DE102008009774A1 - Element i.e. disk, for use in e.g. clinic, has film operated in two states, and laminated glass elements including surface, where glass elements provide protection against ionizing radiation and ultra-violet radiation - Google Patents

Element i.e. disk, for use in e.g. clinic, has film operated in two states, and laminated glass elements including surface, where glass elements provide protection against ionizing radiation and ultra-violet radiation Download PDF

Info

Publication number
DE102008009774A1
DE102008009774A1 DE102008009774A DE102008009774A DE102008009774A1 DE 102008009774 A1 DE102008009774 A1 DE 102008009774A1 DE 102008009774 A DE102008009774 A DE 102008009774A DE 102008009774 A DE102008009774 A DE 102008009774A DE 102008009774 A1 DE102008009774 A1 DE 102008009774A1
Authority
DE
Germany
Prior art keywords
coating
semitransparent
layer
substrate
disc
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE102008009774A
Other languages
German (de)
Inventor
Angelika Dr. Ullmann
Marten Dr. Walther
Bernd Albrecht
Daniel Grimm
Horst Schillert
Matthias Anton
Peter Kracht
Ernst-Friedrich Düsing
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Schott AG
Original Assignee
Schott AG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Schott AG filed Critical Schott AG
Priority to DE102008009774A priority Critical patent/DE102008009774A1/en
Priority to EP08014490A priority patent/EP2036714A1/en
Priority to PCT/EP2008/007266 priority patent/WO2009033607A1/en
Priority to US12/205,147 priority patent/US8187682B2/en
Publication of DE102008009774A1 publication Critical patent/DE102008009774A1/en
Withdrawn legal-status Critical Current

Abstract

The element has a film (420) operated in two states, where the film is made of an electrochromic substance and a liquid crystal substance. Laminated glass elements (400, 410) i.e. X-ray protective glass, have a surface, where the glass elements provide protection against ionizing radiations and ultra-violet (UV) radiations. The surface of the glass elements is partially covered by a poly vinyl butyrate (PVB) film (412). The liquid crystal substance is operated in a disordered non-transparent state, in which the substance scatters visible light, and operated in an ordered non-scattering state.

Description

Gebiet der ErfindungField of the invention

Die Erfindung betrifft ein semitransparentes Element, insbesondere ein Fassadenelement, umfassend wenigstens ein erstes scheibenförmiges Element und ein zweites scheibenförmiges Element, wobei das erste scheibenförmige Element und das zweite scheibenförmige Element einen Abstand zueinander aufweisen und mit einer Verbindungsvorrichtung miteinander verbunden sind.The The invention relates to a semitransparent element, in particular a Façade element comprising at least a first disc-shaped Element and a second disc-shaped element, wherein the first disc-shaped element and the second disc-shaped Element have a distance from each other and with a connecting device to each other are connected.

Unter einem semitransparenten Element wird in der vorliegenden Anmeldung ein Element verstanden, bei dem die Transmission des Lichtes zumindest in Teilbereichen des sichtbaren Wellenlängenbereich von 90% des einfallenden Lichtes bis 35% des einfallenden Lichtes reicht. Das semitransparente Element zeichnet sich also durch eine hohe Reflektivität des Lichtes zumindest in Teilbereichen des sichtbaren Wellenlängenbereich von 420 nm bis 700 nm aus, wobei die Reflektivität im Bereich zwischen 10% bis 80% des einfallenden Lichtes liegt.Under a semitransparent element is used in the present application understood an element in which the transmission of light at least in subregions of the visible wavelength range of 90% of the incident light reaches 35% of the incident light. The semitransparent element is thus characterized by a high reflectivity of the light at least in subregions of the visible wavelength range from 420 nm to 700 nm, the reflectivity in the range between 10% to 80% of the incident light.

Stand der TechnikState of the art

Semitransparente Elemente, insbesondere Fassadenelemente, werden heute in immer größerer Zahl insbesondere beim Bau von repräsentativen Gebäuden eingesetzt. Mit Hilfe von semitransparenten Elementen ist es beispielsweise möglich, Farbeffekte in Fassaden zu realisieren. Solche Farbeffekte wurden in Fassaden insbesondere durch Fassadenelemente erreicht, die Farbeffekte aufgrund von Absorptionen bestimmter Wellenlängen im sichtbaren Bereich aufwiesen. Aufgrund der mit Hilfe der Absorption erzeugten Farbeffekte kam es dabei aber stets zu einer starken Erwärmung des Farbglases bei direkter Sonneneinstrahlung.semi-transparent Elements, especially facade elements, are becoming more and more popular today especially in the construction of prestigious buildings used. For example, with the help of semitransparent elements possible to realize color effects in facades. Such Color effects were in facades in particular by facade elements achieves the color effects due to absorption of certain wavelengths in the visible range. Because of with the help of absorption However, the color effects were always strong of the colored glass in direct sunlight.

Der Einsatz von Farbgläsern in Fassaden mit direkter Sonneneinstrahlung ist dabei beschränkt, speziell in Gegenden mit hoher Sonnenintensität. Das Farbglas konnte daher oft nicht in einen Verbund, insbesondere nicht in einen Isolierglasverbund eingebracht werden. Beispiele für derartige Farbeffektgläser, die aufgrund von Absorption Farbeffekte mit intensiven Farben erzielten und im Fassadenbau eingesetzt wurden, sind die Farbgläser, die beispielsweise unter dem Markennamen ARTISTA® der Firma Schott AG, Mainz, vertrieben wurden.The use of colored glass in facades with direct sunlight is limited, especially in areas with high solar intensity. The colored glass could therefore often not be incorporated into a composite, in particular not in an insulating glass composite. Examples of such color effect glasses, which achieved due to absorption color effects with intense colors and were used in facade construction, the color glasses, for example, under the brand name ARTISTA ® Schott AG, Mainz, were sold.

Diesbezüglich wird auf den Prospekt 987-20D/12/05-C der Schott AG, Mainz verwiesen sowie auf die Internetseite www.schott.com\architecture .In this respect, reference is made to the prospectus 987-20D / 12/05-C Schott AG, Mainz and the website www.schott.com \ architecture ,

Beschreibung der ErfindungDescription of the invention

Aufgabe der Erfindung ist es, ein semitransparentes Element anzugeben, das einerseits Farbeffekte zulässt, andererseits eine Erwärmung vermeidet und für eine Verwendung im Architekturbereich eine hohe Wärmedämmung mit einem niedrigen Emissionsvermögen aufweist.task The invention is to provide a semitransparent element, the on the one hand allows color effects, on the other hand, a warming avoids and for use in the architecture sector high thermal insulation with a low emissivity having.

Eine derartige Aufgabe wird durch ein semitransparentes Element, insbesondere Fassadenbauelement erfüllt, das in Form eines Isolierglaselementes ausgeführt ist. Das Isolierglaselement umfasst zwei scheibenförmigen Elementen, die beabstandet zueinander und miteinander verbunden sind. Zwischen den beiden zueinander beabstandeten und verbundenen Scheiben ist ein Gas, bevorzugt ein Edelgas, eingebracht, das Wärmeverluste minimiert. Derartig aufgebaute Elemente werden auch als Isolierglasverbunde bezeichnet.A Such object is achieved by a semitransparent element, in particular Façade component meets, in the form of an insulating glass element is executed. The insulating glass element comprises two disc-shaped Elements spaced apart and interconnected are. Between the two spaced apart and connected Slices is a gas, preferably a noble gas, introduced, the heat losses minimized. Such constructed elements are also called Isolierglasverbunde designated.

Gemäß der Erfindung kann ein derartiges semitransparentes, als Isolierglaselement aufgebautes Bauteil einen Farbeffekt aufweisen, wenn wenigstens eines der beiden scheibenförmigen Elemente eine Beschichtung aufweist, die für den Betrachter zu einem Farbeffekt im sichtbaren Wellenlängenbereich von 420 nm bis 700 nm führt und die Beschichtung, die für die Erzeugung des Farbeffektes verantwortlich ist, im sichtbaren Wellenlängenbereich lediglich eine Absorption < 5%, insbesondere < 3%, bevorzugt < 2%, ganz bevorzugt < 1% des einfallenden Lichtes aufweist. Zur Verstärkung der Farbeffekte, beispielsweise zum Erhalt von Nachteffektgläsern umfasst das semitransparente Element in einer ersten Ausgestaltung Leuchtmittel.According to the Invention may be such a semi-transparent, as insulating glass element constructed component have a color effect, if at least one the two disc-shaped elements a coating which gives the viewer a color effect in the visible wavelength range from 420 nm to 700 nm leads and the coating necessary for the creation of the color effect is responsible, in the visible wavelength range only an absorption <5%, in particular <3%, preferably <2%, very preferably <1% having the incident light. To reinforce the Color effects, for example, to obtain Nachteffektgläsern comprises the semitransparent element in a first embodiment Lamps.

In einer alternativen Ausgestaltung der Erfindung umfasst das semitransparentes ein Verbundglas und/oder das Verbundsicherheitsglas mit einer Funktionsfolie.In An alternative embodiment of the invention comprises the semitransparent a laminated glass and / or the laminated safety glass with a functional film.

Die Funktionsfolie kann eine der nachfolgenden Funktionsfolien sein:

  • – eine Folie umfassend Leuchtmittel
  • – eine Folie umfassend eine schaltbare Substanz, insbesondere einen Flüssigkristall oder eine elektrochrome Substanz
  • – eine Folie umfassend Streuzentren.
The functional film can be one of the following functional films:
  • A foil comprising bulbs
  • - A film comprising a switchable substance, in particular a liquid crystal or an electrochromic substance
  • - A film comprising scattering centers.

Bei der vorliegenden Erfindung beziehen sich die oben angegebenen Werte für die Absorption nur auf die Absorptionswerte der Farbeffektbeschichtung. Die Absorptionswerte anderer unter Umständen noch zusätzlich aufgebrachter Schichten wie beispielsweise Schichten mit niedriger Emittivität bleiben hierbei unberücksichtigt.at The present invention relates to the values given above for absorption only to the absorption values of the color effect coating. The absorption values of others may be additional applied layers such as lower layers Emittivity is not taken into account.

Auf diese Art und Weise wird der Wärmeeintrag durch Absorption im Glas in den Isolierverbund stark vermindert und damit ein Spannungsbruch oder ein Aufbrechen der Versiegelung des Isolierglasverbundes aufgrund eines zu hohen Wärmeeintrages vermieden.In this way, the heat input by absorption in the glass in the insulating composite greatly reduced and thus a stress rupture or breaking the seal of the insulating glass composite due to excessive heat input avoided.

Bei der Beschichtung, die zu dem Farbeffekt führt, handelt es sich um ein Schichtsystem, das einen Teilbereich des Lichtes im sichtbaren Wellenlängenbereich mit einer hohen Reflektivität reflektiert. Das Licht des Teilbereiches, das zu einem großen Anteil reflektiert wird, weist nur eine geringe Transmission auf.at the coating that leads to the color effect is it is a layered system that is a subset of the light in the visible wavelength range with a high reflectivity reflected. The light of the subarea, to a large extent is reflected, has only a low transmission.

Aufgrund dieses im sichtbaren Wellenlängenbereich von 380 nm bis 780 nm selektiven Reflektionsverhaltens durch Vielfachbeschichtung kommt es für einen Betrachter je nach Betrachtungswinkel zu einem Farbeffekt. Derartige Beschichtungen sind Interferenzschichtsysteme, die sich dadurch auszeichnen, dass sie wenigstens zwei Teilschichten umfassen, eine erste und eine zweite Teilschicht, wobei die zweite Teilschicht auf die erste Teilschicht aufgebracht ist und die zweite Teilschicht die letzte einem gasförmigen Medium zugewandte Schicht nach der Beschichtung des Interferenzschichtsystems ist. Die letzte einem gasförmigen Medium zugewandte Schicht bezieht sich nur auf die letzte Teilschicht, die bei der Beschichtung auftritt. Nach einem nachfolgendem Laminiervorgang kann die Schicht dann schon wieder nach innen liegen und braucht keinen Kontakt zum Gas haben. Diese letzte Schicht weist entweder einen hohen Brechungsindex auf und wird als so genannte T-Schicht bezeichnet, mit einem hohen Brechungsindex nh ≥ 1,8, bevorzugt zwischen 1,9 < nh < 2,3 oder eine mittelbrechende Schicht, eine so genannte M-Schicht mit einem mittleren Brechungsindex 1,6 < nm < 1,8 gemessen jeweils bei einer Referenzwellenlänge von 550 nm. Die Schichtdicken der einzelnen Schichten liegen bevorzugt im Bereich 10 nm bis 200 nm, bevorzugt zwischen 20 nm und 100 nm.Because of this in the visible wavelength range from 380 nm to 780 nm selective reflection behavior by multiple coating it comes to a viewer depending on the viewing angle to a color effect. Such coatings are interference layer systems which are characterized in that they comprise at least two partial layers, a first and a second partial layer, the second partial layer being applied to the first partial layer and the second partial layer being the last layer facing a gaseous medium after coating of the interference layer system is. The last layer facing a gaseous medium only relates to the last partial layer which occurs during the coating. After a subsequent lamination process, the layer can then be inside again and need not have any contact with the gas. This last layer either has a high refractive index and is referred to as a so-called T-layer, with a high refractive index n h ≥ 1.8, preferably between 1.9 <n h <2.3 or a medium refractive index, a so-called M layer having a mean refractive index 1.6 <nm <1.8 measured in each case at a reference wavelength of 550 nm. The layer thicknesses of the individual layers are preferably in the range 10 nm to 200 nm, preferably between 20 nm and 100 nm.

Für die hochbrechende Schicht kann Titanoxid TiO2, Nioboxid Nb2O5, Tantaloxid Ta2O5, Ceroxid CeO2, Hafniumoxid HfO2 oder Mischungen dieser Stoffe miteinander eingesetzt werden.For the high refractive index layer of titanium oxide TiO 2, niobium oxide Nb 2 O 5, Ta 2 O 5 tantalum oxide, cerium oxide CeO 2, hafnium oxide HfO 2 or mixtures of these substances can be used together.

Für die mittelbrechende Schicht kann eine Mischung aus Titanoxid und Siliziumoxid TiO2/SiO2, sowie auch Mischungen mit Aluminiumoxid Al2O3 oder Zirkonoxid ZrO2 zum Einsatz kommen. Für den Fachmann ergeben sich weitere Materialsysteme, die die geforderten Brechungsindices erreichen, jedoch in der Beschichtungstechnologie weniger üblich sind.A mixture of titanium oxide and silicon oxide TiO 2 / SiO 2 , as well as mixtures with aluminum oxide Al 2 O 3 or zirconium oxide ZrO 2 can be used for the medium-refractive layer. Those skilled in the art will find other material systems that achieve the required refractive indices, but are less common in coating technology.

Betreffend die Wahl der Schichtzusammensetzungen für die unterschiedlichen Schichten, die Auftragsverfahren, die Substratmaterialien bzw. Substratgläser wird auf die US-Anmeldungen US 6,720,081 und US 7,169,441 verwiesen, deren Offenbarungsgehalt vollumfänglich in diese Anmeldung mit aufgenommen wird.Concerning the choice of coating compositions for the different ones Layers, the application method, the substrate materials or substrate glasses Reference is made to US applications US 6,720,081 and US 7,169,441, the disclosure of which is fully incorporated in this application is recorded.

Die einzelnen Schichten des Interferenzschichtsystems können sowohl Einzelschichten sein, aber auch Mehrfachschichten, aufgebaut aus mehreren Schichten von Materialien gleichen Brechungsindex.The individual layers of the interference layer system can be both single layers, but also multiple layers, built from several layers of materials same refractive index.

Bei erfindungsgemäßen semitransparenten Elementen als Isolierglasverbund weist das erste scheibenförmige Element ein erstes Substrat mit einer ersten Fläche, die als Fläche 1 bezeichnet wird, und einer zweiten Fläche, die als Fläche 2 bezeichnet wird, auf, wobei die zweite Fläche dem zweiten scheibenförmigen Element gegenüberliegt.In semitransparent elements according to the invention as an insulating glass composite, the first disk-shaped element has a first substrate with a first surface which serves as a surface 1 is called, and a second surface, as the surface 2 is referred to, wherein the second surface opposite to the second disc-shaped element.

Ebenso weist das zweite scheibenförmige Element ein zweites Substrat auf, wobei das zweite Substrat eine dritte Fläche umfasst, die als Fläche 3 bezeichnet wird und eine vierte Fläche, die als Fläche 4 bezeichnet wird, wobei die dritte Fläche der zweiten Fläche zugewandt ist.Likewise, the second disc-shaped element has a second substrate, wherein the second substrate comprises a third surface serving as a surface 3 is called and a fourth surface, which is called surface 4 is designated, wherein the third surface facing the second surface.

In einer bevorzugten Ausgestaltung wird die erfindungsgemäße Beschichtung, die den Farbeffekt hervorruft, um einen Angriff der Fläche beispielsweise durch ungünstige atmosphärische Bedingungen wie salzhaltige Luft zu verhindern, auf der zweiten Fläche des ersten Substrates beziehungsweise der dritten Fläche des zweiten Substrates aufgebracht, da die zweite Fläche und die dritte Fläche in einem Isolierglasverbund stets die Flächen sind, die dem zwischen die beiden scheibenförmigen Elemente eingebrachten Gas zugewandte Seiten sind. In den meisten Anwendungsfällen kann das Farbeffektglas jedoch auch in Kontakt mit der Umgebungsatmosphäre eingesetzt werden, und dann auf den Flächen 1 und 2 und oder Flächen 3 und 4 den Farbeffekt aufweisen.In a preferred embodiment, the coating according to the invention, which causes the color effect to prevent attack of the surface, for example, by unfavorable atmospheric conditions such as salty air, applied to the second surface of the first substrate or the third surface of the second substrate, since the second surface and the third surface in an insulating glass composite are always the surfaces that are facing the gas introduced between the two disk-shaped elements. However, in most applications, the color effect glass can also be used in contact with the ambient atmosphere, and then on the surfaces 1 and 2 and or surfaces 3 and 4 have the color effect.

Bevorzugt ist es, wenn als Gas zwischen die beiden scheibenförmigen Elemente ein besonders inertes Gas, beispielsweise ein Edelgas wie Argon, Xenon oder Krypton eingebracht wird, um die Isolationswirkung des Verbundes zu steigern.Prefers it is when as a gas between the two disc-shaped Elements a particularly inert gas, such as a noble gas such as Argon, xenon or krypton is introduced to the isolation effect to increase the network.

Neben der Farbeffekt-Beschichtung weist der aus erstem und zweitem scheibenförmigem Element bestehende Isolierglasverbund bevorzugt noch weitere Beschichtungen auf. Insbesondere ist es vorteilhaft, um eine besonders hohe Wärmedämmung zu erreichen, eine weitere Beschichtung niedriger Emittivität oder eine Sonnenschutzbeschichtung auf eine Fläche des ersten und/oder des zweiten Substrates aufzubringen. Bevorzugt werden auch diese Schichten auf Flächen aufgebracht, die im Isolierglasverbund dem Gas gegenüberliegen.Next the color effect coating has the first and second disc-shaped Element existing insulating glass composite prefers even more coatings on. In particular, it is advantageous to have a particularly high level of thermal insulation achieve another low emissivity coating or a sunscreen coating on an area of the first and / or the second substrate. To be favoured These layers are also applied to surfaces in the insulating glass composite facing the gas.

Wärmedämmschichten sind Schichten, die im langwelligen IR-Bereich hochreflektierend beziehungsweise niedrigemittierend (niedrig-ε) sind, und dadurch den Wärmeverlust minimieren. Derartige Wärmedämmschichten können beispielsweise in Hochleistungskathodenzerstäubungsverfahren im Vakuum hergestellt werden und sind beispielsweise unter dem Handelsnamen „arcon n41, arcon n33, arcon n32 und arcon n30" der arcon, Flachglas-Veredelung GmbH & Co. KG, Feuchtwangen, erhältlich. Alternativ zu den Wärmedämmschichten ist auch die Verwendung von Sonnenschutzschichten möglich, die sich zum einen durch eine hohe Wärmedämmung auszeichnen, zum anderen aber auch einen geringen Gesamtenergiedurchlass zur Verhinderung starker Aufheizungen. Derartige Schichtsysteme sind beispielsweise unter den Markennamen Sunbelt, arcon, Flachglas-Veredelung GmbH & Co. KG, Feuchtwangen, bekannt geworden.Thermal barrier coatings are layers that are highly reflective in the long-wave IR range or low-emitting (low-ε), and thereby minimize heat loss. Such thermal barrier coatings For example, in high performance cathode sputtering processes are manufactured under vacuum and are for example under the trade name "arcon n41, arcon n33, arcon n32 and arcon n30 "the arcon, flat glass finishing GmbH & Co. KG, Feuchtwangen, available. Alternative to the thermal barrier coatings The use of sunscreen is also possible On the one hand, they are characterized by high thermal insulation, on the other hand also a small total energy passage to Prevention of strong heatings. Such layer systems are For example, under the brand name Sunbelt, arcon, flat glass finishing GmbH & Co. KG, Feuchtwangen, became known.

Die Substrate des ersten und zweiten scheibenförmigen Elementes können Einscheibenglas, Einscheibensicherheitsglas, teilvorgespanntes Einscheibenglas, Verbundsicherheitsglas, Verbundsicherheitsglas umfassend Einscheibensicherheitsglas, Verbundsicherheitsglas umfassend ein teilvorgespanntes Glas sein.The Substrates of the first and second disk-shaped element can use single pane glass, toughened safety glass, partially tempered Single pane glass, laminated safety glass, laminated safety glass comprising single-pane safety glass comprising laminated safety glass to be a partially toughened glass.

Derartige für die Verwendung im Architekturbereich einsetzbare Gläser sind beispielsweise in dem Handbuch Basisgläser 2007 der Firma Pilkington, Deutschland AG, Haydnstraße 19, 45884 Gelsenkirchen, offenbart, das auch über die Internetseite www.pilkington.com abrufbar ist. Sämtliche dort genannten Gläser werden in den Offenbarungsgehalt der vorliegenden Anmeldung vollumfänglich mit eingeschlossen.Such glasses which can be used for use in the field of architecture are disclosed, for example, in the Handbuch Basisgläser 2007 by Pilkington, Germany AG, Haydnstraße 19, 45884 Gelsenkirchen, which is also available on the Internet site www.pilkington.com is available. All of the glasses mentioned therein are fully included in the disclosure of the present application.

Während bevorzugt im Architekturbereich für Fassaden bevorzugt Glasverbunde aus flachen Scheiben eingesetzt werden, ist es selbstverständlich möglich, durch Nachverarbeitung Scheiben zu biegen, so dass vom Umfang der Anmeldung auch gebogene Scheiben mit umfasst werden.While preferred in the architectural field for facades preferred Glass composites are used from flat slices, it goes without saying possible to bend discs by post-processing, so that the scope of the application also includes curved discs become.

Das semitransparente Element gemäß der Erfindung, das als Isolierglasverbund ausgelegt ist, umfasst übliche Verbindungseinrichtungen aus einem Metallabstandsstück sowie einer Versiegelung zwischen den beiden, den Isolierglasverbund ausbildenden Scheibenelementen.The semitransparent element according to the invention, which is designed as insulating glass composite includes conventional Connecting means of a metal spacer and a seal between the two, the insulating glass composite forming disc elements.

Die Beschichtung und/oder die weitere Beschichtung können auf verschiedene Art und Weise aufgetragen werden. Beispielsweise ist dies möglich durch Kathodenzerstäubung im Vakuum, so genannte Sputtertechnik, durch physikalisches Aufdampfen, durch chemische Gasphasenabscheidung, durch Schleuderverfahren oder durch eine Tauchverfahren, insbesondere in Sol-Gel-Technik sowie durch eine Sprühbeschichtung, die direkt nach Herstellung des Flachglases auf das noch warme Glas aufgebracht wird.The Coating and / or the further coating can on various ways are applied. For example this is possible by sputtering under vacuum, so-called sputtering technique, by physical vapor deposition, by chemical vapor deposition, by spin coating or by a dipping method, in particular in sol-gel technique as well as by a spray coating directly after the manufacture of the flat glass is applied to the still warm glass.

Ein besonderer Effekt kann erzielt werden, wenn der Isolierglasverbund mit Leuchtmitteln, zum Beispiel organische oder anorganische Leuchtdioden, versehen ist. Sind diese einzelnen Leuchtdioden ansteuerbar, so können in Kombination mit den Farbeffektschichten Lichteffekte und sogar die Anzeige von Bildern generiert werden. Die Leuchtmittel können Weißlicht abstrahlen (sog. Weißlichtleuchtdioden) oder auch farbiges Licht.One special effect can be achieved if the insulating glass composite with illuminants, for example organic or inorganic light-emitting diodes, is provided. If these individual LEDs can be controlled, then can combine with the color effect layers light effects and even the display of images are generated. The bulbs can Emit white light (so-called white light emitting diodes) or even colored light.

Die Montage der Leuchtmittel kann beispielsweise auf dem bzw. den Substraten erfolgen die die scheibenförmigen Elemente ausbilden, beispielsweise, wie in der EP-A-1 450 416 beschrieben. Die Leuchtmittel können direkt auf einer Fläche des Substrates aufgebracht sein. Alternativ können die Leuchtmittel auch in einer Folie angeordnet sein.The mounting of the lighting means can be carried out, for example, on the substrate or substrates which form the disk-shaped elements, for example, as in US Pat EP-A-1 450 416 described. The lighting means can be applied directly to a surface of the substrate. Alternatively, the bulbs can also be arranged in a foil.

Werden als Leuchtmittel LED-Bauformen verwandt, die beispielsweise die drei Grundfarben des Videopixels (Rot, Grün und Blau) erzeugen, so können Farbeffekte erzielt werden oder Fernsehbilder erzeugt werden. In einer besonderen Ausgestaltung werden RGB-Leuchtdioden verwandt, die in einem einzigen LED-Chip alle Grundfarben eines Fernsehbildes (rot, grün, blau) realisieren.Become used as light sources LED types, for example, the generate three basic colors of the video pixel (red, green and blue), so color effects can be achieved or television pictures be generated. In a particular embodiment, RGB light emitting diodes used in a single LED chip all the basic colors of a Realize TV picture (red, green, blue).

Alternativ können auch drei LED nebeneinander eng benachbart angeordnet werden. Eine der Leuchtdioden emittiert dann rotes Licht, die andere grünes Licht und die dritte blaues Licht.alternative Also, three LED can be juxtaposed closely adjacent become. One of the LEDs then emits red light, the other green Light and the third blue light.

Besonders bevorzugt werden die Leuchtmittel, d. h. die einzelnen Leuchtdioden für einen Betrachter in der Ferne mit großem Abstand zum semitransparenten Element unauffällig, insbesondere unsichtbar mit Strom versorgt und angesteuert. Hierfür geeignet sind beispielsweise transparente Leiterbahnen wie sie beispielsweise in der EP 1450416 oder aber auch der WO 2006/018066 bekannt geworden sind.Particularly preferably, the lighting means, ie the individual light-emitting diodes for a viewer in the distance with a large distance to the semitransparent element inconspicuous, in particular invisible supplied with electricity and controlled. Suitable for this purpose, for example, transparent conductor tracks such as those in the EP 1450416 or even the WO 2006/018066 have become known.

Der Offenbarungsgehalt der beiden Schriften WO 2006/018066 und EP-A-1 450 416 wird in vorliegender Anmeldung vollumfänglich mit auf genommen. Die Leiterbahnen dienen sowohl der Stromversorgung wie der Ansteuerung der einzelnen Leuchtmittel.The revelation content of the two writings WO 2006/018066 and EP-A-1 450 416 will be included in the present application in full. The tracks serve both the power supply as well as the control of the individual bulbs.

Besonders vorteilhaft ist es, wenn die transparenten Leiterbahnen aus einer transparenten, elektrisch leitenden und leistungsübertragenden Schicht bestehen. Dadurch können auch höhere Ströme über diese Leiterbahnen übertragen werden, so dass auch mehrere Leuchtmittel über eine Leiterbahn versorgt werden können.Especially It is advantageous if the transparent conductor tracks from a transparent, electrically conductive and power-transmitting layer consist. This can also higher currents over these interconnects are transmitted, so that several Bulbs can be supplied via a conductor track.

Neben transparenten können auch Leiterbahnen beispielsweise auf Basis von Silberleitpaste eingesetzt werden.Next transparent can also be printed circuit traces, for example Base of silver conductive paste can be used.

Die Verwendung der semitransparenten Elemente mit Farbeffekten gemäß der Erfindung erfolgt vorzugsweise im Bereich der Architekturgläser, hier bevorzugt im Bereich der Fassadenelemente, insbesondere der Außenfassaden. Denkbar wäre aber auch eine Anwendung im Bereich des Fensterbaus oder für die Innenarchitektur sowie als Schaufensterscheiben. Des weiteren können die Elemente als dekorative Außenfassaden, in denen entweder die Einzelelemente (Isolierverglasung) noch farblich strukturiert sind, oder Fassaden, in denen Elemente mit und ohne Farbeffekt wechselnd eingesetzt werden, verwendet werden, um eine farbige Gesamtfassade zu erreichen.The Use of semitransparent elements with color effects according to Invention preferably takes place in the field of architectural glasses, Here preferred in the field of facade elements, in particular the Exterior facades. It would also be conceivable, however, an application in the field of window construction or for interior design as well as showcase windows. Furthermore, the Elements as decorative exterior facades in which either the individual elements (insulating glazing) still structured in color are, or facades in which elements with and without color effect changing be used, used to a colored overall facade to reach.

Selbstverständlich umfasst die Erfindung nicht nur einen Isolierglasverbund aus zwei Scheiben. Dies ist lediglich die kleinste Einheit. Das semitransparente Element kann selbstverständlich Teil eines Isolierglasverbundes bestehend aus mehr als zwei Scheiben, beispielsweise ein Drei-Scheiben- oder Vier-Scheiben-Isolierglasverbund sein. Die Erfindung soll diesbezüglich nicht eingeschränkt sein.Of course The invention does not only comprise an insulating glass composite of two Slices. This is just the smallest unit. The semitransparent Element can of course be part of an insulating glass composite consisting of more than two discs, such as a three-disc or Be four-pane insulating glass composite. The invention is intended in this regard not restricted.

Insbesondere ist es möglich, dass eine Scheibe des Isolierverbundes eine Verbundglasscheibe ist, bestehend aus wenigstens zwei Scheiben, die mit wenigstens einer Folie, beispielsweise einer PVB-Folie verbunden sind.Especially is it possible for a washer of the insulating composite a laminated glass pane consisting of at least two panes, which is connected to at least one film, for example a PVB film are.

Die Folien, die in die Verbundglasscheibe einlaminiert werden, können auch spezielle Folien sein, beispielsweise eine Folie, die Flüssigkeitskristalle oder elektrochrome Substanzen enthält. Eine derartige Folie ermöglicht es, die Folie von einem nicht transparenten in einen transparenten Zustand durch Anlegung von Spannungen zuschalten. Hierbei wird beispielsweise ein Phasenübergang der Flüssigkristalle von einer zunächst völlig ungeordneten Struktur, die die Folie in Transmission trübe erscheinen lässt, in eine geordnete Phase, die sichtbares Licht transmittieren lässt, umgeschaltet. Die Folie erscheint dann transparent und nicht mehr milchig. Die schaltbare Folie kann die gesamte Fläche des Elementes überdecken oder nur einen Teil.The Foils which are laminated into the laminated glass pane can also be special films, such as a film, the liquid crystals or contains electrochromic substances. Such a film allows the film from a non-transparent switch to a transparent state by applying voltages. Here, for example, a phase transition of the liquid crystals from an initially completely disordered structure, which makes the film appear cloudy in transmission, into an ordered phase that transmits visible light, switched. The slide will then appear transparent and no longer milky. The switchable film can cover the entire surface of the element or only part of it.

Alternativ oder zusätzlich zu einer Folie, die Flüssigkristalle enthält, kann als Folie auch eine Folie verwandt werden, die Streuzentren umfasst. Eine Folie, die Streuzentren umfasst, ist beispielsweise aus der DE-U-200 009 099 oder der DE-U-200 012 471 bekannt geworden. Die Folien, die Streuzentren, beispielsweise eine Streuschicht, umfassen, eignen sich zur Sichtbarmachung projizierter Lichtbilder in dem Bereich der Streufolie.As an alternative or in addition to a film which contains liquid crystals, it is also possible to use as a film a film which comprises scattering centers. A film comprising scattering centers, for example, from the DE-U-200 009 099 or the DE-U-200 012 471 known. The films comprising scattering centers, for example a scattering layer, are suitable for visualizing projected photographs in the area of the scattering film.

Zur Kontrastverstärkung kann zwischen die Streufolie und eine der beiden Scheiben des Verbundglases eine Graufolie als Kontrastverstärkungsmittel eingebracht werden.to Contrast enhancement can be between the scattering foil and a of the two panes of laminated glass, a gray film as a contrast enhancer be introduced.

Wird die Streufolie als eine Folie mit Flüssigkristallen ausgebildet, wie oben beschrieben, so lässt sich die Projektionsfläche von dem streuenden milchig trüben Zustand der schaltbaren Folie mit Flüssigkristallen ausbilden. Eine derartige Projektionsfläche könnte dann wieder, falls keine Projektion mehr vorgenommen wird, in einen transparenten Zustand umgeschaltet werden.Becomes the scattering film is formed as a film with liquid crystals, As described above, so can the projection surface from the scattering milky cloudy state of the switchable Form film with liquid crystals. Such a projection surface could then again, if no projection made is switched to a transparent state.

Die Projektionsfläche lässt die Auf- und Rückprojektion von Bildern und insbesondere Logos zu.The Projection surface leaves the front and back projection of images and in particular logos too.

Ist das transparente Element als Verbundglaselement ausgebildet, so können die Leuchtmittel nicht nur auf dem transparenten Substrat vorgesehen sein, sondern beispielsweise in die transparente Folie einlaminiert sein. Die Folie ist dann Träger der Leuchtmittelis formed the transparent element as a laminated glass element, so The bulbs can not only on the transparent Substrate be provided, but for example in the transparent film be laminated. The film is then the carrier of the bulbs

Für den Fachmann ebenso offensichtlich ist es, dass die Erfindung nicht auf die angegebenen Kombinationen beschränkt ist, sondern selbstverständlich Kombinationen sämtlicher Erfindungselemente untereinander möglich sind, ohne vom Gedanken der Erfindung abzuweichen.For It is also obvious to the person skilled in the art that the invention is not is limited to the specified combinations, but Of course, combinations of all invention elements are possible with each other without departing from the spirit of the invention departing.

Die Erfindung soll nachfolgend anhand der Figuren beispielhaft beschrieben werden, ohne hierauf beschränkt zu sein.The Invention will be described below by way of example with reference to FIGS be, without being limited thereto.

Es zeigen:It demonstrate:

1 den prinzipiellen Aufbau eines Isolierglasverbundes, bestehend aus einem ersten scheibenförmigen Element und einem zweiten scheibenförmigen Element; 1 the basic structure of a Isolierglasverbundes, consisting of a first disc-shaped element and a second disc-shaped element;

2 eine erste Ausführungsform eines erfindungsgemäßen semitransparenten Elementes mit einem ersten scheibenförmigen Element und einem zweiten als Verbundsicherheitsglas ausgebildeten zweiten scheibenförmigen Element; 2 a first embodiment of a semitransparent element according to the invention with a first disc-shaped element and a second formed as a laminated safety glass second disc-shaped element;

3 eine zweite Ausführungsform eines erfindungsgemäßen semitransparenten Elementes, wobei das erste scheibenförmige Element als Verbundsicherheitsglas und das zweite scheibenförmige Element als Verbundsicherheitsglas ausgebildet sind; 3 a second embodiment of a semitransparent element according to the invention, wherein the first disc-shaped element as a laminated safety glass and the second disc-shaped element are formed as laminated safety glass;

4 das Transmissions- und Reflektionsverhalten der Farbeffektbeschichtung; 4 the transmission and reflection behavior of the color effect coating;

5 das Transmissions- und Reflektionsverhalten einer Sonnenschutzbeschichtung der Firma Arcon. 5 the transmission and reflection Behavior of a sunscreen coating company Arcon.

In 1 ist der prinzipielle Aufbau eines erfindungsgemäßen semitransparenten Elementes 12 dargestellt. Das semitransparente Element umfasst zwei scheibenförmige Elemente, ein erstes scheibenförmiges Element 10 und ein zweites scheibenförmiges Element 20.In 1 is the basic structure of a semitransparent element according to the invention 12 shown. The semitransparent element comprises two disc-shaped elements, a first disc-shaped element 10 and a second disc-shaped element 20 ,

Wird das erste scheibenförmige Element 10 in einem Fassadenbauteil eingesetzt, so grenzt es die Außenseite AUSSEN der Fassade und das zweite scheibenförmige Element 20 an die Innenseite INNEN der Fassade. Das erste scheibenförmige Element 10 wird durch eine erste Fläche 1, die der Außenseite zugewandt ist und eine zweite Fläche 2, die der gasförmigen mediumgefüllten Seite des Isolierglasverbundes zugewandt ist, charakterisiert.Will be the first disk-shaped element 10 used in a façade component, it borders the outside EXTERIOR of the facade and the second disc-shaped element 20 to the inside INSIDE the facade. The first disk-shaped element 10 is through a first surface 1 facing the outside and a second surface 2 characterized the gaseous medium-filled side of the insulating glass composite, characterized.

Das zweite scheibenförmige Element 20 wird durch eine dritte Fläche 3, die dem gasförmigen Medium zugewandt ist, und eine vierte Fläche 4, die der Innenseite eines Gebäudes zugewandt ist, charakterisiert. Die beiden scheibenförmigen Elemente 10, 20 sind mit Abstand zu einem Isolierglasverbund verbunden. Die beiden scheibenförmigen Elemente 10, 20 werden mit einer Verbindungseinrichtung 105 verbunden. Der Abstand der Scheiben des Isolierglasverbundes wird durch ein Metallstück 110, bevorzugt Aluminium erhalten. Der Abstand A zwischen der Fläche 2 und der Fläche 3 liegt im Bereich von 5 mm bis 50 mm, bevorzugt im Bereich 10 mm bis 30 mm, insbesondere bei 16 mm. Üblicherweise wird im Inneren des Metallstückes noch ein Trockenmittel eingefüllt (nicht gezeigt), das die dauerhafte Entfernung von Wasser aus dem gasgefüllten Innenraum gewährleistet.The second disk-shaped element 20 is through a third area 3 which faces the gaseous medium and a fourth surface 4 , which faces the inside of a building, characterized. The two disk-shaped elements 10 . 20 are connected at a distance to an insulating glass composite. The two disk-shaped elements 10 . 20 be with a connection device 105 connected. The distance between the panes of the insulating glass composite is through a piece of metal 110 , preferably aluminum. The distance A between the surface 2 and the area 3 is in the range of 5 mm to 50 mm, preferably in the range 10 mm to 30 mm, in particular 16 mm. Usually, a desiccant is still filled inside the metal piece (not shown), which ensures the permanent removal of water from the gas-filled interior.

Um das Abstandsstück 110 gegenüber den scheibenförmigen Elementen abzudichten, ist ein Dichtmaterial 120 vorgesehen, das vorzugsweise aus einem Butylkautschuk besteht.To the spacer 110 To seal against the disc-shaped elements, is a sealing material 120 provided, which preferably consists of a butyl rubber.

Eine vollständige Abdichtung des Zwischenraumes 130 zwischen erstem und zweitem scheibenförmigem Element wird durch unterhalb des Abstandselementes 110 aufgebrachten Butylkautschuk erreicht. Zwischen dem ersten und zweiten scheibenförmigem Element befindet sich bevorzugt ein gasförmiges Medium. Bei erhöhten thermischen Anforderungen wird hier insbesondere ein Edelgasmedium eingesetzt. Das Edelgasmedium kann beispielsweise die Elemente Argon oder Xenon oder Krypton umfassen.A complete seal of the gap 130 between the first and second disc-shaped element is through below the spacer element 110 applied butyl rubber achieved. Between the first and second disk-shaped element is preferably a gaseous medium. In the case of increased thermal requirements, in particular a noble gas medium is used here. The noble gas medium may comprise, for example, the elements argon or xenon or krypton.

Üblicherweise werden die Farbeffektschichten 25 auf beiden Seiten eines Glases aufgetragen. Bei Einsatz einer monolithischen Scheibe wird das Glas auf Fläche 1 und/oder 2 oder Fläche 3 und 4 eingesetzt. Wenn eine Version eines laminierten Glases zum Einsatz kommt, wie es beispielsweise in 2 oder 3 dargestellt ist, wird nur eine der Flächen 1 bis 4 die Beschichtung aufweisen. Bei beidseitiger Beschichtung liegt dann eine mit dem Farbeffekt versehene Fläche innenliegend zwischen Fläche 1 und 2 oder Fläche 3 und 4 wie in 2 und 3 dargestellt. Der beidseitige Auftrag tritt vor allem bei Tauchbeschichtungen auf.Usually, the color effect layers 25 applied on both sides of a glass. When using a monolithic disk, the glass is on surface 1 and or 2 or area 3 and 4 used. If a version of a laminated glass is used, such as in 2 or 3 is shown, only one of the surfaces 1 to 4 have the coating. If coated on both sides, then there is a surface provided with the color effect on the inside between the surface 1 and 2 or area 3 and 4 as in 2 and 3 shown. The two-sided application occurs especially in dip coatings.

Es ist aber auch möglich, dass die Farbeffektschicht 25 entweder nur auf die Fläche 2 oder auf die Fläche 3 aufgebracht werden. Die ist möglich, wenn als Beschichtungsverfahren beispielsweise Sputterverfahren eingesetzt werden. Auch ein Aufbringen nur auf die Fläche 1 wäre möglich. Die Anordnung auf den im Zwischenraum zugewandten Flächen 2 und 3 ist aber bevorzugt, da die Farbeffektschicht dann vor Umwelteinflüssen, insbesondere beispielsweise salzhaltiger Luft, geschützt wird.But it is also possible that the color effect layer 25 either just on the surface 2 or on the surface 3 be applied. This is possible if, for example, sputtering methods are used as the coating method. Also applying only on the surface 1 could be possible. The arrangement on the surfaces facing in the space 2 and 3 However, it is preferred because the color effect layer is then protected from environmental influences, in particular, for example, saline air.

Die auf die Gläser aufgebrachte Farbeffektschicht 25 ist ein Interferenzschichtsystem. Das Interferenzschichtsystem bildet einen winkelsensitiven dichroitischen Spiegel aus, dessen Farbeindruck beziehungsweise Farbeffekt sich mit dem Betrachtungswinkel ändert. Bevorzugt werden die Interferenzschichten der Farbeffektbeschichtung mit Sol-Gel-Tauchtechniken hergestellt. Das Interferenzschichtsystem mit der Farbeffektbeschichtung besteht bevorzugt aus mehr als vier Teilschichten, wobei jede Teilschicht einen unterschiedlichen Brechungsindex aufweist.The color effect layer applied to the glasses 25 is an interference layer system. The interference layer system forms an angle-sensitive dichroic mirror whose color impression or color effect changes with the viewing angle. Preferably, the interference layers of the color effect coating are prepared by sol-gel immersion techniques. The interference coating system with the color effect coating preferably consists of more than four partial layers, each partial layer having a different refractive index.

Ganz allgemein zeichnen sich die Farbeffektschichtsysteme dadurch aus, dass die letzte Schicht der Beschichtung, die dem gasförmigen Medium zugewandt ist, das heißt die letzte Schicht aus Sicht des Substrates gesehen, eine hochbrechende T-Schicht oder eine mittelbrechende M-Schicht ist. Durch nachfolgende Prozesse können diese abschließenden Schichten aber später innerhalb eines Verbundes liegen und dann nicht mehr der gasförmigen Seite des Isolierglasverbundes zugewandt sein.All In general, the color effect layer systems are characterized by that the last layer of the coating that is the gaseous Medium facing, that is, the last layer View of the substrate, a high-refractive T-layer or is a medium refractive M layer. Through subsequent processes but these final shifts can be done later lie within a composite and then no longer the gaseous Be facing side of the insulating glass composite.

Die T-Schicht weist einen hohen Brechungsindex nh ≥ 1,8, bevorzugt zwischen 1,9 < nh < 2,5, die M-Schicht einen mittleren Brechungsindex 1,6 < nm < 1,8 gemessen jeweils bei einer Referenzwellenlänge von 550 nm auf. Die Schichtdicken der einzelnen Schichten liegen bevorzugt im Bereich 10 nm bis 200 nm, bevorzugt zwischen 20 nm und 100 nm.The T-layer has a high refractive index n h ≥ 1.8, preferably between 1.9 <n h <2.5, the M-layer has an average refractive index 1.6 <nm <1.8 measured in each case at a reference wavelength of 550 nm. The layer thicknesses of the individual layers are preferably in the range 10 nm to 200 nm, preferably between 20 nm and 100 nm.

Für die hochbrechende Schicht kann Titanoxid TiO2, Nioboxid Nb2O5, Tantaloxid Ta2O5, Ceroxid CeO2, Hafniumoxid HfO2 oder Mischungen dieser Stoffe miteinander eingesetzt werden.For the high refractive index layer of titanium oxide TiO 2, niobium oxide Nb 2 O 5, Ta 2 O 5 tantalum oxide, cerium oxide CeO 2, hafnium oxide HfO 2 or mixtures of these substances can be used together.

Für die mittelbrechende Schicht kann eine Mischung aus Titanoxid und Siliziumoxid TiO2/SiO2, sowie auch Mischungen mit Aluminiumoxid Al2O3 oder Zirkonoxid ZrO2 zum Einsatz kommen. Für den Fachmann ergeben sich weitere Materialsysteme, die die geforderten Brechungsindices erreichen, jedoch in der Beschichtungstechnologie weniger üblich sind.For the mid-refractive layer, a mixture of titanium oxide and silicon oxide TiO 2 / SiO 2 , as well as mixtures with aluminum oxide Al 2 O 3 or zirconium oxide ZrO 2 are used. Those skilled in the art will find other material systems that achieve the required refractive indices, but are less common in coating technology.

Betreffend die Wahl der Schichtzusammensetzungen für die unterschiedlichen Schichten, die Auftragsverfahren, die Substratmaterialien bzw. Substratgläser wird auf die US-Anmeldungen US 6,720,081 und US 7,169,441 verwiesen, deren Offenbarungsgehalt vollumfänglich in diese Anmeldung mit aufgenommen wird.Concerning the choice of coating compositions for the different ones Layers, the application method, the substrate materials or substrate glasses Reference is made to US applications US 6,720,081 and US 7,169,441, the disclosure of which is fully incorporated in this application is recorded.

Bevorzugt weisen die Farbeffektschichten mehr als vier Schichten unterschiedlichen Brechungsindexes auf.Prefers the color effect layers have more than four layers of different Refractive index on.

Folgende Schichtaufbauten für Farbeffektschichten wären möglich:
Substrat und optional S-Schicht mit Brechungsindex weitgehend dem Substrat entsprechend, T-Schicht, S-Schicht, T-Schicht, S-Schicht, T-Schicht, Luft.The following layer structures for color effect layers would be possible:
Substrate and optionally S-layer with refractive index largely corresponding to the substrate, T-layer, S-layer, T-layer, S-layer, T-layer, air.

Alternativ wäre möglich beispielsweise der Aufbau
Substrat und optional S-Schicht mit Brechungsindex weitgehend dem Substrat entsprechend, M-Schicht, S-Schicht, T-Schicht, S-Schicht, M-Schicht,
wobei die T-Schicht eine hochbrechende Schicht, die M-Schicht eine mittelbrechende Schicht und die S-Schicht eine niedrigbrechende Schicht mit Brechungsindex ist. Die S-Schicht weist als niedrigbrechende Schicht einen Brechungsindex nn < 1,6, bevorzugt im Bereich zwischen 1,38 und 1,50 bei einer Referenzwellenlänge von 550 nm auf. Als Materialien für die niedrigbrechende Schicht kann SiO2 verwandt werden. Anstelle von SiO2 kann für die niedrigbrechende Schicht auch MgF2 eingesetzt werden. Aus diesen Kombinationen können weitere Schichtsysteme abgeleitet werden, die jeweils alternierende Grundelemente aus S-Schicht/T-Schicht und/oder S-Schicht/M-Schicht aufweisen. Dabei steigt die Steilheit der Filterwirkung mit ansteigender Schichtanzahl. Üblicherweise werden aus ökonomischen Gründen Vielfachschichtsysteme mit weniger als 13 Einzelschichten eingesetzt. Im Sinne der Erfindung ist dies jedoch nicht beschränkend.Alternatively, for example, the structure would be possible
Substrate and optionally S-layer with refractive index substantially corresponding to the substrate, M-layer, S-layer, T-layer, S-layer, M-layer,
wherein the T-layer is a high refractive index layer, the M layer is a medium refractive index layer, and the S layer is a low refractive index refractive index layer. The S-layer has, as a low-refractive index layer, a refractive index n n <1.6, preferably in the range between 1.38 and 1.50 at a reference wavelength of 550 nm. SiO 2 can be used as materials for the low refractive index layer. Instead of SiO 2 , MgF 2 can also be used for the low-index layer. From these combinations, further layer systems can be derived, each having alternating primitives of S-layer / T-layer and / or S-layer / M-layer. The steepness of the filter effect increases with increasing number of layers. Usually, multilayer systems with fewer than 13 individual layers are used for economic reasons. For the purposes of the invention, however, this is not restrictive.

Im Gegensatz zur aus der US 6,720,081 , der US 7,169,441 bekannten Interferenzbeschichtungen für eine breitbandige Entspiegelung zeichnet sich das Farbeffektschichtsystem gemäß der vorliegenden Erfindung dadurch aus, dass als letzte, dem gasförmigen Medium zugewandte Schicht keine niedrigbrechende S-Schicht eingesetzt wird, sondern stets eine T-Schicht und eine M-Schicht. Speziell bei Schichtsystemen mit wenigen Einzelschichten ist diese letzte Schicht bestimmend für das Reflektionsverhalten und damit den Farbeffekt des Interferenz-Schichtsystems. Bei Schichtsystemen mit hoher Schichtanzahl (typischerweise mehr als 5-Schichten) sinkt die Bedeutung der letzten Schicht, so dass ggf. sogar eine S-Abschlussschicht tolerabel wird.In contrast to from the US 6,720,081 , of the US 7,169,441 known interference coatings for a broadband anti-reflection coating, the color effect layer system according to the present invention is characterized in that the last, the gaseous medium-facing layer is not used low-breaking S-layer, but always a T-layer and an M-layer. Especially in layer systems with few individual layers, this last layer is decisive for the reflection behavior and thus the color effect of the interference layer system. For layer systems with a high number of layers (typically more than 5 layers), the significance of the last layer decreases, so that even an S-terminating layer may possibly become tolerable.

In 2 ist ein alternativer Aufbau der Erfindung gezeigt. Im Gegensatz zu 1 weist das Isolierglaselement 200 gemäß 2 ein erstes scheibenförmiges Element 210, das als Einscheibenglas ausgebildet ist, beispielsweise ein Einscheibensicherheitsglas oder ein teilvorgespanntes Einscheibenglas und ein zweites scheibenförmiges Element 220, das als Verbundglasscheibe ausgebildet ist, auf. Verbundglasscheiben sind aus dem Stand der Technik hinlänglich bekannt. Sie weisen zwei Einzelscheiben 220.1, 220.2 auf, die beispielsweise mit einem Gießharz oder einer Folie direkt zu einem Verbund laminiert sind. Vorliegend handelt es sich um einen Folienverbund. Die zwischen die beiden Scheiben und die Sicherheitsscheibe eingebrachte Folie ist mit Bezugsziffer 222 bezeichnet. Bei dem vorliegenden Ausführungsbeispiel ist auf die Fläche 2 des ersten scheibenförmigen Elementes 210 eine Sonnenschutzbeschichtung 224, wie sie beispielsweise von der Firma arcon, Feuchtwangen unter dem Markennamen „sunbelt" angeboten wird, aufgebracht. Die Sonnenschutzbeschichtung zeichnet sich durch eine hohe Lichttransmission des Tageslichtes, einen geringen Gesamtenergiedurchlass zur Verhinderung von starken Aufheizungen sowie eine hohe Wärmedämmung zur Verhinderung von Wärmeverlusten im Winter aus.In 2 an alternative construction of the invention is shown. In contrast to 1 has the insulating glass element 200. according to 2 a first disc-shaped element 210 , which is designed as a single-pane glass, for example, a single-pane safety glass or a teilvorgespanntes single-pane glass and a second disc-shaped element 220 , which is designed as a laminated glass pane, on. Laminated glass panes are well known in the art. They have two individual discs 220.1 . 220.2 on, for example, with a casting resin or a film laminated directly into a composite. In the present case, it is a film composite. The foil inserted between the two discs and the safety disc is numbered 222 designated. In the present embodiment is on the surface 2 of the first disc-shaped element 210 a sunscreen coating 224 , as offered for example by the company arcon, Feuchtwangen under the brand name "sunbelt." The sunscreen coating is characterized by a high light transmission of daylight, a low total energy to prevent strong heat-up and high thermal insulation to prevent heat loss in winter out.

Die Folie 222 hat in der dargestellten Ausführungsform keine weitere Funktion. Möglich wäre aber auch eine Folie 222 vorzusehen die über Funktionen verfügt oder eine weitere nicht dargestellte Folie.The foil 222 has no other function in the illustrated embodiment. But it would also be possible to have a foil 222 provide the features or has another film, not shown.

Beispielsweise könnte die Folie 222 eine Folie sein, in die Leuchtmittel beispielsweise Leuchtdioden eingebracht sind.For example, the film could 222 be a film in the light bulbs, for example, LEDs are introduced.

Alternativ oder zusätzlich könnte die Folie eine Folie sein, die Flüssigkristalle oder elektrochrome Substanzen umfasst und mittels zweier Elektroden in zwei Zustände, nämlich einem transmittiven und einen nicht oder weniger transmittiven Zustand geschaltet werden könnte. Als Elektroden können beispielsweise leitfähige Beschichtungen auf dem Glas selbst dienen, beispielsweise ITO oder ATO-Schichten oder Polyesterfolien, die mit einer leitfähigen Beschichtung versehen werden und zusätzlich eingebracht werden. Wird dann an die Elektroden eine Spannung angelegt, so kann ein Schalten zwischen zwei Zuständen erreicht werden. In einer ersten Ausgestaltung kann beispielsweise ein Flüssigkeitskristall von einem streuenden und damit weitgehend nicht transmittiven Zustand in einen geordneten und damit transmittiven Zustand geschaltet werden. Bei elektrochromen Substanzen ist es möglich von einem helltransparenten in einen dunkeltransparenten Zustand und damit weitgehend unsichtbaren Zustand zu schalten.Alternatively or additionally, the film could be a film comprising liquid crystals or electrochromic substances and could be switched by means of two electrodes in two states, namely a transmissive and a non or less transmissive state. For example, conductive coatings on the glass itself can serve as electrodes, for example ITO or ATO layers or polyester films, which are provided with a conductive coating and are additionally introduced. If a voltage is then applied to the electrodes, switching between two states can be achieved. In a first embodiment, for example, a liquid crystal switched from a scattering and therefore largely non-transmissive state into an ordered and thus transmissive state become. With electrochromic substances, it is possible to switch from a light transparent to a dark transparent state and thus a largely invisible state.

Bei Flüssigkristallen wäre es des Weiteren möglich, noch zusätzlich Polarisationsfolien einzubringen und in Flüssigkeitskristallen durch Anlegen von Spannungen an den beiden Elektrode von einem ersten Polarisationszustand in einen zweiten Polarisationszustand zu schalten.at Liquid crystals would also be possible additionally to introduce polarizing films and in Liquid crystals by applying voltages to the two electrodes from a first polarization state into one to switch to the second polarization state.

Durch eine derartige schaltbare Folie könnte das erfindungsgemäße Element einmal transparent und einmal für den Betrachter intransparent erscheinen.By Such a switchable film could be the inventive Element once transparent and once for the viewer appear intransparent.

Des Weiteren wäre es möglich, die Folie als eine Folie auszubilden die mit Streukörpern versehen ist. Eine solche mit Streukörpern versehene Folie gibt dann die Möglichkeit einer Auf- oder Rückprojektion zur Darstellung von projizierten Bildern auf dem optischen Element.Of Further, it would be possible to use the film as a film form which is provided with scattering bodies. Such With foils provided foil then gives the opportunity an up or back projection to represent projected Pictures on the optical element.

Eingesetzt werden kann eine derartige Streufolie zur Projektion bei einer Fassadenkonstruktion einer Multimediafassade, bei denen Bilder projiziert werden sollen.used can be such a scattering film for projection in a facade construction a multimedia façade where images are to be projected.

Das Einbringen von Leuchtdioden wäre nicht nur im Rahmen einer Folie möglich, sondern auch beispielsweise dadurch, dass eines der beiden scheibenförmigen Elemente 210 bzw. 220 auf der Innenseite mit einer leitfähigen Beschichtung beispielsweise aus einem oder mehreren der nachfolgenden Metalloxide:

  • InOx:Sn
  • – SnOx:F
  • – SnOx:Sb
  • – ZnOx:Ga
  • – ZnOx:B
  • – ZnOx:F
  • – ZnOx:Al
  • – Ag/TiOx
versehen ist.The introduction of light-emitting diodes would not only be possible in the context of a film, but also, for example, in that one of the two disk-shaped elements 210 respectively. 220 on the inside with a conductive coating, for example of one or more of the following metal oxides:
  • InO x: Sn
  • - SnO x: F
  • - SnO x : Sb
  • - ZnO x: Ga
  • - Zno x : B
  • - ZnO x : F
  • - ZnO x : Al
  • - Ag / TiO x
is provided.

Besonders bevorzugt ist die leitfähige Beschichtung als hochleitfähige Beschichtung mit einem Schichtwiderstand R☐ ≤ 15 Ohms/square (Ω/☐), insbesondere ≤ 10 Ohms/square (Ω/☐), insbesondere ≤ 9 Ohms/square (Ω/☐), insbesondere ≤ 7 Ohms/square (Ω/☐), insbesondere ≤ 5 Ohms/square (Ω/☐) ausgebildet. Die Schichtdicken der hochleitfähigen Schichten betragen bevorzugt mehr als 150 nm, bevorzugt mehr als 180 nm, insbesondere bevorzugt mehr als 280 nm, ganz bevorzugt mehr als 420 nm, insbesondere bevorzugt mehr als 500 nm, ganz besonders bevorzugt mehr als 550 nm. Die Durchlässigkeit bei einer Wellenlänge von 550 nm derartiger Schichten beträgt mehr als 82%, insbesondere mehr als 87%, ganz besonders bevorzugt mehr als 89%. Ein weiterer Vorteil der SnOx:F, insbesondere der SnO2:F-Schicht ist, dass diese nicht nur als leitfähige Schicht, sondern auch als Wärmedämmschicht wirkt.The conductive coating is particularly preferably a highly conductive coating having a sheet resistance R ≦ ≦ 15 ohms / square (Ω / □), in particular ≦ 10 ohms / square (Ω / □), in particular ≦ 9 ohms / square (Ω / □), in particular ≦ 7 ohms / square (Ω / □), in particular ≤ 5 ohms / square (Ω / □) is formed. The layer thicknesses of the highly conductive layers are preferably more than 150 nm, preferably more than 180 nm, more preferably more than 280 nm, more preferably more than 420 nm, more preferably more than 500 nm, most preferably more than 550 nm a wavelength of 550 nm of such layers is more than 82%, in particular more than 87%, very particularly preferably more than 89%. Another advantage of the SnO x : F, in particular the SnO 2 : F layer, is that it not only acts as a conductive layer, but also as a thermal barrier coating.

Bei dem zweiten scheibenförmigen Element 220 ist erfindungsgemäß eine Farbeffektschicht 226 als Interferenzschicht gemäß dem zuvor beschriebenen Aufbau z. B. ein Fünf-Schicht System T-Schicht, S-Schicht, T-Schicht, S-Schicht, T-Schicht aufgebracht. Die Dicke D1 der ersten Scheibe liegt im Bereich von 6 mm bis 20 mm, bevorzugt bei 10 mm, die Dicke D2 der Verbundscheibe liegt bevorzugt zwischen 6 mm und 20 mm, bevorzugt ebenfalls bei 10 mm, und der Scheibenabstand A bei 16 mm. Als Füllgas ist zwischen die beiden Scheibenelemente bevorzugt zu 100% Argon mit einem Gasfüllgrad von 95% eingebracht.In the second disc-shaped element 220 is a color effect layer according to the invention 226 as an interference layer according to the structure described above z. B. a five-layer system T-layer, S-layer, T-layer, S-layer, T-layer applied. The thickness D1 of the first disc is in the range of 6 mm to 20 mm, preferably 10 mm, the thickness D2 of the composite disc is preferably between 6 mm and 20 mm, preferably also 10 mm, and the disc spacing A is 16 mm. As the filling gas is preferably introduced between the two disc elements to 100% argon with a Gasfüllgrad of 95%.

In 3 ist eine alternative Ausgestaltung der Erfindung dargestellt. Das semitransparente Element 300 besteht aus einem ersten scheibenförmigen Element 310, das als Verbundscheibe ausgebildet ist, und einem zweiten scheibenförmigen Element 320, das ebenfalls als Verbundscheibe ausgebildet ist. Die Dicke des ersten scheibenförmigen Elementes D1 beträgt ungefähr 10 mm und die Dicke des zweiten scheibenförmigen als Verbundscheibe ausgebildeten Elementes 220 beträgt ungefähr 8 mm. Der Abstand A zwischen den zwei scheibenförmigen Elementen beträgt 16 mm. Die Farbeffektschicht als Interferenzschicht ist in vorliegendem Ausführungsbeispiel auf die Fläche 2 aufgebracht und mit Bezugsziffer 326 bezeichnet und kann als Fünf-Schicht-System T-Schicht, S-Schicht, T-Schicht, S-Schicht, T-Schicht ausgeführt sein. Die Fläche 3 des Isolierglasscheibenverbundes ist mit einer Wärmedämmschicht, beispielsweise der Wärmedämmschicht arcon n30 der Firma arcon, Feuchtwangen beschichtet mit einem Emissionsvermögen von ε = 0,02. Das zwischen die beiden Scheiben des Isolierglasverbundes eingebrachte Gas ist wiederum zu 100% ein Argon-Edelgas, wobei der Gasfüllgrad 95% beträgt.In 3 an alternative embodiment of the invention is shown. The semitransparent element 300 consists of a first disk-shaped element 310 , which is formed as a composite disc, and a second disc-shaped element 320 , which is also designed as a composite disc. The thickness of the first disk-shaped element D1 is about 10 mm and the thickness of the second disc-shaped element formed as a composite disk 220 is about 8 mm. The distance A between the two disc-shaped elements is 16 mm. The color effect layer as an interference layer is in the present embodiment on the surface 2 applied and with reference numeral 326 and can be designed as a five-layer system T-layer, S-layer, T-layer, S-layer, T-layer. The area 3 of the insulating glass pane composite is coated with a heat-insulating layer, for example the heat-insulating layer arcon n30 from arcon, Feuchtwangen, with an emissivity of ε = 0.02. The gas introduced between the two panes of the insulating glass composite is again 100% argon inert gas, the degree of gas filling being 95%.

Obwohl hier nur einige Aufbauten gezeigt sind, sind diese nicht einschränkend. Die Farbeffektschicht kann auf Fläche 1, Fläche 2, Fläche 3 oder Fläche 4 aufgebracht sein oder auf Grenzflächen innerhalb des ersten oder des zweiten Substrates des ersten bzw. zweiten scheibenförmigen Elementes. Grenzen innerhalb des Substrates ergeben sich beispielsweise im Falle von Verbundscheiben, z. B. dort wo zwischen zwei Scheiben eines Verbundes eine Folie einlaminiert ist. Ebenso können zusätzliche Schichten wie Sonnenschutzschichten oder Schichten niedriger Emittivität auf Fläche 2 oder 3 oder eine Grenze im ersten oder im zweiten Substrat aufgebracht sein. Auch ein Aufbringen auf eine Farbeffektschicht oder umgekehrt einer Farbeffektschicht auf die weitere Beschichtung wäre möglich, ohne dass vom Gedanken der Erfindung abgewichen wird.Although only a few constructions are shown here, these are not limiting. The color effect layer can be on area 1 , Area 2 , Area 3 or area 4 be applied or on interfaces within the first or the second substrate of the first and second disc-shaped element. Borders within the substrate arise, for example in the case of composite discs, z. B. where between two discs of a composite a film is laminated. Likewise, additional layers such as sunscreens or layers of lower emissivity on area 2 or 3 or a boundary may be applied in the first or in the second substrate. Also an application on a color effect Layer or vice versa a color effect layer on the further coating would be possible without departing from the spirit of the invention.

In 4a ist das Reflektions- und Transmissionsverhalten mit einer Farbeffektschicht mit mehr als vier Schichten, beispielsweise ein Fünf-Schicht-System T-Schicht, S-Schicht, T-Schicht, S-Schicht, T-Schicht, hergestellt mit Sol-Gel-Tauchtechnik dargestellt. Das Interferenzschichtsystem arbeitet nach dem Prinzip des dichroitischen Spiegels. Wie aus 4a deutlich zu ersehen, reflektiert das durch das Interferenzlichtsystem ausgebildete Farbeffektschichtsystem mehr als 20% des einfallenden Lichtes im Wellenlängenbereich von 400 nm bis 500 nm, wohingegen die Transmission in diesem Bereich weniger als 60% beträgt. Aufgrund der Interferenzeigenschaft der Beschichtung verschiebt sich dieses spektrale Transmissions- und Reflektionsverhaltens je nach Betrachtungswinkel der dichroitische Spiegel und erscheint unterschiedlich farbig.In 4a is the reflection and transmission behavior with a color effect layer with more than four layers, for example, a five-layer system T-layer, S-layer, T-layer, S-layer, T-layer, prepared with sol-gel immersion shown , The interference layer system works on the principle of the dichroic mirror. How out 4a clearly seen, formed by the interference light system color effect layer system reflects more than 20% of the incident light in the wavelength range of 400 nm to 500 nm, whereas the transmission in this range is less than 60%. Due to the interference property of the coating, this spectral transmission and reflection behavior shifts depending on the viewing angle of the dichroic mirror and appears differently colored.

Im Gegensatz zu dem Interferenzschichtsystem, das Farbeffekte alleine durch unterschiedliches Reflektionsverhalten im sichtbaren Wellenlängenbereich erzeugt hat, sind bei vielen Systemen gemäß dem Stand der Technik Farbeffekte immer durch Absorption erreicht worden, beispielsweise indem dem Licht absorbierende Stoffe bei der Glasherstellung dem Gemenge zugeben wird. Das Transmissions- und Reflektionsverhalten einer derartigen Beschichtung, die im vorliegenden Falle aufgrund der hohen Lichtabsorption und damit des hohen Wärmeeintrages nicht geeignet ist für einen Isolierglasverbund, ist in 4b gezeigt. Wie hieraus zu ersehen, ist die Absorption im Wellenlängenbereich von 500 nm bis 650 nm erheblich, da im allgemeinen gilt, dass R + T + A ungefähr 1 ist, wobei R die Reflektion, T die Transmission und A die Absorption eines Mediums bezeichnet.In contrast to the interference layer system, which has produced color effects solely by different reflectivity in the visible wavelength range, in many prior art systems color effects have always been achieved by absorption, for example by adding light absorbing substances to the batch in glassmaking. The transmission and reflection behavior of such a coating, which in the present case due to the high light absorption and thus the high heat input is not suitable for an insulating glass composite, is in 4b shown. As can be seen, the absorption in the wavelength range of 500 nm to 650 nm is significant, since it is generally true that R + T + A is about 1, where R denotes the reflection, T the transmission and A the absorption of a medium.

In 5 schließlich ist das Transmissions- und Reflektionsverhalten einer Sonnenschutzbeschichtung, wie sie im Ausführungsbeispiel gemäß 2 auf Fläche 2 eingesetzt wird, gemäß dem Stand der Technik aus dem Datenblatt der arcon Flachglas-Veredelung GmbH & Co. KG, Industriestraße 10, 91555 Feuchtwangen, dargestellt. Wie aus 5 ersichtlich, zeichnet sich das Sonnenschutzglas durch eine sehr hohe Reflektivität im Bereich von Wellenlängen > 700 nm aus. Eine derartige Schicht besteht aus einem Schichtaufbau mit bis zu 15 Einzelschichten.In 5 Finally, the transmission and reflection behavior of a sunscreen coating, as in the embodiment according to 2 on surface 2 is used, according to the prior art from the data sheet of arcon flat glass processing GmbH & Co. KG, Industriestraße 10, 91555 Feuchtwangen, shown. How out 5 As can be seen, the solar control glass is characterized by a very high reflectivity in the range of wavelengths> 700 nm. Such a layer consists of a layer structure with up to 15 individual layers.

Mit der vorliegenden Erfindung wird somit erstmals ein Isolierglasverbund bestehend aus wenigstens zwei scheibenförmigen Elementen angegeben, der einen Farbeffekt aufweist, die sich durch eine hohe Wärmedämmung auszeichnet.With The present invention thus becomes an insulating glass composite for the first time consisting of at least two disc-shaped elements indicated, which has a color effect, which is characterized by a high Thermal insulation distinguishes.

Besonders bevorzugte Effekte werden erzielt in Kombination des erfindungsgemäßen semitransparenten Element mit Leuchtmitteln und zwar sowohl mit Leuchtmitteln in Form von Leuchtdioden wie auch einfachen Hintergrundbeleuchtungen. Mit Leuchtmitteln ist es möglich, die Lichtwirkung der Hinterleuchtung bei einem Fassadenelement durch Anpassung der Beschichtung, insbesondere durch Variierung der Lichttransmission gezielt zu verändern. Hierdurch lassen sich Nachteffektgläser herstellen, die je nach Beschichtung unterschiedliche farbliche Gestalt annehmen. Insbesondere ist dies bei einer flächen- oder partiellen Hinterleuchtung des semitransparenten Elementes bei der Verwendung als Fassadenelementen von Interesse.Especially preferred effects are achieved in combination of the invention semitransparent element with bulbs and both with Light sources in the form of LEDs as well as simple backlighting. With bulbs it is possible to increase the lighting effect of Backlighting of a façade element by adaptation of the coating, in particular by varying the light transmission to change specifically. As a result, night effect glasses can be produced which depending on the coating, take on different colors. In particular, this is in a surface or partial Backlighting of the semitransparent element in use as facade elements of interest.

ZITATE ENTHALTEN IN DER BESCHREIBUNGQUOTES INCLUDE IN THE DESCRIPTION

Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list The documents listed by the applicant have been automated generated and is solely for better information recorded by the reader. The list is not part of the German Patent or utility model application. The DPMA takes over no liability for any errors or omissions.

Zitierte PatentliteraturCited patent literature

  • - EP 1450416 A [0031, 0035] - EP 1450416 A [0031, 0035]
  • - EP 1450416 [0034] EP 1450416 [0034]
  • - WO 2006/018066 [0034, 0035] WO 2006/018066 [0034, 0035]
  • - DE 200009099 U [0042] - DE 200009099 U [0042]
  • - DE 200012471 U [0042] - DE 200012471 U [0042]
  • - US 6720081 [0071] - US 6720081 [0071]
  • - US 7169441 [0071] - US 7169441 [0071]

Zitierte Nicht-PatentliteraturCited non-patent literature

  • - www.schott.com\architecture [0005] - www.schott.com \ architecture [0005]
  • - www.pilkington.com [0026] - www.pilkington.com [0026]

Claims (35)

Semitransparentes Element, insbesondere Fassadenelement, umfassend wenigstens ein erstes scheibenförmiges Element; wenigstens ein zweites scheibenförmiges Element; wenigstens eine Verbundeinrichtung zum Verbinden von erstem und zweitem scheibenförmigem Element mit einem Abstand zueinander, dadurch gekennzeichnet, dass, das erste und/oder das zweite scheibenförmige Element wenigstens teilweise eine Beschichtung aufweist, wobei die Beschichtung für einen Betrachter zu einem Farbeffekt im sichtbaren Wellenlängenbereich führt und die die Absorption der Beschichtung im sichtbaren Wellenlängenbereich < 5%, insbesondere < 3%, bevorzugt < 2%, ganz bevorzugt < 1% des auf die Beschichtung einfallenden Lichtes ist.Semitransparent element, in particular facade element, comprising at least a first disk-shaped element; at least one second disc-shaped element; at least one composite device for connecting the first and second disc-shaped element with a distance from one another, characterized in that the first and / or the second disc-shaped element at least partially has a coating, wherein the coating for a viewer leads to a color effect in the visible wavelength range, and which is the absorption of the coating in the visible wavelength range <5%, in particular <3%, preferably <2%, very preferably <1% of the light incident on the coating. Semitransparentes Element, insbesondere Fassadenelement, umfassend wenigstens ein erstes scheibenförmiges Element; wenigstens ein zweites scheibenförmiges Element; wenigstens eine Verbundeinrichtung zum Verbinden von erstem und zweitem scheibenförmigem Element mit einem Abstand zueinander, dadurch gekennzeichnet, dass, das erste und/oder das zweite scheibenförmige Element wenigstens teilweise eine Beschichtung aufweist, wobei die Beschichtung für einen Betrachter zu einem Farbeffekt im sichtbaren Wellenlängenbereich führt und die die Absorption der Beschichtung im sichtbaren Wellenlängenbereich < 5%, insbesondere < 3%, bevorzugt < 2%, ganz bevorzugt < 1% des auf die Beschichtung einfallenden Lichtes ist und das erste und/oder das zweite scheibenförmige Element Leuchtmittel umfasst.Semitransparent element, in particular facade element, full at least one first disc-shaped element; at least a second disc-shaped member; at least one Composite device for connecting the first and second disk-shaped Element with a distance to each other, characterized, that, the first and / or the second disk-shaped Element has at least partially a coating, wherein the Coating for a viewer to a color effect in the visible wavelength range leads and which the Absorption of the coating in the visible wavelength range <5%, in particular <3%, preferably <2%, more preferably <1% of the on Coating incident light is and the first and / or the second disc-shaped element comprises bulbs. Semitransparentes Element nach Anspruch 1 oder 2, dadurch gekennzeichnet, dass innerhalb des sichtbaren Wellenlängenbereiches von 420 nm bis 700 nm durch die Beschichtung mindestens ein Übergang von erhöhter Reflektivität auf ein niedrige Reflektivität zur Verfügung gestellt wird, der den Farbeffekt verursacht.Semitransparent element according to claim 1 or 2, characterized in that within the visible wavelength range from 420 nm to 700 nm through the coating at least one transition from increased reflectivity to low reflectivity is provided, which causes the color effect. Semitransparentes Element nach einem der Ansprüche 1 bis 3, dadurch gekennzeichnet, dass die Beschichtung wenigstens zwei Teilschichten umfasst, eine erste Teilschicht und eine zweite Teilschicht, wobei die zweite Teilschicht auf die erste Teilschicht aufgebracht ist und die zweite Teilschicht die letzte, einem gasförmigem Medium zugewandte Schicht der Beschichtung ist, wobei die zweite Schicht entweder eine T- oder M-Schicht ist mit einem Brechungsindex für eine T-Schicht: nh ≥ 1,8, bevorzugt zwischen 1,9 < nh < 2,3 M-Schicht: 1,6 < nm < 1,8 ist.Semitransparent element according to one of claims 1 to 3, characterized in that the coating comprises at least two sub-layers, a first sub-layer and a second sub-layer, wherein the second sub-layer is applied to the first sub-layer and the second sub-layer, the last, facing a gaseous medium Layer of the coating is, wherein the second layer is either a T or M layer with a refractive index for a T-layer: n h ≥ 1.8, preferably between 1.9 <n h <2.3 M layer: 1.6 <nm <1.8. Semitransparentes Element nach Anspruch 4, dadurch gekennzeichnet, dass die erste und/oder die zweite Teilschicht aus mehreren Einzelschichten besteht.Semitransparent element according to claim 4, characterized in that the first and / or the second partial layer consists of consists of several individual layers. Semitransparentes Element nach einem der Ansprüche 1 bis 5, dadurch gekennzeichnet, dass das erste scheibenförmige Element ein erstes Substrat mit einer ersten Fläche (1) und einer zweiten Fläche (2), die dem zweiten scheibenförmigen Element zugewandt ist, umfasst.Semitransparent element according to one of claims 1 to 5, characterized in that the first disc-shaped element, a first substrate having a first surface ( 1 ) and a second surface ( 2 ) facing the second disc-shaped member. Semitransparentes Element nach einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, dass das zweite scheibenförmige Element ein zweites Substrat mit einer dritten Fläche (3) und einer vierten Fläche (4) umfasst, wobei die dritte Fläche (3) der zweiten Fläche (2) des ersten scheibenförmigen Elementes zugewandt ist.Semitransparent element according to one of claims 1 to 6, characterized in that the second disc-shaped element, a second substrate having a third surface ( 3 ) and a fourth surface ( 4 ), wherein the third surface ( 3 ) of the second surface ( 2 ) faces the first disc-shaped element. Semitransparentes Element nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, dass die Beschichtung auf die erste Fläche des ersten Substrates und/oder die zweite Fläche des ersten Substrates aufgebracht ist.Semitransparent element according to one of the claims 1 to 7, characterized in that the coating on the first Surface of the first substrate and / or the second surface of the first substrate is applied. Semitransparentes Substrat nach Anspruch 8, dadurch gekennzeichnet, dass das erste Substrat keine Grenze zwischen erster und zweiter Fläche aufweist, die beschichtet ist.Semitransparent substrate according to claim 8, characterized characterized in that the first substrate is not a boundary between the first and second surface which is coated. Semitransparentes Substrat nach Anspruch 8, dadurch gekennzeichnet, dass das erste Substrat mindestens eine Grenze aufweist, beispielsweise die Grenze bei einem Verbundglas und die mindestens eine Grenze die Beschichtung aufweist.Semitransparent substrate according to claim 8, characterized characterized in that the first substrate has at least one boundary, For example, the limit for a laminated glass and the at least one Border has the coating. Semitransparentes Substrat nach Anspruch 8, dadurch gekennzeichent, dass das erste Substrat keine Grenze zwischen erster und zweiter Fläche aufweist und die zweite Fläche eine weitere Beschichtung aufweist, wobei die weitere Beschichtung eine oder beide der nachfolgenden Beschichtungen ist: – eine Beschichtung mit niedriger Emittivität – eine Sonnenschutzschicht – eine IR-reflektierende Beschichtung – eine leitfähige BeschichtungSemitransparent substrate according to claim 8, characterized characterized in that the first substrate is not a boundary between the first and second surface and the second surface having a further coating, wherein the further coating a or both of the following coatings is: - one Low emissivity coating - one Solar control coating - An IR-reflective coating - one conductive coating Semitransparentes Substrat nach Anspruch 8, dadurch gekennzeichnet, dass das erste Substrat mindestens eine Grenze aufweist, beispielsweise die Grenze bei einem Verbundglas und die mindestens eine Grenze eine weitere Beschichtung aufweist, wobei die Beschichtung eine oder beide der nachfolgenden Beschichtungen ist: – eine Beschichtung mit niedriger Emittivität – eine Sonnenschutzschicht – eine IR-reflektierende Beschichtung – eine leitfähige BeschichtungSemitransparent substrate according to claim 8, characterized characterized in that the first substrate has at least one boundary, For example, the limit for a laminated glass and the at least one Border has another coating, wherein the coating one or both of the following coatings is: - one Low emissivity coating - one Solar control coating - An IR-reflective coating - one conductive coating Semitransparentes Element nach einem der Ansprüche 8 bis 12, dadurch gekennzeichnet, dass die dritte Fläche des zweiten Substrates eine weitere Beschichtung aufweistSemitransparent element according to one of the claims 8 to 12, characterized in that the third surface the second substrate has a further coating Semitransparentes Element nach Anspruch 13, dadurch gekennzeichnet, dass die weitere Beschichtung eine der nachfolgenden Schichten ist: eine Beschichtung niedriger Emittivität (niedrig ε-Schicht), insbesondere eine Wärmeschutzschicht.Semitransparent element according to claim 13, characterized marked that the further coating one of the subsequent layers is: a low emissivity coating (low ε layer), in particular a heat protection layer. Semitransparentes Element gemäß einem der Ansprüche 1 bis 14, dadurch gekennzeichnet, dass die Beschichtung auf die dritte Fläche (3) und/oder die vierte Fläche (4) des zweiten Substrates aufgebracht ist.Semitransparent element according to one of claims 1 to 14, characterized in that the coating on the third surface ( 3 ) and / or the fourth surface ( 4 ) of the second substrate is applied. Semitransparentes Substrat nach Anspruch 15, dadurch gekennzeichnet, dass das zweite Substrat keine Grenze zwischen dritter und vierter Fläche aufweist, die beschichtet ist.Semitransparent substrate according to claim 15, characterized characterized in that the second substrate is not a boundary between third and fourth surface which is coated. Semitransparentes Substrat nach Anspruch 15, dadurch gekennzeichnet, dass das zweite Substrat mindestens eine Grenze aufweist, beispielsweise die Grenze bei einem Verbundglas und dass die Grenze die Beschichtung aufweist.Semitransparent substrate according to claim 15, characterized characterized in that the second substrate has at least one boundary has, for example, the limit in a laminated glass and that the border has the coating. Semitransparentes Substrat nach Anspruch 15, dadurch gekennzeichent, dass das erste Substrat keine Grenze zwischen erster und zweiter Fläche aufweist und die zweite Fläche eine weitere Beschichtung aufweist, wobei die weitere Beschichtung eine oder beide der nachfolgenden Beschichtungen ist: – eine Beschichtung mit niedriger Emittivität – eine Sonnenschutzschicht – eine leitfähige Beschichtung – eine IR-reflektierende BeschichtungSemitransparent substrate according to claim 15, characterized characterized in that the first substrate is not a boundary between the first and second surface and the second surface having a further coating, wherein the further coating a or both of the following coatings is: - one Low emissivity coating - one Solar control coating A conductive coating - one IR-reflective coating Semitransparentes Substrat nach Anspruch 15, dadurch gekennzeichnet, dass das erste Substrat mindestens eine Grenze aufweist, beispielsweise die Grenze bei einem Verbundglas und dass die Grenze eine weitere Beschichtung aufweist, wobei die Beschichtung eine oder beide der nachfolgenden Beschichtungen ist: – eine Beschichtung mit niedriger Emittivität – eine Sonnenschutzschicht – eine leitfähige Beschichtung – eine IR-reflektierende BeschichtungSemitransparent substrate according to claim 15, characterized characterized in that the first substrate has at least one boundary, for example, the limit for a laminated glass and that the limit is one further coating, wherein the coating one or both of the following coatings are: - one Low emissivity coating - one Solar control coating A conductive coating - one IR-reflective coating Semitransparentes Element nach einem der Ansprüche 15 bis 19, dadurch gekennzeichnet, dass die zweite Fläche (2) des ersten Substrates eine weitere Beschichtung aufweist.Semitransparent element according to one of claims 15 to 19, characterized in that the second surface ( 2 ) of the first substrate has a further coating. Semitransparentes Element nach Anspruch 20, dadurch gekennzeichnet, dass die weitere Beschichtung eine der nachfolgenden Schichten ist: – eine Beschichtung niedriger Emittivität (niedrig ε-Schicht); – eine Sonnenschutzschicht – eine leitfähige Beschichtung – eine IR-reflektierende BeschichtungSemitransparent element according to claim 20, characterized marked that the further coating one of the subsequent layers is: A low emissivity coating (low ε-layer); - a sunscreen - one conductive coating - an IR-reflective coating Semitransparentes Element nach einem der Ansprüche 1 bis 21, dadurch gekennzeichnet, dass das erste und/oder das zweite Substrat eines der nachfolgenden Substrate ist: ein Einscheibenglas; ein Einscheibensicherheitsglas (ESG); ein teilvorgespanntes Einscheibenglas (TESG); ein Verbundglas ein Verbundsicherheitsglas (VSG); ein Verbundsicherheitsglas (VSG), umfassend ein Einscheibensicherheitsglas (ESG); ein Verbundsicherheitsglas (VSG), umfassend ein teilvorgespanntes Glas (TSG).Semitransparent element according to one of the claims 1 to 21, characterized in that the first and / or the second substrate of one of the following substrates is: one toughened; a toughened safety glass (ESG); one semi-tempered single-pane glass (TESG); a laminated glass one Laminated safety glass (VSG); a laminated safety glass (VSG), comprising a toughened safety glass (ESG); a laminated safety glass (VSG), comprising a semi-tempered glass (TSG). Semitransparentes Element nach einem der Ansprüche 1 bis 22, dadurch gekennzeichnet, dass das erste und/oder das zweite Scheibenelement eine flache Scheibe ist.Semitransparent element according to one of the claims 1 to 22, characterized in that the first and / or the second Disc element is a flat disc. Semitransparentes Element nach einem der Ansprüche 1 bis 23, dadurch gekennzeichnet, dass das erste und/oder das zweite Scheibenelement eine gebogene Scheibe ist.Semitransparent element according to one of the claims 1 to 23, characterized in that the first and / or the second Disc element is a curved disc. Semitransparentes Element nach einem der Ansprüche 1 bis 24, dadurch gekennzeichnet, dass die Verbindungseinrichtung ein Metallabstandsstück und eine Versiegelung umfasst.Semitransparent element according to one of the claims 1 to 24, characterized in that the connecting device a metal spacer and a seal. Semitransparentes Element nach einem der Ansprüche 1 bis 25, dadurch gekennzeichnet, dass die Beschichtung und/oder die weitere Beschichtung eine durch Sputtern aufgebrachte Schicht ist.Semitransparent element according to one of the claims 1 to 25, characterized in that the coating and / or the further coating is a sputtered layer is. Semitransparentes Element nach einem der Ansprüche 1 bis 25, dadurch gekennzeichnet, dass die Beschichtung und/oder die weitere Beschichtung eine Tauchschicht ist.Semitransparent element according to one of the claims 1 to 25, characterized in that the coating and / or the further coating is a dip layer. Semitransparente Beschichtung nach einem der Ansprüche 1 bis 25, dadurch gekennzeichnet, dass die Beschichtung und/oder die weitere Beschichtung eine durch Sprühen aufgebrachte Schicht ist.Semi-transparent coating according to one of the claims 1 to 25, characterized in that the coating and / or the further coating applied by spraying Layer is. Semitransparentes Element gemäß einem der Ansprüche 1 bis 28, dadurch gekennzeichnet, dass die Leuchtmittel anorganische Leuchtdioden umfassen.Semitransparent element according to one of Claims 1 to 28, characterized in that the lighting means inorganic light emitting diodes include. Semitransparentes Element nach einem der Ansprüche 1 bis 29, dadurch gekennzeichnet, dass die Leuchtmittel organische Leuchtdioden umfassen.Semitransparent element according to one of claims 1 to 29, characterized in that the bulbs comprise organic light-emitting diodes. Semitransparentes Element nach einem der Ansprüche 22 bis 30, dadurch gekennzeichnet, dass das Verbundglas und/oder das Verbundsicherheitsglas eine Folie umfasst.Semitransparent element according to one of the claims 22 to 30, characterized in that the laminated glass and / or the laminated safety glass comprises a film. Semitransparentes Element nach Anspruch 31, dadurch gekennzeichnet, dass die Folie eine Funktionsfolie ist.Semitransparent element according to claim 31, characterized characterized in that the film is a functional film. Semitransparentes Element nach Anspruch 32, dadurch gekennzeichnet, dass die Funktionsfolie eine der nachfolgenden Funktionsfolien ist. – eine Folie umfassend Leuchtmittel – eine Folie umfassend eine schaltbare Substanz, insbesondere einen Flüssigkristall oder eine elektrochrome Substanz – eine Folie umfassend Streuzentren.Semitransparent element according to claim 32, characterized marked that the functional film one of the following Functional films is. A foil comprising bulbs - one Film comprising a switchable substance, in particular a liquid crystal or an electrochromic substance - comprising a film Scattering centers. Semitransparentes Element, insbesondere Fassadenelement, umfassend wenigstens ein erstes scheibenförmiges Element; wenigstens ein zweites scheibenförmiges Element; wenigstens eine Verbundeinrichtung zum Verbinden von erstem und zweitem scheibenförmigem Element mit einem Abstand zueinander, dadurch gekennzeichnet, dass, das erste und/oder das zweite scheibenförmige Element wenigstens teilweise eine Beschichtung aufweist, wobei die Beschichtung für einen Betrachter zu einem Farbeffekt im sichtbaren Wellenlängenbereich führt und die die Absorption der Beschichtung im sichtbaren Wellenlängenbereich < 5%, insbesondere < 3%, bevorzugt < 2%, ganz bevorzugt < 1% des auf die Beschichtung einfallenden Lichtes ist und das erste und/oder das zweite Substrat eines der nachfolgenden Substrate ein Verbundglas oder ein Verbundsicherheitsglas (VSG) ist und das Verbundglas und/oder das Verbundsicherheitsglas eine Funktionsfolie umfasst, wobei die Funktionsfolie eine der nachfolgenden Funktionsfolien ist: – eine Folie umfassend Leuchtmittel – eine Folie umfassend eine schaltbare Substanz, insbesondere einen Flüssigkristall oder eine elektrochrome Substanz – eine Folie umfassend Streuzentren.Semitransparent element, in particular facade element, full at least one first disc-shaped element; at least a second disc-shaped member; at least one Composite device for connecting the first and second disk-shaped Element with a distance to each other, characterized, that, the first and / or the second disk-shaped Element has at least partially a coating, wherein the Coating for a viewer to a color effect in the visible wavelength range leads and which the Absorption of the coating in the visible wavelength range <5%, in particular <3%, preferably <2%, more preferably <1% of the on Coating incident light is and the first and / or the second substrate of one of the following substrates a laminated glass or a laminated safety glass (VSG) and the laminated glass and / or the laminated safety glass comprises a functional film, wherein the Functional foil is one of the following functional foils: - one Foil comprising bulbs - comprising a film a switchable substance, in particular a liquid crystal or an electrochromic substance - comprising a film Scattering centers. Verwendung des semitransparenten Elementes nach einem der Ansprüche 1 bis 34 im Bereich: – Fassaden, Außenfassaden, insbesondere Außenfassaden in denen Wärmedämmung notwendig ist – Schaufenster für den Außenbereich, insbesondere Schaufenster mit Wärmedämmung – dekorative AußenfassadenUse of the semitransparent element according to one of claims 1 to 34 in the range: - facades, Exterior facades, in particular exterior facades in which Thermal insulation is necessary - Store window for outdoor use, especially shop windows with thermal insulation - decorative exterior facades
DE102008009774A 2007-09-06 2008-02-19 Element i.e. disk, for use in e.g. clinic, has film operated in two states, and laminated glass elements including surface, where glass elements provide protection against ionizing radiation and ultra-violet radiation Withdrawn DE102008009774A1 (en)