CN1308559C - Human body fluid soluble inorganic ceramic fiber sound absorption board and process of production - Google Patents
Human body fluid soluble inorganic ceramic fiber sound absorption board and process of production Download PDFInfo
- Publication number
- CN1308559C CN1308559C CNB200310105699XA CN200310105699A CN1308559C CN 1308559 C CN1308559 C CN 1308559C CN B200310105699X A CNB200310105699X A CN B200310105699XA CN 200310105699 A CN200310105699 A CN 200310105699A CN 1308559 C CN1308559 C CN 1308559C
- Authority
- CN
- China
- Prior art keywords
- human body
- parts
- body fluid
- sound absorption
- soluble
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
一种可溶于人体体液的无机硅酸盐纤维吸声板及其制作方法，该吸声板主要成分的重量百分组成为：可溶纤维30～60%，无机结合剂10～20%，有机结合剂3～5%，填料10～40%其他材料3～9%；可溶于人体体液的无机硅酸盐纤维，该纤维的重量百分组成为SiO2 56～85%，CaO+MgO 11～40%，B2O3 1～2%，Al2O3 0～1%，Fe2O3 0～0.5%，Na2O+K2O 0～0.5%。其制作方法是可溶纤维为主体材料并造粒，加入配比量的结合剂配浆制浆，经成型、干燥、表面处理切割、压花、精切等工序加工而成。可溶纤维吸声板采用与人体体液相溶的可溶纤维为主要原材料，使产品对人体健康的影响降至最低。An inorganic silicate fiber sound-absorbing board soluble in human body fluids and a manufacturing method thereof. The main components of the sound-absorbing board are composed of 30-60% soluble fiber, 10-20% inorganic binder, organic Binder 3-5%, filler 10-40%, other materials 3-9%; inorganic silicate fiber soluble in human body fluids, the weight percentage of the fiber is SiO 2 56-85%, CaO+MgO 11- 40%, B 2 O 3 1-2%, Al 2 O 3 0-1%, Fe 2 O 3 0-0.5%, Na 2 O+K 2 O 0-0.5%. The production method is that the soluble fiber is used as the main material and granulated, and a proportioned amount of binder is added to make pulp, and then processed through molding, drying, surface treatment cutting, embossing, fine cutting and other processes. Soluble fiber sound-absorbing panels use soluble fiber that is compatible with human body fluids as the main raw material to minimize the impact of the product on human health.
Description
Technical field
The present invention relates to a kind of inorganic silicate fiber sound absorption plate that dissolves in human body fluid and preparation method thereof.
Background technology
Traditional architecture acoustical board product serves as the main adhesive that adds proper proportion with raw material such as asbestos, rock wool, mineral wool, expanded perlite, vermiculites mainly, processes through operations such as moulding, drying, cutting, embossing, facings.
There is following problem in the acoustical board product of above manufacture of materials:
Though the acoustical board price of using asbestos to produce is comparatively cheap and since proved asbestos produce and use in, the dust of generation has the human carcinogen is acted on, and is limited or stops using.
Using rock wool, mineral wool, expanded perlite, vermiculite only is about 450 ℃-600 ℃ as the acoustical board product serviceability temperature of main raw material(s) production, is difficult to the requirement that reaches fire-resistant.
Summary of the invention
The objective of the invention is by adopting soluble fibre to replace manufacture of materials soluble fibre acoustical boards such as traditional asbestos, rock wool, mineral wool, expanded perlite, vermiculite, because soluble fibre has enough solubility in human body fluid, the time of staying of fiber in human body can be shortened, fiber is reduced to the infringement of human body minimum, thereby make the soluble fibre plate become the product that does not harm human body.
The technical solution used in the present invention is: develop a kind of inorganic silicate fiber sound absorption plate that dissolves in human body fluid, it is characterized in that this acoustical board predominant quantity percentage composition is:
Soluble fibre 30～60%
Inorganic bonding agent 10～20%
Organic bond 3～5%
Filler 10～40%
Other materials 3～9%.
The above-mentioned inorganic silicate fiber sound absorption plate that dissolves in human body fluid, soluble fibre wherein is the inorganic silicate fiber that dissolves in human body fluid, the weight percent of this fiber consists of:
SiO
2 56～85％
CaO+MgO 11～40％
B
2O
3 1～2％
Al
2O
3 0～1％
Fe
2O
3 0～0.5％
Na
2O+K
2O 0～0.5％。
Above-mentioned inorganic bonding agent is silicon dioxide gel, alumina sol, silicate of soda and/or aluminum sulfate; Above-mentioned organic bond is starch, polyvinyl alcohol, carboxymethyl cellulose, cassava and/or acorn nut powder; Above-mentioned filler is clay, kieselguhr and/or expanded perlite;
Above-mentioned other materials is reinforcing fibre, anti-blushing agent and anticorrisive agent; Wherein: reinforcing fibre is string and/or short glass fiber; Anti-blushing agent is that solid paraffin and/or rosin acid are received; Anticorrisive agent is boric acid, sodium pentachlorophenate and/or bisnaphthol.
A kind of method for making that dissolves in the inorganic silicate fiber sound absorption plate of human body fluid, it is characterized in that soluble fibre is material of main part and granulation, the binding material that adds proportional quantity is joined slurry slurrying, operation such as cuts through moulding, drying, surfacing cutting, embossing, essence and processes;
The step of preparation method is as follows:
(1) fiber granulation: with the soluble fibre granulation, the granularity of granulated wool is 5～20mm, and its slag ball content is 0～5%;
(2) join slurry slurrying: granulated wool and binding material are mixed in required ratio, be stirred to slurry and be suspension, the cotton pulp ratio is≤10%;
(3) moulding: be molded on the fourdrinier and carry out, comprise approach flow, vacuum suction filter dehydration, suction press dehydration and liquid drugs injection cutting part;
(4) drying: the wet mat moisture content is 100～120%, dry 50～150min between 100～350 ℃;
(5) cutting, facing: machine cuts becomes slab, the surface plane planing, and surperficial sprayed coating,
(6) redrying: through the slab of surface spraying, at 100～120 ℃, dry 1～15min;
(7) embossing, machine cuts become accurate finished size, promptly.
The quality index of soluble fibre acoustical board of the present invention is as follows:
Bulk density: 220-600kg/m
3
Flexural strength: 0.7-1.0MPa
Moisture content: 0～3%
Flammable: the A level is not fired
Coefficient of thermal conductivity: normal temperature 0.035-0.0.042W/m.k
Average sound absorption coefficient (125HZ-4000HZ): 0.45-0.7
Solubility: 100-250mg/L
The invention has the advantages that compared with the prior art:
1. adopting the soluble fibre that mixes with human body fluid is main raw material(s), and it is minimum that effect on human health is reduced to.
2. can increase substantially the fire-resistant serviceability temperature (can reach 1000 ℃) of acoustical board,
The specific embodiment
Embodiment 1
One, solvable dimension part weight proportion (kg): SiO
285 parts, 11 parts of CaO+MgO, B
2O
32 parts, Al
2O
31 part, Fe
2O
30.5 part, Na
2O+K
20.5 part of O.
After the step above-mentioned raw materials of preparation method mixed, 1500～1800 ℃ were melt into liquid state in special resistance furnace (or electric arc furnaces, glass have a rest stove), utilized blowing process or got rid of a method (0.3～0.6Mpa blast) and carry out fiber production.
Existing resistance furnace is set up 3 groups of electrodes, because raw material changes, resistance is increased, and conductance reduces, and causes the fusing difficulty, for this increases by 3 groups of electrodes to existing resistance furnace, becomes 6 groups of electrodes, to improve the conductance of raw material.
The inorganic silicate fiber that dissolves in human body fluid that the present invention produces, softness and high resilience, average fibre diameter 1～5 μ m, fibre length is 30～150mm, slag ball content is 5～10%.
Fiber that the present invention obtains in PH7.3～7.5, soaks 24h in the meta-alkalescence solution that temperature is 37 ± 0.5 ℃, uses atomic absorption spectrometry, and its solubility is 100～250mg/L; And the conventional ceramic fiber solubility of contrast is 0mg/L.
Two, soluble fibre acoustical board part predominant quantity proportioning (kg):
60 parts of soluble fibres, 20 parts of silicate of soda or silicon dioxide gels, 5 parts of starch and/or polyvinyl alcohol, 10 parts of kieselguhr and/or expanded perlites, 5 parts of other materials.Other materials is reinforcing fibre (string); Anti-blushing agent (solid paraffin); Anticorrisive agent (boric acid and/or sodium pentachlorophenate)
The step of preparation method of the present invention is as follows;
1, fiber granulation: adopt comminutor to carry out, the granularity of granulated wool is at 10～20mm, and its slag ball content is 5%;
2, join slurry slurrying: granulated wool and binding material are mixed, stir in required ratio, and cotton pulp is than 10%;
3, moulding: on fourdrinier, carry out, comprise approach flow, vacuum suction filter dehydration or suction press dehydration and liquid drugs injection cutting part.Through the wet mat after the dehydration, its moisture content is generally 100～120%.
4, drying: at 100～350 ℃/50～150min, its moisture content of the dried goods of process is below 3%.
5, cutting: cutting comprises rip cutting, crosscut composition, all adopts machine cuts.
6, planing surface: cut, the slab after the crosscut, planish by surface plane.
7, surface spraying: the slab behind the planing surface, carry out surperficial flush coater, the coating for preparing (coating is made by polyvinyl alcohol, calcium carbonate superfine powder powder, titanium dioxide, calcite in powder, SPA202 defoamer etc.) by the pump weight feed, sprays glue with nozzle from the coating storage tank.
8, redrying: the slab through the surface spraying, enter the redrying stove, baking temperature is 100～120 ℃, drying time is at 1～15min.
9, embossing: embossing has several forms such as roll extrusion flower, mold pressing flower, heat embossing.
10, essence is cut: the plate that adopts the machine cuts method will be pressed with decorative pattern cuts into accurate finished size, and size is generally 300 * 300; 400 * 400; 600 * 600 (mm).
The technical indicator of soluble fibre acoustical board of the present invention is as follows:
Bulk density: 220-600kg/m
3
Flexural strength: 0.7-1.0MPa
Moisture content: 0～3%
Flammable: the A level is not fired
Coefficient of thermal conductivity: normal temperature 0.035-0.0.042W/m.k
Average sound absorption coefficient (125HZ-4000HZ): 0.45-0.7
Solubility: 100-250mg/L
Soluble fibre acoustical board of the present invention is equal to except technical indicator or is better than the common acoustical board, can increase substantially the fire-resistant serviceability temperature (can reach 1000 ℃) of acoustical board.
Embodiment 2
One, soluble fibre part weight proportion (kg): SiO
256.5 part, 40 parts of CaO+MgO, B
2O
32 parts, Al
2O
31 part, Fe
2O
30.5 part;
The step of preparation method: 1800～2000 ℃ of fusions; 0.3～0.6Mpa blast; Diameter 5～10 μ m; Length 90～250mm; Slag ball content 5～10%; Solubility 100～250mg/L.
Two, soluble fibre acoustical board part predominant quantity proportioning (kg):
30 parts of soluble fibres, 20 parts in silicate of soda and/or aluminum sulfate, 3 parts of starch and/or carboxymethyl celluloses, 40 parts of kieselguhr or expanded perlites, 7 parts of other materials.Other materials is reinforcing fibre (string and/or a short glass fiber); Anti-blushing agent (rosin acid is received); Anticorrisive agent (boric acid or sodium pentachlorophenate).
The step of preparation method: the soluble fibre granulation to granularity at 5～10mm, slag ball content is 0～1%; Granulated wool and binding material mix, stir in required ratio, and cotton pulp is than 9%; Net forming, vacuum suction filter dehydration, liquid drugs injection cutting on the fourdrinier spreading mass; Moisture content 100～120%, 100～150 ℃/100～150min, to moisture content 2%; Machine cuts, surface plane planing; (100～120 ℃/10～15min of surface spraying, redryings.), embossing, accurately become required finished size, packing.
The quality index of soluble fibre acoustical board: bulk density 220～600kg/m
3Flexural strength: 0.7～1.0Mpa; Moisture content: 0～3%; Flammable: the A level is not fired; Coefficient of thermal conductivity: normal temperature 0.035-0.042W/m.k; Average sound absorption coefficient (125HZ-4000HZ): 0.45～0.7; Solubility: 100～250mg/L (with the assay method of above-mentioned soluble fibre); All the other are with example 1.
Embodiment 3
Soluble fibre part weight proportion (kg): SiO
256 parts, 40 parts of CaO+MgO, B
2O
32 parts, Al
2O
31 part, Fe
2O
30.5 part, Na
2O+K
20.5 part of O; 1800～2000 ℃ of fusions; 0.3～0.6Mpa blast; Diameter 1～6 μ m; Length 100～250mm; Slag ball content 5～8%; Solubility 190～250mg/L.
Soluble fibre acoustical board part predominant quantity proportioning (kg): 50 parts of soluble fibres, 20 parts in silicate of soda and/or aluminum sulfate, totally 24 parts of 3 parts of polyvinyl alcohol and/or carboxymethyl celluloses, kieselguhr and expanded perlite, 3 parts of other materials.Other materials is reinforcing fibre (string or a short glass fiber); Anti-blushing agent (solid paraffin); Anticorrisive agent (sodium pentachlorophenate or sodium pentachlorophenate).
The step of preparation method: soluble fibre granulation, granularity are at 8～15mm, and slag ball content is 1～2%; Granulated wool and binding material mix, stir by dosage, and cotton pulp is than 7.5%; Approach flow moulding, vacuum suction filter dehydration, liquid drugs injection cutting; Moisture content 100～110%, 200～250 ℃/100～120min, to moisture content 2%; Machine cuts, surface plane planing; (100～120 ℃/10～15min of surface spraying, redryings.), embossing, accurately become required finished size, packing.
The quality index of soluble fibre acoustical board: bulk density 220～300kg/m
3Flexural strength: 0.7～1.0Mpa; Moisture content: 0～3%; Flammable: the A level is not fired; Coefficient of thermal conductivity: normal temperature 0.035-0.042W/m.k; Average sound absorption coefficient (125HZ-4000HZ): 0.45～0.7; Solubility: 100～250mg/L (with the assay method of above-mentioned soluble fibre); All the other are with example 1.
Embodiment 4
Soluble fibre (hereinafter to be referred as fiber) part weight proportion (kg): SiO
258 parts, 40 parts of CaO+MgO, B
2O
31 part, Fe
2O
30.5 part, Na
2O+K
20.5 part of O;
1800～2000 ℃ of fusions; 0.3～0.6Mpa blast; Diameter 6～10 μ m; Length 150～250mm; Slag ball content 5～14%; Solubility 180～250mg/L.
Soluble fibre plate (hereinafter to be referred as plate) part proportioning (kg): 60 parts of soluble fibres, 10 parts of silicate of soda and/or silicon dioxide gels, 5 parts in cassava and/or acorn nut powder, 16 parts of kieselguhr or expanded perlites, 9 parts of other materials.
Other materials is reinforcing fibre (short glass fiber); Anti-blushing agent (rosin acid is received); Anticorrisive agent (boric acid or sodium pentachlorophenate).
The step of preparation method: soluble fibre granulation, granularity are at 10～15mm, and slag ball content is 2～3%; Granulated wool and binding material mix, stir by dosage, and cotton pulp is than 6.5%; Approach flow moulding, vacuum suction filter dehydration, liquid drugs injection cutting; Moisture content 100～110%, 200～250 ℃/100～120min, to moisture content 2%; Machine cuts, surface plane planing; (100～120 ℃/10～15min of surface spraying, redryings.), embossing, accurately become required finished size, packing.
The quality index of plate: bulk density 220～300kg/m
3Flexural strength: 0.7～1.0Mpa; Moisture content: 2.5%; Flammable: the A level is not fired; Coefficient of thermal conductivity: normal temperature 0.035-0.042W/m.k; Average sound absorption coefficient (125HZ-4000HZ): 0.45～0.7; Solubility: 100～250mg/L (with the assay method of above-mentioned soluble fibre); All the other are with example 1.
Embodiment 5
Fibre furnish (kg): SiO
260 parts, 38.5 parts of CaO+MgO, B
2O
31 part, Na
2O+K
20.5 part of O; 1800～2000 ℃ of fusions; 0.3～0.6Mpa blast; Diameter 2～5 μ m: length 30～200mm; Slag ball content 5～15%; Solubility 100～200mg/L.
Plate proportioning (kg): 45 parts of soluble fibres, 20 parts in silicate of soda and/or aluminum sulfate, 5 parts in carboxymethyl cellulose and/or acorn nut powder, 21 parts in clay and/or kieselguhr, 9 parts of other materials.
Other materials is reinforcing fibre (short glass fiber); Anti-blushing agent (rosin acid is received); Anticorrisive agent (boric acid or sodium pentachlorophenate).
The soluble fibre granulation, granularity 10～15mm, slag ball content 2～3%; Granulated wool and binding material mix, stir by dosage, and cotton pulp is than 8.5%: moisture content 100～110%, 200～250 ℃/100～120min, do to moisture content 2%; 100～120 ℃/10～15min of redrying.
The quality of plate: bulk density 550～600kg/m
3Flexural strength: 0.7～1.0Mpa; Moisture content: 1.5%: combustibility: the A level is not fired; Coefficient of thermal conductivity: normal temperature 0.035-0.042W/m.k; Average sound absorption coefficient (125HZ-4000HZ): 0.45～0.7; Solubility: 100～250mg/L (with the assay method of above-mentioned soluble fibre); All the other are with example 2.
Embodiment 6
Soluble fibre weight proportion (kg): SiO
270 parts, 27.5 parts of CaO+MgO, B
2O
32 parts, Na
2O+K
20.5 part of O; 1500～1900 ℃ of fusions; 0.3～0.6Mpa blast: diameter 2～5 μ m; Length 90～250mm; Slag ball content 5～13%; Solubility 100～200mg/L.
Soluble fibre acoustical board part predominant quantity proportioning (kg): 55 parts of soluble fibres, 18 parts of silicate of soda and/or silicon dioxide gels, 5 parts of starch and/or polyvinyl alcohol, 13 parts of kieselguhr or expanded perlites, 9 parts of other materials.
Other materials is reinforcing fibre (short glass fiber); Anti-blushing agent (rosin acid is received); Anticorrisive agent (boric acid or sodium pentachlorophenate).
The soluble fibre granulation, granularity 15～20mm, slag ball content 2.5～3%; Cotton pulp is than 8.5%; Moisture content 100～110%, 200～250 ℃/100～120min are done to moisture content 1.5%; 100～120 ℃/10～15min of redrying.
The quality of plate: bulk density 500～550kg/m
3Flexural strength: 0.7～1.0Mpa; Moisture content: 1.5%; Flammable: the A level is not fired; Coefficient of thermal conductivity: normal temperature 0.035-0.042W/m.k; Average sound absorption coefficient (125HZ-4000HZ): 0.45～0.7; Solubility: 100～250mg/L (with the assay method of above-mentioned soluble fibre); All the other are with example 1.
Embodiment 7
Soluble fibre part weight proportion (kg down together): SiO
262 parts, 35.5 parts of CaO+MgO, B
2O
32 parts, Fe
2O
30.5 part; 1800～2000 ℃ of fusions; 0.3～0.6Mpa blast; Diameter 4～7 μ m; Length 70～250mm; Slag ball content 5～8%; Solubility 200～250mg/L.
Soluble fibre acoustical board part predominant quantity proportioning (kg): 45 parts of soluble fibres, 20 parts of silicon dioxide gel and/or alumina sols, 5 parts of starch or polyvinyl alcohol, 27 parts of kieselguhr or expanded perlites, 3 parts of other materials.
Other materials is reinforcing fibre (short glass fiber); Anti-blushing agent (solid paraffin and rosin acid are received); Anticorrisive agent (boric acid and/or bisnaphthol).
The soluble fibre granulation, granularity 10～15mm, slag ball content 3.5～4%; Cotton pulp is than 5.5%; Moisture content 100～110%, 300～350 ℃/50～100min are done to moisture content 0.5%; 100～120 ℃/10～15min of redrying.
The quality of plate: bulk density 400～450kg/m
3Flexural strength: 0.7～1.0Mpa; Moisture content: 0.5%; Flammable: the A level is not fired; Coefficient of thermal conductivity: normal temperature 0.035-0.042W/m.k; Average sound absorption coefficient (125HZ-4000HZ): 0.45～0.7; Solubility: 100～250mg/L (with the assay method of above-mentioned soluble fibre); All the other are with example 1.
Embodiment 8
Soluble fibre weight proportion: SiO
258.5 part, 39.5 parts of CaO+MgO, B
2O
31 part, Al
2O
30.1 part, Fe
2O
30.5 part, Na
2O+K
20.4 part of O; 1800～2000 ℃ of fusions; 0.3～0.6Mpa blast; Diameter 4～8 μ m; Length 30～200mm; Slag ball content 5～10%; Solubility 200～250mg/L.
Soluble fibre acoustical board part, predominant quantity proportioning (kg): 52 parts of soluble fibres, 18 parts of alumina sol and/or silicate of soda, 4 parts of starch and/or carboxymethyl celluloses, 23 parts of kieselguhr or clays, 3 parts of other materials.
Other materials is reinforcing fibre (short glass fiber); Anti-blushing agent (solid paraffin and rosin acid are received); Anticorrisive agent (boric acid and/or bisnaphthol).
The soluble fibre granulation, granularity 10～13mm, slag ball content 3～4%; Cotton pulp is than 7.5%; Moisture content 100～110%, 300～350 ℃/50～100min are done to moisture content 0.5%; 100～120 ℃/10～15min of redrying.
The quality of plate: bulk density 300～350kg/m
3Flexural strength: 0.7～1.0Mpa; Moisture content: 0.5%; Flammable: the A level is not fired; Coefficient of thermal conductivity: normal temperature 0.035-0.042W/m.k; Average sound absorption coefficient (125HZ-4000HZ): 0.45～0.7; Solubility: 100～250mg/L (with the assay method of above-mentioned soluble fibre); All the other are with example 1.
Embodiment 9
Soluble fibre weight proportion: SiO
257 parts, 40 parts of CaO+MgO, B
2O
32 parts, Al
2O
30.3 part, Fe
2O
30.3 part, Na
2O+K
20.4 part of O; 1900～2000 ℃ of fusions; 0.3～0.6Mpa blast; Diameter 6～10 μ m; Length 150～250mm; Slag ball content 5～12%; Solubility 150～250mg/L.
53 parts of soluble fibres, 17 parts of silicon dioxide gel and/or silicate of soda, 5 parts starch and/or cassavas, 22 parts of expanded perlite or clays, 3 parts of other materials.
Other materials is reinforcing fibre (string and/or a short glass fiber); Anti-blushing agent (solid paraffin and/or rosin acid are received); Anticorrisive agent (boric acid and/or bisnaphthol).
The soluble fibre granulation, granularity 10～15mm, slag ball content 4～5%; Cotton pulp is than 6.5%; Moisture content 100～110%, 300～350 ℃/50～100min are done to moisture content 0.85%; 100～120 ℃/10～15min of redrying.
The quality of plate: bulk density 250～300kg/m
3Flexural strength: 0.7～1.0Mpa; Moisture content: 0.5%; Flammable: the A level is not fired; Coefficient of thermal conductivity: normal temperature 0.035-0.042W/m.k; Average sound absorption coefficient (125HZ-4000HZ): 0.45～0.7; Solubility: 100～250mg/L (with the assay method of above-mentioned soluble fibre); All the other are with example 1.
Embodiment 10
Fibre furnish (kg): SiO
280 parts, 17 parts of CaO+MgO, B
2O
32 parts, Fe
2O
30.5 part, Na
2O+K
2O0.5 part; 1900～2000 ℃ of fusions; 0.3～0.6Mpa blast; Diameter 3～6 μ m; Length 100～250mm; Slag ball content 5～14%; Solubility 100～240mg/L.
Plate proportioning: 53 parts of soluble fibres, 12 parts of silicon dioxide gels, 3 parts of starch and/or polyvinyl alcohol, 5 parts starch and/or cassavas, 23 parts of expanded perlite or clays, 4 parts of other materials.
Other materials is reinforcing fibre (string and/or a short glass fiber); Anti-blushing agent (solid paraffin and/or rosin acid are received); Anticorrisive agent (boric acid and/or bisnaphthol).
The soluble fibre granulation, granularity 16～20mm, slag ball content 3～4%; Cotton pulp is than 9.5%; Moisture content 100～110%, 300～350 ℃/50～100min are done to moisture content 0.5%; 100～120 ℃/10～15min of redrying.
The quality of plate: bulk density 300～350kg/m
3Flexural strength: 0.7～1.0Mpa; Moisture content: 0.5%; Flammable: the A level is not fired; Coefficient of thermal conductivity: normal temperature 0.035～0.042W/m.k; Average sound absorption coefficient (125HZ-4000HZ): 0.45～0.7; Solubility: 100～250mg/L (with the assay method of above-mentioned soluble fibre); All the other are with example 1.
Claims (6)
1. inorganic silicate fiber sound absorption plate that dissolves in human body fluid is characterized in that:
(1) this acoustical board predominant quantity percentage composition is:
Soluble fibre 30～60%
Inorganic bonding agent 10～20%
Organic bond 3～5%
Filler 10～40%
Other materials 3～9%;
(2) described soluble fibre is the inorganic silicate fiber that dissolves in human body fluid, and the weight percent of this fiber consists of:
SiO
2 56～85％
CaO+MgO 11～40％
B
2O
3 1～2％
Al
2O
3 0～1％
Fe
2O
3 0～0.5％
Na
2O+K
2O 0～0.5％。
2. according to the described inorganic silicate fiber sound absorption plate that dissolves in human body fluid of claim 1, it is characterized in that described inorganic bonding agent is silicon dioxide gel, alumina sol, silicate of soda and/or aluminum sulfate.
3. according to the described inorganic silicate fiber sound absorption plate that dissolves in human body fluid of claim 1, it is characterized in that described organic bond is starch, polyvinyl alcohol, carboxymethyl cellulose, cassava and/or acorn nut powder.
4. according to the described inorganic silicate fiber sound absorption plate that dissolves in human body fluid of claim 1, it is characterized in that described filler is clay, kieselguhr and/or expanded perlite.
5. according to the described inorganic silicate fiber sound absorption plate that dissolves in human body fluid of claim 1, it is characterized in that described other materials is reinforcing fibre, anti-blushing agent and anticorrisive agent; Wherein: reinforcing fibre is string and/or short glass fiber; Anti-blushing agent is that solid paraffin and/or rosin acid are received; Anticorrisive agent is boric acid, sodium pentachlorophenate and/or bisnaphthol.
6. according to the described preparation method that dissolves in the inorganic silicate fiber sound absorption plate of human body fluid of claim 1, it is characterized in that soluble fibre is material of main part and granulation, the binding material that adds proportional quantity is joined slurry slurrying, processes through moulding, drying, surfacing cutting, embossing, smart cutting process;
The step of preparation method is as follows:
(1) fiber granulation: with the soluble fibre granulation, the granularity of granulated wool is 5～20mm, and its slag ball content is 0～5%;
(2) join slurry slurrying: granulated wool and binding material are mixed in required ratio, be stirred to slurry and be suspension, cotton pulp is than≤10%;
(3) moulding: be molded on the fourdrinier and carry out, comprise approach flow, vacuum suction filter dehydration or suction press dehydration and liquid drugs injection cutting part;
(4) drying: the wet mat moisture content is 100～120%, dry 50～150min between 100～350 ℃;
(5) cutting, facing: machine cuts becomes slab, the surface plane planing, and surperficial sprayed coating,
(6) redrying: through the slab of surface spraying, at 100～120 ℃, dry 1～15min;
(7) embossing, machine cuts become accurate finished size, promptly.