[go: up one dir, main page]

DE10049005A1 - Treating or pre-treating containers made e.g. of aluminum and aluminum-containing alloys, comprises applying lubricating agent during treatment or pre-treatment - Google Patents

Treating or pre-treating containers made e.g. of aluminum and aluminum-containing alloys, comprises applying lubricating agent during treatment or pre-treatment

Info

Publication number
DE10049005A1
DE10049005A1 DE10049005A DE10049005A DE10049005A1 DE 10049005 A1 DE10049005 A1 DE 10049005A1 DE 10049005 A DE10049005 A DE 10049005A DE 10049005 A DE10049005 A DE 10049005A DE 10049005 A1 DE10049005 A1 DE 10049005A1
Authority
DE
Germany
Prior art keywords
treatment
group
pretreatment
agent
aluminum
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
DE10049005A
Other languages
German (de)
Inventor
Karl-Heinz Bischoff
Lars Sebralla
Norbert Kliehm
Manfred Walter
Markus Wahren
Mats Eriksson
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Chemetall GmbH
Original Assignee
Chemetall GmbH
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chemetall GmbH filed Critical Chemetall GmbH
Priority to DE10049005A priority Critical patent/DE10049005A1/en
Priority to EP01945168.1A priority patent/EP1294834B1/en
Priority to US10/297,138 priority patent/US7344757B2/en
Priority to DK01945168.1T priority patent/DK1294834T3/en
Priority to CA2410321A priority patent/CA2410321C/en
Priority to CNB018136621A priority patent/CN1214097C/en
Priority to PCT/EP2001/005778 priority patent/WO2001092445A2/en
Publication of DE10049005A1 publication Critical patent/DE10049005A1/en
Withdrawn legal-status Critical Current

Abstract

Treating or pre-treating containers comprises applying a lubricating agent during treatment or pre-treatment. The agent contains and/or is a lubricant which does not substantially comprise titanium and/or zirconium with fluoride and a polymer. The lubricant is formed in the agent used for treatment or pretreatment and/or when the coating resulting from it is formed. Preferred Features: A conversion coating of a first and/or second type is formed on the substrate for the pre-treatment or treatment (treating agent). The treating agent is an aqueous solution or an aqueous dispersion free from fluoride. The treating agent contains not more than 10, preferably not more than 6 wt.% phosphate. The treating agent is preferably an aqueous solution containing 1-300 of a rare earth element including scandium, yttrium, lanthanum; 0.05-500 mg/l bismuth, antimony, selenium or tellurium; 0.02-250 mg/l EDTA, HEDTA or NTA; 1-100 g/l of an oxidant based on a peroxide; and 30 mg/l hydrochloric acid having a pH of 1-3.

Description

Die Erfindung betrifft ein Verfahren zur Behandlung oder Vorbehandlung von Behältern aus Aluminium oder Aluminium-haltigen Legierungen, Magnesium-haltigen Legierungen, Weißblech, Stahl oder Kunststoff. Diese Behälter können Beutel, Tüten und ähnliche Verpackungen, Flaschen, Dosen, Kanister, Fässer usw. sein.The invention relates to a method for the treatment or pretreatment of Containers made of aluminum or alloys containing aluminum, magnesium-containing ones Alloys, tinplate, steel or plastic. These containers can be bags, sachets and similar packaging, bottles, cans, canisters, barrels, etc.

Allgemein werden Behälter in kontinuierlichen Vorbehandlungsanlagen zur Lackierung vorbereitet. Derartige Behälter, insbesondere Dosen, werden in Großserie unter Verwendung von Folien, Blechen oder Formkörpern aus Aluminium, Aluminiumlegierungen, Weißblech oder Kunststoff hergestellt und nach der Reinigung, Vorbehandlung, Lackierung und Trocknung mit Getränken, Lebensmitteln oder anderen Produkten gefüllt und geschlossen bzw. verschlossen. Dosen werden in den meisten Dosenvorbehandlungsanlagen mit einer Geschwindigkeit im Bereich von 500 bis 5000 Dosen pro Minute vorbehandelt. Daher werden an die Geschwindigkeit aller Abläufe und an die sichere Beherrschung aller Prozeßschritte hohe Anforderungen gestellt. Außerdem werden hohe Anforderungen an die Gleiteigenschaften der Behälter in der kontinuierlichen Vorbehandlungsanlage einschließlich Printer bzw. Lackieranlage sowie an die Haftfestigkeit für Lack bzw. andere nachfolgende Beschichtungen und an die Korrosionsbeständigkeit gestellt.In general, containers are used in continuous pretreatment systems Paintwork prepared. Such containers, especially cans, are in large series using foils, sheets or shaped bodies made of aluminum, Made of aluminum alloys, tinplate or plastic and according to the Cleaning, pre-treatment, painting and drying with drinks, food or other products filled and closed or closed. Cans are in most can pretreatment lines at a speed in the range of 500 to 5000 cans pretreated per minute. Hence, speed of all processes and high mastery of all process steps Requirements. In addition, high demands are placed on the Sliding properties of the containers in the continuous pretreatment system including printer or painting system as well as the adhesive strength for paint or other subsequent coatings and corrosion resistance.

Aufgabe der Erfindung ist es, die Nachteile des Standes der Technik zu überwinden und insbesondere ein einfacheres und kostengünstigeres Verfahren zur Behandlung bzw. Vorbehandlung der Behälter vorzuschlagen, das bei den sehr hohen Geschwindigkeiten der Großserienfertigung eine sichere Vorbehandlung bzw. Behandlung und einen sehr hohen Korrosionsschutz bietet. The object of the invention is to overcome the disadvantages of the prior art and in particular a simpler and cheaper method of treatment or to suggest pretreatment of the containers, which is the case with the very high High-volume production speeds a safe pretreatment or Treatment and a very high level of corrosion protection.  

Die Aufgabe wird durch das in den Ansprüchen 1 bis 6 angegebene Verfahren und durch das in Anspruch 38 genannte Mittel gelöst. Die weiteren Ansprüche gestalten das Verfahren bzw. das Mittel weiter aus.The object is achieved by the method and in the claims 1 to 6 solved by the means mentioned in claim 38. Design the other claims the procedure or the means further.

Das Mittel zur Behandlung bzw. Vorbehandlung liegt vorzugsweise als wässerige oder/und in organischem Lösemittel gelöste Lösung vor. Es enthält oder/und ist erfindungsgemäß gleichzeitig ein Gleitmittel, damit die hiermit eingesprühten äußeren Partien beim Kontakt gleichartiger Behälter untereinander bzw. mit den Führungen der Anlage besser gleiten.The agent for treatment or pretreatment is preferably an aqueous one or / and solution dissolved in organic solvent. It contains or / and is according to the invention at the same time a lubricant so that the outer sprayed with it Batches in the contact of similar containers with each other or with the guides of the Sliding system better.

Claims (38)

1. Verfahren zur Behandlung oder Vorbehandlung von Behältern aus Aluminium, Aluminium-haltigen Legierungen, Magnesium-haltigen Legierungen, Eisenwerkstoffe, Stahl, beschichtete Eisenwerkstoffe wie verzinkter Stahl, verzinkte oder mit Aluminium/Al-Legierungen beschichtete metallische Werkstoffen, Weißblech, Messing, Bronze oder Kunststoff, insbesondere von Beuteln, Tüten, Flaschen, Dosen, Kanistern, Fässern oder Hülsen, dadurch gekennzeichnet, daß die Verfahrensstufen der Behandlung bzw. Vorbehandlung mit der der Aufbringung des Gleitmittels zusammenfallen, wobei das hierzu eingesetzte Mittel zur Vorbehandlung bzw. Behandlung, das auch ein Gleitmittel enthält oder ist, nicht im wesentlichen aus Ti oder/und Zr mit F und Polymer besteht. (ein- oder mehrteiligen Hülsen, insbesondere Patronenhülsen, Tablettenhülsen, Zigarrenhülsen; insbesondere verzinktem Metall, Galvalum = Stahl mit ZnAL, Weißblech = verzinnter Stahl)1.Process for the treatment or pretreatment of containers made of aluminum, aluminum-containing alloys, magnesium-containing alloys, iron materials, steel, coated iron materials such as galvanized steel, galvanized or coated with aluminum / aluminum alloys metallic materials, tinplate, brass, bronze or Plastic, in particular bags, bags, bottles, cans, canisters, barrels or sleeves, characterized in that the treatment or pretreatment process steps coincide with the application of the lubricant, the pretreatment or treatment agent used for this, which also contains or is a lubricant, does not consist essentially of Ti or / and Zr with F and polymer. (single or multi-part sleeves, in particular cartridge cases, tablet cases, cigar cases; in particular galvanized metal, Galvalum = steel with ZnAL, tinplate = tinned steel) 2. Verfahren zur Behandlung oder Vorbehandlung von Behältern aus Aluminium, Aluminium-haltigen Legierungen, Magnesium-haltigen Legierungen, Stahl, Weißblech oder Kunststoff, insbesondere von Beuteln, Tüten, Flaschen, Dosen, Kanistern oder Fässern, dadurch gekennzeichnet, daß das hierbei zur Behandlung bzw. Vorbehandlung aufgebrachte Mittel gleichzeitig auch ein Gleitmittel ist.2. methods of treating or pretreating aluminum containers, Aluminum-containing alloys, magnesium-containing alloys, steel, Tinplate or plastic, especially bags, bags, bottles, cans, Canisters or barrels, characterized in that the Treatment or pretreatment applied agents at the same time Is lubricant. 3. Verfahren zur Behandlung oder Vorbehandlung von Behältern aus Aluminium, Aluminium-haltigen Legierungen, Magnesium-haltigen Legierungen, Stahl, Weißblech oder Kunststoff, insbesondere von Beuteln, Tüten, Flaschen, Dosen, Kanistern oder Fässern, dadurch gekennzeichnet, daß die behandelten bzw. vorbehandelten Behälter bei einer Temperatur von mindestens 180°C in der Serienfertigung getrocknet werden. (vorzugsweise ≧ 200°C, ≧ 220°C, ≧ 250°C. Gerade bei einem Bandstillstand bei der Vorbehandlung und Lackierung von Dosen kann es im Bereich der Trocknung zu erhöhten Temperaturen kommen. Der Bandstillstand kann dabei in manchen Fällen z. B. eine halbe Stunde oder sogar länger andauern.)3. methods for treating or pretreating aluminum containers, Aluminum-containing alloys, magnesium-containing alloys, steel, Tinplate or plastic, especially bags, bags, bottles, cans, Canisters or barrels, characterized in that the treated or pretreated container at a temperature of at least 180 ° C in the Series production can be dried. (preferably ≧ 200 ° C, ≧ 220 ° C, ≧ 250 ° C. Especially in the event of a belt standstill during the pretreatment and painting of  Cans can reach elevated temperatures in the drying area. The tape stoppage can in some cases, for. B. half an hour or last even longer.) 4. Verfahren zur Behandlung oder Vorbehandlung von Behältern aus Aluminium, Aluminium-haltigen Legierungen, Magnesium-haltigen Legierungen, Stahl, Weißblech oder Kunststoff, insbesondere von Beuteln, Tüten, Flaschen, Dosen, Kanistern oder Fässern, dadurch gekennzeichnet, daß die behandelten bzw. vorbehandelten Behälter bei einer Temperatur von höchstens 150°C in der Serienfertigung getrocknet werden. (vorzugsweise ≦ 120°C, ≦ 100°C, ≦ 80°C, ≦ 50°C, insbesondere von Raumtemperatur bis zu diesen Temperaturen; wobei die überschüssige Vorbehandlungsflüssigkeit insbesondere in Form von Tropfen auf den Behälteroberflächen abgeblasen wird; hierbei wird insbesondere der Umschlag von hydrophilen auf hydrophobe Eigenschaften der beschichteten, insbesondere mit P-haltigen Verbindungen wie Diphosphonverbindungen beschichteten Oberflächen benutzt, von denen sich die überschüssige Flüssigkeit besonders leicht abblasen läßt und von daher sehr niedrige Trockentemperaturen einstellen lassen: kostengünstiger aufgrund erheblich verringerter Trocknungsaufwendungen).4. methods for treating or pretreating aluminum containers, Aluminum-containing alloys, magnesium-containing alloys, steel, Tinplate or plastic, especially bags, bags, bottles, cans, Canisters or barrels, characterized in that the treated or pretreated container at a temperature of at most 150 ° C in the Series production can be dried. (preferably ≦ 120 ° C, ≦ 100 ° C, ≦ 80 ° C, ≦ 50 ° C, in particular from room temperature to these temperatures; in which the excess pretreatment liquid, in particular in the form of drops is blown off on the container surfaces; here in particular the Change from hydrophilic to hydrophobic properties of the coated, especially with P-containing compounds such as diphosphonic compounds coated surfaces, of which the excess Liquid can be easily blown off and therefore very low Allow drying temperatures to be set: less expensive due to considerable reduced drying costs). 5. Verfahren zur Behandlung oder Vorbehandlung von Behältern aus Aluminium, Aluminium-haltigen Legierungen, Magnesium-haltigen Legierungen, Stahl, Weißblech oder Kunststoff, insbesondere von Beuteln, Tüten, Flaschen, Dosen, Kanistern oder Fässern, dadurch gekennzeichnet, daß verschiedenartige Behälter für verschiedene Einsatzzwecke, insbesondere verschiedenartige Dosen, auf der gleichen Anlage mit gleichartigen Einstellungen und/oder in gleichartigen Bädern vorbehandelt oder behandelt werden. (verschiedenartige Bäder: gleiche Zusammensetzung, aber unterschiedliche Konzentration)5. Process for treating or pretreating aluminum containers, Aluminum-containing alloys, magnesium-containing alloys, steel, Tinplate or plastic, especially bags, bags, bottles, cans, Canisters or barrels, characterized in that different types Containers for different purposes, especially different ones Cans, on the same system with similar settings and / or in similar baths are pretreated or treated. (Various Baths: same composition, but different concentration) 6. Verfahren nach mindestens einem der vorstehenden Ansprüche, dadurch abgewandelt, daß Silizium-haltige Legierungen eingesetzt werden. (Die Gehalte an Aluminium, Magnesium oder/und Silizium können hierbei auch vergleichsweise gering sein, z. B. nur etwa 1% betragen.)6. The method according to at least one of the preceding claims, characterized modified that silicon-containing alloys are used. (The salaries  of aluminum, magnesium and / or silicon can also be used here be comparatively small, e.g. B. only be about 1%.) 7. Verfahren nach mindestens einem der vorstehenden Ansprüche, dadurch gekennzeichnet, daß das Mittel zur Behandlung bzw. Vorbehandlung, das ggf. ein Gleitmittel ist, mindestens eine Seltenerdelement-Verbindung enthält, insbesondere mindestens eine Verbindung ausgewählt aus der Gruppe aus Chlorid, Nitrat, Sulfat, Sulfamat sowie Komplexen z. B. mit einem Halogen oder mit einer Aminocarboxylsäure, insbesondere Komplexen mit EDTA, NTA oder HEDTA, wobei auch Scandium, Yttrium und Lanthan als Seltenerdelemente angesehen werden.7. The method according to at least one of the preceding claims, characterized characterized in that the agent for treatment or pretreatment, which may is a lubricant, contains at least one rare earth element compound, in particular at least one compound selected from the group Chloride, nitrate, sulfate, sulfamate and complexes such. B. with a halogen or with an aminocarboxylic acid, especially complexes with EDTA, NTA or HEDTA, with scandium, yttrium and lanthanum as rare earth elements be considered. 8. Verfahren nach Anspruch 7, dadurch gekennzeichnet, daß die Seltenerd­ element-Verbindung Cer enthält, insbesondere in einer Mischung mit anderen Seltenerdelementen.8. The method according to claim 7, characterized in that the rare earth element compound contains cerium, especially in a mixture with others Rare earth elements. 9. Verfahren nach Anspruch 7 oder 8, dadurch gekennzeichnet, daß das Mittel zur Behandlung bzw. Vorbehandlung auch mindestens ein Oxidationsmittel, insbesondere ein Peroxid, oder/und mindestens einen Beschleuniger, vorzugsweise eine Verbindung von Bi, Cu oder/und Zn, enthält.9. The method according to claim 7 or 8, characterized in that the means for Treatment or pretreatment also at least one oxidizing agent, in particular a peroxide, and / or at least one accelerator, preferably contains a compound of Bi, Cu or / and Zn. 10. Verfahren nach mindestens einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß das Mittel zur Behandlung bzw. Vorbehandlung, das ggf. auch ein Gleitmittel ist, mindestens ein Silan enthält, insbesondere mindestens eine Verbindung ausgewählt aus der Gruppe der Mono-, Bis- und Multi-Silanen, insbesondere:
  • - Mono-Silane der allgemeinen Formel SiXmY4-m
    mit m = 1 bis 3, vorzugsweise m = 2 bis 3,
    mit X = Alkoxy, insbesondere Methoxy, Ethoxy oder/und Propoxy, und
    mit Y als einer funktionellen organischen Gruppe ausgewählt aus der Gruppe von Alkyl, Acrylat, Amino, Epoxy, Glycidoxy, Harnstoff, Isocyanat, Mercapto, Methacrylat oder/und Vinyl,
  • - Bis-Silane der allgemeinen Formel Y3-pXp-Si-Z-Si-XnY3-n
    mit p und n = 1 bis 3 gleich oder verschieden,
    mit X = Alkoxy, insbesondere Methoxy, Ethoxy oder/und Propoxy,
    mit Y als funktionellen organischen Gruppen ausgewählt aus der Gruppe von Alkyl, Acrylat, Amino, Epoxy, Glycidoxy, Harnstoff, Isocyanat, Mercapto, Methacrylat, Schwefel Sq mit q = 1 bis 20 und Vinyl,
    mit Z ausgewählt aus der Gruppe von CnH2n mit n = 2 bis 20 jeweils verzweigt oder unverzweigt, von einfach ungesättigte Alkylketten der allgemeinen Formel CnH2n-2 mit n = 2 bis 20 jeweils verzweigt oder unverzweigt, von zweifach oder/und mehrfach ungesättigten Alkyl-Verbindungen der allgemeinen Formeln CnH2n-4 mit n = 4 bis 20 jeweils verzweigt oder unverzweigt, CnH2n-6 mit n = 6 bis 20 jeweils verzweigt oder unverzweigt bzw. CnH2n-8 mit n = 8 bis 20 jeweils verzweigt oder unverzweigt, von Ketonen, Monoalkylaminen, Ethylen und NH,
  • - Multi-Silane der allgemeinen Formel Y3-pXp-Si-Z'-Si-XnY3-n,
    mit p und n = 1 bis 3 gleich oder verschieden,
    mit X = Alkoxy, insbesondere Methoxy, Ethoxy oder/und Propoxy,
    mit Y als funktionellen organischen Gruppen ausgewählt aus der Gruppe von Alkyl, Acrylat, Amino, Epoxy, Glycidoxy, Harnstoff, Isocyanat, Mercapto, Methacrylat, Schwefel Sq mit q = 1 bis 20 und Vinyl
    und mit Z' = N-Si-XrY3-r mit r = 1 bis 3,
  • - Multi-Silane der allgemeinen Formel Y3-pXpSi-Z"-Si-XnY3-n
    mit p und n = 1 bis 3 gleich oder verschieden,
    mit X = Alkoxy, insbesondere Methoxy, Ethoxy oder/und Propoxy,
    mit Y als funktionellen organischen Gruppen ausgewählt aus der Gruppe von Alkyl, Acrylat, Amino, Epoxy, Glycidoxy, Harnstoff, Isocyanat, Mercapto, Methacrylat, Schwefel Sq mit q = 1 bis 20 und Vinyl
    und mit Z" = -R-C[(SiXsY3-s)(SiXtY3-t)]-R'-,
    mit s und t = 1 bis 3 gleich oder verschieden,
    mit R und R' gleich oder verschieden ausgewählt aus der Gruppe von CnH2n
    mit n = 2 bis 20 jeweils verzweigt oder unverzweigt, von einfach ungesättigte Alkylketten der allgemeinen Formel CnH2n-2 mit n = 2 bis 20 jeweils verzweigt oder unverzweigt, von zweifach oder/und mehrfach ungesättigten Alkyl- Verbindungen der allgemeinen Formeln CnH2n-4 mit n = 4 bis 20 jeweils verzweigt oder unverzweigt, CnH2n-6 mit n = 6 bis 20 jeweils verzweigt oder unverzweigt bzw. CnH2n-8 mit n = 8 bis 20 jeweils verzweigt oder unverzweigt, von Ketonen, Monoalkylaminen, Ethylen und NH,
wobei die Silane jeweils hydrolysiert, teilhydrolysiert oder/und nicht hydrolysiert in einer Lösung, Emulsion oder/und Suspension vorliegen können.10. The method according to at least one of claims 1 to 6, characterized in that the agent for treatment or pretreatment, which is optionally also a lubricant, contains at least one silane, in particular at least one compound selected from the group of mono-, bis and multi-silanes, in particular:
  • - Monosilanes of the general formula SiX m Y 4-m
    with m = 1 to 3, preferably m = 2 to 3,
    with X = alkoxy, in particular methoxy, ethoxy and / or propoxy, and
    with Y as a functional organic group selected from the group of alkyl, acrylate, amino, epoxy, glycidoxy, urea, isocyanate, mercapto, methacrylate and / or vinyl,
  • Bis-silanes of the general formula Y 3 -p X p -Si-Z-Si-X n Y 3-n
    with p and n = 1 to 3 the same or different,
    with X = alkoxy, in particular methoxy, ethoxy and / or propoxy,
    with Y as functional organic groups selected from the group of alkyl, acrylate, amino, epoxy, glycidoxy, urea, isocyanate, mercapto, methacrylate, sulfur S q with q = 1 to 20 and vinyl,
    with Z selected from the group of C n H 2n with n = 2 to 20 each branched or unbranched, from monounsaturated alkyl chains of the general formula C n H 2n-2 with n = 2 to 20 each branched or unbranched, from double or / and polyunsaturated alkyl compounds of the general formulas C n H 2n-4 with n = 4 to 20 each branched or unbranched, C n H 2n-6 with n = 6 to 20 each branched or unbranched or C n H 2n-8 with n = 8 to 20 each branched or unbranched, of ketones, monoalkylamines, ethylene and NH,
  • Multi-silanes of the general formula Y 3-p X p -Si-Z'-Si-X n Y 3-n ,
    with p and n = 1 to 3 the same or different,
    with X = alkoxy, in particular methoxy, ethoxy and / or propoxy,
    with Y as functional organic groups selected from the group of alkyl, acrylate, amino, epoxy, glycidoxy, urea, isocyanate, mercapto, methacrylate, sulfur S q with q = 1 to 20 and vinyl
    and with Z '= N-Si-X r Y 3-r with r = 1 to 3,
  • - Multi-silanes of the general formula Y 3-p X p Si-Z "-Si-X n Y 3-n
    with p and n = 1 to 3 the same or different,
    with X = alkoxy, in particular methoxy, ethoxy and / or propoxy,
    with Y as functional organic groups selected from the group of alkyl, acrylate, amino, epoxy, glycidoxy, urea, isocyanate, mercapto, methacrylate, sulfur S q with q = 1 to 20 and vinyl
    and with Z "= -RC [(SiX s Y 3-s ) (SiX t Y 3-t )] - R'-,
    with s and t = 1 to 3 the same or different,
    with R and R 'selected identically or differently from the group of C n H 2n
    with n = 2 to 20 each branched or unbranched, from monounsaturated alkyl chains of the general formula C n H 2n-2 with n = 2 to 20 each branched or unbranched, from mono- or / and polyunsaturated alkyl compounds of the general formulas C n H 2n-4 with n = 4 to 20 each branched or unbranched, C n H 2n-6 with n = 6 to 20 each branched or unbranched or C n H 2n-8 with n = 8 to 20 each branched or unbranched, of ketones, monoalkylamines, ethylene and NH,
wherein the silanes can each be hydrolyzed, partially hydrolyzed or / and not hydrolyzed in a solution, emulsion or / and suspension. 11. Verfahren nach mindestens einem der Ansprüche 1 bis 6, dadurch gekennzeichnet, daß das Mittel zur Behandlung bzw. Vorbehandlung, das ggf. ein Gleitmittel ist, mindestens eine Verbindung des Typs XYZ, X*Y*Z* oder/und X*Y*Z*Y*X* enthält,
wobei Y eine organische Gruppe mit 2 bis 50 C Atomen ist,
wobei X und Z gleich oder verschieden eine OH-, SH-, NH2-, NHR'-, CN-, CH=CH2-, OCN-, CONHOH-, COOR'-, Acrylsäureamid-, Epoxy-, CH2=CR"-COO-, COOH-, HSO3-, HSO4-, (OH)2PO-, (OH)2PO2-, (OH)(OR')PO-, (OH)(OR')PO2-, SiH3- oder/und eine Si(OH)3-Gruppe sind,
wobei R' eine Alkylgruppe mit 1 bis 4 C-Atomen ist,
wobei R" ein H-Atom oder eine Alkylgruppe mit 1 bis 4 C-Atomen ist und wobei die Gruppen X und Z jeweils an die Gruppe Y in ihrer Endstellung gebunden sind,
wobei Y* eine organische Gruppe mit 1 bis 30 C-Atomen ist,
wobei X* und Z* gleich oder verschieden eine OH-, SH-, NH2-, NHR'-, CN-, CH=CH2-, OCN-, CONHOH-, COOR'-, Acrylsäureamid-, Epoxy-, CH2=CR"-COO-, COOH-, HSO3-, HSO4-, (OH)2PO-, (OH)2PO2-, (OH)(OR')PO-, (OH)(OR')PO2-, SiH3-, Si(OH)3, <N-CH2-PO(OH)2- oder/und eine -N-[CH2-PO(OH)2]2-Gruppe sind,
wobei R' eine Alkylgruppe mit 1 bis 4 C-Atomen ist und
wobei R" ein H-Atom oder eine Alkylgruppe mit 1 bis 4 C-Atomen ist.11. The method according to at least one of claims 1 to 6, characterized in that the agent for treatment or pretreatment, which is optionally a lubricant, at least one compound of the type XYZ, X * Y * Z * or / and X * Y * Z * Y * X * contains
where Y is an organic group with 2 to 50 C atoms,
where X and Z are identical or different OH, SH, NH 2 , NHR ', CN, CH = CH 2 , OCN, CONHOH, COOR', acrylic acid amide, epoxy, CH 2 = CR "-COO-, COOH-, HSO 3 -, HSO 4 -, (OH) 2 PO-, (OH) 2 PO 2 -, (OH) (OR ') PO-, (OH) (OR') PO 2 -, SiH 3 - and / or an Si (OH) 3 group,
where R 'is an alkyl group with 1 to 4 carbon atoms,
where R "is an H atom or an alkyl group having 1 to 4 C atoms and where the groups X and Z are each bound to the group Y in their end position,
where Y * is an organic group with 1 to 30 C atoms,
where X * and Z *, the same or different, are OH, SH, NH 2 , NHR ', CN, CH = CH 2 , OCN, CONHOH, COOR', acrylic acid amide, epoxy, CH 2 = CR "-COO-, COOH-, HSO 3 -, HSO 4 -, (OH) 2 PO-, (OH) 2 PO 2 -, (OH) (OR ') PO-, (OH) (OR' ) PO 2 -, SiH 3 -, Si (OH) 3 , <N-CH 2 -PO (OH) 2 - or / and a -N- [CH 2 -PO (OH) 2 ] 2 group,
where R 'is an alkyl group having 1 to 4 carbon atoms and
where R "is an H atom or an alkyl group having 1 to 4 C atoms. 12. Verfahren nach mindestens einem der Ansprüche 1 bis 6 oder/und 11, dadurch gekennzeichnet, daß das Mittel zur Behandlung bzw. Vorbehandlung, das ggf. ein Gleitmittel ist, mindestens eine Verbindung des Typs XYZ enthält, wobei X eine COOH-, HSO3-, HSO4-, (OH)2PO-, (OH)2PO2-, (OH)(OR')PO- oder (OH)(OR')PO2-Gruppe ist,
wobei Y eine organische Gruppe R ist, die 2 bis 50 C-Atome enthält, von denen mindestens 60% dieser C-Atome als CH2-Gruppen vorliegen,
wobei Z eine OH-, SH-, NH2-, NHR'-, CN-, CH=CH2-, OCN-, Epoxy-, CH=CR"- COOH-, Acrylsäureamid-, COOH-, (OH)2PO-, (OH)2PO2-, (OH)(OR')PO- oder (OH)(OR')PO2-Gruppe ist,
wobei R' eine Alkylgruppe mit 1 bis 4 C-Atomen ist
und wobei R" ein H-Atom oder eine Alkylgruppe mit 1 bis 4 C-Atomen ist.12. The method according to at least one of claims 1 to 6 or / and 11, characterized in that the agent for treatment or pretreatment, which is optionally a lubricant, contains at least one compound of the type XYZ, where X is a COOH, HSO 3 -, HSO 4 -, (OH) 2 PO-, (OH) 2 PO 2 -, (OH) (OR ') PO or (OH) (OR') PO 2 group,
where Y is an organic group R which contains 2 to 50 C atoms, of which at least 60% of these C atoms are present as CH 2 groups,
where Z is OH, SH, NH 2 , NHR ', CN, CH = CH 2 , OCN, epoxy, CH = CR "-COOH, acrylic acid amide, COOH, (OH) 2 Is PO-, (OH) 2 PO 2 -, (OH) (OR ') PO or (OH) (OR') PO 2 group,
where R 'is an alkyl group with 1 to 4 carbon atoms
and wherein R "is an H atom or an alkyl group having 1 to 4 C atoms. 13. Verfahren nach Anspruch 11, dadurch gekennzeichnet, daß die Gruppen X* und Z* der Verbindung des Typs X*Y*Z* oder/und X*Y*Z*Y*X* jeweils an die Gruppe Y* in ihrer Endstellung gebunden sind.13. The method according to claim 11, characterized in that the groups X * and Z * of the type X * Y * Z * or / and X * Y * Z * Y * X * connection to the group Y * are bound in their end position. 14. Verfahren nach mindestens einem der Ansprüche 11 bis 13, dadurch gekennzeichnet, daß die Verbindung des Typs XYZ, X*Y*Z* oder/und X*Y*Z*Y*X* geeignet ist, selbst anordnende Moleküle auszubilden, die eine Schicht dieser selbst anordnenden Moleküle auf der metallischer Oberfläche formen können, insbesondere eine monomolekulare Schicht. 14. The method according to at least one of claims 11 to 13, characterized characterized in that the connection of the type XYZ, X * Y * Z * or / and X * Y * Z * Y * X * is suitable for forming self-assembling molecules, the one Layer of these self-assembling molecules on the metallic surface can form, especially a monomolecular layer.   15. Verfahren nach mindestens einem der Ansprüche 11 bis 14, dadurch gekennzeichnet, daß Y oder Y* eine lineare unverzweigte Gruppe ist.15. The method according to at least one of claims 11 to 14, characterized characterized in that Y or Y * is a linear unbranched group. 16. Verfahren nach mindestens einem der Ansprüche 11 bis 14, dadurch gekennzeichnet, daß Y oder Y* eine lineare, verzweigte Gruppe mit wenigstens einer funktionellen Gruppe ist. (vorzugsweise eine mit wenigstens einer Alkylgruppe und/oder einer aromatischen Gruppe verzweigte Gruppe.)16. The method according to at least one of claims 11 to 14, characterized characterized in that Y or Y * is a linear, branched group with at least a functional group. (preferably one with at least one Alkyl group and / or an aromatic group branched group.) 17. Verfahren nach mindestens einem der Ansprüche 11 bis 16, dadurch gekennzeichnet, daß die wirksameren Verbindungen des Typs XYZ, X*Y*Z* oder/und X*Y*Z*Y*X* eine Gruppe Y oder Y* aufweist, die eine gerade Zahl von C-Atomen hat.17. The method according to at least one of claims 11 to 16, characterized characterized in that the more active compounds of the type XYZ, X * Y * Z * or / and X * Y * Z * Y * X * has a group Y or Y * that is an even number of Has C atoms. 18. Verfahren nach mindestens einem der Ansprüche 11 bis 17, dadurch gekennzeichnet, daß mindestens eine Verbindung des Typs XYZ, X*Y*Z* oder/und X*Y*Z*Y*X* in einer wässerigen Lösung als Salz oder/und Säure vorliegt.18. The method according to at least one of claims 11 to 17, characterized characterized in that at least one connection of the type XYZ, X * Y * Z * or / and X * Y * Z * Y * X * in an aqueous solution as a salt and / or acid is present. 19. Verfahren nach mindestens einem der Ansprüche 11 bis 18, dadurch gekennzeichnet, daß die Gruppe Y oder Y* der wirksameren Verbindungen des Typs XYZ, X*Y*Z* oder/und X*Y*Z*Y*X* eine unverzweigte geradkettige Alkylgruppe mit 3 bis 30 C Atomen ist.19. The method according to at least one of claims 11 to 18, characterized characterized in that the group Y or Y * of the more effective compounds of Types XYZ, X * Y * Z * or / and X * Y * Z * Y * X * an unbranched straight-chain Is alkyl group with 3 to 30 C atoms. 20. Verfahren nach mindestens einem der Ansprüche 11 bis 19, dadurch gekennzeichnet, daß das Mittel zur Behandlung bzw. Vorbehandlung mindestens eine Verbindung des Typs XYZ, X*Y*Z* oder/und X*Y*Z*Y*X* enthält, bei der Y oder Y* eine unverzweigte Alkylgruppe mit 2 bis 20 C-Atomen oder eine unverzweigte, aus 1 bis 4 aromatischen, in p-Stellung verbundenen C6H4- Kernen bestehende Gruppe oder eine aus 1 oder 2 unverzweigten Alkylresten mit jeweils 1 bis 20 C-Atomen sowie 1 bis 4 aromatischen, in p-Stellung verbundenen C6H4-Kernen bestehende Gruppe ist.20. The method according to at least one of claims 11 to 19, characterized in that the agent for treatment or pretreatment contains at least one compound of the type XYZ, X * Y * Z * or / and X * Y * Z * Y * X * , in which Y or Y * is an unbranched alkyl group with 2 to 20 C atoms or an unbranched group consisting of 1 to 4 aromatic C 6 H 4 nuclei connected in the p-position or one or 1 or 2 unbranched alkyl radicals each with 1 to 20 carbon atoms and 1 to 4 aromatic, 6 -linked C 6 H 4 nuclei group. 21. Verfahren nach mindestens einem der Ansprüche 11 bis 20, dadurch gekennzeichnet, daß das Mittel zur Behandlung bzw. Vorbehandlung mindestens eine Verbindung des Typs XYZ, X*Y*Z* oder/und X*Y*Z*Y*X* enthält, bei der Y oder Y* eine unverzweigte Alkylgruppe mit 6 bis 20 oder vorzugsweise mit 10 bis 18 C-Atomen oder eine p-CH2-C4H6-CH2-Gruppe oder eine p,p'-C6H4-C6H4- Gruppe ist.21. The method according to at least one of claims 11 to 20, characterized in that the agent for treatment or pretreatment contains at least one compound of the type XYZ, X * Y * Z * or / and X * Y * Z * Y * X * , in which Y or Y * is an unbranched alkyl group having 6 to 20 or preferably having 10 to 18 C atoms or a p-CH 2 -C 4 H 6 -CH 2 group or a p, p'-C 6 H 4 -C 6 H 4 group. 22. Verfahren nach mindestens einem der Ansprüche 11 bis 21, dadurch gekennzeichnet, daß das Mittel zur Behandlung bzw. Vorbehandlung mindestens eine Verbindung des Typs XYZ, X*Y*Z* oder/und X*Y*Z*Y*X* enthält, bei der X oder X* eine (OH)2PO2- oder (OH)(OR')PO2-Gruppe ist.22. The method according to at least one of claims 11 to 21, characterized in that the agent for treatment or pretreatment contains at least one compound of the type XYZ, X * Y * Z * or / and X * Y * Z * Y * X * , in which X or X * is an (OH) 2 PO 2 or (OH) (OR ') PO 2 group. 23. Verfahren nach mindestens einem der Ansprüche 11 bis 22, dadurch gekennzeichnet, daß das Mittel zur Behandlung bzw. Vorbehandlung mindestens eine Verbindung des Typs XYZ, X*Y*Z* oder/und X*Y*Z*Y*X* enthält, bei der Z oder Z* eine (OH)2PO2-, (OH)(OR')PO2-, OH-, SH-, NHR'-, CH=CH2- oder CH=CR"-COOH-Gruppe ist.23. The method according to at least one of claims 11 to 22, characterized in that the agent for treatment or pretreatment contains at least one compound of the type XYZ, X * Y * Z * or / and X * Y * Z * Y * X * , where Z or Z * is an (OH) 2 PO 2 -, (OH) (OR ') PO 2 -, OH-, SH-, NHR'-, CH = CH 2 - or CH = CR "-COOH- Group is. 24. Verfahren nach mindestens einem der Ansprüche 11 bis 23, dadurch gekennzeichnet, daß das Mittel zur Behandlung bzw. Vorbehandlung mindestens eine der folgenden Verbindungen des Typs XYZ, X*Y*Z* oder/und X*Y*Z*Y*X* enthält:
1-Phosphonsäure-12-mercaptododecan,
1-Phosphonsäure-12-(N-ethylamino)dodecan,
1-Phosphonsäure-12-dodecen,
p-Xylylen-diphosphonsäure,
1,10-Decandiphosphonsäure,
1,12-Dodecandiphosphonsäure,
1,14-Tetradecandiphosphonsäure,
1-Phosphorsäure-12-hydroxydadecan,
1-Phosphorsäure-12-(N-ethylamino)dodecan,
1-Phosphorsäure-12-dodecen,
1-Phosphorsäure-12-mercaptododecan,
1,10-Decandiphosphorsäure,
1,12-Dodecandiphosphorsäure,
1,14-Tetradecandiphosphorsäure,
p,p'-Biphenyldiphosphorsäure,
1-Phosphorsäure-12-Acryloyldodecan,
1,8-Octandiphosphonsäure,
1,6-Hexandiphosphonsäure,
1,4-Butandiphosphonsäure,
1,8-Octandiphosphorsäure,
1,6-Hexandiphosphorsäure,
1,4-Butandiphosphorsäure,
Aminotrimethylenphosphonsäure,
Ethylendiamintetramethylenphosphonsäure,
Hexamethylendiamintetramethylenphosphonsäure,
Diethylentriaminpentamethylenphosphonsäure,
2-Phosphonbutan-1,2,4-tricarboxylsäure.24. The method according to at least one of claims 11 to 23, characterized in that the agent for treatment or pretreatment at least one of the following compounds of the type XYZ, X * Y * Z * or / and X * Y * Z * Y * X * contains:
1-phosphonic acid-12-mercaptododecan,
1-phosphonic acid-12- (N-ethylamino) dodecane,
1-phosphonic acid-12-dodecene,
p-xylylene diphosphonic acid,
1,10-Decandiphosphonsäure,
1,12-dodecanediphosphonic acid,
1,14-Tetradecandiphosphonsäure,
1-phosphoric acid-12-hydroxydadecan,
1-phosphoric acid-12- (N-ethylamino) dodecane,
1-phosphoric acid-12-dodecene,
1-phosphoric acid-12-mercaptododecan,
1,10-Decandiphosphorsäure,
1,12-Dodecandiphosphorsäure,
1,14-Tetradecandiphosphorsäure,
p, p'-Biphenyldiphosphorsäure,
1-phosphoric acid-12-Acryloyldodecan,
1.8 Octandiphosphonsäure,
1,6-Hexandiphosphonsäure,
1,4-Butandiphosphonsäure,
1.8 Octandiphosphorsäure,
1,6-Hexandiphosphorsäure,
1,4-Butandiphosphorsäure,
aminotrimethylenephosphonic,
ethylene diamine,
Hexamethylendiamintetramethylenphosphonsäure,
diethylenetriaminepentamethylenephosphonic,
2-phosphonobutane-1,2,4-tricarboxylic acid. 25. Verfahren nach mindestens einem der Ansprüche 11 bis 24, dadurch gekennzeichnet, daß das Mittel zur Behandlung bzw. Vorbehandlung mit mindestens einer Verbindung des Typs XYZ, X*Y*Z* oder/und X*Y*Z*Y*X* in einer wässerigen Lösung enthalten ist, wobei insbesondere 0,01 bis 50% des Wassers durch einen Alkohol mit 1 bis 4 C-Atomen, durch Aceton, durch Dioxan oder/und durch Tetrahydrofuran ersetzt sein kann. (vorzugsweise 0,1 bis 50% des Wassers) 25. The method according to at least one of claims 11 to 24, characterized characterized in that the agent for treatment or pretreatment with at least one connection of the type XYZ, X * Y * Z * or / and X * Y * Z * Y * X * in an aqueous solution is contained, in particular 0.01 to 50% of the Water through an alcohol with 1 to 4 carbon atoms, through acetone, through dioxane or / and can be replaced by tetrahydrofuran. (preferably 0.1 to 50% of the water)   26. Verfahren nach mindestens einem der Ansprüche 11 bis 25, dadurch gekennzeichnet, daß das Mittel zur Behandlung bzw. Vorbehandlung mindestens eine Verbindung des Typs XYZ, X*Y*Z* oder/und X*Y*Z*Y*X* enthält, die im Bereich der kritischen Mizellbildungskonzentration oder unterhalb liegt, insbesondere bei einer Konzentration von 0,05 bis 10 g/L. (vorzugsweise 0,1 bis 3 g/L; besonders bevorzugt mit 50 bis 1000 mg/L, ganz besonders bevorzugt mit 100 bis 600 mg/L, wobei die Löslichkeitsgrenze z. B. bei der 1,2- Dodecandiphosphonsäure durch Zusatz von organischem Lösemittel signifikant gesteigert werden kann; insbesondere in 0,5 Sekunden bis 10 Minuten kontaktiert; insbesondere mit einem pH-Wert im Bereich von 1 bis 10, vorzugsweise im Bereich von 2 bis 4; bei der Beschichtung von Containern insbesondere Dosen wird vorzugsweise eine Mineralsäure wie z. B. Schwefelsäure zugegeben, so daß der pH-Wert dieser wässerigen Lösung dann vorzugsweise bei 0,5 bis 2,5 liegt; insbesondere durch Verwendung von vollentsalztem Wasser, das vorzugsweise eine elektrische Leitfähigkeit von ≦ 120 µS/cm, besonders bevorzugt von ≦ 20 µS/cm aufweist; die Belegung der Oberfläche mit mindestens einer der Verbindungen des Typs XYZ, X*Y*Z* oder/und X*Y*Z*Y*X* kann unvollständig sein oder/und diese Verbindung(en) muß/müssen nicht wie sonst bei selbst anordnenden Molekülen senkrecht zur Oberfläche und parallel zueinander ausgerichtet sein - dennoch ist eine hohe Wirksamkeit dieser Beschichtung gewährleistet; je länger die Oberfläche mit dem erfindungsgemäßen Mittel beschichtet wird, desto höher ist üblicher der Anteil der mit dieser/diesen Verbindung(en) beschichteten Oberfläche und desto eher sind ihre Moleküle senkrecht zur Oberfläche und parallel zueinander ausgerichtet.)26. The method according to at least one of claims 11 to 25, characterized characterized in that the agent for treatment or pretreatment at least contains a connection of the type XYZ, X * Y * Z * or / and X * Y * Z * Y * X *, which in the Range of critical micelle concentration or below especially at a concentration of 0.05 to 10 g / L. (preferably 0.1 to 3 g / L; particularly preferably with 50 to 1000 mg / L, very particularly preferably with 100 to 600 mg / L, the solubility limit z. B. at the 1,2- Significant dodecanediphosphonic acid by adding organic solvent can be increased; especially in 0.5 seconds to 10 minutes contacted; in particular with a pH in the range from 1 to 10, preferably in the range from 2 to 4; when coating containers especially cans is preferably a mineral acid such as. B. Sulfuric acid added so that the pH of this aqueous solution then preferably 0.5 to 2.5; especially by using demineralized water, which preferably has an electrical conductivity of ≦ 120 µS / cm, particularly preferably of ≦ 20 µS / cm; the occupancy of the Surface with at least one of the connections of the type XYZ, X * Y * Z * or / and X * Y * Z * Y * X * can be incomplete or / and this connection (s) must / do not have to be perpendicular to the self as in self-assembling molecules Surface and aligned parallel to each other - is still high Guaranteed effectiveness of this coating; the longer the surface with the agent according to the invention is coated, the higher the usual Proportion of the surface coated with this compound (s) and the more rather, their molecules are perpendicular to the surface and parallel to each other aligned.) 27. Verfahren nach mindestens einem der Ansprüche 11 bis 26, dadurch gekennzeichnet, daß das Mittel zur Behandlung bzw. Vorbehandlung mindestens eine Verbindung des Typs XYZ, X*Y*Z* oder/und X*Y*Z*Y*X* enthält, die in der Lösung als Salz vorliegt. 27. The method according to at least one of claims 11 to 26, characterized characterized in that the agent for treatment or pretreatment at least contains a connection of the type XYZ, X * Y * Z * or / and X * Y * Z * Y * X *, which in the Solution is present as a salt.   28. Verfahren nach mindestens einem der vorstehenden Ansprüche, dadurch gekennzeichnet, daß das Mittel zur Behandlung bzw. Vorbehandlung auch einen Entschäumer oder/und einen Lösungsvermittler enthält, insbesondere in einer Menge von jeweils 0,005 bis 5 Gew.-%. (vorzugsweise 0,1 bis 3 Gew.-%)28. The method according to at least one of the preceding claims, characterized characterized in that the agent for treatment or pretreatment also Defoamer and / or contains a solubilizer, especially in one Amount of 0.005 to 5 wt .-% each. (preferably 0.1 to 3% by weight) 29. Verfahren nach mindestens einem der vorstehenden Ansprüche, dadurch gekennzeichnet, daß das Mittel zur Behandlung bzw. Vorbehandlung durch Tauchen oder Walzen, vorzugsweise durch Spritzen, Sprühen oder Vernebeln, auf den Behältern innen oder/und außen aufgebracht wird, insbesondere über eine Zeit pro Behälter im Bereich von 0,5 bis 120 Sekunden. (vorzugsweise 1 bis 80 s, 1,5 bis 40 s, 2 bis 20 s)29. The method according to at least one of the preceding claims, characterized characterized in that the agent for treatment or pretreatment by Dipping or rolling, preferably by spraying, spraying or atomizing, is applied to the inside or / and outside of the containers, especially via a time per container in the range of 0.5 to 120 seconds. (preferably 1 to 80 s, 1.5 to 40 s, 2 to 20 s) 30. Verfahren nach mindestens einem der vorstehenden Ansprüche, dadurch gekennzeichnet, daß gegebenenfalls mindestens eine Spülung durchgeführt wird nach dem Aufbringen des Mittels zur Behandlung bzw. Vorbehandlung, das gleichzeitig auch ein Gleitmittel ist oder enthält.30. The method according to at least one of the preceding claims, characterized characterized in that at least one rinse is carried out if necessary after application of the agent for treatment or pretreatment, the is or contains a lubricant at the same time. 31. Verfahren nach mindestens einem der vorstehenden Ansprüche, dadurch gekennzeichnet, daß das Mittel zur Behandlung bzw. Vorbehandlung auf eine gereinigte, gespülte oder/und gebeizte Oberfläche oder auf eine vorgeglühte Oberfläche aufgebracht wird.31. The method according to at least one of the preceding claims, characterized characterized in that the agent for treatment or pretreatment to a cleaned, rinsed and / or pickled surface or on a preheated surface Surface is applied. 32. Verfahren nach mindestens einem der vorstehenden Ansprüche, dadurch gekennzeichnet, daß die Oberfläche des Behälters vor dem Aufbringen des Mittels zur Behandlung bzw. Vorbehandlung neutral, sauer oder alkalisch gereinigt wird, ggf. gespült wird, ggf alkalisch oder sauer gebeizt wird und ggf. erneut gespült wird, wobei als Lösemittel Wasser oder/und organisches Lösemittel eingesetzt werden kann.32. The method according to at least one of the preceding claims, characterized characterized in that the surface of the container before the application of the Agents for treatment or pretreatment neutral, acidic or alkaline is cleaned, if necessary rinsed, if necessary alkali or acid pickled and if necessary is rinsed again, water or / and organic as solvent Solvents can be used. 33. Verfahren nach mindestens einem der vorstehenden Ansprüche, dadurch gekennzeichnet, daß vor dem Aufbringen des Mittels zur Behandlung bzw. Vorbehandlung ein andersartiges Mittel zur Behandlung bzw. Vorbehandlung aufgebracht wird, insbesondere ein Mittel, das Ionen aus der Gruppe von Ti, Zr, Hf, Cu, Fe, Mn, Ni, Zn, PO4 und F enthält.33. The method according to at least one of the preceding claims, characterized in that before the application of the agent for treatment or pretreatment another type of agent for treatment or pretreatment is applied, in particular an agent which contains ions from the group of Ti, Zr, Hf , Cu, Fe, Mn, Ni, Zn, PO 4 and F. 34. Verfahren nach mindestens einem der vorstehenden Ansprüche, dadurch gekennzeichnet, daß nach dem Aufbringen des Mittels zur Behandlung bzw. Vorbehandlung ggf. gespült wird, ggf. mit einer Nachspüllösung nachgespült wird, ggf. erneut gespült wird und getrocknet wird, wobei als Lösemittel Wasser oder/und organisches Lösemittel eingesetzt werden kann.34. The method according to at least one of the preceding claims, characterized characterized in that after the application of the agent for treatment or Pretreatment is rinsed if necessary, if necessary rinsed with a rinse solution is optionally rinsed again and dried, using water as the solvent or / and organic solvent can be used. 35. Verfahren nach mindestens einem der vorstehenden Ansprüche, dadurch gekennzeichnet, daß nach dem Aufbringen des Mittels zur Behandlung bzw. Vorbehandlung nicht mehr gespült wird. (gilt für alle Getränkedosen mit Verbindungen des Typs XYZ, X*Y*Z* oder/und X*Y*Z*Y*X*, insbesondere mit SAM = selbst anordnenden Molekülen = self assembling molecules)35. The method according to at least one of the preceding claims, characterized characterized in that after the application of the agent for treatment or Pretreatment is no longer rinsed. (applies to all beverage cans with Compounds of the type XYZ, X * Y * Z * or / and X * Y * Z * Y * X *, in particular with SAM = self-assembling molecules) 36. Verfahren nach mindestens einem der vorstehenden Ansprüche, dadurch gekennzeichnet, daß mindestens eine Verbindung des Typs XYZ, X*Y*Z* oder/und X*Y*Z*Y*X* für die Verbesserung der Korrosionsbeständigkeit oder/und der Lackhaftung eingesetzt wird. (evtl. unabhängiger Anspruch?)36. The method according to at least one of the preceding claims, characterized characterized in that at least one connection of the type XYZ, X * Y * Z * or / and X * Y * Z * Y * X * for improving corrosion resistance or / and paint adhesion is used. (possibly independent claim?) 37. Verfahren nach mindestens einem der vorstehenden Ansprüche, dadurch gekennzeichnet, daß nach dem Trocknen des Mittels zur Behandlung bzw. Vorbehandlung mindestens ein Lack - insbesondere ein Elektro-tauchlack, Pulverlack, Coil-Coating-Lack, Naßlack, Lösemittel-armer High-Solid-Lack oder ein mit Wasser verdünnter Lack -, mindestens eine andersartige organische Beschichtung, mindestens eine Klebstoffschicht, mindestens eine Folie, mindestens eine Papierschicht oder/und mindestens eine Druckfarbe aufgebracht wird. 37. The method according to at least one of the preceding claims, characterized characterized in that after drying the agent for treatment or Pretreatment of at least one varnish - in particular an electro-dip varnish, Powder paint, coil coating paint, wet paint, low-solvent high-solid paint or a lacquer diluted with water, at least one different organic Coating, at least one adhesive layer, at least one film, at least one layer of paper and / or at least one printing ink is applied.   38. Mittel zur Behandlung oder Vorbehandlung von Behältern aus Aluminium, Aluminium-haltigen Legierungen, Magnesium-haltigen Legierungen, Silizium­ haltigen Legierungen, Weißblech, Stahl oder Kunststoff, insbesondere von Dosen, Flaschen oder Beuteln, dadurch gekennzeichnet, daß es gleichzeitig ein Mittel zur Behandlung bzw. Vorbehandlung und ein Gleitmittel ist oder/und enthält.38. agents for treating or pretreating aluminum containers, Aluminum-containing alloys, magnesium-containing alloys, silicon containing alloys, tinplate, steel or plastic, especially from Cans, bottles or bags, characterized in that it is a Treatment or pretreatment agent and a lubricant is or / and contains.
DE10049005A 2000-05-31 2000-09-27 Treating or pre-treating containers made e.g. of aluminum and aluminum-containing alloys, comprises applying lubricating agent during treatment or pre-treatment Withdrawn DE10049005A1 (en)