DE19900488A1 - Process for the production of loadable plastic foams - Google Patents
Process for the production of loadable plastic foamsInfo
- Publication number
- DE19900488A1 DE19900488A1 DE1999100488 DE19900488A DE19900488A1 DE 19900488 A1 DE19900488 A1 DE 19900488A1 DE 1999100488 DE1999100488 DE 1999100488 DE 19900488 A DE19900488 A DE 19900488A DE 19900488 A1 DE19900488 A1 DE 19900488A1
- Authority
- DE
- Germany
- Prior art keywords
- base polymer
- extruder
- plastic foams
- chemical blowing
- additives
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
Die Erfindung betrifft ein Verfahren zur Herstellung beladbarer Kunststoff schäume, wobei man zu wenigstens einem thermoplastischen Basispolyme ren ein chemisches Treibmittel gibt, die Masse schmilzt, vor und/oder nach dem Schmelzen mischt, und die Mischung unter Bildung eines schüttfähi gen, porösen Trägermaterials abkühlt, mit der Maßgabe, daß man in einem Extruder oder mehrwelligen Kneter-Extruder arbeitet und wenigstens zeit weise ein inertes Gas in die Schmelze von Basispolymer und chemischem Treibmittel einleitet. Dabei führt man die Extrusion in Gegenwart eines Nu kleierungsmittels durch.The invention relates to a method for producing loadable plastic foams, with at least one thermoplastic base polymer There is a chemical blowing agent that melts the mass before and / or after mixes, and the mixture to form a pourable gene, porous support material cools, with the proviso that in one Extruder or multi-screw kneader extruder works and at least time assign an inert gas to the melt of the base polymer and chemical Propellant initiates. The extrusion is carried out in the presence of a nu lubricant through.
Polymere bestehen aus Molekülketten mit zahlreichen, sich praktisch endlos wiederholenden Bausteinen, welche sich in bezug auf die physikalischen Eigenschaften von niedermolekularen Verbindungen unterscheiden. So wei sen Polymere im Vergleich zu niedermolekularen Verbindungen beispiels weise hohe Zugfestigkeiten und Elastizität auf. Polymers consist of molecular chains with numerous, practically endless repeating building blocks, which are related to the physical Differentiate properties of low molecular weight compounds. So white Sen polymers compared to low molecular weight compounds, for example have high tensile strength and elasticity.
In polymerisierte Kunststoffmassen werden im Zuge der industriellen Verar beitung - je nach Weiterverarbeitung und Zweckbestimmung - geeignete Zusatzstoffe, sogenannte Additive, eingemischt. Auf diese Weise können Basispolymere an individuelle Bedürfnisse hinsichtlich der gewünschten Eigenschaften angepaßt werden.In the course of industrial processing, polymerized plastic masses are processing - depending on further processing and purpose - suitable Additives, so-called additives, mixed in. That way you can Base polymers to meet individual needs with regard to the desired Properties can be adjusted.
In der Regel bestehen zwischen Basispolymeren einerseits und flüssigen oder leicht schmelzbaren Additiven andererseits relativ große Viskositäts unterschiede, die zu Unverträglichkeiten führen können. Aufgrund dieser Tatsache lassen sich meist nur geringe Anteile von Additiven in Basispoly mere einmischen, sofern nicht spezielle Maßnahmen getroffen werden. Zur Vermeidung von Dosierproblemen und zum Erreichen einer homogene ren Verteilung bevorzugen viele Kunststoffverarbeiter ein Konzentrat des jeweiligen Additivs in den Basispolymeren. Dabei wird jeweils ein Basispo lymer bzw. eine Mischung mehrerer Basispolymere mit einem oder mehre ren Additiven erwärmt, aufgeschmolzen, gemischt und in eine schüttfähige Form überführt, beispielsweise in mit Additiven beladene Trägermaterialien in Granulafform. Diese werden auch Additivmasterbatches genannt.As a rule, there are basic polymers on the one hand and liquid ones or easily meltable additives, on the other hand, relatively high viscosity differences that can lead to intolerance. Based on these In fact, only small proportions of additives can be found in base poly Mix in mers unless special measures are taken. To avoid dosing problems and to achieve a homogeneous Many plastics processors prefer a concentrate of the respective additives in the base polymers. In each case there is a basic PO lymer or a mixture of several base polymers with one or more heated additives, melted, mixed and poured into a pourable Form transferred, for example in carrier materials loaded with additives in granular form. These are also called additive masterbatches.
Zur Erzielung poröser oder mikroporöser Polymerstrukturen sind dem Fachmann zahlreiche Herstellverfahren bekannt, beispielsweise die Pha seninversion, ein Nuklearbeschuß zur Einlagerung mikroporöser Festteil chen und die Zusammensinterung von kleinen mikroporösen Partikeln.To achieve porous or microporous polymer structures are the Numerous manufacturing processes known to those skilled in the art, for example the Pha seninversion, a nuclear bombardment for the storage of microporous solid parts and the sintering together of small microporous particles.
Ein besonders attraktives Verfahren zur Herstellung additiv beladener, porö ser Trägermaterialien ist aus EP-A-657 489 bekannt. Bei diesem Verfahren geht man von thermoplastischen Basispolymeren aus, versetzt sie mit Auf schäumhilfen, schmilzt und mischt die Masse und erhält nach dem Abkühlen ein schüttfähiges poröses Trägermaterial, das anschließend mit einem ge wünschten Additiv beladen wird. Als geeignete Aufschäumhilfen sind dazu Azodicarbonamide und Zitronensäurederivate offenbart. In einer bevorzug ten Ausführungsform wird in die Schmelze von Basispolymeren und Auf schäumhilfen wenigstens zeitweise zusätzlich ein inertes Gas, beispiels weise Stickstoff, eingeleitet, um besonders hohe Porositäten zu erzielen.A particularly attractive process for producing additively loaded, porous Water carrier materials is known from EP-A-657 489. With this procedure if you start from thermoplastic base polymers, you add Auf foaming aids, melts and mixes the mass and gets after cooling a pourable porous carrier material, which is then coated with a ge desired additive is loaded. As suitable foaming aids Azodicarbonamides and citric acid derivatives are disclosed. In one preferred Embodiment is in the melt of base polymers and on Foaming aids, at least occasionally, an inert gas, for example wise nitrogen, introduced to achieve particularly high porosities.
Die Aufgabe der vorliegenden Erfindung bestand in der Entwicklung eines verbesserten Verfahrens zur Herstellung beladbarer Kunststoffschäume. Unter "Kunststoffschäumen" sind - wie in der Fachwelt allgemein üblich - Kunststoffe zu verstehen, die aufgrund vorhandener innerer Hohlräume mit Additiven beladen werden können. Die Beladung sollte dabei in einfacher Weise derart möglich sein, daß der erfindungsgemäße Kunststoffschaum, der ein poröses Trägermaterial darstellt, mit wenigstens einem Additiv ver setzt wird und mit diesem bei einer unter dem Schmelzpunkt der Basispoly meren, die zur Herstellung des Kunststoffschaums eingesetzt wurden, je doch über dem Schmelzpunkt des Additivs liegenden Temperatur gemischt wird; dabei fließt das Additiv in die inneren Hohlräume des Kunststoff schaumes, d. h. der Kunststoffschaum nimmt aufgrund seiner speziellen Struktur die flüssigen Additive quasi wie ein Schwamm auf. Unter Additiven werden im Rahmen der vorliegenden Erfindung Kunststoffadditive verstan den. Dem Fachmann ist klar, was unter Kunststoffadditiven zu verstehen ist. Es existiert hierzu eine umfangreiche Literatur, darunter eine Reihe von speziellen Monographien. Lediglich beispielhaft sei auf das Buch "Taschen buch der Kunststoff-Additive" von R. Gächter und H. Müller (München 1983) verwiesen. The object of the present invention was to develop a improved process for the production of loadable plastic foams. Under "plastic foams" - as is common practice in the professional world - To understand plastics that are due to existing internal cavities Additives can be loaded. The loading should be easier Be possible in such a way that the plastic foam according to the invention, which is a porous carrier material, with at least one additive ver is set and with this at a below the melting point of the base poly mers, which were used to manufacture the plastic foam, each but mixed above the melting point of the additive becomes; the additive flows into the inner cavities of the plastic foam, d. H. the plastic foam takes on due to its special Structure the liquid additives like a sponge. Under additives plastic additives are understood in the context of the present invention the. It is clear to the person skilled in the art what is meant by plastic additives. There is extensive literature on this, including a number of special monographs. The book "Taschen book of plastic additives "by R. Gächter and H. Müller (Munich 1983).
Gegenstand der vorliegenden Erfindung ist ein Verfahren zur Herstellung beladbarer Kunststoffschäume, wobei man zu wenigstens einem ther moplastischen Basispolymeren ein chemisches Treibmittel gibt, die Masse schmilzt, vor und/oder nach dem Schmelzen mischt, und die Mischung unter Bildung eines schüttfähigen, porösen Trägermaterials abkühlt, mit der Maßgabe, daß man in einem Extruder oder mehrwelligen Kneter-Extruder arbeitet und wenigstens zeitweise ein inertes Gas in die Schmelze von Ba sispolymer und chemischem Treibmittel einleitet und wobei man die Extru sion in Gegenwart eines Nukleierungsmittels durchführt.The present invention relates to a method for the production loadable plastic foams, with at least one ther plastic base polymers give a chemical blowing agent, the mass melts, mixes before and / or after melting, and the mixture under Formation of a pourable, porous carrier material cools with the Provided that one in an extruder or multi-screw kneader extruder works and at least temporarily an inert gas in the melt of Ba initiates sispolymer and chemical blowing agent and taking the extru sion in the presence of a nucleating agent.
Die durch das Verfahren gemäß der vorliegenden Erfindung zugänglichen Produkte stellen schüttfähige, poröse Trägermaterialien dar und werden im folgenden - wie auch bereits oben geschehen - als Kunststoffschäume be zeichnet. Die gemäß dem erfindungsgemäßen Verfahren zugänglichen Kunststoffschäume weisen Makro-Poren auf, die untereinander verbunden sind. Dies läßt sich beispielsweise durch rasterelektronenmikroskopische Aufnahmen von Längs- bzw. Querschnitten der Kunststoffschäume nach weisen. Die Poren weisen Durchmesser in der Größenordnung von 100 µm auf und sind ellipsoid, wobei das Verhältnis des längsten zum kürzesten In nendurchmesser bei 2 : 1 bis 5 : 1 liegt.Those accessible by the method according to the present invention Products are pourable, porous carrier materials and are used in following - as already happened above - be as plastic foams draws. The accessible according to the inventive method Plastic foams have macro pores that are interconnected are. This can be done, for example, by scanning electron microscopy Shots of longitudinal or cross sections of the plastic foams point. The pores have diameters in the order of 100 microns on and are ellipsoidal, with the ratio of the longest to the shortest In nominal diameter is 2: 1 to 5: 1.
Unter einem Nukleierungsmittel wird ein Kristallisationsbeschleuniger ver standen. Synonym für den Begriff des Nukleierungsmittels wird in der Fach literatur auch der Begriff des Keimbildners verwendet. Nukleierungsmittel sind bei der Verarbeitung von Kunststoffen insbesondere deshalb von Be deutung, weil sie die Kristallwachstumsgeschwindigkeit von Polymeren be einflussen. Durch den Zusatz von Nukleierungsmitteln zum Basispolymer werden Zahl und Größe der entstehenden Sphärolithe bestimmt. Dies hat zur Folge, daß nukleierte Polymere ein feinkörnigeres Gefüge aufweisen als nicht nukleierte, was sich in ihren physikalisch-chemischen Eigenschaften bemerkbar macht; so sind beispielsweise grob sphärolithische Kunststoffe bei gleichem kristallinen Anteil spröder und weniger transparent bzw. trans luzent als solche mit fein sphärolitischer Struktur.A crystallization accelerator is placed under a nucleating agent stood. A synonym for the term nucleating agent is in the field literature also uses the term nucleating agent. Nucleating agents are especially useful for processing plastics interpretation because they are the crystal growth rate of polymers influence. By adding nucleating agents to the base polymer the number and size of the spherulites formed are determined. this has consequence that nucleated polymers have a finer grain structure than not nucleated what is in their physico-chemical properties noticeable; for example, roughly spherulitic plastics with the same crystalline content brittle and less transparent or trans lucent as such with a fine spherulitic structure.
Im Rahmen der vorliegenden Erfindung wird durch das Nukleierungsmittel, das aus ein oder mehreren Verbindungen bestehen kann, darüber hinaus bewirkt, daß die Lamellenstruktur des nach dem erfindungsgemäßen Ver fahren erhältlichen Kunststoffschaumes besonders fein und gleichmäßig ist. In einer Ausführungsform setzt man das Nukleierungsmittel in einer Menge von 0,001 bis 5,0 Gew.-% - bezogen auf die Basispolymeren - ein. Dabei ist der Bereich von 0,1 bis 0,8 Gew.-% besonders bevorzugt. Die Einarbeitung des Nukleierungsmittels geschieht vorzugsweise vor der Extrusion, d. h. man suspendiert das Nukleierungsmittel in einer Schmelze aus Basispoly meren und chemischem Treibmittel und unterwirft dieses Gemisch anschlie ßend der Extrusion.In the context of the present invention, the nucleating agent, which can consist of one or more connections, in addition causes the lamellar structure of the Ver available plastic foam is particularly fine and even. In one embodiment, the nucleating agent is used in an amount from 0.001 to 5.0% by weight, based on the base polymers. It is the range from 0.1 to 0.8% by weight is particularly preferred. The training of the nucleating agent is preferably done before extrusion, i. H. the nucleating agent is suspended in a melt of base poly mers and chemical blowing agent and then subjects this mixture eats the extrusion.
Als Nukleierungsmittel kommen insbesondere solche Stoffe in Betracht, die durch das Basispolymer benetzbar bzw. absorbierbar sind, im Basispolymer unlöslich sind, einen Schmelzpunkt aufweisen, der oberhalb des Schmelz punktes des Basispolymeren liegt und die darüber hinaus in möglichst fein teiliger Form - in der Regel mit Teilchengrößen im Bereich von etwa 1 bis 10 µm - in der Polymerschmelze homogen dispergierbar sind. In einer be vorzugten Ausführungsform setzt man als Nukleierungsmittel anorganische Stoffe wie Talkum, Kieselsäure oder Kaolin ein. Beispiele für geeignete or ganische Verbindungen, die sich als Nukleierungsmittel eignen, sind Salze von Mono- oder Polycarbonsäuren. Substances which are particularly suitable as nucleating agents are: are wettable or absorbable by the base polymer in the base polymer are insoluble, have a melting point above the enamel point of the base polymer and which is as fine as possible particulate form - usually with particle sizes in the range of about 1 to 10 µm - are homogeneously dispersible in the polymer melt. In a be preferred embodiment, inorganic nucleating agents are used Substances such as talc, silica or kaolin. Examples of suitable or ganic compounds which are suitable as nucleating agents are salts of mono- or polycarboxylic acids.
Das chemische Treibmittel wird in einer Menge von 0,01 bis 5 Gew.-% und insbesondere in einer Menge von 0,1 bis 2 Gew.-% - bezogen auf die Basis polymeren - eingesetzt. Dabei kann man entweder ein oder mehrere Sub stanzen als chemisches Treibmittel einsetzen. Vorzugsweise wählt man das chemische Treibmittel aus der Gruppe der Diazoverbindungen, N-Ni trosoverbindungen, Sulfohydrazide, Harnstoffderivate, Guanidinderivate, Borhydrid/Wasser-Systeme, Zitronensäure und deren Ester, Carbonate und Hydrogencarbonate aus. In einer bevorzugten Ausführungsform der vorlie genden Erfindung setzt man als chemisches Treibmittel Carbonate, Hydro gencarbonate, Zitronensäure und deren Ester oder Gemische dieser Ver bindungen ein.The chemical blowing agent is used in an amount of 0.01 to 5 wt .-% and especially in an amount of 0.1 to 2 wt .-% - based on the base polymers - used. You can either use one or more sub use punching as a chemical blowing agent. Preferably you choose that chemical blowing agents from the group of the diazo compounds, N-Ni troso compounds, sulfohydrazides, urea derivatives, guanidine derivatives, Borohydride / water systems, citric acid and its esters, carbonates and Hydrogen carbonates. In a preferred embodiment of the present The present invention is set as a chemical blowing agent carbonate, hydro gene carbonates, citric acid and their esters or mixtures of these ver bindings.
In einer Ausführungsform wird der Extruder in einem Temperaturbereich von 100 bis 265°C, einem Druckbereich von 50 bis 100 bar und einer Schnec kendrehzahl von 50 bis 100 U/min betrieben. Dabei richten sich die optima len Extrusionstemperaturen im wesentlichen nach der Art der eingesetzten Basispolymeren, insbesondere deren Melt Flow Indices (MFI). Sofern als Basispolymer ein Ethylen-Vinylacetat-Copolymer eingesetzt wird, stellt man in der Einzugszone des Extruders vorzugsweise eine Temperatur im Bereich von 100 bis 120°C und im Düsenbereich eine Temperatur im Bereich von 160 bis 180°C ein. Sofern als Basispolymer Polypropylen eingesetzt wird, stellt man in der Einzugszone des Extruders vorzugsweise eine Temperatur im Bereich von 130 bis 150°C und im Düsenbereich eine Temperatur im Bereich von 235 bis 265°C ein. Sofern man als Basispolymer LDPE (low density polyethylene) einsetzt, stellt man in der Einzugszone des Extruders vorzugsweise eine Temperatur im Bereich von 120 bis 140°C und im Düsenbereich eine Temperatur im Bereich von 180 bis 210°C ein. In one embodiment, the extruder is in a temperature range of 100 to 265 ° C, a pressure range of 50 to 100 bar and a Schnec speed from 50 to 100 rpm. The optima are aligned len extrusion temperatures essentially according to the type of used Base polymers, especially their melt flow indices (MFI). Unless as Base polymer, an ethylene-vinyl acetate copolymer is used, one makes in the feed zone of the extruder preferably a temperature in the range from 100 to 120 ° C and in the nozzle area a temperature in the range of 160 to 180 ° C. If polypropylene is used as the base polymer, a temperature is preferably set in the feed zone of the extruder a temperature in the range of 130 to 150 ° C and in the nozzle area Range from 235 to 265 ° C. If you use LDPE (low density polyethylene) is used, it is placed in the feed zone of the extruder preferably a temperature in the range of 120 to 140 ° C and in Nozzle area a temperature in the range of 180 to 210 ° C.
Wie bereits gesagt leitet man im Zuge des erfindungsgemäßen Verfahrens wenigstens zeitweise ein inertes Gas in die Schmelze von Basispolymer und chemischem Treibmittel ein. Dabei wird das inerte Gas in den Extruder, in dem sich die Schmelze von Basispolymer und chemischem Treibmittel be findet, eingeleitet. Vorzugsweise geschieht das Einleiten des inerten Gases während des gesamten Extrusionsvorganges. Das Gas wird insbesondere fein versprüht eingeleitet, wobei sich die Menge des Gases insbesondere nach der Art der Basispolymeren, dem Anteil an chemischem Treibmittel sowie der Temperatur und der Gesamtmenge der Schmelze richtet. Vor zugsweise stellt man Gasdrucke auf Werte ein, die 5 bis 30 bar oberhalb des Extrusionsdruckes liegen. Die Menge des Gases wird vorzugsweise auf einen Wert im Bereich von 50 bis 100 Volumen-% - bezogen auf das Volumen der extrudierten Polymere - eingestellt; unter "Volumen" ist dabei der Durchsatz des Polymeren pro Zeit (Volumenausstoß in Litern pro Stunde) zu verstehen.As already said, one leads in the course of the method according to the invention at least temporarily an inert gas in the melt of base polymer and chemical blowing agent. The inert gas is in the extruder, in which is the melt of base polymer and chemical blowing agent takes place. The inert gas is preferably introduced during the entire extrusion process. The gas in particular finely sprayed, the amount of gas in particular according to the type of base polymer, the proportion of chemical blowing agent as well as the temperature and the total amount of the melt. Before In addition, gas pressures are set to values which are 5 to 30 bar above of the extrusion pressure. The amount of gas is preferably increased to a value in the range of 50 to 100% by volume - based on the Volume of extruded polymers - adjusted; is under "volume" the throughput of the polymer per time (volume output in liters per Hour) to understand.
Bei den genannten chemischen Treibmitteln handelt es sich um Verbindun gen, die durch chemische Reaktionen Gase abspalten und in der polymeren Matrix des oder der Basispolymeren innere Hohlräume erzeugen können. Die freiwerdenden Gase sind beispielsweise Kohlendioxid oder Stickstoff und enthalten keine explosiven Bestandteile. Die Abspaltung wird vorzugs weise in einem relativ kleinen Temperaturintervall, nämlich dem Zerset zungstemperaturbereich des/der jeweils eingesetzten chemischen Treib mittel, durchgeführt und der Verarbeitungstemperatur des/der eingesetzten Basispolymeren angepaßt.The chemical blowing agents mentioned are compounds gene that split off gases by chemical reactions and in the polymer Matrix of the base polymer (s) can create internal cavities. The gases released are, for example, carbon dioxide or nitrogen and contain no explosive components. The spin-off is preferred wise in a relatively small temperature interval, namely the decomposition temperature range of the chemical blowing agent used medium, carried out and the processing temperature of the used Base polymers adapted.
Die chemischen Treibmittel lassen sich prinzipiell in zwei Gruppen einteilen. Treibmittel mit endothermer Zersetzungsreaktion benötigen eine ständige Wärmezufuhr zur Zersetzung und Gasabspaltung. Die Zersetzung beginnt je nach Art des Treibmittels relativ früh schon bei 85°C und verläuft langsam und gleichmäßig. Sie wird beendet, sobald keine Wärmezufuhr mehr erfolgt und das geschäumte Formteil unterhalb der Zersetzungstemperatur des Treibmittels abgekühlt ist. Der Gasdruck endothermer Treibmittel liegt üblicherweise im Bereich von etwa 8 bis 10 bar. Beispiele für endotherme Treibmittel sind etwa Mischungen aus Carbonaten und Hydrogencarbona ten. Ein besonders attraktiver Vertreter dieser Art von Treibmitteln ist Natri umhydrogencarbonat.The chemical blowing agents can basically be divided into two groups. Blowing agents with an endothermic decomposition reaction require a constant Heat supply for decomposition and gas elimination. The decomposition begins Depending on the type of blowing agent, it starts relatively early at 85 ° C and runs slowly and even. It ends as soon as heat is no longer applied and the foamed molding below the decomposition temperature of the Propellant has cooled. The gas pressure of endothermic blowing agents is usually in the range of about 8 to 10 bar. Examples of endothermic Blowing agents are mixtures of carbonates and hydrogen carbonates A particularly attractive representative of this type of blowing agent is Natri umhydrogencarbonate.
Treibmittel mit exothermer Zersetzungsreaktion benötigen eine Startenergie, um beim Erreichen der Zersetzungstemperatur quasi explosionsartig Gas freizusetzen. Der Gasdruck exothermer Treibmittel beträgt in der Regel etwa 12 bis 15 bar. Beispiele exothermer Treibmittel sind Sulfohydrazide und Semicarbazide. Exemplarisch sei in diesem Zusammenhang 4,4'-Oxybis benzolsulfohydrazid und Toluol-4-Sulfonohydrazid genannt.Blowing agents with an exothermic decomposition reaction require a starting energy to quasi explosive gas when the decomposition temperature is reached release. The gas pressure of exothermic blowing agents is usually around 12 to 15 bar. Examples of exothermic blowing agents are sulfohydrazides and Semicarbazides. An example in this context is 4,4'-oxybis called benzenesulfohydrazide and toluene-4-sulfonohydrazide.
Der nach dem erfindungsgemäßen Verfahren hergestellte Kunststoff schaum, d. h. das poröse Extrudat, wird mit an sich bekannten geeigneten Einrichtungen in granulat- oder pelletförmiges Trägermaterial überführt, beispielsweise durch Stranggranulation.The plastic produced by the method according to the invention foam, d. H. the porous extrudate is used with known suitable ones Devices converted into granular or pellet-shaped carrier material, for example by strand granulation.
Die im Zuge des erfindungsgemäßen Verfahrens einzusetzenden Basispo
lymere, bei denen es sich um thermoplastische Kunststoffe handelt, können
an sich beliebig gewählt werden. Beispiele für geeignete Basispolymere
sind:
The basic polymers to be used in the course of the method according to the invention, which are thermoplastic materials, can in themselves be chosen as desired. Examples of suitable base polymers are:
- 1. Homopolymere aus einem α-Olefin mit zwei bis acht Kohlenstoffatomen, Copolymerisate von zwei entsprechenden α-Olefinen, vorzugsweise Copolymerisate aus Ethylen, Ethylen-Homopolymerisate wie HDPE (high density polyethylene), LDPE (low density polyethylene), VLDPE (very low density polyethylene), LLEPE (linear low density polyethylene), MDPE (medium density polyethylene), UHMPE (ultra high molecular po lyethylene), VPE (vernetztes Polyethylen), HPPE (high pressure polyethylene), isotaktisches Polypropylen, syndiotaktisches Polypropylen, Metallocen-katalysiert hergestelltes Polypropylen, schlagzäh-modi fiziertes Polypropylen, Random-Copolymere auf Basis Ethylen und Pro pylen, Blockcopolymere auf Basis Ethylen und Propylen, Homopolymere auf Basis 1-Butylen, 1-Pentylen, 1-Hexylen, 1-Octylen, Isobutylen, 2- Methyl-1-Butylen, 3-Methyl-1-Pentylen, 4-Methyl-1-Pentylen, 2,3-Di methyl-1-Butylen, 2-Ethyl-1-Butylen sowie Mischungen davon.1. homopolymers of an α-olefin with two to eight carbon atoms, Copolymers of two corresponding α-olefins, preferably Copolymers of ethylene, ethylene homopolymers such as HDPE (high density polyethylene), LDPE (low density polyethylene), VLDPE (very low density polyethylene), LLEPE (linear low density polyethylene), MDPE (medium density polyethylene), UHMPE (ultra high molecular po lyethylene), VPE (cross-linked polyethylene), HPPE (high pressure polyethylene), isotactic polypropylene, syndiotactic polypropylene, Metallocene-catalyzed polypropylene, impact-resistant modes Defined polypropylene, random copolymers based on ethylene and pro pylene, block copolymers based on ethylene and propylene, homopolymers based on 1-butylene, 1-pentylene, 1-hexylene, 1-octylene, isobutylene, 2- Methyl-1-butylene, 3-methyl-1-pentylene, 4-methyl-1-pentylene, 2,3-di methyl-1-butylene, 2-ethyl-1-butylene and mixtures thereof.
- 2. Copolymerisate von Ethylen mit 1-Butylen, 1-Hexylen, 1-Octylen und 4- Methyl-1-Pentylen.2. Copolymers of ethylene with 1-butylene, 1-hexylene, 1-octylene and 4- Methyl 1-pentylene.
- 3. Ethylen-Vinylacetat-Copolymerisate, Ethylenethylacetat-Copolymerisate, Ethylenacrylsäure-Copolymerisate und Mischungen davon.3. ethylene-vinyl acetate copolymers, ethylene-ethyl acetate copolymers, Ethylene acrylic acid copolymers and mixtures thereof.
- 4. Ethylenpropylengummi (EPDM), auch Dien-modifiziert (EPR), Styrol-But adien-Styrol-Copolymerisate (SBS), Styrol-Ethylen-Butylen-Styrol-Co polymerisate (SEBS) und Mischungen davon.4. Ethylene propylene rubber (EPDM), also modified with diene (EPR), styrene-but adiene-styrene copolymers (SBS), styrene-ethylene-butylene-styrene-Co polymers (SEBS) and mixtures thereof.
Die Basispolymere, die im Zuge des erfindungsgemäßen Verfahrens einge setzt werden, liegen in der Praxis granalien- oder pelletförmig vor. Sie sind gut schütt- und rieselfähig und daher zum Mischen mit chemischen Treib mitteln gut geeignet.The base polymers used in the course of the method according to the invention in practice are granular or pellet-shaped. they are easy to pour and pour and therefore to mix with chemical blowing agents well suited.
Da die Struktur der erfindungsgemäß hergestellten Kunststoffschäume in hohem Maße durch elliptische untereinander verbundene Makro-Poren cha rakterisiert ist, ist verständlich, daß eine Beladung der Kunststoffschäume mit beliebigen Additiven in einfacher Weise möglich ist. Hierzu wird der er findungsgemäß hergestellte Kunststoffschaum mit wenigstens einem Additiv versetzt und mit diesem bei einer unter dem Schmelzpunkt des bei der Herstellung des Kunststoffschaumes eingesetzten Basispolymeren, jedoch über dem Schmelzpunkt des Additiv liegenden Temperatur gemischt.Since the structure of the plastic foams produced according to the invention in to a high degree due to elliptical interconnected macro-pores cha is characterized, it is understandable that loading of the plastic foams is easily possible with any additives. For this he will Plastic foam produced according to the invention with at least one additive offset and with this at a below the melting point of the at Production of the plastic foam used base polymers, however temperature above the melting point of the additive mixed.
Die Additive können im Rahmen der vorliegenden Erfindung aus den dem Fachmann einschlägig bekannten Additiven zur Verarbeitung von ther moplastischen Kunststoffen an sich beliebig gewählt werden. Beispiele für geeignete Additive sind: Antistatika, Antischleiermittel, Antioxidantien, UV- Stabilisatoren, Haftmittel, Kalandrierhilfen, Formtrennmittel, Gleitmittel, Trennmittel, Schmiermittel, Weichmacher, Duftmittel, Flammschutzmittel, Füllstoffe, Vernetzungsmittel und Mittel zur Erhöhung der Thermostabilität.In the context of the present invention, the additives can be obtained from the Additives known to those skilled in the art for processing ther moplastic plastics themselves can be chosen arbitrarily. examples for suitable additives are: antistatic agents, antifoggants, antioxidants, UV Stabilizers, adhesives, calendering aids, mold release agents, lubricants, Release agents, lubricants, plasticizers, fragrances, flame retardants, Fillers, crosslinking agents and agents for increasing thermal stability.
Die Additiv-beladenen Kunststoffschäume werden auch als Additiv-Master batches bezeichnet. Diese Additiv-Masterbatches können bei der Verar beitung von Massenkunststoffen eingesetzt werden. Dabei kann die Verar beitung dieser Massenkunststoffe auf an sich beliebige Art erfolgen; insbe sondere seien hier Extrusions-, Kalandrier-, Spritzguß- und Blasformverfah ren genannt.The additive-loaded plastic foams are also called additive masters called batches. These additive masterbatches can be processing of bulk plastics. The Verar processing of these bulk plastics can be done in any way per se; esp special extrusion, calendering, injection molding and blow molding processes ren called.
Ein weiterer Gegenstand der vorliegenden Erfindung ist dementsprechend die Verwendung der nach dem Verfahren der vorliegenden Erfindung herge stellten Kunststoffschäume zur Additivierung von Massenkunststoffen.Another object of the present invention is accordingly the use of the according to the method of the present invention provided plastic foams for the additive of bulk plastics.
Claims (2)