CN1303237C - 铝合金螺丝的制备方法 - Google Patents
铝合金螺丝的制备方法 Download PDFInfo
- Publication number
- CN1303237C CN1303237C CNB2005100944413A CN200510094441A CN1303237C CN 1303237 C CN1303237 C CN 1303237C CN B2005100944413 A CNB2005100944413 A CN B2005100944413A CN 200510094441 A CN200510094441 A CN 200510094441A CN 1303237 C CN1303237 C CN 1303237C
- Authority
- CN
- China
- Prior art keywords
- aluminium alloy
- preparation
- quenching
- bars
- screw
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种铝合金螺丝的制备方法，所述合金成份的原料组成重量份为：Al 88.9～91.7、Mg 2.0～3.0、Zn 5.1～6.1、Cu 1.2～2.0。其制备方法如下：一、按配比将原料置于熔炼炉内熔炼，熔炼炉内铝合金熔融液温度控制在700～720℃，然后拉制成铝合金棒；二、将步骤一制备的铝合金棒置于加热炉内加热保温，使铝合金棒成份均匀化，加热温度控制在450～475℃，保温时间8～12小时，然后将上述铝合金棒置于挤压机上挤压成型，挤压温度：320～450℃；三、将步骤二制备的铝合金螺丝半成品置于时效淬火炉内时效淬火，淬火温度138±5℃，保温时间16±2小时，得铝合金螺丝成品。本发明铝合金螺丝硬度高、耐酸性好，塑性又好，其制备方法简单，方便，实用。
Description
技术领域：
本发明涉及一种螺丝。尤其是涉及一种铝合金材料制作的铝合金螺丝的制备方法。主要用于建筑门窗行业的铝合金表面处理作紧固件，属金属连接件技术领域。
背景技术：
螺丝是建筑门窗行业的重要连接件，在本发明作出以前，传统的用于门窗行业的螺丝均为钢制螺丝。钢制螺丝不耐酸，塑性差，耗用大，成本高。
发明内容：
本发明的目的在于克服上述不足，提供一种耐酸、塑性好、成本低的铝合金螺丝的制备方法。
本发明的目的是这样实现的：一种铝合金螺丝的制备方法，所述合金中主要成份为铝，铝合金成份原料组成重量份为：Al 88.9～91.7、Mg 2.0～3.0、Zn 5.1～6.1、Cu 1.2～2.0，其特征在于：其制备方法包括以下工艺步骤：
步骤一、制备铝合金棒 按重量份将Al、Mg、Zn和Cu置于熔炼炉内熔炼，熔炼炉内铝合金熔融液温度控制在700～720℃，熔炼炉表面加入覆盖剂，然后拉制成铝合金棒；
步骤二、制备铝合金螺丝半成品 将步骤一制备的铝合金棒置于加热炉内加热保温，使铝合金棒成份均匀化，加热温度控制在450～475℃，保温时间8～12小时，然后将上述铝合金棒置于挤压机上挤压成型，挤压温度：320～450℃；
步骤三、时效淬火 将步骤二制备的铝合金螺丝半成品置于时效淬火炉内时效淬火，淬火温度138±5℃，保温时间16±2小时，得铝合金螺丝成品。
纯铝塑性好，但硬度低，耐酸腐蚀性差，本发明在铝料中加锌和镁可以形成强化相，提高螺丝的硬度、塑性和耐腐蚀性能；加铜可以增强螺丝的硬度和延伸力。因此本发明铝合金螺丝硬度高，塑性好，延伸力强，耐酸防腐性能好，成本低。
本发明制备方法简单，方便，实用。
具体实施方式：
实施例1：
步骤一、制备铝合金棒 按重量份将Al 90.7、Mg 2.0、Zn 6.1和Cu 1.2置于熔炼炉内熔炼，熔炼炉内铝合金熔融液温度控制在700℃，熔炼炉表面加入覆盖剂，然后拉制成铝合金棒；
步骤二、制备铝合金螺丝半成品 将步骤一制备的铝合金棒置于加热炉内加热保温，使铝合金棒成份均匀化，加热温度控制在450℃，保温时间12小时，然后将上述铝合金棒置于挤压机上挤压成型，挤压温度：320℃；
步骤三、时效淬火 将步骤二制备的铝合金螺丝半成品置于时效淬火炉内时效淬火，淬火温度138℃，保温时间16小时，得铝合金螺丝成品。
实施例2：
步骤一、制备铝合金棒 按重量份将Al 88.9、Mg 3.0、Zn 5.1和Cu 2.0置于熔炼炉内熔炼，熔炼炉内铝合金熔融液温度控制在710℃，熔炼炉表面加入覆盖剂，然后拉制成铝合金棒；
步骤二、制备铝合金螺丝半成品 将步骤一制备的铝合金棒置于加热炉内加热保温，使铝合金棒成份均匀化，加热温度控制在475℃，保温时间8小时，然后将上述铝合金棒置于挤压机上挤压成型，挤压温度：450℃；
步骤三、时效淬火 将步骤二制备的铝合金螺丝半成品置于时效淬火炉内时效淬火，淬火温度143℃，保温时间14小时，得铝合金螺丝成品。
实施例3：
步骤一、制备铝合金棒 按重量份将Al 91.7、Mg 2.5、Zn 5.5、Cu 1.5置于熔炼炉内熔炼，熔炼炉内铝合金熔融液温度控制在720℃，熔炼炉表面加入覆盖剂，然后拉制成铝合金棒；
步骤二、制备铝合金螺丝半成品 将步骤一制备的铝合金棒置于加热炉内加热保温，使铝合金棒成份均匀化，加热温度控制在460℃，保温时间10小时，然后将上述铝合金棒置于挤压机上挤压成型，挤压温度：400℃。
步骤三、时效淬火 将步骤二制备的铝合金螺丝半成品置于时效淬火炉内时效淬火，淬火温度133℃，保温时间18小时，得铝合金螺丝成品。
Claims (1)
1、一种铝合金螺丝的制备方法，所述合金中主要成份为铝，合金成份的原料组成重量份为：Al 88.9～91.7、Mg 2.0～3.0、Zn 5.1～6.1、Cu 1.2～2.0，其特征在于：其制备方法包括以下工艺步骤：
步骤一、制备铝合金棒按重量份将Al、Mg、Zn和Cu置于熔炼炉内熔炼，熔炼炉内铝合金熔融液温度控制在700～720℃，熔炼炉表面加入覆盖剂，然后拉制成铝合金棒；
步骤二、制备铝合金螺丝半成品将步骤一制备的铝合金棒置于加热炉内加热保温，使铝合金棒成份均匀化，加热温度控制在450～475℃，保温时间8～12小时，然后将上述铝合金棒置于挤压机上挤压成型，挤压温度：320～450℃；
步骤三、时效淬火将步骤二制备的铝合金螺丝半成品置于时效淬火炉内时效淬火，淬火温度138±5℃，保温时间16±2小时，得铝合金螺丝成品。