DE2314750A1 - PROCESS FOR MANUFACTURING SEAMLESS, HOMOGENOUS AND PORE-FREE ROOF COATING - Google Patents
PROCESS FOR MANUFACTURING SEAMLESS, HOMOGENOUS AND PORE-FREE ROOF COATINGInfo
- Publication number
- DE2314750A1 DE2314750A1 DE19732314750 DE2314750A DE2314750A1 DE 2314750 A1 DE2314750 A1 DE 2314750A1 DE 19732314750 DE19732314750 DE 19732314750 DE 2314750 A DE2314750 A DE 2314750A DE 2314750 A1 DE2314750 A1 DE 2314750A1
- Authority
- DE
- Germany
- Prior art keywords
- weight
- parts
- polybutene
- oil
- enamel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Description
CHEMISGHE WERKE HÜLS AG 4370 Marl, 23. März 1973CHEMISGHE WERKE HÜLS AG 4370 Marl, March 23, 1973
- RSP PATENTE -- RSP PATENTS -
Verfahren zur Herstellung nahtloser, homogener und porenfreier DachbeSchichtungenProcess for the production of seamless, homogeneous and pore-free roof coatings
Gegenstand der Erfindung ist ein Verfahren zur Herstellung nahtloser, homogener und porenfreier Dachbeschichtungen auf der Grundlage von Polyolefinen.The invention relates to a method for production seamless, homogeneous and pore-free roof coatings based on polyolefins.
Es ist bekannt, Flachdächer mit Dachneigungen von 0 bis ca, 20 zum Zwecke der Abdichtung mit Dichtungsbahnen aus Bitumen und/ oder geeigneten elastischen" oder thermoplastischen Kunststoffen zu belegen. Diese Bahnen werden meist in mehreren Lagen aufgenagelt und/oder aufgeklebt.It is known to have flat roofs with roof pitches from 0 to approx for the purpose of sealing with sealing sheets made of bitumen and / or suitable elastic or thermoplastic plastics to prove. These sheets are usually nailed and / or glued on in several layers.
Ferner ist es bekannt, Dachabdichtungen mit aufgenagelten und/- oder aufgeklebten Bitumendichtungsbahnen und einer oberen Kunststoff -Dachbahnüberklebung aus elastischem oder thermoplastischem Material durchzuführen.It is also known to seal roofs with nailed and / - or glued-on bitumen sealing sheets and an upper plastic - Carry out a roof membrane covering made of elastic or thermoplastic material.
Schließlich ist es bekannt, Dachabdeckungen mit Hilfe von Bahnen aus elastischen oder thermoplastischen Kunststoffen durchzuführen, wobei diese Kunststoffbahnen zu Planen vorgefertigt werden, die dann lose verlegt und mit Kies oder ähnlichen Materialien beschwert werden (Bauen mit Kunststoffen, Mitteilungsblatt 3/72, 15· Jahrgang und H. Jungnickel "Abdichtungs- und Bedachungstechnik mit Kunststoffbahnen", Verlagsgesellschaft Rudolf Müller, Köln-Braunsfeld, I969).Finally, it is known to carry out roof coverings with the help of sheets made of elastic or thermoplastic plastics, these plastic sheets are prefabricated into tarpaulins, which are then loosely laid and covered with gravel or similar materials be weighed down (building with plastics, bulletin 3/72, 15 · Volume and H. Jungnickel "Sealing and roofing technology with plastic sheeting", Rudolf Müller publishing company, Cologne-Braunsfeld, 1969).
Bei allen diesen BahnenbeSchichtungen wird die Dichtigkeit der Beläge zum großen Teil durch die recht problematischen Naht-, Stoß- und Überlappungsführungen bestimmt. An diesen Stellen muß immer besonders sorgfältig und gewissenhaft, d.h. mit gro-In all of these membrane coatings, the impermeability of the Coverings largely determined by the problematic seam, butt and overlap guides. In these places must always be particularly careful and conscientious, i.e. with great
1/73 409841/0049 1/73 409841/0049
- 2 - O. Z. 2703 - 2 - OZ 2703
23.3.1973March 23, 1973
ßem Zeitaufwand gearbeitet werden. Außerdem ist meist der Einsatz besonderer Kleber oder Klebestreifen erforderlich.be worked in a very time-consuming process. In addition, mostly the use special glue or tape required.
Zur Überwindung dieses Problems der Naht-, Stoß--und Überlappung sabdichtungen sind bereits Verfahren bekannt, bei denen eine Schmelzmasse auf Bitumenbasis als Dachbeschichtung aufgetragen wird. Dabei wird die gesamte Dachfläche mit einer naht- und fugenlosen Haut, die auf dem Untergrund haftet, überzogen.To overcome this problem of seams, joints and overlaps Seals are already known processes in which a bitumen-based melt applied as a roof coating will. The entire roof surface is covered with a seamless and jointless skin that adheres to the subsurface.
Bei den Beschichtungen mit den bekannten bituminösen Heißmassen ist zur Verbesserung der Haftfähigkeit auf einem andersartigen Untergrund stets ein Voranstrich erforderlich, der vor dem Auftragen der Heißmassen gut abtrocknen muß und deshalb eine Arbeitsunterbrechung verursacht.In the case of the coatings with the known bituminous hot masses, a different type of material is used to improve the adhesion The substrate always requires a primer, which must dry well before the hot mass is applied and therefore a Work interruption caused.
Außerdem zeigen solche bituminösen DachbeSchichtungen durch klimatische Einwirkungen nach gewisser Zeit,Rißbildungen und Alterungserscheinungen durch Verspröden, wodurch die Dichtigkeit beeinträchtigt wird. - -In addition, such bituminous roof coatings show through climatic effects after a certain time, cracks and Signs of aging due to embrittlement, reducing the tightness is affected. - -
Aufgabe der Erfindung war es, die. Verfahren des relevanten Standes der Technik zu verbessern.The object of the invention was the. Procedure of the relevant state to improve technology.
Es wurde nun,gefunden, daß man nahtlose, homogene und porenfreie DachbeSchichtungen auf der Grundlage von Polyolefinen in einfacher ¥eise herstellen kann, wenn man eine auf I50 bis 24o C erwärmte Schmelzmasse, bestehend aus 7 bis kO Gewichtsteilen eines weitgehend amorphen Polyolefins, TO bis 40 Gewichtsteilen eines Polybutenöles, 30 bis 70 Gewichtsteilen eines Füllstoffes und gegebenenfalls 1 bis 15 Gewichtsteilen eines trocknenden Öls, verwendet. .It has now been found that seamless, homogeneous and pore-free roof coatings based on polyolefins can be produced in a simple manner if a melt mass heated to 150 to 24o C, consisting of 7 to kO parts by weight of a largely amorphous polyolefin, TO bis 40 parts by weight of a polybutene oil, 30 to 70 parts by weight of a filler and optionally 1 to 15 parts by weight of a drying oil are used. .
Besonders bevorzugt bei dem erfindungsgemäßen Verfahren sind solche Schmelzmassen, die aus I5 bis 33 Gewichtsteilen eines weitgehend amorphen Polyolefins, 20 bis 3° Gewichtsteilen eines Polybutenöls, 35 bis 60 Gewichtsteilen eines Füllstoffs und gegebenenfalls 5 bis 10 Gewichtsteilen eines trocknenden Öls bestehen. '409841/0049Particularly preferred in the process according to the invention are those enamel masses which are composed of 15 to 33 parts by weight of a largely amorphous polyolefin, 20 to 3 ° parts by weight of one Polybutene oil, 35 to 60 parts by weight of a filler and optionally 5 to 10 parts by weight of a drying oil exist. '409841/0049
- 3 - O.Z. 2703 - 3 - OZ 2703
23.3.1973March 23, 1973
Geeignete weitgehend amorphe Polyolefine sind z.B. weitgehend ataktisches Polypropylen, Polybuten-1 und Polyhexen-1, dessen Copolymere aus den entsprechenden Monomeren untereinander und/ oder mit bis zu 20 Gewichtsprozent Äthylen, bezogen auf Buten-1 und/oder Propylen, sowie Gemische dieser Homo- und Copolymere mit einem ätherlöslichen Anteil von über $0 <$>, insbesondere von 6o bis 90 $, und RSV-Werten von 0,2 bis 2,5 dl/g, vorzugsweise von 0,3 bis 1,2 dl/g. Diese RSV-¥erte entsprechen Molekulargewichten, berechnet nach der Lösungsviskosität, von 12 000 bis 300 000, vorzugsweise von 19 000 bis 125 000 für Polypropylen und von 35 000 bis 1 000 000, vorzugsweise von 60 000 bis 400 000 für Polybuten-1.Suitable largely amorphous polyolefins are, for example, largely atactic polypropylene, polybutene-1 and polyhexene-1, the copolymers of which are composed of the corresponding monomers with one another and / or with up to 20 percent by weight of ethylene, based on butene-1 and / or propylene, and mixtures of these homo- and copolymers with an ether-soluble fraction of over $ 0 <$> , in particular from 60 to 90 $, and RSV values from 0.2 to 2.5 dl / g, preferably from 0.3 to 1.2 dl / g. These RSV values correspond to molecular weights, calculated according to the solution viscosity, from 12,000 to 300,000, preferably from 19,000 to 125,000 for polypropylene and from 35,000 to 1,000,000, preferably from 60,000 to 400,000 for polybutene-1.
Bevorzugt wird als weitgehend amorphes Polyolefin ein weitgehend ataktisches Polybuten-1 mit ätherlöslichen Anteilen von über 50 $, vorzugsweise von 60 bis 90 $, und RSV-Werten von vorzugsweise 0,3 bis 1,2 dl/g, insbesondere von 0,4 bis 0,6 dl/g.A largely amorphous polyolefin is preferred atactic polybutene-1 with ether solubles of over $ 50, preferably from $ 60 to $ 90, and RSV values of preferably 0.3 to 1.2 dl / g, in particular from 0.4 to 0.6 dl / g.
Die bei dem erfindungsgemäßen Verfahren einsetzbaren Schmelzmassen enthalten 7 bis kO Gewichtsteile, vorzugsweise 15 bis 33 Gewichtsteile dieser weitgehend amorphen Polyolefine. Dabei werden die höheren Gewichtsteile innerhalb dieser Bereiche bei solchen Polyolefinen bevorzugt, die durch Molekulargewichte kleiner 0,6 dl/g und/oder ätherlösliche Anteile größer 70 $ gekennzeichnet sind. ,The melt masses which can be used in the process according to the invention contain 7 to 10 parts by weight, preferably 15 to 33 parts by weight, of these largely amorphous polyolefins. The higher parts by weight within these ranges are preferred for those polyolefins which are characterized by molecular weights less than 0.6 dl / g and / or ether-soluble proportions greater than 70 $. ,
Die genannten weitgehend amorphen Polyolefine werden z.B. nach dem Verfahren der US-PS 3 678 023 und der deutschen Patentanmeldung P 23 06 667.3 hergestellt.The above-mentioned largely amorphous polyolefins are produced, for example, by the process of US Pat. No. 3,678,023 and the German patent application P 23 06 667.3 produced.
Für das erfindungsgemäße Verfahren geeignete Polybutenöle sind solche mit Molekulargewichten von 5OO bis 1000 und ViskositätenPolybutene oils suitable for the process according to the invention are those with molecular weights from 500 to 1000 and viscosities
o.O.
von 1000 bis 100 000 cP/20 C, vorzugsweise von 2000 bis 20 cP/20 C, insbesondere von 4000 bis 10 000 cP/20 C. Diese Polybutenöle sollen keine leichtsiedenden Anteile enthalten, diefrom 1000 to 100,000 cP / 20 C, preferably from 2000 to 20 cP / 20 C, in particular from 4000 to 10,000 cP / 20 C. These polybutene oils should not contain any low-boiling components that
409841/0049409841/0049
- 4 - O.Z. 2703 - 4 - OZ 2703
23.3.1973March 23, 1973
unter 100 C bei 15 mm Hg sieden. Bei den Schmelzmassen des beanspruchten Verfahrens werden sie in Mengen von 10 bis 40 Gewichtsteilen, vorzugsweise von 20 bis 30 Gewichtsteilen zugesetzt. Dabei wählt man niedere Anteile, wenn man steife Schmelzmassen herstellen will bzw. wenn weitgehend amorphe Polyolefine mit Molekulargewichten kleiner 0,6 dl/g-und/oder unlöslichem Ätheranteil größer 70 $ eingesetzt werden, und höhere Anteile, wenn man weniger steife, leichter verarbeitbare Schmelzmassen bevorzugt, bzw. wenn man'weitgehend amorphe Polyolefine mit Molekulargewichten größer 0,6 dl/g und/oder unlöslichem Ätheranteil kleiner 70 %> verwendet.boil below 100 C at 15 mm Hg. In the case of the melt masses of the claimed process, they are added in amounts of 10 to 40 parts by weight, preferably 20 to 30 parts by weight. Lower proportions are chosen if one wants to produce stiff enamel masses or if largely amorphous polyolefins with molecular weights less than 0.6 dl / g and / or insoluble ether content greater than 70 $ are used, and higher proportions if less stiff, more easily processable ones are used Melting compounds are preferred, or if largely amorphous polyolefins with molecular weights greater than 0.6 dl / g and / or an insoluble ether content of less than 70 % are used.
Die für das erfindungsgemäße Verfahren geeigneten Polybutenole können z.B. durch Polymerisation von Butenen mit Friedel-Crafts-Katalysatoren gemäß dem Verfahren der DT-OS 2 005 207 hergestellt werden.The polybutenols suitable for the process according to the invention can be prepared, for example, by polymerizing butenes with Friedel-Crafts catalysts produced according to the method of DT-OS 2 005 207 will.
Als Füllstoffe für die Schmelzmassen des erfindungsgemäßen Verfahrens sind zunächst alle für einen solchen Zweck bekannten und gängigen anorganische und mineralische Füllstoffe in Pulverform, d.h. vorzugsweise der Körnung =0,09 nun, geeignet. Vorzugsweise werden als Füllstoffe Kieselsäure, Graphit und Sulfate, Carbonate und Silikate der wichtigsten Elemente der 1. bis 3» Hauptgruppe des Periodischen Systems der Elemente, wie z.B. Talkum, Kaolin, Kalk, Kreide, Dolomit, Schwerspat oder Schiefermehl verwendet. Aber auch Elektrofilter-Asche, Quarzmehl, Steinstaub und bituminöse Stoffe können verwendet werden. Den Füllstoffen können gegebenenfalls anorganische und/oder organische Farbstoffe zugesetzt werden, um der Dachbeschichtung eine bestimmte Farbe zu geben.As fillers for the enamel masses of the process according to the invention are initially all inorganic and mineral fillers known and used for such a purpose in powder form, i.e. preferably of grit = 0.09 now, suitable. Preferably The fillers used are silica, graphite and sulfates, carbonates and silicates of the most important elements of the 1st to 3rd » Main group of the periodic system of the elements, such as talc, kaolin, lime, chalk, dolomite, barite or slate flour used. But also electrostatic precipitator ash, quartz powder, stone dust and bituminous materials can be used. The fillers can optionally contain inorganic and / or organic dyes can be added to give the roof coating a certain To give color.
Die Füllstoffe sind in der Schmelzmasse des 'erfindungsgemäßen Verfahrens mit 30 bis 70, vorzugsweise 35 bis 60, Gewichtsteilen enthalten.The fillers are in the melt of the 'according to the invention Process with 30 to 70, preferably 35 to 60, parts by weight contain.
409841/0049409841/0049
23U75023U750
- 5 -■ O.Z. 2703 - 5 - ■ OZ 2703
23.3.1973March 23, 1973
Der Einsatz von 1 bis 5 $, bezogen auf* die Ge samt mischung, einer hochdispersen Kieselsäure mit niedrigem Schuttgewicht, wie sie z.B. unter der Bezeichnung Aerosil ^.im Handel ist, wird zur Verbesserung der Standfestigkeit der Schmelzmasse, vor allem der mit Kreide gefüllten, bevorzugt.The stake of 1 to 5 $, based on * the total mixture, one highly dispersed silica with low bulk weight, like them e.g. under the name Aerosil ^. is commercially available, is used for Improving the stability of the enamel, above all the one filled with chalk, preferred.
Geeignete trocknende Öle, die den Schmelzmassen der vorliegenden Erfindung gegebenenfalls in Mengen von 1 bis 15 Gewichtsteilen, vorzugsweise von 5 bis 10 Gewichtsteilen, zugesetzt werden können, sind z.B. Polybutadienöle und trocknende Triglyceride, wie z.B. Leinöl. Als Polybutadienöle sind vorzugsweise solche mit Molekulargewichten von I5OO bis 3000, Viskositäten von 750 bis 3OOO cP/20 °C und Jodzahlen zwischen 400 und 5OO g Jod/100 g geeignet, wie sie nach dem Verfahren der DT-PS 1 186 631 hergestellt werden können.Suitable drying oils which the melt masses of the present invention optionally in amounts of 1 to 15 parts by weight, preferably from 5 to 10 parts by weight, added are e.g. polybutadiene oils and drying triglycerides such as linseed oil. As polybutadiene oils are preferred those with molecular weights from 150 to 3000, viscosities from 750 to 3OOO cP / 20 ° C and iodine numbers between 400 and 5OO g iodine / 100 g suitable as they are according to the method of the DT-PS 1 186 631 can be produced.
Den PolybutadienÖlen und den trocknenden Triglyceriden kann zur schnelleren Härtung 0,1 bis 0,2 Gewichtsprozent, bezogen auf das trocknende Triglycerid bzw. das Polybutadienöl, eines Sikkatives, z.B. einer Kobaltverbindung wie Kobaltoctoat oder -naphthenat zugegeben werden. Die trocknende Öle enthaltenden Schmelzmassen härten an der Oberfläche durch oxidative Vernetzung nach, bleiben aber unterhalb der Oberfläche plastisch.The polybutadiene oils and the drying triglycerides can be used for faster hardening 0.1 to 0.2 percent by weight, based on the drying triglyceride or polybutadiene oil, of a siccative, e.g., a cobalt compound such as cobalt octoate or naphthenate. The enamel masses containing drying oils harden on the surface through oxidative crosslinking, but remain plastic below the surface.
Die Schmelzmassen des erfindungsgemäßen Verfahrens zeichnen sich durch eine Haftfestigkeit gegenüber den zur Beschichtung anstehenden Untergründe, wie z.B. aus Beton, Stein, Mauerwerk, Asbestzement, Holz, Metall, Bitumen oder Kunststoff aus, und sie können im Gegensatz zu bekannten heißflüssig zu verarbeitenden bituminösen Schmelzmassen ohne Voranstrich aufgetragen werden. Gegenüber den bekannten lösungsmittelfreien elastischen PoIyurethan-Beschichtungssystemen haben die'vorliegenden Schmelz-The enamel masses of the process according to the invention stand out due to an adhesive strength compared to the pending coating Substrates, such as concrete, stone, masonry, asbestos cement, wood, metal, bitumen or plastic, and you can In contrast to known bituminous melts that are processed in hot liquid form, they can be applied without a primer. Compared to the known solvent-free elastic polyurethane coating systems have the 'present enamel
409841/0049409841/0049
ο.ζ. 2703ο.ζ. 2703
23.3.1973March 23, 1973
massen den Vorteil, daß sie bei der Herstellung so vorgefertigt werden, daß sie auf der Baustelle als witterungsunempfindliche, praktisch feste Einkomponentenmassen mit einer unbegrenzten Gebrauchsdauer angeliefert werden können und außerdem wiederholt aufschmelzbar sind.have the advantage that they are prefabricated during manufacture that they are insensitive to the weather on the construction site, practically solid one-component masses with an unlimited service life can be delivered and can also be melted repeatedly.
Das Auftragen der Schmelzmassen erfolgt im heizgeschmolzenen Zustand entweder durch Aufstreichen mit Bürsten oder durch Aufgießen und anschließendes Verteilen mit Schiebern oder Rakeln oder durch Auf spachteln mit Stahlkellen. Auch ist ein nachträgliches Glätten und/oder Porenschließen mit Stahlglättern nach einem kurzzeitigen Beflammen der Oberfläche möglich.The application of the enamel takes place in the hot melt Condition either by spreading on with brushes or by pouring on and then spreading with sliders or squeegees or by filling with steel trowels. Subsequent smoothing and / or pore closing with steel smoothing tools is also required short-term flaming of the surface is possible.
Zur Dachabdichtung reicht im allgemeinen ein einschichtiger Belag mit einer Schichtdicke von 1 bis h mm aus. Die Schmelzmasse kann jedoch auch mehrschichtig aufgetragen werden. Dabei ist möglich, zur Erhöhung der Zugfestigkeit der Beschichtung auch vorteilhaft zwischen den einzelnen Schichten Gewebe- und/oder Vlies-Verstärkungen aus Natur- und/oder Kunstfasern, wie z.B. aus Jute, Wollfilz, Asbest, Glas, gesättigten Polyestern, Polyamiden, .Polyolefinen oder Tetrafluoräthylen einzuarbeiten. Bevorzugt verwendet man Glasvliese bzw. Glasseidenmatten mit einem Flächen-For roof waterproofing a single layer coating is enough, in general with a layer thickness of 1 from to h mm. However, the enamel can also be applied in several layers. It is possible to increase the tensile strength of the coating also advantageously between the individual layers of fabric and / or fleece reinforcements made of natural and / or synthetic fibers, such as jute, wool felt, asbestos, glass, saturated polyesters, polyamides, polyolefins or tetrafluoroethylene to incorporate. Preference is given to using glass fleece or glass silk mats with a surface
2 22 2
gewicht von 30 bis 900 g/m , insbesondere 50 bis 450 g/m . Außerdem können zwischen den einzelnen Schichten der Schmelzmasse, vor allem zur Erhöhung des Dampffussionswiderstandes, auch 0,01 bis 0,3 nun, vorzugsweise 0,03 bis 0,1 mm dicke geprägte oder ungeprägte Metallfolien, vorzugsweise aus Aluminium oder Kupfer oder 0,05 bis 2,0 mm, vorzugsweise 0,1 bis 1,0 mm dicke Kunststoffolien, z.B. aus Polyolefinen oder Polyvinylchlorid, eingearbeitet werden.weight from 30 to 900 g / m, in particular 50 to 450 g / m. In addition, between the individual layers of the melt, especially to increase the resistance to steam fusing, also 0.01 to 0.3 now, preferably 0.03 to 0.1 mm thick embossed or unembossed metal foils, preferably made of aluminum or copper or 0.05 to 2.0 mm, preferably 0.1 to 1.0 mm thick plastic films, e.g. made of polyolefins or polyvinyl chloride, be incorporated.
Die nach dem erfindungsgemäßen Verfahren herstellbaren Dachbe-Schichtungen können auch mit bekiesten und besplitteten Oberflächenbehandlungen ausgeführt werden. Dabei werden in die The roof coatings which can be produced by the method according to the invention can also be carried out with gravel and gravel surface treatments. The
409841/0049409841/0049
23H75023H750
- 7 - O,Z. 2703 - 7 - O, Z. 2703
23.3.1973March 23, 1973
heißflüssig aufgetragene(η) Schmelzmasse(η) Kies oder Splitt eingestreut. Bevorzugt wird dafür ein Kies mit einem Korndurchmesser von ca. 1 bis-i6 mm, vorzugsweise von 1 bis 8 mm und ein Splitt, vorzugsweise Schiefersplitt, mit ca. 1 bis 16 mm, vorzugsweise 1 bis 3 nun Kornabmessung eingesetzt. Im kalten Zustand der Beschichtung ist dann der Kies oder der Splitt dichtschließend und aufgrund der guten Klebkraft und Dauerelastizität der Schmelzmassen festhaftend und auch bei Kälte ohne Versprödungserscheinungen eingebettet.hot liquid applied (η) melt (η) gravel or chippings interspersed. A gravel with a grain diameter of approximately 1 to 16 mm, preferably 1 to 8 mm, and a gravel are preferred Chippings, preferably slate chippings, with about 1 to 16 mm, preferably 1 to 3 now used grain size. When cold the coating is then the gravel or the chippings tightly and due to the good adhesive strength and permanent elasticity of the Enamel masses firmly adhering and embedded without any signs of embrittlement even in the cold.
Das erfindungsgemäße Verfahren soll durch die nachfolgend aufgeführten Beispiele erläutert werden.The method of the invention is intended to be carried out by those listed below Examples are explained.
Beispiel 1 ■ Example 1 ■
Eine Masse aus 30 Gewichtsteilen eines weitgehend amorphen Polybuten-1 mit einem RSV-Wert von 0,5 dl/g (Molekulargewicht 132 000) und einem ätherlöslichen Anteil von 67 $, 30 Gewichtsteilen eines Polybutenöles mit einem Molekulargewicht von 69O,und einer Viskosität von 43ΟΟ cP/20 C, das keine leichtsiedendenden Anteile enthält, die unterhalb I50 C bei 15 mm Hg sieden, und kO Gewichtsteilen Talkum werden an der Verarbeitungsstelle in einem aus der Bauindustrie bekannten Kocher mit Gas-, Kohle- oder sonstiger Feuerung und Rührwerk gemischt und bei Temperaturen von 150 bis 240 C zu einer gieß- und/oder streichfähigen Masse geschmolzen. Anschließend wird die Masse im heißflüssigen Zustand ohne Voranstrich auf die abzudichtende Fläche aus Beton aufgegossen und mit Schiebern verteilt oder mit Bürsten aufgetragen. Im erkalteten Zustand erhält man einen dichten, homogenen und elastoplastischen Dachbelag, der sich durch eine gute Haftung auszeichnet.A mass of 30 parts by weight of a largely amorphous polybutene-1 with an RSV value of 0.5 dl / g (molecular weight 132,000) and an ether-soluble fraction of $ 67, 30 parts by weight of a polybutene oil with a molecular weight of 69O, and a viscosity of 43ΟΟ cP / 20 C, which does not contain any low-boiling components that boil below 150 C at 15 mm Hg, and kO parts by weight of talc are mixed and mixed at the processing point in a cooker known from the construction industry with gas, coal or other furnace and agitator melted at temperatures of 150 to 240 C to form a pourable and / or spreadable mass. Then the mass is poured in the hot liquid state without primer onto the concrete surface to be sealed and spread with sliders or applied with brushes. When cooled, a dense, homogeneous and elastoplastic roof covering is obtained, which is characterized by good adhesion.
409841/0049409841/0049
23U75023U750
- 8 - - O. Z. 2703 - 8 - - OZ 2703
23.3.1973March 23, 1973
Eine Schmelzmasse aus 25 Gewichtsteilen eines weitgehend amorphen Buten-1-Propylen-Copolymeren, das etwa 12 $ Propylen enthält, mit einem RSV-Wert von 0,6 dl/g und einem ätherlöslichen Anteil von 91 $» 2.k Gewi ent st eil en eines Polybutenöles mit einem Molekulargewicht von 7^0, einer Viskosität von 12 400 cP/20 °C und einem Leichtsiederanteil von kleiner 0,1 ^ und 51 Gewichtsteilen Talkum wird bei einer Temperatur von 200 bis 220 C durch Spachteln mit Stahlkellen auf einer trockenen Dachfläche aus den nachfolgend aufgeführten Materialien aufgetragen. Anschließend wird die Oberfläche durch ein kurzzeitiges Beflammen der Oberfläche geglättet. Hierbei werden gegebenenfalls vorhandene Poren geschlossen. Die Haftung der Masse auf Beton, Stein, Mauerwerk, Holz, Metall, Bitumen und Kunststoffen ist so gut, daß kein Voranstrich erforderlich ist. Die Masse ist gegen Flugfeuer und strahlende Wärme widerstandsfähig. Sie erfüllt die Forderungen der DIN 41O2. ' A melt mass of 25 parts by weight of a largely amorphous butene-1-propylene copolymer, which contains about 12 $ propylene, with an RSV value of 0.6 dl / g and an ether-soluble fraction of 91 $ » 2.k parts by weight en a polybutene oil with a molecular weight of 7 ^ 0, a viscosity of 12 400 cP / 20 ° C and a low boiler content of less than 0.1 ^ and 51 parts by weight of talc is at a temperature of 200 to 220 C by spatula with steel trowels on a dry Roof surface made from the materials listed below. The surface is then smoothed by briefly applying a flame to the surface. Any pores that may be present are closed here. The adhesion of the compound to concrete, stone, masonry, wood, metal, bitumen and plastics is so good that no primer is required. The mass is resistant to flying sparks and radiant heat. It meets the requirements of DIN 41O2. '
Zur Herstellung von bekiesten oder besplitteten Oberflächen von Dachbelägen wird sofort nach der Herstellung der Dachabdeckung Kies oder Splitt in die noch heiße Schmelzmasse eingestreut.For the production of gravel or split surfaces of roof coverings immediately after the production of the roof cover Gravel or grit sprinkled into the hot melt.
Eine Schmelzmasse aus 30 Gewichtsteilen eines weitgehend ataktischen Polybuten-1 mit einem RSV-Wert von 0,7 dl/g und einem ätherlöslichen Anteil von Jk $, 25 Gewichtsteilen eines Polybutenöles mit einem Molekulargewicht von 810 und einer Viskosität von 65 700 cP/20 °C, das keine leichtsiedenden Anteile enthält, die unterhalb 150 C bei I5 mm Hg sieden, kO Gewichtsteilen Kreide und 5 Gewichtsteilen Leinöl, das 0,01 Gewichtsteile Ko-A melt of 30 parts by weight of a largely atactic polybutene-1 with an RSV value of 0.7 dl / g and an ether-soluble fraction of Jk $, 25 parts by weight of a polybutene oil with a molecular weight of 810 and a viscosity of 65,700 cP / 20 ° C, which does not contain any low-boiling components that boil below 150 C at 15 mm Hg, kO parts by weight of chalk and 5 parts by weight of linseed oil, which is 0.01 parts by weight of
409841/0049409841/0049
-9 - ο.ζ. 2703 -9 - ο.ζ. 2703
23.3.1973March 23, 1973
baltoctoat enthält, -wird bei einer Temperatur von 180 bis 200 C durch Spachteln mit Stahlkellen auf einer trockenen Dachfläche aufgetragen. Anschließend wird die Oberfläche geglättet. Im erkalteten Zustand erhält man einen homogenen, porenfreien und plastischelastischen Dachbelag, der an der Oberfläche nach mehreren Tagen erhärtet. Unter der Oberfläche bleibt die Masse weich.Contains baltoctoate, -will at a temperature of 180 to 200 C applied by troweling with steel trowels on a dry roof surface. The surface is then smoothed. In the cold State you get a homogeneous, pore-free and plastically elastic roof covering, which on the surface after several Days hardened. The mass remains soft beneath the surface.
Man erhält einen vergleichbaren Dachbelag, wenn man anstelle von hO Gewichtsteilen Kreide 40 Gewichtsteile Kaolin einsetzt.A comparable roof covering is obtained if 40 parts by weight of kaolin are used instead of 50 parts by weight of chalk.
Zur Herstellung eines an der Luft härtenden Dachbelages kann man anstelle der 5 Gewichtsteile Leinöl auch 5 Gewichtsteile eines Polybutadienöles der genannten Spezifikation- einsetzen.For the production of a roof covering that cures in the air can instead of the 5 parts by weight of linseed oil, 5 parts by weight of a polybutadiene oil of the specified specification are also used.
Setzt man der Masse zusätzlich 0,5 Gewichtsteile Ultramarinblau zu, so erhält man einen blauen Dachbelag.If an additional 0.5 part by weight of ultramarine blue is added to the mass, a blue roof covering is obtained.
Eine Schmelzmasse aus 30 Gewichtsteilen eines weitgehend ataktischen Polybuten-1 mit einem RSV-¥ert von 0,7 dl/g und einem ätherlöslichen Anteil von 7^ $» 30 Gewichtsteilen eines PoIybutenöles mit einem Molekulargewicht von 810 und einer Viskosität von 65 7OO op/20 C, das keine leichtsiedenden Anteile enthält, die unterhalb 15Ο C bei 15 nun Hg sieden, 10 Gewicht steilen Bitumen B 200 und 30 Gewichtsteilen Kaolin wird bei einer Temperatur von I80 bis 200 C zu einer spachtelfähigen Masse geschmolzen. Dann wird die Dachhaut aus der aufgeschmolzenen Polyolefinmasse in einem oder mehreren Aufzügen mit Kellen gleichmäßig aufgetragen und anschließend die Oberfläche der so hergestellten Dichtungsschicht mit einer Lötlampe, Propan- oder Acetylenflamme vorsichtig durch Erwärmen wieder angeschmolzen und mit Stahlkellen sämtliche verbliebenen Poren geschlossen und die gesamte Fläche geglättet. Im erkalteten Zustand erhält man eine porenfreie, homogene und elastoplastische Dichtschicht, die auch an steilen und senkrechten Flächen unter starker Sonnenbestrahlung oder Wärmeeinwirkung noch ein gutes Standvermögen hat,An enamel mass of 30 parts by weight of a largely atactic one Polybutene-1 with an RSV- ¥ ert of 0.7 dl / g and an ether-soluble fraction of 7% 30 parts by weight of a polybutene oil with a molecular weight of 810 and a viscosity of 65 7OO op / 20 C, which does not contain any low-boiling components, which boil below 15Ο C at 15 now Hg, 10 weight steep Bitumen B 200 and 30 parts by weight of kaolin is used in one Temperature of 180 to 200 C to a level that can be troweled melted. Then the roof skin is melted from the Polyolefin mass in one or more elevators with trowels evenly applied and then the surface of the sealing layer produced in this way with a blowtorch, propane or Acetylene flame carefully melted again by heating and all remaining pores are closed with steel trowels and the entire surface is smoothed. Receives when cold a pore-free, homogeneous and elastoplastic sealing layer that can also be used on steep and vertical surfaces under strong sunlight or heat exposure still has good stability,
409841/0049409841/0049
2.3 TA 75 O2.3 TA 75 O
- 10 - O.Z. 2703 - 10 - OZ 2703
. 23.3.1973. March 23, 1973
Beispiel 5 - . . Example 5 -. .
Eine Masse, die nach Beispiel 1 zusammengesetzt und durch Erhitzen und Rühren zu einer streichfähigen Masse aufbereitet , ist, wird im heißflüssigen Zustand auf die abzudichtende Fläche durch Aufstreichen mit Bürsten oder durch Aufgießen und Verteilen mit Schiebern aufgetragen und in die noch nicht erstarrte Masse eine Lage Glasseidenmatten mit einem Flächengewicht von ^50 g/m eingelegt. Danach wird auf die eingebettete Glasfaserschicht ein Deckanstrich aus der vorgenannten Masse aufgetragen. Im erkalteten Zustand erhält man einen mit Glasfasern verstärkten, nahtlosen, dichten, homogenen und elastoplastischen Dachbelag. A mass composed according to Example 1 and heated by heating and stirring prepared to a spreadable mass, is, in the hot liquid state on the surface to be sealed by brushing on with a brush or by pouring on and spreading applied with sliders and in the not yet solidified mass a layer of glass silk mats with a weight per unit area of ^ 50 g / m inserted. Then it is applied to the embedded fiberglass layer a top coat made of the above compound is applied. When cold, you get a glass fiber reinforced, seamless, dense, homogeneous and elastoplastic roof covering.
Werden anstelle von Glasseidenmatten Glasvliese und/oder Glasfasergewebe eingelegt und/oder im Faserspritzverfahren Glasfasern eingebettet, so erhält man vergleichbare Ergebnisse.Instead of glass silk mats, glass fleece and / or glass fiber fabric are used If glass fibers are inserted and / or embedded in the fiber spraying process, comparable results are obtained.
Zur weiteren Erhöhung der Zugfestigkeit des Dachbelages können die Glasfasereinlagen auch mehrlagig mit je einer Zwischenschicht aus Polyolefin-Schmelzmassen ausgeführt werden.To further increase the tensile strength of the roof covering you can the fiberglass inlays also have multiple layers, each with an intermediate layer are made from polyolefin melts.
Eine Masse, die nach Beispiel 1 zusammengesetzt und durch Erhitzen und Rühren zu einer streichfähigen Masse aufbereitet ist, wird im heißflüssigen Zustand auf die abzudichtende Fläche durch Aufstreichen mit Bürsten oder durch Aufgießen und Verteilen mit Schiebern aufgetragen und in die noch nicht erstarrte Masse eine Lage Aluminiumfolie mit d = 0,035 n™ Dicke eingelegt und eingedrückt und/oder eingewalzt. Danach wird auf die Aluminiumfolie ein Deckanstrich aus der vorgenannten Masse aufgetragen. Im erkalteten Zustand erhält man eine Dachabdichtung mit einem um u · d = ca. 700 000 · O,Q35 mm. = ca. 2^,5 m erhöhten Wasserdampffusionswiderstand.A mass composed according to Example 1 and heated by heating and stirring is prepared to a spreadable mass, is in the hot liquid state on the surface to be sealed applied by brushing on or by pouring on and spreading with sliders and into which it has not yet solidified A layer of aluminum foil with d = 0.035 n ™ thickness is inserted and pressed in and / or rolled in. Then it is applied to the aluminum foil a top coat made of the above compound is applied. A roof seal is obtained when it has cooled down with around u · d = approx. 700,000 · O, Q35 mm. = about 2 ^, 5 m raised Water vapor fusion resistance.
4 0 9 8 4 1 / Q 04 0 9 8 4 1 / Q 0
23H75023H750
- 11 - O.Z. 2703 - 11 - OZ 2703
23.3.1973March 23, 1973
¥ird anstelle von Aluminiumfolie Kupferiölie eingebaut oder wenn man dickere Metallfolien verwendet, so erhält man noch höhere Wasserdampffusionswiderstandswerte.¥ ¥ ¥ ¥ Is built in copper oil instead of aluminum foil or if if thicker metal foils are used, even higher water vapor fusion resistance values are obtained.
Wird anstelle einer Metallfolie eine Kunststoff-Folie eingebaut, so erhöht sich der Wasserdampffusionswiderstand geringer.If a plastic film is installed instead of a metal film, the resistance to water vapor fusion increases less.
Bei einer Beschichtung, die nach Beispiel 1, 2, 3» ^f 5 oder 6 aufgetragen ist, wird in die noch nicht erstarrte obere Polyolefin schmelzma ssen schicht trockener Kies mit einem Korndurchmesser von 1 bis k mm dichtschließend eingestreut. Nach dem Erstarren der Polyolefinschmelzmasse wird der lose verbleibende Kies abgefegt. Dann erhält man einen porenfreien, homogenen und elastoplastischen Dachbelag, in dem das Bestreuungsgut etwa bis zur Hälfte der Korngröße in der Polyolefinschmelzmasse dichtschließend und festhaftend, das ohne Ausführung eines eventuellen Walzvorganges.-erreicht wird, eingebettet ist.In the case of a coating applied according to Example 1, 2, 3, 5 or 6, dry gravel with a grain diameter of 1 to k mm is sprinkled tightly into the not yet solidified upper polyolefin schmelzma ssen layer. After the polyolefin melt has solidified, the loosely remaining gravel is swept away. Then a pore-free, homogeneous and elastoplastic roof covering is obtained, in which the material to be sprinkled is embedded tightly and firmly adhering to about half the grain size in the polyolefin melt, which is achieved without performing any rolling process.
Wird anstelle von Kies trockener Schiefersplitt der Körnung 1 bis 3 mm eingestreut, so erhält man ein vergleichbares Ergebnis.Instead of gravel, dry slate chippings of grain size 1 interspersed up to 3 mm, a comparable result is obtained.
409841/Q(Kä409841 / Q (Kä
Claims (8)