DE1214875B - Process for the production of laminated bodies - Google Patents
Process for the production of laminated bodiesInfo
- Publication number
- DE1214875B DE1214875B DEP17180A DEP0017180A DE1214875B DE 1214875 B DE1214875 B DE 1214875B DE P17180 A DEP17180 A DE P17180A DE P0017180 A DEP0017180 A DE P0017180A DE 1214875 B DE1214875 B DE 1214875B
- Authority
- DE
- Germany
- Prior art keywords
- styrene
- layers
- rubber
- copolymers
- vulcanization
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Description
Verfahren zum Herstellen von Schichtkörpern Es ist bekannt, Bodenbeläge oder Matten, wie sie z. B. in Kraftfahrzeugen zur Anwendung kommen, aus Kautschukplatten herzustellen. Neben der Vulkanisation in der Presse sind auch Verfahren bekannt und üblich, bei denen die unvulkanisierten Kautschukplatten mittels Vakuum an eine Formwandung angesaugt und dann die Vulkanisation im Dampf durchgeführt wird.Method for producing laminated bodies It is known, floor coverings or mats, as they are e.g. B. are used in motor vehicles, made of rubber sheets to manufacture. In addition to vulcanization in the press, processes are also known and usual, in which the unvulcanized rubber sheets by means of vacuum to a Sucked in the mold wall and then the vulcanization is carried out in the steam.
Für verschiedene Zwecke werden diese Bodenbeläge mit Farblacken bestrichen oder übersprüht. Hierbei können Nachteile verschiedener Art auftreten. So ist es z. B. möglich, daß Bestandteile aus der Grundplatte den farbigen Überzug durchdringen und verfärben. These floor coverings are coated with colored lacquers for various purposes or sprayed over. Disadvantages of various kinds can occur here. That's the way it is z. B. possible that components from the base plate penetrate the colored coating and discolor.
Ferner muß das für den Lack verwendete Lösungsmittel verdampfen, wobei der Arbeitsablauf bei der Herstellung zwangläufig verzögert wird.Furthermore, the solvent used for the paint must evaporate, with the production workflow is inevitably delayed.
Es ist weiterhin bekannt, Polystyrol oder Mischpolymerisate aus Styrol und Butadien als Zusätze zu Kautschukmischungen zu verwenden und die Härte des Endvulkanisates zu erhöhen. Diese Zusätze werden normalerweise in Mengen von 5 bis 300/o Styrol, bezogen auf 100 Teile Gummi, verwendet. It is also known to use polystyrene or styrene copolymers and butadiene to be used as additives to rubber mixtures and the hardness of the end vulcanizate to increase. These additives are normally used in amounts of 5 to 300 / o styrene, based on 100 parts of rubber.
Ferner ist es bekannt, für Behälter mehrschichtige Überzüge herzustellen, die eine Schicht aus nicht vulkanisiertem Kautschuk enthalten und dessen andere Schicht aus einem vulkanisierfähigen Gemisch aus einem Styrolmischpolymerisat -mit ldeineren Mengen eines kautschukartigen Butadien-Styrol-Mischpolymerisates besteht. It is also known to produce multilayer coatings for containers, which contain a layer of unvulcanized rubber and the other Layer of a vulcanizable mixture of a styrene copolymer -with ldeiner amounts of a rubber-like butadiene-styrene copolymer.
Bei diesem Schichtmaterial bestehen beide Schichten gleichzeitig aus Kautschuk und Styrol-Butadien-Mischpolymerisat mit hohem Styrolgehalt wechselnder Zusammensetzung. With this layer material, both layers exist at the same time made of rubber and styrene-butadiene mixed polymer with a high styrene content Composition.
Ein solcher Schichtstoff hat aber eine zu geringe Elastizität und Strukturfestigkeit, um den Anforderungen, die an Automatten, Schläuche und Fensterrahmenprofile gestellt werden, gerecht zu werden. Die Thermoplastizität dieser Schichtstoffe ist ein weiteres Hindernis für die vorteilhafte Anwendung bei den genannten Fällen. However, such a laminate has too little elasticity and Structural strength to meet the requirements placed on car mats, tubes and window frame profiles be asked to meet. The thermoplasticity of these laminates is another obstacle to the advantageous application in the named cases.
Für das Überziehen von Metallteilen mit Polystyrol ist es bekannt, eine Zwischenschicht aus Polyvinylchlorid, Natur- oder Kunstkautschuk vorzusehen. For coating metal parts with polystyrene, it is known to provide an intermediate layer of polyvinyl chloride, natural or synthetic rubber.
Bekanntlich ist aber reines Polystyrol recht spröde, so daß zur Aufgabe und Lösung der Erfindung keine Beziehung besteht.As is known, however, pure polystyrene is quite brittle, so that the task and solution of the invention is not related.
Bei der Herstellung von Spielbällen ist es auch bekannt, die Außenschicht mit einer Schicht aus Guttapercha und thermoplastischen Vinylharzen zu überziehen. In the manufacture of game balls, it is also known to use the outer layer to be covered with a layer of gutta-percha and thermoplastic vinyl resins.
Zur Bildung eines Schutzüberzuges im Innern eines Reifens oder ähnlicher Gegenstände ist es auch schon bekanntgeworden, Mischungen aus Kautschuk, Kunstkautschuk und Weichmachern aufzutragen. To form a protective coating inside a tire or the like It is already objects become known, mixtures of rubber, synthetic rubber and to apply plasticizers.
Zum Herstellen von Formkörpern wie z. B. Schuhen ist außerdem bekannt, die Form durch Tauchen in Latex mit einer Schicht zu überziehen. Dabei können Mischpolymerisate aus Styrol, Butadien oder Acrylsäurenitril angewendet werden. For the production of moldings such. B. Shoes is also known to coat the mold with a layer by dipping it in latex. Copolymers can be used made of styrene, butadiene or acrylonitrile can be used.
Schließlich ist auch die Herstellung eines Gleitschutzes für Laufflächen durch Aufbringen von Überzügen aus weichmacherhaltigen Polymerisaten oder Kondensaten bekannt. Die zuletzt genannten Verfahren stehen nicht in Beziehung zum Erfindungsgegenstand. Finally, there is also the production of anti-skid protection for running surfaces by applying coatings of plasticizer-containing polymers or condensates known. The last-mentioned methods are not related to the subject matter of the invention.
Gegenstand der Erfindung ist ein Verfahren zum Herstellen von Schichtkörpern durch Verbinden einer oder mehrerer vulkanisierbarer Kautschukschichten mit einer oder mehreren Schichten aus Polystyrol oder Mischpolymerisaten aus Styrol und Butadien, die einen hohen Styrolgehalt besitzen, und Verschweißen der erhaltenen Schichtkörper durch Vulkanisation, das dadurch gekennzeichnet ist, daß solche Schichten aus Homo- oder Mischpolymerisaten des Styrols verwendet werden, die außerdem Chlorparaffin und vulkanisierbare synthetische Kautschukpolymerisate enthalten. Die Schichtkörper sind geeignet für Bodenbeläge, Schläuche, Spritzkörper und andere Artikel. The invention relates to a method for producing laminated bodies by joining one or more vulcanizable rubber layers with one or several layers of polystyrene or copolymers of styrene and butadiene, which have a high styrene content, and welding of the laminated bodies obtained by vulcanization, which is characterized in that such layers of homo- or copolymers of styrene can be used, which also contain chlorinated paraffin and vulcanizable synthetic rubber polymers. The laminated body are suitable for floor coverings, hoses, spray bodies and other items.
Die erhaltenen Schichtkörper besitzen eine hohe Strukturfestigkeit und verfärben die - Deckschichten nicht. Dabei kann bei der Grundplatte von einer Mischung ausgegangen werden, die einen hohen Anteil an Regenerat enthält, so daß neben den niedrigen Materialkosten eine für die Verarbeitung so sehr erwünschte Standfestigkeit des Rohlings erhalten wird. The laminated bodies obtained have a high structural strength and do not discolor the - top layers. In this case, one can use the base plate Mixture are assumed that contains a high proportion of regrind, so that In addition to the low material costs, one that is so very desirable for processing Stability of the blank is obtained.
Als Kautschuk wird hier Natur- und Synthesekautschuk verstanden. Natural and synthetic rubber are understood here as rubber.
Ein Vorteil des beanspruchten Verfahrens ist es, daß auf diese Weise auch eine hochstyrolhaltige Mischung bei der Vulkanisation noch untrennbar mit Kautschuk verschweißt werden kann. Dabei ist es von Bedeutung, daß durch die polystyrolhaltige Schicht mit Chlorparaffin keine Bestandteile der Kautschukzusatzstoffe, insbesondere Alterungsschutzmittel, mehr hindurchdringen können, die die gefärbten Schichten unansehnlich machen. An advantage of the claimed method is that in this way Even a mixture with a high styrene content is still inseparable from rubber during vulcanization can be welded. It is important that the polystyrene-containing Layer with chlorinated paraffin no components of the rubber additives, in particular Anti-aging agents, more that can penetrate the colored layers make unsightly.
Nach der Erfindung hat es sich als vorteilhaft erwiesen, daß der vulkanisierbare Anteil, bezogen auf Polystyrol, mindestens 50/0 beträgt. According to the invention it has proven advantageous that the vulcanizable proportion, based on polystyrene, is at least 50/0.
Zur Verbesserung der Wetterbeständigkeit können zusätzlich Polychloropren, Butylkautschuk oder chlor sulfoniertes Polyäthylen mit verwendet werden. To improve the weather resistance, polychloroprene, Butyl rubber or chlorosulfonated polyethylene can also be used.
Als Weichmacher für das Gemisch aus Polystyrol oder Styrolmischpolymerisat und Kautschuk kommt Chlorparaffin als Weichmacher in Frage. As a plasticizer for the mixture of polystyrene or styrene copolymer and rubber can be used as a plasticizer with chlorinated paraffin.
Bei der oben beschriebenen Überzugsmischung kann auch Polyvinylchlorid, insbesondere als Mischpolymerisat mit Styrol, verwendet werden. Hierdurch wird eine weitere Verbesserung der Festigkeit, Dehnung und Verschleißfestigkeit der Überzüge erreicht und gleichzeitig die Verarbeitungseigenschaft der Mischung verbessert. In the coating mixture described above, polyvinyl chloride, can be used in particular as a copolymer with styrene. This creates a further improvement of the strength, elongation and wear resistance of the coatings achieved and at the same time the processing properties of the mixture improved.
Als Füllstoffe können gefällte Kreide und alle übrigen in der Kautschuk- und Kunststoffindustrie verwendeten Füllstoffe verwendet werden. Precipitated chalk and all the rest of the rubber can be used as fillers. and fillers used in the plastics industry.
Folgende Beispiele erläutern die Erfindung: Beispiel 1 Eine hochregenerathaltige vulkanisierbare Naturkautschukplatte wird am Kalander mit einer Folie doubliert, die aus folgender Mischung besteht: Gewichtsteile Butadien-Styrol-Mischpolymerisat ....... 100 Polystyrol ............................ 100 Chlorparaffin (Chlorgefalt: 70%) ....... 25 Dioctylphthalat ....................... 25 Titanweiß ............................ 5 Farbstoff............................. 1 Zinkweiß 5 Schwefel ............................. 2,5 Umsetzungsprodukt aus Mercaptobenzothiazol und Cyclohexylamin .......... 2 Tetramethylthiuramdisulfid ............. 2 Anschließend erfolgen die Verarbeitung und Vulkanisation auf der Mattenherstellungsmaschine.Dabei wird der doublierte Mattenrohling auf eine Mattenform gelegt, durch Vakuum abgesaugt, geformt und anschließend der Formkörper auf der Matte in einem Druckkessel 8 Minuten bei 188°C vulkanisiert. Der Überzug hat die folgenden Eigenschaften: Festigkeit (kg/cm2) 120 Dehnun (%) ...................... 150 Shorehärte (A) 95 Beispiel 2 Für die Herstellung einer Riefenmatte wird eine Grundplatte wie im Beispiell mit einem Überzug versehen, der aus der folgenden Mischung besteht: Gewichtsteile Styrol-Butadien-Mischpolymerisat (70 : 30) ......................... 100 Styrol-Butadien-Mischpolymerisat (90 : 10) ......................... 100 Chlorparaffin (Chlorgehalt: 60% .... 40 Chlorbutadienpolymerisat ............ 20 Magnesiumoxyd, schwer ......... 1 Zinkoxyd .... . ........... 2 Schwefel ........................... 1,5 Umsetzungsproduckt aus Mercaptobenzothiazol und Cyclohexylamin ........ 1 Tetramethylthiuramdisulfid ........... 1 Vulkanisation: 6 Minuten bei 155°C. The following examples explain the invention: Example 1 A highly regenerated vulcanizable natural rubber sheet is lined with a film on the calender, which consists of the following mixture: parts by weight of butadiene-styrene copolymer ....... 100 polystyrene ............................ 100 chlorinated paraffin (chlorine content: 70%) ....... 25 dioctyl phthalate ....................... 25 titanium white ............. ............... 5 dye ............................. 1 zinc white 5 sulfur ............... .............. 2.5 Reaction product of mercaptobenzothiazole and cyclohexylamine .......... 2 Tetramethylthiuram disulfide ............. 2 Processing and vulcanization then take place on the Mat manufacturing machine, in which the doubled mat blank is placed on a mat shape placed, sucked off by vacuum, shaped and then the shaped body on the Mat vulcanized in a pressure vessel at 188 ° C for 8 minutes. The coating has the following properties: strength (kg / cm2) 120 elongation (%) ...................... 150 Shore hardness (A) 95 Example 2 For the production of a grooved mat, a Base plate provided with a coating as in the example, which consists of the following mixture consists: Parts by weight of styrene-butadiene copolymer (70:30) ......................... 100 styrene-butadiene copolymer (90:10) ......................... 100 chlorinated paraffin (Chlorine content: 60% .... 40 chlorobutadiene polymer ............ 20 magnesium oxide, heavy ......... 1 zinc oxide ..... ........... 2 sulfur ........................... 1.5 Reaction product from mercaptobenzothiazole and cyclohexylamine ........ 1 tetramethylthiuram disulfide ........... 1 vulcanization: 6 minutes at 155 ° C.
Für den Überzug wurden die folgenden Eigenschaften ermittelt: Festigkeit (kg/cm²) ................. 120 Dehnung (%) ...................... 250 Schorehärte (A) ..................... 98 Alterung nach 6 Wochen Bewetterung einer 0,2-mm-Folie ................ gut B e i s p i e l 3 Für die Herstellung von Schläuchen wird das Verfahren in der Weise durchgeführt, daß mit dem Strangpressen des Schlauches ein zweiter Vorgang verbunden wird, der in dem gleichen Profilkopf vorgenommen wird. The following properties were determined for the coating: Strength (kg / cm²) ................. 120 elongation (%) ...................... 250 Shore hardness (A) ..................... 98 Aging after 6 weeks of exposure to a 0.2 mm film ................ good Example 3 For the manufacture of hoses, that is Process carried out in such a way that with the extrusion of the hose a second operation is connected, which is carried out in the same profile head.
Der Innenschlauch hat folgende Zusammensetzung: Gewichtsteile Rohkautschuk ..................... 20 Butadienstyrolkautschuk ............. 20 Bitumen ........................... 4 Weichmacher ......................... 5,6 Schwefel ........................... 0,9 Zinkweiß .......................... 3,0 Beschleuniger Vulkacit CZ (Mercaptobenzothiazol-Cyclohexylamin) ...... 0,6 Ruß halbaktiv .. ................. 28 Kieselkreide ........................ 17,7 Alterungsschutzmittel ............... 0,2 Der Überzug des Schlauches besteht aus der folgenden Zusammensetzung: Gewichtsteile Styrol-Butadien-Mischpolymerisat (70 : 30) ......................... 100 Styrol-Butadien-Mischpolymerisat (90 : 10) ......................... 100 Chlorparaffin (Chlorgehalt: 60%) ..... 40 Isobutylen-Isopren-Mischpolymerisat .. 20 Zinkoxyd .......................... 2 Schwefel ........................... 1,5 Umsetzungsprodukt aus Mercaptobenzothiazol und Cyclohexylamin ........ 1 Tetramethylthiuramdisulfid ........... 1 Vulkanisation: 6 Minuten bei 155°C. The inner tube has the following composition: parts by weight of raw rubber ..................... 20 butadiene styrene rubber ............. 20 bitumen ............ ............... 4 plasticizers ......................... 5,6 sulfur ................... ........ 0.9 zinc white .......................... 3.0 accelerator Vulkacit CZ (mercaptobenzothiazole-cyclohexylamine) ...... 0.6 soot semi-active .. ................. 28 pebble chalk .................. ...... 17.7 Anti-aging agent ............... 0.2 The hose is coated from the following composition: parts by weight of styrene-butadiene copolymer (70: 30) ......................... 100 styrene-butadiene copolymer (90: 10) ......................... 100 Chlorinated paraffin (chlorine content: 60%) ..... 40 Isobutylene-isoprene copolymer .. 20 zinc oxide .......................... 2 sulfur .................. ......... 1.5 Reaction product of mercaptobenzothiazole and cyclohexylamine ........ 1 tetramethylthiuram disulfide ........... 1 vulcanization: 6 minutes at 155 ° C.
Der Schlauchüberzug weist die folgenden Eigenschaften auf: Festigkeit (kg/cm²) .................. 130 Dehnung (%) ...................... 270 Shorehärte (A) ..................... 97 Alterung nach 6 Wochen Bewetterung einer 0,2-mm-Folie ................ sehr gut Beispiel 4 Die Herstellung von Profilen erfolgt wie im Beispiel 3. The hose cover has the following properties: Strength (kg / cm²) .................. 130 elongation (%) ...................... 270 shore hardness (A) ..................... 97 Aging after 6 weeks of exposure to a 0.2 mm film ................ very good Example 4 The manufacture of profiles takes place as in example 3.
Als Überzug dient die folgende Mischung: Gewichtsteile Styrol-Butadien-Mischpolymerisat (70 : 30) ............... ....... . 100 Styrol-Butadien-Mischpolymerisat (90:10) .......................... 100 Chlorparaffin (Chlorgehalt: 60°/o) .. 40 Chlorsulfoniertes Polyäthylen . 20 Zinkoxyd ............. ....... 2 Hydrierte Harzsäuren ............. 3 Schwefel ........................... 1,5 Umsetzungsprodukt aus Mercaptobenzothiazol und Cyclohexylamin ...... 1 Tetramethylthiuramdisulfid .......... 1 Vulkanisation: 6 Minuten bei 155"C.The following mixture is used as the coating: parts by weight of styrene-butadiene copolymer (70: 30) ............... ........ 100 styrene-butadiene copolymer (90:10) .......................... 100 chlorinated paraffin (chlorine content: 60%) .. 40 chlorosulphonated Polyethylene. 20 Zinc Oxide ............. ....... 2 Hydrogenated Resin Acids ............. 3 Sulfur ........................... 1.5 Reaction product from mercaptobenzothiazole and cyclohexylamine ...... 1 tetramethylthiuram disulfide .......... 1 vulcanization: 6 minutes at 155 "C.
Der Überzug hat die folgenden Eigenschaften: Festigkeit (kg/cm2) 110 Dehnung (%) ...................... 300 Shorehärte (A) ..................... 98 Alterung nach 6 Wochen Bewetterung einer 0,2-mm-Folie gut Beispiel 5 Ein Fußbodenbelag wird wie im Beispiel 1 hergestellt, wobei der Überzug aus folgender Mischung besteht: Gewichtsteile Styrol-Butadien-Mischpolymerisat (90 : 10) ......................... 100 Vinylchlorid-Styrol-Mischpolymerisat (70 : 30) ......................... 100 Butadien-Styrol-Mischpolymerisat (76:24) 40 40 Chlorparaffin (Chlorgehalt: 700/o) 30 Dioctylphthalat ..................... 30 Titandioxyd ........................ 20 The coating has the following properties: Strength (kg / cm2) 110 Elongation (%) ...................... 300 Shore hardness (A) .................. ... 98 Aging after 6 weeks of weathering a 0.2 mm film good Example 5 A floor covering is produced as in Example 1, with the coating consisting of the following mixture: Parts by weight of styrene-butadiene copolymer (90:10) ......................... 100 vinyl chloride-styrene copolymer (70:30) ......................... 100 Butadiene-styrene copolymer (76:24) 40 40 chlorinated paraffin (chlorine content: 700 / o) 30 dioctyl phthalate ..................... 30 titanium dioxide ........................ 20th
Claims (2)