DE20107742U1 - Natural stone dummy - Google Patents
Natural stone dummyInfo
- Publication number
- DE20107742U1 DE20107742U1 DE20107742U DE20107742U DE20107742U1 DE 20107742 U1 DE20107742 U1 DE 20107742U1 DE 20107742 U DE20107742 U DE 20107742U DE 20107742 U DE20107742 U DE 20107742U DE 20107742 U1 DE20107742 U1 DE 20107742U1
- Authority
- DE
- Germany
- Prior art keywords
- natural stone
- dummy according
- dummy
- facing layer
- chippings
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
NatursteinattrappeNatural stone dummy
Die Erfindung betrifft eine Natursteinattrappe, bestehend aus einem Träger, insbesondere aus Kernbeton und einer wasserundurchlässigen Vorsatzschicht aus zementgebundenem Natursteinsplitt.The invention relates to a natural stone dummy, consisting of a carrier, in particular of core concrete, and a water-impermeable facing layer of cement-bonded natural stone chippings.
In historischen Altstädten weit verbreitet sind Flächenbefestigungen aus sogenannten Krustenplatten, die einstückig aus Granit oder aus festem Naturstein bestehen, mit unterschiedlichen Abmessungen und planebenen Oberflächen, jedoch bruchrauhen, gewölbten Unterseiten.Widely used in historic old towns are surface paving made of so-called crust plates, which consist of a single piece of granite or solid natural stone, with different dimensions and flat surfaces, but with rough, curved undersides.
Da es sich bei dem verwendeten Material um sehr alte Baustoffe handelt, ist die Neubeschaffung aus einigen Vorkommen, z. B. Arnsdorfer Granit, nicht oder nur mit sehr hohen Kosten möglich, da die Vorkommen sich erschöpfen. Ein weiterer Nachteil der Krustenplatten ist die unterschiedliche Plattenstärke aufgrund der gewölbten Plattenunterseite, so daß jede Platte einzeln durch Grabungen auf Verlegehöhe gebracht werden muß.Since the material used is very old, it is not possible to purchase new ones from some deposits, such as Arnsdorf granite, or only at great expense, as the deposits are depleted. Another disadvantage of the crust plates is the varying plate thickness due to the curved underside of the plate, so that each plate has to be individually excavated to the laying height.
Aus dem Stand der Technik sind eine Reihe von Lösungen bekannt, bei denen auf einer tragfähigen Schicht, z. B. aus Beton, eine dekorativen Zwecken dienende Deck- oder Vorsatzschicht aufgebracht ist.A number of solutions are known from the state of the art in which a covering or facing layer serving decorative purposes is applied to a load-bearing layer, e.g. made of concrete.
So ist aus der DE 198 35 298 Al ein Schichtaufbau für mehrschichtige wasserdurchlässige Formelemente und Flächengebilde bekannt, der aus einer Tragschicht auf der Basis von wasserdurchlässigem hydraulisch gebundenem Polymerbeton aus zerkleinerten hochpolymeren Abfällen und einer Deckschicht aus hydraulisch gebundenen mineralischen Stoffen besteht, dadurch gekennzeichnet, dass die hydraulische Bindung der hochpolymeren Abfälle der Tragschicht durch Beigabe von wässriger Natriumsilikatlösung und/oder Tensidlösung verbessert ist, und dass die Deckschicht aus hydraulisch gebundenen Zuschlagstoffen mit einem Komgxößenbereich von 2 bis 11 mm besteht und eine Schichtdicke vom 1,5- bis 2-fachen der verwendeten maximalen Korngröße d aufweist. Der Erfindung liegt die Aufgabe zugrunde, einen kostengünstigen und mit einfachen Mitteln herstellbaren Schichtaufbau für mehrschichtige wasserdurchlässigeFor example, DE 198 35 298 A1 discloses a layer structure for multi-layered water-permeable molded elements and surface structures, which consists of a base layer based on water-permeable hydraulically bound polymer concrete made from crushed high-polymer waste and a covering layer made of hydraulically bound mineral materials, characterized in that the hydraulic binding of the high-polymer waste of the base layer is improved by adding aqueous sodium silicate solution and/or surfactant solution, and that the covering layer consists of hydraulically bound aggregates with a grain size range of 2 to 11 mm and has a layer thickness of 1.5 to 2 times the maximum grain size d used. The invention is based on the object of providing a cost-effective layer structure for multi-layered water-permeable
Formelemente und Flächengebilde zu entwickeln, dessen Tragschicht auf der Basis von wasserdurchlässigem hydraulisch gebundenem Polymerbeton aus zerkleinerten hochpolymeren Abfällen mit einer wasserdurchlässigen, verschleißarmen, beständigen und optisch ansprechenden Deckschicht aus hydraulisch gebundenen mineralischen Stoffen verbunden ist. Das erfindungsgemäße Formelement ist vollständig wasserdurchlässig, besitzt eine verschleißfeste und widerstandsfähige Oberfläche und eine gute Haltbarkeit und Beständigkeit.To develop molded elements and surface structures whose base layer based on water-permeable, hydraulically bound polymer concrete made from crushed high-polymer waste is combined with a water-permeable, low-wear, durable and visually appealing top layer made of hydraulically bound mineral materials. The molded element according to the invention is completely water-permeable, has a wear-resistant and resilient surface and good durability and resistance.
Aus der DE 199 44 593 Al bekannt sind Bauelemente zum Belegen von festen und losen, insbesondere sandigen Flächen, dadurch gekennzeichnet, dass sie wenigstens teilweise aus einem mit einem Reaktionsharz gebundenen, eingefärbten Quarz (Coloritquarz) oder einer Mischung aus einem solchen Coloritquarz mit ungefärbtem Naturgestein hergestellt sind, wobei der Coloritquarz und gegebenenfalls das Naturgestein eine Korngröße von 0,1 mm bis 8 mm aufweist und die Körner des Coloritquarzes mit einer Schicht umhüllt sind, die aus Reaktionsharzen auf der Basis von Wasserglas, Ein- oder Zweikomponenten-Polyurethan, Einkomponenten-Acryl oder Zweikomponenten-Epoxid unter Zugabe von Farbmitteln (Pigmente, Pigmentfarbstoffe, Farbstoffe, Metallicpigmente) in nahezu beliebigen Farben besteht. Der Erfindung liegt die Aufgabe zugrunde, Bauelemente der eingangs erwähnten Art anzugeben, die mit zahlreichen Dekorfarben versehen sind und die je nach Bedarf mit guter Wasserdurchlässigkeit oder auch mit völliger Wasserundurchlässigkeit herstellbar sind. Die mit der Erfindung erzielten Vorteile bestehen insbesondere darin, dass die Bauelemente nach freier Wahl mit zahlreichen Dekorfarben versehen werden können, wobei auch auf der Oberfläche jedes einzelnen Bauelementes verschiedene Farbmuster darstellbar sind. Ferner können je nach Wunsch oder Bedarf Bauelemente mit guter Wasserdurchlässigkeit oder auch mit völliger Wasserundurchlässigkeit hergestellt werden, was auf einfache Weise durch entsprechende Wahl der Korngröße und des Prozentsatzes des zugesetzten Bindemittels erreicht werden kann.DE 199 44 593 A1 discloses building elements for covering solid and loose, particularly sandy surfaces, characterized in that they are made at least partially from a colored quartz (colored quartz) bound with a reaction resin or a mixture of such a colored quartz with uncolored natural stone, the colored quartz and optionally the natural stone having a grain size of 0.1 mm to 8 mm and the grains of the colored quartz being coated with a layer consisting of reaction resins based on water glass, one- or two-component polyurethane, one-component acrylic or two-component epoxy with the addition of colorants (pigments, pigment dyes, dyes, metallic pigments) in almost any color. The invention is based on the object of specifying building elements of the type mentioned at the beginning, which are provided with numerous decorative colors and which can be produced with good water permeability or also with complete water impermeability as required. The advantages achieved with the invention are in particular that the building elements can be provided with a wide range of decorative colors, whereby different color patterns can also be displayed on the surface of each individual building element. Furthermore, depending on the desire or requirement, building elements can be produced with good water permeability or even with complete water impermeability, which can be achieved in a simple manner by appropriately selecting the grain size and the percentage of the binder added.
Aus DE 197 44 834 Al bekannt ist ein Verfahren zur Herstellung und Verwendung eines rutschfesten und/oder dekorativen Einlegelements, bestehend aus einem organischen sowie anorganischen Bindemittel- System, dadurch gekennzeichnet, dass manFrom DE 197 44 834 Al a method is known for the production and use of a non-slip and/or decorative insert element, consisting of an organic and inorganic binder system, characterized in that
eine fließ- oder spachtelfähige, maschinell verarbeitbare Einlegelement-Masse herstellt, in der man rutschfeste und/oder dekorative Partikel wie Korund, Siliciumcarbit, Glimmer, Glitter, Pigmente, Thixotropiemittel, sowie Trennmittel und Entschäumer einsetzt. Die so hergestellten rutschfesten/dekorativen Einlegelemente werden in einem noch nicht ausgehärteten appliziertem Beschichtungs-System und/oder einer Belagsmasse und/oder in einem Halbfabrikat-Teil eingelegt. Nach der Aushärtung im Verbund mit der Beschichtungs- oder Belags-Masse oder dem Halbfabrikat-Teil, erhält man so auf mineralische und/oder metallische Untergründe einen rutschfesten und/oder dekorativen hochbelastbaren Bodenbelag von besonders langer Lebensdauer. Aufgabe der vorliegenden Erfindung ist es, ein neuartiges rutschfestes/dekoratives Einlegelement von gleichbleibender Form, Größe, Grad der Rutschfestigkeit und dekorativer Vielfalt mit gleichbleibender Qualität zuschaffen, das eine porenfreie rutschfeste/dekorative Oberfläche ergibt. Die Einlegelemente sind beständig gegen chemische und mechanische Beanspruchungen, so dass sie die beschichteten Oberflächen in Kfz-Betrieben, Nassbetrieben, auf Gehwegbereichen, Treppentrittflächen, Betonfahrbahnen und Bitumenoberflächen sicher vor rutschempfindlichen Eigenschaften schützen. Gemäß der Erfindung lässt sich somit ein Beschichtungs- und/oder Belags-Aufbau in Kombination mit dem Einlegelement herstellen, wobei in nur einem oder mehreren Auftragsschichten beliebig starke Schichtstärken erzielt werden. Die in der Beschichtungs- und/oder Belags-Masse eingelegten Einlegelemente, sind gleichmäßig hinsichtlich der Rutschfestigkeit und dekorativen Vielfalt. Besonders beständig sind diese gegen Abrieb und chemische Belastungen von Säuren und Laugen.a flowable or trowelable, machine-processable inlay element mass is produced, in which non-slip and/or decorative particles such as corundum, silicon carbide, mica, glitter, pigments, thixotropic agents, as well as release agents and defoamers are used. The non-slip/decorative inlay elements produced in this way are inserted into an applied coating system and/or a covering mass that has not yet hardened and/or into a semi-finished part. After hardening in combination with the coating or covering mass or the semi-finished part, a non-slip and/or decorative, highly resilient floor covering with a particularly long service life is obtained on mineral and/or metallic substrates. The object of the present invention is to create a novel non-slip/decorative inlay element of consistent shape, size, degree of slip resistance and decorative variety with consistent quality, which results in a pore-free non-slip/decorative surface. The insert elements are resistant to chemical and mechanical stress, meaning that they reliably protect the coated surfaces in car workshops, wet areas, on sidewalks, stair treads, concrete roadways and bitumen surfaces from slip-sensitive properties. According to the invention, a coating and/or covering structure can be produced in combination with the insert element, whereby any desired layer thickness can be achieved in just one or more applied layers. The insert elements inserted in the coating and/or covering mass are uniform in terms of slip resistance and decorative variety. They are particularly resistant to abrasion and chemical stress from acids and alkalis.
Aus DE 43 24 190 Al bekannt ist ein Kunststein, insbesondere Kunststeinplatte für Radwege, bestehend aus mindestens einem ausgehärteten Bindemittel und mindestens einem dem Bindemittel beigemischten Zusatzstoff, dadurch gekennzeichnet, dass der Kunststein aus einer Deckschicht und mindestens einer fest mit der Deckschicht verbundenen Tragschicht besteht und dass das Bindemittel der Deckschicht ein Kunstharz, insbesondere ein Acryl- oder Polyesterharz ist, dem als Zusatzstoffe Altglaspartikel und ein Farbstoff beigemischt sind. Aufgabe der Erfindung ist es, einen gattungsgemäßen Kunststein zu bilden, dessen Oberfläche eine hohe Verschleiß- und Abriebfestigkeit sowie eine leuchtende und gut sichtbare Signalfarbe aufweist und dessen Materialeigen-From DE 43 24 190 Al, an artificial stone is known, in particular an artificial stone slab for cycle paths, consisting of at least one hardened binding agent and at least one additive mixed into the binding agent, characterized in that the artificial stone consists of a covering layer and at least one base layer firmly connected to the covering layer and that the binding agent of the covering layer is a synthetic resin, in particular an acrylic or polyester resin, to which waste glass particles and a dye are mixed as additives. The object of the invention is to form a generic artificial stone whose surface has a high wear and abrasion resistance as well as a bright and clearly visible signal color and whose material properties
schäften wie Härte und Dichte in weiten Bereichen variierbar sind, wobei bei der Herstellung des Kunststeines ein möglichst großer Altstoff-Anteil verwendet wird. Durch die Ausbildung des Kunststeines in zwei unterschiedlichen Schichten lassen sich die Materialeigenschaften des Kunststeines in weiten Bereichen variieren, wobei die notwendigen Eigenschaften seiner Oberfläche, nämlich die ausreichend hohe Verschleiß- und Abriebsfestigkeit sowie die markante Farbgebung lediglich von der Deckschicht erfüllt werden müssen.Properties such as hardness and density can be varied over a wide range, with the greatest possible proportion of recycled material being used in the manufacture of the artificial stone. By forming the artificial stone in two different layers, the material properties of the artificial stone can be varied over a wide range, with the necessary properties of its surface, namely sufficiently high wear and abrasion resistance and the striking coloring, only having to be fulfilled by the top layer.
Aus DE 41 34 296 Cl bekannt ist eine Verbundsteinplatte aus wenigstens zwei im verlegten Zustand übereinander angeordneten, im wesentlichen ganzflächig miteinander verbundenen Schichten, wobei die obere Schicht von einem Naturstein und die untere Schicht von einer Betonschicht gebildet ist, dadurch gekennzeichnet, daß die groben Zuschlagstoffe der Betonschicht durch kantig geformten Splitt aus dem gleichen Natursteinmaterial wie die obere Schicht gebildet sind. Der Erfindung liegt die Aufgabe zugrunde, eine Verbundsteinplatte der eingangs genannten Art zu schaffen, bei der das Auftreten von Spannungen zwischen der oberen Schicht aus Naturstein und der unteren aus Beton bestehenden Schicht vermindert wird. Der durch die Erfindung erreichte Fortschritt beruht im wesentlichen darauf, daß durch den kantig geformten Split ein höherer Anteil dieser Zuschlagstoffe gegenüber Kies im Beton erreicht wird, so dass der Anteil an Zement verringert werden kann. Dadurch tritt beim Abbinden des Betons ein deutlich geringerer Schwund ein, wodurch auch mögliche Spannungen kleiner gehalten werden.DE 41 34 296 Cl discloses a composite stone slab made of at least two layers arranged one above the other when laid and connected to one another essentially over the entire surface, the upper layer being made of a natural stone and the lower layer being made of a concrete layer, characterized in that the coarse aggregates of the concrete layer are made of angularly shaped chippings made of the same natural stone material as the upper layer. The invention is based on the object of creating a composite stone slab of the type mentioned at the beginning, in which the occurrence of tensions between the upper layer made of natural stone and the lower layer made of concrete is reduced. The progress achieved by the invention is based essentially on the fact that the angularly shaped chippings achieve a higher proportion of these aggregates in the concrete compared to gravel, so that the proportion of cement can be reduced. As a result, there is significantly less shrinkage when the concrete sets, which also keeps possible tensions lower.
Aufgrund der begrenzten Vorkommen an Natursteinen in den erforderlichen Dimensionen sind die vorgeschlagenen Lösungen nicht geeignet für die Herstellung von Ersatzoder Austauschplatten, die sowohl mechanisch hoch belastbar, insbesondere befahrbar und witterungsresistent sein müssen und zum anderen den qualifizierten Forderungen des Denkmalschutzes genügen.Due to the limited availability of natural stone in the required dimensions, the proposed solutions are not suitable for the production of replacement or exchange slabs, which must be highly mechanically resilient, in particular trafficable and weather-resistant, and on the other hand meet the qualified requirements of monument protection.
Der Erfindung liegt daher die Aufgabe zugrunde, einen kostengünstigen und dauerhaften Ersatz für Krustenplatten und andere, mechanisch belastbare, insbesondere befahrbare Platten oder Formkörper unter besonderer Berücksichtigung denkmalpflegerischerThe invention is therefore based on the object of providing a cost-effective and durable replacement for crust plates and other mechanically resilient, in particular drivable plates or molded bodies, with particular consideration of monument conservation
Aspekte zu schaffen. In die Aufgabenstellung eingeschlossen ist die annähernde Farbgleichheit mit den Originalen, die schnelle Verlegbarkeit durch parallele und höhengleiche Platten oder Formkörper und die Rutschsicherheit der Oberfläche auch bei Nässe.The task includes the approximate color match with the originals, the quick installation through parallel and level panels or molded bodies and the slip resistance of the surface even when wet.
Erfindungsgemäß wird die Aufgabe gelöst durch eine mechanisch belastbare, insbesondere befahrbare Natursteinattrappe, die aus einem Träger aus Beton und einer mit ihm unlösbar verbundenen, wasserundurchlässigen Vorsatzschicht aus einem Bindemittel und Natursteinsplitt besteht. Die Natursteinattrappe wird hergestellt, indem auf den in der Regel plattenförmigen Träger aus noch nicht ausgehärtetem Kernbeton eine Vorsatzschicht aus Natursteinsplitt, gemischt mit Zement als Bindemittel, aufgebracht wird und beide Schichten gemeinsam gepresst und gerüttelt werden. Durch den Pressdruck, der vorzugsweise durch ein von oben wirkendes Presswerkzeug übertragen wird, wird zugleich die Oberflächenformung vorgenommen, wodurch die Natursteinattrappe eine planebene Oberfläche und gefaste Kanten erhält.According to the invention, the object is achieved by a mechanically resilient, in particular drivable, natural stone dummy, which consists of a concrete support and a water-impermeable facing layer made of a binding agent and natural stone chippings that is permanently connected to it. The natural stone dummy is produced by applying a facing layer made of natural stone chippings, mixed with cement as a binding agent, to the usually plate-shaped support made of core concrete that has not yet hardened, and pressing and vibrating both layers together. The pressing pressure, which is preferably transmitted by a pressing tool acting from above, simultaneously shapes the surface, giving the natural stone dummy a flat surface and bevelled edges.
Nach erfolgter Pressung wird die noch nicht vollständig abgebundene Natursteinattrappe vorzugsweise mittels oszillierendem Wasserstrahl an der Oberfläche der Vorsatzschicht behandelt. Hierdurch werden Bindemittel und Feinbestandteile bis etwa zur halben Höhe der Natursteinkörnung ausgewaschen, so dass nach erfolgtem Abbinden des Betons an der Plattenoberfläche reiner Natursteinbelag sichtbar ist.After pressing, the not yet fully set natural stone dummy is preferably treated with an oscillating water jet on the surface of the facing layer. This washes out binding agents and fine particles up to about half the height of the natural stone grain, so that after the concrete has set, pure natural stone covering is visible on the surface of the slab.
Bei Bedarf kann in der Vorsatzschicht mittels Zugabe von Färbemitteln in der Farbe des verwendeten Natursteins ein Grauschleier durch das Bindemittel überdeckt werden bzw. bei Verwendung von hellem Naturstein - z. B. Granit/grau - die gesamte Plattenoberfläche in jeder beliebigen Farbe gestaltet werden.If required, a grey haze can be covered by the binding agent in the facing layer by adding colouring agents in the colour of the natural stone used, or if light natural stone is used - e.g. granite/grey - the entire surface of the panel can be designed in any colour.
Durch die Wahl verschieden starker Natursteinkörnungen bestehen weitere Gestaltungsmöglichkeiten; dazu muss die Wasserstrahlintensität der Körnung angepasst werden. Beim Einsatz von verschiedenfarbigem Natursteinsplitt entstehen vorteilhaft weitere Dekorvarianten.By choosing different grain sizes of natural stone, there are further design options; the water jet intensity must be adjusted to the grain size. Using different colored natural stone chippings creates additional decorative options.
Die Verlegung der plattenförmigen Natursteinattrappen erfolgt analog zu Betonsteinpflaster auf abgezogenem Pflasterbett, die Stärke der Platten von ca. 15 cm sichert die Bruchfestigkeit auch bei Befahren mit LKW.The slab-shaped natural stone dummies are laid in the same way as concrete paving stones on a leveled paving bed; the thickness of the slabs of approx. 15 cm ensures that they are resistant to breakage even when driven over by trucks.
Da durch das Wasserstrahlen die Bruchkanten des verwendeten Natursteinsplitts nicht beschädigt werden, ergibt sich nach dem Aushärten der plattenförmigen Natursteinattrappe eine rutschfeste Oberfläche auch bei Nässe. Durch die Verwendung verschiedener Plattenformate können bedarfsweise unterschiedliche Verlegemuster realisiert werden.Since the water jet does not damage the broken edges of the natural stone chippings used, the surface of the natural stone dummy in the form of a plate hardens and is non-slip, even when wet. By using different plate formats, different laying patterns can be created as required.
Ein Ausführungsbeispiel einer Natursteinattrappe wird nachfolgend beschrieben:An example of a natural stone dummy is described below:
In einer bevorzugten Ausführungsform der Natursteinattrappe mit der Anmutung einer massiven Natursteinplatte zur Befestigung von Verkehrsflächen werden zur Fertigung der Vorsatzschicht Natursteinsplitt mit einer Körnung zwischen 1 mm und 3 mm und Sand mit einer Körnung von 0 bis 2 mm zu annähernd gleichen Gewichtsanteilen vermischt. Dieses Gemisch wird anschließend mit Wasser und Zement gebunden, wobei vorzugsweise Portlandzement PZ 42,5 verwendet wird. Der Zement nimmt einen Anteil von ca. 300 kg bis 400 kg je Kubikmeter Vorsatzbeton ein. Bedarfsweise werden Zementfarben bis zu einem Anteil von 3 bis 5 % der Gesamtmasse des Vorsatzzements zugesetzt.In a preferred embodiment of the natural stone dummy with the appearance of a solid natural stone slab for paving traffic areas, natural stone chippings with a grain size of between 1 mm and 3 mm and sand with a grain size of 0 to 2 mm are mixed in approximately equal proportions by weight to produce the facing layer. This mixture is then bound with water and cement, with Portland cement PZ 42.5 preferably being used. The cement accounts for a proportion of approximately 300 kg to 400 kg per cubic meter of facing concrete. If necessary, cement colors are added up to a proportion of 3 to 5% of the total mass of the facing cement.
Der Vorsatzbeton wird auf eine Schicht aus Kernbeton aufgetragen und anschließend gemeinsam mit dieser unter Druck in Plattenform gepresst. Bevor die so entstandene plattenförmige Natursteinattrappe ausgehärtet ist, wird sie aus dem Formwerkzeug herausgelöst. The facing concrete is applied to a layer of core concrete and then pressed together with this into the form of a slab under pressure. Before the resulting slab-shaped natural stone dummy has hardened, it is removed from the mold.
Anschließend wird die sichtbare Seite der Vorsatzschicht mit einem Wasserstrahl abgesprüht. Der Fließdruck des Wasserstrahls an der Austrittsöffhung der verwendeten Düse oszilliert dabei zwischen 2 bar und 10 bar. Durch die Einwirkung des Wasserstrahls wird der noch nicht abgebundene Beton aus der Oberfläche der Vorsatzschicht herausgewaschen. Hierbei ist darauf zu achten, dass das Herauswaschen nur bis in eine Tiefe erfolgt, die etwa der halben Korngröße des Natursteinsplitts entspricht. AnderenfallsThe visible side of the facing layer is then sprayed with a water jet. The flow pressure of the water jet at the outlet of the nozzle used oscillates between 2 bar and 10 bar. The effect of the water jet washes the concrete that has not yet set out of the surface of the facing layer. Care must be taken to ensure that the washing out only takes place to a depth that corresponds to about half the grain size of the natural stone chippings. Otherwise
• ··
• ·
&phgr; · ·
φ ·
• t · ··• t · ··
lösen sich die Splittkörner der obersten Schicht, so dass die in diesem Einsatzfall gewünschte Ebenheit der sichtbaren Oberfläche verloren geht.the grit of the top layer comes loose, so that the flatness of the visible surface desired in this application is lost.
Aufgrund des differierenden Wasserdrucks wird innerhalb relativ kurzer Zeit das Bindemittel ausgewaschen, ohne dass es - wie bei einer kontinuierlichen Wasserbestrahlung - zu einer zu tiefgehenden Anlösung und Ausspülung des Bindemittels kommen kann. Nach erfolgter Wasserstrahlbehandlung wird die Natursteinattrappe zum endgültigen Abbinden gelagert. Die so entstandene plattenförmige Natursteinattrappe weist eine abriebfeste, rutschsichere Oberfläche und das Aussehen einer massiven Natursteinplatte auf.Due to the varying water pressure, the binding agent is washed out within a relatively short time without the binding agent being dissolved and washed out too deeply, as is the case with continuous water jet treatment. After the water jet treatment, the natural stone dummy is stored for final setting. The resulting plate-shaped natural stone dummy has an abrasion-resistant, non-slip surface and the appearance of a solid natural stone plate.
Durch die gezielte Änderung des Bestrahlungswinkels des Wasserstrahls und/oder durch intensive pulsierende Bestrahlung können bei Bedarf zielgerichtet lokale Auswaschungen auf der Oberfläche der Vorsatzschicht erzeugt werden, die der Natursteinattrappe das gewollte Aussehen eines verwitterten Natursteins verleihen.
Bevorzugt werden zur Wasserbehandlung der Oberfläche Einrichtungen verwendet, die mehrere, einzeln ansteuerbare Wasserdüsen aufweisen. Durch die stochastische Ansteuerung der Düsen, die Änderung des Wasserdrucks und des Einstrahlwinkels können individuell geformte Auswaschungen auf der Oberfläche der Vorsatzschicht erzeugt werden, die der Natursteinattrappe ein unikates Aussehen geben.By specifically changing the angle of the water jet and/or by using intensive pulsating radiation, local washouts can be created on the surface of the facing layer if required, giving the natural stone dummy the desired appearance of a weathered natural stone.
The preferred water treatment device for the surface is one that has several individually controllable water nozzles. The stochastic control of the nozzles, the change in water pressure and the angle of incidence can produce individually shaped washouts on the surface of the facing layer, giving the natural stone dummy a unique appearance.
Durch die Verwendung einer rechnergestützten Anordnung zur Ansteuerung der Wasserdüsen besteht vorteilhaft die Möglichkeit, die Oberfläche von Natursteinattrappen, die später nebeneinander verlegt werden, aufeinander abzustimmen, so dass der Eindruck einer größeren homogenen Fläche entsteht.By using a computer-aided arrangement to control the water jets, it is advantageously possible to coordinate the surface of natural stone dummies that are later laid next to each other, so that the impression of a larger, homogeneous surface is created.
Claims (14)