CN1667070A - Rapid waterproof glue for polymer - Google Patents

Abstract

This invention relates to polymer quick effective waterproof glue. Its receipt weight percentage is that synthesis emulsion 45~60, abio-dispersant 0.1~0.2, organic dispersant 0.1~0.2, antifoaming agent 0.1~0.3, common portland cement 30~40, large calcium carbonate 5~15, cement accelerating agent 0.1~1. Two components of liquid and powder is made according to above receipt, they are agitated uniformly and coated on formation level when it is used. Then elastic waterproof paint film is formed quickly with high tensile strength, high damp base level adhesive strength and certain elongation at rupture capability. In addition, this glue can be used as agglomerant to bond ceramic tile, floor tile and polystyrene foaming warming plate.

Description

The quick-acting waterproof glues of polymkeric substance

Technical field

The present invention relates to the quick-acting waterproof glues of a kind of polymkeric substance.

Background technology

At present common polymer cement-base waterproof coating (being called for short " JS " coating) is Ministry of Construction's recommended products, this product adopts organic materials (synthetic macromolecule emulsion) and composite the forming of inorganic materials (cement), safety and sanitation during use, have no irritating odor, belong to environmentally friendly machine, therefore toilet, kitchen and the vault damp proof insulation layer in residential housing all adopts it as waterproof layer.Yet primary coating can not be too thick when construction for this coating, can ftracture when dry solidification otherwise film, and (1～1.5mm), engineering needs ability completion in 2～3 days therefore will to reach specific thickness.So there is the long deficiency of construction period in it not as the polyurethane coating of reaction-curable from the speed of application aspect.

Summary of the invention

The object of the invention is to provide a kind of polymkeric substance quick-acting waterproof glues, can remedy the long deficiency of common polymer cement-base waterproof coating construction period.

Task of the present invention is achieved in that

Its adopt add that cement hardener makes soon coagulate and consolidate soon the Portland cement that special cement has replaced general " JS " coating all to adopt, thereby make product be converted into reaction-curable with strong hydration activity from moisture content volatilization curing, thereby give product and not only can regulate curing speed as required, can thickly be coated with simultaneously, once constructing and to reach required thickness, and can not ftracture, the cohesive strength of tensile strength and moist basal plane is all above " JS " coating, do special requirement simultaneously, it can be used as waterproof layer and can be used as binding agent again, satisfies the paving requirement of polystyrene foam warming plate.

Of the present invention theing contents are as follows stated:

Starting material are introduced:

1. synthetic emulsion: can be benzene emulsion, also can be pure-acrylic emulsion

2. inorganic dispersant: the phosphoric acid salt dispersion agent is tripoly phosphate sodium STPP, Sodium hexametaphosphate 99

3. organic dispersing agent: ammonium polyacrylate dipersant, also polycarboxylate sodium's dispersion agent

4. defoamer: siliceous hydrophobic type defoamer

5. ordinary Portland cement: model is 325#, 425# etc.

6. water-ground limestone: more than 400 orders

7. cement hardener: 711 type accelerating chemicalss (pulvis), it is made up of aluminium vanadine, soda ash, unslaked lime, is the general a kind of cement auxiliary agent of a kind of market sale

Product of the present invention is divided into first, second two components packing, mixes during use and uses, and formula range is as follows:

1. synthetic emulsion 45～60 (weight part)

2. inorganic dispersant 0.1～0.2 (weight part)

3. organic dispersing agent 0.1～0.2 (weight part)

4. defoamer 0.1～0.3 (weight part)

5. ordinary Portland cement 30～40 (weight part)

6. water-ground limestone 5～15 (weight part)

7. cement hardener 0.1～1 (weight part)

Take by weighing starting material by above-mentioned formula rate, will be 1. 2. 3. 4. mix being made into first liquid material component, will 5. 6. mix being made into second powder component, during use with two component blending.After mixing after waiting in use, be coated on the formation level, can be frozen into fast speed have high tensile, climax wet basis face cohesive strength, and have the elastic water-proof of suitable breaking elongation to film.The quick-acting waterproof glues of this polymkeric substance again can be as binding agent in addition, bonding ceramic tile, floor tile and foamed polystyrene warming plate, and effect is fairly obvious.

As follows through Shanghai City material of construction and component quality supervision and inspection station test result:

Assay gathers
					Interventions Requested title and unit		This technical target of the product	Assay	Individual event is judged
Outward appearance liquid components solid constituent		The powder of the homogeneous latex emulsion inclusion-free of inclusion-free, gel-free, nothing caking	The powder of the homogeneous latex emulsion inclusion-free of inclusion-free, gel-free, nothing caking	Qualified
					The wet surface cohesive strength, MPa		≥0.5	1.1	Qualified
Watertightness		0.3MPa, 30min is waterproof	Waterproof	Qualified
					Solids content, %		≥70	87	Qualified
The tensile strength non-processor, conservation rate after the MPa thermal treatment, conservation rate after the % alkaline purification, %		≥1.8 ≥80 ≥70	2.5 135 121	Qualified qualified
					The elongation at break non-processor, conservation rate after the MPa thermal treatment, conservation rate after the % alkaline purification, %		≥120 ≥65 ≥80	139 90 85	Qualified qualified
Time of drying, h		Surface drying≤2, do solid work≤4	Surface drying≤2, do solid work≤4	Qualified
					Explanation	1. above Interventions Requested are full service checks; 2. proportioning: liquid powder: powder=1: 0.8

Assay of this product and the polymer cement waterproof paint standard in People's Republic of China's building material industry standard are compared as follows:

Interventions Requested title and unit	Technical target of the product	This examination and test of products result	Individual event is judged
				The wet surface cohesive strength, MPa	?≥0.5	????1.1	Qualified
Watertightness	0.3MPa, 30min is waterproof	Waterproof	Qualified
				Solids content, %	?≥65	????87	Qualified
The tensile strength non-processor, conservation rate after the MPa thermal treatment, conservation rate after the % alkaline purification, %	?≥1.8 ?≥80 ?≥80	????2.5 ????135 ????121	Qualified
				The elongation at break non-processor, conservation rate after the MPa thermal treatment, conservation rate after the % alkaline purification, %	?≥80 ?≥65 ?≥65	????139 ????90 ????85	Qualified qualified
Time of drying, h	Surface drying≤4, do solid work≤8	Surface drying≤2, do solid work≤4	Qualified

By above-mentioned data as seen, every assay of this product all is better than relevant every index of relevant industry standard, and its time of drying only be in the standard half, can arrive the purpose of quick-acting waterproof effectively.

Embodiment:

The specific embodiment of the invention sees Table (content is weight percentage):

Claims (2)

1. quick-acting waterproof glues of polymkeric substance is characterized in that prescription is:

1. synthetic emulsion 45～60 (weight part)

2. inorganic dispersant 0.1～0.2 (weight part)

3. organic dispersing agent 0.1～0.2 (weight part)

4. defoamer 0.1～0.3 (weight part)

5. ordinary Portland cement 30～40 (weight part)

6. water-ground limestone 5～15 (weight part)

7. cement hardener 0.1～1 (weight part)

Will be 1. 2. 3. 4. mix being made into first liquid material component, will 5. 6. 7. mix being made into second powder component, during use with two component blending.

2. according to the quick-acting waterproof glues of a kind of polymkeric substance of claim 1, it is characterized in that optimum formula is:

1. benzene emulsion C-601 55 (weight part)

2. tripoly phosphate sodium STPP 0.14 (weight part)

3. DL-102 dispersion agent 0.2 (weight part)

4. contain silicon defoaming agent 0.16 (weight part)

5. 425# ordinary Portland cement 35 (weight part)

6. 400 order water-ground limestones 9 (weight part)

7. 711 type qucik-acting agents 0.5 (weight part)

Will be 1. 2. 3. 4. mix being made into first liquid material component, will 5. 6. 7. mix being made into second powder component, during use with two component blending.