DE19718035A1 - Applying plastic particles to sheet forming roughened product - Google Patents
Applying plastic particles to sheet forming roughened productInfo
- Publication number
- DE19718035A1 DE19718035A1 DE1997118035 DE19718035A DE19718035A1 DE 19718035 A1 DE19718035 A1 DE 19718035A1 DE 1997118035 DE1997118035 DE 1997118035 DE 19718035 A DE19718035 A DE 19718035A DE 19718035 A1 DE19718035 A1 DE 19718035A1
- Authority
- DE
- Germany
- Prior art keywords
- plastic
- flame
- particles
- plastic particles
- plastic plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Die Erfindung betrifft ein Verfahren und eine Vorrichtung zum Aufbringen von Kunststoffpartikel auf eine Kunststoffplatte zur Herstellung einer rauhen Oberfläche, bei welchem die Kunststoffplatte relativ unter wenigstens einem Kunststoffpartikelstrahl bewegt wird. Unter Kunststoffplatten sollen mehr oder weniger steife Kunststoffbahnen aus thermoplastischem Kunststoff oder auch Kunststoffolien mit unterschiedlichen Stärken verstanden werden. Im wesentlichen bezieht sich die Erfindung auf die Art der Aufbringung der Kunststoffpartikel, so daß im folgenden überwiegend von einer Kunststoffplatte die Rede ist, ohne daß damit eine Beschränkung verbunden sein soll.The invention relates to a method and an apparatus for applying Plastic particles on a plastic plate to produce a rough surface, at which the plastic plate relatively under at least one plastic particle beam is moved. Plastic sheets are supposed to be more or less rigid under plastic sheets made of thermoplastic or plastic films with different Strengths are understood. In essence, the invention relates to the type of Application of the plastic particles, so that in the following mainly from one Plastic plate is mentioned without any limitation.
Für das Beschichten einer Oberfläche von Kunststoffplatten mit Kunststoffpartikel sind unterschiedliche Verfahren bekannt. Es ist bekannt, die Kunststoffpartikel lose auf die Oberfläche aufzutragen und die beschichtete Oberfläche anschließend zu erhitzen. Auch ist es bekannt, den aufzubringenden Kunststoff in einem Extruder zu plastifizieren und durch wenigstens eine Düse im wesentlichen gleichmäßig verteilt auf die Oberfläche aufzubringen. Die erhitzten Kunststoffpartikel verschmelzen mit der Kunststoffplatte, so daß ein fester Verbund erzielt wird. Durch die Kunststoffpartikel werden Vorsprünge auf der Oberfläche gebildet, wodurch die Rauhigkeit der Kunststoffplatte entsteht.For coating a surface of plastic sheets with plastic particles different methods known. It is known to loose the plastic particles on the Apply surface and then heat the coated surface. Also it is known to plasticize the plastic to be applied in an extruder and through at least one nozzle essentially uniformly distributed over the surface to apply. The heated plastic particles fuse with the plastic plate, see above that a firm bond is achieved. The plastic particles become protrusions formed on the surface, which creates the roughness of the plastic plate.
Diese Verfahren haben den Nachteil, daß die Kunststoffpartikel und auch die Kunststoffplatte eine relativ lange Zeit erhöhten Temperaturen ausgesetzt sind. Hierdurch wird eine thermische Umstrukturierung der Molekülketten des zu verarbeitenden Kunststoffes bewirkt, so daß der aufgebrachte Kunststoff von seinen ursprünglichen physikalischen Eigenschaften abweicht. Insbesondere ist es nicht möglich, eine Kunststoffplatte der eingangs geschilderten Art so herzustellen, daß bei identischen Ausgangsstoffen die Kunststoffplatte und die aufgebrachten Kunststoffpartikel anschließend die gleichen physikalischen und chemischen Eigenschaften aufweisen.These processes have the disadvantage that the plastic particles and also the Plastic plate are exposed to elevated temperatures for a relatively long time. As a result, thermal restructuring of the molecular chains of the processing plastic causes so that the applied plastic of its deviates from the original physical properties. In particular, it is not possible to produce a plastic plate of the type described so that at identical raw materials, the plastic plate and the applied Plastic particles then the same physical and chemical Have properties.
Der Erfindung liegt die Aufgabe zugrunde, ein anderes Verfahren und eine andere Vorrichtung zum Herstellen derartiger Kunststoffplatten mit wenigstens einer rauhen Oberfläche zu schaffen, mit dem bzw. der die bekannten Nachteile vermieden werden können.The invention has for its object a different method and another Device for producing such plastic plates with at least one rough one To create surface with which the known disadvantages are avoided can.
Die Aufgabe wird gemäß der Erfindung dadurch gelöst, daß die Kunststoffpartikel oberflächlich durch eine Flamme erhitzt werden und in erhitztem Zustand auf die Oberfläche der Kunststoffplatte auftreffen und dort haften. Dieses Verfahren hat den Vorteil, daß die Kunststoffpartikel nur für eine relativ kurze Zeit äußerlich erhitzt werden, so daß eine thermische Umstrukturierung nicht oder nur im begrenzten Ausmaß stattfindet. Die Kunststoffpartikel weisen im Kern noch eine ausreichende Festigkeit auf, während sie an der Oberfläche Schmelztemperatur aufweisen können. Nach dem Auftreffen der Partikel auf der Oberfläche wird somit eine feste Verbindung erreicht. Durch den festen bzw. nicht geschmolzenen Kern der Partikel wird ein vollständiges Verfließen der Partikel vermieden, und die gewünschte Rauhigkeit wird erzielt.The object is achieved according to the invention in that the plastic particles to be superficially heated by a flame and heated to the Hit the surface of the plastic plate and stick there. This procedure has the Advantage that the plastic particles only heat externally for a relatively short time be, so that a thermal restructuring not or only to a limited extent takes place. The plastic particles still have sufficient strength in the core while they may have melting temperature on the surface. After this When the particles hit the surface, a firm connection is achieved. The solid or unmelted core of the particles creates a complete core Flowing of the particles is avoided and the desired roughness is achieved.
Mit dem Verfahren gemäß der Erfindung können die Kunststoffpartikel aus dem gleichen Werkstoff wie die Kunststoffplatte sein. Da die Molekülstruktur der auftreffenden Partikel nicht verändert worden ist, werden die aufgebrachten Partikel nach Erkaltung der rauhen Kunststoffplatte die gleichen physikalischen Eigenschaften aufweisen wie die Kunststoffplatte selbst. Somit wird eine Kunststoffplatte mit rauher Oberfläche aus einem homogenen Material bereitgestellt, was mit den bekannten Verfahren nicht möglich ist.With the method according to the invention, the plastic particles from the same material as the plastic plate. Because the molecular structure of the impinging particles has not been changed, the applied particles after cooling the rough plastic plate the same physical properties have as the plastic plate itself. Thus, a plastic plate with rougher Surface provided from a homogeneous material, what with the known Procedure is not possible.
Gemäß einer bevorzugten Ausführungsform der Erfindung ist vorgesehen, daß die Flamme in Richtung auf die Oberfläche der Kunststoffplatte weist. Dadurch wird erreicht, daß durch den Druck der Flamme die Kunststoffpartikel in Richtung auf die Oberfläche der Kunststoffplatte zusätzlich beschleunigt werden. Hierdurch kann die Verbindung zwischen Partikel und Platte weiter verbessert werden.According to a preferred embodiment of the invention it is provided that the Flame points towards the surface of the plastic plate. This will achieved that the plastic particles in the direction of the Surface of the plastic plate can also be accelerated. This allows the Connection between particle and plate can be further improved.
Es kann zweckmäßig sein, wenn die Kunststoffpartikel eine Größe von etwa 200 µm bis 1 mm aufweisen. Die zu erzielende Temperatur der Oberfläche der Kunststoffpartikel hängt im wesentlichen von der Schmelztemperatur des eingesetzten Kunststoffes ab. Es kann hierbei vorgesehen werden, daß die Kunststoffpartikel an ihrer Oberfläche beim Auftreffen auf die Plattenoberfläche eine Temperatur von 200° bis 300°C aufweisen.It can be expedient if the plastic particles have a size of approximately 200 μm to 1 mm. The temperature of the surface of the plastic particles to be achieved depends essentially on the melting temperature of the plastic used. It can be provided here that the plastic particles on their surface when Have a temperature of 200 ° to 300 ° C on the surface of the plate.
Die Verweilzeit der Kunststoffpartikel hängt ebenfalls von den Eigenschaften des eingesetzten Kunststoffes der Partikel ab. Die Verweilzeit muß so bemessen sein, daß lediglich die Oberfläche der Partikel erhitzt und angeschmolzen wird, während das Innere im wesentlichen starr bleibt oder zumindest noch nicht geschmolzen ist. Die Verweilzeit der Kunststoffpartikel in der Flamme kann dabei typischerweise 1/20 bis 2/10 sec. betragen.The residence time of the plastic particles also depends on the properties of the used plastic from the particles. The dwell time must be such that only the surface of the particles is heated and melted while the Interior remains essentially rigid or at least has not yet melted. The The residence time of the plastic particles in the flame can typically be 1/20 to Amount to 2/10 sec.
Sowohl die erzielte Temperatur als auch die Verweilzeit der Kunststoffpartikel lassen sich durch Wahl der Temperatur der Flamme, dem Abstand der Flamme zur Oberfläche der zu bearbeitenden Kunststoffplatte und dem Druck, mit dem das brennbare Gasgemisch aus der Flammdüse strömt, beeinflussen. Es ist daher vorgesehen, daß der Abstand der Flammdüse zur Oberfläche der Kunststoffplatte und/oder der Druck des ausströmenden brennbaren Gasgemisches und/oder die Temperatur der Flamme in Abhängigkeit von dem eingesetzten Kunststoff und der gewünschten Oberflächentemperatur so eingestellt wird, daß die Kunststoffpartikel an der Oberfläche in etwa Schmelztemperatur aufweisen, während die Partikel im Inneren noch im wesentlichen starr oder zumindest noch nicht geschmolzen sind.Both the temperature achieved and the residence time of the plastic particles leave by choosing the temperature of the flame, the distance of the flame from the surface the plastic plate to be processed and the pressure with which the flammable Influence the gas mixture flowing out of the flame nozzle. It is therefore intended that the Distance of the flame nozzle to the surface of the plastic plate and / or the pressure of the escaping flammable gas mixture and / or the temperature of the flame in Dependence on the plastic used and the desired Surface temperature is set so that the plastic particles on the surface have about melting temperature, while the particles are still inside are essentially rigid or at least not yet melted.
Für eine bessere Verbindung kann es weiterhin zweckmäßig sein, wenn die Kunststoffplatte vor dem Auftragen der Kunststoffpartikel oberflächlich erwärmt wird. Die Temperatur der Oberfläche der Kunststoffplatte kann beispielsweise 100° bis 150°C betragen. Durch die Erwärmung nur an der Oberfläche mit diesen Temperaturen wird keine thermische Umstrukturierung der Kunststoffmoleküle des Kunststoffes der Kunststoffplatte verursacht, so daß nach Erkalten der Kunststoffplatte eine rauhe Oberfläche mit den gewünschten Eigenschaften vorliegt. Die Erwärmung kann durch eine separate Heizvorrichtung oder Flamme erfolgen. Es kann aber auch ausreichend sein, daß die Oberfläche durch die Flamme mit der die Kunststoffpartikel aufgetragen werden, erhitzt wird. Dies wird in der Regel ohnehin nicht zu vermeiden sein.For a better connection, it may still be useful if the Plastic plate is heated on the surface before applying the plastic particles. The temperature of the surface of the plastic plate can be, for example, 100 ° to 150 ° C. be. By heating only on the surface with these temperatures no thermal restructuring of the plastic molecules of the plastic Plastic plate caused, so that after cooling the plastic plate a rough Surface with the desired properties is available. The warming can be caused by a separate heater or flame. But it can also be sufficient be that the surface is applied by the flame with which the plastic particles be heated. As a rule, this will not be avoidable anyway.
Es kann vorgesehen werden, daß die Flamme durch ein brennbares Gemisch aus Gas und Sauerstoff erzeugt wird. Es kann aber auch zweckmäßig sein, wenn die Flamme durch ein brennbares Gemisch aus Gas und Druckluft erzeugt wird. Die Verwendung von Druckluft ist im Vergleich zu reinem Sauerstoff wesentlich kostengünstiger.It can be provided that the flame is caused by a combustible mixture of gas and oxygen is generated. But it can also be useful if the flame is generated by a flammable mixture of gas and compressed air. The usage compressed air is much cheaper than pure oxygen.
Es kann zweckmäßig sein, wenn die Kunststoffpartikel dem brennbaren Gemisch vor der Flammdüse zugegeben werden. Die Kunststoffpartikel können dem brennbaren Gemisch auch hinter der Flammdüse und vor der Flamme, beispielsweise im Zentrum einer ringförmigen Flamme, zugegeben werden. Grundsätzlich ist es auch möglich, die Kunststoffpartikel unmittelbar in die Flamme einzuführen. It can be useful if the plastic particles in front of the combustible mixture be added to the flame nozzle. The plastic particles can be flammable Mixture also behind the flame nozzle and in front of the flame, for example in the center an annular flame. Basically, it is also possible to Introduce plastic particles directly into the flame.
Gemäß einer weiteren Ausführungsform der Erfindung ist vorgesehen, daß die Kunststoffpartikel und die Kunststoffplatte elektrostatisch mit entgegengesetzter Polarität aufgeladen werden. Dies hat den Vorteil, daß die Kunststoffteilchen eine weitere Beschleunigung in Richtung auf die Kunststoffplatte erfahren und mit hoher kinetischer Energie auftreffen. Dadurch kann die Verbindung weiter verbessert werden.According to a further embodiment of the invention it is provided that the Plastic particles and the plastic plate electrostatically with opposite Polarity can be charged. This has the advantage that the plastic particles experienced further acceleration towards the plastic plate and with high of kinetic energy. This can further improve the connection.
Die Erfindung betrifft auch eine Vorrichtung zum Aufbringen von Kunststoffpartikel auf eine Kunststoffplatte zur Herstellung einer rauhen Oberfläche. Die Vorrichtung weist wenigstens eine Flammdüse zum Erzeugen einer Flamme mittels eines brennbaren Gasgemisches, durch die die Kunststoffpartikel oberflächlich erhitzt werden, und wenigstens eine Einbringeinrichtung auf, durch die die Kunststoffpartikel in das brennbare Gasgemisch und/oder die Flamme eingebracht werden. Die Kunststoffplatte wird relativ zu der Flammdüse und dem Kunststoffpartikelstrahl bewegt, so daß eine gleichmäßige Verteilung der Kunststoffpartikel auf der Oberfläche und somit eine gleichmäßige Rauhigkeit erzielt wird.The invention also relates to a device for applying plastic particles on a plastic plate to produce a rough surface. The device has at least one flame nozzle for generating a flame by means of a combustible Gas mixture, through which the plastic particles are heated superficially, and at least one insertion device through which the plastic particles into the combustible gas mixture and / or the flame are introduced. The plastic plate is moved relative to the flame nozzle and the plastic particle jet, so that a uniform distribution of the plastic particles on the surface and thus a uniform roughness is achieved.
Die Flammdüse kann in Richtung auf die Kunststoffplatte ausgerichtet sein. Dies hat den Vorteil, daß die Kunststoffpartikel durch den Druck des brennbaren Gasgemisches in Richtung auf die Kunststoffplatte beschleunigt werden.The flame nozzle can be aligned in the direction of the plastic plate. this has the advantage that the plastic particles by the pressure of the flammable gas mixture be accelerated towards the plastic plate.
Zur Bearbeitung großer Platten ist es zweckmäßig, mehrere Flammdüsen und Einbringeinrichtungen senkrecht zur Förderrichtung der Kunststoffplatte in einem Abstand zueinander anzuordnen, die in dieser Richtung hin- und herbewegbar sind. Durch die Förderbewegung einerseits und die Hin- und Herbewegung der Düsen andererseits wird eine gleichmäßige Verteilung der Kunststoffpartikel erreicht. Die Förderbewegung der Kunststoffplatte kann in der üblichen Weise durch zwei Wickelwellen erfolgen.For processing large plates, it is advisable to use several flame nozzles and Insertion devices perpendicular to the conveying direction of the plastic plate in one To be spaced from each other, which can be moved back and forth in this direction. Through the conveying movement on the one hand and the back and forth movement of the nozzles on the other hand, an even distribution of the plastic particles is achieved. The Conveying movement of the plastic plate can be done in the usual way by two Winding shafts take place.
Die Flammdüse einerseits und die Einbringeinrichtung bilden in der Regel eine Einheit, die Aufbringeinrichtung. Gemäß einer Ausführungsform der Erfindung ist vorgesehen, daß die Einbringeinrichtung einen Injektor aufweist, der in Strömungsrichtung des Gasgemisches vor der Flammdüse angeordnet ist und dessen Saugseite mit einem Vorratsbehälter für die Kunststoffpartikel in Verbindung steht. Es kann aber auch vorgesehen werden, daß die Einbringeinrichtung eine Düse aufweist, die im Bereich der Austrittsöffnung der Flammdüse für das brennbare Gasgemisch angeordnet ist, um die Kunststoffpartikel mittels einer separaten Fördereinrichtung in den Gasgemischstrom vor der Flamme einzugeben. Die Wahl der Ausbildung der Einbringeinrichtung hängt dabei im wesentlichen von der Art und Größe der eingesetzten Kunststoffpartikel ab.The flame nozzle on the one hand and the introduction device generally form a unit, the application device. According to one embodiment of the invention, that the introduction device has an injector in the flow direction of the Gas mixture is arranged in front of the flame nozzle and its suction side with a Storage container for the plastic particles is connected. But it can also be provided that the introduction device has a nozzle which in the area of Outlet opening of the flame nozzle for the combustible gas mixture is arranged to the Plastic particles in the gas mixture flow by means of a separate conveying device to enter before the flame. The choice of training for the feeding device depends it essentially depends on the type and size of the plastic particles used.
Es ist offensichtlich, daß durch das Verfahren und die Vorrichtung gemäß der Erfindung eine Kunststoffplatte oder -folie mit wenigstens einer durch aufgebrachte Kunststoffpartikel rauhen Oberfläche hergestellt werden kann, bei der die Kunststoffpartikel nach dem Aufbringen im wesentlichen die gleichen physikalischen Eigenschaften haben, wie vor dem Aufbringen. Dies ist insbesondere dann vorteilhaft, wenn die rauhe Kunststoffplatte vollständig aus einem Material mit denselben Eigenschaften bestehen muß. Es kann daher ohne weiteres vorgesehen werden, daß die Kunststoffpartikel aus dem gleichen Werkstoff wie die Kunststoffplatte bestehen.It is obvious that by the method and the device according to the invention a plastic plate or sheet with at least one applied through Plastic particles can be produced with a rough surface Plastic particles after application are essentially the same physical Have properties as before application. This is particularly advantageous if the rough plastic plate is completely made of a material with the same Properties must exist. It can therefore be easily provided that the Plastic particles consist of the same material as the plastic plate.
Die Erfindung wird im folgenden anhand der Zeichnung naher erläutert, deren einzige Figur das Schema des Verfahrens und der Vorrichtung zeigt.The invention is explained below with reference to the drawing, the only one Figure shows the scheme of the method and the device.
In der Zeichnung ist grob schematisch eine Kunststoffplatte 11 dargestellt, die in Richtung 12 transportiert wird. Dazu ist eine Vorratsrolle 13 vorgesehen, von der die Kunststoffplatte abgewickelt und auf eine andere Welle 14 gewickelt wird. Zwischen der Vorratsrolle 13 und der Welle 14 befindet sich über der Kunststoffplatte 11 eine Einrichtung 15 zum Aufbringen von Kunststoffpartikeln 16 zum Herstellen einer rauhen Oberfläche 17 der Kunststoffplatte 11. Vor dieser Aufbringeinrichtung 15 kann die Oberfläche 18 der Kunststoffplatte 11 glatt sein.In the drawing, a plastic plate 11 is shown roughly schematically, which is transported in the direction 12 . For this purpose, a supply roll 13 is provided, from which the plastic plate is unwound and wound onto another shaft 14 . Between the supply roll 13 and the shaft 14 is located above the plastic sheet 11 is a means 15 for applying plastic particles 16 for producing a rough surface 17 of the plastic plate. 11 In front of this application device 15 , the surface 18 of the plastic plate 11 can be smooth.
Die Einrichtung 15 weist eine Düseneinrichtung 19 auf, mit der eine Flamme 20 aus einem brennbaren Gasgemisch 21 erzeugt werden kann. Die Düseneinrichtung weist ferner eine nicht naher dargestellte Einbringeinrichtung auf, durch die die zugeführten Kunststoffpartikel 16 in die Flamme oder in das brennbare Gasgemisch eingeführt werden können. Die Kunststoffpartikel gelangen von einem Vorratsbehälter 22 zu der Düseneinrichtung 19. Es kann vorgesehen werden, daß dem Vorratsbehälter ein Granulat mit einer Größe von 2 bis 8 mm zugeführt wird, und daß die aufzubringenden Kunststoffpartikel durch ein Mahlwerk 23 auf die gewünschte Größe von 200 µm bis 1 mm gemahlen werden.The device 15 has a nozzle device 19 with which a flame 20 can be generated from a combustible gas mixture 21 . The nozzle device also has an introduction device (not shown in more detail) through which the supplied plastic particles 16 can be introduced into the flame or into the combustible gas mixture. The plastic particles pass from a storage container 22 to the nozzle device 19 . It can be provided that a granulate with a size of 2 to 8 mm is fed to the storage container and that the plastic particles to be applied are ground to the desired size of 200 μm to 1 mm by a grinder 23 .
Die Kunststoffpartikel 16 werden in der Flamme oberflächlich erhitzt. Es bildet sich ein heißer Randbereich 24, in dem etwa Schmelztemperatur herrscht, und ein Kernbereich 25, in dem ein Partikel noch im wesentlichen starr oder zumindest noch nicht geschmolzen ist. Hierdurch wird erreicht, daß sich jedes Partikel fest mit der Oberfläche verbindet und die gewünschte Rauhigkeit durch den noch festen Kern erreicht wird.The plastic particles 16 are heated superficially in the flame. A hot edge region 24 , in which the melting temperature is approximately, and a core region 25 , in which a particle is still essentially rigid or at least not yet melted, is formed. This ensures that each particle is firmly connected to the surface and the desired roughness is achieved by the still solid core.
Es kann zusätzlich vorgesehen werden, daß die Kunststoffplatte in Transportrichtung 12 vor der Düseneinrichtung 19 oberflächlich erwärmt wird. Hierzu ist eine Heizeinrichtung 26 vorgesehen, die als Heizmittel beispielsweise Heizstäbe 27 aufweist. Hierdurch wird der obere Randbereich 28 der Kunststoffplatte erhitzt, wodurch sich beim Auftreffen der Kunststoffpartikel auf die Oberfläche der Kunststoffplatte ein feste Verbindung ergibt.It can also be provided that the plastic plate is heated superficially in the transport direction 12 in front of the nozzle device 19 . For this purpose, a heating device 26 is provided which, for example, has heating rods 27 as heating means. This heats the upper edge region 28 of the plastic plate, which results in a firm connection when the plastic particles strike the surface of the plastic plate.
Bei dem in der Zeichnung dargestellten Ausführungsbeispiel ist die Kunststoffplatte horizontal unter der Flammdüse angeordnet. Es ist selbstverständlich auch möglich, die Kunststoffpartikel von unten auf die Oberfläche zu bringen. Ohnehin erfolgt der Austrag der Partikel unter Druck, so daß dies ohne weiteres möglich ist. Dies kann insbesondere dann zweckmäßig sein, wenn die Kunststoffplatte in einem Arbeitsschritt von beiden Seiten beschichtet werden soll. Es kann aber auch vorgesehen werden, daß die Kunststoffplatte vertikal verläuft und die Flammdüsen horizontal auf einer Seite oder auf beiden Seiten der Kunststoffplatte angeordnet sind.In the embodiment shown in the drawing, the plastic plate arranged horizontally under the flame nozzle. It is of course also possible that Bring plastic particles onto the surface from below. The discharge takes place anyway the particles under pressure so that this is easily possible. In particular, this can then be useful if the plastic plate in one step of both Sides to be coated. But it can also be provided that the Plastic plate runs vertically and the flame nozzles horizontally on one side or are arranged on both sides of the plastic plate.
Durch das Verfahren wird erreicht, daß die Kunststoffpartikel nur kurze Zeit einer hohen Temperatur ausgesetzt sind. Es entsteht eine lediglich oberflächliche Erhitzung, so daß eine thermische Umstrukturierung der Kunststoffmoleküle nicht zu erwarten ist. Es hat sich gezeigt, daß durch das Aufbringen keine oder nur geringe Unterschiede im Schmelzindex (Melt Flow Rate, MFR) auftreten. Der Schmelzindex des eingesetzten Kunststoffes liegt vor dem Auftragen beispielsweise bei 1,6 bis 1,9. Nach dem Auftragen auf die Oberfläche der Kunststoffplatte konnte ein Schmelzindex von 2,0 gemessen werden. Der Schmelzindex der Kunststoffplatte verändert sich ebenfalls nicht. Bei bisherigen Verfahren konnte der Kunststoff nach dem Auftragen einen Schmelzindex von bis zu 20 aufweisen. Es ist offensichtlich, daß sich die physikalischen und auch die chemischen Eigenschaften der Kunststoffpartikel, die mit dem oben beschriebenen Verfahren auf eine Kunststoffplatte aufgetragen werden, nicht oder nur unwesentlich verändern. Es ist daher möglich, eine Kunststoffplatte, beispielsweise für Deponieabdichtungen, vorzusehen, deren rauhe Vorsprünge aus dem gleichen Kunststoff wie die Kunststoffplatte bestehen, die zudem die gleichen physikalischen und chemischen Eigenschaften aufweisen. The method ensures that the plastic particles only a short time exposed to high temperatures. There is only superficial heating, so that a thermal restructuring of the plastic molecules is not to be expected. It has been shown that no or only slight differences in the Melt flow rate (MFR) occur. The melt index of the used Plastic is, for example, 1.6 to 1.9 before application. After this When applied to the surface of the plastic plate, a melt index of 2.0 was possible be measured. The melt index of the plastic plate also does not change. In previous processes, the plastic could be one after application Have melt index of up to 20. It is obvious that the physical and also the chemical properties of the plastic particles with the method described above are not applied to a plastic plate or change only marginally. It is therefore possible to use a plastic plate, for landfill seals, for example, the rough projections of which the same plastic as the plastic plate, which are also the same have physical and chemical properties.
1111
Kunststoffplatte
Plastic plate
1212th
Transportrichtung
Direction of transport
1313
Vorratsrolle
Supply roll
1414
Welle
wave
1515
Aufbringeinrichtung
Application device
1616
Kunststoffpartikel
Plastic particles
1717th
rauhe Oberfläche der Kunststoffplatte
rough surface of the plastic plate
1818th
ebene Oberfläche der Kunststoffplatte
flat surface of the plastic plate
1919th
Düseneinrichtung
Nozzle device
2020th
Flamme
flame
2121
Gasgemisch
Gas mixture
2222
Vorratsbehälter
Storage container
2323
Mahlwerk
Grinder
2424th
Randbereich
Edge area
2525th
Kernbereich
Core area
2626
Heizeinrichtung
Heating device
2727
Heizstäbe
Heating elements
2828
Randbereich
Edge area
Claims (22)