CN214299906U - 一种海洋防污涂层 - Google Patents
一种海洋防污涂层 Download PDFInfo
- Publication number
- CN214299906U CN214299906U CN202022066734.3U CN202022066734U CN214299906U CN 214299906 U CN214299906 U CN 214299906U CN 202022066734 U CN202022066734 U CN 202022066734U CN 214299906 U CN214299906 U CN 214299906U
- Authority
- CN
- China
- Prior art keywords
- antifouling
- marine
- film
- coating
- utility
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本实用新型涉及一种海洋防污涂层，包括基底和防污层，所述防污层由三维网状的溶蚀性薄膜和充填在溶蚀性薄膜的防污剂组成。本实用新型的防污剂随着溶蚀性薄膜的可控溶蚀，不断释放出足够浓度的铜、银等离子，有效杀菌寿命长，对环境友好无害，有效防治多种海洋生物侵袭。本实用新型海洋防污涂层还可对混凝土微小裂缝进行有效修复，进而提高混凝土抗渗能力，具有很好的实用价值。
Description
技术领域
本实用新型属于涂料技术领域，具体涉及一种海洋防污涂层，可用于滨海电厂处于海水环境下的工程结构表面抗海洋生物污损防护。
背景技术
海洋生物污损是指海洋环境中微生物、植物、动物在被海水浸没的设施表面不断粘附、生长、繁殖而形成的生物附着或生物腐蚀。海洋生物污损已成为人类开发、利用海洋资源所面临的全球性问题，其对港口和滨海电厂水下设施等造成了巨大的技术挑战和经济损失。据估计，每年因海洋生物污损所造成的经济成本高达65亿美元。海洋污损生物种类较多，归纳起来可分为三类：(1)微污损生物(细菌类、真菌类、硅藻微小海藻等)；(2)软性污损生物(大型海藻等)；(3)硬性污损生物(贝类、藤壶、苔藓虫类等)。相关资料显示，当材料浸入海水中，其表面会很快吸附一层由多聚糖、蛋白质、糖蛋白等组成的有机物膜；然后由单细胞微生物如细菌、硅藻和原生动物等相继在有机物膜上附着并分泌胞外代谢产物(EPS)形成微生物膜；随后其它原核生物、真菌、藻类孢子以及大型污损生物幼虫在膜中发育生长；最后形成复杂的生物群落和大型污损生物层。
目前，针对于海水下静态设施的防污技术归纳起来可分为三种：(1)物理滤沥、清除法，(2)直接化学灭活法，(3)海洋防污涂层涂覆。物理滤沥、清除法主要是通过机械设备来清除污损物，效率低且成本高昂；化学直接灭活法是直接向防护对象附近的海水中释放具有强氧化性和毒理性的化学试剂，除污损效果好，但易造成海水环境污染；海洋防污涂层涂覆是研究最早，也是目前应用最广泛的抗海洋生物附着的方法。通常，防污涂料主要由高分子树脂、防污剂、溶剂等组成。但传统有机型防污涂料污染海水环境，分解产物易造成“微塑料”污染，且在流动海水冲蚀条件下防污寿命低。
实用新型内容
本实用新型的目的在于提供一种海洋防污涂层，具有高效耐久抗海洋生物污损的特点，以解决现有技术存在的问题。
一种海洋防污涂层，包括基底和防污层，所述防污层由三维网状的溶蚀性薄膜和充填在溶蚀性薄膜的防污剂组成。
优选的，所述溶蚀性薄膜为硅酸钠与聚合磷酸铝的反应形成。
优选的，所述溶蚀性薄膜内还填充有Al2(Si2O5)(OH)4。Al2(Si2O5)(OH)4作为无机填料加入配方中，能给涂层提供强度，提高涂层耐磨性能。在硅酸钠与聚合磷酸铝固化而成的膜层包裹下，协同形成具有一定溶蚀性的无机薄膜。
优选的，所述防污剂包括质量比为2：1：1：1的Cu2O、CuO、TiO2和Ag2O。Cu2O和TiO2可与吸附在其表面的H2O和O2形成活性很强的羟基自由基和活性氧，这种自由基具有很强的氧化和分解能力，能破坏有机物中C—C、C—H、C—O、O—H键，凝固微生物的蛋白质，对海洋生物细胞膜产生酶抑制作用，从而灭杀附着在其表面的海洋生物，其中对藤壶、贝类、苔藓虫等无脊椎动物特别有效。Cu2O、CuO、Ag2O的离子可与半胱氨酸的—SH基反应，导致藻类中以—SH基为活性点的酶失活，同时还能对藻类的细胞壁、细胞膜的结构造成不可逆损伤，有效防止藻类附着。
优选的，所述防污剂中位粒径为80～150nm。粒径太大，比表面积就会过小，起不到吸附—SH、—COOH等基团的作用；粒径过小，价格高，不经济。复合防污剂中位粒径在80～150nm时具有极大的比表面积，且表面还原电势高，可以吸附细菌体内酶蛋白分子中的—SH、—COOH等基团，并与之反应，阻碍蛋白质的合成和能量来源，破坏了细菌的细胞膜，致使细菌死亡，从而有效防止海洋生物附着、生长。同时，在同样的含量系，纳米颗粒防污剂更有利于在海水条件下保持较高的有效离子浓度。
优选的，所述基底包括陶瓷基材和混凝土基材。
与现有技术相比，本实用新型通过在工程基材表面涂覆高效持久的抗污损功能、耐腐蚀、对环境友好的抗污损涂料，达到预防基材浸蚀和防止海洋生物附着污损的目的。本实用新型以硅酸钠作为粘结材料，通过与聚合磷酸铝的反应，辅以无机填料Al2(Si2O5)(OH)4形成具有一定溶蚀性的无机薄膜，在海水冲蚀下，复合防污剂随着无机薄膜的可控溶蚀，不断释放出足够浓度的铜、银等离子，有效杀菌寿命长，对环境友好无害，有效防治多种海洋生物侵袭。本实用新型海洋防污涂层还可对混凝土微小裂缝进行有效修复，进而提高混凝土抗渗能力，具有很好的实用价值。
附图说明
图1是一种海洋防污涂层示意图，1-基底，2-防污层；图2是防污层三维立体结构示意图，3-溶蚀性薄膜。
具体实施方式
为使本实用新型的目的、技术方案和优点更加清楚，下面将结合附图对本实用新型作进一步地详细描述。
实施例1：
一种海洋防污涂层，如图1所示包括陶瓷基底1和防污层2，所述防污层2由三维网状的溶蚀性薄膜3和充填在溶蚀性薄膜的防污剂组成。溶蚀性薄膜由硅酸钠与聚合磷酸铝的反应形成，溶蚀性薄膜内还填充有Al2(Si2O5)(OH)4。防污剂包括质量比为2：1：1：1的Cu2O、CuO、TiO2和Ag2O；所述防污剂中位粒径为80～150nm。
本实施例的海洋防污涂层的制备方法为：按比例称取硅酸钠15g和中位粒径80nm的复合防污剂25g混合搅拌均匀，复合防污剂包括Cu2O 10g、CuO 5g、TiO2 5g、Ag2O 5g，得到A组分；按比例称取聚合磷酸铝10g、增稠剂海藻酸钠1g、羟乙基纤维素1g，Al2(Si2O5)(OH)420g、分散剂木质素磺酸钙3g，混合搅拌均匀，得到B组分；将A组分和B组分机械搅拌混匀，按比例加入C组分水25g，机械搅拌混匀，得到海洋防污涂层。将所得的海洋防污涂层均匀涂刷在陶瓷基材表面，待其自然固化成型后，在陶瓷基体表面形成均匀、致密的涂层，可有效抗海洋生物污损，保护海水浸没结构表面不受海洋生物侵袭。得到的抗海洋生物污损涂层在2年左右溶蚀掉。
实施例2：
一种海洋防污涂层，如图1所示包括混凝土基底1和防污层2，所述防污层2由三维网状的溶蚀性薄膜3和充填在溶蚀性薄膜的防污剂组成。溶蚀性薄膜由硅酸钠与聚合磷酸铝的反应形成，溶蚀性薄膜内还填充有Al2(Si2O5)(OH)4。
防污剂包括质量比为2：1：1：1的Cu2O、CuO、TiO2和Ag2O；所述防污剂中位粒径为80～150nm。
本实施例的海洋防污涂层的制备方法为：按照实施例1的方法制备得到海洋防污涂层。
将所得的海洋防污涂层喷涂在混凝土基材表面，待其自然固化成型后，在混凝土基体表面形成均匀、致密的涂层，可有效抗海洋生物污损，保护海水浸没结构表面不受海洋生物侵袭。还能阻隔减缓海水对基体的腐蚀。得到的抗海洋生物污损涂层在2年左右溶蚀掉。
表1实施例1-2的海洋防污涂层的性能对比
以上所述实施例仅表达了本实用新型的几种实施方式，其描述较为具体和详细，但并不能因此而理解为对发明专利范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本实用新型构思的前提下，还可以做出若干变形和改进，这些都应落入本实用新型的保护范围。
Claims (2)
1.一种海洋防污涂层，其特征在于，包括基底和防污层，所述防污层由三维网状的溶蚀性薄膜和充填在溶蚀性薄膜的防污剂组成。
2.根据权利要求1所述海洋防污涂层，其特征在于，所述防污剂中位粒径为80～150nm。