CN1939871A - 一种不裂建筑砂浆 - Google Patents
一种不裂建筑砂浆 Download PDFInfo
- Publication number
- CN1939871A CN1939871A CN 200510030034 CN200510030034A CN1939871A CN 1939871 A CN1939871 A CN 1939871A CN 200510030034 CN200510030034 CN 200510030034 CN 200510030034 A CN200510030034 A CN 200510030034A CN 1939871 A CN1939871 A CN 1939871A
- Authority
- CN
- China
- Prior art keywords
- cracking
- mortar
- construction
- building mortar
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种建筑内外墙用砌筑或抹面不裂砂浆及其制备方法领域。本发明所述的不裂建筑砂浆，各组份的质量份数如下：水泥20－35、矿物掺合料2－20、建筑用砂60－75、纤维素醚0.02－0.2、有机纤维0.1－0.2。本发明所述的不裂建筑砂浆在施工规范情况下，可以完全防止内外墙的开裂，同时具有良好的和易性和保水性，硬化后与墙体材料或其他基体具有较高的粘结力。对施工者来说，除了配料快以外，还具有施工快和质量保证的诸多优点。本发明所述的不裂建筑砂浆可以适用于不同墙体材料的砌筑，内外墙的抹面等工程领域。
Description
技术领域
本发明涉及一种建筑工程用不裂砂浆，具体的讲涉及一种建筑内外墙用砌筑或抹面不裂砂浆及其制备方法领域。
背景技术
对于建筑工程中应用的墙体材料，无论是承重墙，还是框架结构中的填充墙，普遍存在严重的墙体开裂和渗漏问题，严重影响了工程质量和正常使用。对控制墙体开裂，目前主要采用构造措施，但效果不尽理想；而外墙渗漏问题则主要采用防水涂料等方法，不仅成本较高，且一旦外墙开裂，防水涂料也不能解决这一问题。可以说，对墙体材料应用中出现的开裂和渗漏问题，至今尚无有效措施加以控制。
墙体材料开裂的主要原因，除了地基不均匀沉降等引起的结构裂缝外，主要可以归结为以下两方面：一是自身收缩比传统的实心粘土砖大。二是采用传统水泥砂浆或混合砂浆自身收缩大、粘结强度低及匹配不合理。
承重墙用混凝土砌块的强度等级一般要求MU10以上，标准砌块的空洞率约为60％以上，亦即实际承重肋的面积小于40％，相当于混凝土实际强度达到25MPa以上，而砌筑砂浆的强度一般为10MPa。因此，从强度匹配上来看，不尽合理，而且墙体砌块与砂浆之间的粘结强度的严重不足。另一方面，砌块自身的收缩比粘土砖大，且砌体吸水率比砖小，砂浆自身收缩大，因此砌块建筑容易出现阶梯裂缝。
针对目前墙体中存在的上述问题，尤其新型墙体材料，开发出具有高施工性、高粘聚性、高粘结强度、高抗裂性的砂浆具有重要的工程应用价值与社会意义。
发明内容
本发明的目的就是克服现有的上述问题，提供一种具有高粘聚性、高粘结强度、高抗裂性的建筑砂浆。调整砂浆的配合比，可以配制不裂抹面砂浆与砌筑砂浆等。
为了实现上述目的，本发明的技术方案是：
一种不裂建筑砂浆，各组份的质量份数如下：
水泥 20-35
矿物掺合料 2-20
建筑用砂 60-75
纤维素醚 0.02-0.2
有机纤维 0.1-0.2。
本发明所述的不裂建筑砂浆，其中所说的水泥可以为硅酸盐水泥、普通硅酸盐水泥、矿渣或火山灰硅酸盐水泥，但强度应不低于42.5强度等级。
本发明所述的不裂建筑砂浆，其中所说的矿物掺合料可以是粉煤灰、磨细水淬高炉矿渣，或石灰石粉，细度应在100目或以下。
本发明所述的不裂建筑砂浆，其中所说的建筑用砂可以采用普通黄砂或河砂。
本发明所述的不裂建筑砂浆，其中所说的纤维素醚可为工业级的产品，其粘度在100-60000Pa·s之间。如羟乙基甲基纤维素、甲基纤维素等。
本发明所述的不裂建筑砂浆，其中所说的有机纤维可以是聚丙烯纤维、聚丙烯酰胺纤维，也可以是尼龙-6等，纤维的单丝长度为12mm±3mm。
本发明所述的不裂建筑砂浆，其中掺加的纤维素醚与有机纤维产生协同作用，使得砂浆具有较高的粘结强度与抗裂性。
本发明所述的不裂建筑砂浆制备方法如下：
按上述给定组份的质量份数称量出各原材料，然后将其搅拌均匀即可形成预混不裂建筑砂浆。一般搅拌3分钟即可。将此不裂建筑砂浆在施工前加入拌和水，搅拌2分钟就可使用。
本发明的有益效果：
1.本发明所述的不裂建筑砂浆在施工规范情况下，可以完全防止内外墙的开裂。
2.本发明所述的不裂建筑砂浆具有良好的和易性和保水性，硬化后与墙体材料或其他基体具有较高的粘结力。
3.对施工者来说，除了配料快以外，还具有施工快和质量保证的诸多优点。
4.本发明所述的不裂建筑砂浆可以适用于不同墙体材料的砌筑，内外墙的抹面等工程领域。
具体实施方式
实施例1～3
按表一给定组份的质量份数称量出各原材料，然后将其搅拌3分钟，形成预混不裂建筑砂浆。
其中实施例1所用的水泥是强度不低于42.5的硅酸盐水泥；矿物掺合料为细度100目以下的石灰石粉；纤维素醚为羟乙基甲基纤维素；有机纤维为聚丙烯纤维，单丝长度12mm。
实施例2所用的水泥是强度不低于42.5的硅酸盐水泥；矿物掺合料为细度100目以下的粉煤灰，纤维素醚为甲基纤维素；有机纤维为聚丙烯纤维，单丝长度12mm。
实施例3所用的水泥是强度不低于42.5的火山灰硅酸盐水泥；矿物掺合料为细度目的矿渣，纤维素醚为羟乙基甲基纤维素；有机纤维为聚丙烯纤维，单丝长度12mm。
将此不裂建筑砂浆在施工前加入拌和水，搅拌2分钟就可使用。
表一
| 组份 | 实施例1 | 实施例2 | 实施例3 |
| 水泥 | 31.8 | 22.8 | 20.0 |
| 矿物掺合料 | 3.3 | 2.0 | 19.8 |
| 建筑用砂 | 65.6 | 75.0 | 60.0 |
| 纤维素醚 | 0.2 | 0.02 | 0.1 |
| 有机纤维 | 0.2 | 0.2 | 0.1 |
各实施例所得预混不裂建筑砂浆与水拌合后的主要性能参数见表二。
表二
| 性能参数 | 抗压强度MPa | 抗拉黏结强度MPa | 塑性开裂情况 | 干缩开裂情况 |
| 实施例1 | 15 | 0.8 | 不开裂 | 不开裂 |
| 实施例2 | 15 | 0.8 | 不开裂 | 不开裂 |
| 实施例3 | 5 | 0.5 | 不开裂 | 不开裂 |
由表二可见，本发明所述的不裂建筑砂浆可以完全防止开裂，硬化后与墙体材料或其他基体具有较高的粘结力。
Claims (6)
1、一种不裂建筑砂浆，各组份的质量份数如下：
水泥 20-35
矿物掺合料 2-20
建筑用砂 60-75
纤维素醚 0.02-0.2
有机纤维 0.1-0.2。
2、如权利要求1所述的不裂建筑砂浆，其特征在于，所说的水泥为强度不低于42.5强度等级的硅酸盐水泥、普通硅酸盐水泥、矿渣或火山灰硅酸盐水泥。
3、如权利要求1所述的不裂建筑砂浆，其特征在于，所说的矿物掺合料是粉煤灰、磨细水淬高炉矿渣或石灰石粉，细度在100目或以下。
4、如权利要求1所述的不裂建筑砂浆，其特征在于，所说的纤维素醚粘度在100-60000Pa·s之间。
5、如权利要求4所述的不裂建筑砂浆，其特征在于，所说的纤维素醚是羟乙基甲基纤维素或甲基纤维素。
6、如权利要求1所述的不裂建筑砂浆，其特征在于，所说的有机纤维是聚丙烯纤维、聚丙烯酰胺纤维或尼龙-6，纤维的单丝长度为12mm±3mm。