DE10139699C2 - Non-grain oriented electrical sheet or strip and process for its manufacture - Google Patents
Non-grain oriented electrical sheet or strip and process for its manufactureInfo
- Publication number
- DE10139699C2 DE10139699C2 DE10139699A DE10139699A DE10139699C2 DE 10139699 C2 DE10139699 C2 DE 10139699C2 DE 10139699 A DE10139699 A DE 10139699A DE 10139699 A DE10139699 A DE 10139699A DE 10139699 C2 DE10139699 C2 DE 10139699C2
- Authority
- DE
- Germany
- Prior art keywords
- strip
- temperature
- magnetic
- sheet
- hot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
Die Erfindung betrifft ein nichtkornorientiertes Elektroblech oder -band und ein Verfahren zu seiner Herstellung. Unter dem Begriff "nichtkornorientiertes Elektroblech" wird in diesem Zusammenhang ein Stahlblech oder ein Stahlblechband verstanden, welches unabhängig von seiner Textur unter die in DIN 46 400 Teil 1 oder 4 genannten Bleche fällt, deren Verlustanisotropie die in DIN 46 400 Teil 1 festgelegten Höchstwerte nicht überschreitet. Insoweit werden hier die Begriffe "Elektroblech" und "Elektroband" synonym verwendet.The invention relates to a non-grain oriented Electrical sheet or strip and a process for its Production. Under the term "non-grain oriented In this context, electrical sheet "becomes steel sheet or understood a sheet steel strip, which is independent of its texture under that in DIN 46 400 part 1 or 4 mentioned sheets falls, the loss anisotropy of which in Maximum values specified in DIN 46 400 Part 1 exceeds. To that extent, the terms here "Electrical sheet" and "electrical steel" used interchangeably.
"B25" bezeichnet im folgenden die magnetische Polarisation bei einer magnetischen Feldstärke "H" von 2500 A/m. Unter "P1,5" wird der Ummagnetisierungsverlust bei einer Polarisation von 1,5 T und einer Frequenz von 50 Hz verstanden. "µ1,5" steht für den aus dem Quotienten B/H gebildeten Wert der magnetischen Permeablität bei einer magnetischen Polarisation "B" von 1,5 T."B 25 " hereinafter denotes the magnetic polarization at a magnetic field strength "H" of 2500 A / m. "P 1.5 " is understood to mean the loss of magnetization at a polarization of 1.5 T and a frequency of 50 Hz. "µ 1.5 " stands for the value of the magnetic permeability formed from the quotient B / H with a magnetic polarization "B" of 1.5 T.
Von der verarbeitenden Industrie wird die Forderung nach nichtkornorietierten Elektroblechen gestellt, deren magnetische Polarisationswerte gegenüber herkömmlichen Blechen angehoben sind und bei denen niedrige Verlustwerte realisiert werden. The manufacturing industry is calling for non-grain-oriented electrical sheets, whose magnetic polarization values compared to conventional ones Sheets are raised and those are low Loss values can be realized.
Durch die Erhöhung der magnetischen Polarisation wird der Magnetisierungsbedarf reduziert. In allen Anwendungsfällen, in denen der Aufbau des magnetischen Feldes auf Basis einer elektrischen Erregung erfolgt, lassen sich auf diese Weise gleichzeitig auch die Kupferverluste senken. Eine Absenkung der Werte der magnetischen Verluste ist daher stets vorteilhaft, um die Gesamtverluste abzusenken. Im Ergebnis läßt sich so der Wirkungsgrad von elektrischen Maschinen verbessern.By increasing the magnetic polarization, the Magnetization requirement reduced. In all Use cases where the structure of the magnetic Field is based on electrical excitation, can also be used in this way Reduce copper losses. A decrease in the values of the magnetic losses is therefore always advantageous to the Lower overall losses. As a result, the Improve the efficiency of electrical machines.
In gleicher Weise ist auch für eine Vielzahl von Anwendungen, bei denen der Aufbau unter Verwendung von Elektroband durch Permanentmagnete erfolgt, eine Absenkung der magnetischen Verluste ein wesentlicher Bestandteil. Niedrige magnetische Verluste ermöglichen auch bei solchen Anwendungen, bei optimierter Werkstoffauswahl den Wirkungsgrad der jeweiligen Maschine zu erhöhen.The same is true for a variety of Applications where the construction using Electrical steel is made by permanent magnets, one Lowering the magnetic losses an essential Component. Allow low magnetic losses even with such applications, with optimized Material selection the efficiency of the respective machine to increase.
Für die Erzeugung von Elektroband werden regelmäßig FeSi- Basislegierungen mit Si-Gehalten von bis zu 3,5 Gew-% und Zusätzen an Al, Mn, Sb, Sn und anderen Bestandteilen verwendet. Der Kohlenstoffgehalt und die Gehalte an Begleitelementen S, Ti, N und O sollten dabei möglichst gering sein.For the production of electrical steel, FeSi- Base alloys with Si contents of up to 3.5% by weight and Additions to Al, Mn, Sb, Sn and other components used. The carbon content and the levels Accompanying elements S, Ti, N and O should be possible be small.
FeSi-Stähle lassen sich nach ihrem Verhalten bei Abkühlung in umwandelnde und nicht umwandelnde Legierungen einteilen. Kennzeichnend für umwandelnde Legierungen ist dabei, daß diese derart beschaffenen Stähle bei ihrer Abkühlung aus der Gießhitze Phasenumwandlungen durchlaufen. So weisen derartige Stähle mit abnehmender Temperatur zunächst ein austenitisches Gebiet (γ-Gebiet), anschließend ein Mischgebiet aus Austenit und Ferrit (γ/α-Mischgebiet) und abschließend ein ferritisches Gebiet (α-Gebiet) auf. Die Temperatur, bei der die erste Phasenumwandlung (γ in γ/α) bei Abkühlung stattfindet, bezeichnet man als Ar3- Temperatur. Die Temperatur, bei der (ebenfalls bei Abkühlung) der Übergang von γ/α zu α stattfindet, wird als Ar1-Temperatur bezeichnet. Nicht umwandelnde Legierungen weisen in keinem Temperaturbereich ein reines Austenitgebiet auf.FeSi steels can be classified into converting and non-converting alloys according to their behavior when cooled. It is characteristic of converting alloys that these steels, which are made in this way, undergo phase transformations as they cool down from the casting heat. Steels of this type, with decreasing temperature, first have an austenitic region (γ region), then a mixed region composed of austenite and ferrite (γ / α mixed region) and finally a ferritic region (α region). The temperature at which the first phase change (γ to γ / α) takes place on cooling is called the A r3 temperature. The temperature in the α (also on cooling) the transition from γ / takes place at α, is referred to as A r1 temperature. Non-converting alloys do not have a pure austenite area in any temperature range.
Bisher wurden in der Praxis für Elektrobleche, die Werte des Ummagnetisierungsverlustes von weniger als 4,7 W/kg aufweisen sollen, stets solche nicht umwandelnden Legierungen eingesetzt. Diese Legierungen weisen den Vorteil auf, daß aufgrund ihrer hohen Si- und/oder Al- sowie Mn-Gehalte eine Erhöhung des spezifischen elektrischen Widerstands eintritt, welcher eine Absenkung der magnetischen Verlustwerte ermöglicht. Nachteilig ist jedoch, daß diese Legierungselemente den Wert der Sättigungsmagnetisierung JS merklich absenken.Up to now, such non-converting alloys have always been used in practice for electrical sheets which are said to have values of the magnetic loss of less than 4.7 W / kg. These alloys have the advantage that, due to their high Si and / or Al and Mn contents, there is an increase in the specific electrical resistance, which enables the magnetic loss values to be reduced. However, it is disadvantageous that these alloying elements markedly lower the value of the saturation magnetization J S.
Sowohl für umwandelnde als auch für nicht umwandelnde Legierungen sind Maßnahmen bekannt, die die Werte der Sättigungsmagnetisierung steigern, wie z. B. Warmbandglühung, zweistufiges Kaltwalzen oder gezielte Phasensteuerung in der Fertigstaffel. In all diesen Fällen ist jedoch eine strenge Einhaltung der notwendigen Arbeitsschritte und Verfahrensparameter erforderlich, die diese Verfahren in der Praxis schwer handhabbar machen.For both converting and non-converting Alloys are known to measure the values of the Increase saturation magnetization, such as. B. Hot strip annealing, two-stage cold rolling or targeted Phase control in the finished series. In all of these However, strict compliance is necessary Steps and process parameters required that make these procedures difficult to use in practice.
Die Aufgabe der Erfindung besteht darin, ein Elektroblech- und -band zur Verfügung zu stellen, das zugleich geringe Ummagnetisierungsverluste und eine gute Sättigungsmagnetisierung, die sich in einer hohen Permeabilität µ (bei Wechselstrom) ausdrückt, aufweist und die keine Einhaltung derartiger strenger Verfahrensvorschriften erfordert.The object of the invention is a To provide electrical sheet and strip that at the same time low magnetic loss and a good one Saturation magnetization, which is in a high Expresses permeability µ (with alternating current) and who don't comply with such strict Procedural requirements required.
In Bezug auf das Produkt wird diese Aufgabe erfindungsgemäß durch ein nichtkornorientiertes Elektroblech oder -band gelöst, welches aus einer Stahlschmelze mit (in Gew.-%) Si: ≦ 1,8%, Al: < 1%, C: ≦ 0,0200%, Mn: < 0,5%, Sn: ≦ 0,03%, Sb: ≦ 0,1%, P: ≦ 0,1%, S: < 0,02%, Ti: ≦ 0,0100%, N: ≦ 0,0100%, O: ≦ 0,0100%, B: ≦ 0,0100% und als Rest Eisen und unvermeidbare Verunreinigungen gewonnen ist, wobei die Stahlschmelze zu Dünnbrammen oder gegossenem Band vergossen worden ist, die in einem kontinuierlich aufeinanderfolgenden Ablauf jeweils zu Warmband warmgewalzt worden ist, wobei das Elektroblech oder -band im Zuge einer von einer mindestens 1150°C betragenden Temperatur ausgehenden Abkühlung zunächst ein austenitisches Gefüge, dann ein aus Austenit und Ferrit bestehendes Mischgefüge und nach Erreichen einer unter 1050°C liegenden Temperatur schließlich ein ferritisches Gefüge aufweist und wobei das Elektroblech oder -band bei einer Polarisation von 1,5 T und einer Frequenz von 50 Hz einen unter 4,7 W/kg liegenden Ummagnetiserungsverlust P1,5, bei einer magnetischen Feldstärke von 2500 A/m eine mindestens 1,60 T betragenden magnetischen Polarisation B25 und bei einer Frequenz von 50 Hz eine magnetischen Permeabilität µ1,5 von mindestens 1500 besitzt. Überraschend hat sich gezeigt, daß erfindungsgemäß beschaffenes Elektroblech trotz des Umstandes, daß der zu seiner Herstellung genutzte Stahl bei seiner Abkühlung mehrfach eine Phasenumwandlung erfährt, geringe magnetische Verluste bei gleichzeitig hervorragenden sonstigen Eigenschaften aufweist. Dabei können diese Eigenschaften unabhängig von besonderen Prozeßparametern auf konventionelle Weise erreicht werden, solange die Legierungszusammensetzung und das Umwandlungsverhalten des verarbeiteten Stahles berücksichtigt werden. Somit steht mit der Erfindung ein hochwertiges, vielseitig verwendbares und den in der Praxis sich stellenden Anforderungen ohne weiteres gerecht werdendes Elektroblech zur Verfügung, daß sich ohne besonderen Aufwand kostengünstig erzeugen läßt.With regard to the product, this object is achieved according to the invention by a non-grain-oriented electrical sheet or strip, which consists of a molten steel with (in% by weight) Si: ≦ 1.8%, Al: <1%, C: 200 0.0200 %, Mn: <0.5%, Sn: ≦ 0.03%, Sb: ≦ 0.1%, P: ≦ 0.1%, S: <0.02%, Ti: ≦ 0.0100%, N: ≦ 0.0100%, O: ≦ 0.0100%, B: ≦ 0.0100% and the rest iron and unavoidable impurities are obtained, the molten steel being cast into thin slabs or cast strip, which is carried out in a continuously successive manner The process has been hot-rolled into hot strip, with the electrical sheet or strip initially cooling in a temperature of at least 1150 ° C, an austenitic structure, then an austenite and ferrite mixed structure and after reaching a temperature below 1050 ° C finally has a ferritic structure and the electrical sheet or strip having a polarization of 1.5 T and a he frequency of 50 Hz has a magnetic loss P 1.5 below 4.7 W / kg, at a magnetic field strength of 2500 A / m a magnetic polarization B 25 of at least 1.60 T and at a frequency of 50 Hz a magnetic permeability µ 1.5 of at least 1500. Surprisingly, it has been found that, despite the fact that the steel used for its manufacture undergoes a phase change several times when it cools, electrical sheet according to the invention has low magnetic losses with outstanding other properties at the same time. These properties can be achieved in a conventional manner, regardless of special process parameters, as long as the alloy composition and the transformation behavior of the processed steel are taken into account. Thus, the invention provides a high-quality, versatile electrical sheet that easily meets the practical requirements, which can be produced inexpensively without any special effort.
Praktische Versuche haben ergeben, daß erfindungsgemäße Elektrobleche sicher Ummagnetisierungsverluste P1,5 von weniger als 4,5 W/kg erreichen, wobei gleichzeitig die magnetische Polarisation B25 mindestens 1,60 T und ihre magnetische Permeabilität µ1,5 mindestens 2000 betragen kann. Eine magnetische Polarisation von < 1,7 T aufweisende erfindungsgemäße Bleche gehören zur Klasse der Elektrobleche mit mittlerer Permeabilität.Practical tests have shown that electrical sheets according to the invention reliably achieve magnetic reversal losses P 1.5 of less than 4.5 W / kg, at the same time the magnetic polarization B 25 being at least 1.60 T and their magnetic permeability μ 1.5 being at least 2000. Metal sheets according to the invention having a magnetic polarization of <1.7 T belong to the class of electrical sheets with medium permeability.
Im Rahmen der erfindungsgemäß vorgegebenen Zusammensetzung der für die Erzeugung verwendeten Schmelze lassen sich Elektroblechgüten erzeugen, die der Gruppe der Elektrobleche mit mittlerem Silizium-Gehalt zugeordnet sind. Dazu werden die Gehalte der Legierungselemente der Stahlschmelze wie folgt bemessen (in Gew.-%): C: ≦ 0,0200, Si: 0,9-1,4%, Al: 0,1-0,5%, mit Si + Al < 1,8%, Mn: ≦ 0,25%, P: ≦ 0,08%, S: ≦ 0,015%, Ti: ≦ 0,0100%, N: ≦ 0,0100%, O ≦ 0,0100%, B: ≦ 0,0100%. Within the scope of the specified according to the invention Composition of the used for the production Electrical steel grades can be produced by the melt Group of electrical sheets with medium silicon content assigned. The contents of the Alloy elements of the molten steel are dimensioned as follows (in% by weight): C: ≦ 0.0200, Si: 0.9-1.4%, Al: 0.1-0.5%, with Si + Al <1.8%, Mn: ≦ 0.25%, P: ≦ 0.08%, S: ≦ 0.015%, Ti: ≦ 0.0100%, N: ≦ 0.0100%, O ≦ 0.0100%, B: ≦ 0.0100%.
Ebenso ist es möglich, erfindungsgemäßes Elektroblech aus niedrige Mengen an Silizium enthaltenden Stählen zu erzeugen. In diesem Fall ist es günstig, wenn die Gehalte der Legierungselemente der Stahlschmelze in folgender Weise aufeinander abgestimmt sind (in Gew.-%): : C: ≦ 0,0200%, Si: 0,15-0,65%, Al: < 0,5%, Mn: ≦ 0,25%, S: ≦ 0,010%, P: ≦ 0,08%, Ti: ≦ 0,0100%, N: ≦ 0,0100%, O ≦ 0,0100%, B: ≦ 0,0100%.It is also possible to use electrical sheet according to the invention low amounts of steels containing silicon produce. In this case, it is beneficial if the levels of the alloying elements of the molten steel in the following Are matched to one another (in% by weight):: C: ≦ 0.0200%, Si: 0.15-0.65%, Al: <0.5%, Mn: ≦ 0.25%, S: ≦ 0.010%, P: ≦ 0.08%, Ti: ≦ 0.0100%, N: ≦ 0.0100%, O ≦ 0.0100%, B: ≦ 0.0100%.
Erfindungsgemäßes Elektroblech läßt sich bevorzugt aus zu Dünnbrammenmaterial vergossenem Stahl oder unter Nutzung einer Gießmaschine erzeugen, bei der das Gießen und Warmwalzen "inline" in einem Schritt erfolgt. Dementsprechend sieht die Erfindung bei der Herstellung von Elektroblech, das im Zuge einer von einer mindestens 1150°C betragenden Temperatur ausgehenden Abkühlung der Dünnbramme bzw. des gegossenen Bandes zunächst ein austenitisches Gefüge, dann ein aus Austenit und Ferrit bestehendes Mischgefüge und nach Erreichen einer unter 1050°C liegenden Temperatur schließlich ein ferritisches Gefüge aufweist und im Fertigband bei einer Polarisation von 1,5 T und einer Frequenz von 50 Hz einen unter 4,7 W/kg liegenden Ummagnetiserungsverlust P1,5, bei einer magnetischen Feldstärke von 2500 A/m eine mindestens 1,60 T betragenden magnetischen Polarisation B25 und bei einer Frequenz von 50 Hz eine magnetische Permeabilität µ1,5 von mindestens 1500 besitzt, vor, in kontinuierlich aufeinander folgenden Arbeitsgängen aus einer aus einer Stahlschmelze folgender Zusammensetzung (in Gew.-%): Si: ≦ 1,8%, Al: < 1%, C: ≦ 0,0200%, Mn: < 0,5%, Sn: ≦ 0,03 %, Sb: ≦ 0,1%, P: ≦ 0,1%, S: < 0,02%, Ti: ≦ 0,0100%, N: ≦ 0,0100%, O: ≦ 0,0100%, B: ≦ 0,0100% und als Rest Eisen und unvermeidbare Verunreinigungen, eine Dünnbramme oder ein Band zu gießen, zu einem Warmband mit einer Warmbanddicke von 1,70 bis 3,2 mm warmzuwalzen, anschließend das Warmband zu beizen, dann das Warmband zu einem Kaltband mit einer Enddicke von weniger als 0,6 mm kaltzuwalzen und schließlich das Kaltband bei einer unterhalb der Ac1-Temperatur liegenden Temperatur zu glühen.Electrical sheet according to the invention can preferably be produced from steel cast into thin slab material or using a casting machine in which the casting and hot rolling are carried out “inline” in one step. Accordingly, in the production of electrical sheet, the invention first sees an austenitic structure, then a mixed structure consisting of austenite and ferrite, and after reaching a temperature below 1050 in the course of a cooling of the thin slab or the cast strip starting from a temperature of at least 1150 ° C ° C finally has a ferritic structure and in the finished strip with a polarization of 1.5 T and a frequency of 50 Hz a magnetic loss P 1.5 below 4.7 W / kg, with a magnetic field strength of 2500 A / m has a magnetic polarization B 25 of at least 1.60 T and a magnetic permeability µ 1.5 of at least 1500 at a frequency of 50 Hz, before, in continuously successive operations from a composition of a steel melt with the following composition (in% by weight ): Si: ≦ 1.8%, Al: <1%, C: ≦ 0.0200%, Mn: <0.5%, Sn: ≦ 0.03%, Sb: ≦ 0.1%, P: ≦ 0.1%, p : <0.02%, Ti: ≦ 0.0100%, N: ≦ 0.0100%, O: ≦ 0.0100%, B: ≦ 0.0100% and the balance iron and unavoidable impurities, a thin slab or a Casting strip, hot rolling to a hot strip with a thickness of 1.70 to 3.2 mm, then pickling the hot strip, then cold rolling to a cold strip with a final thickness of less than 0.6 mm and finally the cold strip at one to glow below the A c1 temperature.
Die Erfindung ermöglicht somit, bei Anwendung an sich bekannter Verfahrensschritte auf überraschend einfache Weise ein für die praktische Anwendung hervorragend geeignetes Elektroblech zu erzeugen, dessen Eigenschaften auch den gesteigerten Anforderungen der Verwender solcher Bleche stets gewachsen sind.The invention thus enables, when used per se known process steps to surprisingly simple Assign an excellent for practical use to produce suitable electrical sheet, its properties also the increased demands of users of such Sheets have always grown.
Vorzugsweise wird während des Warmwalzens mindestens bei einem der letzten Umformstiche mit Schmierung gewalzt. Durch das Warmwalzen mit Schmierung treten einerseits geringere Scherverformungen auf, so daß das gewalzte Band im Ergebnis eine homogenere Struktur über den Querschnitt erhält. Andererseits werden durch die Schmierung die Walzkräfte vermindert, so daß über den jeweiligen Walzstich eine höhere Dickenabnahme möglich ist. Daher kann es, je nach den gewünschten Eigenschaften des zu erzeugenden Elektroblechs, vorteilhaft sein, wenn sämtliche Umformstiche mit einer Walzschmierung durchgeführt werden.Preferably at least during the hot rolling one of the last forming stitches rolled with lubrication. Hot rolling with lubrication occurs on the one hand less shear deformation so that the rolled strip the result is a more homogeneous structure across the cross-section receives. On the other hand, the lubrication Rolling forces reduced, so that over the respective Roll pass a higher thickness reduction is possible. Therefore It can, depending on the desired properties of the producing electrical sheet, may be advantageous if all forming stitches with roll lubrication be performed.
Grundsätzlich eignet sich für die Durchführung des erfindungsgemäßen Verfahrens eine Haspeltemperatur von mindestens 720°C. Bei Einhaltung dieser Haspeltemperatur kann eine Warmbandglühung ganz oder zumindest zum wesentlichen Teil eingespart werden. Das Warmband wird schon im Coil entfestigt, wobei die seine Eigenschaften bestimmenden Merkmale, wie Korngröße, Textur und Ausscheidungen, positiv beeinflußt werden.Basically, is suitable for carrying out the inventive method a reel temperature of at least 720 ° C. If this reel temperature is maintained can hot strip annealing completely or at least for essential part can be saved. The hot strip is already softened in the coil, taking its properties defining characteristics such as grain size, texture and Excretions, positively influenced.
Gemäß einer insbesondere für die Verarbeitung eines Stahls nach einem der Ansprüche 1 bis 5 besonders geeigneten Ausgestaltung der Erfindung wird das Warmband in der Warmwalzstraße mit einer mindestens 820°C betragenden Warmwalzendtemperatur gewalzt und bei einer weniger als 650°C betragenden Haspeltemperatur gehaspelt. Das Warmwalzen und Haspeln bei diesen Temperaturen führt bei den betreffenden Legierungen zu einem verfestigten Warmbandzustand.According to one especially for processing a Steel according to one of claims 1 to 5 in particular A suitable embodiment of the invention is the hot strip in the hot rolling mill with a temperature of at least 820 ° C amount hot rolled end temperature and at a less than 650 ° C reel temperature coiled. Hot rolling and coiling on these Temperatures lead to with the relevant alloys a solidified hot strip condition.
Die abschließende Glühung des kaltgewalzten Elektrobleches erfolgt vorzugsweise in einer mindestens teilweise entkohlenden Atmosphäre.The final annealing of the cold rolled Electrical sheet is preferably made in at least one partially decarburizing atmosphere.
Die Bedingungen beim Warmwalzen lassen sich dann eindeutig vorausbestimmen und entsprechend leicht steuern, wenn das Elektroband oder -blech beim Warmwalzen ein rein ferritisches Gefüge aufweist.The conditions during hot rolling can then be clearly predetermine and correspondingly easy control if the electrical steel or sheet during hot rolling has a purely ferritic structure.
Nachfolgend wird die Erfindung anhand von Ausführungsbeispielen näher erläutert.The invention is described below with reference to Embodiments explained in more detail.
Diag. 1 zeigt schematisch die Phasen von FeSiAl- Legierungen. Diag. 1 schematically shows the phases of FeSiAl alloys.
In Tabelle 1 sind die Zusammensetzungen von Stählen E1 bis E6 und V1 bis V2 angegeben.Table 1 shows the compositions of steels E1 to E6 and V1 to V2 specified.
Bei den Stählen E1 bis E6 handelt es sich um erfindungsgemäße Stähle, während die Stähle V1 und V2 zum Vergleich angegeben worden sind.Steels E1 to E6 are Steels according to the invention, while steels V1 and V2 for Comparison have been given.
Erfindungsgemäße Stähle durchlaufen nach dem Vergießen eine zweifache Phasenumwandlung. Sie gehören als solche in die Gruppe von Stählen, deren Umwandlungsverhalten durch die links der Linie X-X von Diag. 1 in Abhängigkeit von der Temperaturentwicklung dargestellt ist. Im vorliegenden Beispiel liegt die Linie X-X bei einem ca. 1,8 Gew.-% liegenden Wert, der aus dem Si-Gehalt und dem Doppelten des Al-Gehaltes gebildeten Summe (Si + 2Al ≈ 1,8 Gew.-%).Steels according to the invention undergo a double phase change after casting. As such, they belong to the group of steels whose transformation behavior is indicated by the left of line XX from Diag. 1 is shown depending on the temperature development. In the present example, the line XX is approximately 1.8% by weight, the sum formed from the Si content and twice the Al content (Si + 2Al ≈ 1.8% by weight).
Demnach weisen erfindungsgemäße Stähle bei Temperaturen von mehr als 1200°C und einer entsprechenden, aus ihrem Si-Gehalt und ihrem verdoppelten Al-Gehalt gebildeten Summe eine ferritische Phasenstruktur (α-Gebiet) auf. Die Grenze zwischen diesem α-Gebiet und dem α/γ-Mischgebiet, in dem der Stahl abhängig von seiner Temperatur und seinen Si- und Al-Gehalten eine aus Ferrit und Austenit gebildete Mischphasenstruktur aufweist, ist in Diag. 1 durch die Grenzlinie A gekennzeichnet. Das α/γ-Mischgebiet ist gleichzeitig durch eine Grenzlinie B gegenüber dem γ- Gebiet abgegrenzt, in dem sich eine rein austenitische Phasenstruktur des Stahls ergibt. Dieses γ-Gebiet ist an seinen dem α-Gebiet zugewandten Rändern vollständig vom α/γ-Mischgebiet umgeben.Accordingly, steels according to the invention have a ferritic phase structure (α region) at temperatures of more than 1200 ° C. and a corresponding sum formed from their Si content and their doubled Al content. The boundary between this α region and the α / γ mixing region, in which the steel has a mixed phase structure formed from ferrite and austenite depending on its temperature and its Si and Al contents, is in Diag. 1 marked by the boundary line A. The α / γ mixing area is at the same time delimited by a boundary line B from the γ area, in which there is a purely austenitic phase structure of the steel. This γ region is completely surrounded by the α / γ mixed region at its edges facing the α region.
Die Grenzlinien A, B verlaufen dabei mit ihren oberen Abschnitten A', B' ausgehend von den niedrigsten Si- und Al-Gehalten und einer Temperatur von ca. 1390°C mit abnehmender Temperatur parabelförmig in das Gebiet zunehmender Si- und Al-Gehalte, bis bei einer maximalen, für die Linie A durch die Linie X-X dargestellten Summe aus Si- und Al-Gehalten der Umkehrpunkt der Parabel erreicht ist. Da der Umkehrpunkt der Linie B bei niedrigeren Si-/Al-Gehalten liegt, ist zwischen den Linien A, B das α/γ-Mischgebiet eingeschlossen. Von ihren Umkehrpunkten aus läuft der jeweils untere Abschnitt A'', B'' der Grenzlinien A, B mit abnehmender Temperatur zurück zu niedrigen Si- und Al-Gehalten, bis sich die Linien A, B bei einer Temperatur von ca. 920°C bei den niedrigsten Si-, Al-Gehalten wieder treffen.The boundary lines A, B run with their upper ones Sections A ', B' starting from the lowest Si and Al content and a temperature of approx. 1390 ° C with decreasing temperature parabolic in the area increasing Si and Al contents up to a maximum, for line A sum represented by line X-X the reversal point of the parabola from Si and Al contents is reached. Since the reversal point of line B at lower Si / Al contents is between the Lines A, B included the α / γ mixing area. From theirs The lower section runs from reversal points A '', B '' of the boundary lines A, B with decreasing temperature back to low Si and Al contents until the Lines A, B at a temperature of approx. 920 ° C at the meet the lowest Si, Al contents again.
Erfindungsgemäßer Stahl mit gegebenen Si- und Al-Gehalten weist dementsprechend im Verlauf seiner Abkühlung von der Gießtemperatur eine rein austenitische Phasenstruktur auf. Dieses Gebiet wird bei einer Umwandlungstemperatur Ar3 verlassen, wenn die Temperatur des Stahls unter den durch den unteren Abschnitt B'' der Grenzlinie B gekennzeichnete Temperatur sinkt. Mit Unterschreiten der Temperatur Ar3 bildet sich ferritisches Gefüge in dem Stahl, so daß in diesem Zustand wieder ein α/γ-Mischgefüge vorliegt.Steel according to the invention with given Si and Al contents accordingly has a purely austenitic phase structure in the course of its cooling from the casting temperature. This area is left at a transition temperature A r3 when the temperature of the steel falls below the temperature indicated by the lower section B '' of the boundary line B. When the temperature falls below the temperature A r3 , a ferritic structure is formed in the steel, so that an α / γ mixed structure is again present in this state.
Bei weiterer Abkühlung des Stahls wird dann der untere Abschnitt A'' der Grenzlinie A bei einer Umwandlungstemperatur Ar1 unterschritten. Mit Erreichen der Abkühltemperatur Ar3 liegt wieder ein rein ferritisches Gefüge vor. Ein typischer Umwandlungsverlauf ist durch die Linie U im Diag. 1 dargestellt.When the steel is cooled further, the lower section A ″ of the limit line A is undershot at a transition temperature A r1 . When the cooling temperature A r3 is reached, there is again a purely ferritic structure. A typical conversion process is through line U in the diag. 1 shown.
Die entsprechend Tabelle 1 zusammengesetzten Schmelzen sind in kontinuierlich aufeinander folgenden Vorgängen zu Dünnbrammen vergossen worden, die "inline" in eine Warmwalzstraße gefördert und dort bei Warmwalzendtemperaturen ET zu jeweils einem Warmband mit einer Warmbandenddicke dW gewalzt worden sind. Die die Warmwalzstraße verlassenden Warmbänder sind dann bei einer Haspeltemperatur HT gehaspelt und anschließend zu Kaltband mit einer Dicke dK kaltgewalzt worden. Nach dem Kaltwalzen sind die kaltgewalzten Bänder in einer Durchlaufglühe bei einer Glühtemperatur tG für eine Glühzeit Gz geglüht worden.The melts composed according to Table 1 were cast into thin slabs in continuous successive processes, which were conveyed "inline" into a hot rolling mill and were rolled there at hot rolling end temperatures ET to form a hot strip with a final hot strip thickness d W. The hot strips leaving the hot rolling mill are then coiled at a coiling temperature HT and then cold-rolled into cold strips with a thickness d K. After the cold rolling, the cold-rolled strips were annealed in a continuous annealing at an annealing temperature t G for an annealing time Gz.
In Tabelle 2 sind die Prozeßparameter angegeben, die bei der Herstellung der Elektrobleche aus den Stählen E1 bis E6 bzw. A1 und A2 vorgesehen gewesen sind.In Table 2 the process parameters are given, which at the production of electrical sheets from steels E1 to E6 or A1 and A2 have been provided.
Dementsprechend ist aus dem Stahl E1 ein nicht kornorientiertes Elektroblech Eb1, aus dem Stahl E3 ein Elektroblech Eb3, aus dem Stahl E4 ein Elektroblech Eb4 usw. erzeugt worden. Aus dem Stahl E2 sind zwei Elektrobleche Eb2.1 und Eb2.2 hergestellt worden. Genauso sind aus dem Stahl V1 zwei Vergleichselektrobleche Vb1.1 und Vb1.2 gefertigt worden. Der Stahl V2 ist für die Herstellung von drei Vergleichselektroblechen Vb2.1, Vb2.2, Vb2.3 verwendet worden.Accordingly, steel E1 is not a grain-oriented electrical sheet Eb1, made of steel E3 Electric sheet Eb3, from the steel E4 an electric sheet Eb4 etc. have been generated. There are two made of steel E2 Electric sheets Eb2.1 and Eb2.2 have been manufactured. Just like that are two comparative electrical sheets Vb1.1 made of steel V1 and Vb1.2 have been manufactured. The steel V2 is for the Production of three comparative electrical sheets Vb2.1, Vb2.2, Vb2.3 have been used.
Der an den so erhaltenen nichtkornorientierten Elektroblechen festgestellte Ummagnetiserungsverlust P1,5 bei einer Frequenz von 50 Hz, die bei einer magnetischen Feldstärke von 2500 A/m eine ermittelte magnetische Polarisation B25 und die bei einer Frequenz von 50 Hz ermittelte magnetischen Permeabilität µ1,5 sind in Tabelle 3 angegeben.The magnetic reversal loss P 1.5 determined at the non-grain-oriented electrical sheets thus obtained at a frequency of 50 Hz, the magnetic polarization B 25 determined at a magnetic field strength of 2500 A / m and the magnetic permeability μ 1 determined at a frequency of 50 Hz , 5 are given in Table 3.
Es zeigt sich, daß die erfindungsgemäß beschaffenen Elektrobleche E1-E6 den konventionellen Vergleichsblechen jeweils in der Kombination ihrer Eigenschaften jedem der Vergleichsbeispiele Vb1.1-VB2.3 überlegen sind. So ist jeweils mindestens der Wert einer Eigenschaft dem korrespondierenden Wert der Vergleichsbleche deutlich überlegen.It turns out that the invented Electric sheets E1-E6 the conventional Comparison sheets each in the combination of their Properties of each of the comparative examples Vb1.1-VB2.3 are superior. So at least the value is one Property the corresponding value of Clearly superior comparison sheets.
Claims (12)
wobei das Elektroblech oder -band im Zuge einer von einer mindestens 1150°C betragenden Temperatur ausgehenden Abkühlung zunächst ein austenitisches Gefüge, dann ein aus Austenit und Ferrit bestehendes Mischgefüge und nach Erreichen einer unter 1050°C liegenden Temperatur schließlich ein ferritisches Gefüge aufweist und
wobei das Elektroblech oder -band bei einer Polarisation von 1,5 T und einer Frequenz von 50 Hz einen unter 4,7 W/kg liegenden Ummagnetiserungsverlust P1,5, bei einer magnetischen Feldstärke von 2500 A/m eine mindestens 1,60 T betragenden magnetischen Polarisation B25 und bei einer Frequenz von 50 Hz eine magnetische Permeabilität µ1,5 von mindestens 1500 besitzt. 1. Non-grain-oriented electrical sheet or strip, obtained from a steel melt of the following composition (in% by weight): Si: ≦ 1.8%, Al: <1%, C: ≦ 0.0200%, Mn: <0.5 %, Sn: ≦ 0.03%, Sb: ≦ 0.1%, P: ≦ 0.1%, S: <0.02%, Ti: ≦ 0.0100%, N: ≦ 0.0100%, O: ≦ 0.0100%, B: ≦ 0.0100% and the remainder iron and unavoidable impurities, the molten steel being cast into thin slabs or cast strip, which has been hot-rolled into hot strip in a continuous sequence,
the electrical sheet or strip, in the course of cooling from a temperature of at least 1150 ° C., initially has an austenitic structure, then a mixed structure consisting of austenite and ferrite, and finally has a ferritic structure after reaching a temperature below 1050 ° C. and
the electrical sheet or strip having a polarization of 1.5 T and a frequency of 50 Hz has a magnetic loss P 1.5 below 4.7 W / kg, at a magnetic field strength of 2500 A / m an at least 1.60 T absolute magnetic polarization B 25 and at a frequency of 50 Hz has a magnetic permeability µ 1.5 of at least 1500.
daß die Gehalte der Legierungselemente der Stahlschmelze folgende Bedingungen erfüllen (in Gew.-%):
C: ≦ 0,0200%,
Si: 0,9-1,4%,
Al: 0,1-0,5%, mit Si + Al < 1,8%,
Mn ≦ 0,25%,
P: ≦ 0,08%,
S: ≦ 0,015%,
Ti: ≦ 0,0100%,
N: ≦ 0,0100%,
O: ≦ 0,0100%,
B: ≦ 0,0100%.4. Electrical steel strip or sheet according to one of claims 1 to 3, characterized in
that the contents of the alloying elements of the molten steel meet the following conditions (in% by weight):
C: ≦ 0.0200%,
Si: 0.9-1.4%,
Al: 0.1-0.5%, with Si + Al <1.8%,
Mn ≦ 0.25%,
P: ≦ 0.08%,
S: ≦ 0.015%,
Ti: ≦ 0.0100%,
N: ≦ 0.0100%,
O: ≦ 0.0100%,
B: ≦ 0.0100%.
daß, die Gehalte der Legierungselemente der Stahlschmelze folgende Bedingungen erfüllen (in Gew.-%):
C: ≦ 0,0200%,
Si: 0,15-0,65%,
Al: < 0,5%,
Mn: ≦ 0,25%,
S: ≦ 0,010%,
P: ≦ 0,08%,
Ti: ≦ 0,0100%,
N: ≦ 0,0100%,
O: ≦ 0,0100%,
B: ≦ 0,0100%.5. Electrical steel strip or sheet according to one of claims 1 to 3, characterized in
that the contents of the alloying elements of the molten steel meet the following conditions (in% by weight):
C: ≦ 0.0200%,
Si: 0.15-0.65%,
Al: <0.5%,
Mn: ≦ 0.25%,
S: ≦ 0.010%,
P: ≦ 0.08%,
Ti: ≦ 0.0100%,
N: ≦ 0.0100%,
O: ≦ 0.0100%,
B: ≦ 0.0100%.