DE10104820C1 - wall covering - Google Patents

wall covering

Info

Publication number
DE10104820C1
DE10104820C1 DE10104820A DE10104820A DE10104820C1 DE 10104820 C1 DE10104820 C1 DE 10104820C1 DE 10104820 A DE10104820 A DE 10104820A DE 10104820 A DE10104820 A DE 10104820A DE 10104820 C1 DE10104820 C1 DE 10104820C1
Authority
DE
Germany
Prior art keywords
fleece
sizing agent
wall covering
binder
transition temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
DE10104820A
Other languages
German (de)
Inventor
Dieter Sept
Gabriel Koeppel
Lothar Arndt
Detlev Stoltefaut
Gerda Schreiber
Klaus Alsbach
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
FiberMark Lahnstein GmbH and Co OHG
Erfurt und Sohn KG
Original Assignee
FiberMark Lahnstein GmbH and Co OHG
Erfurt und Sohn KG
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by FiberMark Lahnstein GmbH and Co OHG, Erfurt und Sohn KG filed Critical FiberMark Lahnstein GmbH and Co OHG
Priority to DE10104820A priority Critical patent/DE10104820C1/en
Application granted granted Critical
Publication of DE10104820C1 publication Critical patent/DE10104820C1/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

Bei einer Wandbekleidung mit einem die Sichtfläche bildenden Vlies, das durch ein Leimungsmittel verfestigt ist, wird zur Erzielung eines gewünschten Farbeffekts unter Beibehaltung der filigranen Oberflächenstruktur des Vlies vorgesehen, dass das Leimungsmittel aus Bindemittel zu 20-60%, Pigmenten zu 40-80%, Farbstoffen zu 0,01-5% und Hilfsmittel zu 0-5% zusammengesetzt ist, wobei sich die Prozentangaben auf die Masse der Feststoffe in der Zusammensetzung beziehen.In the case of wallcovering with a fleece forming the visible surface, which is solidified by a sizing agent, in order to achieve a desired color effect while maintaining the filigree surface structure of the fleece, it is provided that the sizing agent consists of binder to 20-60%, pigments to 40-80%, Dyes are composed of 0.01-5% and auxiliaries to 0-5%, the percentages relating to the mass of the solids in the composition.

Description

Die Erfindung betrifft eine Wandbekleidung mit einem die Sichtfläche bildenden Vlies, das durch ein Leimungsmittel verfestigt ist, und ein Verfahren zur Herstellung einer sol­ chen Wandbekleidung.The invention relates to a wall covering with a Visible surface-forming fleece, which is made by a sizing agent is solidified, and a method for producing a sol chen wallcovering.

Wandbekleidungen mit einem die Sichtfläche bildenden Vlies haben zahlreiche Verarbeitungsvorteile. Hierbei kann das Vlies aus einer die Sichtfläche der Wandbekleidung bildenden Schicht bestehen oder auch den Träger, d. h. die Wandbekleidung selbst bilden. Solche Wandbekleidungen machen zum Beispiel empfindli­ che Untergründe, wie Untertapeten, stoßempfindliche Putze und Weichfaserplatten, druck- und stoßresistenter. Feine Haar- und Netzrisse und Putz- oder Stoßfugen bei Plattenelementen können durch sie überbrückt werden.Wall coverings with a fleece forming the visible surface have numerous processing advantages. Here, the fleece from a layer forming the visible surface of the wall covering exist or the carrier, d. H. the wallcovering itself form. Such wall coverings make sensitive, for example surfaces, such as wallpaper, plaster sensitive to impact and Soft fiber boards, pressure and shock resistant. Fine hair and Mesh cracks and plaster or butt joints in panel elements can be bridged by them.

Die Oberflächen derartiger Wandbekleidungen sind ausreichend scheuer- und gut lichtbeständig, druckstabil und dauerflexi­ bel.The surfaces of such wall coverings are sufficient abrasion and light resistant, pressure stable and permanently flexible bel.

Darüber hinaus sind sie dimensionsstabil, so dass sichtbare Stöße beim Tapezieren vermieden werden können. Der Vliesstoff ergibt ebenfalls eine hohe Einreißfestigkeit der Wandbeklei­ dung. In addition, they are dimensionally stable, making them visible Bumps when wallpapering can be avoided. The nonwoven also results in a high tear resistance of the wall cladding dung.  

Das Vlies kann sich aus natürlichen und/oder synthetischen Fasern zusammensetzen. Als natürliche Fasern eignen sich zum Beispiel Zellstoff oder Baumwolle. Als Synthesefasern kommen zum Beispiel Polyesterfasern, Fasern aus Niederdruckpolyethy­ len und/oder Polypropylen, die direkt bei der Polymerisation gewonnen werden, in Betracht. Darüber hinaus kann das Vlies auch Mineralfasern, Glasfasern und dergleichen aufweisen. Das Vlies besteht dann aus einer in Folge natürlicher Haftung zusammenhängenden Schicht aus derartigen Fasern. Übliche Vlies-Hilfsmittel sind den Fasern beigefügt. Es handelt sich hierbei insbesondere um Nassfestmittel, um der Vliesbahn wäh­ rend des Herstellungsprozesses bereits eine für die Verarbei­ tung geeignete Festigkeit zu verleihen. Zur Herstellung der Vliesbahn wird der Faserbrei in einer in der Technik üblichen Art und Weise auf eine Papiermaschine aufgegeben und das Vlies ausgebildet.The fleece can be made of natural and / or synthetic Assemble fibers. As natural fibers are suitable for Example pulp or cotton. Coming as synthetic fibers for example polyester fibers, fibers made from low-pressure polyethylene len and / or polypropylene used directly in the polymerization be considered. In addition, the fleece also have mineral fibers, glass fibers and the like. The Fleece then consists of a natural liability as a result coherent layer of such fibers. usual Fleece aids are added to the fibers. It is about especially wet strength agents, around the nonwoven web during the manufacturing process, one for the processing company suitable strength. To make the The nonwoven web becomes the pulp in a manner customary in technology Way abandoned on a paper machine and the fleece educated.

Um die für die Verwendung als Wandbekleidungsmaterial erfor­ derlichen Eigenschaften auszubilden, wird das Vlies durch ein Leimungsmittel verfestigt. Das Leimungsmittel enthält im we­ sentlichen Weißpigmente, Bindemittel und übliche Hilfsmittel.To be researched for use as a wall covering material To develop such properties, the fleece is Sizing agent solidified. The sizing agent contains we substantial white pigments, binders and common auxiliaries.

Als Weißpigmente eignen sich alle üblichen Weißpigmente.All usual white pigments are suitable as white pigments.

Als Bindemittel können generell Bindemittel aus natürlichem Rohstoff wie auch auf synthetischer Basis verwendet werden. Zu den natürlichen Bindemitteln gehören insbesondere Cellulose­ ether, Stärkederivate, Alginate und Kasein. Bevorzugt sind allerdings synthetische Mittel auf Basis von Polymerdispersio­ nen, insbesondere Dispersionen von Additionspolymeren von radikalisch polymerisierbaren Monomeren. Diese Polymere sind insbesondere Homo- und Copolymerisate von Styrol, Butadien, Acrylsäureester, Vinylacetat, Acrylnitril, Acrylamid, Acryl­ säure, Maleinsäure und Methacrylamid. Besonders geeignet sind Dispersionen auf Basis von Styrolbutadiencopolymerisat, ins­ besondere carboxylierte Styrolbutadiencopolymerisate, Poly­ acrylatdispersionen, Copolymerisate von Butylacrylat mit Sty­ rol- oder Vinylacetat und Homo- oder Copolymere von Vinylacetat. Generally, binders made from natural Raw material as well as used on a synthetic basis. To The natural binders include cellulose in particular ether, starch derivatives, alginates and casein. Are preferred however, synthetic agents based on polymer dispersion NEN, especially dispersions of addition polymers of radically polymerizable monomers. These are polymers in particular homopolymers and copolymers of styrene, butadiene, Acrylic acid ester, vinyl acetate, acrylonitrile, acrylamide, acrylic acid, maleic acid and methacrylamide. Are particularly suitable Dispersions based on styrene-butadiene copolymer, ins special carboxylated styrene-butadiene copolymers, poly acrylate dispersions, copolymers of butyl acrylate with sty Rol or vinyl acetate and homo- or copolymers of vinyl acetate.  

Übliche Hilfsmittel, die bei der Formulierung des Leimungs­ mittels verwendet werden, dienen dazu, die Verarbeitbarkeit der Zusammensetzung zu verbessern. Hierunter fallen insbesondere Dispergierhilfsmittel, Entschäumer, Mittel zur Erhöhung der Nassfestigkeit, wie z. B. Melaminformaldehyd, Harnstoff­ formaldehydharz, oder Mittel zur Einstellung der Rheologie.Usual aids in the formulation of the sizing used are used to improve the processability of the Improve composition. This includes in particular Dispersing aids, defoamers, agents for increasing the Wet strength, such as B. melamine formaldehyde, urea formaldehyde resin, or rheology control agent.

In der Zeitschrift Bodenbeläge, Tageten, Heimtextilien 5/1996, Seiten 72 und 73, sind überstreichbare Vlies- Wandbeläge aus Zellstoff- und Synthesefasern mit Acrylbinder und mineralischen Füllstoffen beschrieben, welche die oben beschriebenen Vorteile bieten.In the magazine Flooring, Tageten, Heimtextilien 5/1996, pages 72 and 73, are paintable fleece Wall coverings made of cellulose and synthetic fibers with acrylic binder and mineral fillers described above offer described advantages.

Die DE 196 36 490 A1 offenbart ein Verfahren zur Herstellung von Copolymerisaten aus ethylenisch ungesättigten Verbindungen, die aus als Bindemittel für Vliesstoffe verwendbar sind.DE 196 36 490 A1 discloses a process for the production of copolymers of ethylenically unsaturated Compounds made up as binders for nonwovens are usable.

In der DE 35 41 187 C2 ist ein Verfahren zur Herstellung einer mit Kunstharz imprägnierten Papierbahn aus Eukalyptus- und Kiefernholz-Sulfatzellstoff beschrieben, bei dem eine Imprägnierflüssigkeit verwendet wird, die Acrylsäure- und Maleinsäurecopolymerisate enthält.DE 35 41 187 C2 describes a process for the production a paper web made of eucalyptus impregnated with synthetic resin and pine wood sulfate pulp, in which one Impregnation liquid is used, the acrylic acid and Contains maleic acid copolymers.

Beschichtungsmassen, insbesondere Dispersionsfarben, mit Polymeren niedriger sowie solchen hoher Glasübergangstemperatur, Pigmente und/oder Füllstoffen und Hilfsmitteln sind in der DE 198 38 850 A1 offenbart. Coating compositions, in particular emulsion paints, with Polymers lower and those higher Glass transition temperature, pigments and / or fillers and Aids are disclosed in DE 198 38 850 A1.  

Wandbekleidungen mit einem die Sichtfläche bildenden Vlies zeichnen sich optisch-ästhetisch durch die filigrane Struktur der Sichtfläche aus, insbesondere, wenn diese reliefartig ge­ prägt ist. In vielen Fällen soll die durch den Pigmentanteil des Vlies weiße Wandbekleidung vom Verbraucher in einer ge­ wünschten Farbe gestrichen werden. Durch den Farbauftrag geht jedoch die filigrane Struktur der glatten oder geprägten Sichtfläche des Vlies verloren, so dass der durch das Vlies bestimmte optisch-ästhetische Eindruck beeinträchtigt wird.Wall coverings with a fleece forming the visible surface are visually and aesthetically characterized by the filigree structure the visible surface, especially if it is in relief is shaped. In many cases, this is due to the pigment content the fleece white wallcovering by the consumer in a ge desired color can be deleted. Goes through the paint application however, the filigree structure of the smooth or embossed Visible area of the fleece is lost, so that through the fleece certain visual-aesthetic impression is impaired.

Der Erfindung liegt daher die Aufgabe zugrunde, eine Wandbe­ kleidung mit einem die Sichtfläche bildenden Vlies so auszu­ bilden, dass das Vlies eine gewünschte Farbe besitzen kann, ohne Beeinträchtigung der filigranen Struktur seiner Sicht­ fläche. Eine weitere Aufgabe ist die Bereitstellung eines Herstellungsverfahrens für eine solche Wandbekleidung.The invention is therefore based on the object, a wall clothing with a fleece forming the visible surface form that the fleece can have a desired color, without affecting the delicate structure of his view area. Another task is to provide one Manufacturing process for such a wall covering.

Die Aufgabe wird erfindungsgemäß dadurch gelöst, dass bei einer Wandbekleidung der eingangs genannten Art das Leimungsmittel zusammengesetzt ist aus:
Bindemittel zu 20-60%
Weißpigmenten zu 40-80%
Farbstoffen zu 0,01-5% und
Hilfsmittel zu 0-5%,
wobei sich die Prozentangaben auf die Masse der Feststoffe in der Zusammensetzung beziehen. The object is achieved according to the invention in that in the case of wallcovering of the type mentioned at the outset, the sizing agent is composed of:
Binding agent to 20-60%
White pigments 40-80%
Dyes to 0.01-5% and
Aids at 0-5%,
the percentages refer to the mass of the solids in the composition.

Als Bindemittel bzw. Hilfsmittel können die oben genannten verwendet werden, wobei auch andere geeignete Binde- und/oder Hilfsmittel verwendbar sein.The abovementioned can be used as binders or auxiliaries are used, with other suitable binding and / or Tools can be used.

Durch den Zusatz von Farbstoffen, die auch Farbpigmente sein oder enthalten können, in der erfindungsgemäßen Zusammenset­ zung des Leimungsmittels können die gewünschten Farbeffekte erzielt werden, ohne dass die filigrane Struktur der Sicht­ fläche der Wandbekleidung beeinträchtigt wird. Das mit dem erfindungsgemäßen Leimungsmittel verfestigte Vlies erfüllt darüber hinaus die eingangs genannten Vorteile einer Wandbe­ kleidung. Insbesondere können aufgrund der Dimensionsstabili­ tät des Vliesstoffs sichtbare Stöße beim Tapezieren vermieden werden. Auf das Tapezieren nachfolgende Bearbeitungsschritte können daher vermieden werden.By adding dyes, which are also color pigments or can contain, in the composition according to the invention sizing of the sizing agent can produce the desired color effects can be achieved without the filigree structure of the view surface of the wall covering is impaired. That with the non-woven bonded according to the invention in addition, the advantages of a wallbe mentioned at the beginning dress. In particular, due to the dimensional stability Visible impact of the nonwoven is avoided when wallpapering become. Processing steps subsequent to wallpapering can therefore be avoided.

Da durch den Zusatz von Farbstoffen im Leimungsmittel ein nachträgliches Überstreichen der Sichtfläche des Vlies nicht erwünscht, jedoch nach wie vor möglich ist, sind besondere Anforderungen an die Opazität des Vlies zu stellen. Bei be­ kannten Wandbekleidungen mit einem die Sichtfläche bildenden Vlies war es nicht notwendig, eine hohe Opazität bereits durch den Vliesstoff zu erhalten, um damit eventuell auf dem Unter­ grund vorhandene Flecken oder Zeichnungen usw. zuverlässig zu überdecken. Denn der Vliesstoff wurde bei bekannten Wandbe­ kleidungen üblicherweise vom Verbraucher noch einmal in der gewünschten Farbe gestrichen. Sollen aber gerade die gewünsch­ ten Farbeffekte durch den Vliesstoff selbst zur Verfügung ge­ stellt werden, sind nun höhere Anforderungen an die Opazität zu stellen. Es hat sich ergeben, dass eine Erhöhung des Weiß­ pigmentanteils an der Zusammensetzung des Leimungsmittels auf 40-80% - bezogen auf die Masse der Feststoffe in der Zusam­ mensetzung - die spezifischen Anforderungen an die Opazität erfüllt.Because by adding dyes in the sizing agent do not subsequently paint over the visible surface of the fleece desirable, but still possible, are special To make demands on the opacity of the fleece. At be knew wall coverings with a visible surface It was not necessary to fleece through a high opacity to get the nonwoven to possibly be on the bottom due to existing stains or drawings etc. reliably cover. Because the nonwoven fabric was used in well-known Wandbe clothing usually used again by the consumer painted the desired color. But should just the ones you want The color effects provided by the nonwoven fabric itself are now higher demands on opacity to deliver. It has been found that an increase in white share of pigment in the composition of the sizing agent 40-80% - based on the mass of solids in the total setting - the specific requirements for opacity Fulfills.

In einer bevorzugten Zusammensetzung besteht das Leimungs­ mittel aus:
Bindemittel zu 28-45%
Weißpigmenten zu 50-70%
Farbstoffen zu 0,1-5% und
Hilfsmittel zu 2-4%.
wobei sich die Prozentangaben auf die Masse der Feststoffe in der Zusammensetzung beziehen.In a preferred composition, the sizing agent consists of:
28-45% binder
White pigments 50-70%
Dyes 0.1-5% and
Aids to 2-4%.
the percentages refer to the mass of solids in the composition.

Als für die Erfindung besonders geeignet hat sich eine Zu­ sammensetzung des Leimungsmittels herausgestellt mit:
Bindemittel zu 31-40%
Weißpigmenten zu 57-66%
Farbstoffen zu 0,1-3% und
Hilfsmittel zu 2-4%.
wobei sich die Prozentangaben auf die Masse der Feststoffe in der Zusammensetzung beziehen.A composition of the sizing agent with:
31-40% binder
57-66% white pigments
Dyes to 0.1-3% and
Aids to 2-4%.
the percentages refer to the mass of solids in the composition.

Es wurde festgestellt, dass selbst bei dem für ein farbiges Vlies notwendigen hohen Weißpigmentanteil an dem Leimungs­ mittel ein ausreichendes Pigmentbindevermögen erreicht werden kann, wenn Bindemittel mit einer geeigneten Glasübergangs­ temperatur (Tg) ausgewählt werden. Das Bindemittel sollte hierbei eine Glasübergangstemperatur (Tg) im Bereich zwischen 0°C und 40°C, vorzugsweise 5°C bis 30°C und insbesondere 10°C bis 20°C aufweisen.It was found that even with the high proportion of white pigment in the sizing agent required for a colored nonwoven, sufficient pigment binding capacity can be achieved if binders with a suitable glass transition temperature (T g ) are selected. The binder should have a glass transition temperature (T g ) in the range between 0 ° C. and 40 ° C., preferably 5 ° C. to 30 ° C. and in particular 10 ° C. to 20 ° C.

Hierbei ist es besonders vorteilhaft, eine Mischung von zwei oder mehreren Bindemitteln einzusetzen, die dann insgesamt eine Glasübergangstemperatur (Tg) in dem vorstehend angegebe­ nen Bereich aufweisen.It is particularly advantageous here to use a mixture of two or more binders, which then have a total glass transition temperature (T g ) in the range given above.

Bei chemisch ähnlichen Bindemitteln ist in sehr guter Nährung die Glasübergangstemperatur (Tg) der Mischung gleich dem ent­ sprechend der Zusammensetzung gewichteten Mittel der Glas­ übergangstemperaturen der einzelnen die Mischung bildenden Bindemittel. So hat es sich als besonders zweckmäßig herausge­ stellt, Bindemittelmischungen zu verwenden, die Bindemittel mit niedriger Glasübergangstemperatur (Tg) und Bindemittel mit hoher Glasübergangstemperatur (Tg) enthalten.In the case of chemically similar binders, the glass transition temperature (T g ) of the mixture is, in very good nutrition, equal to the weighted average composition of the glass transition temperatures of the individual binders forming the mixture. It has proven particularly expedient to use binder mixtures which contain binders with a low glass transition temperature (T g ) and binders with a high glass transition temperature (T g ).

Besonders vorteilhaft ist eine Mischung, die Bindemittel mit einer Glasübergangstemperatur im Bereich zwischen 25°C und 45°C und ein Bindemittel mit einer Glasübergangstemperatur im Bereich zwischen -10°C und +5°C enthält. Als besonders ge­ eignet haben sich Mischungen von Acrylatpolymerdispersionen als Beispiel für Bindemittel mit hoher Glasübergangstemperatur und von Alkenylacetatcopolymeren, insbesondere Vinylacetatco­ polymeren, oder Alkylacrylatcopolymeren, insbesondere mit Alkyl=C3 bis C6, insbesondere Butylacrylatcopolymeren, als Beispiel für ein Bindemittel mit niedriger Glasübergangstempe­ ratur erwiesen.A mixture containing binders with a glass transition temperature in the range between 25 ° C. and 45 ° C. and a binder with a glass transition temperature in the range between -10 ° C. and + 5 ° C. is particularly advantageous. Mixtures of acrylate polymer dispersions as an example of binders with a high glass transition temperature and of alkenyl acetate copolymers, in particular vinyl acetate copolymers, or alkyl acrylate copolymers, in particular with alkyl = C 3 to C 6 , in particular butyl acrylate copolymers, have proven to be particularly suitable as an example of a binder with a low glass transition temperature ,

Das Verhältnis der Anteile an Bindemittel mit niedriger und hoher Glasübergangstemperatur kann im Bereich von 10 : 90 bis 80 : 10, vorzugsweise 25 : 75 bis 75 : 25, besonders bevorzugt ca. 50 : 50 betragen. Vorzugsweise sind Bindemittel mit mittleren Glasübergangstemperaturen, die zwischen der niedrigen und hohen Glasübergangstemperatur liegen nur in Anteilen vorhan­ den, die kleiner als die Anteile der Bindemittel mit niedriger oder hoher Glasübergangstemperatur oder vernachlässigbar sind.The ratio of the proportions of binder with lower and high glass transition temperature can range from 10:90 to 80:10, preferably 25:75 to 75:25, particularly preferably approx. 50:50. Preferred are binders with medium Glass transition temperatures between the low and high glass transition temperatures are only present in parts the smaller than the proportion of the binders with lower or high glass transition temperature or are negligible.

Insbesondere bei sehr hohem Pigmentanteil kann es auch zweck­ mäßig sein, eine zusätzliche Oberflächenbeschichtung mit einem Leimungsmittel, das im Wesentlichen nur aus Bindemittel be­ steht, durchzuführen. Hierbei können dieselben Bindemittel wie vorstehend beschrieben verwendet werden.It can also be useful, especially if the pigment content is very high be moderate, an additional surface coating with a Sizing agent, which essentially consists only of binder stands to perform. Here, the same binders as used above.

Als Weißpigmente eignen sich alle üblichen oder andere ge­ eignete Weißpigmente, wobei Titandioxid aufgrund der hohen Opazität besonders bevorzugt ist. Aufgrund des hohen Preises ist es jedoch zweckmäßig, zumindest einen Teil des Titandi­ oxids durch andere Weißpigmente, wie z. B. Calciumcarbonat, zu ersetzen.All usual or other ge are suitable as white pigments suitable white pigments, whereby titanium dioxide due to the high Opacity is particularly preferred. Because of the high price however, it is appropriate to use at least part of the titanium di oxides by other white pigments, such as. B. calcium carbonate replace.

Als Farbstoffe, die auch Farbpigmente sein oder enthalten können, kommen die üblichen Substanzen in Betracht, um die gewünschten Farbeffekte zu erzielen. Auch bei den zur Formu­ lierung des Leimungsmittels verwendeten Hilfsmitteln kommen die üblichen eingangs erwähnten Substanzen zum Einsatz.As dyes, which can also be or contain color pigments can, the usual substances are considered to the  to achieve desired color effects. Even with those for Formu the sizing agent used come the usual substances mentioned at the outset.

Die Erfindung umfasst weiterhin ein Verfahren zur Herstellung einer Wandbekleidung der eingangs genannten Art, wobei das Vlies auf einer Papiermaschine hergestellt wird und durch Imprägnierung mit dem erfindungsgemäß zusammengesetzten Lei­ mungsmittel verfestigt wird.The invention further includes a method of manufacture a wallcovering of the type mentioned, which Fleece is made on a paper machine and by Impregnation with the Lei composed according to the invention is solidified.

Die Herstellung des Vlies kann auf einer üblichen Papierma­ schine erfolgen. Hierzu wird zuerst ein Faserrohstoff, der im Wesentlichen die üblicherweise bei der Vliesherstellung ver­ wendeten Fasern aus natürlichem Material, wie z. B. Zellstoff oder Baumwolle, und/oder aus synthetischem Material, wie z. B. Polyesterfasern, Fasern aus Niederdruckpolyethylen oder Poly­ propylen, die direkt bei der Polymerisation gewonnen werden, enthält, erzeugt. Eine für das erfindungsgemäße Vlies geeigne­ te Rohfaserkombination kann 50% bis 100% Zellstoff und/oder Baumwolle und 0% bis 50% Synthesefasern enthalten. Der An­ teil an Vlies-Hilfsmitteln kann 0,5% bis 4% bezogen auf den Faseranteil betragen. Hierbei werden insbesondere Nassfest­ mittel verwendet, um der Vliesbahn während des Herstellungs­ prozesses bereits eine für die Verarbeitung geeignete Festig­ keit zu verleihen. Zur Herstellung der Vliesbahn wird der Faserbrei in einer in der Technik üblichen Art und Weise auf eine Papiermaschine aufgegeben und das Vlies ausgebildet.The production of the nonwoven can be done on a conventional paper machine machine done. For this purpose, a fiber raw material is first used in Essentially the ver turned fibers from natural material, such as. B. pulp or cotton, and / or synthetic material, such as. B. Polyester fibers, fibers from low pressure polyethylene or poly propylene, which are obtained directly from the polymerization, contains, generated. Suitable for the fleece according to the invention The raw fiber combination can contain 50% to 100% cellulose and / or Contain cotton and 0% to 50% synthetic fibers. The An Part of nonwoven auxiliaries can be 0.5% to 4% based on the Amount of fiber. This is especially wet means used to make the nonwoven web during manufacture process is already suitable for processing to lend. To produce the nonwoven web, the Fiber pulp in a manner customary in the art abandoned a paper machine and formed the fleece.

Die im zweiten Verfahrensschritt vorgesehene Imprägnierung durch das erfindungsgemäße Leimungsmittel kann durch Tauch- oder Schaumimprägnierung des vorgefertigten Vlies erfolgen. Die Tauchimprägnierung wird in einer Leimpresse oder einem Tauchbad vorgenommen. Dabei wird die Aufnahme des auf das Vlies aufgetragenen Leimungsmittels hauptsächlich durch den Feststoffgehalt des Leimungsmittels und den Abquetschvorgang mittels einer Walzenkombination gesteuert. Die das Vlies bil­ denden Fasern und Faserfüllstoffe werden bei der Imprägnierung mit einem Imprägnierfilm regelrecht überzogen. Ein geschlossener Imprägnierfilm entsteht, wenn die Mindestfilmbildungs­ temperatur erreicht wird.The impregnation provided in the second process step by means of the sizing agent according to the invention or foam impregnation of the prefabricated fleece. The dip impregnation is done in a size press or a Dip bath made. The inclusion of the on the Fleece applied sizing agent mainly through the Solids content of the sizing agent and the squeezing process controlled by a combination of rollers. The bil the fleece Ending fibers and fiber fillers are used in the impregnation literally covered with an impregnation film. A closed one  Impregnation film arises when the minimum film formation temperature is reached.

Statt durch Imprägnierung kann das Leimungsmittel auch durch Aufstreichen oder Aufsprühen auf das Vlies aufgetragen werden. Um die filigrane Struktur der Sichtfläche des Vlies zu erhal­ ten, ist zumindest an dieser Fläche vom Vlies nicht aufgenom­ menes Leimungsmittel durch eine Rakel oder einen Schaber zu entfernen.Instead of impregnation, the sizing agent can also be applied Spread or spray on the fleece. To maintain the delicate structure of the visible surface of the fleece at least on this surface is not absorbed by the fleece menes by a squeegee or a scraper remove.

Vor oder nach dem Verfestigen des Vlies durch das erfindungs­ gemäße Leimungsmittel können thermoplastische Anteile des Vlies bzw. des Leimungsmittels auf die Schmelztemperatur der thermoplastischen Anteile oder eine ausreichende Erweichungs­ temperatur erwärmt werden, so dass unter den Verfahrensbedin­ gungen eine Verbindung der thermoplastischen Anteile unterein­ ander erfolgt. Durch die thermische Behandlung der thermopla­ stischen Anteile wird das Vlies weiter verfestigt.Before or after the fleece solidifies by the invention according sizing agents can thermoplastic portions of the Fleece or the sizing agent to the melting temperature of the thermoplastic components or sufficient softening temperature are heated so that under the process conditions a connection of the thermoplastic components other is done. The thermal treatment of thermopla The fleece is further solidified.

Das Leimungsmittel kann zwecks Imprägnierung oder beim Auf­ streichen oder Aufsprüchen in einer Menge von 40-65 g/m2 auf das Vlies aufgebracht werden, wobei sich das Auftragsgewicht auf das Gewicht der Feststoffe im Leimungsmittel bezieht. Vorzugsweise beträgt das Auftragsgewicht 50-60 g/m2. Als be­ sonders für die Erfindung geeignet hat sich ein Auftragsge­ wicht von 53-57 g/m2 herausgestellt.The sizing agent can be applied to the fleece for impregnation or when painting or spraying on in an amount of 40-65 g / m 2 , the application weight based on the weight of the solids in the sizing agent. The application weight is preferably 50-60 g / m 2 . An order weight of 53-57 g / m 2 has been found to be particularly suitable for the invention.

Im Falle einer zusätzlichen Oberflächenverleimung wird nach dem Verfestigen des Vlies eine zusätzliche Schicht aus Lei­ mungsmittel, das im Wesentlichen nur aus Bindemittel besteht, auf das Vlies aufgetragen. Das Auftragsgewicht der zusätzli­ chen Schicht beträgt vorzugsweise 5-15 g/m2.In the case of additional surface gluing, an additional layer of sizing agent, which essentially consists only of binder, is applied to the nonwoven after the nonwoven has solidified. The application weight of the additional layer is preferably 5-15 g / m 2 .

Das mit dem erfindungsgemäßen Leimungsmittel verfestigte Vlies kann anschließend in einer Prägestation des Herstellungsver­ fahrens ein- oder beidseitig geprägt werden. Dabei erhält zumindest die Sichtfläche der Wandbekleidung eine gewünschte reliefartige Oberflächenstruktur.The nonwoven bonded with the sizing agent according to the invention can then in an embossing station of the manufacturing ver driving on one or both sides. Thereby receives at least the visible surface of the wallcovering is a desired one relief-like surface structure.

Claims (21)

1. Wandbekleidung mit einem die Sichtfläche bildenden Vlies, das durch ein Leimungsmittel verfestigt ist, da­ durch gekennzeichnet, dass das Leimungs­ mittel zusammengesetzt ist aus:
Bindemittel zu 20-60%
Weißpigmenten zu 40-80%
Farbstoffen zu 0,01-5% und
Hilfsmittel zu 0-5%,
wobei sich die Prozentangaben auf die Masse der Feststoffe in der Zusammensetzung beziehen.1. Wall covering with a non-woven forming the visible surface, which is solidified by a sizing agent, since characterized in that the sizing agent is composed of:
Binding agent to 20-60%
White pigments 40-80%
Dyes to 0.01-5% and
Aids at 0-5%,
the percentages refer to the mass of the solids in the composition. 2. Wandbekleidung nach Anspruch 1, dadurch ge­ kennzeichnet, dass das Leimungsmittel zusammen­ gesetzt ist aus:
Bindemittel zu 28-45%
Weißpigmenten zu 50-70%
Farbstoffen zu 0,1-5% und
Hilfsmittel zu 2-4%,
wobei sich die Prozentangaben auf die Masse der Feststoffe in der Zusammensetzung beziehen. 2. Wall covering according to claim 1, characterized in that the sizing agent is composed of:
28-45% binder
White pigments 50-70%
Dyes 0.1-5% and
2-4% aids,
the percentages refer to the mass of solids in the composition. 3. Wandbekleidung nach Anspruch 2, dadurch ge­ kennzeichnet, dass das Leimungsmittel zusammen­ gesetzt ist aus:
Bindemittel zu 31-40%
Weißpigmenten zu 57-66%
Farbstoffen zu 0,1-3% und
Hilfsmittel zu 2-4%,
wobei sich die Prozentangaben auf die Masse der Feststoffe in der Zusammensetzung beziehen.3. Wall covering according to claim 2, characterized in that the sizing agent is composed of:
31-40% binder
57-66% white pigments
Dyes to 0.1-3% and
2-4% aids,
the percentages refer to the mass of solids in the composition. 4. Wandbekleidung nach einem der Ansprüche 1-3, da­ durch gekennzeichnet, dass das Binde­ mittel eine Glasübergangstemperatur (Tg) im Bereich zwi­ schen 0°C und 40°C aufweist.4. Wall covering according to one of claims 1-3, characterized in that the binding medium has a glass transition temperature (T g ) in the range between 0 ° C and 40 ° C. 5. Wandbekleidung nach Anspruch 4, dadurch ge­ kennzeichnet, dass das Bindemittel eine Glas­ übergangstemperatur (Tg) von 5°C bis 30°C aufweist.5. Wall covering according to claim 4, characterized in that the binder has a glass transition temperature (T g ) of 5 ° C to 30 ° C. 6. Wandbekleidung nach Anspruch 5, dadurch ge­ kennzeichnet, dass das Bindemittel eine Glas­ übergangstemperatur (Tg) von 10°C bis 20°C aufweist.6. Wall covering according to claim 5, characterized in that the binder has a glass transition temperature (T g ) of 10 ° C to 20 ° C. 7. Wandbekleidung nach einem der Ansprüche 1-6, da­ durch gekennzeichnet, dass das Binde­ mittel aus einer Mischung besteht, die Bindemittelkompo­ nenten mit niedriger Glasübergangstemperatur und Binde­ mittelkomponenten mit hoher Glasübergangstemperatur ent­ hält.7. Wall covering according to one of claims 1-6, there characterized by that the bandage medium consists of a mixture, the binder compo elements with low glass transition temperature and bandage medium components with a high glass transition temperature holds. 8. Wandbekleidung nach Anspruch 7, dadurch ge­ kennzeichnet, dass die Mischung Bindemittel­ komponenten mit einer Glasübergangstemperatur zwischen 25°C und 45°C und Bindemittelkomponenten mit einer Glas­ übergangstemperatur zwischen -10°C und 5°C enthält. 8. Wall covering according to claim 7, characterized ge indicates that the mixture binders components with a glass transition temperature between 25 ° C and 45 ° C and binder components with a glass contains transition temperature between -10 ° C and 5 ° C.   9. Wandbekleidung nach Anspruch 8, dadurch ge­ kennzeichnet, dass die Mischung als eine Binde­ mittelkomponente eine Acrylatpolymerdispersion und als andere Bindemittelkomponente Alkenylacetatcopolymere oder Alkyl=C3 bis C6 acrylatcopolymere enthält.9. Wall covering according to claim 8, characterized in that the mixture contains a binder component as an acrylate polymer dispersion and as another binder component alkenyl acetate copolymers or alkyl = C 3 to C 6 acrylate copolymers. 10. Wandbekleidung nach einem der Ansprüche 1-9, da­ durch gekennzeichnet, dass das Vlies eine zusätzliche Oberflächenbeschichtung mit einem Lei­ mungsmittel aufweist, das im Wesentlichen nur aus Binde­ mittel besteht.10. Wall covering according to one of claims 1-9, there characterized by that the fleece an additional surface coating with a lei Means has essentially only from a bandage medium exists. 11. Wandbekleidung nach einem der Ansprüche 1-10, da­ durch gekennzeichnet, dass das Vlies zumindest an der Sichtfläche der Wandbekleidung relief­ artig geprägt ist.11. Wall covering according to one of claims 1-10, there characterized by that the fleece relief at least on the visible surface of the wallcovering is shaped well. 12. Verfahren zur Herstellung einer Wandbekleidung nach einem der Ansprüche 1-11, dadurch gekennzeich­ net, dass das Vlies auf einer Papiermaschine hergestellt wird und durch Imprägnierung mit dem Leimungsmittel ver­ festigt wird.12. Process for producing a wall covering according to a of claims 1-11, characterized net that the fleece is made on a paper machine and ver by impregnation with the sizing agent is consolidated. 13. Verfahren zur Herstellung einer Wandbekleidung nach einem der Ansprüche 1-11, dadurch gekennzeich­ net, dass das Vlies auf einer Papiermaschine hergestellt wird und durch Aufstreichen oder Aufsprühen mit dem Lei­ mungsmittel verfestigt wird.13. Process for producing a wall covering according to a of claims 1-11, characterized net that the fleece is made on a paper machine and by spreading or spraying with the lei is solidified. 14. Verfahren nach Anspruch 12 oder 13, wobei das Vlies ther­ moplastische Faseranteile und/oder Faserfüllstoffanteile aufweist, dadurch gekennzeichnet, dass das Vlies auf die Schmelztemperatur der thermoplastischen Anteile erwärmt wird.14. The method according to claim 12 or 13, wherein the fleece ther plastic fiber components and / or fiber filler components has, characterized in that the fleece to the melting temperature of the thermoplastic Shares is heated. 15. Verfahren nach einem der Ansprüche 12-14, wobei das Lei­ mungsmittel thermoplastische Anteile aufweist, da­ durch gekennzeichnet, dass das mit dem Leimungsmittel verfestigte Vlies auf die Schmelztemperatur der thermoplastischen Anteile erwärmt wird.15. The method according to any one of claims 12-14, wherein the Lei has thermoplastic components, because characterized by that with the  Sizing agent solidified the fleece to the melting temperature the thermoplastic portion is heated. 16. Verfahren nach einem der Ansprüche 12-15, dadurch gekennzeichnet, dass das Leimungsmittel zwecks Imprägnierung oder beim Aufstreichen oder Aufsprü­ hen in einer Menge von 40-65 g/m2 auf das Vlies aufge­ bracht wird, wobei sich das Auftragsgewicht auf das Ge­ wicht der Feststoffe im Leimungsmittel bezieht.16. The method according to any one of claims 12-15, characterized in that the sizing agent for impregnation or when brushing or spraying is applied in an amount of 40-65 g / m 2 to the nonwoven, the application weight depending on the Ge importance of solids in the sizing agent. 17. Verfahren nach Anspruch 16, dadurch gekenn­ zeichnet, dass das Leimungsmittel zwecks Imprägnie­ rung oder beim Aufstreichen oder Aufsprühen in einer Menge von 50-60 g/m2 auf das Vlies aufgebracht wird.17. The method according to claim 16, characterized in that the sizing agent for the purpose of impregnation or when brushing or spraying is applied in an amount of 50-60 g / m 2 to the nonwoven. 18. Verfahren nach Anspruch 17, dadurch gekenn­ zeichnet, dass das Leimungsmittel zwecks Imprägnie­ rung oder beim Aufstreichen oder Aufsprühen in einer Menge von 53-57 g/m2 auf das Vlies aufgebracht wird.18. The method according to claim 17, characterized in that the sizing agent is applied to the fleece for the purpose of impregnation or when spreading or spraying in an amount of 53-57 g / m 2 . 19. Verfahren nach einem der Ansprüche 12-18, dadurch gekennzeichnet, dass nach dem Verfestigen des Vlies durch das Leimungsmittel eine zusätzliche Schicht aus Leimungsmittel, das im Wesentlichen nur aus Binde­ mittel besteht, auf das Vlies aufgetragen wird.19. The method according to any one of claims 12-18, characterized characterized that after the solidification of the Fleece through the sizing agent an additional layer from sizing agent, which essentially consists only of bandage medium exists, on the fleece is applied. 20. Verfahren nach Anspruch 19, dadurch gekenn­ zeichnet, dass die zusätzliche Schicht mit einem Auftragsgewicht von 5-15 g/m2 aufgetragen wird.20. The method according to claim 19, characterized in that the additional layer is applied with an application weight of 5-15 g / m 2 . 21. Verfahren nach einem der Ansprüche 12-20, dadurch gekennzeichnet, dass das Vlies nach dem Ver­ festigen und gegebenenfalls Auftragen der zusätzlichen Schicht zumindest an der Sichtfläche der Wandbekleidung reliefartig geprägt wird.21. The method according to any one of claims 12-20, characterized characterized that the fleece after Ver solidify and if necessary apply the additional Layer at least on the visible surface of the wall covering is shaped in relief.
DE10104820A 2001-02-01 2001-02-01 wall covering Expired - Fee Related DE10104820C1 (en)