CN1234880C - 钢铁用复合脱硫剂及其制造方法 - Google Patents
钢铁用复合脱硫剂及其制造方法 Download PDFInfo
- Publication number
- CN1234880C CN1234880C CN 03112433 CN03112433A CN1234880C CN 1234880 C CN1234880 C CN 1234880C CN 03112433 CN03112433 CN 03112433 CN 03112433 A CN03112433 A CN 03112433A CN 1234880 C CN1234880 C CN 1234880C
- Authority
- CN
- China
- Prior art keywords
- calcium
- calcium oxide
- calcium carbide
- desulfurizing agent
- steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种钢铁用复合脱硫剂，由20-75%的氧化钙，5-20%的氟化钙，10-60%的碳化钙以及3-10%的碳酸钡组成。其中氧化钙和碳化钙经过钝化处理。较碳化钙脱硫剂制造成本下降20-60%；同时由于引进了碳酸钡，明显提高了脱硫渣中硫化物的稳定性，有效防止了回硫现象；脱硫反应速度明显提高，脱硫效果优良。可广泛应用于冶炼行业钢水和铁水的脱硫精炼。
Description
技术领域 本发明涉及一种用于铁水与钢水脱硫的组合物及其制造方法，特别是一种适用于电炉与冲天炉铁水炉外脱硫的组合物及其制造方法。
背景技术 公开的中国专利CN1158359提出了“一种铸铁冶炼用脱硫剂”，以工业石灰石为基料，再配以白云石、萤石、工业苏打、工业碳化硅以及粘结剂组合而成。这种方案在一定程度上解决了石灰易于吸潮的问题，但其反应速度较慢，且吸热多铁水降温增加。CN1061438则公开了一种由电石、萤石、氯化钠、冰晶粉等原料组成的铸铁、铸钢精炼剂，其主要缺陷是成本较高。而专利号为8510442.7的“细粒状铁水脱硫剂及生铁水脱硫方法”，则选用了碳化钙、释氢化合物和镁组成的组合物。众所周知，金属镁在储存运输中易氧化、易爆炸，脱硫时吸收率低，刺目的镁光影响操作，而且镁的价格非常高，是碳化钙的十倍左右，它的使用势必造成成品造价过高的缺陷。
另外，上述方案中大量采用了碳酸钙、碳酸镁和碳酸钠，这些组分易于分解产生二氧化碳，是一个吸热过程，降低了钢(铁)水的温度，又不利于反应速度的提高。
氧化钙是一种具有一定的脱硫效果而且成本低廉的冶炼脱硫剂制造原料，但由于其单独使用脱硫效果欠佳，长途运输中容易吸潮变性等缺陷在应用中不易达到满意的脱硫效果。
中国专利公开文献CN1317585“钢铁用复合脱硫剂及其制造方法”提供了解决上述问题的一种技术方案，其集中了氧化钙\碳化钙和氟化钙的优点，对于提高脱硫反应速度，改善脱硫效果起到了明显的作用.但该发明专利申请并未公开其”适量助剂”的成分。从实践中得知，采用这一技术方案仍存在以下问题，即在脱硫后，脱硫渣易于返回到铁水(钢水)中去，影响脱硫效果。
发明内容 本发明的目的是克服同行业在选料时的不足，提供一种以氧化钙为主要原料的钢铁用复合脱硫剂组合物，配以防止脱硫渣回硫的有效成分，并提出对该原料进行予处理的工艺方法。本发明的技术方案可在保证脱硫效果和铸件质量的前提下，大幅度降低制造成本，提高钢(铁)液质量与铸件生产经济效益。
本发明的目的可以通过如下措施来达到：一种钢铁用复合脱硫剂，其由以下成分组成(重量百分比)：氧化钙20-75％，氟化钙5-20％，碳化钙10-60％，碳酸钡3-10％。
本发明的目的还可以通过如下措施来达到：一种钢铁用复合脱硫剂，其由以下成分组成(重量百分比)：氧化钙30--70％，氟化钙5-20％，碳化钙20-55％，碳酸钡3-10％。其中碳酸钡及其用量的选择是本发明的关键。
本发明的目的还可以通过如下措施来达到：一种钢铁用复合脱硫剂的制造方法，对氧化钙和碳化钙进行钝化处理，即分别或同时在专用混合搅拌设备中，在氧化钙和碳化钙的表面均匀地挂上一层防潮膜，然后按照比例与其它组分混合均匀。
本发明具有以下特点：(1)、以氧化钙为主要原料，较碳化钙脱硫剂制造成本下降20-60％；(2)、由于引进了碳酸钡，明显提高了脱硫渣中硫化物的稳定性，有效防止了回硫现象；(3)、氧化钙和碳化钙经过防潮钝化处理，其使用性能和安全性能得以保证；(4)、脱硫反应速度明显提高，脱硫效果优良。下面结合反应机理和实施例进一步说明本发明。
化学反应式如下：
CaC2所生成的Ca具有脱硫和脱氧作用。所述的氟化钙和碳酸钡具有降低氧化钙和碳化钙熔点的作用，可加快其反应速度。
具体实施方式
实施例一
各组分含量(重量百分比)：氧化钙75％，碳化钙15％，氟化钙5％，碳酸钡 5％。
首先将定量的氧化钙进行钝化处理，即分别或同时在专用混合搅拌设备中，在氧化钙的表面均匀地挂上一层防潮膜，然后按照比例与其它组分混合均匀。
实施例二
各组分含量(重量百分比)：氧化钙45％，氟化钙5％，碳化钙40％，碳酸钡10％。
首先将定量的氧化钙和碳化钙进行钝化处理，即分别或同时在专用混合搅拌设备中，在氧化钙和碳化钙的表面均匀地挂上一层防潮膜，然后按照比例与其它组分混合均匀。
实施例三
各组分含量(重量百分比)：氧化钙20％，氟化钙20％，碳化钙55％，碳酸钡5％。首先将定量的氧化钙和碳化钙进行钝化处理，即分别或同时在专用混合搅拌设备中，在氧化钙和碳化钙的表面均匀地挂上一层防潮膜，然后按照比例与其它组分混合均匀。
实施例四
各组分含量(重量百分比)：氧化钙49％，氟化钙10％，碳化钙35％，碳酸钡6％。
首先将定量的氧化钙和碳化钙进行钝化处理，即分别或同时在专用混合搅拌设备中，在氧化钙和碳化钙的表面均匀地挂上一层防潮膜，然后按照比例与其它组分混合均匀。
Claims (3)
1、一种钢铁用复合脱硫剂，其特征是：它由以下成分组成：氧化钙20-75％，氟化钙5-20％，碳化钙10--60％，碳酸钡3-10％；
所述百分比为重量百分比。
2、根据权利要求1所述的脱硫剂，其特征是：氧化钙30--70％，氟化钙5-20％，碳化钙20-55％，碳酸钡3-10％。
3、根据权利要求1或2所述的脱硫剂的制造方法，其特征是：对氧化钙和碳化钙进行钝化处理，即分别或同时在混合搅拌设备中，在氧化钙和碳化钙的表面均匀地挂上一层防潮膜，然后按照比例与其它组分混合均匀。