 50 9 Nickelchlorid bei einer Stromdichte von 4 A/dm2 aktiviert. Danach wird wie in Beispiel t beschrieben eine Nickelfolie abgeschieden. Nach der Trennung von der Nickelzwischenfolie erhält man eine nur an der Innenseite mit Hartchrom beschichtete Scherfolie, die hauchdünn eine Nickelschicht aufweist. Example 6 As described in Example ~ is an intermediate nickel foil deposited and passivated and a nickel layer with a thickness of less than 1 micron applied. It is now, as described in Example t, a hard chrome layer deposited. It is now for three minutes in a with hydrochloric acid to a PH of 1.5 set bath containing 50 9 nickel chloride per liter at a current density activated by 4 A / dm2. A nickel foil is then used as described in example t deposited. After separation from the intermediate nickel foil, only one is obtained Shaving foil coated with hard chrome on the inside, the wafer-thin layer of nickel having.
Claims (7)