DE102009058182A1 - Composite component, useful as e.g. an interior component of track, comprises a substrate from thermoplastic containing a polymer e.g. aromatic polyesters, a rubber-modified vinyl(co)polymer and a polymer additive and polyurethane layer - Google Patents

Abstract

Composite component comprises (a) a substrate from a thermoplastic composition containing (A) at least one polymer comprising aromatic polyester carbonates or aromatic polyesters in a proportion of (A) of 20-85 parts by weight, (B1) at least one rubber-modified vinyl(co)polymer in a proportion of (B1) of 15-80 parts by weight, having a rubber content [KB] of at least 25 parts by weight, and (C) at least one polymer additive in a proportion of (C) of 0-30 parts by weight, and (b) at least one polyurethane layer. Composite component comprises (a) a substrate from a thermoplastic composition containing (A) at least one polymer comprising aromatic polyester carbonates or aromatic polyesters in a proportion of (A) of 20-85 parts by weight, based on the sum of components A and B1, (B1) at least one rubber-modified vinyl(co)polymer in a proportion of (B1) of 15-80 parts by weight, based on the sum of components A and B1, having a rubber content [KB] of at least 25 parts by weight, based on component (B1), and (C) at least one polymer additive in a proportion of (C) of 0-30 parts by weight, based on the sum of components A-C, and (b) at least one polyurethane layer, where the thermoplastic composition is characterized by an overall rubber content, based on the sum of components A and B1, of at least 12 parts by weight.

Description

The present invention relates to composite components with high toughness and stable composite adhesion, which contain a structuring support made of a polycarbonate and / or polyester composition having a good processability and at least one polyurethane layer, and their use and a method for their preparation.

• a) Formen eines Substrats in einer ersten Kavität des Formwerkzeugs,
• b) das Einbringen des im vorangegangenen Schritt hergestellten Substrats in eine zweite Kavität des Formwerkzeugs und
• c) Beschichten des Substrats in der zweiten Kavität mit einem Lack, wobei das Beschichten unter erhöhtem Druck erfolgt.

WO 2006/072366 A1 describes a method of forming and coating a substrate in a mold having at least two cavities. The method comprises the steps:

• a) forming a substrate in a first cavity of the mold,
• b) introducing the substrate produced in the previous step into a second cavity of the mold and
• c) coating the substrate in the second cavity with a lacquer, wherein the coating is carried out under elevated pressure.

By way of example and preference, polyurethane coatings and PC + ABS substrates (polycarbonate + acrylonitrile-butadiene-styrene substrates) are mentioned. About the influence of the carrier material composition on the adhesive properties of the composite materials are given no indication in this application.

• a) Herstellen eines Trägerbauteils,
• b) Verbringen oder Umsetzen des Trägerbauteils in eine geöffnete Kavität eines Werkzeugs,
• c) Schließen des Werkzeugs bis auf eine vorbestimmte Position, wobei eine vergrößerte Kavität mit einer ersten Größe geschaffen ist,
• d) Erzeugen eines Unterdrucks in der vergrößerten Kavität erster Größe,
• e) Einfüllen eines Flutungsmaterials in die vergrößerte Kavität und
• f) Durchführen eines Prägeschrittes gleichzeitig mit dem Einfüllen und/oder anschließend an das Einfüllen des Flutungsmaterials, wobei die Kavität zumindest geringfügig verkleinert wird.

DE 10 2006 048 252 B3 discloses a method for producing a composite component, in particular comprising an injection-molded part and a polyurethane element, with the steps

• a) producing a carrier component,
• b) moving or transferring the carrier component into an opened cavity of a tool,
• c) closing the tool to a predetermined position creating an enlarged cavity of a first size,
• d) generating a negative pressure in the enlarged first size cavity,
• e) filling a flooding material in the enlarged cavity and
• f) performing an embossing step simultaneously with the filling and / or subsequent to the filling of the flooding material, wherein the cavity is at least slightly reduced.

To improve the bond adhesion, activation of the surface of the thermoplastic by flaming, plasma or gas is described here. The influence of the carrier material composition on the adhesive properties of the composite material is not mentioned in this publication.

DE 10 2006 033 059 A1 discloses a method for producing plastic interior parts. Here, in a first step, the carrier is formed in a first tool, wherein the first tool is at least partially replaced by a second tool and then in a second step, the cover layer is formed on the carrier. Here comes as a carrier material, a hard component, for. As PA + ABS blends (polyamide + acrylonitrile-butadiene-styrene) or PC + ABS blends (polycarbonate + acrylonitrile-butadiene-styrene), and as a cover layer, a soft component, preferably polyurethane foam used. About the influence of the composition of the support materials on the composite properties of the components thus produced are given no indication in the application. Rather, in DE 10 206 033 059 A1 also proposed to improve the adhesion, to prepare the surface by primer or laser, corona, or plasma treatment.

WO 99/20464 discloses composites of at least two different directly interconnected plastics materials, wherein a) is a thermoplastic polymer or a thermoplastic mixture of polymers comprising at least one polar compound of at least one of the metals of the 1st to 5th main group or the 1st to 8th subgroup of the periodic table as finely divided inorganic powder and b) polyurethane, which is present as a foam, lacquer or as a compact material. For the composite no adhesive layer is needed. On the influence of the carrier material composition in terms of ABS and rubber content on the adhesive properties of the composite material, no indications are given in this publication.

DE 101 09 226 A1 discloses a polycarbonate composition comprising a) aromatic polycarbonate and / or polyester carbonate, b) graft polymer and c) copolymer of styrene and a carboxyl group-containing monomer, wherein the copolymer has an average molecular weight Mw of> = 10,500 g / mol, and wherein the copolymer is a or more vinyl monomers. Component C is preferably a copolymer of styrene and maleic anhydride. DE 101 09 226 A1 continues to disclose Composite components comprising at least a first layer (1) and a second layer (2), wherein layer (1) comprises at least one polycarbonate composition (as indicated under a, b and c) and layer (2) contains at least one polyurethane. The composite is characterized in that the decrease in the foam adhesion between layer (1) and layer (2) after a double-cycle change test (KWT) is at most 35%. About the influence of the carrier material composition in terms of ABS and rubber content on the adhesive properties of the composite material, no indications are given in this publication.

The object of the present invention was to provide alternative composite components with high toughness and improved composite adhesion, which contain a structuring support made of a polycarbonate and / or polyester composition with good processability and at least one polyurethane layer, their use, and methods for producing these composite components.

The polyurethane layer can serve, for example, for improving the surface properties, the feel, the appearance, the noise and heat insulation of the composite components.

• a) einen Träger aus einer thermoplastischen Zusammensetzung enthaltend
• A) mindestens ein Polymer ausgewählt aus der Gruppe der aromatischen Polycarbonate, aromatischen Polyestercarbonate und aromatischen Polyester in einem Anteil von [A] von 20,0 bis 85,0 Gew.-Teilen, bezogen auf die Summe der Komponenten A und B,
• B) mindestens ein kautschukmodifiziertes Vinyl(co)polymerisat in einem Anteil von [B] von 15,0 bis 80,0 Gew.-Teilen, bezogen auf die Summe der Komponenten A und B, mit einem Kautschukgehalt [K_B] von mindestens 25,0 Gew.-Teilen, bezogen auf die Komponente B und
• C) mindestens ein Polymeradditiv in einem Anteil von [C] von 0 bis 30,0 Gew.-Teilen, bezogen auf die Summe der Komponenten A bis C, sowie
• b) mindestens eine Polyurethanschicht, wobei die thermoplastische Zusammensetzung gekennzeichnet ist durch einen Gesamtkautschukgehalt, bezogen auf die Summe der Komponenten A und B, von mindestens 12 Gew.-Teilen.

The object of the present invention is achieved by composite components comprising

• a) containing a carrier of a thermoplastic composition
• A) at least one polymer selected from the group of aromatic polycarbonates, aromatic polyester carbonates and aromatic polyesters in a proportion of [A] of 20.0 to 85.0 parts by weight, based on the sum of components A and B,
• B) at least one rubber-modified vinyl (co) polymer in a proportion of [B] of 15.0 to 80.0 parts by weight, based on the sum of components A and B, having a rubber content [K _B ] of at least 25 , 0 parts by weight, based on the component B and
• C) at least one polymer additive in a proportion of [C] from 0 to 30.0 parts by weight, based on the sum of components A to C, and
• b) at least one polyurethane layer, wherein the thermoplastic composition is characterized by a total rubber content, based on the sum of components A and B, of at least 12 parts by weight.

• a) einen Träger aus einer thermoplastischen Zusammensetzung enthaltend
• A) mindestens ein Polymer ausgewählt aus der Gruppe der aromatischen Polycarbonate, aromatischen Polyestercarbonate und aromatischen Polyester in einem Anteil von [A] von 20,0 bis 85,0 Gew.-Teilen, bezogen auf die Summe der Komponenten A und B,
• B) mindestens ein kautschukmodifiziertes Vinyl(co)polymerisat in einem Anteil von [B] von 15,0 bis 80,0 Gew.-Teilen, bezogen auf die Summe der Komponenten A und B, mit einem Kautschukgehalt [K_B] von mindestens 25,0 Gew.-Teilen, bezogen auf die Komponente B und
• C) mindestens ein Polymeradditiv in einem Anteil von [C] von 0 bis 30,0 Gew.-Teilen, bezogen auf die Summe der Komponenten A bis C, sowie
• b) mindestens eine Polyurethanschicht, wobei die thermoplastische Zusammensetzung gekennzeichnet ist durch einen Quotienten Q = [B]/[K_B] von < 2 und einen Kautschukgehalt [K] = [K_B]·[B]/100, bezogen auf die Summe der Komponenten A und B, von mindestens 12 Gew.-Teilen.

Further and preferred, the object of the present invention is achieved by composite components comprising

• a) containing a carrier of a thermoplastic composition
• A) at least one polymer selected from the group of aromatic polycarbonates, aromatic polyester carbonates and aromatic polyesters in a proportion of [A] of 20.0 to 85.0 parts by weight, based on the sum of components A and B,
• B) at least one rubber-modified vinyl (co) polymer in a proportion of [B] of 15.0 to 80.0 parts by weight, based on the sum of components A and B, having a rubber content [K _B ] of at least 25 , 0 parts by weight, based on the component B and
• C) at least one polymer additive in a proportion of [C] from 0 to 30.0 parts by weight, based on the sum of components A to C, and
• b) at least one polyurethane layer, wherein the thermoplastic composition is characterized by a quotient Q = [B] / [K _B ] of <2 and a rubber content [K] = [K _B ] · [B] / 100, based on the sum of components A and B, of at least 12 parts by weight.

The rubber content of the component B [K _B ] is preferably 25.0 to 80.0 parts by weight, more preferably 25.0 to 50.0 parts by weight, especially 30.0 to 45.0 parts by weight.

The total rubber content and the rubber content [K], in each case based on the sum of components A and B, is at least 12 parts by weight, preferably at least 13 parts by weight, and more preferably at least 14 parts by weight.

The total rubber content and the rubber content [K], in each case based on the sum of the components A and B, is preferably at most 35 parts by weight, more preferably at most 30 parts by weight, particularly preferably 25 parts by weight, wherein the ranges of the above upper and lower limits can be freely combined.

The total rubber content and the rubber content [K] in each case based on the sum of the components A and B is preferably 12-35 parts by weight, more preferably from 13-30 parts by weight and particularly preferably 14 to 25 parts by weight.

The polyurethane layer may be, for example, a PU varnish, a PU foam or a compact PU skin with polyurethane layer thicknesses of, for example, 1 .mu.m up to 20 cm.

In a preferred embodiment, the polyurethane layer is a paint having a layer thickness of 1-1000 microns.

In a further preferred embodiment, the polyurethane layer is a compact skin with a layer thickness of 1 mm-10 mm.

In a further preferred embodiment, the polyurethane layer is a foam with a layer thickness of 4 mm-20 cm.

The composite components can in principle be produced in any known manner.

• – mindestens eine Polyisocyanat-Komponente,
• – mindestens eine polyfunktionelle H-aktive Verbindung, und
• – optional mindestens ein Polyurethan-Additiv und/oder Prozesshilfsstoff

in direktem Kontakt mit dem zuvor aus der thermoplastischen Zusammensetzung geformten und erstarrten Träger.The polyurethane layer is preferably produced by polymerization of a reactive polyurethane raw material mixture containing

• At least one polyisocyanate component,
• At least one polyfunctional H-active compound, and
• Optionally at least one polyurethane additive and / or processing aid

in direct contact with the carrier previously formed and solidified from the thermoplastic composition.

The carrier component can be prefabricated, for example, from the thermoplastic PC + ABS composition and then applied to the reactive polyurethane raw material mixture and reacted. Depending on the reactivity of the polyurethane reaction components, these may already be premixed or mixed during application in a known manner. The application can be done, inter alia, by spraying, knife coating or calendering.

But it is also possible to produce the composites of the invention by coextrusion by known methods.

In the case where foamed composites are to be produced, the reaction mixture can be introduced in a manner known per se into a mold containing the preformed and solidified support component. Optionally, the shape of a further decorative layer (often called "skin") from z. As polyvinyl chloride (PVC), thermoplastic polyolefins (TPO), thermoplastic polyurethane (TPU) or Polyurethanansprühhaut included. In the mold, the foamable reaction mixture foams in contact with the carrier component and optionally the decorative layer and forms the composite component. The foaming of the mold can be carried out in such a way that the composite component has a cell structure on its surface. But it can also be carried out so that the composite component has a compact skin and a cellular core (integral skin foams). The polyurethane components can be introduced into the mold with high-pressure or low-pressure machines. Polyurethane foams can also be made as a block foam.

The production of polyurethane composites can also be done in sandwich construction. The process can be equipped both as a depot or Hüllbauverfahren. Both the Depotbauweise and Hüllbauweise are known per se. In the depot process (filling construction), two half-shells (eg cover layers made of plastics) are prefabricated, placed in a mold and the cavity between the shells is foamed up with the PUR foam. In Hüllbauweise a core of PUR foam is placed in a tool and then with a suitable shell material, eg. B. with one of said thermoplastics wrapped. In the manufacture of sandwich composite bodies, the envelope construction is preferred.

• (i) in einem ersten Verfahrensschritt die Schmelze der thermoplastischen Zusammensetzung in eine erste Werkzeugkavität eingespritzt und nachfolgend abgekühlt wird,
• (ii) in einem zweiten Verfahrensschritt die Kavität des Spritzgusswerkzeugs vergrößert und dadurch ein Spaltraum erzeugt wird,
• (iii) im dritten Verfahrensschritt in den so resultierenden Spaltraum zwischen dem thermoplastischen Bauteil und der Werkzeugoberfläche der vergrößerten Kavität ein reaktives Polyurethanrohstoffgemisch enthaltend
• – mindestens eine Polyisocyanat-Komponente,
• – mindestens eine polyfunktionelle H-aktive Verbindung, und
• – optional mindestens ein Polyurethan-Additiv und/oder Prozesshilfsstoff gespritzt wird, wobei das Polyurethanrohstoffgemisch im direkten Kontakt mit der Oberfläche des thermoplastischen Trägers zu einer kompakten Polyurethanschicht oder zu einer Polyurethanschaumschicht auspolymerisiert, und
• (iv) im vierten Verfahrensschritt das Verbundbauteil aus der Werkzeugkavität entformt wird.

In a preferred embodiment of the invention, the composite components are produced by a method in the

• (i) in a first method step the melt of the thermoplastic composition is injected into a first mold cavity and subsequently cooled,
• (ii) the cavity of the injection molding tool is enlarged in a second method step, thereby creating a gap space,
• (Iii) in the third step in the resulting gap between the thermoplastic component and the tool surface of the enlarged cavity containing a reactive polyurethane raw material mixture
• At least one polyisocyanate component,
• At least one polyfunctional H-active compound, and
• Optionally, at least one polyurethane additive and / or processing aid is sprayed, the polyurethane raw material mixture polymerizing in direct contact with the surface of the thermoplastic carrier to form a compact polyurethane layer or to a polyurethane foam layer, and
• (iv) in the fourth method step, the composite component is removed from the mold cavity.

In a further preferred embodiment of the invention, the method steps (i) to (iv) follow one another directly during composite component production.

The immediate sequence of process steps prevents the temperature of the workpiece from cooling to room temperature during the process. This achieves a reduction of the production times and a higher energy efficiency of the overall process.

The process steps (ii) and (iii) can be repeated at least once, with variation of the polyurethane system, wherein one or more polyurethane layers are applied to only one or both sides of the support so that a composite component of thermoplastic support and at least two identical or different polyurethane layers. Components with possibly also more than two-layer structure results.

Before removing the workpiece in steps (ii) and (iv), the workpiece is cooled to dimensional stability.

To produce the gap in method step (ii), either the injection mold can be opened and subsequently one half of the injection mold cavity replaced by a new half with larger cavity dimensions, or the component from the first mold cavity into a second, with respect to its mold cavity larger cavity thereof or a second tool implemented, or the first cavity to be opened by a gap.

The reaction of the substrate in process step (ii) can be carried out by known processes, as used for example in multicolor injection molding. Typical methods are on the one hand the turntable, insert, Schiebekavität or index plate or similar methods in which the substrate remains on a core. If the substrate remains to be transferred on the core, this has the advantage that the position is defined accurately even after transfer. On the other hand, known from the prior art, methods for reacting a substrate, in which the substrate, for. B. using a handling system, taken from a cavity and placed in another cavity. The reaction with removal of the substrate offers greater design freedom in the coating, for. For example, when generating a wrap around or masked areas.

Preference is given to composite components in which the quotient Q is less than 1.7, in particular less than 1.5.

• A) 30,0 bis 64,9 Gew.-Teile, insbesondere 40,0 bis 64,9 Gew.-Teile, besonders bevorzugt 40,0 bis 55,0 Gew.-Teile, bezogen auf die Summe der Komponenten A und B, mindestens eines Polymers ausgewählt aus der Gruppe der aromatischen Polycarbonate, aromatischen Polyestercarbonate und aromatischen Polyester,
• B) 35,1 bis 70,0 Gew.-Teile, insbesondere 35,1 bis 60,0 Gew.-Teile, besonders bevorzugt 45,0 bis 60,0 Gew.-Teile, bezogen auf die Summe der Komponenten A und B, mindestens eines kautschukmodifizierten Vinyl(co)polymerisats.

The thermoplastic compositions used in the production of the composite components according to the invention preferably contain

• A) 30.0 to 64.9 parts by weight, in particular 40.0 to 64.9 parts by weight, particularly preferably 40.0 to 55.0 parts by weight, based on the sum of components A and B. , at least one polymer selected from the group consisting of aromatic polycarbonates, aromatic polyester carbonates and aromatic polyesters,
• B) 35.1 to 70.0 parts by weight, in particular 35.1 to 60.0 parts by weight, particularly preferably 45.0 to 60.0 parts by weight, based on the sum of the components A and B. , at least one rubber-modified vinyl (co) polymer.

Component C is preferably used in a proportion of 0 to 20.0 parts by weight, in particular 0.1 to 10.0 parts by weight, based on the sum of components A to C, is used.

The thermoplastic compositions used in the production of the composite components according to the invention preferably comprise as component A a mixture of at least one aromatic polycarbonate and / or polyester carbonate and at least one aromatic polyester.

In a preferred embodiment, a thermoplastic polymer composition is used in the first process step, which at room temperature and particularly preferably at -30 ° C a tough fracture behavior in the impact test after ISO 180-1A , characterized by a notch impact value greater than 30 kJ / m ² , and / or a tough (non-splitting) fracture pattern in the puncture test ISO 6603 shows.

The reactive polyurethane raw material mixtures used in the production of the composite components according to the invention preferably have an index of> 80 to <125, more preferably> 100 to <120, and particularly preferably from 105 to 115.

The index is defined as the percentage ratio of the actual amount of isocyanate used to the calculated stoichiometric amount in the case of complete polyol conversion, ie. H. Code = (amount of isocyanate used / amount of iso-stoichiometric, calculated) × 100.

In an alternative embodiment, a thermoplastic polyurethane may also be used instead of the reactive polyurethane raw material mixture.

In a further preferred embodiment, the surface of the injection molding tool which is in contact with the thermoplastic polymer composition in process step (iii) is heated to a temperature in the range from 50 to 95.degree. C., preferably from 60 to 85.degree. C., and particularly preferably from 60 to 80.degree.

In a further preferred embodiment, the surface of the injection molding tool which is in contact with the reactive polyurethane mixture in process step (iii) is at a temperature in the range from 50 to 160.degree. C., preferably from 70 to 120.degree. C., more preferably from 80 to 110.degree preferably heated to 90 to 100 ° C.

In a further preferred embodiment, the contacting with the thermoplastic polymer composition surface of the injection mold in step (iii) to a temperature in the range 50 to 95 ° C, preferably 60 to 85 ° C, and more preferably 60 to 80 ° C tempered and the surface of the injection molding tool in contact with the reactive polyurethane mixture is heated to a temperature in the range from 50 to 160 ° C., preferably from 70 to 120 ° C., more preferably from 80 to 110 ° C., and particularly preferably from 90 to 100 ° C.

In the case of a foamed polyurethane system with a decorative layer, in an alternative embodiment, the surface of the foaming tool which is in contact with the thermoplastic polymer composition or with the decorative skin may be heated to a temperature in the range from 20 to 80 ° C., preferably from 30 to 60 ° C. become.

The composite component according to the invention are particularly suitable as an inner or outer component of a rail, aviation or motor vehicle.

In a particularly preferred embodiment, the composite component at -30 ° C a tough (not splintering) breaking behavior under multiaxial impact load measured on the fracture pattern in the penetration test after ISO 6603 on.

The composite adhesion between the polycarbonate composition carrier and the polyurethane coating in the composite components according to the invention is in a preferred embodiment at least 1 N / mm measured on strip samples taken from the component having a width of 20 mm in a roller peel test according to FIG DIN 53357 A with a test speed of 100 mm / min.

The polymer compositions used in the process according to the invention contain:

Component A

Aromatic polycarbonates and polyester carbonates according to component A which are suitable according to the invention are known from the literature or can be prepared by processes known from the literature (for the preparation of aromatic polycarbonates see, for example Schnell, "Chemistry and Physics of Polycarbonates", Interscience Publishers, 1964 as well as the DE-AS 1 495 626 . DE-A 2 232 877 . DE-A 2 703 376 . DE-A 2 714 544 . DE-A 3 000 610 . DE-A 3 832 396 ; for the preparation of aromatic polyester carbonates, for. B. DE-A 3 077 934 ).

The preparation of aromatic polycarbonates and polyester carbonates takes place for. Example, by reacting diphenols with carbonic acid halides, preferably phosgene, and / or with aromatic dicarboxylic acid dihalides, preferably Benzoldicarbonsäuredihalogeniden, by the interfacial process, optionally using chain terminators, for example monophenols and optionally using trifunctional or more than trifunctional branching agents, for example triphenols or tetraphenols , Likewise, preparation via a melt polymerization process by reaction of diphenols with, for example, diphenyl carbonate is possible.

wobei
A eine Einfachbindung, C₁ bis C₅-Alkylen, C₂ bis C₅-Alkyliden, C₅ bis C₆ Cycloalkyliden, -O-, -SO-, -CO-, -S-, -SO₂-, C₆ bis C₁₂-Arylen, an das weitere aromatische gegebenenfalls Heteroatome enthaltende Ringe kondensiert sein können,
oder ein Rest der Formel (II) oder (III)

B jeweils C₁ bis C₁₂-Alkyl, vorzugsweise Methyl, Halogen, vorzugsweise Chlor und/oder Brom
x jeweils unabhängig voneinander 0, 1 oder 2,
p 1 oder 0 sind, und
R⁵ und R⁶ für jedes X¹ individuell wählbar, unabhängig voneinander Wasserstoff oder C₁ bis C₆-Alkyl, vorzugsweise Wasserstoff, Methyl oder Ethyl,
X¹ Kohlenstoff und
m eine ganze Zahl von 4 bis 7, bevorzugt 4 oder 5 bedeuten, mit der Maßgabe, dass an mindestens einem Atom X¹, R⁵ und R⁶ gleichzeitig Alkyl sind.Diphenols for the preparation of the aromatic polycarbonates and / or aromatic polyester carbonates are preferably those of the formula (I)

in which
A is a single bond, C ₁ to C ₅ alkylene, C ₂ to C ₅ alkylidene, C ₅ to C ₆ cycloalkylidene, -O-, -SO-, -CO-, -S-, -SO ₂ -, C ₆ to C ₁₂ -aryl, to which further aromatic rings containing optionally heteroatoms may be condensed,
or a radical of the formula (II) or (III)

B is in each case C ₁ to C ₁₂ -alkyl, preferably methyl, halogen, preferably chlorine and / or bromine
x each independently 0, 1 or 2,
p is 1 or 0, and
R ⁵ and R ^{6 are} individually selectable for each X ¹ , independently of one another hydrogen or C ₁ to C ₆ -alkyl, preferably hydrogen, methyl or ethyl,
X ¹ carbon and
m is an integer from 4 to 7, preferably 4 or 5, with the proviso that on at least one atom X ¹ , R ⁵ and R ^{6 are} simultaneously alkyl.

Preferred diphenols are hydroquinone, resorcinol, dihydroxydiphenols, bis (hydroxyphenyl) -C ₁ -C ₅ -alkanes, bis (hydroxyphenyl) -C ₅ -C ₆ -cycloalkanes, bis (hydroxyphenyl) ethers, bis (hydroxyphenyl) sulfoxides, bis (hydroxyphenyl) ketones, bis (hydroxyphenyl) sulfones and α, α-bis (hydroxyphenyl) diisopropyl-benzenes and their nuclear-brominated and / or nuclear-chlorinated derivatives.

Particularly preferred diphenols are 4,4'-dihydroxydiphenyl, bisphenol-A, 2,4-bis (4-hydroxyphenyl) -2-methylbutane, 1,1-bis (4-hydroxyphenyl) -cyclohexane, 1,1-bis- (4-hydroxyphenyl) -3,3,5-trimethylcyclohexane, 4,4'-dihydroxydiphenylsulfide, 4,4'-dihydroxydiphenylsulfone and their di- and tetrabrominated or chlorinated derivatives such as 2,2-bis (3-chloro-4-hydroxyphenyl) propane, 2,2-bis (3,5-dichloro-4-hydroxyphenyl) -propane or 2,2-bis (3,5-dibromo-4-hydroxyphenyl) -propane. Particularly preferred is 2,2-bis (4-hydroxyphenyl) propane (bisphenol-A).

The diphenols can be used individually or as any mixtures. The diphenols are known from the literature or obtainable by literature methods.

Chain terminators suitable for the preparation of the thermoplastic, aromatic polycarbonates are, for example, phenol, p-chlorophenol, p-tert-butylphenol or 2,4,6-tribromophenol, but also long-chain alkylphenols, such as 4- [2- (2,4,4 -Trimethylpentyl)] - phenol, 4- (1,3-tetramethylbutyl) phenol according to DE-A 2 842 005 or monoalkylphenol or dialkylphenols having a total of 8 to 20 carbon atoms in the alkyl substituents such as 3,5-di-tert-butylphenol, p-iso-octylphenol, p-tert-octylphenol, p-dodecylphenol and 2- (3,5- Dimethylheptyl) phenol and 4- (3,5-dimethylheptyl) phenol. The amount of chain terminators to be used is generally between 0.5 mol%, and 10 mol%, based on the molar sum of the diphenols used in each case.

The thermoplastic, aromatic polycarbonates may be branched in a known manner, preferably by the incorporation of 0.05 to 2.0 mol%, based on the sum of the diphenols used, of trifunctional or more than trifunctional compounds, for example those with three and more phenolic groups.

Both homopolycarbonates and copolycarbonates are suitable. For the preparation of inventive copolycarbonates according to component A, it is also possible to use from 1 to 25% by weight, preferably from 2.5 to 25% by weight, based on the total amount of diphenols to be used, of hydroxyaryloxy endblocked polydiorganosiloxanes. These are known ( US 3 419 634 ) and produced by literature methods. The preparation of polydiorganosiloxane-containing copolycarbonates is described in U.S. Patent Nos. 4,378,399 and 5,605,842 DE-A 3 334 782 described.

Preferred polycarbonates, in addition to the bisphenol A homopolycarbonates, are the copolycarbonates of bisphenol A with up to 15 mol%, based on the molar sums of diphenols, of other than preferred or particularly preferred diphenols, in particular 2,2-bis (3,5-bis). dibromo-4-hydroxyphenyl) propane.

Aromatic dicarboxylic acid dihalides for the preparation of aromatic polyester carbonates are preferably the diacid dichlorides of isophthalic acid, terephthalic acid, diphenyl ether-4,4'-dicarboxylic acid and naphthalene-2,6-dicarboxylic acid.

Particularly preferred are mixtures of the diacid dichlorides of isophthalic acid and terephthalic acid in the ratio between 1:20 and 20: 1.

In the production of polyester carbonates, a carbonyl halide, preferably phosgene, is additionally used as the bifunctional acid derivative.

As chain terminators for the preparation of the aromatic polyester are in addition to the aforementioned monophenols still their chloroformate and the acid chlorides of aromatic monocarboxylic acids, which may be substituted by C ₁ to C ₂₂ alkyl groups or by halogen atoms, and aliphatic C ₂ to C ₂₂ monocarboxylic acid chlorides into consideration.

The amount of chain terminators is in each case 0.1 to 10 mol%, based on moles of diphenol in the case of the phenolic chain terminators and on moles of dicarboxylic acid dichloride in the case of monocarboxylic acid chloride chain terminators.

The aromatic polyester carbonates may also contain incorporated aromatic hydroxycarboxylic acids.

The aromatic polyester carbonates can be branched both linearly and in a known manner (see DE-A 2 940 024 and DE-A 3 007 934 ).

Examples of suitable branching agents are trifunctional or polyfunctional carboxylic acid chlorides, such as trimesic acid trichloride, cyanuric trichloride, 3,3 ', 4,4'-benzophenone-tetracarboxylic acid tetrachloride, 1,4,5,8-naphthalene tetracarboxylic acid tetrachloride or pyromellitic acid tetrachloride, in amounts of 0.01 up to 1.0 mol% (based on the dicarboxylic acid dichlorides used) or trifunctional or polyfunctional phenols, such as phloroglucinol, 4,6-dimethyl-2,4,6-tri- (4-hydroxyphenyl) -hept-2-ene, 4, 6-Dimethyl-2,4,6-tris (4-hydroxyphenyl) heptane, 1,3,5-tris (4-hydroxyphenyl) benzene, 1,1,1-tri- (4-hydroxyphenyl) - ethane, tri- (4-hydroxyphenyl) -phenylmethane, 2,2-bis [4,4-bis (4-hydroxyphenyl) -cyclohexyl] -propane, 2,4-bis (4-hydroxyphenyl-isopropyl) -phenol , Tetra (4-hydroxyphenyl) methane, 2,6-bis (2-hydroxy-5-methylbenzyl) -4-methyl-phenol, 2- (4-hydroxyphenyl) -2- (2,4-dihydroxyphenyl ) -propane, tetra (4- [4-hydroxyphenyl-isopropyl] -phenoxy) -methane, 1,4-bis [4,4'-dihydroxytri-phenyl) -methyl] -benzene, in amounts of from 0.01 to 1 , 0 mol% based on diphenols used. Phenolic branching agents can be introduced with the diphenols, acid chloride branching agents can be added together with the acid dichlorides.

In the thermoplastic, aromatic polyester carbonates, the proportion of carbonate structural units can vary as desired. The proportion of carbonate groups is preferably up to 100 mol%, in particular up to 80 mol%, particularly preferably up to 50 mol%, based on the sum of ester groups and carbonate groups. Both the ester and the carbonate portion of the aromatic polyester carbonates may be present in the form of blocks or randomly distributed in the polycondensate.

The relative solution viscosity (η _rel ) of the aromatic polycarbonates and polyester carbonates is preferably in the range from 1.18 to 1.4, more preferably in the range from 1.20 to 1.32 (measured on solutions of 0.5 g of polycarbonate or polyester carbonate in 100 ml Methylene chloride solution at 25 ° C). The weight-average molecular weight Mw of the aromatic polycarbonates and polyestercarbonates is preferably in the range of 15,000 to 35,000, more preferably in the range of 20,000 to 33,000, particularly preferably 23,000 to 30,000, determined by GPC (gel permeation chromatography in methylene chloride with polycarbonate as a standard).

The aromatic polyesters which are suitable according to the invention as component A are, in a preferred embodiment, polyalkylene terephthalates. In a particularly preferred embodiment, these are reaction products of aromatic dicarboxylic acids or their reactive derivatives, such as dimethyl esters or anhydrides, and aliphatic, cycloaliphatic or araliphatic diols and mixtures of these reaction products.

Particularly preferred polyalkylene terephthalates comprise at least 80% by weight, preferably at least 90% by weight, based on the dicarboxylic acid component, of terephthalic acid residues and at least 80% by weight, preferably at least 90% by mol, based on the diol component of ethylene glycol and / or butanediol 1,4 radicals.

In addition to terephthalic acid residues, the preferred polyalkylene terephthalates may contain up to 20 mol%, preferably up to 10 mol%, of other aromatic or cycloaliphatic dicarboxylic acids having 8 to 14 carbon atoms or aliphatic dicarboxylic acids having 4 to 12 carbon atoms, such as. As residues of phthalic acid, isophthalic acid, naphthalene-2,6-dicarboxylic acid, 4,4'-diphenyldicarboxylic acid, succinic acid, adipic acid, sebacic acid, azelaic acid, cyclohexanediacetic acid.

The preferred polyalkylene terephthalates, in addition to ethylene glycol or butane-1,4-diol residues, may contain up to 20 mol%, preferably up to 10 mol%, of other aliphatic diols of 3 to 12 carbon atoms or cycloaliphatic diols of 6 to 21 carbon atoms. Contain atoms, z. B. residues of propanediol-1,3,2-ethylpropanediol-1,3, neopentyl glycol, pentanediol-1,5, hexanediol-1,6, cyclohexane-dimethanol-1,4, 3-ethylpentanediol-2,4,2- Methylpentanediol-2,4,2,2,4-trimethylpentanediol-1,3,2-ethylhexanediol-1,3,2,2-diethylpropanediol-1,3, hexanediol-2,5, 1,4-di (β -hydroxyethoxy) benzene, 2,2-bis (4-hydroxycyclohexyl) propane, 2,4-dihydroxy-1,1,3,3-tetramethylcyclobutane, 2,2-bis (4-β-hydroxyethoxy -phenyl) -propane and 2,2-bis (4-hydroxypropoxyphenyl) -propane ( DE-A 2 407 674 . 2 407 776 . 2,715,932 ).

The polyalkylene terephthalates can be prepared by incorporation of relatively small amounts of trihydric or trihydric alcohols or 3- or 4-basic carboxylic acids, e.g. B. according to DE-A 1 900 270 and U.S. Patent 3,692,744 to be branched. Examples of preferred branching agents are trimesic acid, trimellitic acid, trimethylolethane and -propane and pentaerythritol.

Particularly preferred are polyalkylene terephthalates which have been prepared solely from terephthalic acid and its reactive derivatives (eg their dialkyl esters) and ethylene glycol and / or butane-1,4-diol, and mixtures of these polyalkylene terephthalates.

Mixtures of polyalkylene terephthalates contain from 1 to 50% by weight, preferably from 1 to 30% by weight, of polyethylene terephthalate and from 50 to 99% by weight, preferably from 70 to 99% by weight, of polybutylene terephthalate.

The polyalkylene terephthalates preferably used have an intrinsic viscosity of 0.4 to 1.5 dl / g, preferably 0.5 to 1.2 dl / g, as measured in phenol / o-dichlorobenzene (1: 1 parts by weight) at 25 ° C. in the Ubbelohde viscometer.

The polyalkylene terephthalates can be prepared by known methods (see, for example, US Pat. Plastics Handbook, Volume VIII, p. 695 ff., Carl-Hanser-Verlag, Munich 1973 ).

Component B

Component B is rubber-based graft polymers B.1 or mixtures of rubber-based graft polymers B.1 with rubber-free. Vinyl (co) polymers B.2, wherein the rubber content of component B over the sum of the constituents is at least 25.0 parts by weight.

• B.1.1 5 bis 95, vorzugsweise 15 bis 92, insbesondere 25 bis 60 Gew.-%, bezogen auf Komponente B.1, wenigstens eines Vinylmonomeren auf
• B.1.2 95 bis 5, vorzugsweise 85 bis 8, insbesondere 75 bis 40 Gew.-%, bezogen auf Komponente B.1, einer oder mehrerer Pfropfgrundlagen mit Glasübergangstemperaturen < 10°C, vorzugsweise < 0°C, besonders bevorzugt < –20°C,

Component-B rubber-based graft polymers B.1 used

• B.1.1 5 to 95, preferably 15 to 92, in particular 25 to 60 wt .-%, based on component B.1, of at least one vinyl monomer on
• B.1.2 95 to 5, preferably 85 to 8, in particular 75 to 40 wt .-%, based on component B.1, one or more graft bases with glass transition temperatures <10 ° C, preferably <0 ° C, particularly preferably <-20 ° C,

The glass transition temperatures were determined by dynamic differential thermal analysis (DSC) according to the Standard DIN EN 61006 at a heating rate of 10 K / min with definition of T _g as the midpoint temperature (tangent method).

The graft base B.1.2 generally has an average particle size (d ₅₀ value) of 0.05 to 10.00 μm, preferably 0.1 to 5.0 μm, particularly preferably 0.2 to 1.0 μm.

The average particle size d ₅₀ is the diameter, above and below which each 50 wt .-% of the particles are. He can by means of Ultrazentrifugenmessung ( W. Scholtan, H. Lange, Colloid, Z. and Z. Polymere 250 (1972), 782-1796 ).

• B.1.1.1 50 bis 99, bevorzugt 65 bis 85, insbesondere 75 bis 80 Gew.-Teile, bezogen auf B.1.1, Vinylaromaten und/oder kernsubstituierten Vinylaromaten (wie Styrol, α-Methylstyrol, p-Methylstyrol, p-Chlorstyrol) und/oder Methacrylsäure-(C₁-C₈)-Alkylester, wie Methylmethacrylat, Ethylmethacrylat), und
• B.1.1.2 1 bis 50, bevorzugt 15 bis 35, insbesondere 20 bis 25 Gew.-Teilen, bezogen auf B.1.1, Vinylcyanide (ungesättigte Nitrile wie Acrylnitril und Methacrylnitril) und/oder (Meth)Acrylsäure-(C₁-C₈)-Alkylester, wie Methylmethacrylat, n-Butylacrylat, t-Butylacrylat, und/oder Derivate (wie Anhydride und Imide) ungesättigter Carbonsäuren, beispielsweise Maleinsäureanhydrid und N-Phenyl-Maleinimid.

Monomers B.1.1 are preferably mixtures of

• B.1.1.1 50 to 99, preferably 65 to 85, in particular 75 to 80 parts by weight, based on B.1.1, vinylaromatics and / or ring-substituted vinylaromatics (such as styrene, α-methylstyrene, p-methylstyrene, p-chlorostyrene ) and / or methacrylic acid (C ₁ -C ₈ ) -alkyl esters, such as methyl methacrylate, ethyl methacrylate), and
• B.1.1.2 1 to 50, preferably 15 to 35, in particular 20 to 25 parts by weight, based on B.1.1, of vinyl cyanides (unsaturated nitriles such as acrylonitrile and methacrylonitrile) and / or (meth) acrylic acid (C ₁ - C ₈ ) -alkyl esters, such as methyl methacrylate, n-butyl acrylate, t-butyl acrylate, and / or derivatives (such as anhydrides and imides) of unsaturated carboxylic acids, for example maleic anhydride and N-phenyl-maleimide.

Preferred monomers B.1.1.1 are selected from at least one of the monomers styrene, α-methylstyrene and methyl methacrylate, preferred monomers B.1.1.2 are selected from at least one of the monomers acrylonitrile, maleic anhydride and methyl methacrylate. Particularly preferred monomers are B.1.1.1 styrene and B.1.1.2 acrylonitrile.

Examples of suitable graft bases B.1.2 for the graft polymers B.1 are diene rubbers, EP (D) M rubbers, ie those based on ethylene / propylene and optionally diene, acrylate, polyurethane, silicone, chloroprene and ethylene / vinyl acetate. Rubbers and silicone / acrylate composite rubbers.

Preferred graft bases B.1.2 are diene rubbers, for example based on butadiene and isoprene, or mixtures of diene rubbers or copolymers of diene rubbers or mixtures thereof with further copolymerisable monomers (for example according to B.1.1.1 and B.1.1.2), with with the proviso that the glass transition temperature of component B.1.2 below <10 ° C, preferably <0 ° C, more preferably <-20 ° C.

Particularly preferred as the graft base B.1.2 is pure polybutadiene rubber.

Particularly preferred polymers B.1 are, for example, ABS or MBS polymers, as described for. B. in the DE-OS 2 035 390 (= U.S. Patent 3,644,574 ) or in the DE-OS 2 248 242 (= GB-PS 1 409 275 ) or in Ullmanns, Enzyklopadie der Technischen Chemie, Vol. 19 (1980), p. 280 ff. are described.

The graft copolymers B.1 are prepared by free-radical polymerization, for. B. by emulsion, suspension, solution or bulk polymerization, preferably by emulsion or bulk polymerization, in particular by emulsion polymerization.

In the case of graft polymers B.1 prepared in the emulsion polymerization process, the content of graft base B.1.2 is preferably 20 to 95% by weight, particularly preferably 40 to 85% by weight, in particular 50 to 75% by weight, in each case on B.1.

In the case of graft polymers B.1 prepared by the mass process, the content of graft base B.1.2 is preferably 5 to 50% by weight, more preferably 8 to 25% by weight, in particular 10 to 20% by weight, in each case on B.1.

The gel content of the graft base B.1.2 is at least 30% by weight, preferably at least 40% by weight, in particular at least 60% by weight, in each case based on B.1.2 and measured as the insoluble fraction in toluene.

Particularly suitable graft rubbers are also ABS polymers obtained by redox initiation with an initiator system of organic hydroperoxide and ascorbic acid according to U.S. Patent 4,937,285 getting produced.

Since, in the grafting reaction, the graft monomers are not necessarily completely grafted onto the grafting base, graft polymers B.1 according to the invention are also those products which are obtained by (co) polymerization of the grafting monomers in the presence of the grafting base and are obtained during the workup. These products can therefore also free, d. H. not chemically bound to the rubber (co) polymer of the graft monomers.

Suitable acrylate rubbers according to B.1.2 are preferably polymers of alkyl acrylates, optionally with up to 40 wt .-%, based on B.1.2 other polymerizable, ethylenically unsaturated monomers. Preferred polymerizable acrylic acid esters include C ₁ to C ₈ alkyl esters, for example, methyl, ethyl, butyl, n-octyl and 2-ethylhexyl esters; Haloalkyl, preferably halo-C ₁ -C ₈ alkyl esters, such as chloroethyl acrylate and mixtures of these monomers.

For crosslinking, monomers having more than one polymerizable double bond can be copolymerized. Preferred examples of crosslinking monomers are esters of unsaturated monocarboxylic acids having 3 to 8 C atoms and unsaturated monohydric alcohols having 3 to 12 C atoms, or saturated polyols having 2 to 4 OH groups and 2 to 20 C atoms, such as ethylene glycol dimethacrylate, allyl methacrylate ; polyunsaturated heterocyclic compounds such as trivinyl and triallyl cyanurate; polyfunctional vinyl compounds, such as di- and trivinylbenzenes; but also triallyl phosphate and diallyl phthalate. Preferred crosslinking monomers are allyl methacrylate, ethylene glycol dimethacrylate, diallyl phthalate and heterocyclic compounds having at least three ethylenically unsaturated groups. Particularly preferred crosslinking monomers are the cyclic monomers triallyl cyanurate, triallyl isocyanurate, triacryloylhexahydro-s-triazine, triallylbenzenes. The amount of crosslinked monomers is preferably 0.02 to 5.00, in particular 0.05 to 2.00 wt .-%, based on the graft B.1.2. In the case of cyclic crosslinking monomers having at least three ethylenically unsaturated groups, it is advantageous to limit the amount to less than 1.00% by weight of the graft base B.1.2.

Preferred "other" polymerizable, ethylenically unsaturated monomers which may optionally be used in addition to the acrylic acid esters for the preparation of the graft B.1.2, z. As acrylonitrile, styrene, α-methylstyrene, acrylamides, vinyl-C ₁ -C ₆ -alkyl ether, methyl methacrylate, butadiene. Preferred acrylate rubbers as the graft base B.1.2 are emulsion polymers which have a gel content of at least 60% by weight.

Further suitable grafting principles according to B.1.2 are silicone gums with graft-active sites as described in US Pat DE-OS 3 704 657 . DE-OS 3 704 655 . DE-OS 3 631 540 and DE-OS 3 631 539 to be discribed.

The gel content of the graft base B.1.2 or of the graft polymers B.1 is determined at 25 ° C. in a suitable solvent as insoluble in these solvents ( M. Hoffmann, H. Krömer, R. Kuhn, Polymer Analytics I and II, Georg Thieme-Verlag, Stuttgart 1977 ).

The rubber-free vinyl (co) polymers according to component B.2 are preferably rubber-free homopolymers and / or copolymers of at least one monomer from the group of vinylaromatics, vinyl cyanides (unsaturated nitriles), (meth) acrylic acid (C ₁ to C ₈ ) -alkyl esters, unsaturated carboxylic acids and derivatives (such as anhydrides and imides) of unsaturated carboxylic acids.

• B.2.1 50 bis 99 Gew.-%, bevorzugt 60 bis 80 Gew.-%, insbesondere 70 bis 80 Gew.-%, jeweils bezogen auf das Gesamtgewicht des (Co)Polymerisats B.2, mindestens eines Monomeren ausgewählt aus der Gruppe der Vinylaromaten, wie beispielsweise Styrol, α-Methylstyrol, kernsubstituierten Vinylaromaten, wie beispielsweise p-Methylstyrol, p-Chlorstyrol, und (Meth)Acrylsäure-(C₁-C₈)-Alkylester, wie beispielsweise Methylmethacrylat, n-Butylacrylat, tert.-Butylacrylat, und
• B.2.2 1 bis 50 Gew.-%, bevorzugt 20 bis 40 Gew.-%, insbesondere 20 bis 30 Gew.-%, jeweils bezogen auf das Gesamtgewicht des (Co)Polymerisats B.2, mindestens eines Monomeren ausgewählt aus der Gruppe der Vinylcyanide, wie beispielsweise ungesättigte Nitrile wie z. B. Acrylnitril und Methacrylnitril, (Meth)Acrylsäure-(C₁-C₈)-Alkylester, wie beispielsweise Methylmethacrylat, n-Butylacrylat, tert.-Butylacrylat, ungesättigte Carbonsäuren und Derivate ungesättigter Carbonsäuren, wie beispielsweise Maleinsäureanhydrid und N-Phenyl-Maleinimid.

Particularly suitable are (co) polymers B.2

• B.2.1 50 to 99 wt .-%, preferably 60 to 80 wt .-%, in particular 70 to 80 wt .-%, each based on the total weight of the (co) polymer B.2, at least one monomer selected from the group the vinyl aromatic such as styrene, α-methyl styrene, ring-substituted vinyl aromatic such as p-methyl styrene, p-chlorostyrene, and (meth) acrylic acid (C ₁ -C ₈ ) alkyl esters, such as methyl methacrylate, n-butyl acrylate, tert. Butyl acrylate, and
• B.2.2 1 to 50 wt .-%, preferably 20 to 40 wt .-%, in particular 20 to 30 wt .-%, each based on the total weight of the (co) polymer B.2, at least one monomer selected from the group the vinyl cyanides such as unsaturated nitriles such as. As acrylonitrile and methacrylonitrile, (meth) acrylic acid (C ₁ -C ₈ ) alkyl esters, such as methyl methacrylate, n-butyl acrylate, tert-butyl acrylate, unsaturated carboxylic acids and derivatives of unsaturated carboxylic acids, such as maleic anhydride and N-phenyl-maleimide ,

These (co) polymers B.2 are resinous, thermoplastic and rubber-free. The copolymer of B.2.1 styrene and B.2.2 acrylonitrile is particularly preferred.

Such (co) polymers B.2 are known and can be prepared by free-radical polymerization, in particular by emulsion, suspension, solution or bulk polymerization. The (co) polymers preferably have average molecular weights M _w (weight average, determined by GPC) between 15,000 g / mol and 250,000 g / mol, preferably in the range 80,000 to 150,000 g / mol.

Component C

The composition may contain as component C commercial polymer additives. As commercially available polymer additives according to component C are additives such as flame retardants (for example, phosphorus compounds such as phosphoric or phosphonic, phosphonate and phosphazenes or halogen compounds), Flammschutzsynergisten (for example, nanoscale metal oxides), smoke-inhibiting additives (for example, boric acid or bristle), anti-drip agents (for example compounds of the substance classes of fluorinated polyolefins, the silicones and aramid fibers), internal and external lubricants and mold release agents (for example pentaerythritol tetrastearate, stearyl stearate, montan wax or polyethylene wax), flowability aids (for example low molecular weight vinyl (co) polymers), antistatics (for example block copolymers of ethylene oxide and propylene oxide, other polyethers or Polyhydroxyethers, poletheramides, polyesteramides or sulphonic acid salts), conductivity additives (for example carbon black or carbon nanotubes), nucleating agents, stable curatives (for example UV / light stabilizers, heat stabilizers, antioxidants, transesterification inhibitors, hydrolysis protectants), antibacterial additives (for example silver or silver salts), scratch-resistance-improving additives (for example silicone oils or hard fillers such as ceramic (hollow) spheres), IR absorbents, optical brighteners , fluorescent additives, fillers and reinforcing materials (for example talc, optionally milled glass or carbon fibers, glass or ceramic (hollow) spheres, mica, kaolin, CaCO ₃ and glass flakes) and dyes and pigments (for example carbon black, titanium dioxide or iron oxide) Impact impact modifiers, which do not fall under the definition of B.1 and Brönstet acidic compounds as Rasenfänger, or mixtures of several of the additives mentioned in question.

Polyurethane

The coating used is preferably a polyurethane foam or a compact polyurethane layer.

The polyurethanes used according to the invention are obtained by reacting polyisocyanates with H-active polyfunctional compounds, preferably polyols.

In the context of this invention, the term "polyurethane" is also understood as meaning polyurethaneureas in which H-active polyfunctional compounds such compounds having NH functionality, if appropriate in admixture with polyols, are used.

Suitable polyisocyanates are the aromatic, araliphatic, aliphatic or cycloaliphatic polyisocyanates having an NCO functionality of preferably ≥ 2 which are known per se to the person skilled in the art and which also include iminooxadiazinedione, isocyanurate, uretdione, urethane, allophanate, biuret, urea, oxadiazinetrione , Oxazolidinone, acylurea and / or carbodiimide structures. These can be used individually or in any mixtures with each other.

The abovementioned polyisocyanates are based on diisocyanates or triisocyanates known per se with aliphatic, cycloaliphatic, araliphatic and / or aromatically bound isocyanate groups, it being immaterial whether these were prepared by using phosgene or by phosgene-free processes. Examples of such di- or triisocyanates are 1,4-diisocyanatobutane, 1,5-diisocyanatopentane, 1,6-diisocyanatohexane (HDI), 2-methyl-1,5-diisocyanatopentane, 1,5-diisocyanato-2,2- dimethylpentane, 2,2,4- and 2,4,4-trimethyl-1,6-diisocyanatohexane, 1,10-diisocyanatodecane, 1,3- and 1,4-diisocyanatocyclohexane, 1,3- and 1,4- bis- (isocyanatomethyl) -cyclohexane, 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethyl cyclohexane (isophorone diisocyanate, IPDI), 4,4'-diisocyanatodicyclohexylmethane (Desmodur ^® W, Bayer AG, Leverkusen, DE), 4- Isocyanatomethyl-1,8-octane diisocyanate (triisocyanatononane, TIN), ω, ω'-diisocyanato-1,3-dimethylcyclohexane (H ₆ XDI), 1-isocyanato-1-methyl-3-isocyanato-methylcyclohexane, 1-isocyanato-1 -methyl-4-isocyanato-methylcyclohexane, bis (isocyanatomethyl) -norboman, 1,5-naphthalene diisocyanate, 1,3- and 1,4-bis (2-isocyanato-prop-2-yl) -benzene ( TMXDI), 2,4- and 2,6-diisocyanatotoluene (TDI) in particular the 2,4 and 2,6 isomers and technical mixtures of the two isomers, 2,4'- and 4,4'-diisocyanatodiphenylmethane (MDI), polymeric MDI (pMDI) 1,5-diisocyanatonaphthalene, 1,3-bis (isocyanato-methyl) benzene (XDI) and any desired mixtures of said compounds.

The polyisocyanates preferably have an average NCO functionality of from 2.0 to 5.0, preferably from 2.2 to 4.5, particularly preferably from 2.2 to 2.7, and a content of isocyanate groups of from 5.0 to 37 , 0 wt .-%, preferably from 14.0 to 34.0 wt .-% to.

In a preferred embodiment, polyisocyanates or polyisocyanate mixtures of the abovementioned type with exclusively aliphatically and / or cycloaliphatically bonded isocyanate groups are used.

Most preferably, the polyisocyanates of the type mentioned above based on hexamethylene diisocyanate, isophorone diisocyanate, the isomeric bis (4,4'-isdcyanatocyclohexyl) methanes and mixtures thereof.

Among the higher molecular weight, modified polyisocyanates are in particular the known from polyurethane chemistry prepolymers having terminal isocyanate groups in the molecular weight range 400 to 15,000, preferably 600 to 12,000 of interest. These compounds are prepared in a conventional manner by reacting excess amounts of simple polyisocyanates of the type exemplified with organic compounds having at least two isocyanate-reactive groups, in particular organic polyhydroxyl compounds. Suitable such polyhydroxyl compounds are both simple polyhydric alcohols of the molecular weight range 82 to 599, preferably 62 to 200, such as. Example, ethylene glycol, trimethylolpropane, 1,2-propanediol or 1,4-butanediol or butanediol-2,3, but in particular higher molecular weight polyether polyols and / or polyester polyols known in polyurethane chemistry with molecular weights of 600 to 12,000, preferably 800 to 4,000, which have at least two, usually 2 to 8, but preferably 2 to 6 primary and / or secondary hydroxyl groups. Of course, also those NCO prepolymers can be used, for example, from low molecular weight polyisocyanates of the type exemplified and less preferred compounds with isocyanate-reactive groups such. B. Polythioetherpolyolen, hydroxyl-containing polyacetals, polyhydroxypolycarbonates, hydroxyl-containing polyester amides or hydroxyl-containing copolymers of olefinic unsaturated compounds have been obtained.

For the preparation of NCO prepolymers suitable compounds having isocyanate-reactive groups, in particular hydroxyl groups, for example, in the US Pat. No. 4,218,543 disclosed compounds. In the preparation of NCO prepolymers, these compounds with isocyanate-reactive groups with simple polyisocyanates of the above exemplified Art implemented under NCO surplus. The NCO prepolymers generally have an NCO content of 10 to 26, preferably 15 to 26 wt .-%. From this it is already apparent that in the context of the present invention under "NCO prepolymers" or "prepolymers with terminal isocyanate groups" both the reaction products as such and the mixtures with excess amounts of unreacted starting polyisocyanates, which are often also called "semiprepolymers" are meant to be understood.

Suitable aliphatic diols having an OH number of> 500 mg KOH / g are the chain extenders conventionally crosslinked in polyurethane chemistry, such as ethylene glycol, diethylene glycol, propylene glycol, dipropylene glycol, 1,4-butanediol, 1,3-propanediol. Preference is given to diols such as 2-butanediol-1,4, butenediol-1,3, butanediol-2,3, 2-butanediol-1,4 and / or 2-methylpropanediol-1,3. Of course, it is also possible to use the aliphatic diols in a mixture with each other.

Polyols having an average OH number of from 5 to 600 mg KOH / g and an average functionality of from 2 to 6 are suitable as the H-active component. Polyols having an average OH number of from 10 to 50 mg KOH / g are preferred. Polyols suitable according to the invention are, for example, polyhydroxypolyethers obtainable by alkoxylation of suitable starter molecules such as ethylene glycol, diethylene glycol, 1,4-dihydroxybutane, 1,6-dihydroxyhexane, dimethylolpropane, glycerol, pentaerythritol, sorbitol or sucrose. Also suitable as initiators are ammonia or amines such as ethylenediamine, hexamethylenediamine, 2,4-diaminotoluene, aniline or amino alcohols or phenols such as bisphenol-A. The alkoxylation is carried out using propylene oxide and / or ethylene oxide in any order or as a mixture.

In addition to polyols, at least one further crosslinker and / or chain extender may additionally be selected from the group comprising amines and amino alcohols, for example ethanolamine, diethanolamine, diisopropanolamine, ethylenediamine, triethanolamine, isophronediamine, N, N'-dimethyl (diethyl) -ethylenediamine, 2 amino-2-methyl (or ethyl) -1-propanol, 2-amino-1-butanol, 3-amino-1,2-propanediol, 2-amino-2-methyl (ethyl) -1,3-propanediol, and alcohols, for example, ethylene glycol, diethylene glycol, 1,4-dihydroxybutane, 1,6-dihydroxyhexane, dimethylolpropane, glycerol and pentaerythritol, as well as sorbitol and sucrose, or mixtures of these compounds.

Also suitable are polyester polyols, as they are accessible by reacting low molecular weight alcohols with polybasic carboxylic acids such as adipic acid, phthalic acid, hexahydrophthalic acid, tetrahydrophthalic acid or the anhydrides of these acids in a conventional manner, provided that the viscosity of the H-active component is not too large. A preferred polyol having ester groups is castor oil. In addition, preparations with castor oil, as by dissolution of resins, eg. As of aldehyde-ketone resins, and modifications of castor oil and polyols based on other natural oils suitable.

Also suitable are those relatively high molecular weight polyhydroxypolyethers in which high molecular weight polyadducts or polycondensates or polymers in finely dispersed, dissolved or grafted form are present. Such modified polyhydroxy compounds are prepared in a conventional manner z. B. obtained when polyaddition reactions (eg., Reactions between polyisocyanates and amino-functional compounds) or polycondensation reactions (eg., Between formaldehyde and phenols and / or amines) proceed in situ in the hydroxyl-containing compounds. However, it is also possible to mix a finished aqueous polymer dispersion with a polyhydroxyl compound and then to remove the water from the mixture.

Also by vinyl polymers modified polyhydroxyl compounds, as described, for. B. by polymerization of styrene and acrylonitrile in the presence of polyethers or polycarbonate polyols are suitable for the production of polyurethanes. When using polyether polyols, which according to DE-A 2 442 101 . DE-A 2 844 922 and DE-A 2 646 141 By graft polymerization with vinylphosphonic and optionally (meth) acrylonitrile, (meth) acrylamide or OH-functional (meth) acrylic acid esters were modified to obtain plastics of particular flame retardancy.

Representatives of said compounds to be used as H-active compounds are, for. In High Polymers, Vol. XVI, "Polyurethanes Chemistry and Technology", Saunders-Frisch (Ed.) Interscience Publishers, New York, London, Vol. 1, pp. 32-42, 44, 54, and Vol. II, 1984, p , 5-6 and pp. 198-199 described.

It is also possible to use mixtures of the compounds listed.

The limitation of the average OH number and average functionality of the H-active component results in particular from the increasing embrittlement of the resulting polyurethane. In principle, however, the person skilled in the influence on the polymer-physical properties of the polyurethane are known, so that NCO component, aliphatic diol and polyol can be suitably matched to each other.

The polyurethane layer (b) can be foamed or solid, such as. B. as a paint or coating.

For their preparation, all known auxiliaries and additives such. For example, release agents, blowing agents, fillers, catalysts and flame retardants can be used.

If necessary as auxiliaries and admixtures are to be used:

a) water and / or volatile inorganic or organic substances as blowing agent

As organic blowing agents come z. As acetone, ethyl acetate, halogen-substituted alkanes such as methylene chloride, chloroform, ethylidene chloride, vinylidene chloride, monofluorotrichloromethane, chlorodifluoromethane, dichlorodifluoromethane, butane, hexane, heptane or diethyl ether, as inorganic blowing agents air, CO ₂ or N ₂ O in question. A blowing effect can also by adding at temperatures above room temperature with elimination of gases, such as nitrogen, decomposing compounds, eg. As azo compounds such as azodicarbonamide or Azoisobuttersäurenitril be achieved.

b) catalysts

The catalysts are, for example, to
tertiary amines (such as triethylamine, tributylamine, N-methylmorpholine, N-ethylmorpholine, N, N, N ', N'-tetramethylethylenediamine, pentamethyldiethylenetriamine and higher homologs, 1,4-diazabicyclo- (2,2,2) octane, N- Methyl-N'-dimethylaminoethylpiperazine, bis (dimethylaminoalkyl) piperazine, N, N-dimethylbenzylamine, N, N-dimethylcyclohexylamine, N, N-diethylbenzylamine, bis (N, N-diethylamino-ethyl) adipate, N, N, N ', N'-tetramethyl-1,3-butanediamine, N, N-dimethyl-β-phenylethylamine, 1,2-dimethylimidazole, 2-methylimidazole),
monocyclic and bicyclic amides, bis (dialkylamino) alkyl ethers,
Amide groups (preferably formamide groups) having tertiary amines,
Mannich bases of secondary amines (such as dimethylamine) and aldehydes, (preferably formaldehyde or ketones such as acetone, methyl ethyl ketone or cyclohexanone) and phenols (such as phenol, nonylphenol or bisphenol),
tertiary amines containing isocyanate-active hydrogen atoms (for example triethanolamine, triisopropanolamine, N-methyldiethanolamine, N-ethyldietanolamine, N, N-dimethylethanolamine) and also reaction products thereof with alkylene oxides such as propylene oxide and / or ethylene oxide,
secondary tertiary amines,
Silaamines having carbon-silicon bonds (2,2,4-trimethyl-2-silamorpholine and 1,3-diethylaminomethyltetramethyldisiloxane),
nitrogenous bases (such as tetraalkylammonium hydroxides),
Alkali hydroxides (such as sodium hydroxide, alkali phenolates such as sodium phenolate),
Alkali alcoholates (such as sodium methylate), and / or
Methylate.

The reaction between NCO groups and Zerewitinoff-active hydrogen atoms is also greatly accelerated in a manner known per se by lactams and azalactams, initially forming an associate between the lactam and the compound with acidic hydrogen.

It is also possible to use organic metal compounds, in particular organic tin and / or bismuth compounds, as catalysts. Suitable tin compounds in addition to sulfur-containing compounds such as di-n-octyl-tin-mercaptide are preferably tin (II) salts of carboxylic acids such as tin (II) acetate, tin (II) octoate, tin (II) ethylhexoate and tin ( II) laurate and the tin (IV) compounds, z. As dibutyltin oxide, dibutylzimide, dibutyltin diacetate, dibutyltin dilaurate, dibutyltin maleate or Dioctylzinndiacetat into consideration. Organic bismuth catalysts are described, for example, in the patent application WO 2004/000905 described.

Of course, all the catalysts mentioned above can be used as mixtures. Of particular interest are combinations of organic metal compounds and amidines, aminopyridines or hydrazinopyridines.

The catalysts are generally used in an amount of about 0.001 to 10 wt .-%, based on the total amount of compounds having at least two isocyanate-reactive hydrogen atoms.

c) Surface-active additives such as emulsifiers and foam stabilizers.

As emulsifiers z. As the sodium salts of castor oil sulfonates or salts of fatty acids with amines such as diethylamine or diethanolamine stearic acid in question. Also alkali metal ammonium salts of sulfonic acids such as dodecylbenzenesulfonic acid or dinaphthylmethanedisulfonic acid or of fatty acids such as ricinoleic acid or of polymeric fatty acids can also be used as surface-active additives.

Suitable foam stabilizers are in particular polyethersiloxanes, especially water-soluble representatives. These compounds are generally designed so that a copolymer of ethylene oxide and propylene oxide is connected to a Polydimethylsiloxanrest. Of particular interest are branched polysiloxane-polyoxyalkylene copolymers, often via allophanate groups.

d) reaction retarder

As reaction retardants z. B. acidic substances (such as hydrochloric acid or organic acid halides) in question.

e) additives

Suitable PU additives are, for example, cell regulators of the type known per se (such as paraffins or fatty alcohols) or dimethylpolysiloxanes and pigments or dyes and flame retardants of the type known per se (for example tris-chloroethyl phosphate, tricresyl phosphate or ammonium phosphate and polyphosphate), and also stabilizers against aging and weathering, plasticizers and fungistatic and bacteriostatic substances and fillers (such as barium sulfate, silica, carbon black or whiting) into consideration.

Further examples of optionally used according to the invention surface-active additives and foam stabilizers and cell regulators, reaction retardants, stabilizers, flame retardants, plasticizers, dyes and fillers and fungistatic and bacteriostatic substances are known in the art and described in the literature.

Examples

Polycarbonate compositions

Component A

Component A-1

• Linear polycarbonate based on bisphenol A having a weight-average molecular weight M _w of 28,000 g / mol.

Component B

Component B-1

• ABS polymer with an acrylonitrile: butadiene: styrene weight ratio of 20:18:62 parts by weight.

Component B-2

• ABS polymer with an acrylonitrile: butadiene: styrene weight ratio of 20:26:54 parts by weight.

Component C

• C-1: pentaerythritol tetrastearate (PETS) as a lubricating / molding agent
• C-2: Irganox ^® B900: Mixture of 80 wt .-% Irgafos ^® 168 (tris (2,4-di-tert-butyl) phenyl phosphite) and 20 wt .-% Irganox ^® 1076 (octadecyl-3 - (3,5-di-tert-butyl-4-hydroxyphenyl) propionate) (BASF, Germany)
• C-3: Irganox ^® 1076 (octadecyl-3- (3,5-di-tert-butyl-4-hydroxyphenyl) propionate) (BASF, Germany)
• C4: carbon black as pigment

Reactive polyurethane raw material mixture

As a polyurethane coating system is a mixture of Bayflex® ^® VP.PU 471F01A (polyol) and Desmodur ^® VP.PU came 481F30 (diisocyanate component), both of Bayer MaterialScience AG, Leverkusen, Germany, with an index of 95 is used.

Bayflex ^® VP.PU 47IF01A is a polyol based on a long chain polyether containing ethanediol, diethanolamine, isophorone diamine, having a viscosity according to DIN 53019 of 1,600 mPa · s at 20 ° C, one density after DIN 51757 of 1.04 g / cm ³ at 20 ° C and a hydroxyl number of 166 mg KOH / g.

Desmodur ^® VP.PU 48IF30 is an aliphatic isocyanate based on isophorone diisocyanate (IPDI) with an NCO content after DIN EN ISO 11909 of 30.5 wt .-%, a viscosity at 23 ° C after DIN EN ISO 3219 / A.3 of 200 mPa · s and a density at 20 ° C after DIN EN ISO 2811 of 1.1 g / cm ³ .

Production and Characterization of the Polycarbonate Molding Compounds

On a twin-screw extruder (ZSK-25) (Werner and Pfleiderer) the feedstocks listed in Tables 1 to 3 at a speed of 220 rpm and with a throughput of 20 kg / h at a melt temperature in the range of 260 to 280 ° C. compounded and granulated after cooling and solidification of the melt of the compound.

The resulting from the respective compounding granules are. processed on an injection molding machine (Arburg) at a melt temperature of 260 ° C and a mold temperature of 80 ° C to test specimens of dimension 80 mm × 10 mm × 4 mm.

Unless otherwise indicated, the sizes referred to in the present application are determined by the following methods:
The ductility of the molding compositions is assessed on the basis of the impact value a _k measured on these test specimens according to ISO 180-1A at 23 ° C and -30 ° C.

The heat distortion temperature is evaluated by the Vicat B120 value measured on these test pieces according to ISO 306.

The melt flowability is judged from the melt viscosity measured at 260 ° C and a shear rate of 1000 s ^-1 in accordance with ISO 11443 ,

The composite adhesion between the polycarbonate composition substrate and the polyurethane skin is measured on a 20 mm wide strip samples sawn from the partially PU coated 2-component composite panels so produced by a roller peel test DIN 53357 A determined at a test speed of 100 mm / min.

Production of composite components

Partially surface coated moldings having a 412 cm ² projected area were produced on an injection molding machine in a two cavity injection mold (a substrate side cavity and a polyurethane side coating cavity associated with a RIM unit). The composite component is a plate-shaped component made of thermoplastic material (carrier) whose surface has been partially coated with a polyurethane skin. The wall thickness of the carrier molding was about 4 mm. The polyurethane layer thickness was also 4 mm.

The process according to the invention for the preparation of the composite components according to the invention described in the examples is shown for better illustration in FIG 1 shown.

In the first process step, the carrier molding was produced. For this purpose, thermoplastic granules of the compositions as described in Table 1 were melted in an injection cylinder and injected at a temperature of 270 ° C in the first mold cavity of the closed mold (steps 1 and 2 in 1 ). This mold cavity was heated to a temperature of 80 ° C. After expiration of the holding pressure time and cooling time, which led to solidification of the carrier, the tool was opened in the second process step (step 3 in 1 ). The produced carrier component was held on the ejector side of the injection mold and moved from the carrier position (step 3 in FIG 1 ) complete with the tool core via a slider in the coating position (step 4 in ). Thereafter, the injection mold was closed again (step 5 in FIG 1 ), a closing force for a maximum pressure of 200 bar was established and injected in the third step, the solvent-free reactive polyurethane system (see above) under a pressure of about 30 bar in the coating cavity (step 6 in 1 ). The two reactive components of the polyurethane coating system were thereby conveyed by the RIM system in a high-pressure countercurrent mixing head and mixed there before injection. The PU-side cavity was tempered to a temperature of 80 ° C. After the end of the injection, the injection nozzle of the polyurethane mixing head was sealed by means of a hydraulic cylinder under a pressure of initially 50 bar to prevent backflow of the coating material. After the reaction and cooling time has elapsed, the tool was opened a second time in the fourth method step (step 7 in FIG 1 ) and the coated molding removed (step 8 in 1 ).

Table 1 shows the influence of the carrier compositions on the adhesion between the layers of the composite component. The examples show the positive surprising effect of an increase in the rubber content in component B [K _B ] and the rubber content of the composition, based on the sum of A and B, [K] on the adhesion of the carrier to the PU skin. Table 1: 1 (V) 2 A1 50 50 B1 50 B2 50 C1 0.75 0.75 C2 0.10 0.10 C3 0.20 0.20 C4 0.2 0.2 [K _B ] 18 26 [K] 9 13 Quotient Q 2.8 1.9 Adhesion of the wearer to PU skin [N / mm] 0.38 1.1 ak (23 ° C) - 260 ° C [KJ / m ² ] 48 41 ak (-30 ° C) - 260 ° C [KJ / m ² ] 27 56 Vicat B120 [° C] 110.3 115.6 Melt viscosity (260 ° C / 1000s ^-1 ) [Pa · s] 186 236

QUOTES INCLUDE IN THE DESCRIPTION

This list of the documents listed by the applicant has been generated automatically and is included solely for the better information of the reader. The list is not part of the German patent or utility model application. The DPMA assumes no liability for any errors or omissions.

Cited patent literature

• WO 2006/072366 A1 [0002]
• DE 102006048252 B3 [0004]
• DE 102006033059 A1 [0006]
• DE 10206033059 A1 [0006]
• WO 99/20464 [0007]
• DE 10109226 A1 [0008, 0008]
• DE 1495626 [0050]
• DE 2232877A [0050]
• DE 2703376 A [0050]
• DE 2714544 A [0050]
• DE 3000610 A [0050]
• DE 3832396 A [0050]
• DE 3077934 A [0050]
• DE 2842005 A [0056]
• US 3419634 [0058]
• DE 3334782 A [0058]
• DE 2940024 A [0066]
• DE 3007934A [0066]
• DE 2407674A [0073]
• DE 2407776 [0073]
• DE 2715932 [0073]
• DE 1900270 A [0074]
• US 3692744 [0074]
• DE 2035390A [0089]
• US 3644574 [0089]
• DE 2248242A [0089]
• GB 1409275 [0089]
• US 4937285 P [0094]
• DE 3704657 A [0099]
• DE 3704655 A [0099]
• DE 3631540 A [0099]
• DE 3631539 A [0099]
• US 4218543 A [0115]
• DE 2442101 A [0121]
• DE 2844922 A [0121]
• DE 2646141 A [0121]
• WO 2004/000905 [0131]

Cited non-patent literature

• ISO 180-1A [0038]
• ISO 6603 [0038]
• ISO 6603 [0047]
• DIN 53357 A [0048]
• Schnell, "Chemistry and Physics of Polycarbonates", Interscience Publishers, 1964 [0050]
• Kunststoff-Handbuch, Vol. VIII, p. 695 ff., Carl-Hanser-Verlag, Munich 1973 [0078]
• Standard DIN EN 61006 [0081]
• W. Scholtan, H. Lange, Colloid, Z. and Z. Polymere 250 (1972), 782-1796 [0083]
• Ullmanns, Enzyklopadie der Technischen Chemie, Vol. 19 (1980), p. 280 et seq. [0089]
• M. Hoffmann, H. Krömer, R. Kuhn, Polymer Analysis I and II, Georg Thieme-Verlag, Stuttgart 1977 [0100]
• High Polymers, Vol. XVI, "Polyurethanes Chemistry and Technology", Saunders-Frisch (Ed.) Interscience Publishers, New York, London, Vol. 1, pp. 32-42, 44, 54, and Vol. II, 1984, p , 5-6 and pp. 198-199 [0122]
• DIN 53019 [0140]
• DIN 51757 [0140]
• DIN EN ISO 11909 [0141]
• DIN EN ISO 3219 / A.3 [0141]
• DIN EN ISO 2811 [0141]
• ISO 180-1A [0144]
• ISO 306. [0145]
• ISO 11443 [0146]
• DIN 53357 A [0147]

Claims (14)

Composite components comprising a) a carrier of a thermoplastic composition comprising A) at least one polymer selected from the group of aromatic polycarbonates, aromatic polyester and aromatic polyesters in a proportion of [A] from 20.0 to 85.0 parts by weight to the sum of components A and B, B) at least one rubber-modified vinyl (co) polymer in a proportion of [B] of 15.0 to 80.0 parts by weight, based on the sum of components A and B, with a rubber content [K _B ] of at least 25.0 parts by weight, based on component B and C) of at least one polymer additive in a proportion of [C] of 0 to 30.0 parts by weight, based on the sum of Components A to C, and b) at least one polyurethane layer, wherein the thermoplastic composition is characterized by a total rubber content, based on the sum of components A and B, of at least 12 parts by weight. Composite components comprising a) a carrier of a thermoplastic composition comprising A) at least one polymer selected from the group of aromatic polycarbonates, aromatic polyester and aromatic polyesters in a proportion of [A] from 20.0 to 85.0 parts by weight to the sum of components A and B, B) at least one rubber-modified vinyl (co) polymer in a proportion of [B] of 15.0 to 80.0 parts by weight, based on the sum of components A and B, with a rubber content [K _B ] of at least 25.0 parts by weight, based on component B and C) of at least one polymer additive in a proportion of [C] of 0 to 30.0 parts by weight, based on the sum of Components A to C, and b) at least one polyurethane layer, wherein the thermoplastic composition is characterized by a quotient Q = [B] / [K _B ] of <2 and a rubber content [K] = [K _B ] · [B] / 100, based on the sum of components A and B, of at least 12 parts by weight. Composite components according to one of claims 1 or 2, characterized in that the thermoplastic composition of the carrier comprises: A) 30.0 to 64.9 parts by weight, based on the sum of components A and B, of at least one polymer selected from the group consisting of aromatic polycarbonates, aromatic polyester carbonates and aromatic polyesters, and B) 35.1 to 70.0 parts by weight, based on the sum of components A and B, of at least one rubber-modified vinyl (co) polymer. Composite components according to one of claims 1 or 2, characterized in that the thermoplastic composition of the carrier comprises: A) 40.0 to 64.9 parts by weight, based on the sum of components A and B, of at least one polymer selected from the group of aromatic polycarbonates, aromatic polyester carbonates and aromatic polyesters, B) 35.1 to 60 parts by weight, based on the sum of components A and B, of at least one rubber-modified vinyl (co) polymer. Composite components according to one of claims 2 to 4, characterized in that the quotient Q is less than 1.7, in particular less than 1.5. Composite components according to one of claims 1 to 5, characterized in that component A is a mixture of at least one aromatic polycarbonate and / or polyester carbonate and at least one aromatic polyester is used. Composite components according to one of the preceding claims, characterized in that the polyurethane layer is produced by polymerization of a reactive polyurethane raw material mixture comprising - at least one polyisocyanate component, At least one polyfunctional H-active compound, and optionally at least one polyurethane additive and / or processing aid in direct contact with the carrier previously formed and solidified from the thermoplastic composition. Composite components according to one of the preceding claims, characterized in that the polyurethane layer is prepared by Auspolymerisation a reactive polyurethane raw material mixture containing At least one polyisocyanate component, At least one polyfunctional H-active compound, and Optionally at least one polyurethane additive and / or processing aid on the one hand in direct contact with the carrier previously formed and solidified from the thermoplastic composition and on the other side in direct contact with a decorative skin optionally consisting of polyvinyl chloride (PVC), thermoplastic polyolefins (TPO), thermoplastic polyurethane (TPU) or a Polyurethansprühhaut. Composite components according to claim 7 or 8, characterized in that the reactive polyurethane raw material mixture has a ratio of> 80 to <125. Composite components according to one of the preceding claims, characterized in that the component C is selected from at least one member selected from the group consisting of flame retardants, Flammschutzsynergisten, smoke-inhibiting additives, Antidrippingmitteln, internal and external lubricants and mold release agents, flowability aids, antistatic agents, conductivity additives, nucleating agents, Stabilizers, antibacterial additives, scratch resistance additives, IR absorbents, optical brighteners, fluorescent additives, fillers and reinforcing agents, dyes and pigments, impact modifiers not covered by the definition of B.1, and Bronstet acidic compounds. Composite components according to one of the preceding claims manufactured by a method in the (i) in a first method step the melt of the thermoplastic composition is injected into a first mold cavity and subsequently cooled, (ii) the cavity of the injection molding tool is enlarged in a second method step, thereby creating a gap space, (Iii) in the third step in the resulting gap between the thermoplastic component and the tool surface of the enlarged cavity containing a reactive polyurethane raw material mixture At least one polyisocyanate component, At least one polyfunctional H-active compound, and Optionally, at least one polyurethane additive and / or processing aid is sprayed, the polyurethane raw material mixture polymerizing in direct contact with the surface of the thermoplastic carrier to form a compact polyurethane layer or to a polyurethane foam layer, (iv) in the fourth method step, the composite component is removed from the mold cavity, the method steps (i) to (iv) following one another directly. Process for producing a composite component according to one of Claims 1 to 11, characterized in that (i) in a first method step the melt of the thermoplastic composition is injected into a first mold cavity and subsequently cooled, (ii) the cavity of the injection molding tool is enlarged in a second method step, thereby creating a gap space, (Iii) in the third step in the resulting gap between the thermoplastic component and the tool surface of the enlarged cavity containing a reactive polyurethane raw material mixture At least one polyisocyanate component, At least one polyfunctional H-active compound, and Optionally, at least one polyurethane additive and / or processing aid is sprayed, the polyurethane raw material mixture polymerizing in direct contact with the surface of the thermoplastic carrier to form a compact polyurethane layer or to a polyurethane foam layer, (iv) in the fourth method step, the composite component is removed from the mold cavity, the method steps (i) to (iv) following one another directly. A method according to claim 12, characterized in that in step (iii) the contacting with the thermoplastic composition surface of the injection molding tool on a Temperature in the range 50 to 95 ° C and the contacting with the reactive polyurethane mixture surface of the injection mold to a temperature in the range of 50 to 160 ° C is controlled. Use of a composite component according to one of claims 1 to 11 as an inner or outer component of a rail, aviation or motor vehicle.