DE19525689C1

DE19525689C1 - Woven fabric tape used for bridging cracks in walls

Info

Publication number: DE19525689C1
Application number: DE19525689A
Authority: DE
Inventors: Detlev Dr Kapser
Original assignee: Individual
Current assignee: Individual
Priority date: 1995-07-14
Filing date: 1995-07-14
Publication date: 1996-11-14
Anticipated expiration: 2015-07-15

Abstract

The use of woven glass fibre tape as a crack-bridging support for alkaline inorganic coatings on mineral substrates is claimed. The warp and weft threads in the fabric are woven with a wide-meshed plain weave, and the centre section of the tape has additional mesh-filling warp threads.

Description

Die Erfindung betrifft die Verwendung eines Gewebebandes auf mineralischem Untergrund zur Rißüberbrückung.The invention relates to the use of a fabric tape on a mineral base for bridging cracks.

Bei Sanierungs-, Restaurations- und Renovierungsarbeiten an Außen- und Innenfassaden müssen vorhandene Risse beseitigt werden, bevor die Fassade mit einem neuen Anstrich versehen werden kann. Aus der DE-GMS 73 06 581 ist die Verwendung eines Gewebebandes aus Polyester als rißüberbrückender Träger für Anstriche bekannt, dessen Kett- und Schußfäden weitmaschig gewebt sind und in dessen Mittelbereich zusätzliche maschenfüllende Kettfäden eingezogen sind. Das bekannte Gewebe weist an seiner wandseitigen Fläche eine von einer Schutzfolie abgedeckte dauerklebrige Beschichtung aus einem Haftklebstoff auf und kann leicht auf die Fassade aufge bracht sowie im Zuge der Anstricharbeiten überstrichen werden. Im Bereich des Risses bildet das Gewebe einen Träger für das Anstrichmittel und verhindert, daß dieses abplatzt, wenn der Riß arbeitet. Bei organischen Anstrich systemen, beispielsweise Dispersionsfarben auf Acrylharz basis, Butadien-Styrol-Mischpolymerisaten und dergleichen, eignet sich das bekannte Gewebe und erlaubt eine zuver lässige und dauerhafte Rißüberbrückung.For renovation, restoration and renovation work External and internal facades must remove existing cracks be repainted before the facade can be. DE-GMS 73 06 581 describes the use of a Fabric tape made of polyester as a crack-bridging carrier for Paintings known, the warp and weft threads wide are woven and additional in the middle area stitch-filling warp threads are drawn in. The known Tissue has one of one on its wall-side surface Protective film covered permanent adhesive coating from one Pressure sensitive adhesive on and can easily be applied to the facade brings and painted in the course of painting will. The tissue forms one in the area of the tear Carrier for the paint and prevents this flakes off when the crack works. With organic painting systems, for example emulsion paints on acrylic resin base, butadiene-styrene copolymers and the like, is the known fabric and allows a verver casual and permanent crack bridging.

Als wetter- und waschbeständige Anstriche werden bevorzugt anorganische, alkalische Anstriche auf mineralischen Untergründen verwendet. Dazu gehören insbesondere Wasser glasanstriche, die eine hohe Beständigkeit gegenüber Säuren und Laugen aufweisen. Sie reagieren hochalkalisch, vor allem während der Abbindezeit und weisen auch nach Jahren noch eine Alkalität um pH 10 auf. Die Anstriche sind beständig gegen die in der Luft enthaltenen sauren Abgase, schützen säureempfindliche Untergründe, wie Sandstein, Putz usw. und zeichnen sich infolge ihres kristallinen Charakters durch eine hohe Gas- und Wasserdampfdurchlässig keit aus, so daß im Baukörper vorhandene Feuchtigkeit nach außen abgegeben werden kann. Bei Verwendung alkalischer, anorganischer Anstrichsysteme ist allerdings eine Über brückung von Rissen in der zu überstreichenden Fassade nicht oder nur unbefriedigend möglich. Bekannte Trägergewebe aus Polyester sind ungeeignet. Die Haftung der Anstrichmittel an diesen Geweben ist schlecht. In der Praxis werden die Risse mit Spachtelmasse verfüllt. Die Risse treten jedoch zumeist nach kurzer Dauer wieder auf.As weather and wash resistant coatings are preferred inorganic, alkaline coatings on mineral Substrates used. This particularly includes water glass paints that have a high resistance to acids and have alkalis. You react highly alkaline, before all during the setting time and show even after years alkalinity around pH 10. The paintings are resistant to the acidic exhaust gases contained in the air, protect acid-sensitive substrates, such as sandstone, plaster etc. and stand out due to their crystalline Character of a high gas and water vapor permeability speed, so that moisture present in the building can be delivered outside. When using alkaline, inorganic paint systems is, however, an over bridging cracks in the facade to be painted not possible or only unsatisfactorily. Known Backing fabrics made of polyester are unsuitable. The liability of Paint on these fabrics is bad. In the In practice, the cracks are filled with filler. The However, cracks usually reappear after a short period.

Der Erfindung liegt die Aufgabe zugrunde, eine dauerhafte Überbrückung von Rissen in Wandflächen vorzusehen, die mit einem alkalischen, anorganischen Anstrich versehen werden sollen.The invention has for its object a permanent Bridging cracks in wall surfaces to be provided with an alkaline, inorganic paint should.

Gegenstand der Erfindung und Lösung dieser Aufgabe ist die Verwendung eines Textilglas-Gewebebandes, dessen Kett- und Schußfäden mit einer Leinwandbindung weitmaschig gewebt sind und in dessen Mittelbereich zusätzliche maschen ausfüllende Kettenfäden eingezogen sind, als rißüber brückender Träger für alkalische anorganische Anstriche auf mineralischem Untergrund. Zur Herstellung des Textilglas gewebes eignen sich Glasfilamentgarne und Glasstapel fasergarne. Eine möglichst geringe Faserdicke wird angestrebt. Die Abmessungen des Mittelbereiches sind so gewählt, daß der Riß einschließlich seiner Einzugsbereiche großzügig überspannt wird. Bei einer üblichen Rißbreite von 2 bis 3 mm sollte der Mittelbereich eine Breite von 3 bis 5 cm aufweisen. An diesen schließen sich seitliche Randbereiche von mehreren Zentimetern Breite an. Die Maschenweite in den beiden Randbereichen des Textil glasgewebes ist so eingestellt, daß unter Einbettung des Textilglasgewebes ein inniger Kontakt zwischen dem Anstrich und dem mineralischen Untergrund hergestellt wird, wenn der Anstrich auf den Untergrund aufgetragen wird. Quadratische Maschen mit einer Maschenweite von 1 bis 3 mm sind bevorzugt.The object of the invention and solution to this problem is Use of a textile glass fabric tape, its warp and Weft threads with a plain weave woven wide are and in the middle area additional stitches filling chain threads are drawn in as tears bridging support for alkaline inorganic paints mineral background. For the production of textile glass glass filament yarn and glass stacks are suitable fiber yarns. The smallest possible fiber thickness is sought. The dimensions of the middle area are like this chosen that the crack including its catchment areas is spanned generously. With a usual crack width of The middle area should be 2 to 3 mm wide by 3 to 5 cm exhibit. These are connected to the sides Border areas several centimeters wide. The Mesh size in the two edge areas of the textile glass fabric is set so that with embedding the Textile glass fabric an intimate contact between the paint and the mineral substrate is produced when the Paint is applied to the surface. Square Stitches with a mesh size of 1 to 3 mm prefers.

Der Mittelbereich bildet eine Trennschicht zwischen An strichmittel und mineralischem Untergrund im Rißbereich. Als vorteilhaft erweist es sich jedoch, wenn der auf das Textilglasgewebe aufgebrachte Anstrich in dem rißüber brückenden Mittelbereich des Textilglasgewebes an gleich mäßig verteilten Kontaktpunkten Berührungskontakt mit dem mineralischen Untergrund hat.The middle area forms a separating layer between An paint and mineral substrate in the crack area. However, it proves to be advantageous if the on the Textile glass fabric applied in the crack above bridging central area of the textile glass fabric at the same moderately distributed contact points in contact with the has mineral subsurface.

Der punktweise Berührungskontakt fördert die Haftung des Gitters bis hin zur unmittelbaren Nähe des Risses und verhindert das Bilden störender Lufttaschen zwischen dem Textilglasgewebe und dem mineralischen Untergrund. Die Durchlässigkeit ist durch die Anzahl bzw. den Abstand der Kettfäden beeinflußbar. Im Rahmen der Erfindung liegt es auch, den Mittelbereich mit feinen Perforationen zu versehen. Der Anteil der für den Berührungskontakt zwischen Anstrich und Untergrund maßgebenden freien Fläche ist klein und beträgt bezogen auf die Oberfläche des Mittelbereichs maximal 5%, vorzugsweise etwa 1 bis 3%. The point-to-point contact promotes the liability of the Grid up to the immediate vicinity of the crack and prevents the formation of annoying air pockets between the Textile glass fabric and the mineral base. The Permeability is determined by the number or spacing of the Warp threads can be influenced. It is within the scope of the invention also, the middle section with fine perforations too Mistake. The share of the touch contact between The paint and sub-surface area is small and is based on the surface of the central region at most 5%, preferably about 1 to 3%.

Im Rahmen der Erfindung liegt es, die wandseitige Fläche des Textilglasgewebes einschließlich des Mittelbereiches mit einer von einer Schutzfolie abgedeckten dauerklebrigen Beschichtung aus einem Haftklebstoff auszurüsten. Eine selbstklebende Haftschicht erleichtert die Montage des Textilglas-Gewebebandes auf dem Untergrund. Nach dem Auftrag des Anstrichmittels bedarf es der zusätzlichen Klebeverbindung durch die Beschichtung nicht mehr. Insofern ist unschädlich, wenn der Haftklebstoff alkaliunbeständig ist und seine Wirkung verliert, nachdem das Anstrichmittel aufgebracht ist.The wall-side surface lies within the scope of the invention of the textile glass fabric including the middle area with a permanent adhesive covered with a protective film Equip coating with a pressure sensitive adhesive. A self-adhesive layer facilitates the assembly of the Textile glass fabric tape on the surface. After this Applying the paint requires the additional Adhesive connection through the coating no longer. To that extent is harmless if the pressure sensitive adhesive is alkali-resistant and loses its effect after the paint is applied.

Für die erfindungsgemäße Verwendung bevorzugt ist ein Textilglas-Gewebeband mit der folgenden Spezifikation:A is preferred for the use according to the invention Textile glass fabric tape with the following specification:

Material, Kette und Schuß: 340 dtex Z 28 Textilglas EC 9T 8Material, warp and weft: 340 dtex Z 28 textile glass EC 9T 8

Ausrüstung: SBR-LatexEquipment: SBR latex

Fadendichte:
Kette: ca. 14,5 Fd/cm
Schuß: ca. 6,1 Fd/cmThread density:
Chain: about 14.5 Fd / cm
Weft: approx.6.1 Fd / cm

Gesamtflächengewicht: ca. 86 g/m²
Randbereich: ca. 57 g/m²
verstärker Mittelbereich: ca. 150 g/m²Total weight: approx. 86 g / m²
Edge area: approx. 57 g / m²
reinforced middle area: approx. 150 g / m²

Höchstzugkraft:
Kette im Randbereich: ca. 128 N/cm
Kette im verstärkten Mittelbereich: ca. 544 N/cm
Schuß: ca. 75 N/cmMaximum traction:
Chain in the edge area: approx. 128 N / cm
Chain in the reinforced central area: approx. 544 N / cm
Shot: approx. 75 N / cm

Höchstzugkraftdehnung:
Kette: ca. 2,5%
Schuß: ca. 2,5%.Maximum tensile strain:
Chain: approx.2.5%
Shot: approx. 2.5%.

Claims

1. Use of a textile glass fabric tape, its warp and Weft threads with a plain weave woven wide are and in the middle area additional stitches Filling warp threads are drawn in as tears bridging support for alkaline, inorganic paints on a mineral surface.

2. Use of a textile glass fabric tape according to claim 1, with the glass fibers in at the center area laterally subsequent edge areas of the fabric tape square Form stitches with a mesh size of 1 to 3 mm.

3. Use of a textile glass fabric tape according to claim 1 or 2, the central region being 3 to 5 cm wide having.

4. Use of a textile glass fabric tape according to one of the Claims 1 to 3, wherein the permeability of the agent range is set so that the applied paint at evenly distributed contact points with the mineral underground.

5. Use of a textile glass fabric tape according to claim 4, the proportion of the touch contact between Paint and substrate related to the relevant free area maximum 5% on the surface of the central area, is preferably about 1 to 3%.

6. Use of a textile glass fabric tape according to one of the Claims 1 to 5, wherein the wall-side surface of the Textile glass fabric including the central area one permanent adhesive coating covered by a protective film from a pressure sensitive adhesive.